One aspect of this disclosure relates to a method for forming an integrated circuit. According to various embodiments of the method, a plurality of transistors is formed. For each transistor, a gate dielectric is formed on a substrate, a substitutable structure is formed on the gate dielectric, and source/drain...http://www.google.es/patents/US7674698?utm_source=gb-gplus-sharePatente US7674698 - Metal-substituted transistor gates

One aspect of this disclosure relates to a method for forming an integrated circuit. According to various embodiments of the method, a plurality of transistors is formed. For each transistor, a gate dielectric is formed on a substrate, a substitutable structure is formed on the gate dielectric, and source/drain regions for the transistor are formed. At least two substitution processes are performed. Each substitution process includes substituting a desired gate material for the substitutable structure. Other aspects and embodiments are provided herein.

Imágenes(6)

Reclamaciones(34)

1. A method for forming an integrated circuit, comprising:

forming a plurality of transistors, including:

for each transistor, forming a gate dielectric on a substrate, forming a substitutable structure on the gate dielectric, and forming source/drain regions for the transistor; and

performing at least two substitution processes, each substitution process including substituting a desired gate material for the substitutable structure using a metal substitution reaction,

wherein the substitutable structure for at least one of the plurality of transistors includes a substitutable carbon structure and at least one of the at least two substitution processes includes substituting for the substitutable carbon structure.

2. The method of claim 1, wherein performing at least two substitution processes includes performing a first substitution process for one of N-type and P-type transistors for a CMOS integrated circuit, and a second substitution process for the other one of the N-type and P-type transistors.

3. The method of claim 2, wherein the first substitution process is a higher temperature process than the second temperature process.

4. The method of claim 2, wherein the substitutable structure for at least another one of the plurality of transistors includes a substitutable structure that includes germanium, the substitution reaction with carbon involving a higher temperature than the substitution reaction with germanium.

5. The method of claim 2, wherein the desired gate material for P-type transistors is selected for a desired gate work function for the P-type transistors, and the desired gate material for N-type transistors is selected for a desired gate work function for the N-type transistors.

6. A method for forming an integrated circuit, comprising:

forming a gate dielectric on a substrate, forming a substitutable structure for P-type transistors and a substitutable structure for N-type transistors on the gate dielectric, forming source/drain regions for the P-type transistors, forming source/drain regions for the N-type transistors, substituting a desired P-type transistor gate material for the substitutable structure for the P-type transistors using a first metal substitution reaction, and substituting a desired N -type transistor gate material for the substitutable structure for the N-type transistors using a second metal substitution reaction, the P-type transistor gate material being different than the N-type transistor gate material, wherein the substitutable structure for N-type transistors or the substitutable structure P-type transistors includes carbon.

7. The method of claim 6, wherein the desired P-type transistor gate material is selected for a desired gate work function for the P-type transistors, and the desired N-type transistor gate material is selected for a desired gate work function for the N-type transistors.

8. The method of claim 6, wherein forming a substitutable structure for P-type transistors and a substitutable structure of N-type transistors on the gate dielectric includes forming the substitutable structure for P-type transistors using a first material and forming the substitutable structure for N-type transistors using a second material different than the first material.

9. The method of claim 6, wherein:

forming a substitutable structure for P-type transistors includes forming the substitutable structure using a first material; and

forming a substitutable structure for the N-type transistors on the gate dielectric includes forming the substitutable structure using the first material.

10. The method of claim 6, wherein:

the substitutable structure for P-type transistors is different from the substitutable structure of N-type transistors.

11. The method of claim 6, wherein forming the gate dielectric on the substrate includes performing an atomic layer deposition process, an evaporation deposition process, or a metal oxidation process.

12. A method for forming an integrated circuit, comprising:

forming a high-k gate dielectric on a substrate, forming a substitutable structure for P-type transistors and a substitutable structure for N-type transistors on the high-k gate dielectric, forming source/drain regions for the P-type transistors, forming source/drain regions for the N-type transistors, substituting a desired P-type transistor gate material for the substitutable structure for the P-type transistors using a first metal substitution reaction, and substituting a desired N-type transistor gate material for the substitutable structure for the N-type transistors using a second metal substitution reaction, the P-type transistor gate material being different than the N-type transistor gate material, wherein the substitutable structure for N-type transistors or the substitutable structure for P-type transistors includes carbon.

