New polysilane copolymers comprise recurring units of --Si(X)(Y)-- and Si(A)(B)--, Si(X)(Y) being different from Si(A)(B), whereinX and Y together have 1-13 carbon atoms, and X and Y each independently is hydrogen, alkyl, cycloalkyl, phenyl, alkylphenyl, or phenylalkyl, with the proviso that only one of X and Y contains a phenyl moiety, or together X and Y are an alkylene group forming a ring with the adjoining Si atom, and whereinA and B together have 3-13 carbon atoms, and A and B each independently is alkyl or cycloalkyl, with the proviso (a) that when one of A and B is ethyl, the other is not methyl or ethyl, and (b) that when one of A ad B is n-propyl and the other is methyl, X and Y are not both methyl.Corresponding homopolysilanes are also provided.Upon ultraviolet irradiation, they photodepolymerize to form volatile products. As a result, they represent a new class of photoresists which enable direct formation of a positive image eliminating the heretofore required development step.

Claim:

What is claimed is:

1. A method of photopatterning a positive image onto a substrate coated with a polysilane, comprising irradiating the coated substrate with actinic radiation forming a patternof said positive image on the substrate, whereby the portions of the polysilane coating on which said radiation impinges are photodepolymerized to form products which volatilize and whereby said substrate becomes uncoated in the pattern of said positiveimage,

wherein said polysilane is a homopolymer which is substantially free of low molecular weight oligomers or cyclic materials and which comprises recurring units of --Si(X)(Y)--, wherein X and Y together have 4 to 13 carbon atoms, and X and Y eachindependently is hydrogen, alkyl, cycloalkyl, substituted phenyl, 1- or 2-naphthyl, or phenylalkyl, or togehter X and Y are an alkylene group forming a ring with the adjoining Si atom, wherein X and Y groups which are not H can be substituted by one ofC.sub.1-6 -alkoxy, mono- or di(C.sub.1-3 -alkyl)amino, C.sub.2-6 -alkanoyl or the corresponding C.sub.2-3 -ketal thereof, C.sub.1-6 -alkyl, --NH.sub.2 or --OH; with the proviso that only one of X and Y can be a substituted phenyl, and wherein, as aresult of the selection of X and Y, said polysilane has sufficient photosensitivity to depolymerize upon exposure to actinic radiation, forming products which volatilize; or

wherein said polysilane is a copolymer comprising recurring units of --Si(X)(Y)--, and Si(A)(B)--, Si(X)(Y)-- being different from Si(A)(B)--,

wherein X and Y together have 1 to 13 carbon atoms, and X and Y each independently is hydrogen, alkyl, cycloalkyl, phenyl, alkylphenyl, or phenylalkyl, with the proviso that only one of X and Y contains a phenyl moiety, or together X and Y are analkylene group forming a ring with the adjoining Si atom,

and wherein A and B together have 3 to 13 carbon atoms, and A and B each independently is alkyl, 1- or 2-naphthyl, or cycloalkyl, wherein X, Y, A, or B groups which are not H can be substituted by one of C.sub.1-6 -alkoxy, mono- or di-(C.sub.1-3-alkyl)amino, C.sub.2-6 -alkanoyl or the corresponding C.sub.2-3 -ketal thereof, C.sub.1-6 -alkyl, --NH.sub.2, or --OH;

with the proviso (a) that when one of A and B is ethyl, the other is not methyl or ethyl, and (b) that when one of A and B is n-propyl and the other is methyl, X and Y are not both methyl,

wherein A and B are substituents imparting sufficient steric hindrance to the copolymer that it photodepolymerizes upon exposure to actinic radiation, and wherein X and Y are substituents of sufficiently low weight that the products of saidphotodepolymerization volatilize at the instantaneous temperature of the depolymerizing polymer during irradiation;

and wherein said substituents in homo- or copolymers are such that the polymer undergoes substantially no self-crosslinking upon exposure to actinic radiation.

2. A method of claim 1 wherein the temperature of the polysilane coating during the irradiation is about room temperature.

3. A method of claim 1 wherein the temperature of the polysilane coating during the irradiation is from about room temperature to about 230.degree. C.

4. A method of claim 1 wherein the actinic radiation is U.V. radiation of a wavelength of about 250 nm or shorter and is of an intensity such that the average temperature of the polysilane coating remains substantially unchanged duringirradiation.

5. A method of claim 3 wherein the actinic radiation is U.V. radiation of a wavelength of about 250 nm or shorter and is of an intensity sufficiently high to raise the instantaneous temperature of the depolymerizing polysilane duringirradiation to a level sufficient to volatilize the products of the photodepolymerization but insufficient to cause irreversible thermal effects in the remaining polysilane which is not depolymerized.

6. A method of claim 1 wherein the resolution of the photopatterned positive image is about 1-4 .mu.m.

7. The method of claim 1 wherein neither X nor Y in the copolymer is H.

8. A method of claim 1 wherein X and Y are both methyl and wherein one of A and B is methyl and the other is cyclohexyl.

9. A method of claim 1 wherein one of X and Y is methyl and the other is n-propyl, and one of A and B is methyl and the other is isopropyl.

10. A method of claim 1 wherein X and Y each is methyl, ethyl, or propyl, or X and Y together form pentamethylene; and wherein one of A and B is n-propyl, isopropyl, t-butyl, cyclohexyl, n-hexyl, or n-dodecyl and the other is methyl or ethyl.

11. A method of claim 1 wherein X and Y each is methyl, and one of A and B is cyclohexyl, n-hexyl or n-dodecyl; or wherein one of X and Y is methyl and the other is n-propyl, and one of A and B is methyl and the other is isopropyl.

