Abstract

The invention provides a golf ball having a core and a cover of at least one layer. The core is formed of a rubber composition which includes a polybutadiene-containing base rubber, an unsaturated carboxylic acid and/or a metal salt thereof, an organic peroxide and sulfur, and for which the value of [sulfur (mol)÷available active oxygen content in organic peroxide] is at least 0.01 and not more than 0.019.

Description

BACKGROUND OF THE INVENTION

The present invention relates to a golf ball having a core and a cover composed of at least one layer. More specifically, the invention relates to a golf ball which is capable of achieving satisfactory distances on shots with both drivers and middle irons used by professional golfers and skilled amateurs.

Solid golf balls have a relatively simple inner structure composed of a core and a cover, although various golf ball properties such as rebound, feel, spin on approach shots and durability depend to a large degree on synergy between the core and the cover. In numerous disclosures to date, efforts have been made to optimize the rebound and feel of the ball, and also the spin rate of the ball on approach shots, by closely specifying the cross-sectional hardness of the core. Such art is described in, for example, the following technical literature: JP-A 2011-136020 (and the corresponding published U.S. Patent Application No. 2011/0159999), JP-A 2011-136021 (and the corresponding published U.S. Patent Application No. 2011/0159998), JP-A 2007-152090 (and the corresponding U.S. Pat. No. 7,273,425), JP-A 2008-194473 (and the corresponding U.S. Pat. No. 7,481,722), and JP-A 2010-214105 (and the corresponding U.S. Pat. No. 7,909,710).

In addition, numerous disclosures have been made on art which, in rubber compositions for golf ball cores, specifies the hardness profile of the core from the standpoint of the rubber formulation. For example, JP-A 2006-312044 (and the corresponding published U.S. Pat. No. 7,278,929) discloses art in which powdered sulfur is added so as to increase the hardness difference between the center and surface of the core to at least a given value. In addition, technical documents which describe rubber formulations created in order to adjust the hardness profile of the core include, for example, JP-A 2006-167452 (and the corresponding U.S. Pat. No. 7,276,560), JP-A 2006-289074 (and the corresponding U.S. Pat. No. 7,381,776), JP-A 2002-000765 (and the corresponding U.S. Pat. No. 6,679,791), JP-A 2010-188199 (and the corresponding U.S. Pat. No. 6,679,791, which is the same as the preceding), JP-A 2007-167257, JP-A 2008-68077 (and the corresponding U.S. Pat. No. 7,335,115), and JP-A 2008-119461 (and the corresponding U.S. Pat. No. 7,300,362).

However, although a certain degree of improvement can be expected for conventional rubber formulations and core hardness profiles, even further increases in distance and improvements in durability are desired. Lately, research and development on golf balls has been especially intense and, in order to secure a competitive advantage with the ball, there has existed a desire to raise the level of the overall properties of the ball.

SUMMARY OF THE INVENTION

It is therefore an object of the invention to provide a golf ball which is capable of achieving satisfactory distances on shots with both drivers and middle irons used by professional golfers and skilled amateurs.

As a result of extensive investigations aimed at achieving the above object, the inventor has discovered that, in formulating a rubber composition for a golf ball core, by carrying out formulation such that the composition includes a polybutadiene-containing base rubber, an unsaturated carboxylic acid and/or a metal salt thereof, an organic peroxide and sulfur, and such that the value of [sulfur (mol)÷available active oxygen content in the organic peroxide] falls in a specific range, golf balls containing the core are capable of achieving satisfactory distances, both on shots with drivers and on shots with middle irons such as a number six iron (I#6).

Among recent golf balls in particular, three-piece solid golf balls and four-piece solid golf balls featuring a urethane cover are widely used by professional golfers and skilled amateurs. The present invention was achieved through repeated improvements aimed at, by optimization of the core formulation in the above ball, increasing not only the distance achieved on shots with drivers used by professionals and skilled amateurs, but also the distance achieved with middle irons such as a number six iron (I#6) used by such golfers.

Accordingly, the invention provides the following golf ball.

[1] A golf ball comprising a core and a cover of at least one layer, wherein the core is formed of a rubber composition which comprises a polybutadiene-containing base rubber, an unsaturated carboxylic acid and/or a metal salt thereof, an organic peroxide and sulfur, and for which the value of [sulfur (mol)÷available active oxygen content in the organic peroxide] is at least 0.01 and not more than 0.019.
[2] The golf ball of [1], wherein the core has a diameter of from 32 to 41 mm.
[3] The golf ball of [1], wherein the core is composed of a single layer.

BRIEF DESCRIPTION OF THE DIAGRAMS

FIG. 1 is a cross-sectional view showing a golf ball according to one embodiment of the invention.

FIG. 2 is a plan view showing the dimples used in the working examples of the invention and the comparative examples.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is described more fully below.

The golf ball of the invention has a construction which includes a core and a cover of at least one layer. As mentioned above, the core may be composed of a single layer or may be formed of a plurality of two or more layers, although it is preferable in this invention for the core to be composed of a single layer. Also, in this invention, the “cover” refers collectively to whatever layers are formed to the outside of the core, and is composed of at least one layer. That is, in cases where the cover is composed of a plurality of layers, in addition to the outermost layer of the cover, it includes also an intermediate layer interposed between the outermost layer and the core. Accordingly, the cover may be a two-layer cover composed of, in order from the inside: an intermediate layer and an outermost layer. In addition, an envelope layer may be provided between the core and the intermediate layer, in which case the cover may be a three-layer cover composed of, in order from the inside: an envelope layer, an intermediate layer and an outermost layer. A large number of dimples are generally formed on the outside surface of the outermost layer of the cover.

The core used in the invention is described. This core includes a polybutadiene-containing base rubber, an unsaturated carboxylic acid and/or a metal salt thereof, an organic peroxide, and sulfur.

The polybutadiene serving as the above rubber component must be one having a cis-1,4 bond content of at least 60% (here and below, “%” refers to percent by weight), preferably at least 80%, more preferably at least 90%, and most preferably at least 95%. If the cis-1,4 bond content is too low, the resilience will decrease. In addition, the polybutadiene has a 1,2-vinyl bond content of preferably not more than 2%, more preferably not more than 1.7%, and even more preferably not more than 1.5%.

The polybutadiene has a Mooney viscosity (ML1+4 (100° C.)) of preferably at least 30, and more preferably at least 35, with the upper limit being preferably not more than 100, and more preferably not more than 90.

