Analysis of the microstructure of the stainless steels 16Cr15Ni3MoNb and 18Cr10NiTi, irradiated at temperatures where changes in phase stability occur due to radiation-induced segregation, shows that the stability of second-phase particles depends on the structure of particle-matrix interface.