Method of making an article, the method comprising coalescing a plurality of the glass particles. Examples of articles include kitchenware (e.g., plates), dental brackets, and reinforcing fibers, cutting tool inserts, abrasives, and structural components of gas engines, (e.g., valves and bearings).

Images(21)

Claims(77)

1. A method of making an article, the method comprising:

providing a substrate having an outer surface;

providing at least a glass having an outer surface, wherein the glass comprises at least two different metal oxides, wherein the glass has a Tg and Tx, and wherein the difference between the Tg and the Tx of the glass is at least 5K, the first glass comprising one of a REO-Al2O3—ZrO2, Y2O3—Al2O3—ZrO2, REO-Al2O3—ZrO2—SiO2, Y2O3—Al2O3—ZrO2—SiO2, REO-Al2O3, or Y2O3—Al2O3 composition, and the glass containing less than 20% by weight SiO2, less than 20% by weight B2O3, and less than 40% by weight P2O5;

heating the glass above the Tg such that at least a portion of the glass wets at least a portion of the outer surface of the substrate and provides an article comprising the glass attached to the at least a portion of the outer surface of the substrate, wherein the heating of the glass is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. sufficient to increase the rate of densification of the glass as compared to the same glass heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. is in direct contact with at least a portion of the outer surface of the glass.

2. The method according to claim 1 to increased the rate of densification of the glass is by a factor of at least 1.5.

3. The method according to claim 1, wherein, the heating of the glass is conducted in an atmosphere at a pressure of at least 1.25 atm.

4. The method according to claim 3, wherein the difference between the Tg and the Tx is at least 25K.

5. The method according to claim 4, wherein the glass has a T1, and wherein the ratio of the Tg to T1 is at least 0.5.

6. The method according to claim 5, wherein the glass comprises less than 40 percent by weight glass collectively SiO2, B2O3, and P2O5, based on the total weight of the glass.

7. The method according to claim 6, wherein the glass is a REO-Al2O3 glass.

8. The method according to claim 7, wherein the glass collectively comprises at least 80 percent by weight of the Al2O3 and REO, based on the total weight of the glass.

9. The method according to claim 6, wherein the glass is a REO-Al2O3—ZrO2 glass.

10. The method according to claim 9, wherein the glass collectively comprises at least 80 percent by weight of the Al2O3, REO, and ZrO2, based on the total weight of the glass.

11. The method according to claim 3 further comprises heat-treating the glass of the article to convert at least a portion of the glass to crystalline ceramic and provide glass-ceramic.

12. The method according to claim 1, wherein, the heating of the glass is conducted in an atmosphere at a pressure of at least 2 atm.

13. A method of making an article, the method comprising:

providing a substrate having an outer surface;

providing at least a plurality of particles comprising glass, the particles comprising glass having an outer surface, wherein the glass comprises at least two different metal oxides, wherein the glass has a Tg and Tx, and wherein the difference between the Tg and the Tx of the glass is at least 5K, the glass comprising REO-Al2O3—ZrO2, Y2O3—Al2O3—ZrO2, REO-Al2O3—Zr2—SiO2, Y2O3—Al2O3—ZrO2—SiO2, REO-Al2O3, or Y2O3—Al2O3 composition, and the glass containing less than 20% by weight SiO2, less than 20% by weight B2O3, and less than 40% by weight P2O5;

heating the glass above the Tg such that at least a portion of the glass of the plurality of particles wets at least a portion of the outer surface of the substrate and provides an article comprising the glass attached to the at least a portion of the outer surface of the substrate, wherein the heating of the glass is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. sufficient to increase the rate of densification of the glass as compared to the same glass heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. is in direct contact with at least a portion of the outer surface of at least a portion the particles comprising glass.

14. The method according to claim 13 to increased the rate of densification of the glass is by a factor of at least 1.5.

15. The method according to claim 14, wherein, the heating of the glass is conducted in an atmosphere at a pressure of at least 1.25 atm.

16. The method according to claim 15, wherein the difference between the Tg and the Tx is at least 25K.

17. The method according to claim 16, wherein the glass has a T1, and wherein the ratio of the Tg to T1 is at least 0.5.

18. The method according to claim 17, wherein the glass comprises less than 40 percent by weight collectively SiO2, B2O3, and P2O5, based on the total weight of the glass.

19. The method according to claim 18, wherein the glass is a REO-Al2O3 glass.

20. The method according to claim 19, wherein the glass collectively comprises at least 80 percent by weight of the Al2O3 and REO, based on the total weight of the glass.

21. The method according to claim 18, wherein the glass is a REO-Al2O3—ZrO2 glass.

22. The method according to claim 21, wherein the glass collectively comprises at least 80 percent by weight of the Al2O3, REO, and ZrO2, based on the total weight of the glass.

23. The method according to claim 15, further comprises heat-treating the glass of the article to convert at least a portion of the glass to crystalline ceramic and provide glass-ceramic.

24. The method according to claim 13, wherein, the heating of the glass is conducted in an atmosphere at a pressure of at least 2 atm.

25. A method of making an article, the method comprising:

providing at least a first glass and second glass each having an outer surface, wherein the first glass comprises at least two different metal oxides, wherein the first glass has a Tg1 and Tx1, and wherein the difference between the Tg1 and the Tx1 is at least 5K, the first glass comprising one of a REO-Al2O3—ZrO2, Y2O3—Al2O3—ZrO2, REO-Al2O3—Zr2—SiO2, Y2O3—Al2O3—ZrO2—SiO2, REO-Al2O3, or Y2O3—Al2O3 composition, and the first glass containing less than 20% by weight SiO2, less than 20% by weight B2O3, and less than 40% by weight P2O5;

heating the first and second glasses above at least Tg1 and at least the first glass coalescing with the second glass to provide the article, wherein the heating of at least the first and second glasses is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. sufficient to increase the rate of densification of the glass as compared to the same glass heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. is in direct contact with at least a portion of the outer surfaces of the first and second glasses.

26. The method according to claim 25 to increased the rate of densification of the first glass is by a factor of at least 1.5.

27. The method according to claim 25, wherein, the heating of at least the first and second glasses is conducted in an atmosphere at a pressure of at least 1.25 atm.

28. The method according to claim 27, wherein the difference between the Tg1 and the Tx1 is at least 25K.

29. The method according to claim 28, wherein the first glass has a T1, and wherein the ratio of the Tg1 to T11 is at least 0.5.

30. The method according to claim 29, wherein the first glass comprises less than 40 percent by weight collectively SiO2, B2O3, and P2O5, based on the total weight of the glass.

31. The method according to claim 30, wherein the first glass is a REO-Al2O3 glass.

32. The method according to claim 31, wherein the first glass collectively comprises at least 80 percent by weight of the Al2O3 and REO, based on the total weight of the glass.

33. The method according to claim 30, wherein the first glass is a REO-Al2O3—ZrO2 glass.

34. The method according to claim 33, wherein the first glass collectively comprises at least 80 percent by weight of the Al2O3, REO, and ZrO2, based on the total weight of the glass.

35. The method according to claim 27, further comprises heat-treating at least the first and second glasses of the article to convert at least a portion of the glass to crystalline ceramic and provide glass-ceramic.

36. The method according to claim 24, wherein, the heating of the first glass is conducted in an atmosphere at a pressure of at least 2 atm.

37. A method of making an article, the method comprising:

providing at least a first glass and second glass each having an outer surface, wherein the first glass comprises at least two different metal oxides, wherein the first glass has a Tg1 and Tx1, and wherein the difference between the Tg1 and the Tx1 is at least 5K, the first glass comprising one of a REO-Al2O3—ZrO2, Y2O3—Al2O3—ZrO2, REO-Al2O3—Zr2—SiO2, Y2O3—Al2O3—ZrO2—SiO2, REO-Al2O3, or Y2O3—Al2O3 composition, and the first glass containing less than 20% by weight SiO2, less than 20% by weight B2O3, and less than 40% by weight P2O5, and wherein the second glass comprises at least two different metal oxides, wherein the second glass has a Tg2 and Tx2, and wherein the difference between the Tg2 and the Tx2 is at least 5K, the second glass containing less than 20% by weight SiO2, less than 20% by weight B2O3, and less than 40% by weight P2O5;

heating at least the first and second glasses above the higher of Tg1 or Tg2 and coalescing the first and second glasses to provide the article, wherein the heating of at least the first and second glasses is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. sufficient to increase the rate of densification of the glass as compared to the same glasses heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. is in direct contact with at least a portion of the outer surfaces of the first and second glasses.

