Abstract

The present work investigates the ablative and thermal properties of an epoxy resin which was modified with titanium dioxide nanoparticles having different size. Prepared samples were submitted to temperatures above 1900 °C and tested for their thermo-protective and ablative properties. The effect of epoxy composite components on thermo-protective and ablative properties: the maximum back side temperature, and the average weight loss under intensive heat flow conditions as well as temperature distribution on the ablation surface of the sample using a thermographic camera and a pyrometer have been established. A statistical analysis of the test results was made. It was confirmed that epoxy resin crosslinked with polyaminoamide hardener and modified with TiO2(21 nm) i TiO2(100 nm+1% Mn) showed improved thermo-protective properties in comparison with unmodified epoxy matrix.

Keywords

Epoxy nanocomposites Ablative properties Thermal resistance

1 Introduction

Ablation is a self-regulating process of heat and mass exchange leading to occurrence of physical changes and chemical reactions, irreversible structural and chemical changes of the material with the simultaneous heat absorption. This process is initiated and sustained from external sources of thermal energy. The thermal decomposition in the initial phase of the ablation process and the pyrolysis reactions at a higher temperature leads to the formation of a porous carbon layer with a very low thermal conductivity coefficient (so-called ablative layer) up to 2/3 of the initial matrix weight (Lin 2005; Yu 2004; Dimitrienko 1997).

The term ablation refers to the exchange of heat and mass in the body’s upper layer in thermochemical and mechanical processes. There are many technical applications for ablative material. Polymeric ablation materials are increasingly used in the field of thermal protection systems. They can be used in the design of passive refractories for load-bearing structures of large-size buildings (NIST NCSTAR 1 2005; Wilkinson 2002), communication tunnels (Haack 2004; Ono and Otsuka 2006) and for protection of data stored on electronic, optical, magnetic, etc.

Modeling ablative thermo-protective properties consists in the selection of materials with high specific heat cp(t) and high density ρ, high thermal capacity and with low thermal conductivity coefficient λ(t) (i.e. small thermal diffusivity α(t)) (Kucharczyk 2007; Song et al. 2003a, b). In polymeric composites, when the ablation temperature Ta is exceeded, there are endothermic reactions related to the thermal decomposition of the matrix material, which results in effective specific heat cp with high values. In their pure form, polymers are good ablative materials (Bahramian and Kokabi 2009; Bakar et al. 2016) with a very low heat conduction coefficient λ. However, due to their softening, low density and low thermal stability as well as the porosity and brittleness of the ablative layer formed in the ablation process, they need to be modified with mineral fillers (Bahramian and Kokabi 2009; Lombardi et al. 2012) or reinforcing fibers (Jackowski 1986; Bahramian 2013; Kucharczyk 2012; Patton et al. 2002) increasing their thermal stability, resistance to heat flow, and consequently the thermal insulation of the composite.

Epoxy composites and specific shells will protect machines, devices, components of building structures and people during incidental thermal loads much higher than expected, when the temperature increase, e.g. of carbon steel above 800 °C, can cause a sixfold–eightfold decrease in its tensile strength and almost twice reducing its stiffness. Classical refractory materials do not protect against the temperature increase on the back surfaces of the protective layers as effectively as polymeric ablation materials, whose high thermal resistance of rkp (m2 K/W), allows to reduce the temperature in the range from several dozen degrees to 2000 °C, with the use of insulating walls of small thickness (Kucharczyk et al. 2018).

Ablative screens can also protect stored data of electronic, optical, magnetic carriers, etc. Classic materials and fire-fighting systems do not provide this possibility, because in emergency situations even rapid fire suppression does not reduce the heat transfer through the protective wall to the extent that it does not exceed the allowed operating temperature of the data carrier (Kucharczyk 2010).

Recently, attempts have been made to obtain hybrid composites based on epoxy resins that contain two different modifiers. An important advantage of hybrid materials is a unique combination of mechanisms for properties improvement which may lead to synergistic effect unrealizable with traditional composites with one modifier (Bakar et al. 2014; Szymanska et al. 2017). Due to the ease of processing and fairly good physical properties, there is an increasing interest in using not only thermoplastics but also thermosetting plastics as matrix for composite materials (Kucharczyk et al. 2013; Bakar et al. 2010, Szymanska et al. 2017).

