Light emitting device

Title: Light emitting device.Abstract: A light emitting device including a substrate, a first conductive semiconductor layer on the substrate, an active layer on the first conductive semiconductor layer, a second conductive semiconductor layer on the active layer, and a reflective layer under the substrate and including a light reflection pattern configured to reflect light emitted by the active layer in directions away from the reflective layer. ...

BACKGROUND OF THE INVENTION

The present invention relates to a light emitting device and a method of manufacturing the same.

2. Discussion of the Background

A light emitting diode (LED) uses a compound semiconductor to convert an electric signal into light. Thus, light emitting devices use the LED or produce light such as in small handheld devices like calculators, digital watches, etc. However, the LEDs generally only output a small amount of light and thus are used only in small electronic devices.

SUMMARY

Accordingly, one object of the present invention is to address the above-noted and other problems of the related art.

Another object of the present invention is to provide a light emitting device with improved light emitting efficiency.

To achieve these and other advantages and in accordance with the purpose of the present invention, as embodied and broadly described herein, the present invention provides in one aspect a light emitting device including a substrate, a first conductive semiconductor layer on the substrate, an active layer on the first conductive semiconductor layer, a second conductive semiconductor layer on the active layer, and a reflective layer under the substrate and including a light reflection pattern configured to reflect light emitted by the active layer in directions away from the reflective layer.

In another aspect, the present invention provides a light emitting device including a substrate, a first conductive semiconductor layer on the substrate, an active layer on the first conductive semiconductor layer, a second conductive semiconductor layer on the active layer, a resin layer under the substrate, and a reflective layer under the resin layer and configured to reflect light emitted by the active layer in directions away from the reflective layer.

Further scope of applicability of the present invention will become apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and specific examples, while indicating preferred embodiments of the invention, are given by illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from this detailed description.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will become more fully understood from the detailed description given hereinbelow and the accompanying drawings, which are given by illustration only, and thus are not limitative of the present invention, and wherein:

FIG. 1 is a cross-sectional view illustrating a light emitting device according to a first embodiment of the present invention;

FIG. 2 is a cross-sectional view illustrating a light emitting device according to a second embodiment of the present invention;

FIG. 3 is a cross-sectional view illustrating a light emitting device according to a third embodiment of the present invention;

FIG. 4 is a cross-sectional view illustrating a light emitting device according to a fourth embodiment of the present invention;

FIG. 5 is a cross-sectional view illustrating a light emitting device according to a fifth embodiment of the present invention; and

FIG. 6 is a graph illustrating a light extraction efficiency of a light emitting device according to the embodiments of the present invention.

DETAILED DESCRIPTION

Reference will now be made in detail to the preferred embodiments of the present invention, examples of which are illustrated in the accompanying drawings.

FIG. 1 is a cross-sectional view illustrating a light emitting device according to a first embodiment of the present invention. As shown, the light emitting device includes a substrate 10, a Un-doped GaN layer 20 formed on the substrate 10, a first conductive semiconductor layer 30 formed on the Un-doped GaN based-layer 20, an active layer 40 formed on the first conductive semiconductor 30, and a second conductive semiconductor layer 50 formed on the active layer 40.

The light emitting device also includes a first electrode layer 60 on the first conductive semiconductor layer 30 and a second electrode layer 70 on the second conductive semiconductor layer 50. In addition, the first conductive semiconductor layer 30 may be an n-type semiconductor and the second conductive semiconductor layer 50 may be a p-type semiconductor layer and vice versa. Thus, the light emitting device emits light from the active layer 60 by being supplied with power through the electrodes 60 and 70.

In addition, in the embodiment shown in FIG. 1, the substrate 10 may be formed of at least one of sapphire (Al2O3), Si, SiC, GaAs, ZnO or MgO. A buffer layer with a stacked structure such as AlInN/GaN, InxGa1-xN/GaN, AlxInyGa1-x-yN/InxGa1-xN/GaN, etc., may also be formed between the substrate 10 and the Un-doped GaN layer 20. Further, the substrate 10 can be a growth substrate for growing the Un-doped GaN layer 20, the first conductive semiconductor layer 30, the active layer 40 and the second conductive semiconductor layer 50.

