C08F2410/05—Transitioning, i.e. transition from one catalyst to another with use of a deactivating agent

Abstract

The present invention relates to a process for the continuous transition between two different and compatible polymerisation catalysts.

Description

[0001]

The present invention relates to a process for the continuous transition between two different and compatible polymerisation catalysts.

[0002]

The present invention also relates to a process for the continuous transition between two different and compatible polymerisation catalysts and between either two ethylene or two propylene polymers.

[0003]

In particular, the present invention relates to a process for the continuous transition between two different and compatible polymerisation catalysts and between two ethylene copolymers containing a different comonomer.

[0004]

More particularly, the present invention relates to a process for the continuous transition in a gas phase fluidised bed reactor between two different and compatible polymerisation catalysts and between two ethylene copolymers containing a different comonomer.

[0005]

It is well known that polymerisation conditions can be adjusted to produce a wide variety of products. This is also true for the production of ethylene copolymers. It is not unusual that one reactor system can produce resins useful in injection moulding, blow moulding, rotomoulding applications, wire coating, piping and films. Fluidised bed technology can also be used to make a wide variety of polyolefin products, e.g., homopolymers and copolymers of polyethylene, polypropylene, C4-C12 alpha olefins; ethylene-propylene-diene monomer (EPDM), polybutadiene, polyisoprene, and other rubbers.

[0006]

However, generally, the polymer products made by a given reactor system use the same reactants but in different ratios and at different temperatures. Each of these polymer products can be made with a number of different resin properties, or grades. Each grade of polymer product has a narrow limit on its properties, e.g., density and melt index. Industrial reactors require time to adjust to the new conditions (e.g., temperature, reactant pressures, and reactant ratios) and produce material in the interim that is constantly changing but not within the properties (e.g., melt index and density) of either the old product or the new one. New products cannot be made instantaneously and require a quantifiable period of transiency in becoming adjusted to the new, desired conditions.

[0007]

Generally, industrial control systems for gas phase, fluidised bed polymerisation reactors are designed to permit the operators to control the reactor by allowing the operators to select a desired melt index and density. Correlations of these properties are usually well known by the operators and those in the art for the particular reactor design and catalyst used.

[0008]

The prior art has devised a number of methods to reduce the transient, off grade material. These methods typically involve some combination of adjusting the automatic flow/ratio controllers to a new value either at or above the ultimately desired value ("dial-in transition" and "overshoot"), removing the reactant gas entirely ("inventory blow down"), reducing the level of the catalyst ("low bed"), and adding a nonreactive gas ("nitrogen addition").

[0009]

DE 4,241,530 describes using a kill gas to stop a polymerization reaction, blowing the gas inventory for that reaction out of the reactor, and rebuilding a new gas inventory for a new product. This method reduces transition material. The cost associated with throwing away the old gas inventory and rebuilding a new inventory is very high for commercial transitions between closely related grades.

[0010]

The prior art also discloses additional discontinuous transition process, said process usually including a gas phase purge and the addition of catalyst killer compounds.

[0011]

McAuley et al. ("Optimal. Grade Transitions in a Gas Phase Polyethylene Reactor", AIChE J., Vol. 38, No. 10: 1992, pp. 1564-1576) discloses three manual, labour-intensive transition strategies for gas phase polyethylene reactors. The first is an adjustment to the controls to overshoot the melt index and density values. The hydrogen feed and co-monomer feeds are increased to meet the designated properties. The second is an increase in temperature and manipulation of the slow vent to move the melt index of the produced product. The third is a drop in the catalyst level while keeping the bed resin residence time at a constant value to reduce off grade production.

EP798318 claims a process for controlling a gas phase polymerization reaction in a reactor when changing from a first product made at a first set of conditions to a second product made at a second set of conditions, said process comprising the steps of:

(a) comparing the first product reaction temperature and the second product reaction temperature, change the product reaction temperature setpoint to the second product reaction temperature if said second product reaction temperature is lower than said first product reaction temperature,

(b) setting a melt index setpoint that is either 0-150% higher or 0-70% lower than the desired second product melt index value,

(c) setting a reaction temperature setpoint that is: 1-15°C above the desired second product reaction temperature if the second product melt index value is higher than the first product melt index value, or 1-15°C below the actual second product reaction temperature if the second product melt index is lower than the first product melt index,

(d) setting a product rate-limiting reactant partial pressure setpoint that is: 1-25 psig either below the first product rate-limiting reactant partial pressure if the second product melt index value is higher than the first product melt index value, or above the first product rate-limiting reactant partial pressure if the second product melt index value is lower than the first product melt index value;

(e) maintaining said melt index setpoint, temperature setpoint, and rate-limiting reactant partial pressure setpoint values until said polymerization product exhibits an average melt index and average product density with an acceptable range from the desired second product melt index value and second product density value;

(g) changing said product reaction temperature setpoint to a value that is: (i) 0-15°C above said desired second product reaction temperature if the second product melt index value is higher than the first product melt index value, or (ii) 0-15°C below said desired second product reaction temperature if the second product melt index value is lower than the first product melt index value;

(h) changing said rate-limiting partial pressure setpoint to a value that is: (i) 0-25 psig either below the desired second product rate-limiting partial pressure if the second melt index value is higher than the first melt index value, or (ii) 0-25 psig above the second product rate-limiting partial pressure if the second melt index value is lower than the first melt index value; and

(i) changing the reaction temperature setpoint and the rate-limiting reactant partial pressure setpoint values to the desired second product reaction temperature and second rate-limiting reactant partial pressure value when the reaction product exhibits an average melt index value within acceptable limits of the second product melt index value.