The investigation of such materials is particularly important for the researchers and industrialists, because it is in connection with the existing terrorist threat. This subject is becoming more and more important and was included in the NATO-DAT (Defense Against Terrorism) program. Based on the analysis of the effects of terrorist attacks in Oklahoma City, on the World Trade Center (NIST NCSTAR 1 2005; Wilkinson 2002), the behavior of this type of materials is tested and analyzed using computer programs (Willam et al. 2004). These materials are beginning to be used in the protection of few but important public utilities. Despite many years of use of ablative materials, there are still unexplored qualitative and quantitative relationships between the indicated type-phase composition and thermo-protecting properties of composites.

Conducting research will develop hypotheses for the preparation of polymer ablation composites to protect people, machines, devices and load-bearing construction structures against short-term exposure to high temperature flux, as well as to describe the quantitative and qualitative impact of epoxy modifiers on the ablation process and their selected strength properties.

The results of the work can be application-oriented, form the basis for the design of thermal shields, especially for the protection of civil structures, and can be a preliminary stage for designing structures and developing technologies for modern aviation components with such systems.

The purpose of the present study was to determine the effect of nanoparticles on the ablative properties, i.e. the maximum temperature of the rear surface area Ts_max and ablative weight loss Ua of epoxy composites containing two TiO2 nanoparticles with different particles size (21 nm and 100 nm). Prepared epoxy nanocomposites have to be used as thermal protective surfaces in machines and equipments.

2 Evaluation of ablative properties

The research works was carried out based on a developed research plan as follows:

1.

Material samples were made for classical, thermo-protective ablative tests.

2.

A classic ablation study was carried out using the effects of high temperature heat flux.

3.

The effect of components on erosive and ablative material wear as well as the temperature of the back surface of the sample wall of the tested composites in classical ablation tests was assessed.

4.

A statistical analysis of the test results was made.

5.

Probable reasons for the interaction between the epoxy composites components and the possibilities of thermo-protective protection of the structures were discussed and established.

The so-called “ablative gun” (Song et al. 2003a, b) of our own design (Kucharczyk 2007) was used or the classical ablation tests of thermo protective properties, allowing the effect of high temperature, stabilized, homogeneous flammable gas stream on the sample. The temperature distributions was recorded on the ablation surfaces and the back surfaces of the sample walls by using the available pyrometers, thermovision camera and thermocouples. Ablation weight loss were determined.

The research on ablation properties of thermo protective hybrid epoxy nanocomposites, was carried out on the basis of the developed statistical program of the first-order type 23 experimental test with repetitions (Montgomery 2009; Leszek 1997).

2.1 Materials used for epoxy-nanocomposites preparation

Considering the differences of some specific physicochemical, technological and performance properties, ease of processing, production costs, availability of components as well as results of literature analysis, epoxy nanocomposites modified with titanium dioxide nanoparticles were selected for the study.

A liquid epoxy resin Epidian 52 produced by Sarzyna Chemical Company (Nowa Sarzyna, Poland) was chosen as a matrix for nanocomposites. It is a mixture of a low-molecular diglycidyl ether of Bisphenol A and an active diluent which reacts with the hardener during the epoxy resin curing process (Czub et al. 2002).

A polyaminoamide hardener with the trade name PAC produced by ZCh Ciech-Sarzyna in Nowa Sarzyna (Table 1) was used as crosslinking agent.

The hardener (PAC) is mainly used for the modification and curing of low molecular weight epoxy resin. It is a low-reactive, viscous liquid that can be used in a wide range of weight ratios. The lifetime of the epoxy composition with PAC hardener is several hours, and complete curing takes place within 4–7 days.

Two types of titanium nanodioxide (Sigma-Aldrich Co 2014) were selected to modify the epoxy matrix:

Titanium oxide exists in many types of rocks and minerals in three crystalline forms, as rutile, anatase or brookite. It is the ninth most common element in the Earth’s crust. Additionally, it absorbs UV rays in the range of 290–400 nm and is usually considered as chemically inert (Anselme 2013; Bowers 2012) (Fig. 1).

