Spalting is any form of wood coloration caused by fungi. Although primarily found in dead trees, spalting can also occur under stressed tree conditions or even in living trees. Although spalting can cause weight loss and strength loss in the wood, the unique coloration and patterns of spalted wood are sought after by woodworkers.[1]

Spalted Beech Bowl

Spalted Oak Bowl

Macro of Spalting in Beech showing White Rot and Zone Lines

Spalted Maple Guitar

Contents

Types[edit]

Spalting in hardwoods is divided into three main types: pigmentation, white rot and zone lines. Spalted wood may exhibit one or all of these types in varying degrees. Softwoods are susceptible to brown rot which degrades the wood too quickly to be used for woodworking.[2]

Pigmentation[edit]

Also known as sapstain, or in its most common form, bluestain, this type of spalting occurs when the darkly-pigmented fungal hyphae grow in the sapwoodparenchyma of a tree.[3][4] A visible color change can be seen if enough hyphae are concentrated in an area.[5] These pigmentation fungi often colonize wood via the rays, but are not considered decay fungi due to their non-destructive use of easily available wood carbohydrates.[6][7] The most common groups of pigmentation fungi are the imperfect fungi and the Ascomycetes.[7] Mold fungi, such as Trichoderma spp., are not considered to be spalting fungi, as their hyphae do not colonize the wood internally.

While pigmentation fungi do not degrade the wood cell wall, this type of decay can lead to a reduction in toughness (amount of energy absorbed before breaking), and increased permeability.[8] Pigmentation can occur on both hardwood and softwood, unlike other types of spalting which are more host specific.

White rot[edit]

The mottled white pockets and bleaching effect seen in spalted wood is due to white rot fungi. Primarily found on hardwoods, these fungi 'bleach' by consuming lignin, which is the slightly pigmented area of a wood cell wall.[9] Some white rotting can also be caused by an effect similar to pigmentation, in which the white hyphae of a fungus, such as Trametes versicolor (Fr.) Pil., is so concentrated in an area that a visual effect is created.[10]

Both strength and weight loss occur with white rot decay, causing the 'punky' area often referred to by woodworkers. Brown rots, the 'unpleasing' type of spalting, do not degrade lignin, thus creating a crumbly, cracked surface which cannot be stabilized.[5] Both types of rot, if left uncontrolled, will turn wood useless.

Zone lines[edit]

Dark dotting, winding lines and thin streaks of red, brown and black are known as zone lines. This type of spalting does not occur due to any specific type of fungus, but is instead an interaction zone in which different fungi have erected barriers to protect their resources.[7] They can also be caused by a single fungus delineating itself. The lines are often clumps of hard, dark mycelium, referred to as pseudosclerotial plate formation.[11]

Zone lines themselves do not damage the wood. However, the fungi responsible for creating them often do.

Conditions[edit]

Conditions required for spalting are the same as the conditions required for fungal growth: fixed nitrogen, micronutrients, water, warm temperatures and oxygen.[5][12]

The majority of fungi prefer warm temperatures between 10 and 40°C,[8] with rapid growth occurring between 20 and 32°C.[13]

Oxygen:

Fungi do not require much oxygen, but conditions such as waterlogging will inhibit growth.[14][15]

Time:

Different fungi require different amounts of time to colonize wood. Research conducted on some common spalting fungi found that Trametes versicolor, when paired with Bjerkandera adusta, took 8 weeks to spalt 1.5" cubes of Acer saccharum.[1] Colonization continued to progress after this time period, but the structural integrity of the wood was compromised. The same study also found that Polyporus brumalis, when paired with Trametes versicolor, required 10 weeks to spalt the same size cubes.

Commonly spalted woods[edit]

The Ohio Department of Natural Resources found that pale hardwoods had the best ability to spalt.[16] Some common trees in this category include maple (Acer spp.), birch (Betula spp.) and beech (Fagus spp.). However, recent research suggests that sugar maple ("Acer saccharum") and aspen ("Populus" sp.) are preferred by both white rot and pigment fungi [17][18]

Common spalting fungi[edit]

One of the more tricky aspects to spalting is that some fungi cannot colonize wood alone; they require other fungi to have gone before them to create more favorable conditions. Fungi progress in waves of primary and secondary colonizers,[4] where primary colonizers initially capture and control resources, change the pH of the wood and its structure, and then must defend against secondary colonizers that then have the ability to colonize the substrate.[4][19]

Ceratocystis spp. (Ascomycetes) contains the most common blue stain fungi.[20]Trametes versicolor, (Basidiomycetes) is found all over the world and is a quick and efficient white rot of hardwoods.[4]Xylaria polymorpha (Pers. ex Mer.) Grev. (Ascomycetes) has been known to bleach wood, but is unique in that it is one of the few fungi that will erect zone lines without any antagonism from other fungi.[21]

Spalting research[edit]

Initial lab work was conducted on spalting in the 1980s at Brigham Young University. A method for improving machinability in spalted wood using methyl methacrylate was developed in 1982,[22] and several white rot fungi responsible for zone line formation were identified in 1987.[23] Current research at Michigan Technological University has identified specific time periods at which certain spalting fungi will interact, and how long it takes for said fungi to render the wood useless.[1] Researchers from this university also developed a test for evaluating the machinability of spalted wood using a universal test machine.[24]