12. A method of claim 1 wherein the substrate is one suitable for use in a microelectronic device.

13. A method of claim 1 further comprising, prior to said irradiation step, coating said substrate with said polysilane.

14. A radiative method of producing a positive image of a desired pattern in a surface of a substrate, comprising,

(a) coating the surface with a polysilane,

(b) photopatterning the polysilane coating with a positive image of said desired pattern according to the method of claim 1, the polysilane of step (a) above being that recited in claim 1, whereby the portions of the polysilane coating on whichsaid radiation impinges are photodepolymerized to form products which volatilize and whereby said substrate becomes uncoated in the pattern of said positive image,

(c) treating the thus-exposed surface areas to form the desired pattern in the substrate surface; and

(d) removing the polysilane remaining on the surface.

15. A method of claim 14 wherein step (d) is carried out by exposing the surface to actinic radiation effective to photodepolymerize and volatilize the remaining polysilane or solvent.

16. A method of claim 14 wherein step (d) is carried out by dissolving the remaining polysilane in a solvent.

Description:

BACKGROUND OF THE INVENTION

This invention relates to new photoresist materials which can be used to directly achieve a positive image of a desired pattern on a substrate and to methods for their use which eliminate the conventional developing step.

Printed circuit boards, ubiquitous components of modern electronic equipment, are manufactured by the millions using photoresists. Typically, the photoresist is a thin layer of a photoreactive monomer which polymerizes on exposure to light,changing from a soluble to an insoluble form. Like a photographic plate, the image is a negative one developed by solvent removal of the unexposed areas. This development step contributes a significant amount to the overall cost of printed circuitproduction. Its elimination could, therefore, reduce costs by a considerable amount.

There remains a need to provide photoresists which are simpler and easier to use and which have the properties desirable in the photopatterning process used, e.g., in the microelectronics industry. At the same time, it is desirable to extend therange of uses of the polysilanes into this area.

SUMMARY OF THE INVENTION

Accordingly, it is an object of this invention to provide new photoresist materials which can be used directly to form a positive image of a desired pattern on the surface of a substrate.

It is another object of this invention to provide such positive photoresist materials which are based on polysilanes.

It is also another object of this invention to provide such polysilanes and new uses therefor.

Upon further study of the specification and appended claims, further objects and advantages of this invention will become apparent to those skilled in the art.

These objects have been attained by providing polysilanes comprising recurring units of

wherein

X and Y together have 4-13 carbon atoms, and

X and Y each independently is hydrogen, alkyl, cycloalkyl or phenylalkyl, or together X and Y are an alkylene group forming a ring with the adjoining Si atom, with the proviso that only one of X and Y contains a phenylalkyl group.

These objects have also been attained by providing polysilane copolymers comprising recurring units of --Si(X)(Y)-- and --Si(A)(B)--, Si(X)(Y) being different from Si(A)(B), wherein

X and Y together have 1-13 carbon atoms, and

X and Y each independently is hydrogen, alkyl, cycloalkyl, phenyl, alkylphenyl, or phenylalkyl, with the proviso that only one of X and Y contains a phenyl moiety, or together X and Y are an alkylene group forming a ring with the adjoining Siatom,

and wherein

A and B together have 3-13 carbon atoms, and

A and B each independently is alkyl or cycloalkyl, with the proviso (a) that when one of A and B is ethyl, the other is not methyl or ethyl, and (b) that when one of A and B is n-propyl and the other is methyl, X and Y are not both methyl.

These objects have further been attained by providing a photofabrication method wherein X and Y each is methyl, and one of A and B is methyl and the other is cyclohexyl, n-hexyl or n-dodecyl; or wherein one of X and Y is methyl and the other isn-propyl, and one of A and B is methyl and the other is isopropyl.

These objects have been provided, in preferred aspects by providing homopolysilanes wherein X and Y each is methyl, ethyl, phenethyl, isopropyl, n-propyl, t-butyl, n-hexyl, or n-dodecyl, or X and Y together form a pentamethylene group; byproviding polysilane copolymers wherein X and Y each is methyl, ethyl, or propyl, or X and Y together form pentamethylene; and wherein one of A and B is n-propyl, isopropyl, t-butyl, cyclohexyl, n-hexyl, or n-dodecyl and the other is methyl or ethyl; byproviding polysilane copolymers wherein X and Y each is methyl, and one of A and B is cyclohexyl, n-hexyl or n-dodecyl; or wherein one of X and Y is methyl and the other is n-propyl, and one of A and B is methyl and the other is isopropyl; and byproviding such polysilanes and a corresponding photopatterning method whereby a high resolution of 1-4 .mu.m or higher is provided during the photoresist processing.

These objects have further been achieved by providing a corresponding process comprising coating a substrate, photopatterning it and removing the coating from the substrate in a photoresist-type process; they have further been attained byproviding compositions comprising the mentioned photoresist polysilanes along with other conventional ingredients used in photoresist processing and also by providing the products of such processes as well as the combination of substrates, typicallymicroelectronic substrates, and polysilane coatings.

