Need help with 308

I've recently bought some military 308 brass to use and am having some problems with it. After processing the brass and loading it,using the same procedure as I do with commerical brass, it fits very tight into my chamber so tight that I almost can't lock the bolt down. Thinking that it may need to be fire formed to fit my chamber I went to the range and after firing it it stills fits pretty snug. With the commerical brass I have no problems at all either before or after firing it. My thoughts are that because it's military brass the neck may need to be turned some to reduce the thinkness at the neck. Anybody have any other thoughts on what maybe the cause of this?

Military brass is usually thicker than commercial brass and you may have a close to minimum spec chamber, which is good.
Smoke a case after sizing with a candle or use a marker pen on it to see where it's tight as it will shine the brass where it's touching. Then you can decide how to approach a fix for the issue.
It will either entail sizing the cases a bit deeper if it's near the base, or as you mentioned, turning the necks if it's tight there, or both.
You are full length sizing, correct?

If the cases are an interference fit, shooting them seldom makes them smaller.

When cases are fired they get larger. So does the chamber. After the pressure drops, the chamber is back to normal dimensions, and the case shrinks a little due to springback. If your case was an interference fit to begin with, when it "springs back", you will often have even more of an interference fit.

This is another example of not using a case gage to set up your sizing dies. At best you are following the "size to the shellholder and add an eighth turn". This advice is so bogus.

At a minimum, buy a cartridge case gage and size to gage minimum. You will find that pot luck, once fired cases, don't necessarily size to gage minimum. That's why I keep a case gage on the bench and check mystery brass. If the stuff comes out too large, I set my small base die to size a bit more.

Also, I will bet that you are using standard sizing dies.

Here is an example of two military cases fired in a Zepplin sized chamber. One the left is a Wilson gage, on the right a reamer cut gage. The reamer cut gage was a barrel stub cut to depth with a chambering reamer. (My gunsmith did this for $35.00) The Wilson gage only measures length, but the reamer cut chamber will tell me if my cases are too long, and "too fat".

One case sized in a standard sizing die: It is an interference fit after sizing.

The other case sized in this Small Base die: It drops in all the way.

You will find examples of brass fired in chambers so large, that even a small base die won't bring them back.

Although The High Road has attempted to provide accurate information on the forum, The High Road assumes no responsibility for the accuracy of the information. All information is provided "as is" with all faults without warranty of any kind, either express or implied. Neither The High Road nor any of its directors, members, managers, employees, agents, vendors, or suppliers will be liable for any direct, indirect, general, bodily injury, compensatory, special, punitive, consequential, or incidental damages including, without limitation, lost profits or revenues, costs of replacement goods, loss or damage to data arising out of the use or inability to use this forum or any services associated with this forum, or damages from the use of or reliance on the information present on this forum, even if you have been advised of the possibility of such damages.