38. The method according to claim 37 to increased the rate of densification of the first glass is by a factor of at least 1.5.

39. The method according to claim 37, wherein, the heating of at least the first and second glasses is conducted in an atmosphere at a pressure of at least 1.25 atm.

40. The method according to claim 39, wherein the difference between each of Tg1 and Tx1 and Tg2 and Tx2 is at least 25K.

41. The method according to claim 40, wherein the ratio of each of Tg1 to Tx1 and Tg2 to Tx2 is at least 0.5.

42. The method according to claim 41, wherein each of the first and second glasses comprise less than 40 percent by weight collectively SiO2, B2O3, and P2O5, based on the total weight of the glass.

43. The method according to claim 42, wherein the first glass is a REO-Al2O3 glass.

44. The method according to claim 43, wherein the first glass collectively comprises at least 80 percent by weight of the Al2O3 and REO, based on the total weight of the glass.

45. The method according to claim 42, wherein the first glass is a REO-Al2O3—ZrO2 glass.

46. The method according to claim 45, wherein the first glass collectively comprises at least 80 percent by weight of the Al2O3, REO, and ZrO2, based on the total weight of the glass.

47. The method according to claim 40, wherein the first and second glasses have the same compositions.

48. The method according to claim 40, wherein the first and second glasses have different compositions.

49. The method according to claim 39, further comprising heat-treating the glass of the article to convert at least a portion of the glass to crystalline ceramic and provide glass-ceramic.

50. The method according to claim 37, wherein, the heating of at least the first and second glasses is conducted in an atmosphere at a pressure of at least 2 atm.

51. A method of making an article, the method comprising:

providing at least a first plurality of particles comprising glass, the particles comprising glass having an outer surface, wherein the glass comprises at least two different metal oxides, wherein the glass has a Tg and Tx, and wherein the difference between the Tg and the Tx of the glass is at least 5K, the glass comprising one of a REO-Al2O3—ZrO2, Y2O3—Al2O3—ZrO2, REO-Al2O3—Zr2—SiO2, Y2O3—Al2O3—ZrO2—SiO2, REO-Al2O3, or Y2O3—Al2O3 composition, and the glass containing less than 20% by weight SiO2, less than 20% by weight B2O3, and less than 40% by weight P2O5;

heating the glass above the Tg and coalescing at least a portion of the first plurality of particles to provide the article, wherein the heating of the glass is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. sufficient to increase the rate of densification of the glass as compared to the same glass heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. is in direct contact with at least a portion of the outer surface of at least a portion the particles comprising glass.

52. The method according to claim 51 to increased the rate of densification of the glass is by a factor of at least 1.5.

53. The method according to claim 51, wherein, the heating of the glass is conducted in an atmosphere at a pressure of at least 1.25 atm.

54. The method according to claim 53, wherein the difference between the Tg and the Tx is at least 25K.

55. The method according to claim 54, wherein the glass has a T1, and wherein the ratio of the Tg to T1 is at least 0.5.

56. The method according to claim 55, wherein the glass comprises less than 40 percent by weight collectively SiO2, B2O3, and P2O5, based on the total weight of the glass.

57. The method according to claim 56, wherein the glass is a REO-Al2O3 glass.

58. The method according to claim 57, wherein the glass collectively comprises at least 80 percent by weight of the Al2O3 and REO, based on the total weight of the glass.

59. The method according to claim 56, wherein the glass is a REO-Al2O3—ZrO2 glass.

60. The method according to claim 59, wherein the glass collectively comprises at least 80 percent by weight of the Al2O3, REO, and ZrO2, based on the total weight of the glass.

61. The method according to claim 53, further comprising heat-treating the glass of the article to convert at least a portion of the glass to crystalline ceramic and provide glass-ceramic.

62. The method according to claim 51, wherein the heating of the glass is conducted in an atmosphere at a pressure of at least 2 atm.

identifying a glass comprising at least two different metal oxides, wherein the class has a Tg and Tx, and wherein the difference between the Tg and the Tx of the class is at least 5K, the glass containing less than 20% by weight SiO2, less than 20% by weight B2O3, and less than 40% by weight P2O5;

providing at least the glass, wherein the glass has an outer surface:

providing a substrate having an outer surface; and

heating the glass above the Tg such that at least a portion of the glass wets at least a portion of the outer surface of the substrate and provides an article comprising the glass attached to the at least a portion of the outer surface of the substrate, wherein the heating of the glass is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. sufficient to increase the rate of densification of the glass as compared to the same glass heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. is in direct contact with at least a portion of the outer surface of the glass.

69. The method according to claim 68, further comprising heat-treating the glass of the article to convert at least a portion of the glass to crystalline ceramic and provide glass-ceramic.

70. A method of making an article, the method comprising:

identifying a glass comprising at least two different metal oxides, wherein the glass has a Tg and Tx, and wherein the difference between the Tg and the Tx of the glass is at least 5K, the glass containing less than 20% by weight SiO2, less than 20% by weight B2O3, and less than 40% by weight P2O5;

providing at least a plurality of particles comprising the glass, the particles comprising the glass having an outer surface;

providing a substrate having an outer surface; and

heating the glass above the Tg such that at least a portion of the glass of the plurality of particles wets at least a portion of the outer surface of the substrate and provides an article comprising the glass attached to the at least a portion of the outer surface of the substrate, wherein the heating of the glass is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. sufficient to increase the rate of densification of the glass as compared to the same glass heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. is in direct contact with at least a portion of the outer surface of at least a portion the particles comprising glass.

71. The method according to claim 70, further comprises heat-treating the glass of the article to convert at least a portion of the glass to crystalline ceramic and provide glass-ceramic.

72. A method of making an article, the method comprising:

identifying a first glass comprising at least two different metal oxides, wherein the first glass has as a Tg1 and Tx1, and wherein the difference between the Tg1 and the Tx1 is at least 5K, the first glass containing less than 20% by weight SiO2, less than 20% by weight B2O3, and less than 40% by weight P2O5;

providing at least the first glass and a second glass each having an outer surface; and

heating the first and second glasses above at least Tg1 and at least the first glass coalescing with the second glass to provide the article, wherein the heating of at least the first and second glasses is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. sufficient to increase the rate of densification of the glasses as compared to the same glasses heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. is in direct contact with at least a portion of the outer surfaces of the first and second glasses.

73. The method according to claim 72, further comprises heat-treating at least the first and second glasses of the article to convert at least a portion of the glass to crystalline ceramic and provide glass-ceramic.

74. A method of making an article, the method comprising:

identifying a first glass comprising at least two different metal oxides, wherein the first glass has a Tg1 and Tx1, and wherein the difference between the Tg1 and the Tx1 is at least 5K, the first glass containing less than 20% by weight SiO2, less than 20% weight B2O3, and less than 40% by weight P2O5, and wherein the second glass comprises at least two different metal oxides, wherein the second glass has a Tg2 and Tx2, and wherein the difference between the Tg2 and the Tx2 is at least 5K, the second glass containing less than 20% by weight SiO2, less than 20% by weight B2O3, and less than 40% by weight P2O5;

providing at least the first glass and a second glass each having an outer surface; and

heating at least the first and second glasses above the higher of Tg1 or Tg2 and coalescing the first and second glasses to provide the article, wherein the heating of at least the first and second classes is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. sufficient to increase the rate of densification of the glasses as compared to the same glasses heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. is in direct contact with at least a portion of the outer surfaces of the first and second glasses.

75. The method according to claim 74, further comprising heat-treating the glass of the article to convert at least a portion of the glass to crystalline ceramic and provide glass-ceramic.

