I have laid down some of my best beads ever, that nobody will ever see

Fusion: Tasslehawf and I were talking about THIS comment you made. But now I think we took it out of text. You mean no one will see it, 'cause that's the part underwater!!! If I'm wrong...SHOW US THE BEADS, MAN!!!!

4 1/2" Aluminum Wheels

Originally Posted by tasslehawf

Now I see what you're saying... grinding down the electrode with your aluminum-caked grinder. Heh. I have been doing that lately.

I have two 4 1/2" wheels, one coarse and one fine. The coarse is marked stainless and alum. I can't read the fine one, it's rubbed off. But I can push really hard on either one, without it ever loading up. The fine one is my aluminum mill. If you haven't tried either, they're worth finding. Got them at the LWS.

Not dangerous at all, all you do is ground the tungsten til it turns red and then dip the tip of it in the chemsharp powder until you have the desired tip you want. Trust me if the Navy thought it was dangerous they would not have it.