DETAILED DISCUSSION

All of the polysilane polymers of this invention are useful for several purposes For example, these polysilanes can be formulated with conventional, usually commercially available, crosslinking agents. Such agents can be coated onto surfaces,articles, etc. to provide protective layers Furthermore, the polysilanes are useful in processes involving photopatterning, e.g., in conventional photolithography and photoresist applications. These include the patterning of decorative features on awide variety of substrates, low resolution patterning of preselected designs on such substrates and high resolution patterning of highly complex patterns thereon, e.g., those required in the microelectronics industry. A major advantage of this inventionfor all such uses is that the desired pattern is produced in a positive image as will be explained more fully below. This eliminates the costly and time consuming development step required in the prior art photopatterning techniques. The highresolution photopatterning processes are preferred in this invention; consequently, the following discussion will be framed primarily in terms appropriate for this use. However, this is not intended to limit the scope of this invention or to exclude theother uses of the polysilanes.

In general, for high resolution applications, the polysilane will have a high photosensitivity under actinic radiation resulting in photodepolymerization of the irradiated areas. The products of the photodepolymerization step must besufficiently volatile at the polysilane temperature so that the products vaporize, thereby exposing the underlying substrate. In addition, the polysilane must be formable into a film and must have a low crystallinity in film form. Otherwise, there willbe significant light scattering effects which will degrade resolution. Of course, the polysilane structure must be of a nature that the film does not crosslink under actinic radiation, preferably ultraviolet radiation. Various combinations ofsubstituents on the silicon-atom backbone of a polysilane molecule are effective to achieve these properties to varying degrees. Suitable polymers for any of the foregoing uses and having a desired combination of properties can be conventionallyprepared, perhaps with a few routine preliminary experiments using the guidelines discussed herein.

Polysilane homopolymers will have two substituents on each silicon atom, denoted as X and Y. Preferably, these substituents together will have 4-13 carbon atoms. Combinations of X and Y substituents having fewer than 4 carbon atoms in total tendto be highly crystalline and are not satisfactory for use in high resolution processes. However, these are included within the scope of this invention in methods which do not demand high resolution. For example, they can be successfully used in verylow resolution processes such as those wherein decorative effects are to be achieved on substrates. Light scattering due to a high crystallinity of a polymer can even be of advantage in such applications, e.g., in view of the interesting effects whichcan be produced thereby. Polysilanes wherein X and Y in combination have a total number of carbon atoms greater than 13 are also within the scope of this invention. However, such homopolymers will depolymerize to form relatively heavy fragmentsrequiring relatively high temperatures for volatilization. Applications wherein such high temperatures can be used, however, are within the scope of this invention; consequently, the corresponding polysilanes which decompose into fragments whichvolatilize only at such high temperatures, e.g., on the order of 200.degree. C. or higher, are contemplated as equivalents within the scope of this invention. Similarly, also within the scope of this invention are other substituents X and Y which arenot based upon hydrocarbon moieties, especially those bonded to Si atoms via C-atoms.

Typically, the substituents X and Y will be selected independently among hydrogen, alkyl, cycloalkyl or phenylalkyl groups. Together, X and Y can also form alkylene groups linking with the connecting silicon atom to form a ring. Polysilaneswherein neither X nor Y is hydrogen are preferred. Hydrogen atoms on the polymer chain cause a high tendency toward reaction with oxygen making the polymers very difficult to handle. However, where such constraints are not a problem, hydrogensubstituents are employable.

Suitable alkyl groups have 1-12 carbon atoms, e.g., include methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, t-butyl, n-pentyl and its isomers, n-hexyl and its isomers, n-heptyl and its isomers, n-octyl and its isomers, n-nonyland its isomers, n-decyl and its isomers, n-undecyl and its isomers, and n-dodecyl and its isomers. Similarly, suitable cycloalkyl groups have 3-12 carbon atoms and include all of the various possibilities derived from the corresponding alkyl groups,e.g., those mentioned above, including those cycloalkyl groups having alkyl substituents. Preferably, the cycloalkyl group is cyclopentyl, cyclohexyl, cycloheptyl, etc., most preferably cyclohexyl. Suitable phenylalkyl groups are those based on thementioned alkyl groups, e.g., the C.sub.1-6 -alkyl groups. The alkylene groups formed by X and Y together also encompass all of the various possibilities derived from the corresponding alkyl groups mentioned above, i.e., are of 2-12 carbon atoms,including those having alkyl substituents. As can be seen, the Si atoms can be bonded to primary, secondary or tertiary C-atoms.

The foregoing discussion of suitable groups is not meant to be precisely limiting on the number of carbon atoms possible. As discussed above, under appropriate circumstances and for suitable uses, moieties having a greater number of carbon atomswill be suitable and, consequently, are contemplated as equivalents within the scope of this invention.

The substituents X and Y are selected to provide the proper balance, at the polysilane temperature during irradiation, between photosensitivity to actinic radiation and volatility of the fragments which result from the photodepolymerization. That is, the substituents X and Y must be of sufficient bulkiness to provide significant steric hindrance which, it is believed, contributes toward destabilization of the polysilane. However, they must also be sufficiently lightweight to producesufficiently small fragments to be volatile at the instantaneous local temperature of the polymer during the irradiation period. As mentioned, selection of appropriate substituents for the intended end use can be achieved easily, perhaps with a fewroutine preliminary experiments, in accordance with this discussion.

For example, cyclohexyl-methyl homopolysilane has good photosensitivity toward depolymerization due to the presence of the cyclohexyl group. It undergoes only low ablation at room temperature but at elevated temperatures has good ablationproperties Homodi-n-hexyl polysilane undergoes photodecomposition but does not ablate well at room temperature; however, at elevated temperatures its ablation is increased, whereby good photopatterning can be achieved. The polymer does have considerablecrystallinity which limits resolution. The properties of homomethyl-n-dodecyl polysilane are very similar to those described for the di-n-hexyl homopolymer. Homomethylphenethyl polisilane does undergo photodepolymerization and will ablate attemperatures above room temperature.