The term “Mooney viscosity” used herein refers to an industrial indicator of viscosity (JIS K6300) as measured with a Mooney viscometer, which is a type of rotary plastometer. This value is represented by the unit symbol ML1+4 (100° C.), wherein “M” stands for Mooney viscosity, “L” stands for large rotor (L-type), and “1+4” stands for a pre-heating time of 1 minute and a rotor rotation time of 4 minutes. The “100° C.” indicates that measurement was carried out at a temperature of 100° C.

From the standpoint of obtaining a molded and vulcanized rubber composition having a good resilience, the polybutadiene is preferably one synthesized with a rare-earth catalyst or a group VIII metal compound catalyst.

Such rare-earth catalysts are not subject to any particular limitation, although preferred use may be made of a lanthanum series rare-earth compound. Also, where necessary, an organoaluminum compound, an alumoxane, a halogen-bearing compound and a Lewis base may be used in combination with a lanthanum-series rare-earth compound. Preferred use may be made of, as the various foregoing compounds, those mentioned in JP-A 11-35633, JP-A 11-164912 and JP-A 2002-293996.

Of the above rare-earth catalysts, the use of a catalyst which employs any of the lanthanum series rare-earth elements neodymium, samarium and gadolinium is preferred, with the use of a neodymium catalyst being especially recommended. In such cases, a polybutadiene rubber having a high 1,4-cis bond content and a low 1,2-vinyl bond content can be obtained at an excellent polymerization activity.

The polybutadiene has a molecular weight distribution Mw/Mn (where “Mw” stands for weight-average molecular weight, and “Mn” stands for number-average molecular weight) of preferably at least 1.0, and more preferably at least 1.3. The upper limit is preferably not more than 6.0, and more preferably not more than 5.0. If Mw/Mn is too small, the workability may decrease, whereas if it is too large, the resilience may decline.

The above polybutadiene is used as the base rubber, in which case the proportion of the polybutadiene within the overall rubber is preferably at least 40 wt %, more preferably at least 60 wt %, even more preferably at least 80 wt %, and most preferably at least 90 wt %. The above polybutadiene may account for 100 wt %, preferably 98 wt % or less, and even more preferably 95 wt % or less, of the base rubber.

Examples of cis-1,4-polybutadiene rubber that may be used include the high-cis products BR01, BR11, BR02, BR02L, BR02LL, BR730 and BR51 available from JSR Corporation.

Rubber components other than the above-described polybutadiene may also be included in the base rubber, insofar as the objects of the invention can be achieved. Illustrative examples of such other rubber components include polybutadienes other than the above polybutadiene, and other diene rubbers, such as styrene-butadiene rubbers, natural rubbers, isoprene rubbers and ethylene-propylene-diene rubbers.

The unsaturated carboxylic acid and/or metal salt thereof functions primarily as a co-crosslinking agent for the above-described base rubber. Examples of suitable unsaturated carboxylic acids include acrylic acid, methacrylic acid, maleic acid and fumaric acid. The use of acrylic acid or methacrylic acid is especially preferred. The metal salts of unsaturated carboxylic acids are exemplified by the above unsaturated carboxylic acids which have been neutralized with a desired metal ion. Illustrative examples include the zinc salts and magnesium salts of methacrylic acid and acrylic acid. The use of zinc acrylate is especially preferred. The content of these unsaturated carboxylic acids and/or metal salts thereof per 100 parts by weight of the base rubber is preferably at least 10 parts by weight, more preferably at least 15 parts by weight, and even more preferably at least 20 parts by weight. The upper limit is preferably not more than 45 parts by weight, more preferably not more than 43 parts by weight, and even more preferably not more than 41 parts by weight.

A known organic peroxide may be used as the organic peroxide. Illustrative examples include dicumyl peroxide, 1,1-di(t-butylperoxy)cyclohexane, t-butylperoxy laurate, dibenzoyl peroxide, dilauroyl peroxide and 1,1-bis(t-butylperoxy)-3,3,5-trimethylcyclohexane. These may be used singly or two or more may be used in combination. Commercial products may be used as these organic peroxides. Illustrative examples of such commercial products include those available under the trade names “Percumyl D,” “Perhexa C-40,” “Perbutyl L” (all from NOF Corporation), the trade names “Niper BW” and “Peroyl L” (both from NOF Corporation), and the trade name “Trigonox 29” (from Kayaku Akzo Corporation).

The organic peroxide is included in an amount, per 100 parts by weight of the base rubber, of preferably at least 0.1 part by weight, more preferably at least 0.2 part by weight, and even more preferably at least 0.3 part by weight. The upper limit is preferably not more than 5.0 parts by weight, more preferably not more than 4.0 parts by weight, even more preferably not more than 3.0 parts by weight, and most preferably not more than 2.0 parts by weight. Including too much may make the core too hard, resulting in an unpleasant feel at impact, and may markedly lower the durability to cracking. On the other hand, if the amount included is too small, the core may become too soft, resulting in an unpleasant feel at impact and markedly lowering productivity.

As with the above organic peroxide, sulfur is also included as an essential ingredient in the rubber composition. The sulfur is exemplified by the product available from Tsurumi Chemical Industry Co., Ltd. under the trade name “Sulfax-5.” The amount of sulfur included can be set to more than 0, and may be set to preferably at least 0.005 part by weight, and more preferably at least 0.01 part by weight, per 100 parts by weight of the base rubber. The upper limit in the amount of sulfur, although not subject to any particular limitation, may be set to preferably not more than 0.5 part by weight, more preferably not more than 0.4 part by weight, and even more preferably not more than 0.1 part by weight. By adding sulfur, hardness differences in the core can be increased. However, adding too much sulfur may result in undesirable effects during hot molding, such as explosion of the rubber composition, or may considerably lower the rebound.

In this invention, when using both an organic peroxide and sulfur in the above rubber composition, the value of [sulfur (mol)÷available active oxygen content in the organic peroxide] is adjusted so as to be at least 0.01 and not more than 0.019. As used herein, the “active oxygen content” is a numerical value indicating the quantity of free radicals generated from the organic peroxide. For example, as shown by the formula below, the stoichiometric amount of active oxygen in an organic peroxide at 100% concentration is represented for each individual organic peroxide as the atomic weight of the active oxygens divided by the molecular weight of the organic peroxide, expressed as a percentage.