76. A method of making an article, the method comprising:

identifying a class comprising at least two different metal oxides, wherein the glass has a Tg and Tx, and wherein the difference between the Tg and the Tx of the glass is at least 5K, the glass containing less than 20% by weight SiO2, less than 20% by weight B2O3, and less than 40% by weight P2O5;

providing at least a first plurality of particles comprising the glass, the particles comprising the class having an outer surface; and

heating the glass above the Tg and coalescing at least a portion of the first plurality of particles to provide the article, wherein the heating of the glass is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. sufficient to increase the rate of densification of the glass as compared to the same glass heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. is in direct contact with at least a portion of the outer surface of at least a portion the particles comprising glass.

77. The method according to claim 76, further comprising heat-treating the glass of the article to convert at least a portion of the glass to crystalline ceramic and provide glass-ceramic.

Description

BACKGROUND

A number of amorphous materials (e.g., glass) and glass-ceramic compositions are known. Some amorphous materials can be consolidated via coalescing to provide articles, including articles having complex shapes (see, e.g., PCT publication No. 03/011776, published Feb. 13, 2003).

Various pressure-assisted consolidation methods are known in the ceramic art, and include hot-pressing, die-extrusion, hot-isostatic pressing, sinter-forging and variations of thereof. These consolidation methods are generally assisted by application of external force either directly through the use of punches as in hot-pressing, die-extrusion and sinter-forging, or indirectly through gas pressurization of a sealed container as in hot-isostatic pressing. In the latter method, the material to be consolidated is placed in a container (e.g., a metal container) and evacuated and sealed from an atmosphere. The sealed material is mechanical pressed thereby isostatically pressurizing the container with gas and causing the container to shrink.

Some amorphous compositions can be heat-treated to form glass-ceramics. The glass-ceramics tend to be more temperature resistant than the glass from which they are formed.

It is desirable to provide articles, including articles having complex shapes, comprising amorphous and glass-ceramics materials.

SUMMARY OF THE INVENTION

The present invention provides a method of making articles from glass. Optionally, the articles may be a composite of two or more different glass compositions. In some embodiments, the glass is optionally heat-treated to at least partially crystallize the glass and provide a glass-ceramic.

One embodiment of the present invention provides a method of making an article, the method comprising:

providing at least a glass (i.e., at least one glass) (e.g., in the form of a sheet(s), particle(s) (including a microsphere(s), and fiber(s)) having an outer surface (wherein if the glass is in the form of a sheet(s), particle(s), and/or a fiber(s), etc., it is understood that there are outer surfaces), wherein the glass comprises at least two different metal oxides (i.e., the metal oxides do not have the same cation(s)), wherein the glass has a Tg and Tx, and wherein the difference between the Tg and the Tx of the glass is at least 5K (or even, at least 10K, at least 15K, at least 20K, at least 25K, at least 30K, or at least 35K), the glass containing less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, P2O5);

heating the glass above the Tg such that at least a portion of the glass wets at least a portion of the outer surface of the substrate and provides an article comprising the glass attached to the at least a portion of the outer surface of the substrate, wherein the heating of the glass is conducted in a gaseous atmosphere at a pressure greater than 1.1 atmosphere (atm.) (in some embodiments, at a pressure greater than 1.25 atm., 1.5 atm., 2 atm., 5 atm., or even greater than 10 atm.) sufficient to increase the rate of densification of the glass as compared to the same glass heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. (in some embodiments, at a pressure greater than 1.25 atm., 1.5 atm., 2 atm., 5 atm., or even greater than 10 atm.) is in direct contact with at least a portion of the outer surface of the glass. Optionally, the method can be practiced with a second, a third, or more, different glass, including glasses having, respectively, a Tg and Tx, and wherein the difference between the Tg and the Tx for at least one additional glass (in some embodiments, between each respective Tg and Tx) is at least 5K (or even, at least 10K, at least 15K, at least 20K, at least 25K, at least 30K, or at least 35K), one or more of the additional glasses optionally contain less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, P2O5). In some embodiments, the glass, or if more than one glass is used, at least one of the glasses, comprises less than 40 percent (in some embodiments, less than 35, 30, 25, 20, 15, 10, 5, or even 0) by weight glass collectively SiO2, B2O3, and P2O5, based on the total weight of the glass. In some embodiments, the increased rate of densification of the glass is by a factor of at least 1.1, 1.25, 1.5, 2, or even at least 3.

Another embodiment of the present invention provides a method of making an article, the method comprising:

providing at least a plurality of particles comprising glass (including glass particles), the particles comprising glass having an outer surface, wherein the glass comprises at least two different metal oxides, wherein the glass has a Tg and Tx, and wherein the difference between the Tg and the Tx of the glass is at least 5K or even, at least 10K, at least 15K, at least 20K, at least 25K, at least 30K, or at least 35K), the glass containing less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, P2O5);

heating the glass above the Tg such that at least a portion of the glass of the plurality of particles wets at least a portion of the outer surface of the substrate and provides an article comprising the glass attached to the at least a portion of the outer surface of the substrate, wherein the heating of the glass is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. (in some embodiments, at a pressure greater than 1.25 atm., 1.5 atm., 2 atm., 5 atm., or even greater than 10 atm.) sufficient to increase the rate of densification of the glass as compared to the same glass heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. (in some embodiments, at a pressure greater than 1.25 atm., 1.5 atm., 2 atm., 5 atm., or even greater than 10 atm.) is in direct contact with at least a portion of the outer surface of at least a portion the particles comprising glass. Optionally, the method can be practiced with a second, a third, or more, different pluralities of particles comprising glass (i.e., each plurality comprising different glasses), including glasses having, respectively, a Tg and Tx, and wherein the difference the Tg and the Tx for at least one additional glass (in some embodiments, between each respective Tg and Tx) Tx is at least 5K (or even, at least 10K, at least 15K, at least 20K, at least 25K, at least 30K, or at least 35K), one or more of the additional glasses optionally contain less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, P2O5). In some embodiments, the glass, or if more than one glass is used, at least one of the glasses, comprises less than 40 (in some embodiments, less than 35, 30, 25, 20, 15, 10, 5, or even 0) percent by weight glass collectively SiO2, B2O3, and P2O5, based on the total weight of the glass. In some embodiments, the increased rate of densification of the glass is by a factor of at least 1.1, 1.25, 1.5, 2, or even at least 3.

Another embodiment of the present invention provides a method of making an article, the method comprising:

providing at least a first glass and second glass (e.g., sheets, particles (including microspheres), and fibers) each having an outer surface, wherein the first glass comprises at least two different metal oxides, wherein the first glass has a Tg1 and Tx1, and wherein the difference between the Tg1 and the Tx1 is at least 5K (or even, at least 10K, at least 15K, at least 20K, at least 25K, at least 30K, or at least 35K), the first glass containing less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, P2O5);

heating the first and second glasses above at least Tg1 and at least the first glass coalescing with the second glass to provide the article, wherein the heating of the glass is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. (in some embodiments, at a pressure greater than 1.25 atm., 1.5 atm., 2 atm., 5 atm., or even greater than 10 atm.) sufficient to increase the rate of densification of the glass as compared to the same glass heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. (in some embodiments, at a pressure greater than 1.25 atm., 1.5 atm., 2 atm., 5 atm., or even greater than 10 atm.) is in direct contact with at least a portion of the outer surfaces of the first and second glasses. Optionally, the second glass has a Tg2 and Tx2, wherein the difference between Tg2 and Tx2 is at least 5K (or even, at least 10K, at least 15K, at least 20K, at least 25K, at least 30K, or at least 35K). Optionally, the second glass contains less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, P2O5). Optionally, the method can be practiced with a third, a fourth, glass, etc. including glasses having, respectively, a Tg and Tx, and wherein the difference between the Tg and the Tx for at least one additional glass (in some embodiments, between each respective Tg and Tx) is at least 5K (or even, at least 10K, at least 15K, at least 20K, at least 25K, at least 30K, or at least 35K), one or more of the additional glasses optionally contain less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, P2O5). The glasses may have the same composition, different composition, or combinations thereof. In some embodiments, at least one of the glasses comprise less than 40 (in some embodiments, less than 35, 30, 25, 20, 15, 10, 5, or even 0) percent by weight glass collectively SiO2, B2O3, and P2O5, based on the total weight of the glass. In some embodiments, the increased rate of densification of the glass is by a factor of at least 1.1, 1.25, 1.5, 2, or even at least 3.