Homopolymers based on X and Y moieties which are methyl and/or ethyl in each case tend to be highly crystalline, again limiting the achievable resolution. In addition since these substituents are relatively small, photosensitivity is not high. However, each of these polymers can be employed in one of the uses which places low demands on resolution, volatility, speed, etc. Some of these homopolymers which have been made include those wherein X and Y are both methyl (highly insoluble) andwherein one is methyl and the other is ethyl. Crystallinity is also observed for homopolymer films wherein one of X and Y is methyl and the other is isopropyl (much less crystalline than the dimethyl homopolymer). Homopolymers containing Si-arylmoieties tend to be too photoinsensitive to provide sufficient depolymerization under the influence of ultraviolet radiation, presumably because of regularities in the alignment of the pendant phenyl groups, i.e., due to low steric hindrance effects. For instance, homomethylphenylpolysilane is very photoinsensitive in the solid state throughout the ultraviolet region.

The foregoing discussion of typical homopolymers demonstrates the nature of size effects on both photosensitivity and volatility. Further guidance in selecting an appropriate homo- or co-polysilane for a given use can be obtained from routinestudies of a polysilane's photosensitivity in solution. However, there is no direct correlation with the photosensitivity of a corresponding film.

In various preferred aspects, the homopolymers of this invention have X and Y moieties which together have at least 5, 6, 7 or 8 carbon atoms and also which have a maximum of 12, 11, 10, or 9 carbon atoms. In general, it is preferred that eachof X and Y be selected among methyl, ethyl, phenethyl, isopropyl, n-propyl, t-butyl, n-hexyl and n-dodecyl.

It is preferred that the polysilane used in this invention be a copolymer of recurring units (--Si(X)(Y)--Si(A)(B)--)n. In this way, one set of units can be selected to appropriately tailor the photosensitivity of the polysilane towardsphotodepolymerization and the other can be used to appropriately tailor the volatility of the fragments which result. That is, one unit will be selected to be sufficiently bulky to provide sufficient steric hindrance that the polysilanephotodepolymerizes, while the other will be selected to be sufficiently lightweight that the resultant fragments volatilize at the temperature of the polysilane during actinic irradiation. Moreover, the copolymers are preferred because they have a lowertendency toward crystallinity.

In general, the entire discussion above regarding the structure of the homopolymers applies to the copolymers unless indicated otherwise.

In the following description of suitable polysilane copolymers, the moieties X and Y are used to define the volatile component. Preferably, this component is one in which both X and Y are methyl The suitability of employing dimethyl units will,of course, depend upon the nature of the A/B units used. The smaller the size of the substituents in the volatile unit, the greater is the tendency toward crystallization. This tendency will be exacerbated when the A/B moieties are also relativelysmall in size. However, in general, the volatile units can have X and Y moieties of a total number of carbon atoms in the range of 1-13. Even larger moieties can be employed under appropriate conditions as indicated above, primarily when highpolysilane temperatures are achieved during irradiation and/or when the A/B unit is of relatively small size. Consequently, X/Y moieties having a total number of carbon atoms greater than 13 are contemplated equivalents within the scope of thisinvention.

As mentioned above, it is preferred that neither X nor Y be hydrogen Suitable alkyl and cycloalkyl moieties include those mentioned above. These include the alkyl portions of the alkylphenyl and phenylalkyl moieties as long as the carbon atomlimitations are observed. The same alkylene groups formed by X and Y together in the homopolymers are employable in the copolymers.

The unit denoted as having A and B substituents is the photosensitivity contributor. Again, the stated total carbon atom range of 3-13 is generally appropriate. However, under some circumstances moieties having fewer than 3 or greater than 13carbon atoms could be successfully employed; consequently, they are contemplated as equivalents within the scope of this invention. Suitable alkyl and cycloalkyl groups are those described above. Typically, the photosensitivity contributor will have atleast one relatively bulky substituent such as isopropyl, t-butyl, n-hexyl, n-dodecyl, any of the branched and unbranched alkyl groups intermediate in C-number between the latter two alkyl groups, cyclohexyl, cyclopentyl, cycloheptyl, etc.

For example, the preferred copolysilane of this invention is one wherein both X and Y are methyl and wherein one of A and B is methyl and the other is cyclohexyl. It has a high photosensitivity to photodepolymerization and produces volatilefragments as discussed more in detail below. This polymer has a ratio of X/Y units to A/B units of 1/1. When the ratio of dimethyl units to methylcyclohexyl units is about 1/4, the resulting copolymer has good photosensitivity, but, due to theincreased fragment weight caused by the increased relative content of cyclohexyl groups, the copolymer does not ablate well at room temperature. Nevertheless, this copolysilane is useful within the scope of this invention, especially when higherpolysilane temperatures are involved during the irradiation period. The complementary copolymer wherein the ratio of dimethyl units to cyclohexylmethyl units is 4/1 has lower photosensitivity but produces depolymerization products which are volatile atlower temperatures. In addition, because of the increased content of methyl groups, the polymer has an increased crystallinity which lowers the achievable resolution. Nevertheless, the polymer is valuable for many of the less demanding uses discussedherein.

The copolymer of dimethyl units and isopropylmethyl units or t-butylmethyl units is highly crystalline. However, these polymers can be used within the broad scope of this invention in view of their inherent photosensitivity and the volatility ofthe depolymerization fragments. Also highly crystalline are copolymers of ethyl/methyl units with dimethyl units and of methyl/n-propyl units with dimethyl units. These copolymers similarly can be employed within the broad scope of the uses of thisinvention. The copolymer of phenylmethyl units with dimethyl crosslinks under the influence of ultraviolet radiation making its use within the scope of this invention problematic.