[0014]

EP798318 depicts in its figures 3-5 a flowchart of the process control. The initial steps are similar to figures 1-2 (which depict the EP798318) prior art methods, i.e. a transition including the lowering of the bed level. All the examples of EP798318 relate to transitions between ethylene copolymers having the same comonomer, i.e. hexene.

[0015]

EP1578808 relates to processes for transitioning among polymerization catalyst systems, preferably catalyst systems, which are incompatible with each other. In particular, it relates to processes for transitioning among olefin polymerization reactions utilizing Ziegler-Natta catalyst systems, metallocene catalyst systems and chromium-based catalyst systems.

[0016]

Again, this prior art includes inter alia the step of lowering the reactor bed during the transition; and the examples relate to transitions between ethylene copolymers having the same comonomer, i.e. hexene.

[0017]

Despite this wide variety of available schemes, the Applicants could not find in the prior art a satisfactory process for the transition between two different and compatible polymerisation catalysts; and also between two ethylene copolymers containing a different comonomer. It is therefore an object of the present invention to provide such process allowing to reduce the amount of off grade material produced during the transition, e.g. to provide a better control over potential hot spots and/or static in the reactor and thus reducing and/or eliminating the formation of agglomerates, lumps and/or sheets. Additional benefits provided by the present invention will be depicted in the description and example hereafter.

[0018]

The present invention provides a process for the transition T1 between an ethylene or a propylene polymerization process carried out in a polymerization reactor in the presence of a catalyst a1, ethylene E or propylene P and an optional olefin co-monomer A to produce an ethylene polymer or a propylene polymer P1 into an ethylene or a propylene polymerization process carried out in the same polymerization reactor in the presence of a catalyst a2, ethylene E or propylene P and the same optional olefin co-monomer A to produce an ethylene polymer or a propylene polymer P2 characterised in that

catalyst a1 and a2 are different and compatible;

catalyst a1 and catalyst a2 are both active and present in the reactor during at least part of the transition T1 from P1 to P2; and

the transition T1 is performed continuously.

[0019]

For the purpose of the present description and appended claims, the transition T1 is defined as the period between the steady state production of the polymer P1 and the steady state production of the polymer P2.

[0020]

According to the present invention, the transition T1 is operated between compatible catalysts. The term "compatible catalysts", as used herein, includes two or more catalysts having similar kinetics of termination and insertion of monomer and comonomer(s) and/or that do not detrimentally interact with each other. The term "compatible catalysts", as used herein, includes those that satisfy one or more of the following:

1) those catalysts that in each others presence reduce the activity of at least one of the catalysts by less than 50%, preferably less than 75%, more preferably less than 90%;

2) those catalysts such that under the same reactive conditions one of the catalysts does not produces polymers having a molecular weight more than two times higher than any other catalyst in the system; and

3) those catalysts that differ in comonomer incorporation or reactivity ratio under the same conditions by less than about 30%.

[0021]

The terms "catalysts" and "catalyst systems" are used interchangeably herein.

[0022]

For the avoidance of doubt, the present invention does not cover the transition T1 between identical catalysts (system); e.g. the present invention does not cover the transition between different batches of identical catalysts (systems).

[0023]

The transition T1 according to the present invention is performed continuously. For the purpose of the present invention and appended claims, a continuous transition must fulfil at least one of the following conditions:

1. the polymerisation production rate ("R"), defined as the amount of polymer produced by unit of time (e.g. tons/hour), must fulfil the following equation 0.55⁢x RP⁢1<RT⁢1<1.45⁢x RP⁢1

wherein RP1 is the steady state production rate of the polymer P1 just before the start of the transition, and RT1 is the production rate of the polymer during the transition T1;
a preferred polymerisation production rate of the present invention must fulfil the following equation 0.80⁢x RP⁢1<RT⁢1<1.20⁢x RP⁢1

2. no deinventorying of the reaction system contents is operated during the transition T1. For example, the main monomer (ethylene or propylene) partial pressure (pMM) must fulfil the following equation 0.55⁢x pMMP⁢1<pMMT⁢1<1.45⁢x pMMP⁢1

wherein pMMP1 is the main monomer partial pressure just before the start of the transition T1, and pMMT1 is the main monomer partial pressure during the transition T1;
a preferred main monomer partial pressure of the present invention must fulfil the following equation 0.80⁢x pMMP⁢1<pMMT⁢1<1.20⁢x pMMP⁢1

3. the transition T1 is preferably operated in the absence of injection in the reactor of a catalyst killer (also identified as polymerisation inhibitor and/or poison). Whilst not preferred, the addition of a catalyst killer during the transition is tolerated only if it does not reduce by more then 40%, preferably more than 20%, the activity of the catalyst system a1 and the activity of the catalyst system a2. The catalyst killer is a compound or mixture of compounds that is capable of deactivating the catalyst system. For the purposes of the present application, the term "catalyst killer" does not include the minor portion of similar compounds that may be present in the monomer or comonomer feed streams during normal polymerisation conditions, such as internal olefins or hydrogen, for example. An exemplary catalyst killer includes one or more compounds selected from the group consisting of water, oxygen, alcohols, glycols, phenols, ethers, carbonyl compounds such as ketones, aldehydes, carboxylic acids, esters, fatty acids, alkynes such as acetylene, amines, nitrites, nitrous compounds, pyridine, pyroles, carbonylsulfide (COS), mercaptans, derivatives thereof, or any mixtures or combinations thereof.