Another embodiment of the present invention provides a method of making an article, the method comprising:

providing at least a first glass and second glass (e.g., sheets, particles (including microspheres), and fibers) each having an outer surface, wherein the first glass comprises at least two different metal oxides, wherein the first glass has a Tg1 and Tx1, and wherein the difference between the Tg1 and the Tx1 is at least 5K (or even, at least 10K, at least 15K, at least 20K, at least 25K, at least 30K, or at least 35K), the first glass containing less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, P2O5), and wherein the second glass comprises at least two different metal oxides, wherein the second glass has a Tg2 and Tx2, and wherein the difference between the Tg2 and the Tx2 is at least 5K, the second glass containing less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, P2O5);

heating the glasses above the higher of Tg1 or Tg2 and coalescing the first and second glasses to provide the article, wherein the heating of the glass is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. (in some embodiments, at a pressure greater than 1.25 atm., 1.5 atm., 2 atm., 5 atm., or even greater than 10 atm.) sufficient to increase the rate of densification of the glass as compared to the same glass heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. (in some embodiments, at a pressure greater than 1.25 atm., 1.5 atm., 2 atm., 5 atm., or even greater than 10 atm.) is in direct contact with at least a portion of the outer surfaces of the first and second glasses. Optionally, the method can be practices with a third, a fourth, glass, etc. including glasses having, respectively, a Tg and Tx, and wherein the difference between the Tg and the Tx for at least one additional glass (in some embodiments, between each respective Tg and Tx) is at least 5K (or even, at least 10K, at least 15K, at least 20K, at least 25K, at least 30K, or at least 35K), one or more of the additional glasses optionally contain less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, P2O5). The glasses may have the same composition, different composition, or combinations thereof. In some embodiments, at least one of the glasses comprise less than 40 (in some embodiments, less than 35, 30, 25, 20, 15, 10, 5, or even 0) percent by weight glass collectively SiO2, B2O3, and P2O5, based on the total weight of the glass. In some embodiments, the increased rate of densification of the glass is by a factor of at least 1.1, 1.25, 1.5, 2, or even at least 3.

Another embodiment of the present invention provides a method of making an article, the method comprising:

providing at least a first plurality of particles comprising glass (including glass particles), the particles comprising glass having an outer surface, wherein the glass comprises at least two different metal oxides, wherein the glass has a Tg and Tx, and wherein the difference between the Tg and the Tx of the glass is at least 5K (or even, at least 10K, at least 15K, at least 20K, at least 25K, at least 30K, or at least 35K), the glass containing less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, P2O5);

heating the glass above the Tg and coalescing at least a portion of the first plurality of particles to provide the article, wherein the heating of the glass is conducted in a gaseous atmosphere at a pressure greater than 1.1 atm. (in some embodiments, at a pressure greater than 1.25 atm., 1.5 atm., 2 atm., 5 atm., or even greater than 10 atm.) sufficient to increase the rate of densification of the glass as compared to the same glass heated in the same manner except the pressure during the later heating is conducted in an atmosphere at a pressure of 1.0 atm., and wherein the gaseous atmosphere at a pressure greater than 1.1 atm. (in some embodiments, at a pressure greater than 1.25 atm., 1.5 atm., 2 atm., 5 atm., or even greater than 10 atm.) is in direct contact with at least a portion of the outer surface of at least a portion the particles comprising glass. In some embodiments, the ceramic is glass. Optionally, the method can be practiced with a second, a third, or more, different pluralities of particles comprising glass (i.e., each plurality comprising different glasses), including glasses having, respectively, a Tg and Tx, and wherein the difference between the Tg and the Tx for at least one additional glass (in some embodiments, between each respective Tg and Tx) is at least 5K (or even, at least 10K, at least 15K, at least 20K, at least 25K, at least 30K, or at least 35K), one or more of the additional glasses optionally contain less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5% by weight, or even zero percent, by weight, P2O5). In some embodiments, the glass, or if more than one glass is used, at least one of the glasses, comprises less than 40 (in some embodiments, less than 35, 30, 25, 20, 15, 10, 5, or even 0) percent by weight glass collectively SiO2, B2O3, and P2O5, based on the total weight of the glass. In some embodiments, the increased rate of densification of the glass is by a factor of at least 1.1, 1.25, 1.5, 2, or even at least 3.

Desirably, the ratio of a Tg to T1 is at least 0.5. Examples of useful glass particles include those comprising REO-Al2O3—ZrO2, Y2O3—Al2O3—ZrO2, REO-Al2O3—ZrO2—SiO2, and Y2O3—Al2O3—ZrO2—SiO2 glasses. Other useful glasses may also include REO (i.e., rare earth oxide(s))-Al2O3 and Y2O3—Al2O3 glasses.

Embodiments of the method according to the present invention, including for certain ceramic compositions, allow for the formation of article shapes and sizes that were obtainable from conventional methods. Coalescence of the glass is typically enhanced if the glass is under pressure during heating. In one embodiment, a charge of glass (e.g., particles (including beads), fibers, etc.) is placed into a die and hot-pressing is performed at temperatures above glass transition where viscous flow of glass leads to coalescence into an article.

In this application:

“amorphous material” refers to material derived from a melt and/or a vapor phase that lacks any long range crystal structure as determined by X-ray diffraction and/or has an exothermic peak corresponding to the crystallization of the amorphous material as determined by a DTA (differential thermal analysis) as determined by the test described herein entitled “Differential Thermal Analysis”;

Further, it is understood herein that unless it is stated that a metal oxide (e.g., Al2O3, complex Al2O3.metal oxide, etc.) is crystalline, for example, in a glass-ceramic, it may be glass, crystalline, or portions glass and portions crystalline. For example, if a glass-ceramic comprises Al2O3 and ZrO2, the Al2O3 and ZrO2 may each be in a glass state, crystalline state, or portions in a glass state and portions in a crystalline state, or even as a reaction product with another metal oxide(s) (e.g., unless it is stated that, for example, Al2O3 is present as crystalline Al2O3 or a specific crystalline phase of Al2O3 (e.g., alpha Al2O3), it may be present as crystalline Al2O3 and/or as part of one or more crystalline complex Al2O3.metal oxides.

Optionally, certain glass articles made according to the present invention can be heat-treated to convert at least a portion of the glass to crystalline ceramic and provide glass-ceramic.

DETAILED DESCRIPTION

In general, glasses and ceramics comprising glass useful in practicing the method of the present invention can be made by heating (including in a flame) the appropriate metal oxide sources to form a melt, desirably a homogenous melt, and then rapidly cooling the melt to provide glass or ceramic comprising glass.

Examples of useful glass for carrying out the present invention include those comprising REO-Al2O3—ZrO2, Y2O3—Al2O3—ZrO2, REO-Al2O3—ZrO2—SiO2, and Y2O3—Al2O3—ZrO2—SiO2 glasses. Other useful glasses may also include REO (i.e., rare earth oxide(s))-Al2O3 and Y2O3—Al2O3 glasses. Useful glass formulations include those at or near a eutectic composition. In addition to the REO-Al2O3—ZrO2, Y2O3—Al2O3—ZrO2, REO-Al2O3—ZrO2—SiO2, and Y2O3—Al2O3—ZrO2—SiO2 compositions disclosed herein, other compositions, including eutectic compositions, will be apparent to those skilled in the art after reviewing the present disclosure. For example, phase diagrams depicting various compositions, including eutectic compositions, are known in the art.

Sources, including commercial sources, of (on a theoretical oxide basis) ZrO2 include zirconium oxide powders, zircon sand, zirconium, zirconium-containing ores, and zirconium salts (e.g., zirconium carbonates, acetates, nitrates, chlorides, hydroxides, and combinations thereof). In addition, or alternatively, the ZrO2 source may contain, or provide ZrO2, as well as other metal oxides such as hafnia. Sources, including commercial sources, of (on a theoretical oxide basis) HfO2 include hafnium oxide powders, hafnium, hafnium-containing ores, and hafnium salts. In addition, or alternatively, the HfO2 source may contain, or provide HfO2, as well as other metal oxides such as ZrO2.

Sources, including commercial sources, of BaO include barium oxide powders, barium-containing ores, barium salts, barium nitrates, and barium carbonates. The barium oxide source may contain, or only provide, barium oxide. Alternatively, the barium oxide source may contain, or provide barium oxide, as well as one or more metal oxides other than barium oxide (including materials of or containing complex barium oxide•other metal oxides).