13. The method of claim 12, wherein the substitutable structure for N-type transistors or the substitutable structure for P-type transistors includes polysilicon.

14. The method of claim 12, wherein the substitutable structure for N-type transistors or the substitutable structure for P-type transistors includes germanium.

15. The method of claim 12, wherein the substitutable structure for N-type transistors or the substitutable structure for P-type transistors includes silicon-germanium.

16. The method of claim 12, wherein at least one of the P-type transistor gate material or the N-type transistor gate material includes gold or silver.

17. The method of claim 12, wherein at least one of the P-type transistor gate material or the N-type transistor gate material is selected from a group consisting of platinum, rhenium, ruthenium, rhodium, nickel, osmium, palladium, iridium, cobalt and germanium.

18. A method for forming an integrated circuit, comprising:

forming a high-k gate dielectric on a substrate, forming a substitutable structure for P-type transistors and a substitutable structure for N-type transistors on the high-k gate dielectric, forming source/drain regions for the P-type transistors, forming source/drain regions for the N-type transistors, substituting a first metal gate material for the substitutable structure for the P-type transistors using a first metal substitution reaction, and substituting a second metal gate material for the substitutable structure for the N-type transistors using a second metal substitution reaction, the first metal gate material being different than the second metal gate material, wherein the substitutable structure for N-type transistors or the substitutable structure for P-type transistors includes carbon.

19. The method of claim 18, wherein the substitutable structure for N-type transistors or the substitutable structure for P-type transistors includes polysilicon.

20. The method of claim 18, wherein the substitutable structure for N-type transistors or the substitutable structure for P-type transistors includes germanium.

21. The method of claim 18, wherein the substitutable structure for N-type transistors or the substitutable structure for P-type transistors includes silicon-germanium.

22. The method of claim 18, wherein at least one of the first or second metal gate materials includes silver.

23. The method of claim 18, wherein at least one of the first or second metal gate materials includes gold.

24. The method of claim 18, wherein at least one of the first or second metal gate materials includes an alloy of gold or silver.

25. A method for forming an integrated circuit, comprising:

performing a first substitution process using a first metal substitution reaction to replace a first substitutable material on a first dielectric material with a first electrically-conductive material on the first dielectric material at a first substitution processing temperature; and

performing a second substitution process using a second metal substitution reaction to replace a second substitutable material on a second dielectric material with a second electrically-conductive material on the second dielectric material at a second substitution processing temperature lower than the first substitution process temperature, the first substitution process being performed before the second substitution process, wherein at least one of the first substitutable material or second substitutable material includes carbon.

26. The method of claim 25, further comprising forming transistor gate stacks using at least one of the first electrically-conductive material on the first dielectric material or the second electrically-conductive material on the second dielectric material.

27. The method of claim 25, wherein at least one of the first dielectric material or the second dielectric material includes a high-k dielectric material.

28. The method of claim 25, wherein the first electrically-conductive material includes a first metal, and the second electrically-conductive material includes a second metal different from the first metal.

29. The method of claim 25, wherein the first substitutable material and the second substitutable material are different materials.

30. The method of claim 25, wherein the other one of the first or second substitutable material includes silicon.

31. The method of claim 25, wherein the other one of the first or second substitutable material includes germanium.

32. The method of claim 25, wherein the other one of the first or second substitutable material includes silicon-germanium.

33. The method of claim 25, wherein the first dielectric material is different from the second dielectric material.

34. A method for forming an integrated circuit, comprising:

forming a plurality of transistors, including:

for each transistor, forming a gate dielectric on a substrate, forming a substitutable structure on the gate dielectric, and forming source/drain regions for the transistor; and

performing at least two substitution processes, each substitution process including substituting a desired gate material for the substitutable structure,

wherein performing at least two substitution processes includes performing a first substitution process for one of N-type and P-type transistors for a CMOS integrated circuit, and a second substitution process for the other one of the N-type and P-type transistors, and

wherein performing at least two substitution processes includes using a substitution reaction with carbon and using a substitution reaction with germanium, the substitution reaction with carbon involving a higher temperature than the substitution reaction with germanium.

