For preserving grobal environment and saving resources.we tryed to create the new plastics by materials recycling of waste plastics and rubbers. And new materials were born. Partl-l [Materials recycling for application of Direct Injection Molding(DIM) for Nylon 6 by polymer-alloying] New polymer alloy was proposed here, by blending of small amount of amorphous copolymer by Nylon 6-isophthalate and Nylon 6-terephthalate to waste Nylon 6 in addition of 55% glass fiber(GF) by applying DIM.By the results of trying 6 times molding of the same materials, the micro structure and average molecular weight changed slightly. We got new engineering plastics-Nylon 6+55%GF-in application of DIM without re-pelletting. Partl-2 [Materials recycling by blending of phenol resin and waste silicone rubber] We tryed recycling of waste silicone rubber. which is difficult to recycle, by blending of prepolymer of phenol resin and powder of waste silicone rubber, by sellecting co-solvent. By the results, new ph
… Moreenol resin was improved in surface smoothness, gloss and shearing fatigue strength. Part2 [New engineering plastics by recycling of waste PET] By using waste PET bottles as raw materials, we created new engineering plastics by blending of the acid modified thermoplastics elastomer. glass fiber and the special modifier, with DIM.BY the results, Impact strength of waste PET was improved remarkably, and other mechanical properties including torsional shearing properties and environment-stress resistance were cleared, so we proposed such materials as new engineering plastics. Our challenges were presented in several conferences and Part2 was published in 「Seikei Kakau(Bulletin of The Japan Society of Polymer Processing)」.PARTI その1「ポリアミド系GF強化ポリマーアロイの直接成形法による再成形リサイクリング」工場内廃棄物のナイロン6に少量のナイロン6イソフタレート・6テレフタレートの非晶性共重合体とをブレンドし、直接成形法によりアロイ化しながら、さらにガラス繊維を55%まで充填した試料を6回まで再成形した結果、ミクロ相構造の大幅な変化は見られず、分子量の低下もわずかであり、マテリアルリサイクリングが有望となった。PARTI その2「フェノール樹脂と廃シリコーンゴムのブレンド」フェノール樹脂のプレポリマーと廃シリコーンゴムに、相溶解剤を選びブレンドした試料を試作して評価した結果、元のフェノール樹脂より表面平滑度と光沢度が向上し、剪断疲労特性が元のフェノール樹脂よりむしろ向上した。その1、その2共にプラスチック成形加工学会秋季大会、平成8年10月に発表した。PARTII 「廃PETのエラストマー変性によるリサイクリング」PETボトルの廃品を洗浄し粉化した廃PETを原料として、これに酸変性した熱可塑性エラストマーとガラス繊維と微量成分を選択して、新材料を試作し、直接射出成形法を適用して実験した。その結果、新品PETのガラス繊維強化品に匹敵するエンジニアリングプラスチックが誕生し、メタロセン系のポリオレフィンエラストマー(POE)を導入した結果、廃PETのアイゾット衝撃値3.9が最高80.7まで向上し、一般物性・ねじり剪断特性・耐環境応力性の評価とモルホロジーの観察を進め、新材料を完成し、マテリアルライフ学会、平成10年成形加工シンポジア'98に発表、成形加工学会誌へ投稿、掲載された。 Less