4. the polymerisation catalyst activity, defined as the amount of polymer produced by unit of time and by amount of catalyst (e.g. g/hour/g cata), must fulfil the following equations

a. 0.55⁢x AP⁢1<AT⁢1<1.45⁢x AP⁢1

b. 0.55⁢x AP⁢2<AT⁢1<1.45⁢x AP⁢2

wherein AP1 is the activity of the catalyst system a1 used for the production of the polymer P1 just before the start of the transition T1 (i.e. in steady state operations), AP2 is the activity of the catalyst system a2 used for the production of the polymer P2 just after the end of the transition T1 (i.e. in steady state operations) and AT1 is the catalyst activity of the catalyst system used during the transition;

a preferred polymerisation catalyst activity of the present invention must fulfil the following equations

a. 0.80⁢x AP⁢1<AT⁢1<1.20⁢x AP⁢1

b. 0.80⁢x AP⁢2<AT⁢1<1.20⁢x AP⁢2

[0024]

For the purpose of the present description and appended claims, it will be apparent for the man skilled in the art that

RT1 the production rate during the transition T1,

pMMT1 the main monomer partial pressure during the transition T1, and

AT1 the catalyst activity of the catalyst system during the transition T1

may vary during the transition T1. The above conditions define boundaries between which said parameters may preferably vary.

[0025]

According to the most preferred embodiment of the present invention, condition 1 (polymerisation production rate) must be fulfilled; according to another preferred embodiment of the present invention, a continuous transition must fulfil at least two, preferably three, most preferably all of the above recited conditions.

[0026]

Catalyst system a1 and catalyst system a2 are thus both active and present in the reactor during at least part of the transition T1 from P1 to P2; preferably, such simultaneous presence of both catalyst systems lasts for at least 50% of the duration of the transition.

[0027]

According to an embodiment of the present invention, the transition from P1 to P2 comprises a period during which both fresh catalyst a1 and fresh catalyst a2 are fed simultaneously in the reactor.

[0028]

According to a preferred embodiment, the present invention also provides a process for the transition T between an ethylene co-polymerization process carried out in a polymerization reactor in the presence of a catalyst a1, ethylene E and an olefin co-monomer A to produce an ethylene copolymer P1 in an ethylene co-polymerization process carried out in the same polymerization reactor in the presence of a catalyst a2, ethylene E and an olefin co-monomer B to produce an ethylene copolymer P3 characterised in that

catalyst a1 and a2 are different and compatible;

co-monomer A and co-monomer B are different; and

the transition T is performed continuously and comprises two distinct and consecutive transitions T1 and T2 wherein

o the first transition corresponds to the hereinabove defined transition T1 from P1 to P2, and

o the first transition T1 is followed by a second transition T2 between an ethylene co-polymerization process carried out in the same polymerization reactor in the presence of catalyst a2, ethylene E and an olefin co-monomer A to produce an ethylene copolymer P2 in an ethylene co-polymerization process carried out in the same polymerization reactor in the presence of the same catalyst a2, ethylene E and an olefin co-monomer B to produce an ethylene copolymer P3 characterised in that

■ co-monomer A and co-monomer B are both present in the reactor during at least part of the transition T2 from P2 to P3, and

■ the transition T2 is performed continuously from P2 to P3.

[0029]

For the purpose of the present description and appended claims, the transition T2 is defined as the period between the steady state production of the copolymer P2 and the steady state production of the copolymer P3. For the purpose of the present description and appended claims, the transition T is defined as the period between the steady state production of the copolymer P1 and the steady state production of the copolymer P3.

[0030]

The respective steady state productions of P1, P2 and P3 exclusively relates to copolymers. Whilst some terpolymer TEAB is inherently produced during the transition T2, the present invention does not cover the transition between terpolymers.

[0031]

The transition T2 according to the present invention is performed continuously. For the purpose of the present invention and appended claims, a continuous transition T2 must fulfil at least one of the following conditions:

1. the polymerisation production rate ("R"), defined as the amount of polymer produced by unit of time (e.g. tons/hour), must fulfil the following equation 0.55⁢x RP⁢2<RT⁢2<1.45⁢x RP⁢2

wherein RP2 is the steady state production rate of the copolymer P2 just before the start of the transition T2, and RT2 is the production rate of the polymer during the transition T2;
a preferred polymerisation production rate of the present invention must fulfil the following equation 0.80⁢x RP⁢2<RT⁢2<1.20⁢x RP⁢2

2. no deinventorying of the reaction system contents is operated during the transition T2. For example, the ethylene partial pressure (pC2=) must fulfil the following equation 0.55⁢x pC2=P⁢2<pC2=T⁢2<1.45⁢x pC2=P⁢2

wherein pC2=P2 is the ethylene partial pressure just before the start of the transition T2, and pC2=T2 is the ethylene partial pressure during the transition T2;
a preferred ethylene partial pressure of the present invention must fulfil the following equation 0.80⁢x pC2=P⁢2<pC2=T⁢2<1.20⁢x pC2=P⁢2