Sources, including commercial sources, of CaO include calcium oxide powders and calcium-containing ores. The calcium oxide(s) source may contain, or only provide, calcium oxide. Alternatively, the calcium oxide source may contain, or provide calcium oxide, as well as one or more metal oxides other than calcium oxide (including materials of or containing complex calcium oxide other metal oxides).

Sources, including commercial sources, of SiO2 include silica powders, silicon metals, silicon-containing ores. The silicon oxide source may contain, or only provide, silicon oxide. Alternatively, the silicon oxide source may contain, or provide silicon oxide, as well as one or more metal oxides other than silicon oxide (including materials of or containing complex silicon oxide other metal oxides).

Sources, including commercial sources, of SrO include strontium oxide powders, strontium carbonates, and strontium-containing ores. The strontium oxide source may contain, or only provide, strontium oxide. Alternatively, the strontium oxide source may contain, or provide strontium oxide, as well as one or more metal oxides other than strontium oxide (including materials of or containing complex strontium oxide•other metal oxides).

Sources, including commercial sources, of TiO2 include titanium oxide powders, titanium metals and titanium-containing ores. The titanium oxide source may contain, or only provide, titanium oxide. Alternatively, the titanium oxide source may contain, or provide titanium oxide, as well as one or more metal oxides other than titanium oxide (including materials of or containing complex titanium oxide•other metal oxides).

Sources, including commercial sources, of (on a theoretical oxide basis) Y2O3 include yttrium oxide powders, yttrium, yttrium-containing ores, and yttrium salts (e.g., yttrium carbonates, nitrates, chlorides, hydroxides, and combinations thereof). The Y2O3 source may contain, or only provide, Y2O3. Alternatively, the Y2O3 source may contain, or provide Y2O3, as well as one or more metal oxides other than Y2O3 (including materials of or containing complex Y2O3.metal oxides (e.g., Y3Al5O12)).

Sources, including commercial sources, of (on a theoretical oxide basis) ZrO2 include zirconium oxide powders, zircon sand, zirconium, zirconium-containing ores, and zirconium salts (e.g., zirconium carbonates, acetates, nitrates, chlorides, hydroxides, and combinations thereof). In addition, or alternatively, the ZrO2 source may contain, or provide ZrO2, as well as other metal oxides such as hafnia. Sources, including commercial sources, of (on a theoretical oxide basis) HfO2 include hafnium oxide powders, hafnium, hafnium-containing ores, and hafnium salts. In addition, or alternatively, the HfO2 source may contain, or provide HfO2, as well as other metal oxides such as ZrO2.

Optionally, ceramics according to the present invention further comprise additional metal oxides beyond those needed for the general composition. The addition of certain metal oxides may alter the properties and/or the crystalline structure or microstructure of ceramics made according to the present invention, as well as the processing of the raw materials and intermediates in making the ceramic. For example, oxide additions such as MgO, CaO, Li2O, and Na2O have been observed to alter both the Tg and Tx of glass. Although not wishing to be bound by theory, it is believed that such additions influence glass formation. Further, for example, such oxide additions may decrease the melting temperature of the overall system (i.e., drive the system toward lower melting eutectic), and ease of glass-formation. Complex eutectics in multi component systems (quaternary, etc.) may result in better glass-forming ability. The viscosity of the liquid melt and viscosity of the glass in its' “working” range may also be affected by the addition of metal oxides beyond those needed for the general composition.

The inclusion of at least one of Nb2O5 or Ta2O5 glasses comprising Al2O3, REO, and at least one of ZrO2 or HfO2, can significantly influence the crystallization of the glasses (e.g., increases the rate of at least one of crystalline Zro2 or crystalline HfO2 formation from the glass (in some embodiments, by at least a factor of 1.5, 2, 2.5, or even at least 3 as compared to a comparative glass-ceramic made by heat-treating, in the same manner, the same glass free of Nb2O5 and Ta2O5 (i.e., the comparative glass is made and heat-treated the same manner as the glass comprising the Al2O3, REO, at least one of ZrO2 or HfO2, and Nb2O5 and/or Ta2O5 except no Nb2O5 or Ta2O5 was used to make the glass (i.e., such glass contains zero percent by weight Nb2O5 or Ta2O5, based on the total weight of the glass)))).

In some embodiments, the glass comprising at least 35 (in some embodiments, at least 40, 45, 50, 55, 60, 65, 70, or even at least 75; in some embodiments, in a range from 35 to 75, 40 to 75, 45 to 75, 50 to 75, 55 to 75, or even from 60 to 75) percent by weight Al2O3, based on the total weight of the glass, REO (e.g., Gd2O3, La2O3, and/or Nd2O3; in some embodiments, at least 0.5, 1, 2, 3, 4, 5, or even at least 10; in some embodiments, in a range from 0.5 to 70, 1 to 70, 5 to 70, 10 to 70, 0.5 to 50, 1 to 50, 5 to 50, 10 to 50, 0.5 to 40, 1 to 40, 5 to 40, 10 to 40, 0.5 to 30, 1 to 30, 5 to 30, 10 to 30, 0.5 to 25, 1 to 25, 5 to 25, or even from 10 to 25 percent by weight REO, based on the total weight of the glass), and ZrO2 (in some embodiments, ZrO2 and/or (including collectively) HfO2) (in some embodiments, at least 5, 10, 15, or even at least 20; in some embodiments, in a range from 5 to 30, 5 to 25, 10 to 25, 10 to 30, 15 to 30, 20 to 30, 15 to 25, or even from 15 to 20 percent by weight ZrO2 (in some embodiments, ZrO2 and/or (including collectively) HfO2), based on the total weight of the glass), and at least one of Nb2O5 or Ta2O5 (in some embodiments, at least 1, 2, 3, 4, 5, 10, 15, 20, or even at least 25; in some embodiments, in a range from 1 to 20, 5 to 20, 10 to 20, or even from 5 to 15 percent by weight at least one of Nb2O5 or Ta2O5, based on the total weight of the glass), wherein the glass contains not more than 10 (in some embodiments, not more than 9, 8, 7, 6, 5, 4, 3, 2, 1, 0.5, 0.1, or even zero) percent by weight collectively As2O3, B2O3, GeO2, P2O5, SiO2, TeO2, and V2O5, based on the total weight of the glass. For additional details regarding inclusion of Nb2O5 and/or Ta2O5, see, for example, copending application having U.S. Ser. No. 10/666,615, filed Sep. 18, 2003.

In some instances, it may be preferred to incorporate limited amounts of metal oxides selected from the group consisting of: Na2O, P2O5, SiO2, TeO2, V2O3, and combinations thereof. Sources, including commercial sources, include the oxides themselves, complex oxides, ores, carbonates, acetates, nitrates, chlorides, hydroxides, etc. These metal oxides may be added, for example, to modify a physical property of the resulting abrasive particles and/or improve processing. These metal oxides when used are typically are added from greater than 0 to 20% by weight, in some embodiments, greater than 0 to 5% by weight, or even greater than 0 to 2% by weight of the glass-ceramic depending, for example, upon the desired property.

For glasses that devitrify to form glass-ceramics, crystallization may also be affected by the additions of materials beyond those needed for the general composition. For example, certain metals, metal oxides (e.g., titanates and zirconates), and fluorides, for example, may act as nucleation agents resulting in beneficial heterogeneous nucleation of crystals. Also, addition of some oxides may change nature of metastable phases devitrifying from the glass upon reheating. In another aspect, for ceramics according to the present invention comprising crystalline ZrO2, it may be desirable to add metal oxides (e.g., Y2O3, TiO2, CaO, and MgO) that are known to stabilize tetragonal/cubic form of ZrO2.