The titanium oxide in the nano form with particles have a size less than 100 nm has been selected in the present study. The particles are strongly bound or connected with each other by means of chemical bonds, forming aggregates, i.e. particles of micro scale size (Anselme 2013).

Titanium dioxide is characterized by: high refractive index in the range of 2.616–2.903 (higher than for diamond); low optical absorption in the visible range; good chemical stability; high chemical resistance; high hardness of about 6 on the Mohs scale; high permeability (120 for rutile); high resistance (Sigma-Aldrich Co 2014).

Titanium dioxide has been used for several decades in many industries, including in the production of fibers, printing inks, adhesives, varnishes, rubber composites, LCD screens, self-cleaning glass and ceramics, antibacterial materials, resistant to UV rays and conductive, food packaging, air and sewage treatment processes, and also in the metallurgical and aerospace industries and cosmonautic (Rao Rao et al. 2012; Fujishima and Zhang 2006; Hu et al. 2003; Li et al. 2003).

Titanium dioxide in the nano scale is characterized by significantly better properties and a wider range of use compared to standard titanium oxide.

Al-Ajaj et al. (2013) as well as Rajabi et al. (2013) conducted research on the effect of titanium dioxide on the properties of epoxy resin. Both research groups have shown that the use of titanium dioxide nanoparticles increases the flexural strength, Young’s modulus and resistance to cracking as well as an the glass transition temperature. This is caused by a reduction in the distance between the nanofillers and the polymer chain, the polarity of the particles, the strength of the van der Waals bonds in the matrix and the length of the polymer chains, as confirmed by Merad et al. (2011), Hsieh et al. (2010). However, Chen and Mao (2007) and Chatterjee and Islam (2008) and their research groups showed that, the stiffness of the epoxy composite increases with increasing content of the nanofillers. This is mainly attributed to the increased limitations of the polymer chains movement due to the presence of solid particles.

In addition, Chatterjee et al. showed significantly improvement in the thermal, mechanical and viscoelastic properties of the epoxy resin with the addition of titanium dioxide nanoparticles. Chang et al. (2005) investigated the effect of the addition of titanium dioxide on the tribological properties of epoxy resin. They showed that a small amount of the nanofiller visibly reduces the coefficient of friction. Wetzel et al. (2006) modified epoxy resin by using titanium dioxide and aluminum oxide nanoparticles. The controlled dispersion process was obtained by using high energy process to reduce the size of agglomerates and to obtain a homogeneous distribution of individual nanoparticles in the resin. They observed different fracture mechanisms such as crack deflection, plastic deformation, and crack pinning due to the presence of the nanoparticles in epoxy composites.

2.2 Experimental research plan

The number of sample phase compositions, equal to the number of scheduled experiments (N = 8), was determined on the basis of the experiment plan described by an orthogonal 1st order full-factorial matrix of the type 23 (Table 2). It included single replications, where two state levels (lower level − 1 and upper level + 1) and three independent input variables (xi) (i = 1, 2, 3) occur (Montgomery 2009; Leszek 1997):

([phr] − number of parts by weight of the hardener per 100 parts of resin)

(−) 60 i (+) 100, x1(śr) = 80, Δx1 = 20;

x2 − volume fraction of the mixture of both TiO2 nanofillers in the composite [%]

(–) 2% i (+) 5%, x2(śr) = 3.5%, Δx2 = 1.5%;

x3 − weight fraction of TiO2(21 nm) to the sum of the weight of both nanofillers

TiO2(21 nm)/[TiO2(100 nm + 1% Mn) + TiO2(21 nm)], [%],

(–) 60% i (+) 90%, x3(śr) = 75%, Δx2 = 15%.

The components of the response variable y (the output parameters) are the average maximal temperature of the rear surface of specimen Ts_max (°C) and an average relative ablative (erosive) weight loss Ua (%) after 120 s of treatment with hot combustion gases.