As noted above, the range of suitable carbon atom content for the X/Y moieties of this invention can preferably be defined as a minimum of 2,3,4,5, or 6 or as having a maximum of 12,11,10,9,8 or 7. Similarly, A and B together can have a totalpreferred carbon atom content of 4,5,6 or 7 or a preferred maximum carbon atom content of 12,11,10,9 or 8.

The molar ratio of the X/Y units to the A/B units is not critical. In general, this ratio is limited at the upper end (increasing volatility-unit content) by the tendency toward crystallization contributed by the relatively smaller size of the Xand Y moieties. Simlarly, as this ratio gets larger, the photosensitizing effect contributed by the A/B groups may become too small. At the lower end (increasing A/B content), the ratio is limited by a tendency of the depolymerization fragments toremain nonvolatile even at elevated temperatures. However, in most cases, a very broad range of suitable ratios will be useful and can be routinely selected for each polymer.

Similarly, the molecular weight of the polysilanes is also uncritical Typically, the number of monomer units in a polymer varies from 3 to 20,000 or 50,000. All chain lengths will be photosensitive as long as sufficiently short wavelengthactinic radiation is utilized, e.g., about 250 nm or shorter. Molecular weights up to 2,000,000 or more can be involved with no problems. In general, as the molecular weight increases, the maximum wavelength effective to cause photodepolymerizationwill also increase. Consequently, as the photodepolymerization process ensues, the maximum effective wavelength will decrease to shorter values, i.e., the ultraviolet energy necessary to continue the photodepolymerization process will increase. Forthis reason, actinic radiation well below the maximum effective wavelength at the beginning of a process will be employed. As mentioned, wavelengths less than about 250 nm will usually be effective for this purpose. Nevertheless, if desired,wavelengths throughout the ultraviolet range can be utilized in dependence upon the particular polymer employed in accordance with the foregoing.

Although U.V. radiation is preferred, actinic wavelengths in the visible range are also possible, as are higher energy radiations such as X-ray or gamma ray and charged particle beams, e.g., electron beams. A very wide variety of actinicradiation sources can be used, spanning a very broad range of low intensity devices to very high power, e.g., laser devices. The preferred mode uses laser irradiation, e.g., from a pulsed excimer laser, typically of an intensity of 1.times.10.sup.-6 to1 J/cm.sup.2, higher or lower values being employable depending on whether local heating is desired and on other factors discussed herein or obvious to skilled workers. Of course, irradiation with high power sources has the advantage that polysilanes ofrelatively lower photochemical sensitivity can be employed. These are more easily handled than are the more reactive polysilanes.

In general, the polymers will be photodepolymerized at about room temperature. That is, actinic radiation intensities will be selected to cause photodepolymerization quickly without significantly thermally affecting the remaining polysilane. However, where desirable, e.g., in order to increase the volatility of photodepolymerization products, increased polysilane temperatures can be used during actinic irradiation. The polysilane temperature can be increased by simple, conventional heatingof the substrate and/or the polysilane coating itself, e.g., by inductive, conductive or radiative means. It can also be increased by employing high energy, pulsed or continuous wave lasers or other high intensity sources which will raise theinstantaneous local temperature of the polysilane molecules undergoing photodepolymerization.

The volatile products of the depolymerization reactions are environmentally benign. In vacuo, the fragments are simple low molecular weight silylenes such as dimethyl silylene and higher homologues, in dependence upon the precise structure ofthe recurring units, or are simple subunits of the polymeric chain, i.e., typically monomers, dimers, trimers, tetramers, etc. In air, the products are the corresponding oxidized fragments, e.g., the corresponding low molecular weight siloxanes. Thesiloxanes are physiologically innocuous and pose essentially no risk to personnel. Similarly, they are noncorrosive and pose essentially no risk to equipment as long as routine conventional safeguards are employed, e.g., adequate ventilation isprovided. These are very important properties for the commercial utilizability of the polysilanes, e.g., in photofabrication processes.

Without intending to limit the scope of this invention in any way, it is believed that photodepolymerization of the polysilanes used in this invention occurs via chain scission at the silicon atoms having the most sterically hinderedsubstituents. UV absorption occurs via electronic transitions in the silicon atoms. The resultant high energy excited state is unstable and results in depolymerization producing the fragments discussed above. The resultant depolymerized area(substrate) is essentially completely flat, there being essentially no observable traces of polymer fragments.

It has been discovered that this depolymerization process is a highly efficient one, e.g., a quantum yield of about 6 has been measured for the depolymerization of (cyclohexylmethyl Si/dimethyl Si).sub.n. This compares very favorably withquantum yields of 0.1 to 0.4 for commercial photoresists. The high yield for this invention suggests a free radical mechanism in the unzipping of the chain, most probably, it is theorized, via the intermediacy of diradicals. Furthermore, thefluorescence quantum yield for the same polymer is about 0.6, indicating that 40% or less of the impinging photons actually result in an effective depolymerization absorption. On this basis alone, quantum yields improved by a factor of about 2 will beachieved by using polymers having decreased fluorescence yields, a parameter which can be readily measured for any candidate polymer. A further increase in quantum yield can be achieved by increasing the temperature of the polysilane since diradicalprocesses are generally observed to be strongly temperature activated. Overall, it can be seen that the photofabrication processes of this invention will proceed with heretofor unachievable efficiency.