In some embodiments, it may be advantageous for at least a portion of a metal oxide source (in some embodiments, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, or even at least 95 percent by weight) to be obtained by adding particulate, metallic material comprising at least one of a metal (e.g., Al, Ca, Cu, Cr, Fe, Li, Mg, Ni, Ag, Ti, Zr, and combinations thereof), M, that has a negative enthalpy of oxide formation or an alloy thereof to the melt, or otherwise metal them with the other raw materials. Although not wanting to be bound by theory, it is believed that the heat resulting from the exothermic reaction associated with the oxidation of the metal is beneficial in the formation of a homogeneous melt and resulting glass. For example, it is believed that the additional heat generated by the oxidation reaction within the raw material eliminates, minimizes, or at least reduces insufficient heat transfer, and hence facilitates formation and homogeneity of the melt, particularly when forming glass particles with x, y, and z dimensions over 150 micrometers. It is also believed that the availability of the additional heat aids in driving various chemical reactions and physical processes (e.g., densification, and spherodization) to completion. Further, it is believed for some embodiments, the presence of the additional heat generated by the oxidation reaction actually enables the formation of a melt, which otherwise is difficult or not practical due to high melting point of the materials. Further, the presence of the additional heat generated by the oxidation reaction actually enables the formation of glass that otherwise could not be made, or could not be made in the desired size range.

Embodiments of glass useful for practicing the present invention can be made, for example, by melting the metal oxide sources in any suitable furnace (e.g., an inductive heated furnace, a gas-fired furnace, or an electrical furnace), or, for example, in a plasma. The resulting melt is cooled (e.g., discharging the melt into a cooling media (e.g., high velocity air jets, liquids, metal plates (including chilled metal plates), metal rolls (including chilled metal rolls), metal balls (including chilled metal balls), and the like)).

In one method, glass useful for the present invention can be made utilizing flame fusion as disclosed, for example, in U.S. Pat. No. 6,254,981 (Castle). In this method, the metal oxide sources materials are fed (e.g., in the form of particles, sometimes referred to as “feed particles”) directly into a burner (e.g., a methane-air burner, an acetylene-oxygen burner, a hydrogen-oxygen burner, and like), and then quenched, for example, in water, cooling oil, air, or the like. Feed particles can be formed, for example, by grinding, agglomerating (e.g., spray-drying), melting, or sintering the metal oxide sources. The size of feed particles fed into the flame generally determines the size of the resulting glass particles/beads.

The present invention can be useful, for example, to obtain ceramic articles without limitations in dimensions. This was found to be possible through a coalescence step performed at temperatures above glass transition temperature. For instance, glass useful in carrying out the present invention undergoes glass transition (Tg) before significant crystallization occurs (Tx) as evidenced by the existence of endotherm (Tg) at lower temperature than exotherm (Tx). This allows for bulk fabrication of articles of any dimensions from relatively small pieces of glass. More specifically, for example, an article made according to the present invention, can be provided by heating, for example, glass particles (including beads and microspheres), fibers, etc. useful in carrying out the present invention above the Tg such that the glass particles, etc. coalesce to form a shape and cooling the coalesced shape to provide the article. In certain embodiments, heating is conducted at at least one temperature in a range of about 725° C. to about 1100° C.

For certain embodiments, coalescence may be conducted at temperatures significantly higher than crystallization temperature (Tx). Although not wanting to be bound by theory, it s is believed the relatively slow kinetics of crystallization allow access to higher temperatures for viscous flow. Surprisingly, I discovered coalescence is enhanced by methods according to the present invention. While not wishing to be bound by theory, it is believed that viscosity of glass decreases as the gas pressure increases causing increases in densification rates.

Heat-treatment can be carried out in any of a variety of ways, including those known in the art for heat-treating glass to convert at least a portion of the glass to crystalline ceramic and provide glass-ceramics. For example, heat-treatment can be conducted in batches, for example, using resistive, inductively or gas heated furnaces. Alternatively, for example, heat-treatment can be conducted continuously, for example, using rotary kilns. In the case of a rotary kiln, the material can be fed, for example, directly into a kiln operating at the elevated temperature. The time at the elevated temperature may range from a few seconds (in some embodiments, even less than 5 seconds) to a few minutes to several hours. The temperature may range anywhere from 900° C. to 1600° C., typically between 1200° C. to 1500° C. It is also within the scope of the present invention to perform some of the heat-treatment in batches (e.g., for the nucleation step) and another continuously (e.g., for the crystal growth step and to achieve the desired density). For the nucleation step, the temperature typically ranges between about 900° C. to about 1100° C., in some embodiments, in a range from about 925° C. to about 1050° C. Likewise for the density step, the temperature typically is in a range from about 1100° C. to about 1600° C., in some embodiments, in a range from about 1200° C. to about 1500° C. This heat treatment may occur, for example, by feeding the material directly into a furnace at the elevated temperature. Alternatively, for example, the material may be feed into a furnace at a much lower temperature (e.g., room temperature) and then heated to desired temperature at a predetermined heating rate. It is within the scope of the present invention to conduct heat-treatment in an atmosphere other than air. In some cases it might be even desirable to heat-treat in a reducing atmosphere(s). Also, for, example, it may be desirable to heat-treat under gas pressure as in, for example, hot-isostatic press, or in gas pressure furnace.

The particular selection of metal oxide sources and other additives for making ceramics according to the present invention typically takes into account, for example, the desired composition and microstructure of the resulting ceramics, the desired degree of crystallinity, if any, the desired physical properties (e.g., hardness or toughness) of the resulting ceramics, avoiding or minimizing the presence of undesirable impurities, the desired characteristics of the resulting ceramics, and/or the particular process (including equipment and any purification of the raw materials before and/or during fusion and/or solidification) being used to prepare the ceramics.

The metal oxide sources and other additives can be in any form suitable to the process and equipment utilized for the present invention. The raw materials can be melted and quenched using techniques and equipment known in the art for making oxide glasses and amorphous metals. Desirable cooling rates include those of 50K/s and greater. Cooling techniques known in the art include roll-chilling. Roll-chilling can be carried out, for example, by melting the metal oxide sources at a temperature typically 20-200° C. higher than the melting point, and cooling/quenching the melt by spraying it under high pressure (e.g., using a gas such as air, argon, nitrogen or the like) onto a high-speed rotary roll(s). Typically, the rolls are made of metal and are water cooled. Metal book molds may also be useful for cooling/quenching the melt.

Other techniques for forming melts, cooling/quenching melts, and/or otherwise forming glass include vapor phase quenching, plasma spraying, melt-extraction, and gas atomization. Vapor phase quenching can be carried out, for example, by sputtering, wherein the metal alloys or metal oxide sources are formed into a sputtering target(s) which are used. The target is fixed at a predetermined position in a sputtering apparatus, and a substrate(s) to be coated is placed at a position opposing the target(s). Typical pressures of 10−3 torr of oxygen gas and Ar gas, discharge is generated between the target(s) and a substrate(s), and Ar or oxygen ions collide against the target to start reaction sputtering, thereby depositing a film of composition on the substrate. For additional details regarding plasma spraying, see, for example, copending application having U.S. Ser. No. 10/211,640, filed Aug. 2, 2002.

Gas atomization involves melting feed particles to convert them to melt. A thin stream of such melt is atomized through contact with a disruptive air jet (i.e., the stream is divided into fine droplets). The resulting substantially discrete, generally ellipsoidal glass particles are then recovered. Melt-extraction can be carried out, for example, as disclosed in U.S. Pat. No. 5,605,870 (Strom-Olsen et al.). Container-less glass forming techniques utilizing laser beam heating as disclosed, for example, in PCT application having Publication No. WO 01/27046 A1, published Apr. 4, 2001, may also be useful in making glass according to the present invention.

The cooling rate is believed to affect the properties of the quenched glass. For instance, glass transition temperature, density and other properties of glass typically change with cooling rates.

Rapid cooling may also be conducted under controlled atmospheres, such as a reducing, neutral, or oxidizing environment to maintain and/or influence the desired oxidation states, etc. during cooling. The atmosphere can also influence glass formation by influencing crystallization kinetics from undercooled liquid. For example, larger undercooling of Al2O3 melts without crystallization has been reported in argon atmosphere as compared to that in air.

