In-situ neutron diffraction experiments were performed on room temperature compressed 14YWT nanostructured ferritic alloys at 1100°C and 1150°C to understand their thermally activated static recrystallization mechanisms. The existence of high density of Y-Ti-O rich nano-oxides (<5 nm) shift the recrystallization temperature up due to Zener pinning of the grain boundaries, making these materials attractive for high temperature applications. This study serves to quantify the texture evolution in-situ and understand the effect of particles on the recrystallization mechanisms in 14YWT alloys. We have shown, both experimentally and theoretically, that there is considerable recovery in the 20% compressed sample after 6.5 h annealing at 1100°C while recrystallization occurs within an hour of annealing at 1100°C and 1150°C in the 60% compressed samples. Moreover, the 60% compressed samples show {112}<110> and {112}<111> texture components during annealing, in contrast to the conventional recrystallization textures in body centered cubic alloys. Furthermore, nano-oxide size, shape, density and distribution are considerably different in unrecrystallized and abnormally grown grains. Transmission electron microscopy analysis shows that oxide particles having a size between 5 and 30 nm play a critical role for recrystallization mechanisms in 14YWT nanostructured ferritic alloys.

@article{osti_1422892,
title = {High temperature microstructural stability and recrystallization mechanisms in 14YWT alloys},
author = {Aydogan, E. and El-Atwani, O. and Takajo, S. and Vogel, S. C. and Maloy, S. A.},
abstractNote = {In-situ neutron diffraction experiments were performed on room temperature compressed 14YWT nanostructured ferritic alloys at 1100°C and 1150°C to understand their thermally activated static recrystallization mechanisms. The existence of high density of Y-Ti-O rich nano-oxides (<5 nm) shift the recrystallization temperature up due to Zener pinning of the grain boundaries, making these materials attractive for high temperature applications. This study serves to quantify the texture evolution in-situ and understand the effect of particles on the recrystallization mechanisms in 14YWT alloys. We have shown, both experimentally and theoretically, that there is considerable recovery in the 20% compressed sample after 6.5 h annealing at 1100°C while recrystallization occurs within an hour of annealing at 1100°C and 1150°C in the 60% compressed samples. Moreover, the 60% compressed samples show {112}<110> and {112}<111> texture components during annealing, in contrast to the conventional recrystallization textures in body centered cubic alloys. Furthermore, nano-oxide size, shape, density and distribution are considerably different in unrecrystallized and abnormally grown grains. Transmission electron microscopy analysis shows that oxide particles having a size between 5 and 30 nm play a critical role for recrystallization mechanisms in 14YWT nanostructured ferritic alloys.},
doi = {10.1016/j.actamat.2018.02.006},
journal = {Acta Materialia},
number = ,
volume = 148,
place = {United States},
year = {2018},
month = {2}
}

Dispersions of nanoscale precipitates in metallic alloys have been known to play a key role in strengthening, by increasing their strain hardenability and providing resistance to deformation. Although these phenomena have been extensively investigated in the last century, the traditional approaches employed in the past have not rendered an authoritative microstructural understanding in such materials. The effect of the precipitates’ inherent complex morphology and their 3D spatial distribution on evolution and deformation behavior have often been precluded. This study reports, for the first time, implementation of synchrotron-based hard X-ray nanotomography in Al–Cu alloys to measure kinetics of different nanoscale phasesmore » in 3D, and reveals insights behind some of the observed novel phase transformation reactions. The experimental results of the present study reconcile with coarsening models from the Lifshitz–Slyozov–Wagner theory to an unprecedented extent, thereby establishing a new paradigm for thermodynamic analysis of precipitate assemblies. Lastly, this study sheds light on the possibilities for establishing new theories for dislocation–particle interactions, based on the limitations of using the Orowan equation in estimating precipitation strengthening.« less

Dispersions of nanoscale precipitates in metallic alloys have been known to play a key role in strengthening, by increasing their strain hardenability and providing resistance to deformation. Although these phenomena have been extensively investigated in the last century, the traditional approaches employed in the past have not rendered an authoritative microstructural understanding in such materials. The effect of the precipitates’ inherent complex morphology and their 3D spatial distribution on evolution and deformation behavior have often been precluded. This study reports, for the first time, implementation of synchrotron-based hard X-ray nanotomography in Al–Cu alloys to measure kinetics of different nanoscale phasesmore » in 3D, and reveals insights behind some of the observed novel phase transformation reactions. The experimental results of the present study reconcile with coarsening models from the Lifshitz–Slyozov–Wagner theory to an unprecedented extent, thereby establishing a new paradigm for thermodynamic analysis of precipitate assemblies. Lastly, this study sheds light on the possibilities for establishing new theories for dislocation–particle interactions, based on the limitations of using the Orowan equation in estimating precipitation strengthening.« less

Here in this study, the high temperature compressive response of cast aluminum alloys 319 and RR350 is compared in light of their microstructures. The 319 alloy is widely used in thermally critical automotive applications and provides a baseline for comparison with the RR350 alloy, whose microstructural stability at high homologous temperatures was recently reported. Cylindrical compression samples from each alloy were tested at four temperatures up to 300 °C at a constant true strain rate that was varied over four orders of magnitude. Although both alloys are strengthened by metastable precipitates (nominally Al 2Cu) in the as-aged condition, their mechanicalmore » response diverges at temperatures greater than 250 °C as the strengthening precipitates evolve in the 319 alloy and retain their as-aged morphology in the RR350 alloy. Deformation mechanisms of each alloy are examined using microstructural analysis and empirical activation energy calculations. The stability of the θ' phase in the RR350 alloy leads to effective precipitation hardening at homologous temperatures up to 0.6 and an extensive regime of grain boundary controlled deformation.« less

In this paper, an extended stability alloy design strategy for multicomponent γ-γ' nickel-base alloys with near-zero lattice misfit and as low as possible interfacial energy was investigated by isothermal annealing of two experimental alloys at 900 °C for times up to 256 h. The coarsening behavior of the spherical γ' precipitates and the phase compositions determined by atom probe tomography were utilized to exploit a modified Lifshitz-Slyozov-Wagner relationship to estimate the interfacial energies. The estimated interfacial energies are much lower than predicted by a CALPHAD-based software as well as those typically reported for multicomponent γ-γ' nickel alloys. Finally, despite successfullymore » minimizing the interfacial energy and γ-γ' lattice misfit, these factors alone were not sufficient to impart high temperature extended stability through reduced coarsening kinetics.« less

Cr-stabilized nanostructured ferritic alloys (NFAs), dispersion strengthened by an ultra-high density of nanooxides, are attractive candidates for many nuclear energy applications due to their high-temperature strength, in-service stability and remarkable irradiation tolerance. However, typical NFA deformation processing paths lead to crystallographic texturing, formation of brittle microstructures and low toughness orientations, making fabricating components very difficult. In this paper, we characterize the dislocation-mediated deformation mechanisms that lead to the brittle texture component. The as-extruded bar is less brittle than the cross-rolled plate, which contains a large population of pre-existing cleavage microcracks. More generally, deformed ODS/NFAs are most often textured and havemore » anisotropic low toughness orientations, even absent microcracks. However, cross-rolling produces a very high volume fraction of a plate normal {001}<110>-texture component, which constitutes the brittle cleavage system in iron. Finally, microcracks propagate along {001} low angle deformation induced subgrain boundaries in <110> directions after nucleating by the Cottrell mechanism.« less