From f9642d1ca08b912e116227e22336451b2ef7af42 Mon Sep 17 00:00:00 2001
From: Bdale Garbee
Date: Fri, 19 May 2017 11:08:14 -0600
Subject: [PATCH] first attempt at making igniters
---
rockets/research/2017-batch-02.mdwn | 49 +++++++++++++++++++++++++++++
rockets/research/index.mdwn | 3 +-
2 files changed, 51 insertions(+), 1 deletion(-)
create mode 100755 rockets/research/2017-batch-02.mdwn
diff --git a/rockets/research/2017-batch-02.mdwn b/rockets/research/2017-batch-02.mdwn
new file mode 100755
index 0000000..faabcef
--- /dev/null
+++ b/rockets/research/2017-batch-02.mdwn
@@ -0,0 +1,49 @@
+# Batch 2017-batch-02 #
+
+We're nearly out of [Quickburst](quickburst.net) igniters, they haven't been
+great at lighting erythritol grains anyway, and they're kind of
+expensive... So we decided to experiment with making igniters, and the
+first ones we decided to try are "epoxy fire" using a formula from
+[Scott Berfield](http://www.berfield.com/igniters.html).
+
+For our first attempt, we made up a 10g batch with the following formula:
+
+* 68% KNO3, 6.80g, hand ground with mortar and pestle to fine grain size
+* 7% magnesium powder, 0.70g
+* 1% air float charcoal, 0.10g
+* 24% West Systems 105+205 epoxy, 2.40g
+** 2.01g 105 resin
+** 0.39g 205 hardener
+
+Two folded papers were used to weigh out the KNO3 in one, and a mixture of
+the magnesium powder and charcoal in another. The epoxy was mixed in a small
+disposable plastic cup with a popsicle stick, then the magnesium and charcoal
+were poured in and mixed until complete wetted. Then the KNO3 was added and
+mixed until everything became a homogenous mix. It was a dry-ish, crumbly
+consistency, but packed into lumps easily.
+
+We used Chinese made e-matches with 2m leads, and used plastic drinking straws
+about 1/4" in diameter cut into 1" lengths. The procedure was to slide the
+ematch through the straw, pack material into the straw from the "back" end
+until it was mostly full, then pull the ematch lead until the match head was
+just at the forward end of the straw, then pack more material in the front
+end of the straw until the match head was just covered. Using nitrile-gloved
+fingers, it was then easy to mash on both ends simultaneously to make sure
+we had good packing with minimal voids, leaving both ends flush with the
+straw.
+
+The matches were left to cure overnight, and then the straws were carefully
+sliced lengthwise with a razor blade and peeled off, revealing what looked
+like very solid cylindrical igniters. They look a lot like the Quickburst
+ones.
+
+These igniters were made on 17 May 2017.
+
+## Results ##
+
+## Observations ##
+
+A 10g batch was just enough to make up 6 igniters, and the pot life seemed
+a little tight. Next time, it seems like trying a 15g batch with the slower
+206 hardener might be a good plan?
+
diff --git a/rockets/research/index.mdwn b/rockets/research/index.mdwn
index 89da801..7f47669 100755
--- a/rockets/research/index.mdwn
+++ b/rockets/research/index.mdwn
@@ -11,7 +11,8 @@
### 2017 ###
-* [2017 batch 01](2017-batch-01.html) - May 2017 - 16 54mm KNSO grains
+* [2017 batch 02](2017-batch-02.html) - 17 May 2017 - 6 epoxy fire igniters
+* [2017 batch 01](2017-batch-01.html) - 15 May 2017 - 16 54mm KNSO grains