The properties of the polysilanes used in this invention are excellent for the wide variety of photofabrication and other uses mentioned herein. As discussed, they have widely varying crytallinities in dependence upon the structure of themonomeric units incorporated. High crystallinity will be tolerable or even desired when attractive decorative effects are to be patterned in a substrate. For higher resolution imaging, of course, a very low or essentially zero crystallinity will bedesired, e.g., typically causing less than about 20% scattering of incident visible radiation and preferably much less.

The polysilanes of this invention also have high stability properties, e.g., mechanically, chemically and thermally. The mechanical stability of the polymers is retained when the polymers are coated onto a wide variety of substrates, includingquartz, glass, metals, e.g., silicon and other semiconductor substrates, ceramics, polymers, etc. The polysilanes adhere well to all such surfaces, without any special surface pretreatments. Mechanical stability as well as chemical stability is alsoretained after exposure to the common etchants employed in photofabrication processes, e.g., ferric chloride, stannous chloride, etc. The polymers have good thermal stability. For example, differential scanning calorimetry has revealed thecyclohexylmethyl/dimethyl copolymer to be thermally stable to 390.degree. C. Thermogravimetric methods have shown no weight loss for this polymer up to about 220.degree. C., and some weight loss (about 10%) only at about 325.degree. C. probably due tothe presence of lower molecular weight chains (oligomers). Consequently, this polymer will be employable in high temperature processing. Similar results are observed for the other polysilanes, precise results being routinely determinable in each case.

Another important requirement for certain photofabrication processes, e g., in the semiconductor industry, is a low content of trace metals, e.g., sodium cations derived from the preparative methods discussed below. Routine purificationprocedures and/or modifications of the preparative chemistry can readily achieve the necessarily low metal contamination concentrations, e.g., less than about 10 ppm or lower. Many other properties of the polysilane films of this invention are alsoexcellent for the intended purposes.

Because of the wide variety of structural combinations available in the polysilanes of this invention, many of these properties can be fine tuned for an intended end use. This is especially the case for the polysilane copolymers, which provideat least two basic monomeric units for structural variation. The copolymers, of course, can comprise more than two basic units, i.e., the copolymer can comprise not only one volatility-contributing unit and one photosensitivity-contributing unit butalso 3, 4 or more different recurring monomeric units. This provides a high tailorability of properties.

As mentioned above, this invention is also directed to the use of the polysilanes. All these polymers can be used for the conventional purpose of providing protective coatings on a wide variety of substrates. Such coatings can be conventionallyprepared by incorporating a conventional crosslinking agent in effective amounts into the polysilane coating. Upon UV irradiation, a crosslinked protective coating will result. They also can be used conventionally as impregnating agents forstrengthening ceramics, precursors for beta-SiC fibers, and as dopable semiconductors. See, e.g., J. Am. Chem. Soc., 103, 7352 (1981); J. Am. Ceram. Soc., 61, 504 (1978); and Chem. Lett., 551 (1976).

However, primarily, this invention is directed to the use of the polysilanes in photofabrication, e.g., in the application of positive image patterns onto substrate surfaces, that is as a new class of unique photoresists. The uniqueness isderived from the fact that upon exposure to a pattern of actinic radiation, the polysilanes depolymerize to directly expose the underlying surface in the same pattern. This eliminates the development step heretofor necessary in conventional photoresisttechnology.

In one use, the photoresists of this invention are applied to a substrate and then irradiated with actinic radiation to produce a decorative pattern. In such applications, crystallinity of the polysilane is often not a problem and can even be anadvantage since unique decorative patterns can be produced by the scattering of light by the crystal centers. More preferably, the photoresists of this invention are used n low resolution imaging where integrity of an irradiated pattern is required butline widths are relatively large, e.g., on the order of many tens or hundreds of micrometers. In this application, crystallinity is also often not a problem.

Most preferably, this invention is directed to high resolution imaging using the photoresists of this invention. Here, resolution of a few microns is necessary (e.g., about 2-10 .mu.m; VLSI applications) or even lower (ULSI applications).

For all the photofabrication techniques of this invention, the general method is to coat the desired substrate with a photoresist of this invention. The image of the desired pattern is then focused on the coating whereby those portions of theunderlying coating on which the actinic radiation impinges are depolymerized, exposing the underlying surface. The exposed surface is then treated as desired, whereupon the remaining photoresist is removed by flooding the entire surface with actinicradiation causing the entire photoresist to ablate. As can be seen, this general method not only eliminates the heretofor necessary development step, but also replaces the previous chemical stripping of the remaining photoresist by the much simplerphotolytic method. The stripping step can also be carried out using solvents if desired, e.g., those employable in the polymerization of the polysilanes (see below) or others in which the polymers are soluble (see e.g., Example 1 below).

The polymers of this invention can be coated onto any substrate using conventional means such as pouring, dipping, brushing, spreading, spraying, spin casting, etc. The polymers can be applied neat or dissolved in a compatible inert solvent suchas THF, chlorinated hydrocarbons, toluene, xylene, hexane, etc. The coatings can be dried at room temperature over a period of hours, e.g., 3-4 hours, or can be heated or sprayed to set at shorter times. Storage of the polymers is not a problem unlesslong times are involved whereupon conventional means to protect them from actinic radiation can be taken, e.g., they can be stored in foil-covered or otherwise light blocking vials.

The polysilanes can be applied in any appropriate thickness, e.g., from about 1 .mu.m to about 1 mil. The thickness will be chosen in accordance with the desired resolution, smaller thicknesses generally being employed when higher resolutionsare desired. For example, for a resolution of about 1 .mu.m, a thickness of about 1 .mu.m will suffice. Thickness is controlled conventionally, e.g., by varying concentration, the number of layers are deposited, etc.