As used herein, the “available active oxygen content” refers to the active oxygen content (%) within the amount of organic peroxide (number of moles) included in the rubber composition, and is expressed as a molar quantity. In this invention, by adjusting not the amount of organic peroxide itself, but rather the quantitative balance between the amount of free radicals generated from the organic peroxide and the sulfur, owing to the synergistic effects of these compounds, a core having the desired physical properties was discovered. Moreover, by using this core, a golf ball can be obtained which achieves satisfactory distances on shots with both drivers and middle irons (e.g., I#6) used by professional golfers and skilled amateurs. In the present invention, the value of [sulfur (mol)÷available active oxygen content in the organic peroxide] is set to at least 0.01 and not more than 0.019.

The above-described rubber composition contains the foregoing essential ingredients of the invention, although fillers may also be included therein as additional ingredients. Fillers that may be preferably used include zinc oxide, barium sulfate and calcium carbonate. These may be used singly or two or more may be used in combination. The amount of filler included per 100 parts by weight of the base rubber may be set to preferably at least 1 part by weight, and more preferably at least 3 parts by weight. The upper limit in the amount included per 100 parts by weight of the base rubber may be set to preferably not more than 200 parts by weight, more preferably not more than 150 parts by weight, and even more preferably not more than 100 parts by weight. At a filler content which is too high or too low, a proper weight and a suitable rebound may be impossible to obtain.

In the practice of the invention, an antioxidant may be included as an optional ingredient in the rubber composition. For example, use may be made of a commercial product such as Nocrac NS-6, Nocrac NS-30 or Nocrac 200 (all products of Ouchi Shinko Chemical Industry Co., Ltd.). These may be used singly, or two or more may be used in combination.

The amount of antioxidant included per 100 parts by weight of the base rubber, although not subject to any particular limitation, is preferably at least 0.05 part by weight, and more preferably at least 0.1 part by weight. The upper limit is preferably not more than 1.0 part by weight, more preferably not more than 0.7 part by weight, and even more preferably not more than 0.4 part by weight. If the antioxidant content is too high or too low, a suitable core hardness gradient may not be obtained, as a result of which it may not be possible to obtain a good rebound, durability, and spin rate-lowering effect on full shots.

In addition, an organosulfur compound may be included in the rubber composition so as to impart an excellent rebound. Thiophenols, thionaphthols, halogenated thiophenols, and metal salts thereof are recommended for this purpose. Illustrative examples include pentachlorothiophenol, pentafluorothiophenol, pentabromothiophenol, p-chlorothiophenol, and the zinc salt of pentachlorothiophenol; and diphenylpolysulfides, dibenzylpolysulfides, dibenzoylpolysulfides, dibenzothiazoylpolysulfides and dithiobenzoylpolysulfides having 2 to 4 sulfurs. The use of diphenyldisulfide or the zinc salt of pentachlorothiophenol is especially preferred.

The amount of the organosulfur compound included per 100 parts by weight of the base rubber is at least 0.05 part by weight, preferably at least 0.07 part by weight, and more preferably at least 0.1 part by weight. The upper limit is not more than 5 parts by weight, preferably not more than 4 parts by weight, more preferably not more than 3 parts by weight, and most preferably not more than 2 parts by weight. Including too much organosulfur compound may excessively lower the hardness, whereas including too little is unlikely to improve the rebound.

The core can be produced by vulcanizing and curing the rubber composition containing the various above ingredients. For example, production may be carried out by using a mixing apparatus such as a Banbury mixer or a roll mill to mix the ingredients, carrying out compression molding or injection molding using a core-forming mold, then suitably heating, and thereby curing, the molded body at a temperature sufficient for the organic peroxide and the co-crosslinking agent to act, such as from about 100° C. to about 200° C. for a period of 10 to 40 minutes.

The core diameter, although not subject to any particular limitation, is preferably at least 32 mm, and more preferably at least 33 mm. The upper limit is preferably not more than 41 mm, and more preferably not more than 40 mm. At a core diameter outside of this range, the ball's durability to cracking may dramatically decline, or the initial velocity of the ball may decrease.

It is essential for the above core to have a cross-sectional hardness which, letting D (mm) be a radius of the core, O be a JIS-C hardness at a center of the core, Q be a JIS-C hardness at a position 55% of D from the core center, and T be a JIS-C hardness at a position 85% of D from the core center, satisfies the formulas (1) and (2) below:

Q-O≦5 (1)

T-Q≧10. (2)

By adjusting the cross-sectional hardness of the core so as to satisfy formulas (1) and (2), that is, conceptually, by finishing the core to a hardness profile in which the cross-sectional hardness from the core center to a position at a given distance therefrom is relatively soft and free of large fluctuations in hardness and in which the subsequent cross-sectional hardness up to the core surface rises at a steep gradient, excessive deformation of the core on full shots with a driver or with a middle iron is suppressed, core deformation is optimized, and a loss of initial velocity and an increase in the spin rate can be suppressed. As a result, satisfactory distances can be obtained on shots with drivers and on shots with middle irons such as a I#6 used by professional golfers and skilled amateurs, in addition to which the durability to cracking on repeated impact can be improved.

Also, in above formula (1), if the Q-O value is too large, a sufficient spin rate-lowering effect may not be obtained, as a result of which the desired distance may not be achieved. The Q-O value has a lower limit of preferably at least 0.

Moreover, in above formula (2), if the T-Q value is too small, a sufficient spin rate-lowering effect may not be obtained, as a result of which the intended distance may not be achieved. The T-Q value has a lower limit of preferably at least 11, and more preferably at least 12, and an upper limit of preferably not more than 20, and more preferably not more than 18.

The U-O value, which is the JIS-C hardness difference between the surface of the core and the center of the core, has a lower limit of preferably at least 10, more preferably at least 12, and even more preferably at least 14, and an upper limit of preferably not more than 45, more preferably not more than 40, and even more preferably not more than 35. If the above value is too large, a good initial velocity may not be obtained and the durability may worsen. On the other hand, if the above value is too small, the spin rate may rise excessively, resulting in a poor distance, and the feel at impact may harden. The JIS-C hardness at the core center, although not subject to any particular limitation, has a minimum value of preferably at least 50, more preferably at least 52, and even more preferably at least 54, and a maximum value of preferably not more than 70, more preferably not more than 68, and even more preferably not more than 66. The JIS-C hardness at the core surface, although not subject to any particular limitation, has a minimum value of preferably at least 75, more preferably at least 77, and even more preferably at least 79, and a maximum value of preferably not more than 100, more preferably not more than 98, and even more preferably not more than 96.

