Preparation of carbon coated ceramic foams by pyrolysis of polyurethane

Abstract

Electronically conducting carbon coatings over alumina foams were prepared by the foams’ impregnation in a polyurethane solution, followed by pyrolysis of the polymer layer. An optimal coating procedure was developed, using a commercial polyurethane lacquer. Pyrolysis was performed by heating the coated foams to 650–1,200 °C in Argon for 2–8 h. Coating characterization included surface area, phase composition, morphological and electrical conductivity measurements. Auger electron spectroscopy (AES) showed the composition was mostly carbon, with trace levels of oxygen impurities. Thickness, microstructure and interface between the alumina foam surface and the carbon film were analyzed using scanning electron microscopy (SEM and HR-SEM).

The carbon film’s specific electrical resistivity was 1–10 (Ω m×10−2), depending on the pyrolysis time, temperature and number of coatings. The resistivity was found to decrease by a factor of six when the pyrolysis temperature was increased from 750 to 1,200 °C. A second carbon layer, reduced the resistivity further by about a factor of two. These effects are attributed to densification, improved connectivity between the carbon grains and an overall thickening of the carbon layer. Thermal analysis and Raman measurements on the carbon films point to a grain rearrangement that is consistent with the improved conductivity of the films.

Keywords

Notes

Acknowledgements

The investigations were supported by the Technion’s fund for the promotion of research and in part by a joint grant from the Center for Adsorption in Science of the Ministry of Immigrant Absorption State of Israel and the Committee for Planning and Budgeting of the Council for Higher Education under the framework of the KAMEA Program.