In this present investigation, the mechanical properties of industrial drawn copper wires have been studied by tensile tests. The effect of prior heat treatments at 500°C on the drawn wires behavior was the main goal of this investigation. We have found that the mechanical behavior of drawn wires depends strongly on those treatments. SEM observations of the wire cross section after tensile tests have shown that the mechanism of rupture was mainly controlled by the void formation.

Novel rose-like three-dimensional Sn(HPO{sub 4}){sub 2}.H{sub 2}O nanostructures self-assembled by tightly stacked nanopetals were successfully synthesized by a simple cetyltrimethylammonium bromide (CTAB)/water/cyclohexane/n-pentanol microemulsion system under solvothermal conditions for the first time. A series of compared experiments were carried out to investigate the factors that influence the morphology and size of the products. It was found that the molar ratio of water to CTAB and the concentration of SnCl{sub 4} aqueous solution play important roles in the formation of the rose-like nanostructures. A possible formation mechanism of rose-like nanostructures was proposed, which may be related to the crystal structure of Sn(HPO{submore » 4}){sub 2}.H{sub 2}O and the spherical micelles formed by the microemulsion. The electrochemical properties of Sn(HPO{sub 4}){sub 2}.H{sub 2}O were investigated through cyclic voltammetry (CV) measurements. X-ray powder diffraction (XRD), transmission electron microscopy (TEM), and field-emission scanning electron microscope (FE-SEM) were used to characterize the products.« less

Highly uniform, porous {beta}-Co(OH){sub 2} nanostructures with an appearance reminding of certain spherical corals were synthesized via a facile, one-step hydrothermal route using ethanol-water mixtures as solvents. The rough surfaces of the nanostructures consist of numerous randomly distributed, interconnecting nanoflakes, resulting in a network-like structure with many cavities. The coral-like product has a high Brunauer-Emmet-Teller specific surface area of 163 m{sup 2}/g. The diameter of the coral-like {beta}-Co(OH){sub 2} nanostructures is adjustable from 800 nm to 2 {mu}m. The effects of the ethanol/water ratio, the Co{sup 2+} concentration, the hydrothermal temperature, and the reaction time on the formation of themore » coral-like structures were investigated. Cyclic voltammetry and galvanostatic charge-discharge tests show that the {beta}-Co(OH){sub 2} possesses excellent capacitive properties. This is mainly attributed to the high porosity, which allows a deep penetration by electrolytes. - Abstract: Coral-like {beta}-Co(OH){sub 2} nanostructures were synthesized via a facile ethanol-assisted hydrothermal route. Their high porosity facilitates a deep penetration by electrolytes and thus contributes to the excellent capacitive properties.« less