3. the transition T2 is preferably operated in the absence of injection of a catalyst killer in the reactor (also identified as polymerisation inhibitor and/or poison). Whilst not preferred, the addition of a catalyst killer during the transition T2 is tolerated only if it does not reduce by more then 40%, preferably more than 20%, the activity of the catalyst. The catalyst killer is a compound or mixture of compounds that is capable of deactivating the catalyst system. For the purposes of the present application, the term "catalyst killer" does not include the minor portion of similar compounds that may be present in the monomer or comonomer feed streams during normal polymerisation conditions, such as internal olefins or hydrogen, for example. An exemplary catalyst killer includes one or more compounds selected from the group consisting of water, oxygen, alcohols, glycols, phenols, ethers, carbonyl compounds such as ketones, aldehydes, carboxylic acids, esters, fatty acids, alkynes such as acetylene, amines, nitrites, nitrous compounds, pyridine, pyroles, carbonylsulfide (COS), mercaptans, derivatives thereof, or any mixtures or combinations thereof.

4. the polymerisation catalyst activity, defined as the amount of polymer produced by unit of time and by amount of catalyst (e.g. g/hour/g cata), must fulfil the following equation 0.55⁢x AP⁢2<AT⁢2<1.45⁢x AP⁢2

wherein AP2 is the activity of the catalyst system a2 used for the production of the copolymer P2 just before the start of the transition T2 (i.e. in steady state operations), and AT2 is the catalyst activity of the catalyst system a2 used during the transition T2;
a preferred polymerisation catalyst activity of the present invention must fulfil the following equation 0.80⁢x AP⁢2<AT⁢2<1.20⁢x AP⁢2

[0032]

Again, for the purpose of the present description and appended claims, it will be apparent for the man skilled in the art that

RT2 the production rate during the transition T2,

pC2=T2 the ethylene partial pressure during the transition T2, and

AT2 the catalyst activity of the catalyst system during the transition T2

may vary during the transition. The above conditions define boundaries between which said parameters may preferably vary.

[0033]

According to the most preferred embodiment of the present invention, condition 1 (polymerisation production rate) must be fulfilled; according to another preferred embodiment of the present invention, a continuous transition T2 must fulfil at least two, preferably three, most preferably all of the above recited conditions.

[0034]

One of the many advantages of the present invention over the prior art relates directly to the respect of the environment. Indeed, whilst the prior art operates transitions with substantial hydrocarbon release (e.g. gas reactor inventory renewal), i.e. with important pollution of the atmosphere, the applicants have managed to develop a technology which reduces considerably - or even eliminates - the said releases.

[0035]

According to this embodiment of the present invention, co-monomer A and co-monomer B are both present in the reactor during at least part of the transition T2 from P2 to P3; preferably, such simultaneous presence of both co-monomer A and co-monomer B lasts for at least 50% of the duration of the transition T2. According to a preferred embodiment of the present invention, the transition from P2 to P3 comprises a period during which both fresh co-monomer A and fresh co-monomer B are fed simultaneously in the reactor.

[0036]

According to a preferred embodiment of the present invention, the transition T1 is operated between different catalysts belonging to the same catalyst family. For example, if a chromium catalyst a1 is used as the catalyst for producing P1, the catalyst a2 for producing P2 and optionally P3 will also be a chromium catalyst; e.g. said chromium catalysts have at least one chemical constituent which is different when comparing composition a1 and composition a2. For example, if a Ziegler-Natta catalyst is used as the catalyst for producing P1, the catalyst for producing P2 and optionally P3 will also be a Ziegler-Natta catalyst; e.g. said Ziegler-Natta catalysts have at least one chemical constituent which is different when comparing composition a1 and composition a2. For example, if a metallocene catalyst is used as the catalyst for producing P1, the catalyst for producing P2 and optionally P3 will also be a metallocene catalyst; e.g. said metallocene catalysts have at least one chemical constituent which is different when comparing composition a1 and composition a2.

[0037]

According to the present invention, the same catalyst is used for the production of both the copolymer P2 and the copolymer P3.

[0038]

According to a preferred embodiment of the present invention, the melt index (MI) of the polymer P1 and polymer P2 fulfil the following equation

o 0.55x MIP⁢1<MIP⁢2<1.45x MIP⁢1

preferably

o 0.9x MIP⁢1<MIP⁢2<1.1x MIP⁢1

more preferably

o 0.95x MIP⁢1<MIP⁢2<1.05x MIP⁢1

wherein the melt index is preferably measured using the standard ISO 1133 at a temperature of 190 °C under load of 5 Kg.

[0039]

According to an additional preferred embodiment of the present invention, the melt index (MI) of the copolymer P2 and copolymer P3 fulfil the following equation

o 0.55x MIP⁢2<MIP⁢3<1.45x MIP⁢2

preferably

o 0.9x MIP⁢2<MIP⁢3<1.1x MIP⁢2

more preferably

o 0.95x MIP⁢2<MIP⁢3<1.05x MIP⁢2

wherein the melt index is preferably measured using the standard ISO 1133 at a temperature of 190 °C under load of 5 Kg.