With regard to making particles, for example, the resulting ceramic (e.g., glass or ceramic comprising glass may be larger in size than that desired. The ceramic can be, and typically is, converted into smaller pieces using crushing and/or comminuting techniques known in the art, including roll crushing, canary milling, jaw crushing, hammer milling, ball milling, jet milling, impact crushing, and the like. In some instances, it is desired to have two or multiple crushing steps. For example, after the ceramic is formed (solidified), it may be in the form larger than desired. The first crushing step may involve crushing these relatively large masses or “chunks” to form smaller pieces. This crushing of these chunks may be accomplished with a hammer mill, impact crusher or jaw crusher. These smaller pieces may then be subsequently crushed to produce the desired particle size distribution. In order to produce the desired particle size distribution (sometimes referred to as grit size or grade), it may be necessary to perform multiple crushing steps. In general the crushing conditions are optimized to achieve the desired particle shape(s) and particle size distribution.

The shape of particles can depend, for example, on the composition of the glass, the geometry in which it was cooled, and the manner in which the glass is crushed (i.e., the crushing technique used), if the particles were formed by crushing.

Certain articles according to the present invention comprising glass can be heat-treated to increase or at least partially crystallize the glass to provide glass-ceramic. The heat-treatment of certain glasses to form glass-ceramics is well known in the art. The heating conditions to nucleate and grow glass-ceramics are known for a variety of glasses. Alternatively, one skilled in the art can determine the appropriate conditions from a Time-Temperature-Transformation (TTT) study of the glass using techniques known in the art. One skilled in the art, after reading the disclosure of the present invention should be able to provide TTT curves for glasses according to the present invention, determine the appropriate nucleation and/or crystal growth conditions to provide crystalline ceramics, glass-ceramics, and ceramic comprising glass according to the present invention.

Typically, glass-ceramics are stronger than the glasses from which they are formed. Hence, the strength of the material may be adjusted, for example, by the degree to which the glass is converted to crystalline ceramic phase(s). Alternatively, or in addition, the strength of the material may also be affected, for example, by the number of nucleation sites created, which may in turn be used to affect the number, and in turn the size of the crystals of the crystalline phase(s). For additional details regarding forming glass-ceramics, see, for example, Glass-Ceramics, P. W. McMillan, Academic Press, Inc., 2nd edition, 1979.

For example, during heat-treatment of a glass such as a glass comprising Al2O3, La2O3, and ZrO2 formation of phases such as La2Zr2O7, and, if ZrO2 is present, cubic/tetragonal ZrO2, in some cases monoclinic ZrO2, have been observed at temperatures above about 900° C. Although not wanting to be bound by theory, it is believed that zirconia-related phases are the first phases to nucleate from the glass. For example, of Al2O3, ReAlO3 (wherein Re is at least one rare earth cation), ReAl11O18, Re3Al5O12, Y3Al5O12, etc. phases are believed to generally occur at temperatures above about 925° C. Crystallite size during this nucleation step may be on the order of nanometers. For example, crystals as small as 10-15 nanometers have been observed. Longer heat-treating temperatures typically lead to the growth of crystallites and progression of crystallization. For at least some embodiments, heat-treatment at about 1300° C. for about 1 hour provides a full crystallization.

Certain ceramic articles made according to the present invention contain less than less than 20% by weight SiO2 (or even less than 15%, less than 10%, less than, 5% by weight, or even zero percent, by weight, SiO2), less than 20% by weight B2O3 (or even less than 15%, less than 10%, less than, 5% by weight, or even zero percent, by weight, B2O3), and less than 40% by weight P2O5 (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than, 5% by weight, or even zero percent, by weight, P2O5), based on the total metal oxide weight of the ceramic.

The microstructure or phase composition (glassy/crystalline) of a material can be determined in a number of ways. Various information can be obtained using optical microscopy, electron microscopy, differential thermal analysis (DTA), and x-ray diffraction (XRD), for example.

Using optical microscopy, glass is typically predominantly transparent due to the lack of light scattering centers such as crystal boundaries, while crystalline material shows a crystalline structure and is opaque due to light scattering effects.

Using DTA, the material is classified as amorphous if the corresponding DTA trace of the material contains an exothermic crystallization event (Tx). If the same trace also contains an endothermic event (Tg) at a temperature lower than Tx it is considered to consist of a glass phase. If the DTA trace of the material contains no such events, it is considered to contain crystalline phases.

Differential thermal analysis (DTA) can be conducted using the following method. DTA runs can be made (using an instrument such as that obtained from Netzsch Instruments, Selb, Germany under the trade designation “NETZSCH STA 409 DTA/TGA”) using a −140+170 mesh size fraction (i.e., the fraction collected between 105-micrometer opening size and 90-micrometer opening size screens). An amount of each screened sample (typically about 400 milligrams (mg)) is placed in a 100-microliter Al2O3 sample holder. Each sample is heated in static air at a rate of 10° C./minute from room temperature (about 25° C.) to 1100° C.

Using powder x-ray diffraction, XRD, (using an x-ray diffractometer such as that obtained under the trade designation “PHILLIPS XRG 3100” from Phillips, Mahwah, N.J., with copper K α1 radiation of 1.54050 Angstrom) the phases present in a material can be determined by comparing the peaks present in the XRD trace of the crystallized material to XRD patterns of crystalline phases provided in JCPDS (Joint Committee on Powder Diffraction Standards) databases, published by International Center for Diffraction Data. Furthermore, an XRD can be used qualitatively to determine types of phases. The presence of a broad diffused intensity peak is taken as an indication of the amorphous nature of a material. The existence of both a broad peak and well-defined peaks is taken as an indication of existence of crystalline matter within an amorphous matrix. The initially formed glass or ceramic (including glass prior to crystallization) may be larger in size than that desired. The glass or ceramic can be converted into smaller pieces using crushing and/or comminuting techniques known in the art, including roll crushing, canary milling, jaw crushing, hammer milling, ball milling, jet milling, impact crushing, and the like. In some instances, it is desired to have two or multiple crushing steps. For example, after the ceramic is formed (solidified), it may be in the form of larger than desired. The first crushing step may involve crushing these relatively large masses or “chunks” to form smaller pieces. This crushing of these chunks may be accomplished with a hammer mill, impact crusher or jaw crusher. These smaller pieces may then be subsequently crushed to produce the desired particle size distribution. In order to produce the desired particle size distribution (sometimes referred to as grit size or grade), it may be necessary to perform multiple crushing steps. In general the crushing conditions are optimized to achieve the desired particle shape(s) and particle size distribution. Resulting particles that are of the desired size may be recrushed if they are too large, or “recycled” and used as a raw material for re-melting if they are too small.

The shape of particles can depend, for example, on the composition and/or microstructure of the ceramic, the geometry in which it was cooled, and the manner in which the ceramic is crushed (i.e., the crushing technique used). In general, where a “blocky” shape is preferred, more energy may be employed to achieve this shape. Conversely, where a “sharp” shape is preferred, less energy may be employed to achieve this shape. The crushing technique may also be changed to achieve different desired shapes. For some particles an average aspect ratio ranging from 1:1 to 5:1 is typically desired, and in some embodiments, 1.25:1 to 3:1, or even 1.5:1 to 2.5:1.

Ceramic articles (including glass-ceramics) made according to the present invention may comprise at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 1 micrometer. In another aspect, ceramic articles (including glass-ceramics) made according to the present invention may comprise less than at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 0.5 micrometer. In another aspect, ceramics (including glass-ceramics) according to the present invention comprise less than at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 0.3 micrometer. In another aspect, ceramic articles (including glass-ceramics) made according to the present invention may comprise less than at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 0.15 micrometer. In another aspect, ceramic articles (including glass-ceramics) made according to the present invention may be free of at least one of eutectic microstructure features (i.e., is free of colonies and lamellar structure) or a non-cellular microstructure.

Certain articles made according to the present invention comprise glass comprising REO and Al2O3, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the REO and Al2O3, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising glass (e.g., at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume glass), the glass comprising REO and Al2O3, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the REO and Al2O3, based on the total weight of the glass.

Certain articles made according to the present invention comprise glass comprising REO and Al2O3, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the REO and Al2O3, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising glass (e.g., at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume glass), the glass comprising REO, Al2O3, and ZrO2, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the REO and Al2O3 and ZrO2, based on the total weight of the glass.

