HEART OF THE SYSTEM, Hobie Hewett reviews the process data on the MPCS system that provides a direct link to METALAST.

MITCHELL masks parts carefully, using tiny brushes and applicators.

1. Coating formation vs. anodizing time.

SAMPLE of the type of parts anodized at Universal Metal Finishing.

Universal Metal Finishing has built a reputation in the automotive, electronic, diecasting and aviation industries for quality hardcoat anodizing. Now the company has implemented an innovative technology that allows it to give its customers the best hardcoating possible.

In the spring of 1995, Charles Roberts, president of Universal, Chicago, Illinois, took some parts to Newport Beach, California, to check out a new anodizing process. "When I saw how well the process worked, I was a convert," stated Mr. Roberts.

Universal did not bring the new technology in house immediately, however. Capital equipment upgrades were necessary so the computers could communicate with the rectifiers. Universal also rebussed some tanks. Upgrades were completed the fall of 1996, and in January 1997, Universal hooked up its first process line. The balance of the lines was upgraded in May 1997. Most of the processing parameters, such as pH and temperature have remained the same. The biggest difference is the chemistry and computer process control.

The process provides for increased surface hardness, greater abrasion resistance and excellent surface lubricity. Universal has also found that the process greatly reduces edge effects and crazing.

Universal's rectifier upgrades allowed it to interface with the MPCS computerized system that completely automates the actual run portion of the anodizing process. The system accepts job information entered by the operator at Universal, including alloy, target oxide thickness and surface area to obtain desired finish characteristics. The MPCS automatically controls and monitors Universal's rectifier output and monitors other bath parameters. After the production run, the system verifies the process with a printed job ticket with the operating parameters.

The MPCS is connected to the central monitoring system at METALAST, which provides operating support and updated anodizing recipes. Updated recipes are downloaded from the master monitoring system to each MPCS in the field.

The control system incorporates a proprietary rectification control algorithm that allows Universal's existing rectifiers to produce a pulsed output. This allows the anodizing solution to cool faster and reduce burning. Recirculating acid through the chiller keeps the baths cool.

The "special ingredient" in the new bath is a proprietary additive that prevents aluminum from burning and limits color fading and discoloration at high temperatures. It also provides Universal's parts, such as pistons, with a more uniform oxide.

"The bath requires a lot of attention," noted Mr. Roberts. "However, there are no hazardous materials in the discharge water, and there is little aluminum buildup in the anodizing electrolyte." Universal also uses polypropylene 10-, 12-, 18- and 20-ft tanks. The polypropylene makes it easier to control the anode:cathode ratio.

Another advantage for Universal is that it no longer has to tweak the concentrations in the bath to handle various alloys. Most of the alloys anodized at Universal are the standard 6061. It also anodizes 70 series and 20 series, which are mainly aircraft components. Extensive testing was done with the process prior to its implementation. Part of the research and development effort was experimenting with anodizing difficult alloys and dicecastings to prevent burning and, in certain cases, produce a maximum oxide thickness. The bath anodized all types of aluminum.

Testing revealed that the bath could produce the exact anodic oxide desired at any reasonable bath temperature. The process operates at various levels, depending on the type of surface finish needed on the various parts processed at Universal.

So, how difficult was it to convince its customers that the new bath was all it needed and more? "We were able to easily convert most of our 450 customers," stated Mr. Roberts.

Other customers, such as a major automotive manufacturer, came to Universal because through METALAST research and development problems were addressed and solved. The automotive manufacturer was having an adhesion problem with a typical production part. The company mounts a PC board to one side of the aluminum and plastic to the other. METALAST and the automotive manufacturer worked out a solution, and Universal provides the finish. All this was at no charge to Universal or the automobile manufacturer. "If we didn't have the link with METALAST, I don't think we could have had the job. This is a service they provide to us as part of our license," said Hobie Hewett, vice president. "The typical job shop cannot afford research and development such as this. METALAST does it for us, saving us the expense."

TABLE ICorrosion Resistance Results

Alloy

Salt Spray HoursAt Failure

2024-T3

4566

3003-H14

4065

5005-H34

4065

6061-T6

4065

6063-T52

4732

7075-T6

4065

METALAST has also done some specific performance testing in addition to head-to-head comparisons between the process and conventional anodizing. Tests include corrosion resistance, thickness and coating formation rate. (See Tables I-III and Figure 1.)

"We thought we would have to charge a premium price for this process," stated Mr. Roberts, "but we are finding that is just not true." Universal can run the processes more quickly, and the savings in production time has translated into savings for the customers. "The major difference between our anodizing and all others is that while many anodizers are able to achieve a good surface most of the time, Universal can achieve it all of the time," concluded Mr. Roberts.

TABLE IITarget and Resultant Thickness of Anodic Coatings

Type II Coating Thickness

Type III Coating Thickness

(mil)

(mil)

Alloy

Targeted

Resultant

Targeted

Resultant

1100-H14

0.7

0.74±0.03

-

-

2024-T3

0.7

0.71±0.04

1.5

1.50±0.06

3003-H14

0.7

0.73±0.03

1.5

1.53±0.04

5005-H34

0.7

0.74±0.04

1.5

1.50±0.04

6061-T6

0.7

0.73±0.03

1.5

1.48±0.04

6063-T52

0.7

0.72±0.04

1.5

1.47±0.05

7075-T6

0.7

0.72±0.03

1.5

1.52±0.05

TABLE III--Coating Formation Rate at Various Current Densities

Coating Formation Rate (mil/min)

METALAST-Type II

METALAST-Type III

Alloy Type

18 asf

24 asf

24 asf

30 asf

40 asf

2024-T3

0.022

0.031

0.037

0.045

0.064

3003-H14

0.025

0.034

0.042

0.051

0.070

5005-H34

0.025

0.034

0.042

0.051

0.070

6061-T6

0.025

0.034

0.042

0.052

0.072

6063-T52

0.025

0.034

0.042

0.052

0.072

7075-T6

0.025

0.034

0.042

0.052

0.072

356

0.025

0.034

-

0.039

0.051