[0040]

According to a preferred embodiment of the present invention, the density (d) of the polymer P1 and polymer P2 fulfil the following equation

o dP⁢1-0.010<dP⁢2<dP⁢1+0.010

preferably

o dP⁢1-0.005<dP⁢2<dP⁢1+0.005

more preferably

o dP⁢1-0.001<dP⁢2<dP⁢1+0.001

wherein the density is given in Kg/m3 and is preferably measured according to the standard ISO 1183-1 (Method A).

[0041]

According to an additional preferred embodiment of the present invention, the density (d) of the copolymer P2 and copolymer P3 fulfil the following equation

o dP⁢2-0.010<dP⁢3<dP⁢2+0.010

preferably

o dP⁢2-0.005<dP⁢3<dP⁢2+0.005

more preferably

o dP⁢2-0.001<dP⁢3<dP⁢2+0.001

wherein the density is given in Kg/m3 and is preferably measured according to the standard ISO 1183-1 (Method A).

[0042]

According to an additional preferred embodiment of the present invention, there is no substantial change of the reactor solids inventory during the transitions T, T1 and T2. For example, this may be translated by the fact that the mass of polymer present in the reactor during the transition (T1 and T2) is at least 75% of the mass of polymer just before the start of the transition (i.e during steady production of the polymer), preferably at least 80%, more preferably at least 90%, most preferably at least 95%. For example, for a gas phase fluidised bed reactor, this may be translated by the fact that the reactor bed height during the transition (T1 and T2) is at least 75% of the reactor bed height just before the start of the transition (i.e during steady production of the polymer), preferably at least 80%, more preferably at least 90%, most preferably at least 95%. The man skilled in the art knows how to measure bed heights, e.g by using nucleonic devices or pressure differential measurements. For the purpose of the present invention and appended claims, the bed height is measured by using the pressure measurement method as described in the Perry's Chemical Engineers' Handbook, Seventh Edition, International Edition 1998, page 17-13.

[0043]

The transitioning process of the present invention is thus applied to a continuous polymerisation reaction process. Said polymerisation reaction can take place in any appropriate reactor, e.g. a gas phase reactor, a gas/liquid phase reactor or a slurry reactor.

[0044]

When the olefin polymerisation reaction is in slurry phase, the reactor is preferably a slurry loop reactor. Slurry phase polymerisation of olefins is well known wherein an olefin monomer and an olefin comonomer are polymerised in the presence of a catalyst in a diluent in which the solid polymer product is suspended and transported. Liquid full loop reactors are particularly well known in the art and are described for example in U.S. Patent Numbers 3,152,872, 3,242,150 and 4,613,484.

[0045]

Polymerisation is typically carried out at temperatures in the range 50-125°C and at pressures in the range 1-100 bara. The catalyst used can be any catalyst typically used for olefin polymerisation such as chromium oxide, Ziegler-Natta or metallocene-type catalysts. The product slurry comprising polymer and diluent, and in most cases catalyst, olefin monomer and comonomer can be discharged intermittently or continuously, optionally using concentrating devices such as hydrocyclones or settling legs to minimise the quantity of fluids withdrawn with the polymer.

[0046]

The loop reactor is of a continuous tubular construction comprising at least two, for example four, vertical sections and at least two, for example four, horizontal sections. The heat of polymerisation is typically removed using indirect exchange with a cooling medium, preferably water, in jackets surrounding at least part of the tubular loop reactor. The volume of the loop reactor can vary but is typically in the range 20 to 120 cubic meters.

[0047]

When polymerisation reaction is in the gas phase, the method may be carried out in a stirred and/or gas fluidised bed. Gas phase polymerisation of a mixture of polymerisable olefin to produce normally solid polymer substances using a quench-cooled, gas-phase polymerisation reactor containing a sub-fluidised particulate bed of polymerised olefin has been described in a number of patents including: US 3,957,448, US 3,965,083 and US 3,971,758. These US Patents describe polymerisation processes and apparatus in which polymer is formed from gaseous olefin in horizontal stirred-bed vessels.

[0048]

According to the most preferred embodiment of the present invention, the method of the present invention is carried out continuously in the gas phase in a fluidised-bed reactor. Such processes are well-known, and examples include EP 0 475 603, EP 1 240 217, EP 1 484 344 and EP 0 855 411.

[0049]

In such processes, the particles of polymer being formed are maintained in the fluidised state by virtue of a reaction gas mixture containing the monomer(s) to be polymerised travelling in a rising stream. The polymer thus manufactured in powder form is generally drained from the reactor in order to keep the bed of fluidised polymer particles at a more or less constant volume. The process generally employs a fluidisation grid which distributes the reaction gas mixture through the bed of polymer particles and which acts as a support for the bed in the event of a cut in the flow of the rising gas. The reaction gas mixture leaving at the top of the fluidised-bed reactor is recycled to the base of the latter under the fluidisation grid by means of an external circulation conduit.

[0050]

The polymerisation of the olefins is an exothermic reaction. The reaction mixture comprising the olefins to be polymerised is generally cooled by means of at least one heat exchanger arranged on the outside of the reactor before being recycled. Liquid, especially but not limited to liquid condensed from the cooled reaction mixture during recycle, may be injected in the reaction zone. Vaporisation of the liquid in the reaction zone provides the effect of cooling directly in the reaction zone.