Descripción

This application is a divisional of U.S. application Ser. No. 11/176,738, filed Jul. 7, 2005 now U.S. Pat. No. 7,195,999, which is incorporated herein by reference.

TECHNICAL FIELD

This disclosure relates generally to integrated circuits, and more particularly, to transistor structures and methods of formation.

BACKGROUND

Many integrated circuits include a metal-oxide-semiconductor, field-effect transistor, or “MOSFET” for short, which includes a gate, a source, a drain, and a body. An issue in MOSFET design involves the structure and composition of its gate. Some early MOSFET designs included aluminum gates, and later MOSFET designs used polysilicon gates because of the desire for a self-aligned gate as well as the tendency of aluminum to diffuse through the underlying insulative layer and also because of problems that the relatively low melting temperature of aluminum caused with annealing processes. Polysilicon can be doped to act as a conductor, but with significantly more electrical resistance than aluminum. This higher resistance can be ameliorated somewhat by silicidation. However, the higher resistance of even the salicided polysilicon gates combines with inherent integrated-circuit capacitances to cause significant delays in conducting signals from one circuit point to another, ultimately limiting how fast integrated circuits operate.

Currently, the semiconductor industry relies on the ability to reduce or scale the dimensions of its basic devices, including the gate dielectric, of its transistor devices to obtain lower power consumption and higher performance. To reduce transistor size, the thickness of the gate dielectric is reduced in proportion to the shrinkage of the gate length. Increased scaling and other requirements in microelectronic devices have created the need to use other dielectric materials as gate dielectrics, in particular dielectrics with higher dielectric constants (k) to replace the conventional use of various combinations of SiO2, Si3N4 and SiON. Practical higher dielectric constant (k) materials have the properties of high permittivity, thermal stability, high film and surface quality and smoothness, low hysteresis characteristics, low leakage current density, and long term reliability. However, polysilicon gates and high-k dielectric materials have interface instability issues.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A-1E illustrate a process for forming a metal substituted gate for a transistor structure, according to various embodiments of the present subject matter.

FIG. 3 illustrates a wafer, upon which the transistors with metal substituted gates can be fabricated according to embodiments of the present subject matter.

FIG. 4 illustrates a simplified block diagram of a high-level organization of an electronic system that includes the transistor with the metal-substituted gate, according to various embodiments.

FIG. 5 illustrates a simplified block diagram of a high-level organization of an electronic system that includes transistors with metal substituted gates, according to various embodiments.

FIG. 6 illustrates two substitution processes.

DETAILED DESCRIPTION

The following detailed description refers to the accompanying drawings which show, by way of illustration, specific aspects and embodiments in which the present invention may be practiced. The various embodiments are not necessarily mutually exclusive, as aspects of one embodiment can be combined with aspects of another embodiment. Other embodiments may be utilized and structural, logical, and electrical changes may be made without departing from the scope of the present invention. In the following description, the terms wafer and substrate are used interchangeably to refer generally to any structure on which integrated circuits are formed, and also to such structures during various stages of integrated circuit fabrication. Both terms include doped and undoped semiconductors, epitaxial layers of a semiconductor on a supporting semiconductor or insulating material, combinations of such layers, as well as other such structures that are known in the art. The terms “horizontal” and “vertical”, as well as prepositions such as “on”, “over” and “under” are used in relation to the conventional plane or surface of a wafer or substrate, regardless of the orientation of the wafer or substrate. References to “an”, “one”, or “various” embodiments in this disclosure are not necessarily to the same embodiment, and such references contemplate more than one embodiment. The following detailed description is, therefore, not to be taken in a limiting sense, and the scope of the present invention is defined only by the appended claims, along with the full scope of equivalents to which such claims are entitled.