Moreover, the U-Q value, which is the JIS-C hardness difference between the surface of the core and a position 55% of D from the center of the core, has a lower limit of preferably at least 10, more preferably at least 12, and even more preferably at least 14, and an upper limit of preferably not more than 30, more preferably not more than 28, and even more preferably not more than 25. If the above value is too large, a good initial velocity may not be obtained and the durability may worsen. On the other hand, if the above value is too small, the spin rate may rise excessively, as a result of which a good distance may not be achieved, and the feel at impact may harden.

In the cover used in this invention, the material making up the outermost layer, although not subject to any particular limitation, is exemplified by ionomers and polyurethanes.

From the standpoint of controllability and scuff resistance, it is preferable to use a polyurethane as the outermost layer material. The use of a thermoplastic polyurethane elastomer in particular is preferred from the standpoint of amenability to mass production.

In cases where the outermost layer material is a thermoplastic polyurethane elastomer, it is preferable to use one type of resin pellet composed of a resin blend in which the main components are (A) a thermoplastic polyurethane and (B) a polyisocyanate compound and, when the resin pellets are charged into an injection molding machine just prior to injection molding, it is preferable for at least some isocyanate compound to be present in which all the isocyanate groups on the molecule remain in an unreacted state. Golf balls composed of such thermoplastic polyurethane elastomers have an excellent rebound, spin performance and scuff resistance.

To fully and effectively achieve the objects of the invention, a necessary and sufficient amount of unreacted isocyanate groups should be present within the outermost layer-forming resin material. Specifically, it is recommended that the total weight of components A and B combined be preferably at least 60%, and more preferably at least 70%, of the overall weight of the outermost layer. Above components A and B are described in detail below.

In describing the thermoplastic polyurethane (A), the structure of this thermoplastic polyurethane includes soft segments composed of a polymeric polyol that is a long-chain polyol (polymeric glycol), and hard segments composed of a chain extender and a polyisocyanate compound. Here, the long-chain polyol serving as a starting material is not subject to any particular limitation, and may be any that is used in the prior art relating to thermoplastic polyurethanes. Exemplary long-chain polyols include polyester polyols, polyether polyols, polycarbonate polyols, polyester polycarbonate polyols, polyolefin polyols, conjugated diene polymer-based polyols, castor oil-based polyols, silicone-based polyols and vinyl polymer-based polyols. These long-chain polyols may be used singly or as combinations of two or more thereof. Of the long-chain polyols mentioned here, polyether polyols are preferred because they enable the synthesis of thermoplastic polyurethanes having a high rebound resilience and excellent low-temperature properties.

Illustrative examples of the above polyether polyol include poly(ethylene glycol), poly(propylene glycol), poly(tetramethylene glycol) and poly(methyltetramethylene glycol) obtained by the ring-opening polymerization of cyclic ethers. The polyether polyol may be used singly or as a combination of two or more thereof. Of the above, poly(tetramethylene glycol) and/or poly(methyltetramethylene glycol) are preferred.

It is preferable for these long-chain polyols to have a number-average molecular weight in the range of 1,500 to 5,000. By using a long-chain polyol having such a number-average molecular weight, golf balls made with a thermoplastic polyurethane composition having excellent properties such as resilience and manufacturability can be reliably obtained. The number-average molecular weight of the long-chain polyol is more preferably in the range of 1,700 to 4,000, and even more preferably in the range of 1,900 to 3,000.

The number-average molecular weight of the long-chain polyol refers here to the number-average molecular weight computed based on the hydroxyl number measured in accordance with JIS K-1557.

Chain extenders that may be suitably used include those employed in the prior art relating to thermoplastic polyurethanes. For example, low-molecular-weight compounds which have a molecular weight of 400 or less and bear on the molecule two or more active hydrogen atoms capable of reacting with isocyanate groups are preferred. Examples of the chain extender include, but are not limited to, 1,4-butylene glycol, 1,2-ethylene glycol, 1,3-butanediol, 1,6-hexanediol and 2,2-dimethyl-1,3-propanediol. Of these chain extenders, aliphatic diols having 2 to 12 carbons are preferred, and 1,4-butylene glycol is more preferred.

The polyisocyanate compound is not subject to any particular limitation; preferred use may be made of one that is used in the prior art relating to thermoplastic polyurethanes. Specific examples include one or more selected from the group consisting of 4,4′-diphenylmethane diisocyanate, 2,4-toluene diisocyanate, 2,6-toluene diisocyanate, p-phenylene diisocyanate, xylylene diisocyanate, naphthylene-1,5-diisocyanate, tetramethylxylene diisocyanate, hydrogenated xylylene diisocyanate, dicyclohexylmethane diisocyanate, tetramethylene diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate, norbornene diisocyanate, trimethylhexamethylene diisocyanate and dimer acid diisocyanate. Depending on the type of isocyanate used, the crosslinking reaction during injection molding may be difficult to control. In the practice of the invention, to provide a balance between stability at the time of production and the properties that are manifested, it is most preferable to use 4,4′-diphenylmethane diisocyanate, which is an aromatic diisocyanate.

It is most preferable for the thermoplastic polyurethane serving as above component A to be a thermoplastic polyurethane synthesized using a polyether polyol as the long-chain polyol, using an aliphatic diol as the chain extender, and using an aromatic diisocyanate as the polyisocyanate compound. It is desirable, though not essential, for the polyether polyol to be a polytetramethylene glycol having a number-average molecular weight of at least 1,900, for the chain extender to be 1,4-butylene glycol, and for the aromatic diisocyanate to be 4,4′-diphenylmethane diisocyanate.

The mixing ratio of active hydrogen atoms to isocyanate groups in the above polyurethane-forming reaction may be adjusted within a desirable range so as to make it possible to obtain a golf ball which is composed of a thermoplastic polyurethane composition and has various improved properties, such as rebound, spin performance, scuff resistance and manufacturability. Specifically, in preparing a thermoplastic polyurethane by reacting the above long-chain polyol, polyisocyanate compound and chain extender, it is desirable to use the respective components in proportions such that the amount of isocyanate groups on the polyisocyanate compound per mole of active hydrogen atoms on the long-chain polyol and the chain extender is from 0.95 to 1.05 moles.

No particular limitation is imposed on the method of preparing the thermoplastic polyurethane used as component A. Production may be carried out by either a prepolymer process or a one-shot process which uses a long-chain polyol, a chain extender and a polyisocyanate compound and employs a known urethane-forming reaction. Of these, a process in which melt polymerization is carried out in a substantially solvent-free state is preferred. Production by continuous melt polymerization using a multiple screw extruder is especially preferred.

It is also possible to use a commercially available product as the thermoplastic polyurethane serving as component A. Illustrative examples include Pandex T8295, Pandex T8290, Pandex T8283 and Pandex T8260 (all available from DIC Bayer Polymer, Ltd.).

