welding 50mm pipe (steam return line)

i have been replace aprox 18M of a steam return line. this line has minimul pressure as its nere the end of the line (open end)

it is going to be tig welded.
i am not a welder or a boiler maker. (im a plumber) i am at tafe (collage as you guys say) doing a welding couse and we have just finshed off tig in all positions (sheet only no pipe) i have welded a few bits of pipe to make a bull bar for my car.

i think this job will be a good job to help build up my skills in pipe welding. i have welded some threads on the end of 15mm stainless steel tube on a compressed air line ready to be used and they held the pressure fine.

so you guys think i should go ahead and do it? i know alot of you guys are coded welders and dont like seeing a newbi welding somthing that could case damage.
i my oppinion this is low pressure so its going to be more forgiving on stuff ups, with tig there realy isnt anything you can stuff up on only undercut. so there for its should be ok for me to give it ago.

i was going to prep the pipe with a V and used a 1.5mm gap and used a 2.4mm ER70S-2 for both runs. would probably need 2 runs i would think

i have been replace aprox 18M of a steam return line. this line has minimul pressure as its nere the end of the line (open end)

it is going to be tig welded.
i am not a welder or a boiler maker. (im a plumber) i am at tafe (collage as you guys say) doing a welding couse and we have just finshed off tig in all positions (sheet only no pipe) i have welded a few bits of pipe to make a bull bar for my car.

i think this job will be a good job to help build up my skills in pipe welding. i have welded some threads on the end of 15mm stainless steel tube on a compressed air line ready to be used and they held the pressure fine.

so you guys think i should go ahead and do it? i know alot of you guys are coded welders and dont like seeing a newbi welding somthing that could case damage.
i my oppinion this is low pressure so its going to be more forgiving on stuff ups, with tig there realy isnt anything you can stuff up on only undercut. so there for its should be ok for me to give it ago.

All I can say is that steam can kill and or severely burn you. In certain situations it can even blow up.

Just by reading your posts I am very skeptical of your welding skills.

I'm actually a very skilled welder owning my own business for 21 years now.

And guess what, I dont even consider welding hi pressure steam.

Theres more to welding steam pipe than just welding.

I have some friends that are pipe welders that have told me horror stories about guys welding steam pipe and things going wrong and an explosion in a steam line tunnel when some opened a valve to fast and the steam going into a cold pipe.

I dont remember all the details but I can say if you dont have an expert guiding you I'd highly recommend you leaving this job to an expert.

You may disregaurd my recommendation and get lucky that every thing worked when you leave but I can assure you, You wont get lucky to many more times.