Abstract

Elastic properties of lead phosphomolybdate [PbO-1bMoO3-1bP2O5] glasses have been investigated using ultrasonic velocity measurements at 10MHz. The composition dependence of elastic moduli, Poisson's ratio and the Debye temperature are found to be consistent with a structural model proposed earlier. According to this model lead acts both as a network former and as a network modifier in different composition regimes. It is suggested that the incorporation of lead into the network is accompanied by the conversion of three-connected [POO3/2] tetrahedra into four-connected [PO4/2]+ tetrahedra in the network.