In addition, the Un-doped GaN based-layer 20 can be grown by injecting trimethyl gallium (TMGa) gas into a chamber together with nitrogen gas, hydrogen gas and ammonium gas. Also, the first conductive semiconductor layer 30 may be a nitride semiconductor layer into which a first conductive impurity ion is implanted. For example, the first conductive semiconductor layer 30 may be a semiconductor layer into which an n-type impurity ion is implanted. Further, the first conductive semiconductor layer 30 can be grown by injecting trimethyl gallium (TMGa) gas and silane (SiH4) gas including an n-type impurity (for example, Si) into the chamber together with hydrogen gas and ammonia gas.

In addition, the active layer 40 may be formed of a single quantum well structure, a multi-quantum well structure, a quantum-wire structure and a quantum dot structure. For example, the active layer 40 may be formed of a stacked structure of an InGaN well layer/GaN barrier layer.

Also, the second conductive semiconductor layer 50 may be a nitride semiconductor layer into which the second conductive impurity ion is implanted. For example, the second conductive semiconductor layer 50 may be a semiconductor layer into which a p-type impurity ion is implanted. The second conductive semiconductor layer 50 can be grown by injecting trimethyl gallium (TMGa) gas and bicetyl cyclo pentadienyl (EtCp2Mg) {Mg(C2H5C5H4)2} including p-type impurity (for example, Mg) into the chamber together with hydrogen gas and ammonia gas.

Further, the first embodiment of the present invention advantageously forms a reflective layer 80 under the substrate 10 and a light extraction pattern 51 on the upper surface of the second conductive semiconductor layer 50 to improve a light extraction efficiency in the light emitting device.

In more detail, the reflective layer 80 may be formed of at least one of titanium (Ti), chromium (Cr), nickel (Ni), aluminum (Al), platinum (Pt), gold (Au) or silver (Ag). Thus, the light emitted from the active layer 40 and that traveled in a direction towards the substrate is reflected by the reflective layer 80 and emitted upward from the light emitting device. Therefore, the light extraction efficiency of the light emitting device is improved.

In addition, the light extraction pattern 51 formed on the upper surface of the second conductive semiconductor layer 50 further increases the light emission efficiency of the device. That is, light that cannot be emitted to the outside due to a high refractive index of the second conductive semiconductor layer 50 is extracted to the outside via the light extraction pattern 51.

Further, in the embodiment shown in FIG. 1, the light extraction pattern 51 has a hemispherical shape. However, the pattern 51 can be formed in various other shapes of projections or grooves such as a cylindrical shape, a cone shape, a random shape, etc. In the embodiment shown in FIG. 1, the hemispherical shape of the patterns 51 preferably has a radius of 1.5 μm. In addition, the light extraction pattern 51 may be formed by selectively removing the second conductive semiconductor layer 50 or selectively growing the second conductive semiconductor layer 50.

Thus, as described above, the light emitting device in the first embodiment includes the reflective layer 80 under the substrate 10 and the light extraction pattern 51 on the second conductive semiconductor layer 50 such that light generated from the active layer 40 can be effectively extracted to the outside.

Next, FIG. 2 is a cross-sectional view illustrating a light emitting device according to a second embodiment of the present invention. Also, in describing the light emitting device according to the following additional embodiments, the same elements described in the first embodiment will not be repeated in detail.

Referring to FIG. 2, the light emitting device includes the substrate 10, the Un-doped GaN based-layer 20 formed on the substrate 10, the first conductive semiconductor layer 30 formed on the Un-doped GaN layer 20, the active layer 40 formed on the first conductive semiconductor layer 30, and the second conductive semiconductor layer 50 formed on the active layer 40. Further, the light emitting device includes the first electrode layer 60 on the first conductive semiconductor layer 30 and the second electrode layer 70 on the second conductive semiconductor layer 50.