Next, various types of isocyanates may be employed without particular limitation as the polyisocyanate compound serving as component B. Illustrative examples include one or more selected from the group consisting of 4,4′-diphenylmethane diisocyanate, 2,4-toluene diisocyanate, 2,6-toluene diisocyanate, p-phenylene diisocyanate, xylylene diisocyanate, naphthylene-1,5-diisocyanate, tetramethylxylene diisocyanate, hydrogenated xylylene diisocyanate, dicyclohexylmethane diisocyanate, tetramethylene diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate, norbornene diisocyanate, trimethylhexamethylene diisocyanate and dimer acid diisocyanate. Of the above group of isocyanates, the use of 4,4′-diphenylmethane diisocyanate, dicyclohexylmethane diisocyanate and isophorone diisocyanate is preferable in terms of the balance between the influence on processability of, e.g., the rise in viscosity accompanying the reaction with the thermoplastic polyurethane serving as component A and the physical properties of the outermost layer material of the resulting golf ball.

A thermoplastic elastomer (component C) other than the above-described thermoplastic polyurethane may be included as an optional component together with components A and B. By including this component C in the above resin blend, the flow properties of the resin blend can be further increased and improvements can be made in various properties required of the outermost layer material of a golf ball, such as resilience and scuff resistance.

The thermoplastic elastomer other than the above thermoplastic polyurethane which is used as component C may be of one, two or more types selected from among polyester elastomers, polyamide elastomers, ionomer resins, styrene block elastomers, hydrogenated styrene-butadiene rubbers, styrene-ethylene/butylene-ethylene block copolymers and modified forms thereof, ethylene-ethylene/butylene-ethylene block copolymers and modified forms thereof, styrene-ethylene/butylene-styrene block copolymers and modified forms thereof, ABS resins, polyacetals, polyethylenes and nylon resins. In particular, because they increase the resilience and scuff resistance due to reaction with the isocyanate groups while at the same time maintaining a good productivity, the use of polyester elastomers, polyamide elastomers and polyacetals is especially preferred.

The above components A, B and C have a compositional ratio, expressed as a weight ratio, which, although not subject to any particular limitation, is preferably A:B:C=100:2 to 50:0 to 50, and more preferably A:B:C=100:2 to 30:8 to 50.

In the present invention, the resin blend is prepared by mixing together component A, component B and, additionally, component C. At this time, it is essential to select conditions such that, of the polyisocyanate compound, there exists at least some portion in which all the isocyanate groups remain in an unreacted state. For example, a treatment such as mixture in an inert gas such as nitrogen or in a vacuum state must be provided. The resin blend is then injection-molded around a core that has been placed in a mold. For easy and trouble-free handling, it is preferable to form the resin blend into pellets having a length of 1 to 10 mm and a diameter of 0.5 to 5 mm. Isocyanate groups in an unreacted state remain within these resin pellets; while the resin blend is being injection-molded about the core, or due to post-treatment such as annealing thereafter, the unreacted isocyanate groups react with component A and component C to form a crosslinked material.

The outermost layer may be molded by a method which involves, for example, feeding the above-described resin blend to an injection-molding machine, and injecting the molten resin blend over the core. In this case, the molding temperature varies depending on the type of thermoplastic polyurethane, but is preferably in the range of 150 to 250° C.

When injection molding is carried out, it is desirable though not essential to carry out molding in a low-humidity environment such as by purging with an inert gas (e.g., nitrogen) or a low-temperature gas (e.g., low dew-point dry air), or vacuum treating, some or all places on the resin paths from the resin feed area to the mold interior. Preferred, non-limiting, examples of the medium used for transporting the resin under applied pressure include low-humidity gases such as low dew-point dry air or nitrogen. By carrying out molding in such a low-humidity environment, reaction by the isocyanate groups is kept from proceeding before the resin has been charged into the mold interior. As a result, polyisocyanate in which the isocyanate groups are to some degree in an unreacted state is included in the molded resin material, thus making it possible to reduce variable factors such as an unwanted rise in viscosity and enabling the real crosslinking efficiency to be enhanced.

Techniques that may be used to confirm the presence of polyisocyanate compound in an unreacted state within the resin blend prior to injection molding about the core include those which involve extraction with a suitable solvent that selectively dissolves out only the polyisocyanate compound. An example of a simple and convenient method is one in which confirmation is carried out by simultaneous thermogravimetric and differential thermal analysis (TG-DTA) measurement in an inert atmosphere. For example, when the resin blend (outermost layer material) which may be used in this invention is heated in a nitrogen atmosphere at a temperature ramp-up rate of 10° C./min, a gradual drop in the weight of diphenylmethane diisocyanate can be observed from about 150° C. On the other hand, in a resin sample in which the reaction between the thermoplastic polyurethane material and the isocyanate mixture has been carried out to completion, a weight drop is not observed from about 150° C., but a weight drop can be confirmed from about 230 to 240° C.

After the resin blend has been molded as described above, the properties as a golf ball outermost layer can be additionally improved by carrying out annealing so as to induce the crosslinking reaction to proceed further. “Annealing,” as used herein, refers to aging the cover in a fixed environment for a fixed length of time.

In addition to the above-described resin components, various additives may be optionally included in the outermost layer material in the invention. Examples of such additives include pigments, dispersants, antioxidants, ultraviolet absorbers, ultraviolet stabilizers, parting agents, plasticizers, and inorganic fillers (e.g., zinc oxide, barium sulfate, titanium dioxide, tungsten).

Next, the thickness of the outermost layer in this invention, although not particularly limited, is preferably at least 0.1 mm, more preferably at least 0.3 mm, and even more preferably at least 0.5 mm. The maximum thickness is preferably not more than 1.4 mm, more preferably not more than 1.2 mm, and even more preferably not more than 1.0 mm. If the outermost layer is thicker than the above range, the rebound on W#1 shots may be inadequate or the spin rate may increase, possibly resulting in a poor distance. If the outermost layer is thinner than the above range, the scuff resistance may worsen, or the controllability even by professional golfers and skilled amateurs may be inadequate.

The material hardness of the outermost layer, expressed as the Shore D hardness, although not particularly limited, is preferably at least 34, more preferably at least 37, and even more preferably at least 40. The maximum value is preferably not more than 66, more preferably not more than 63, and even more preferably not more than 60. At a low Shore D hardness, the ball may be too receptive to spin on full shots, possibly resulting in a poor distance. At a Shore D hardness which is too high, the ball may not be receptive to spin on approach shots, which may result in a poor controllability even by professional golfers and skilled amateurs. It should be noted here that the material hardness of the outermost layer refers to the hardness when the material has been molded into a sheet of a given thickness. Below, the material hardnesses of the intermediate layer and the envelope layer are defined in the same way.