The regression and interaction coefficients (bi) of all function components have been calculated. The statistical analysis of the results enabled to determine the threshold relevance of the regression coefficients (bi) and estimation of their effect on the output parameters (y). The output value was calculated from the following equation of the experiment objective (1) (Montgomery 2009; Leszek 1997):

Moreover, the variance s(y), regression error and interaction coefficients s(bi), as well as the level of their statistical significance (bsign ≥ bi) have been determined on the basis of t-Student test at the confidence level αp = 0.05 (Montgomery 2009; Leszek 1997).

2.3 Samples preparation

The polymer matrix of the composite samples was Epidian 52 epoxy resin, cross-linked at room temperature with PAC hardener during 14 days. The ablation properties of the resins were modified by adding high density bulk nanofillers (titanium dioxide with a grain size of 21 nm and 100 nm).

The weight fraction of the hardener (x1) and the content of powder fillers (x2—the volume fraction of the mixture of both fillers in the composite and x3—the weight fraction of TiO2(21 nm) in the total weight of both nanofillers) were independent variables of the Type I test plan with repetition and were presented using an orthogonal full-matrix matrix. The weight compositions of the obtained composites are summarized in Table 3.

Table 3

The mass phase compositions of the composites

No.

x1

x2

x3

Resin, (g)

Curing agent, (g)

TiO2(21 nm + 100 nm), (g)

TiO2(21 nm) (g)

TiO2(100 nm) (g)

1

−

−

−

14.898

8.939

1.896

1.138

0.758

2

+

−

−

11.823

11.822

1.896

1.138

0.758

3

−

+

−

14.442

8.665

4.741

2.845

1.896

4

+

+

−

11.460

11.461

4.741

2.845

1.896

5

−

−

+

14.898

8.939

1.896

1.706

0.190

6

+

−

+

11.823

11.822

1.896

1.706

0.190

7

−

+

+

14.442

8.665

4.741

4.267

0.474

8

+

+

+

11.460

11.461

4.741

4.267

0.474

The epoxy composite samples were prepared as follows:

appropriate amount of TiO2(21 nm) was added to epoxy resin Epidian 52 and mixing of ingredients was carried out by using a Hielscher UP200H homogenizer (cycle: 1, amplitude: 100%) during 15 min;

addition of a second nanofiller TiO2(100 nm + 1% Mn) to the mixture;

mixing of ingredients using homogenizer during additional 15 min;

cooling of obtained mixture to room temperature;

addition of the curing agent;

mechanical mixing of obtained composite for 5 min;

pouring the mixture into previously prepared forms;

curing of samples at room temperature during 14 days.

The “reference” samples (unmodified, cured epoxy resins) were prepared by adding appropriate amounts of hardener to the epoxy resin followed by mixing. The sample 01 contained 60 phr of PAC hardener, while sample 02 contained 100 phr of hardener. The curing time of the samples in the molds was 4 days at room temperature and then post-cured at 70 °C for 72 h. The samples for ablative tests were prepared under laboratory conditions. A total of 20 composite samples with dimensions of 12 × 35 × 26 mm were prepared for the tests.

2.4 Ablative tests

Composite samples were weighed and mounted on plasterboard shields on a stand designed for ablation research prior to ablation test. Next, in a test which lasted t = 120 s, the samples were exposed to a stabilized stream of combustible gases (Fig. 2). The heat source was a burning of propane-butane mixture (65% propane and 35% butane) with temperature of flammable gases above 1900 °C. The flame was stabilized with an ablation gun (Fig. 2b), whose axis was set perpendicularly to the front surface of the sample (26 × 35 mm). The gun nozzle was set at a distance of 30 mm away from the surface of the ablation surface. The above configuration of the ablation test stand allows stabilizing the flame, unifying the temperature on the ablation surface as well as ensuring the repeatability of results for all test samples.

Measurement stand: (1) the ablative gun with flammable gases stabilization, (2) a tripod, (3) a torch, (4) a flame, (5) the testing sample, (6) a sample casing, (7) the thermocouple, (8) the temperature measurer of Ts(t), (9) a computer, (10) the pyrometer or the thermovision camera to Tpa(t) measurement

1.