One aspect of this disclosure relates to a method for forming a transistor. According to various method embodiments, a gate dielectric is formed on a substrate, a substitutable structure is formed on the gate dielectric, and source/drain regions for the transistor are formed. A desired gate material is substituted for the starting or substitutable structure to provide the desired gate material on the gate dielectric. Some embodiments use carbon for the substitutable material. Various embodiments replace carbon starting material with gold (Au), silver (Ag), gold alloy, silver alloy, copper (Cu), platinum (Pt), rhenium (Re), ruthenium (Ru), rhodium (Rh), nickel (Ni), osmium (Os), palladium (Pd), iridium (Ir), cobalt (Co), and germanium (Ge). Some embodiments use silicon, germanium or silicon-germanium for the starting or substitutable material. Various embodiments replace silicon, germanium or silicon-germanium starting material with aluminum, copper, silver, gold, alloys of silver, or alloys of gold. Some embodiments form a high-k gate dielectric, such as may be formed by an atomic layer deposition process, an evaporated deposition process, and a metal oxidation process. According to various embodiments, the high-k gate dielectric includes one or more of the following: AlOX, LaAlO3, HfAlO3, Pr2O3-based lanthanide oxide, HfSiON, Zr—Sn—Ti—O, ZrON, HfO2/Hf, ZrAlXOY, ZrTiO4, Zr-doped Ta, HfO2—Si3N4, lanthanide oxide, TiAlOX, LaAlOX, La2Hf2O7, HfTaO amorphous lanthanide doped TiOx, TiO2, HfO2, CrTiO3, ZrO2, Y2O3, Gd2O3, praseodymium oxide, amorphous ZrOXNY, Y—Si—O, LaAlO3, amorphous lanthanide-doped TiOX, HfO2/La2O3 nanolaminates, La2O3/Hf2O3 nanolaminates, HfO2/ZrO2 nanolaminates, lanthanide oxide/zirconium oxide nanolaminates, lanthanide oxide/hafnium oxide nanolaminates, TiO2/CeO2 nanolaminates, PrOX/ZrO2 nanolaminates, Hf3N4/HfO2 nanolaminates, and Zr3N4/ZrO2 nanolaminates. Other aspects and embodiments are provided herein.

Disclosed herein, among other things, is a transistor device structure with substituted metal gates. Various embodiments provide the substituted metal gates over and in contact with a high-k dielectric. Those of skill in the art will understand that the term high-k dielectric refers to a dielectric material having a dielectric constant greater than that of silicon dioxide. That is, a high-k dielectric has a dielectric constant greater than 4. A transistor device structure with a high-k gate dielectric and a substituted metal gate increases the capacitance and reduces the resistance of integrated circuits, which is useful for nanoscale integrated circuits. Additionally, the transistor device disclosed herein is capable of being manufactured with gates engineered to have differing work functions. Thus, in CMOS designs, a transistor metal gate is able to provide a desired work function (within 0.2 eV of the EC of silicon) for NMOS devices and a desired work function (within 0.2 eV of the EV of silicon) for PMOS devices.

The substituted metal gates replace a substitutable material formed on a gate dielectric. Various embodiments provide a substituted gate where the starting material is a mixture of silicon and germanium over the entire range of silicon and germanium from 0 to 100 percent silicon. Various embodiments replace the silicon, germanium or silicon-germanium starting material with aluminum, copper, silver, gold, alloys of silver, or alloys of gold. As the silicon-germanium phase relationship is one of a continuous series of solid solutions, the metal substitution of aluminum, silver or gold will work with all mixtures of silicon and germanium. Various embodiments provide a substituted gate where the starting material is carbon. Various embodiments replace the carbon starting material with gold (Au), silver (Ag), gold alloy, silver alloy, copper (Cu), platinum (Pt), rhenium (Re), ruthenium (Ru), rhodium (Rh), nickel (Ni), osmium (Os), palladium (Pd), iridium (Ir), cobalt (Co), and germanium (Ge).