In the golf ball of the invention, numerous dimples are provided on the surface of the outermost layer for the sake of aerodynamic performance. The number of dimples formed on the outermost layer surface is not subject to any particular limitation. However, to enhance the aerodynamic performance of the ball and increase the distance traveled by the ball, the number of dimples is preferably at least 250, more preferably at least 270, even more preferably at least 290, and most preferably at least 300. The maximum number of dimples is preferably not more than 400, more preferably not more than 380, and even more preferably not more than 360.

In the practice of the invention, by further increasing the number of layers in the ball structure, it is possible to improve the ball performance to a level desired in particular by professional golfers and skilled amateurs. For example, an intermediate layer may be interposed between the above-described core and the above-described outermost layer, although the invention is not limited to this construction.

In the above case, the material hardness of the intermediate layer, expressed as the Shore D hardness, although not particularly limited, is preferably at least 50, more preferably at least 55, and even more preferably at least 60. The upper limit is preferably not more than 70, more preferably not more than 66, and even more preferably not more than 63. If the material hardness of the intermediate layer is too low, the ball as a whole may be too receptive to spin on full shots, as a result of which a good distance may not be achieved. On the other hand, if the material hardness of the intermediate layer is too high, the durability to cracking when repeatedly struck may worsen or the feel at impact on shots with a putter or on short approach shots may be too hard.

From the standpoint of lowering the spin rate both on shots with a driver and on shots with a middle iron, it is preferable for the JIS-C hardness at the surface of a sphere composed of the core covered by the intermediate layer to be at least 90.

The thickness of the intermediate layer, although not particularly limited, is preferably at least 0.5 mm, more preferably at least 0.7 mm, and even more preferably at least 0.9 mm. The upper limit is preferably not more than 2.0 mm, and more preferably not more than 1.7 mm. If the thickness of the intermediate layer is larger than the above range, the spin rate-lowering effect on shots with a W#1 may be inadequate, as a result of which a good distance may not be obtained. If the intermediate layer is too thin, the ball may have a poor durability to cracking when repeatedly struck and a poor durability at low temperatures.

The intermediate layer material is not subject to any particular limitation. For example, advantageous use may be made of known ionomer resins, thermoplastic elastomers and thermoset elastomers. Illustrative examples of thermoplastic elastomers include various types of thermoplastic elastomers, such as polyester elastomers, polyamide elastomers, polyurethane elastomers, olefin elastomers and styrene elastomers. It is especially preferable to use an ionomer resin as the base resin for the intermediate layer material. In this case, it is desirable that formulation of the ionomer resin composition involve using a mixture of a zinc ion (Zn2+)-neutralized ionomer resin and a sodium ion (Na+)-neutralized ionomer resin. The mixing ratio therebetween, or zinc ion (Zn2+)-neutralized ionomer resin (I)/sodium ion (Na+)-neutralized ionomer resin (II), expressed in terms of weight percent, is preferably from 25/75 to 75/25, more preferably from 35/65 to 65/35, and even more preferably from 45/55 to 55/45. If the (I)/(II) resin ratio does not satisfy the above range, there is a possibility that the rebound of the overall ball will become smaller, which may make it impossible to obtain the desired flight performance. Moreover, the durability to cracking when repeatedly struck at ordinary temperatures may worsen, and the durability to cracking at low temperatures (sub-zero Celsius) may also worsen.

It is preferable to subject the surface of the intermediate layer to abrasion treatment so as to increase adhesion with the outermost layer located on the outside thereof. In addition, following such abrasion treatment, a primer may be applied to the surface. It is also possible to increase adhesion by adding an adhesion reinforcing agent to the intermediate layer material.

In the practice of the invention, in addition to the above intermediate layer, an envelope layer may be provided between the core and the intermediate layer. In such a case, there is obtained a multi-piece solid golf ball G having a four-layer construction which, as shown in FIG. 1, is composed of, in order from the inside: a core 1, an envelope layer 2, an intermediate layer 3, and an outermost layer 4 having numerous dimples D on the surface thereof.

In the above case, the envelope layer has a material hardness, expressed as the Shore D hardness, which is not particularly limited, but is preferably at least 40, more preferably at least 42, and even more preferably at least 44. The upper limit is preferably not more than 61, more preferably not more than 59, and even more preferably not more than 57. If the material hardness of the envelope layer is too low, the overall ball may be too receptive to spin on full shots, as a result of which a good distance may not be achieved. On the other hand, if the material hardness of the envelope layer is too high, the durability to cracking when repeatedly struck may worsen, or the ball may have a hard feel at impact.

The thickness of the envelope layer, although not particularly limited, is preferably at least 1.0 mm, more preferably at least 1.2 mm, and even more preferably at least 1.4 mm. The upper limit is preferably not more than 4.0 mm, more preferably not more than 3.0 mm, and even more preferably not more than 2.0 mm. At an envelope layer thickness greater than the above range, the initial velocity of the ball may be inadequate even when struck with a driver, as a result of which the desired distance may not be achieved. On the other hand, if the envelope layer is too thin, the spin rate-lowering effect may be inadequate, as a result of which the desired distance may not be achieved.

Although no particular limitation is imposed on the envelope layer material, preferred use may be made of, for example, a known ionomer resin, a thermoplastic elastomer, or a thermoset elastomer. Illustrative examples of thermoplastic elastomers include various types of thermoplastic elastomers, such as polyester elastomers, polyamide elastomers, polyurethane elastomers, olefin elastomers and styrene elastomers.

It is especially preferable to use, as the envelope layer material, a mixture obtained by compounding (f) a base resin of (a) an olefin-unsaturated carboxylic acid random copolymer and/or a metal ion neutralization product of an olefin-unsaturated carboxylic acid random copolymer blended with (b) an olefin-unsaturated carboxylic acid-unsaturated carboxylic acid ester random terpolymer and/or a metal ion neutralization product of an olefin-unsaturated carboxylic acid-unsaturated carboxylic acid ester random terpolymer in a weight ratio of from 100:0 to 0:100, (e) a non-ionomeric thermoplastic elastomer, (c) from 5 to 80 parts by weight of a fatty acid and/or fatty acid derivative having a molecular weight of from 228 to 1500, and (d) from 0.1 to 17 parts by weight of a basic metal compound capable of neutralizing un-neutralized acid groups in the above base resin and component (c). In this case, it is preferable for the weight ratio of the base resin (f) to the non-ionomeric thermoplastic elastomer (e) to be adjusted within the range of 100:0 to 100:100, and for a mixture of component (f), component (c) and component (d) to be prepared, and it is also preferable to use all of above components (c), (d), (e) and (f). In this way, the ball rebound and flight performance can be further improved.