The ablative surface Tpa with a thermovision camera Thermo Tracer NEC H2640 at the 60th second of each test.

2.

The ablative surface Tpa(t) using an optical pyrometer OPTCT2MHCF by Optris GmbH, set at an emissivity of ε = 0.95 and featuring a continuous electronic recording of temperature variations using Compact Connect 1.7.3 software.

3.

The rear sample wall surface Ts(t) by means of TP-204N (NiCrSi-NiSi) thermocouple by Czaki Thermo-Product using a measurement module USB-4718 by Advantech.

The temperature distribution on the ablation surfaces of the tested samples was recorded by using a thermovision camera. Figure 4 shows the results of temperature measurement on the surface for sample no. 8, after 60 s of the ablative sample exposition to heat flow. The brightest area in the upper part of the sample (point A) corresponds to the highest temperature on the surface—equal to 961.5 °C. The darker areas (points B and C) correspond in turn to its lower values, 780.7 °C and 616 °C. Further away from the hot spot of the sample, the lower temperature values. The position of the point A in the upper area of the sample is caused by the rising of the hot gas jet upwards.

Example of the temperature field on the ablative surface after 60 s of the ablative sample exposition the heat flow (sample no. 8)

The temperature of ablative surface (shown in Fig. 5) resulted from the heat transfer at boundary between gas and solid state material, the heat conduction through the wall of the composite and the ablative processes taking place on surface layer (endothermic chemical reactions, polymer degradation and different structural changes). The value of this temperature depended on physical properties of solid material and gas, as well as insulating wall geometry. Ablative surface temperature Tpa was considered as an indirect input testing parameter and was assumed as first type boundary condition for Dirchlet (determined by the temperature distribution anytime on the surface of the body), enabling in the future the resolution of Fourier Kirchhoff differential equation of unsteady heat conduction in solids (Kucharczyk 2007; Bakar et al. 2016). The average value of all measured maximum temperature Tpa_max was 875 °C with a standard deviation of 14 °C (Fig. 6).

Average maximum temperature on the surface of ablation Tpa_max for particular phase compositions after 120 s of the heat flow exposition

The temperature values obtained on the surface of the rear wall Ts_max depend upon the possibility of using the material as a protective shield for a wide range of applications. The temperature of the surface on the rear wall Ts(t) was measured for a period of 120 s. Figure 7 shows the temperature curves on the surface of the rear wall of the samples for each tested ablative composite.

Changing of the rear surface temperature Ts(t) during 120 s of the heat flow exposition

The highest temperature Ts_max of unmodified epoxy resin crosslinked with 100 phr of PAC hardener (composition no. 2) was almost three times higher than that of epoxy composite samples. During the last seconds of the test, the sample was destroyed as recorded by a sharp increase in temperature on its back surface (Fig. 7). However, the reduction of the hardener content to 60 phr (composition no 1) resulted in decrease of Ts_max, which still remained almost 30% higher than for the epoxy nanocomposites (Figs. 7 and 8).

Average maximum temperature on the rear surface Ts_max for particular phase compositions after 120 s of the heat flow exposition

Resin Epidian 52 modified with a nanofiller showed better thermo-protective properties. The epoxy composite no. 1 based on 60 phr of hardener PAC, with a content of 2% by weight of a mixture of titanium dioxides, including 60% by weight TiO2(21 nm), reached the lowest temperature Ts_max from all tested composites.

The histograms of temperature changes Tpa(t), for samples from unmodified resins (compositions no. 1 and no. 2), are well below the graphs for epoxy nanocomposites (Fig. 5). Under fixed conditions, the heat transfer between gas and solid depends on the resistance of heat transfer rkp, i.e. the value that include the physical properties of the material and gas with the geometry of the insulating wall. Thus, from the analysis of histograms temperature Tpa(t), and Ts(t) (Figs. 5 and 7), it follows that the lower temperature of the ablation surface Tpa is due to higher rates of heat transfer at the border gas–solid, and thermal conduction through the wall of the composite, which is equivalent to an increase in the temperature of the rear face of the wall Ts of a given material and depends directly on its phase composition. The greatest degree of reduction in temperature difference or Tpa(t) − Ts, the characterized nanocomposite epoxy compositions no 1 and no 8. According to the laws of Pécelta have the greatest resistance to heat transfer replacement rkp of the test materials. From the point of view of thermo-protecting properties, it is important that the temperature of the rear surface of the wall Ts of the ablative shield (s) is the lowest after a given time of exposure to the heat flux. However, composites with a higher temperature on the ablation surface and a lower temperature on the back surface of the sample wall (higher temperature gradient) are subjected to higher thermo-mechanical stresses, which can lead to the destruction of the ablation shield (Kucharczyk 2010).