Gold and silver may be substituted for carbon. However, gold and silver are not able to be substituted for all ranges of carbon-silicon or carbon-germanium alloys. Carbon and germanium are not soluble, such that the solid phase is a two phase material. The melting point of carbon (3828° C.) is much higher than that of germanium (938° C.). Thus, alloys with significant amounts of carbon may provide a problem. Silicon and carbon are insoluble and have an intermetallic compound SiC (silicon carbide) as it forms peritectoidly at 2545° C., while the eutectic temperature between silicon and silicon carbide is at 1404° C. Thus, it appears unlikely that one could replace silicon carbide in a silicon rich starting material. However, in a carbon rich silicon carbide material that is properly formed, the temperature of the material could be raised to just under 2545° C. without forming a liquid phase. Thus, it appears that an alloy having above 50 atomic percent carbon is a possible candidate.

FIGS. 1A-1E illustrate a process for forming a metal substituted gate for a transistor structure, according to various embodiments of the present subject matter. FIG. 1A illustrates a substrate 101 and shallow trench isolation (STI) regions 102. The substrate 101 can be a semiconductor wafer as well as structures having one or more insulative, semi-insulative, conductive, or semiconductive layers and materials. Thus, for example, the substrate can include silicon-on-insulator, silicon-on-sapphire, and other structures upon which semiconductor devices are formed.

FIG. 1B further illustrates a gate dielectric layer 103 formed on the substrate 101, and a gate substitutable layer 104 formed on the gate dielectric layer 103. According to some embodiments, the gate dielectric layer includes a silicon oxide, such as silicon dioxide. In various embodiments, the gate dielectric layer includes a high-k dielectric, such as AlOX, LaAlO3, HfAlO3, Pr2O3-based Lanthanide Oxide, HfSiON, Zr—Sn—Ti—O, ZrON, HfO2/Hf, ZrAlXOY, ZrTiO4, Zr-doped Ta, HfO2—Si3N4, lanthanide oxide, TiAlOX, LaAlOX, La2Hf2O7, HfTaO amorphous lanthanide doped TiOx, TiO2, HfO2, CrTiO3, ZrO2, Y2O3, Gd2O3, praseodymium oxide, amorphous ZrOXNY, Y—Si—O, LaAlO3, amorphous lanthanide-doped TiOX, HfO2/La2O3 nanolaminates, La2O3/Hf2O3 nanolaminates, HfO2/ZrO2 nanolaminates, lanthanide oxide/zirconium oxide nanolaminates, lanthanide oxide/hafnium oxide nanolaminates, TiO2/CeO2 nanolaminates, PrOX/ZrO2 nanolaminates, Hf3N4/HfO2 nanolaminates, Zr3N4/ZrO2 nanolaminates, and the like. The use of the high-k dielectric increases the capacitance, which is useful for nanoscale integrated circuits. As will be described in more detail below, the material of the gate substitutable layer 104 is selected with respect to the desired gate material, to allow the gate material to replace the gate substitutable layer to form a gate of the desired gate metal where the substitutable material was positioned on the gate dielectric.

As illustrated in FIG. 1C, portions of the gate dielectric layer 103 and the gate substitutable layer 104 are removed to define a gate 105, and sidewalls or spacers 106 are formed along the gate 105. Source/drain regions are also formed. The source/drain regions 107 can be formed using conventional ion implantation and subsequent annealing. These annealing temperatures can pose problems for aluminum gates and other metal gates that have melting temperatures less than the anneal temperature for the source/drain regions.

With reference to FIG. 1D, an insulative fill layer 108 is provided to match the thickness of the gate stack. A planarization procedure, such as chemical-mechanical polishing, can be used to provide an even surface across the fill layer 108 and the gate substitutable layer 104. A metal layer 109 formed of material intended to be the gate material is deposited over the gate substitutable layer 104 and the fill layer 108. The metal layer 109 is also referred to herein as a layer of gate material. Various deposition processes, such as evaporation, sputtering or chemical vapor deposition, may be used to form the metal layer 109. The volume of layer 109 is significantly larger than the volume of the substitutable material left on the wafer.