Also, to improve the light extraction efficiency, the reflective layer 80 is formed under the substrate 10 and the light extraction pattern 51 is formed on the upper surface of the second conductive semiconductor layer 50. To further improve the light emission efficiency of the device, a light scattering pattern 81 is formed on the reflective layer 80. Also, in this embodiment, the light scattering pattern 81 is formed on the upper surface of the reflective layer 80. In addition, the scattering pattern 81 is illustrated as being formed in a hemispherical shape, but may be formed in various shapes of projections or grooves such as a cylindrical shape, a cone shape, a random shape, etc.

The light scattering pattern 81 selectively etches the lower surface of the substrate 10 to form the projections and grooves and may be almost naturally formed on the upper surface of the reflective layer 80 by forming the reflective layer 80 under the substrate 10. The light scattering pattern 81 may also be disposed on the same horizontal plane with the substrate 10.

Next, FIG. 3 is a cross-sectional view illustrating a light emitting device according to a third embodiment of the present invention. Referring to FIG. 3, the light emitting device includes the substrate 10, the Un-doped GaN layer 20 formed on the substrate 10, the first conductive semiconductor layer 30 formed on the Un-doped GaN layer 20, the active layer 40 formed on the first conductive semiconductor layer 30, and the second conductive semiconductor layer 50 formed on the active layer 40.

Further, the light emitting device includes the first electrode layer 60 on the first conductive semiconductor layer 30 and the second electrode layer 70 on the second conductive semiconductor layer 50. The reflective layer 80 is also formed under the substrate 10 and the light extraction pattern 51 is formed on the upper surface of the second conductive semiconductor layer 50. Further, a light scattering pattern 11 is formed on the substrate 10 to further improve the light emission efficiency of the device.

The light scattering pattern 11 is also formed on the upper surface of the substrate 10, and is illustrated as being formed in a hemispherical shape, but may be formed in various shapes of projections or grooves such as a cylindrical shape, a cone shape, a random shape, etc. In addition, the light scattering pattern 11 may be formed by selectively etching the upper surface of the substrate 10, and may be disposed on the same horizontal plane with the un-doped GaN layer 20.

Next, FIG. 4 is a cross-sectional view illustrating a light emitting device according to a fourth embodiment of the present invention. Referring to FIG. 4, the light emitting device includes the substrate 10, the un-doped GaN layer 20 formed on the substrate 10, the first conductive semiconductor layer 30 formed on the Un-doped GaN layer 20, the active layer 40 formed on the first conductive semiconductor layer 30, and the second conductive semiconductor layer 50 formed on the active layer 40.

Further, as shown, the light emitting device includes the first electrode layer 60 on the first conductive semiconductor layer 30, and the second electrode layer 70 on the second conductive semiconductor layer 50. Also, to further improve the light emission efficiency, the device also includes the reflective layer 80 having the light scattering pattern 81, the light extraction pattern 51 formed on the upper surface of the second conductive semiconductor layer 50, and the light scattering pattern 11 formed on the substrate 10.

Next, FIG. 5 is a cross-sectional view illustrating a light emitting device according to a fifth embodiment of the present invention. Referring to FIG. 5, the light emitting device includes the substrate 10, the Un-doped GaN layer 20 formed on the substrate 10, the first conductive semiconductor layer 30 formed on the Un-doped GaN layer 20, the active layer 40 formed on the first conductive semiconductor layer 30, and the second conductive semiconductor layer 50 formed on the active layer 40.

Further, the light emitting device includes the first electrode layer 60 on the first conductive semiconductor layer 30 and the second electrode layer 70 on the second conductive semiconductor layer 50. Also included is the reflective layer 80 having the light scattering pattern 81 formed under the substrate 10, the light extraction pattern 51 formed on the upper surface of the second conductive semiconductor layer 50, and the light scattering pattern 11 formed on the substrate 10.

