I have been fighting a crack for a couple years. It is thin (1/8 -3/16) cheap stainless, I had a welder try to weld it and it burned thru, and when we turned it down it tore. It’s not like a typical crack I have seen.

After trying to weld it a few times I filled it with high temp JB weld, that held water for about a month. When it started leaking bad again I cleaned it out real well and filled it with regular JB weld, and drilled a hole to a piece that did not pass thru the water jacket. I made a plate of 1/8 cold rolled steel and covered it with red permatex gasket material and screwed it tight. It held for almost a year.

This season I have redone it twice and now I even covered the plate with a 1” insulating material to try to keep it cooler. It’s leaking bad again. I would like to try to make it thru the rest of this season without shutting it down again.

When I do it next time a welder friend told me to try braising the crack. I’m good with that but I would like to hold off till it warms up.

I’m going thru 6 gallons of water a day. I thought it was horrible but then I think about the old steam locomotives and I know those things leaked into the firebox. Is that much water going to hurt anything I haven’t thought of?

New Member2.

NULL

Ya that metal in the picture looks pretty horrible. I think I would be looking for something else. There are always used owb on Craigslist. $1500.00 for the right boiler might buy you quite a few years. Or check the classifieds here. There were some guys selling some eko's for not much more than the price of scrap

Minister of Fire2.

NULL

From the limited photo you are not fixing that crack. IMO, you need to cut out a whole lot of metal and get to place where you can weld it. Once stainless cracks up like that you are going to be chasing cracks forever.

Minister of Fire2.

NULL

1/8 to 3/16 is not thin by any stretch. If it was mine I would cut out the whole bad area and cut up a filler plate and weld it back in. What weld procedure did your friend use? Did the bevel out the crack and clean all, or as much as possible, the corrosion from the gap? If you just tried burning through what is pictured, it doesn't surprise me it failed.

Feeling the Heat2.

NULL

Well I got it cleaned and ready for the welder but he got delayed a few days so I used JB weld and permatex again. here are a few of the pictures I took as I went along. I squeezed the JB weld in between the plates pretty well and then put some insulation on the top to try to keep the heat down. I have had it running a few days now. it is losing some water but not as bad.

Burning Hunk2.

NULL

Yeah that is at the end of it's life cycle. To weld dirty metal, your only option is a cracker box and that's going to burn through that thin metal. Best of luck, but you're probably going to have to scrap that one.