Unlike many photoresists, the photoresists of this invention are usually applied without the copresence of photosensitizers. However, of course, if desired, e.g., if it is desired to use a particular light source to which the polysilanes per seare not sensitive, conventional photosensitizers can be employed in conventional amounts.

Irradiation times will be very short, e.g, on the order of seconds or much shorter in dependence upon the intensity of the actinic radiation source and layer thickness. As mentioned, the nature of the source is not critical, low power (e.g.,10.sup.-6 J/cm.sup.2 or lower) or high power (1 or more J/cm.sup.2) devices being employable such as continuous wave or pulse lasers or lamps. The optics associated with the actinic radiation are fully conventional Preferably, ultraviolet radiation isused, generally lower than 330 nm and preferably lower than 254 nm, e.g., using a KrF excimer laser at 248 nm.

A particularly preferred application of the photofabrication techniques of this invention is in the electronics industry in making printed circuit boards, computer chips, etc. However, the polysilanes may also be used for non silver-basedphotography since the quantum yields are so high. For example, in one method, a crosslinking agent will be included in the polysilane coating. Upon exposure to patterned actinic radiation, a photographic positive image will be preliminarily set in thecoating. Thereafter, by appropriate heating of the remaining polymer containing the conventional cross-linking agent, the positive image will be finally set therein. In a related application, the polysilane films of this invention can be used asinterlayer dielectrics, again by including in the layers conventional crosslinking agents. Upon exposure to patterned actinic radiation, the resultant positive image can be finally set in the dielectric layer by conventional heating of the remainingpolymer. This eliminates the now required additional steps required to achieve such a positive image in a dielectric layer in state-of-the-art microelectronic devices.

The polysilanes of this invention are prepared by processes which are essentially conventional. These are generally described in many of the references cited above. In essence, the corresponding monomeric halosilanes (preferably thedichlorosilanes) are polymerized in the presence of an alkali metal catalyst, preferably sodium, in an inert solvent such as toluene, preferably at elevated temperatures, e.g., 90.degree.-100.degree. C. under reflux. The solvent has a minor effect onthe resultant polymers via its influence on the nature of the end groups of the chains. It is desirable that the sodium be added to the reaction in a uniform manner. This results in a more homogeneous molecular weight distribution. The precise rate ofsodium addition is not critical. Molecular weight can also be controlled by addition of small amounts of monohalosilanes as chain terminators. All of the polysilanes can be prepared analogously to the methods described in the following examples. Alsosee the following which report some of the preparations which are a part of this invention; J. Poly. Sci., Polym. Lett. Ed., 21, 819 (1983); ibid, 823; and J. Poly. Sci., Polym. Chem. Ed., 22, 159 (1984); ibid, 225. As disclosed in the followingexamples and in all of the references mentioned herein, conventional fractionation and other treatments are used to further purify the initially obtained polysilanes, e.g., to eliminate low molecular weight oligomers or cyclic materials and, as well,residual alkali metal cations.

The starting material silanes, preferably the corresponding dichlorosilanes are mostly commercially available either as stock items or as specialty chemicals. All can be routinely prepared by conventional Grignard addition to chlorosilanes. Silanes other than halosilanes can also be used and are commercially available or readily preparable from known starting materials.

In certain less preferred aspects, this invention can exclude the following subclasses of polysilanes per se but not their use in accordance with the preferred methods of this invention. In one subclass, there are excluded homopolymers whereinX/Y are methyl/p-tolyl; in another, copolymers wherein X/Y are beta-phenethyl/methyl and A/B are cyclohexyl/methyl or wherein X/Y are p-tolyl/methyl and A/B are cyclohexyl/ethyl or wherein X/Y together form pentamethylene and A/B are cyclohexyl/methyl. In another, there are excluded homopolymers wherein X/Y are beta-phenethyl/methyl, or methyl/cyclohexyl, or methyl/phenyl, or methyl/n-hexyl or methyl/n-dodecyl or wherein X/Y together form pentamethylene. In yet another, there are excluded copolymerswherein X/Y are methyl/methyl and A/B are methyl/cyclohexyl, or wherein X/Y are methyl/methyl and A/B are methyl/n-hexyl.

Without further elaboration, it is believed that one skilled in the art can, using the preceding description, utilize thepresent invention to its fullest extent. The following preferred specific embodiments are, therefore, to be construed as merely illustrative, and not limitative of the remainder of the disclosure in any way whatsoever. In the following examples, alltemperatures are set forth uncorrected in degrees Celsius; unless otherwise indicated, all parts and percentages are by weight.

