Abstract

The effect of two nanoparticle oxides on friction and wear was studied under laboratory test conditions using a reciprocating test machine and two test configurations. The addition of these nanoparticles in base stock oil under certain conditions reduced the coefficient of friction and improved wear, but that depended on the test configuration. Examination of the rubbed surfaces showed the pronounced formation of a tribofilm in some cases, while polishing on the surface was also observed in other cases. Contact configuration is important when oxide nanoparticles are being evaluated and the conclusions about their efficacy can be vastly different.

@article{osti_1341484,
title = {Experimental Evaluation of Oxide Nanoparticles as Friction and Wear Improvement Additives in Motor Oil},
author = {Demas, Nicholaos G. and Erck, Robert A. and Lorenzo-Martin, Cinta and Ajayi, Oyelayo O. and Fenske, George R.},
abstractNote = {The effect of two nanoparticle oxides on friction and wear was studied under laboratory test conditions using a reciprocating test machine and two test configurations. The addition of these nanoparticles in base stock oil under certain conditions reduced the coefficient of friction and improved wear, but that depended on the test configuration. Examination of the rubbed surfaces showed the pronounced formation of a tribofilm in some cases, while polishing on the surface was also observed in other cases. Contact configuration is important when oxide nanoparticles are being evaluated and the conclusions about their efficacy can be vastly different.},
doi = {10.1155/2017/8425782},
journal = {Journal of Nanomaterials},
number = ,
volume = 2017,
place = {United States},
year = {Mon Jan 30 00:00:00 EST 2017},
month = {Mon Jan 30 00:00:00 EST 2017}
}

Here, the effect of two nanoparticle oxides on friction and wear was studied under laboratory test conditions using a reciprocating test machine and two test configurations. The addition of these nanoparticles in base stock oil under certain conditions reduced the coefficient of friction and improved wear, but that depended on the test configuration. Examination of the rubbed surfaces showed the pronounced formation of a tribofilm in some cases, while polishing on the surface was also observed in other cases. Contact configuration is important when oxide nanoparticles are being evaluated and the conclusions about their efficacy can be vastly different.

Developments of high performance lubricants are driven by increasingly growing industrial demands and environmental concerns. We demonstrate oil-soluble polymer brush-grafted inorganic nanoparticles (hairy NPs) as highly effective lubricant additives for friction and wear reduction. A series of oil-miscible poly(lauryl methacrylate) brush-grafted silica and titania NPs were synthesized by surface-initiated atom transfer radical polymerization. Moreover, these hairy NPs showed exceptional stability in poly(alphaolefin) (PAO) base oil; no change in transparency was observed after being kept at -20, 22, and 100°C for ≥55 days. High-contact stress ball-on-flat reciprocating sliding tribological tests at 100°C showed that addition of 1 wt% of hairy NPsmore » into PAO led to significant reductions in coefficient of friction (up to ≈40%) and wear volume (up to ≈90%). The excellent lubricating properties of hairy NPs were further elucidated by the characterization of the tribofilm formed on the flat. These hairy NPs represent a new type of lubricating oil additives with high efficiency in friction and wear reduction.« less

The development of high performance lubricants has been driven by increasingly growing industrial demands and environmental concerns. Here we demonstrate oil-soluble polymer brush-grafted inorganic nanoparticles (hairy NPs) as highly effective lubricant additives for friction and wear reduction. A series of oil-miscible poly(lauryl methacrylate) brush-grafted silica and titania NPs were synthesized by surface-initiated atom transfer radical polymerization. These hairy NPs showed exceptional stability in polyalphaolefin (PAO) base oil; no change in transparency was observed after being kept at -20, 22, and 100 °C for at least 55 days. High contact stress ball-on-flat reciprocating sliding tribological tests at 100 °C showed thatmore » addition of 1 wt% of hairy NPs into PAO led to significant reductions in coefficient of friction (up to ~ 40%) and wear volume (up to ~ 90%). The excellent lubricating properties of hairy NPs were further elucidated by the characterization of the tribofilm formed on the flat. These hairy NPs represent a new type of lubricating oil additives with high efficiency in friction and wear reduction.« less