In this invention, commercially available products may be used as the base resins of components (a) and (b). Examples of commercial products which may be used as the random copolymer in component (a) include Nucrel 1560, Nucrel 1214 and Nucrel 1035 (all products of DuPont-Mitsui Polychemicals Co., Ltd.), and Escor 5200, Escor 5100 and Escor 5000 (all products of ExxonMobil Chemical). Examples of commercial products which may be used as the random copolymer in component (b) include Nucrel AN4311, Nucrel AN4318 (both products of DuPont-Mitsui Polychemicals Co., Ltd.), and Escor ATX325, Escor ATX320 and Escor ATX310 (all products of ExxonMobil Chemical).

Above component (c) is a fatty acid and/or fatty acid derivative having a molecular weight of at least 228 but not more than 1500. This component has a very small molecular weight compared with the base resin. It suitably adjusts the melt viscosity of the mixture, and thus helps in particular to improve the flow properties. Component (c) of this invention includes a relatively high content of acid groups (or derivatives thereof), and is able to suppress an excessive loss of resilience. Illustrative examples of the fatty acid of component (c) include myristic acid, palmitic acid, stearic acid, 12-hydroxystearic acid, behenic acid, oleic acid, linoleic acid, linolenic acid, arachidic acid and lignoceric acid. Of these, stearic acid, arachidic acid, behenic acid and lignoceric acid are preferred. Behenic acid is especially preferred.

Preferred use may be made of a basic inorganic metal compound as the basic metal compound of component (d). Illustrative examples of the metal ion therein include Li+, Na+, K+, Ca++, Mg++, Zn++, Al+++, Ni++, Fe++, Fe+++, Cu++, Mn++, Sn++, Pb++ and Co++. Known basic inorganic fillers containing these metal ions may be used as the basic inorganic metal compound. Specific examples include magnesium oxide, magnesium hydroxide, magnesium carbonate, zinc oxide, sodium hydroxide, sodium carbonate, calcium oxide, calcium hydroxide, lithium hydroxide and lithium carbonate. In particular, a hydroxide or a monoxide is recommended. Calcium hydroxide and magnesium oxide, each of which has a high reactivity with the base resin, are more preferred. Calcium hydroxide is especially preferred.

Illustrative examples of component (e) include olefin elastomers, styrene elastomers, polyester elastomers, urethane elastomers and polyamide elastomers. From the standpoint of further increasing rebound, the use of an olefin elastomer or a polyester elastomer is especially preferred. A commercially available product may be used as component (e). Examples include olefin elastomers such as Dynaron (JSR Corporation), and polyester elastomers such as Hytrel (DuPont-Toray Co., Ltd.).

Various additives such as pigments, dispersants, antioxidants, ultraviolet absorbers and light stabilizers may be optionally included in the thermoplastic resin. Specific examples of such additives include inorganic fillers such as zinc oxide, barium sulfate and titanium dioxide.

The above material may be obtained by mixing the various above-described components under applied heat. For example, the material may be obtained by using a known mixing apparatus such as a kneading-type twin-screw extruder, a Banbury mixer or a kneader to knead the ingredients at a heating temperature of from 150 to 250° C. Alternatively, direct use may be made of a commercial product, specific examples of which include those having the trade names HPF 1000, HPF 2000 and HPF AD1027, as well as the experimental material HPF SEP1264-3, all produced by E.I. DuPont de Nemours & Co.

The method of manufacturing multi-piece solid golf balls in which the above-described core, envelope layer, intermediate layer and outermost layer are each formed as successive layers is not subject to any particular limitation. Production may be carried out by an ordinary method such as a known injection molding process. By way of illustration, first a core is placed within a given injection mold, following which the envelope layer material is injection-molded over the core to form a first intermediate sphere, which sphere is then placed in another injection mold and the intermediate layer material is injection-molded over the sphere to form a second intermediate sphere. Next, this second intermediate sphere is placed in yet another injection mold and the outermost layer material is injection-molded over the second intermediate sphere, concurrent with which dimples are molded in the outermost layer surface, thereby giving a multi-piece golf ball. Alternatively, instead of the above method in which the materials for the respective layers are injection-molded, use may made of a method in which each of the respective intermediate spheres is enclosed by two half-cups that have been molded beforehand into hemispherical shapes, and the resulting assembly is molded under applied heat and pressure.

The golf ball of the invention has a diameter of not less than 42 mm, preferably not less than 42.3 mm, and more preferably not less than 42.6. The upper limit in the diameter is not more than 44 mm, preferably not more than 43.8 mm, more preferably not more than 43.5 mm, and even more preferably not more than 43 mm.

The weight of the golf ball is preferably not less than 44.5 g, more preferably not less than 44.7 g, even more preferably not less than 45.1 g, and most preferably not less than 45.2 g. The upper limit in the weight is not more than 47.0 g, more preferably not more than 46.5 g, and even more preferably not more than 46.0 g.

As explained above, the golf ball of this invention is capable of achieving satisfactory distances on shots with both drivers and middle irons (e.g., I#6) used by professional golfers and skilled amateurs.

EXAMPLES

Examples of the invention and Comparative Examples are given below by way of illustration, and not by way of limitation.

Examples 1 to 3, Comparative Examples 1 to 3

Golf ball cores were produced by using the rubber formulations in the respective examples of the invention and comparative examples as shown in Table 1 below to prepare core compositions, then molding and vulcanizing the core compositions at a vulcanization temperature of 155° C. and for a vulcanization time of 25 minutes.

TABLE 1

Example

Comparative Example

1

2

3

1

2

3

Polybutadiene

100

100

100

100

100

100

Zinc oxide

5

5

5

5

5

5

Barium sulfate

15

15

15

15

15

15

Antioxidant

0.1

0.1

0.1

0.1

0.1

0.1

Zinc stearate

5

5

5

5

5

5

Zinc salt of

1

1

1

1

1

1

pentachlorothiophenol

Zinc acrylate

30

30

30

30

30

30

Sulfur

0.085

0.08

0.06

0.12

0.1

Peroxide (1)

1.05

0.75

1.05

3

0.3

Peroxide (2)

3

0.3

Molar quantity

Sulfur

0.0003

0.0003

0.0002

0.0004

0.0004

(mol)

Peroxide (1)

0.004

0.003

0.004

0.011

0.001

Peroxide (2)

0.005

0.0005

Available active

Peroxide (1)

0.023

0.016

0.023

0.064

0.006

oxygen content

Peroxide (2)

0.023

0.002

Sulfur (mol) + Available

0.014

0.018

0.010

0.020

0.006

—

active oxygen content

Numbers of ingredient in the table indicate parts by weight.