Purified cyclohexylmethyldichlorosilane (48.9 g, 0.248 mole) and purified dimethyldichlorosilane (32.0 g, 0 248 mole) are added to 500 ml of dry toluene in an oven dried, N.sub.2 -purged, 3-necked flask equipped with reflux condenser, N.sub.2inlet, stirring bar, and pressure equalizing dropping funnel. The toluene solution of monomers is heated to reflux and a mineral oil dispersion of sodium metal (62.74 g of 40% by weight dispersion, 1.091 g-atom) is added cautiously from the droppingfunnel at the most rapid and constant rate permitted by the highly exothermic reaction. Throughout the course of the synthesis and purification of the polymer, it is protected from light to prevent premature photodegradation. Reflux of the dark bluereaction mixture is continued for 4 hours after sodium addition is completed. Neat methanol is then added cautiously to the cooled reaction mixture until H.sub.2 evolution from the destruction of excess Na stops. A volume of saturated aqueous sodiumbicarbonate equal to the volume of the reaction mixture is added in a single portion and the resulting two-phase mixture stirred vigorously until the blue color is completely dissipated. After separation of the layers, the cloudy organic phase isfiltered through filter aid to remove small amounts of insoluble polymer. Removal of the toluene solvent from the filtrate at reduced pressure affords a yellow-brown viscous oil. Crude high molecular weight (cyclohexyl methyl Si/dimethyl Si).sub.n isprecipitated from this oil by addition of ten volumes of ethyl acetate. Filtration gives a slightly tacky polymer which is purified by one precipitation from toluene with ethyl acetate and two precipitations from tetrahydrofuran with methanol. Thisprocedure provides 5.56 g of pure white, flocculent (cyclohexyl methyl Si/dimethyl Si).sub.n. Gel permeation chromatography analysis of this material shows it to possess a trimodal molecular weight distribution (modes at 5000, 40000 and 300000 daltons). Spectral data consistent with the copolymer structure were obtained as follows: UV (nm): .lambda.max 304 (.epsilon.6400), .lambda..sub.max 223(.epsilon.3100); .sup.1 HNMR (relative to tetramethylsilane reference): .delta.1.3 (br. s, Si-CH.sub.3), 1.8and 2.3 (br. m., Si-cyclohexyl); IR (cast film) (cm.sup.-1): 2940, 2880, 1458, 1250, 833, 750, 728. The copolymer is soluble in chlorinated hydrocarbons, aromatic hydrocarbons, and tetrahydrofuran, moderately soluble in alkanes and cycloalkanes, andslightly soluble in ether, acetone, ethyl acetate, and isopropanol. It is essentially insoluble in water, methanol, and other highly polar organic solvents. Thermogravimetric analysis shows the material to suffer essentially no weight loss to220.degree. C., 10% at 325.degree. C., and 50% loss at 380.degree. C. Differential scanning calorimetry shows no detectable transitions (Tg or Tm) from -140.degree. C. to the strong decomposition exotherm at about 390.degree. C. Atomic absorptionanalysis indicated the above sample to contain 80 ppm Na by weight.

Depending on the thickness desired, a solution of the above copolymer in the 0.1-1% concentration (w/w) range in toluene is prepared and particulates removed by passing the solution through a 0.2 .mu.m membrane filter. The solution is thenapplied to the substrate (e.g., glass, quartz, silicon, aluminum, copper) and allowed to evaporate slowly while protected from light. Alternatively, films can be prepared by spin casting. Films of submicron thicknesses up to 1 mil or more can beprepared by these methods and possess excellent adherence to all of the above substrates.

EXAMPLE 3

Patterning of (Cyclohexyl Methyl Si/Dimethyl Si).sub.n Films

A 1 .mu.m thick film of the above polymer on metallic silicon is patterned with pulsed ultraviolet light from a KrF excimer laser (2480 .ANG. max, 10 .ANG. full width at half height) and energy levels of 10.sup.-6 J/cm.sup.2, using a quartzmask. Approximately a thousand 10 nanosecond pulses are sufficient to completely ablate a 1 .mu.m film in the exposed area. The polymer films have also been patterned successfully with a low intensity hand-held low pressure Hg lamp (2537 .ANG.) in lessthan 60 seconds.

EXAMPLE 4

Analogously to Example 1, homopolysilanes and copolysilanes having alkyl or aryl portions as described above but with substituents bonded thereto have been prepared, e.g., homopolysilanes of methyl/p-methoxyphenyl and others. Suitablesubstituents on the alkyl, cycloalkyl, alkylene or phenyl moieties include C.sub.1-6 -alkoxy, mono- or di(CC.sub.1-3 -alkyl)-amino, C.sub.2-6 -alkanoyl or the corresponding C.sub.2-3 -ketals, C.sub.1-6 -alkyl as mentioned above, NH.sub.2, and OH, e.g.,methoxy, ethoxy, etc., methylamino, ethylamino, etc., diethylamino, dimethylamino, etc., acetyl, propanoyl, etc., and the corresponding ethylene or propylene ketals, methyl, ethyl, etc., amino, hydroxy, etc. Generally, suitable alkyl portions of thesesubstituents are those mentioned above in conjunction with the X, Y, A and B moieties. Also prepared were polymers having naphthyl groups attached to the Si-backbone, e.g., .beta.-naphthyl/methyl homopolymer or 100 (phenyl/methyl)/l.beta.-naphthyl/methyl copolymer. .alpha.-naphthyl groups can also be used. The naphthyl groups can also be substituted as described. p-phenyl substitution is preferred. Usually, there is only one substituent per pendant group, but additionalsubstitution is contemplated as an equivalent.

The analogous preparation of these substituted or naphthyl-containing polymers is varied simply by employing the corresponding substituted or naphthyl-containing starting material halosilanes which are all conventionally preparable and/orcommercially available. In addition, where necessary or advisable, as will be readily recognized by skilled workers, groups such as alkanoyl can be conventionally protected during the polymerization, preferably with readily cleavable ketone protectivegroups. Amino and hydroxy groups can also be protected but this is usually not necessary.

The preceding examples can be repeated with similar success by substituting the generically or specifically described reactants and/or operating conditions of this invention for those used in the preceding examples.

From the foregoing description, one skilled in the art can easily ascertain the essential characteristics of this invention, and without departing from the spirit and scope thereof, can make various changes and modifications of the invention toadapt it to various usages and conditions.