After the metal layer 109 is deposited on the gate substitutable layer, a metal-substitution reaction is induced. The reaction can be provided by annealing the structure in a non-oxidizing atmosphere such as a nitrogen gas or a forming gas. The heating urges diffusion or dissolution of the intended gate material in metal layer 109 for the substitutable material 104. The substitution process is bounded by the spacers 106 and the gate dielectric 103.

At the conclusion of the substitution reaction, the method removes the residual metal of layer 109 and the substitutable material, such as may be achieved using conventional planarization. FIG. 1E shows the resulting low-resistance gate structure. The illustrated structure includes a metal substituted gate 110 formed by the substitution of the metal of layer 109. The metal substituted gate 110 may include a small amount of the gate substitutable material which did not diffuse above the planarization level 111. Such small amounts of the gate substitutable material do not significantly affect the conductivity of the metal substituted gate 110, and thus do not significantly affect the performance of the device.

Drain and source contacts (not shown) can be formed, as well as interconnects to other transistors or components, using conventional techniques. Another heat treatment may occur after packaging the integrated circuit in a protective housing in an attempt to minimize the resistivity of the metal gate contacts and other metal interconnections.

The metal gate substitution technique, as disclosed herein, can be applied to MOS devices, as generally illustrated in FIG. 1, as well as to form metal floating gates and/or metal control gates in nonvolatile devices. Additionally, various high-k dielectrics can be used between the floating gate and the substrate, and between the control gate and the floating gate in these nonvolatile devices.

Metal Gate Substitution Technique

FIG. 2 illustrates an embodiment of a metal gate substitution technique. At 212, a gate dielectric is formed on a substrate. The gate dielectric includes a high-k dielectric in some embodiments. Various high-k dielectric embodiments are identified below. At 213, a layer of gate substitutable material is formed on the gate dielectric. Examples of gate substitutable material include polysilicon, germanium, silicon-germanium and carbon. At 214, source/drain regions are formed. A layer of gate material, also referred to herein as a metal layer, is formed at 215 on the gate substitutable material. Examples of such metals include gold, silver, and aluminum. Other metals may be used. At 216, the gate material is substituted for the layer of gate substitutable material.

A metal substitution reaction substitutes or replaces the substitutable material (e.g. silicon, germanium, silicon-germanium, carbon) with a metal. After the substitution, the resulting gate structure includes substantially all of the desired metal. Small amounts of the substitutable material may remain in the gate structure. The substitution reaction can be induced by heating the integrated circuit assembly to a desired temperature in a vacuum, nitrogen, argon, forming gas or other nonoxidizing atmosphere. Heating causes diffusion of the metal layer 109 into the substitutable layer. The annealing temperature for the substitution is less than the eutectic (lowest melting) temperature of materials involved in the substitution for the reaction for substitution to occur. For example, to form a gold gate, one could form the metal layer from gold and anneal at approximately 300° C. to substitute the gold for a silicon substitutable structure, and to form a silver gate one could form the metal layer from silver and anneal at approximately 500-600° C. to substitute the silver for the silicon substitutable structure. A polysilicon and germanium substitutable material can be used, which reduces the anneal temperature.

According to various embodiments, the gate substitutable material 104 shown in FIGS. 1A-1E includes polysilicon. In some embodiments, the gate substitutable material includes germanium. Some embodiments use silicon-germanium, with any percentage of silicon in the range of 0% to 100% as the gate substitutable material 104. Some embodiments use carbon as the gate substitutable material 104.

With respect to embodiments which use polysilicon, germanium or silicon-germanium as the gate substitutable material 104, some embodiments use aluminum as the replacement metal for the substituted gate, some embodiments use silver as the replacement metal, some embodiments use gold as the replacement metal, some embodiments use an alloy of silver as the replacement metal, and some embodiments use an alloy of gold as the replacement metal.

With respect to embodiments which use carbon as the gate substitutable material 104, some embodiment use gold as the replacement metal for the substituted gate, some embodiments use silver as the replacement metal, some embodiments use an alloy of gold as the replacement metal, some embodiments use an alloy of silver as the replacement metal, some embodiments use copper as the replacement metal, some embodiments use platinum as the replacement metal, some embodiments use rhenium as the replacement metal, some embodiments use ruthenium as the replacement metal, some embodiments use rhodium as the replacement metal, some embodiments use nickel as the replacement metal, some embodiments use osmium as the replacement metal, some embodiments use palladium as the replacement metal, some embodiments use iridium as the replacement metal, some embodiments use cobalt as the replacement metal, and some embodiments use germanium as the replacement metal.