However, the light emitting device according to the fifth embodiment includes a resin layer 90 such as an epoxy under the substrate 10 and disposes the reflective layer 80 having the light scattering pattern 81 under the resin layer 90. The resin layer 90 may be a material having a refractive index similar to the substrate 10. The resin layer 90 can also be processed easier than the substrate 10 such that the projections or grooves are formed in a desired form on the lower surface of the resin layer 90, making it possible to easily form the light scattering pattern 81. The light scattering pattern 81 is also disposed on the same horizontal plane with the resin layer 90.

Next, FIG. 6 is graph illustrating the light extraction efficiency for the light emitting device according to the embodiments of the present invention. As shown in FIG. 6, the light extraction efficiency of the light emitting device according to the second embodiment is higher than that of the light emitting device according to the first embodiment. That is, it can be seen that the second light extraction pattern 81 formed on the reflective layer 80 improves the light extraction efficiency.

Further, the light extraction efficiency of the light emitting device according to the third embodiment is higher than the light extraction efficiency of the light emitting device according to the first embodiment. Therefore, it can be seen that the third light extraction pattern 11 formed on the substrate 10 improves the light extraction efficiency.

Further, the light extraction efficiency of the light emitting device according to the fourth embodiment is higher than the light extraction efficiency of the light emitting device according to the first, second and third embodiments. Therefore, when the light scattering pattern 11 is formed on the substrate and the light scattering pattern 81 is formed on the reflective layer 80, it can be seen that the light extraction efficiency is maximized.

Also, in FIG. 6, the X axis indicates an interval between the light extraction patterns 51 formed on the second conductive semiconductor layer 50. Thus, it can be seen that the light extraction efficiency is changed according to the light extraction patterns 51. Meanwhile, at least one of the light extraction pattern 51, the light scattering pattern 81, or the light scattering pattern 11 may be formed in the light emitting device. For example, the light extraction pattern 51 and the light scattering pattern 11 may not be formed in the light emitting device and only the light scattering pattern 81 may be formed in the light emitting device.

Further, in the description of the above-embodiments of the present invention, when each layer (or film), an area, a pattern or structures are described to be formed “on” or “under” each layer (or film), the area, the pattern or the structures, each layer (or film), an area, a pattern or structures can be formed by being directly contacted to each layer (or film), the area, the pattern or the structures and the other layer (or film), other area, other pattern or other structures are additionally formed therebetween. Also, being “on” or “under” each layer is described based on the drawings.

Further, in the drawings, the thickness or size of each layer is exaggerated or schematically illustrated for the convenience and clarity of explanation. Also, the size of each constituent does not necessarily reflect its actual size.

Although embodiments have been described with reference to a number of illustrative embodiments thereof, it should be understood that numerous other modifications and embodiments can be devised by those skilled in the art that will fall within the spirit and scope of the principles of this disclosure. More particularly, various variations and modifications are possible in the component parts and/or arrangements of the subject combination arrangement within the scope of the disclosure, the drawings and the appended claims. In addition to variations and modifications in the component parts and/or arrangements, alternative uses will also be apparent to those skilled in the art.

You can also Monitor Keywords and Search for tracking patents relating to this Light emitting device patent application.
###

How KEYWORD MONITOR works... a FREEservice from FreshPatents1. Sign up (takes 30 seconds). 2. Fill in the keywords to be monitored. 3. Each week you receive an email with patent applications related to your keywords. Start now! - Receive info on patent apps like Light emitting device or other areas of interest.###

Data source: patent applications published in the public domain by the United States Patent and Trademark Office (USPTO). Information published here is for research/educational purposes only. FreshPatents is not affiliated with the USPTO, assignee companies, inventors, law firms or other assignees. Patent applications, documents and images may contain trademarks of the respective companies/authors. FreshPatents is not responsible for the accuracy, validity or otherwise contents of these public document patent application filings. When possible a complete PDF is provided, however, in some cases the presented document/images is an abstract or sampling of the full patent application for display purposes. FreshPatents.com Terms/Support -g2-0.1902