Attention all Knifemakers!.....Product dealers/retailers and/or knife makers/sharpeners/hobbyists (etc) are not permitted to insert business related text/videos/images (company/company name/product references) and/or links into your signature line, your homepage url (within the homepage profile box), within any posts, within your avatar, nor anywhere else on this site. Market research (such as asking questions regarding or referring to products/services that you make/offer for sale or posting pictures of finished projects) is prohibited. These features are reserved for supporting vendors and hobbyists.....Also, there is no need to announce to the community that you are a knifemaker unless you're trying to sell something so please refrain from sharing.
Thanks for your co-operation!

Help Support Kitchen Knife Forums by donating using the link above or becoming a Supporting Member.

Heat treat issue

When I heat treated the blade that I just made I heated to 1500º F. and soaked it for about 5 minutes after the oven returned to heat, and quenched in a slow quench oil from McMaster-Carr. The blade is single bevel, flat on one side. After quenching the blade took on a gentle curve over the whole length away from the side with the bevel. The thickest point on the spine is 3/32" thick.
My next blade is going to be ground on both sides, so am I likely to see a repeat of this warp in some way? Was the warp a result of insufficient soak time in the oven? And is there any way to correct this.
As it is, I don't see this as a problem for the things that I want this knife to do, I think that the curve might help when sliding down the side of a chicken carcass, for instance, butt I will know better when I get around to boning the body of the chicken that I roasted last night.
Any insight or help would be very much appreciated!

Spike C
"The Buddha resides as comfortably in the circuits of a digital computer or the gears of a cycle transmission as he does at the top of a mountain."
Pirsig

Welcome to heat treating! Warping is common, I don't know of any good ways of preventing it, mostly you have to learn how to fix it. There are several methods for doing so. You might pick up tips on a site like bladeforums.com.

single bevels will aways trun on you in quench its a stress thing
and since you are using thin stock and its O1 it will harden all the way through. jsut shape the blade and HT it then grind the bevels. on a side note if you HT then grind a single bevel the stressed build form the other side and can make the blade take a bend also (no ffree lunch with single bevels )

Thanks, that is what I was afraid of! I may have been able to straighten it out during the quench as I have seen done, but I didn't have the chops to do that!
Next knife is double bevel, can I grind the bevels on that before HT?

Spike C
"The Buddha resides as comfortably in the circuits of a digital computer or the gears of a cycle transmission as he does at the top of a mountain."
Pirsig

Thanks, Devin. I have a ShopSmith 6X48 belt sander and belts ranging from 36 to 320 and pretty much everything in between. The machine has variable speeds. I did the grind on this first knife at the slowest speed, but I can speed it up as long as I don't over heat the edge, which is what I was afraid of doing.

Spike C
"The Buddha resides as comfortably in the circuits of a digital computer or the gears of a cycle transmission as he does at the top of a mountain."
Pirsig

single bevels will aways trun on you in quench its a stress thing
and since you are using thin stock and its O1 it will harden all the way through. jsut shape the blade and HT it then grind the bevels. on a side note if you HT then grind a single bevel the stressed build form the other side and can make the blade take a bend also (no ffree lunch with single bevels )

So what might happen if I grind a hollow into the flat side of the knife now? Is it likely to make the situation worse or better?
I stripped a chicken carcass with it last night and it worked a charm, so now it is just experimenting to see what happens!

Spike C
"The Buddha resides as comfortably in the circuits of a digital computer or the gears of a cycle transmission as he does at the top of a mountain."
Pirsig