Additional details regarding ceramics comprising Al2O3, at least one of REO or Y2O3, and at least one of ZrO2 or HfO2, including making, using, and properties, can be found in application having U.S. Ser. Nos. 09/922,527, 09/922,528, and 09/922,530, filed Aug. 2, 2001, and U.S. Ser. Nos. 10/211,629, 10/211,598, 10/211,630, 10/211,639, 10/211,034, 10/211,044, 10/211,628, 10/211,640, and 10/211,684, filed Aug. 2, 2002.

Typically, and desirably, the (true) density, sometimes referred to as specific gravity, of ceramic according to the present invention is typically at least 70% of theoretical density. More desirably, the (true) density of ceramic according to the present invention is at least 75%, 80%, 85%, 90%, 95%, 96%, 97%, 98%, 99%, 99.5%, or 100% of theoretical density.

Examples of articles according of the present invention include kitchenware (e.g., plates), dental restorative materials, orthodontic brackets, ophthalmic lenses and other optical elements, IR-transmitting windows and coatings, reinforcing fibers, cutting tool inserts, abrasive materials, and structural components of gas engines, (e.g., valves and bearings). Other articles include those having a protective coating of ceramic on the outer surface of a body or other substrate. Further, for example, ceramic according to the present invention can be used as a matrix material. For example, ceramics according to the present invention can be used as a binder for ceramic materials and the like such as diamond, cubic-BN, Al2O3, ZrO2, Si3N4, and SiC. Glasses or glass-ceramics made according to present invention may also used as packaging for electronics and immobilizers of a nuclear waste. Examples of useful articles comprising such materials include composite substrate coatings, cutting tool inserts abrasive agglomerates, and bonded abrasive articles such as vitrified wheels. The use of ceramics according to the present invention can be used as binders may, for example, increase the modulus, heat resistance, wear resistance, and/or strength of the composite article.

Advantages and embodiments of this invention are further illustrated by the following non-limiting examples, but the particular materials and amounts thereof recited in these examples, as well as other conditions and details, should not be construed to unduly limit this invention. All parts and percentages are by weight unless otherwise indicated. Unless otherwise stated, all examples contained no significant amount of SiO2, B2O3, P2O5, GeO2, TeO2, As2O3, and V2O5.

EXAMPLESExamples 1-3

A polyethylene bottle was charged with 38.75 grams of alumina particles (obtained under the trade designation “APA-0.5” from Condea Vista, Tucson, Ariz.), 42.5 grams of lanthanum oxide particles (obtained from Molycorp, Inc., Mountain Pass, Calif.), 18.75 grams of yttria-stabilized zirconium oxide particles (obtained from Zirconia Sales, Inc. of Marietta, Ga. under the trade designation “HSY-3”) and 180 grams of DI water. About 200 grams of zirconia milling media (obtained from Tosoh Ceramics, Division of Bound Brook, N.J., under the trade designation “YTZ”) were added to the bottle, and the mixture was milled at 120 revolutions per minute (rpm) for 24 hours. After the milling, the milling media were removed and the slurry poured onto a glass (“PYREX”) pan where it was dried using a heat-gun. The resulting dried mixture was ground with a mortar and pestle and screened through a 70-mesh screen (212-micrometer opening size).

After grinding and screening, some of the −70 mesh screen particles were fed into a hydrogen/oxygen torch flame. The torch used to melt the particles, thereby generating melted glass beads, was a Bethlehem bench burner PM2D model B, obtained from Bethlehem Apparatus Co., Hellertown, Pa., delivering hydrogen and oxygen at the following rates. For the inner ring, the hydrogen flow rate was 8 standard liters per minute (SLPM) and the oxygen flow rate was 3 SLPM. For the outer ring, the hydrogen flow rate was 23 (SLPM) and the oxygen flow rate was 9.8 SLPM. The dried and sized particles were fed directly into the torch flame, where they were melted and transported to an inclined stainless steel surface (approximately 51 centimeters (cm) (20 inches) wide with the slope angle of 45 degrees) with cold water running over (approximately 8 liters/minute) the surface to form beads.

Examples 2 and 3 beads were prepared as described in Example 1, except the raw materials and the amounts of raw materials used are listed in Table 1, below. The sources of the raw materials used are listed in Table 2, below.

TABLE 1

Example

Weight percent of components

Batch amounts, g

2

Gd2O3: 45.32

Gd2O3: 22.66

Al2O3: 42.68

Al2O3: 21.34

ZrO2: 12

ZrO2: 6

3

La2O3: 48.12

La2O3: 24.06

Al2O3: 51.88

Al2O3: 25.94

TABLE 2

Raw Material

Source

Alumina particles (Al2O3)

Obtained from Condea Vista, Tucson, AZ

under the trade designation “APA-0.5”

Gadolinium oxide particles

Obtained from Molycorp, Inc.

(Gd2O3)

Various properties/characteristics of some of Examples 1-3 materials were measured as follows. Powder X-ray diffraction (using an X-ray diffractometer (obtained under the trade designation “PHILLIPS XRG 3100” from PHILLIPS, Mahwah, N.J.) with copper K α1 radiation of 1.54050 Angstrom) was used to qualitatively measure phases present in example materials. The presence of a broad diffused intensity peak was taken as an indication of the amorphous nature of a material. The existence of both a broad peak and well-defined peaks was taken as an indication of existence of crystalline matter within an amorphous matrix. Phases detected in various examples are reported in Table 3, below.

TABLE 3

Phases detected via

Hot-pressing

Example

X-ray diffraction

Color

Tg, ° C.

Tx, ° C.

temp, ° C.

1

Amorphous*

Clear

843

944

935

2

Amorphous*

Clear

862

932

935

3

Amorphous*

Clear

842

946

935

*glass, as the material has a Tg

For differential thermal analysis (DTA), a material was screened to retain glass beads within the 90-125 micrometer size range. DTA runs were made (using an instrument obtained from Netzsch Instruments, Selb, Germany under the trade designation “NETZSCH STA 409 DTA/TGA”). The amount of each screened sample placed in a 100-microliter Al2O3 sample holder was 400 milligrams. Each sample was heated in static air at a rate of 10° C./minute from room temperature (about 25° C.) to 1200° C. The glass transition temperatures (Tg) and crystallization transition temperatures (Tx) are reported in Table 3, above.

Examples 4-6 and Comparative Examples A-C

For each of Examples 4-6 and Comparative Examples A-C, about 4 grams of the glass beads of Examples 1-3, respectively, were placed in a graphite die and hot-pressed using uniaxial pressing apparatus (obtained under the trade designation “HP-50”, Thermal Technology Inc., Brea, Calif.). The hot-pressing was carried out in an nitrogen atmosphere and 48.3 megapascals (MPa) (7000 pounds per square inch (7 ksi)) pressure at 915° C. During hot-pressing of the Examples 4-6 glass beads, nitrogen was introduced at a pressure of 68.9 kPa (10 psi). The densification of the glass beads was monitored by the displacement control unit of the hot pressing equipment. Densification rates were correspondingly derived from slopes on densification-time plot.

Comparative Examples A-C were made as described for Examples 4-6, respectively, except in the atmosphere of flowing nitrogen (i.e., no overpressure). The relative densification rates for Examples 4-6 were determined dividing the Examples 4-6 densification rates by the Comparative Examples A-C densification rates, respectively. The results are reported in Table 4, below.

TABLE 4

Densification

Example

Comp. Ex

rate ratio

4

A

1.6

5

B

1.8

6

C

1.7

Various modifications and alterations of this invention will become apparent to those skilled in the art without departing from the scope and spirit of this invention, and it should be understood that this invention is not to be unduly limited to the illustrative embodiments set forth herein.

Thermally crystallizable mixture containing from about 40 to about 80 weight percent of electric arc furnace dust and from about 10 to about 40 weight percent of glass; electric arc dust contains an iron oxide; free of detectable toxic

Containing two or more crystal phases of different component, having non-regular shape and three-dimensional network, atleast one crystal phase is single crystal; crystal phase being oxides and complex oxides of two or more metals

Screen printing the desired shapes from a dimensionally stable dispersion of a precursor of the ceramic onto a surface, drying the screen printed shapes so obtained and firing them to generate the shaped ceramic articles.

The present invention provides a fused, crystalline eutectic material comprising eutectic of at least (i) crystalline, complex al2o3 y2o3, and (ii) at least one of aluminoxy-d or m-aluminoxy-d, wherein d is at least one of carbide or nitride