[0051]

The method of the invention is particularly suitable for very large industrial reactors; in accordance with one embodiment of the present invention, the reactor used makes it possible to produce quantities of polymer of more than 3000 kg/h, preferably more than 10,000 kg/h. The process of the invention is further particularly suitable for high production rates (i.e. the space time yield in terms of weight of polymer produced per unit volume of reactor space per unit time) in commercial gas fluidised bed reactors; consequently, according to a further embodiment of the present invention, space time yields are higher than 25 kg/m3/h, preferably higher than 50 kg/m3/h, more preferably higher than 80 kg/m3/h.

[0052]

The principal olefin according to the present invention is ethylene or propylene. When used, comonomer olefins are preferably selected from alpha-olefins having 2 to 12 carbon atoms. Suitable comonomer olefins are ethylene, propylene, 1-butene, 1-hexene, 4-methyl-1-pentene and 1-octene. Preferably, the principal olefin is ethylene and the comonomer is 1-butene, 1-hexene or 1-octane. Alternatively, the principal olefin can be propylene and the comonomer ethylene.

[0053]

The reaction mixture may also comprise one or more inert compounds, especially inert gases such as nitrogen, and/or one or more saturated hydrocarbons such as ethane, propane, butane, pentane and hexane.

[0054]

The method according to the present invention may be used to prepare a wide variety of polymer products, e.g. polypropylene, linear low density polyethylene (LLDPE), LLDPE especially based on copolymers of ethylene with 1-butene, 1-hexene or 1-octene.This method is particularly suitable for the production of very low density polyethylene (VLDPE). A further suitable polyethylene product is high density polyethylene (HDPE), especially copolymers of ethylene with a small portion of higher alpha olefin, for example, 1-butene, 1-pentene, 1-hexene or 1-octene.

[0055]

The method is particularly suitable for polymerising olefins in the gas phase at an absolute pressure of between 0.5 and 6 MPa and at a temperature of between 30°C and 130°C. For example, for LLDPE production the temperature is suitably in the range 75-100°C and for HDPE the temperature is typically 80-115°C depending on the activity of the catalyst used and the polymer properties desired.

[0056]

The total pressure in the gas phase polymerisation reactor is most preferably between 1.5 and 3 MPa.

[0057]

The method of the present invention may be applied to polymerisation processes using any suitable polymerisation catalyst, including Ziegler-Natta type catalysts chromium oxide type catalysts, and metallocene type catalysts.

[0058]

The copolymerisation may therefore be carried out, for example, in the presence of a catalyst of Ziegler-Natta type comprising at least one transition metal in combination with a cocatalyst comprising an organometallic compound, for example an organoaluminium compound. The catalyst essentially comprises an atom of a transition metal selected from the metals of groups IV to VI of the periodic classification of the elements, such as titanium, vanadium, chromium, zirconium or hafnium, optionally a magnesium atom and a halogen atom. The catalyst may be supported on a porous refractory oxide such as silica or alumina or may be combined with a solid magnesium compound, such as the chloride, the oxide, the hydroxy chloride or an alcoholate of magnesium. By way of example, mention may be made of the catalysts described in the patents US 4,260,709, EP 0 598 094, EP 0 099 774 and EP 0 175 532. The present invention is also particularly appropriate for silica-supported Ziegler catalysts, for example those described in Patents WO 93/09147, WO 95/13873, WO 95/34380, WO 99/05187 and US 6,140,264. The catalyst can be used as it is or optionally in the form of a coated catalyst or prepolymer containing, for example, from 10-5 to 3, preferably from 10-3 to 10-1, millimoles of transition metal per gram of polymer; it can be used together with a cocatalyst or activator, e.g. an organometallic compound of a metal from groups I to III of the Periodic Classification of the Elements, such as, for example, an organoaluminium compound. It is also possible to use a catalyst complexed by a metal selected from those of group VIII of the periodic classification of the elements, such as, for example, nickel, iron or cobalt. By way of examples, mention may be made of those described in Patent Application WO 98/27124 or WO 98/2638. It is also possible to use catalysts based on platinum or palladium as the transition metal; complexes of this type are described, for example, in the Patent WO 96/23010.

[0059]

The copolymerisation may thus also be carried out in the presence of a chromium oxide catalyst. Examples of chromium oxide catalysts are typically those comprising a refractory oxide support which is activated by a heat treatment advantageously carried out at a temperature of at least 250°C and at most equal to the temperature at which the granular support begins to sinter and under a non-reducing atmosphere and preferably an oxidising atmosphere. This catalyst can be obtained by a great number of known process, in particular by those according to which, in a first stage, a chromium compound, such as a chromium oxide, generally of formula CrO3, or a chromium compound which can be converted by calcination into chromium oxide, such as, for example, a chromium nitrate or sulphate, an ammonium chromate, a chromium carbonate, acetate or acetylacetonate, or a tert-butyl chromate, is combined with a granular support based on refractory oxide, such as, for example, silica, alumina, zirconium oxide, titanium oxide or a mixture of these oxides or aluminium or boron phosphates or mixtures in any proportion of these phosphates with the above mentioned oxides. In a second stage, the chromium compound thus combined with the granular support is subjected to a so-called activation operation by heat treatment in a non-reducing atmosphere and preferably an oxidising atmosphere at a temperature of at least 250°C and at most that at which the granular support begins to sinter. The temperature of the heat treatment is generally between 250°C and 1200°C and preferably between 350 and 1000°C. Such catalyst preferably contains from 0.05 to 5%, more preferably from 0.1 to 2%, by weight of chromium ; it can contain, in addition to the chromium, from 0.1 to 10% of titanium in the form of titanium oxide and/or fluorine and/or aluminium, in particular in the form of aluminium oxide ; it can be used as it is or optionally in the form of a coated catalyst or prepolymer containing, for example, from 10-5 to 3, preferably from 10-3 to 10-1, millimoles of chromium per gram of polymer. The chromium oxide catalysts may be used together with a cocatalyst or activator, e.g. an organometallic compound of a metal from groups I to III of the Periodic Classification of the Elements, such as, for example, an organoaluminium compound. Examples of catalysts can be found, for example, in EP 0 275 675, EP 0 453 116, or WO 99/12978.