Details on the above materials are given below.

Polybutadiene: Available under the trade name “BR730” from JSR Corporation

Antioxidant: 2,2-Methylenebis(4-methyl-6-butylphenol), available under the trade name “Nocrac NS-6” from Ouchi Shinko Chemical Industry Co., Ltd.

Zinc stearate: Available under the trade name “Zinc Stearate G” from NOF Corporation

Sulfur: Available under the trade name “Sulfax-5” from Tsurumi Chemical Industry Co., Ltd. (sulfur concentration, 95%)

Peroxide (2): A mixture of 1,1-di(t-butylperoxy)-cyclohexane and silica, available under the trade name “Perhexa C-40” from NOF Corporation; active oxygen content, 4.92%
[Sulfur (mol)÷Available Active Oxygen Content in Organic Peroxide]

“Available active oxygen content” refers to the active oxygen content (%) in the amount (number of moles) of organic peroxide included in the rubber composition. The active oxygen content is a characteristic value for each compound among organic peroxides. In addition, the values obtained by dividing sulfur (mol) by the available active oxygen contents of the organic peroxides are shown in the above table. The number of moles of sulfur is calculated based on S8 sulfur. In the table, the numerical values for molar quantity (mol), available active oxygen content, and [sulfur (mol)÷available active oxygen content] are shown as values which have been rounded off.

Next, using the respective resin materials shown in Table 2, an envelope layer, an intermediate layer and an outermost layer were formed in this order over the core by injection molding, thereby forming a three-layer cover. A common dimple configuration I (338 dimples; a plan view of the dimple pattern is shown in FIG. 2) was used for the dimples. The dimples were formed, during injection molding of the outermost layer, by impression with numerous outermost layer-forming protrusions provided on the spherical surface of the mold cavity.

Physical properties such as hardness of the individual layers and the ball, and the flight performance (carry) on shots with an I#6 were evaluated according to the criteria described below for the golf balls obtained in each of Examples 1 to 3 and Comparative Examples 1 to 3. The results are presented in Table 3. In (1) to (6) below, measurements were carried out in a 23±1° C. environment.

(1) Center Hardness of Core

The core was cut into hemispheres and the cut face was rendered into a flat plane, following which a durometer indenter was pressed perpendicularly against the center thereof and measurement was carried out. The JIS-C (JIS K6301-1975 standard, defined similarly below) hardness value is indicated.

(2) Surface Hardness of Core

A durometer was set perpendicular on a surface portion of the spherical core, and the hardness was measured based on the JIS-C hardness standard. The result was indicated as a JIS-C hardness value. “U” represents the JIS-C hardness at a position 100% of D from the center of the core; i.e., at the core surface.

(3) Cross-Sectional Hardness of Core

The core was cut with a fine cutter and, letting D (mm) be the radius of the core, O be the JIS-C hardness at a center of the core, Q be the JIS-C hardness at a position 55% of D from the core center, and T be the JIS-C hardness at a position 85% of D from the core center, the JIS-C hardness value at each of these places was measured.

(4) Material Hardnesses of Envelope Layer and Intermediate Layer

The resin material for the envelope layer was formed into a sheet having a thickness of 2 mm, and the hardness was measured with a type D durometer in accordance with ASTM-D2240.

(5) Surface Hardness of Intermediate Layer-Covered Sphere

The indenter of a durometer was set substantially perpendicular to the spherical surface of the intermediate layer, and the JIS-C hardness was measured.

(6) Material Hardness of Outermost Layer

The measurement method was the same as in (4) above.

(7) Flight Test Using a Middle Iron (I#6)

The carry (m) of the ball when struck at a head speed of 44 m/s with, as the middle iron, an X-BLADE CB (a number six iron manufactured by Bridgestone Sports Co., Ltd.) was measured. The results were rated according to the following criteria.

Good: Carry was 150 m or more

NG: Carry was less than 150 m

TABLE 3

Comparative

Example

Example

1

2

3

1

2

3

Core

Diameter (mm)

35.4

35.4

35.4

35.4

35.4

35.4

O

0% of radius D

63

64

62

57

55

62

(core center)

Q

55% of radius D

68

69

66

70

72

71

T

85% of radius D

84

82

82

74

76

80

U

100% of radius

92

84

90

88

80

81

(core surface)

Q-O

(55%-0%)

5

5

4

13

17

9

hardness difference

T-Q

(85%-55%)

16

13

16

4

4

9

hardness difference

Cover

Envelope layer

Material

I

I

I

I

I

I

Thickness (mm)

1.7

1.7

1.7

1.7

1.7

1.7

Sheet D hardness

51

51

51

51

51

51

Intermediate

Material

II

II

II

II

II

II

layer

Thickness (mm)

1.1

1.1

1.1

1.1

1.1

1.1

Sheet D hardness

62

62

62

62

62

62

JIS-C hardness at

98

98

98

98

98

98

surface of

intermediate layer

Outermost

Material

III

III

III

III

III

III

layer

Thickness (mm)

0.8

0.8

0.8

0.8

0.8

0.8

Sheet D hardness

44

44

44

44

44

44

Flight performance

Carry (m)

151

150

153

148

148

148

(I#6)

Rating

good

good

good

NG

NG

NG

As shown in Table 3 above, the golf balls obtained in the examples of the invention had an excellent flight performance when struck using an I#6. By contrast, the balls obtained in Comparative Examples 1 to 3 all had a poor flight performance when an I#6 was used.

Claims (3)

1. A golf ball comprising a core and a cover of at least one layer, wherein the core is formed of a rubber composition which comprises a polybutadiene-containing base rubber, an unsaturated carboxylic acid and/or a metal salt thereof, an organic peroxide and sulfur, and for which the value of [sulfur (mol)÷available active oxygen content in the organic peroxide] is at least 0.01 and not more than 0.019.

2. The golf ball of claim 1, wherein the core has a diameter of from 32 to 41 mm.

3. The golf ball of claim 1, wherein the core is composed of a single layer.