TuskXC2700T is a transparent material with a slight blue tinge. It is suitable for strong, water-resistant prototypes with ABS- and PBT-like specifications (e.g. parts for water flow analysis and wind tunnel testing). Other applications include functional prototypes and high-end finished models.

Technical Specifications

Standard lead time

Minimum of 3 working days , depending on part size, number of components and finishing degrees (offline orders)
4 working days (online orders)

Unfinished parts typically have visible building layers on the surface but post-production finishes can achieve different effects, from high glosses to coarse textures. Stereolithography parts can be sandblasted, smoothed, colored/impregnated, painted, varnished, covered and coated

Datasheet

Units

ASTM#

Range

Density

g/cm³

1.18 – 1.2

Tensile Strength

MPa

D638M

47.1 – 53.6

Tensile Modulus

MPa

D638M

2650 – 2880

Elongation at Break

%

D638M

11- 20

Flexural Strength

MPa

D790M

63.1 – 74.16

Flexural Modulus

MPa

D790M

2040– 2370

Notched Izod Impact

J/m

D256A

20– 30

Hardness

Shore D

D2240

81

Heat Deflection Temp

°C

D648-98c

at 0.46 MPa: 45.9 – 54.5
at 1.81 MPa: 49.0 – 49.7

Actual values may vary with build condition

Finishing Degrees

Finishing

Support removal

Curing

Sandblasting

Smoothing

Primer

Coating/Paint

Basic

◆

◆

Support Marks Removed

◆

◆

◆

Normal

◆

◆

◆

◆
Building layers not visible

Technical Transparent

◆

◆

◆

◆
Building layers slightly visible

◆

◆
Transparent paint on all surfaces

Cosmetic Transparent

◆

◆

◆

◆
Building layers not visible

◆

◆
Transparent paint on all surfaces

How Does Stereolithography Work?

Stereolithography is a laser-based technology that uses a UV-sensitive liquid resin. A UV laser beam scans the surface of the resin and selectively hardens the material corresponding to a cross section of the product, building the 3D part from the bottom to the top. The required supports for overhangs and cavities are automatically generated, and later manually removed.