In this context, the ablation (erosive) weight loss of the Ua composite becomes more important. The smaller loss of mass of the ablation layer, indicates higher thermal stability of the composite and a thicker operating top layer (Kucharczyk 2010) with a low thermal conductivity coefficient λ(t). The smallest erosive wear after 120 s during the impact of the stream of combustible gas, the composition of the sample has suffered phase no 4 (Table 4), which is characterized by a second in order Ts_max low temperature (Fig. 9).

The average values of ablative results of the tests (i.e. the maximum surface temperature of the ablation Tpa_max, the maximum temperature of the back surface area of an ablative sample Ts_max and ablative weight loss Ua) are shown in Table 4.

The lower weight loss is exhibited by composites containing a higher amount of nanofillers, i.e. 5% wt. no. 3, no. 4, no. 7 and no. 8 (Fig. 9). Samples no 4 and no 8 were cross-linked with a higher amount of hardener (100 phr). The smallest weight loss (34%) was shown by the composite no. 4, which contained less TiO2(21 nm), than composite no. 8. The sample “reference” no 2, cross-linked (similarly to composite no. 4) 100 phr of hardener PAC, reached the largest ablation fat loss, up to about 90%. This indicates the adverse effect of a larger amount of PAC hardener on the thermal stability and thermo-protective ablative properties of pure, unmodified Epidian 52 epoxy resin.

Epoxy composites have undergone intensive decomposition and pyrolysis during the ablation process with harmful volatiles products to human health. The formed ablative layer during the process was not consistent but brittle, very porous and automatically separated from the original material (Fig. 10). This constituted a negative phenomenon, which reduced both the strength and durability of coatings and their thermal protective characteristics.

The ablative surfaces and the mass waste of composites after 120 s of heat flux exposition

Composites based on epoxy resins have undergone intensive decomposition and pyrolysis during the ablation process with harmful volatiles products to human health. The formed ablative layer during the process was not consistent but brittle, very porous and automatically separated from the original material (Fig. 10). This constituted a negative phenomenon, which reduced both the strength and durability of coatings and their thermal protective characteristics.

The lowest end temperature of the back wall surface of the sample Ts_max was obtained by the composite sample no. 1 with the following composition: Epidian 52 + 60 phr PAC + 2% by volume of TiO2(21 nm) and TiO2(100 nm + 1% Mn), including 60 wt% of TiO2(21 nm).

The best thermoprotective properties were exhibited by the composite which reached the lowest value of the maximum surface temperature of the sample wall Ts_max (provides the greatest temperature reduction) and the smallest ablation weight loss Ua (has the highest thermal stability and is the thickest and most consistent internally, good adhesion to the original, ablative material exploitation layer with low thermal conductivity). Both conditions are best met by a sample with phase composition no 4.

3 Statistical analysis of the results

Statistical calculations of both the component response functions Ts_max(xi) and Ua(xi) were conducted using the results of ablative testing. Table 5 shows the calculated values of regression coefficients bi and variance s(y), errors of regression coefficients s(bi), and significance levels of regression coefficients bistot. The parameter bi is shown in bold—it is lower than bsign but subject to error s(bi) which, once taken into account to compute bi, helps to estimate the sum total of bi and s(bi) as larger than bistot, that is, still significant statistically (Montgomery 2009; Leszek 1997).