[0060]

The method of the present invention is also preferably applied to a polymerisation process in which the catalyst is a metallocene-type catalyst.

[0061]

With regards to particular metallocene-type catalysts, mention may be made, by way of example, of those corresponding to the formula

[L]mM[A]n

where L is a bulky ligand; A is a leaving group, M is a transition metal and m and n are such that the total valency of the ligand corresponds to the valency of the transition metal.

[0062]

The ligands L and A may be bridged. L is generally a ligand of the cyclopentadienyl type.

The metallocene catalyst may also be represented by the general formula (Cp)m MRnR'p, where Cp is a ring of the cyclopentadienyl type, M is a transition metal of group 4, 5 or 6; R and R' may be selected from halogens and hydrocarbyl or hydrocarboxyl groups; m=1-3, n=0-3, p=0-3 and the sum m+n+p equals the oxidation state of M; preferably, m=2, n=1 and p=1.

[0067]

The metallocene catalyst may be also represented by the general formula

(C5 R'm)p R"s (C5 R'm) Me Q3-p-x,

or

R"s (C5 R'm)2 MeQ'

where Me is a transition metal of group 4, 5 or 6, at least one C5 R'm is a substituted cyclopentadienyl, each R', which may be identical or different, is hydrogen, an alkyl, alkenyl, aryl, alkylaryl or arylalkyl radical having 1 to 20 carbon atoms, or two carbon atoms linked together to form part of a substituted or unsubstituted ring having 4 to 20 carbon atoms, R" is a radical containing one or more or a combination of carbon, germanium, silicon, phosphorus or nitrogen atoms which bridges two rings (C5 R'm), or which bridges one ring (C5 R'm) to M, when p=0, x=1, else "x" is always 0, each Q, which may be identical or different, is an alkyl, alkenyl, aryl, alkylaryl or arylalkyl radical having 1 to 20 carbon atoms, a halogen or an alkoxide, Q' is an alkylidene radical having 1 to 20 carbon atoms, s is 0 or 1, and when s is 0, m is 5 and p is 0, 1 or 2 and when s is 1, m is 4 and p is 1.

where M is a metal of one of groups 4 to 10 of the Periodic Table of the Elements,
Cp is an anionic ligand group,
Z is a divalent moiety linked to Cp and linked to M, comprising boron or an element of group 14 of the Periodic Table of the Elements, and further comprising nitrogen, phosphorus, sulphur or oxygen;
X is a neutral conjugated diene ligand group having up to 60 atoms, or a dianionic derivative, and

C) an ionic cocatalyst capable of converting the metal complex into an active polymerisation catalyst.

The catalyst may be used in the form of a prepolymer prepared beforehand during a prepolymerisation step from catalysts described above. The prepolymerisation may be carried out by any process, for example a prepolymerisation in a liquid hydrocarbon or in gas phase in accordance with a batchwise, semicontinuous or continuous process. The catalyst or the prepolymer may be introduced in the reactor continuously or discontinuously, preferably continuously.

Polymerisation example

[0074]

An industrial fluidised bed gas phase reactor having a diameter of 5 m was operated at 104°C temperature and 23 bara pressure (with ethylene at a pressure of 7.3 bars). In the reactor was added ethylene, hexene (at a rate of 220 kg/hr), nitrogen and the polymerisation catalyst PQC24340 ® from PQ Corporation Catalysts (a chromium compound supported on a silica aluminium cogel containing 1% by weight of chromium and 2.0% by weight of aluminium) so that an ethylene-hexene-copolymer having a high load melt index of 10 g/10 min and a density of 950 kg/m3 was formed under steady state conditions (production rate of 34 T/hr and catalyst injection rate of 10.4 kg/h).

[0075]

The transition from said PQC24340 to another PQ catalyst EP30X (a silica supported chromium catalyst containing 1% by weight of chromium) started with a gradual decrease of the rate of introduction of PQC24340, and a gradual increase of the rate of EP30X.

[0076]

During the transition, the polymerisation production rate ("R") remained within +/- 10% of 34 T/hr, no additional release of ethylene from the reactor was made, no catalyst killer was used, and the polymerisation catalyst activity remained within +/- 10% of its activity during the steady state production of the copolymer PE-hexene.

[0077]

The reactor bed height during the transition remained within +/- 10% of the reactor bed height just before the start of the transition (which was 20 m).

[0078]

The total transition time duration was 30 hours.

