Standard shipping orders are shipped USPS Priority, signature may be required. Super Alloy 5 brazes aluminum at half the melting point of aluminum, with any torch: oxyacetylene, MAPP gas, natural gas, oxy-MAPP, or propane (parent metal MUST reach 600 degrees to flow rod. Oxyacetylene is required for large masses or thick aluminum--if you're unsure which torch you need, please email us before purchasing). The resulting bond is stronger than the parent metal (30,000 psi) and can be bent, drilled, anodized, machined, plated, tapped or threaded. Super Alloy 5 can be used to TIG weld all types of aluminum, and is especially effective with cast aluminum applications. Cast aluminum is a porous metal and can be difficult to weld without the proper tools. Super Alloy 5's powder flux chemically cleans cast aluminum, removes oil and impurities, and enables the welder to TIG weld aluminum without porosity or pinholes (using an oxyacetylene torch). Super Alloy 5 makes easy work of aluminum boat repair (using an oxyacetylene torch). ****************************** Note: An oxyacetylene torch is required for aluminum boats, cast aluminum, large aluminum masses, or diamond plate aluminum. If you're using a torch that will not heat the parent metal to 600°F, you're not using the product as direct...

Storage: placed in a ventilated and dry place, can be stored for a long time Size:50X0.16cm Quantity: 10/20/50PCS Material: Aluminum Color: Silver Melting Point: 647℃～658℃ Diameter: 1.6mm / 0.062" Length: 500mm / 19.7" Recommended for welding or brazing aluminum alloy: 1060, 1350, 3003, 3004, 3005, 5005, 5050, 6053, 6061, 6951, 7005, and cast alloys 710.0 and 711.0 Item Wight: Approx. 2.5g How to Use: Step 1: Clean and polishe the physical surface. Step 2: Heat the surface of the base material, until the temperature of the wire to the operating temperature of 380℃～400℃, so you can rely on the parent metal heat transfer welding wire to form welds, should not use the flame to burn wire. Step 3: When repairing thin aluminum, as long as the aluminum base metal heated to the appropriate working temperature, and then use the wire back and forth friction melting to form a weld, only with a metal brush melt welding wire to weld at the weld. Step 4: Use propane gas to weld s mall object, natural slow cooling after welding. NOTE: 1. The surface of the base metal must be clean. 2. The base metal temperature to reach 400 degrees, including the process of welding the base metal temperature should be maintained a...

Storage: placed in a ventilated and dry place, can be stored for a long time Size:50X0.2cm Quantity: 10/20/50PCS Material: Aluminum Color: Silver Melting Point: 647℃～658℃ Diameter: 2mm / 0.078" Length: 500mm / 19.7" Recommended for welding or brazing aluminum alloy: 1060, 1350, 3003, 3004, 3005, 5005, 5050, 6053, 6061, 6951, 7005, and cast alloys 710.0 and 711.0 Item Wight: Approx. 4g How to Use: Step 1: Clean and polishe the physical surface. Step 2: Heat the surface of the base material, until the temperature of the wire to the operating temperature of 380℃～400℃, so you can rely on the parent metal heat transfer welding wire to form welds, should not use the flame to burn wire. Step 3: When repairing thin aluminum, as long as the aluminum base metal heated to the appropriate working temperature, and then use the wire back and forth friction melting to form a weld, only with a metal brush melt welding wire to weld at the weld. Step 4: Use propane gas to weld s mall object, natural slow cooling after welding. NOTE: 1. The surface of the base metal must be clean. 2. The base metal temperature to reach 400 degrees, including the process of welding the base metal temperature should be maintained at 400℃, and the temperature can be high or low Pa...

SteelStik is a hand-mixable, steel-reinforced, non-rusting epoxy putty that quickly repairs or rebuilds anything made of metal. After mixing, it forms an industrial-strength polymer compound that can be molded into shapes or used to build up, patch and repair steel components. SteelStik sets in 3-5 minutes and after 60 minutes, can be drilled, tapped, machined, ground, filed and painted. SteelStik cures to a dark grey color, is rated at a tensile strength of 900 PSI and will withstand temperatures up to 300ºF.