Table 5

Regression and interaction coefficients of model (1) after 120 s of ablative tests

b0

b1

b2

b3

b12

b13

b23

b123

s(y)

s(bi)

bsign

Ts_max (°C)

42.56

0.81

1.19

− 1.69

− 1.81

1.19

1.34

0.47

1.09

Ua (%)

48.31

− 11.41

3.49

− 2.99

4.73

1.67

3.86

Based on the calculated coefficients of regression and interaction (bi) and considering level of their significance (bsign≥ bi), regression equations of the component response functions (2) and (3) are formulated:

Analysis of numerical results of statistical calculations for the maximum back side temperature of tested samples Ts_max are presented in Table 5 and coefficients of response function Ts_max(xi) Eq. (2) indicates the following rules:

1.

A significant effect on decreasing the temperature of the back surface of the sample wall Ts has two input variables x2 and x3 (negative coefficient b23). They determine respectively: the content of the mixture of TiO2(21 nm) + TiO2(100 nm + 1% Mn) in the composite and the amount of TiO2(21 nm) in the filler mixture. Increasing the number of nanofillers with a higher TiO2(21 nm) content in the mixture resulted in the reduction of the maximum temperature Ts_max. This interaction does not occur when using a larger amount of hardener (changing the sign to positive at the b123 coefficient).

2.

Simultaneous application of larger quantities of hardener and a mixture of nanofillers, resulted in a lower Ts_max temperature. This is evidenced by the negative value of the interaction factor b12.

Input variable x2, denoting the amount of TiO2(21 nm) + TiO2(100 nm + 1% Mn), in the individual interaction (without taking into account the amount of hardener and composition of the nanopowder mixture), does not significantly affect the temperature of the back surface of the sample wall.

Analysis of numerical results of statistical calculations for the ablative weight loss of test samples Ua presented in Table 5 and coefficients of response function Ua(xi) Eq. (3) indicates the following rules:

1.

The input variable x2 (negative value of the coefficient b2) has the most important influence on the ablation reduction of Ua parameter, which means that increasing the amount of TiO2(21 nm) + TiO2(100 nm + 1% Mn) decreases ablation weight loss. The value of coefficient b2 is over three times higher than the coefficients b13 and b123.

2.

Input variables x1 and x3, denoting the amount of hardener and TiO2(21 nm) in the mixture of nanofillers, in mutual interaction (positive value of b13), as well as the interaction of all three variables (negative value b123) do not significantly affect the value of the response function Ua(xi). In addition, the opposite signs, with both of these coefficients, indicate the mutual abolition of influence.

4 Conclusions

Based on obtained results, it can be concluded that:

1.

The composite based on epoxy resin Epidian 52 cross-linked with 60 phr of PAC hardener, with a 2% by volume of a mixture of TiO2(21 nm) + TiO2(100 nm + 1% Mn), including 60% by weight of TiO2(21 nm)), characterized by the lowest temperature of the rear wall surface.

2.

Epoxy resin Epidian 52 cross-linked with 100 phr of PAC hardener, with 5% by volume of a mixture of nanofillers TiO2(21 nm) + TiO2(100 nm + 1% Mn), including 60 wt% of TiO2(21 nm)), shows the smallest abrasive weight loss Ua, i.e. the best thermal stability of the virgin material and cohesion of the ablative layer, which improves the resistance to thermomechanical stresses of the composite and ensures the formation of a passive thermo-protective layer.

3.

Increasing the amount of PAC hardener in Epidian 52 resin-based composites and increasing the amount of both TiO2(21 nm) and TiO2(100 nm + 1% Mn) led to increase of the maximum temperature of the back wall surface Ts_max but at the same time contributed to the reduction of ablative weight loss Ua.

4.

Considering the values of both parameters (Ts_max and Ua), it should be noted that the best thermal protection properties were shown by composite no. 4, which was characterized by a very low, maximum temperature of the wall surface of the sample Ts_max (40 °C) as well as the lowest value of ablation weight loss Ua (35%).

Wilkinson, T.: The World Trade Center and 9/11: the discussion of some engineering design issues. National Conference “Safe Buildings for This Century”. Australian Institute of Building Surveyors, Sydney (2002)Google Scholar

Copyright information

Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.