[0079]

After the transition, the new copolymer PE-hexene was produced under steady state conditions (production rate of 33 T/hr); said ethylene-hexene-copolymer had a high load melt index of 30 g/10 min and a density 953 kg/m3.

Claims (15)

Process for the transition T1 between an ethylene or a propylene polymerization process carried out in a polymerization reactor in the presence of a catalyst a1, ethylene or propylene and an optional olefin co-monomer A to produce an ethylene polymer or a propylene polymer P1 into an ethylene or a propylene polymerization process carried out in the same polymerization reactor in the presence of a catalyst a2, ethylene or propylene and the same optional olefin co-monomer A to produce an ethylene polymer or a propylene polymer P2 characterised in that

- catalyst a1 and a2 are different and compatible;

- catalyst a1 and catalyst a2 are both active and present in the reactor during at least part of the transition T1 from P1 to P2; and

- the transition T1 is performed continuously.

Process according to claim 1 wherein the polymerisation production rate ("R"), defined as the amount of polymer produced by unit of time (e.g. tons/hour), must fulfil the following equation 0.55⁢x RP⁢1<RT⁢1<1.45⁢x RP⁢1

wherein RP1 is the steady state production rate of the polymer P1 just before the start of the transition T1, and RT1 is the production rate of the polymer during the transition T1.

Process according to claim 2 wherein the polymerisation production rate must fulfil the following equation 0.80⁢x RP⁢1<RT⁢1<1.20⁢x RP⁢1

Process according to any of the preceding claims wherein no deinventorying of the reaction system contents is operated during the transition T1.

Process according to any of the preceding claims wherein the main monomer (ethylene or propylene) partial pressure (pMM) must fulfil the following equation 0.55⁢x pMMP⁢1<pMMT⁢1<1.45⁢x pMMP⁢1

wherein pMMP1 is the main monomer partial pressure just before the start of the transition T1, and pMMT1 is the main monomer partial pressure during the transition T1.

Process according to claim 5 wherein the main monomer partial pressure of the present invention must fulfil the following equation 0.80⁢x pMMP⁢1<pMMT⁢1<1.20⁢x pMMP⁢1

Process according to any of the preceding claims wherein the transition T1 is operated in the absence of injection in the reactor of a catalyst killer.

Process according to any of the preceding claims wherein the polymerisation catalyst activity, defined as the amount of polymer produced by unit of time and by amount of catalyst (e.g. g/hour/g cata), must fulfil the following equations

a. 0.55⁢x AP⁢1<AT⁢1<1.45⁢x AP⁢1

b. 0.55⁢x AP⁢2<AT⁢1<1.45⁢x AP⁢2

wherein AP1 is the activity of the catalyst system a1 used for the production of the polymer P1 just before the start of the transition T1 (i.e. in steady state operations), AP2 is the activity of the catalyst system a2 used for the production of the polymer P2 just after the end of the transition T1 (i.e. in steady state operations) and AT1 is the catalyst activity of the catalyst system used during the transition.

Process according to claim 8 wherein the polymerisation catalyst activity must fulfil the following equations

a. 0.80⁢x AP⁢1<AT⁢1<1.20⁢x AP⁢1

b. 0.80⁢x AP⁢2<AT⁢1<1.20⁢x AP⁢2

Process according to any of the preceding claims wherein the transition T1 is operated between different compatible catalysts belonging to the same catalyst family.

Process for the transition T between an ethylene co-polymerization process carried out in a polymerization reactor in the presence of a catalyst a1, ethylene E and an olefin co-monomer A to produce an ethylene copolymer P1 in an ethylene co-polymerization process carried out in the same polymerization reactor in the presence of a catalyst a2, ethylene E and an olefin co-monomer B to produce an ethylene copolymer P3 characterised in that

- catalyst a1 and a2 are different and compatible;

- co-monomer A and co-monomer B are different; and

- the transition T is performed continuously and comprises two distinct and consecutive transitions T1 and T2 wherein

o the first transition T1 is performed according any of claims 1 to 10, and

o the first transition T1 is followed by a second transition T2 between an ethylene co-polymerization process carried out in the same polymerization reactor in the presence of catalyst a2, ethylene E and an olefin co-monomer A to produce an ethylene copolymer P2 in an ethylene co-polymerization process carried out in the same polymerization reactor in the presence of the same catalyst a2, ethylene E and an olefin co-monomer B to produce an ethylene copolymer P3 characterised in that

■ co-monomer A and co-monomer B are both present in the reactor during at least part of the transition T2 from P2 to P3, and

■ the transition T2 is performed continuously from P2 to P3.

Process according to claim 11 wherein the transition from P2 to P3 comprises a period during which both fresh co-monomer A and fresh co-monomer B are fed simultaneously in the reactor.

Process according to any of the preceding claims wherein the mass of polymer present in the reactor during the transition (T1 and T2) is at least 75% of the mass of polymer just before the start of the respective transition (i.e during steady production of the polymer), preferably at least 80%, more preferably at least 90%, most preferably at least 95%.

Process according to any of the preceding claims wherein the main monomer is ethylene or propylene and the optional comonomer is selected from alpha-olefins having 2 to 12 carbon atoms, e.g from ethylene, propylene, 1-butene, 1-hexene, 4-methyl-1-pentene and 1-octene.

Process according to any of the preceding claims wherein the reactor is a gas phase fluidised bed reactor.