Table 1 provides a listing of various embodiments for substituted metal gates formed using various substitutable or starting material and various metal gate material. Table 1 also identifies the eutectic (lowest melting) temperature of the elements, including both the substitutable material and the metal gate material, involved in the substitution process, and the approximate ranges of annealing temperatures that are used in various method embodiments to perform the metal substitution reaction. The identified substitution temperatures are approximate, as they depend on process control tolerances and the effect of impurities. Substitution may occur at other temperatures than that provided as an example in the table.

TABLE 1

APPROXIMATE

APPROXIMATE

SUBSTITUTION

EUTECTIC

TEMPERATURE

SUBSTITUTABLE

GATE

TEMPERATURE

RANGE

MATERIAL

MATERIAL

° C.

° C.

Silicon

Aluminum

577

450-525

Silver

835

700-800

Gold

363

250-325

Alloys of

*

**

Silver

Alloys of

*

**

Gold

Germanium

Aluminum

420

275-325

Silver

653

500-600

Gold

361

250-325

Alloys of

*

**

Silver

Alloys of

*

**

Gold

Silicon-

Aluminum

<420 *

300-375 **

Germanium

Silver

<653 *

475-575 **

Carbon

Gold

<361 *

250-300 **

Alloys of

*

**

Silver

Alloys of

*

**

Gold

Gold

1060

925-1025

Silver ***

962

825-925

Alloys of

*

**

Gold

Alloys of

*

**

Silver

Copper ***

1100

900-1025

Platinum

1705

1500-1625

Rhenium

2505

2300-2450

Ruthenium

1940

1775-1875

Rhodium

1694

1525-1625

Nickel

1326

1150-1275

Osmium

2732

2400-2600

Palladium

1504

1300-1425

Iridium

2296

2050-2200

Cobalt

1320

1150-1275

Germanium

938

775-875

* Ternary diagrams (e.g. Si—Ge—Al phase diagram; Si—Ge—Ag phase diagram; Si—Ge—Au phase diagram) can be used to determine these eutectic temperatures. With respect to the Si—Ge system, silicon and germanium are completely soluble in each other in the solid phase. Thus, there is a possibility that there is a lower melting point in the ternary system than in the binary systems.

** The substitution temperature of ternary systems, as well as the other systems provided herein, can be established by estimating the substitution temperature based on the constituent elements and/or by experiment. The substitution temperatures are less than the eutectic temperatures with some allowance for the effect of any impurities present as well as process control tolerances.

*** Carbon-Silver and Carbon-Copper systems are shallow pertectic systems, rather than eutectic systems. It is believed that such shallow pertectic systems can be used to provide the metal gate substitution process.

Various embodiments form an integrated circuit structure using two or more substitution reactions. FIG. 6 illustrates two substitution processes. Relatively higher temperature substitution processes can be performed before relatively lower temperature substitution processes. For example, a relatively high-temperature substitution reaction with carbon can be performed before a relatively low-temperature substitution reaction with germanium. Examples of substitution temperature ranges are provided above in Table 1. The present subject matter includes multiple substitution reactions involving various combinations of two or more substitution processes illustrated in Table 1. One application for multiple substitution reactions is to independently adjust work functions of NMOS and PMOS transistors in CMOS integrated circuits. Multiple substitution reactions are not limited to this CMOS integrated circuit application.

High-k Dielectric Gate Insulator

As provided above, some embodiments provide the metal substituted gate 110 on a high-k gate dielectric 103. Various embodiments use the specific high-k dielectrics provided below. Some specific process examples are provided below for the identified high-k dielectric. These process examples are not intended to be limited to exclude the identified device structures if the structures are formed using other processes. According to various embodiments, a high-k dielectric can be fabricated using atomic layer deposition (ALD) processes, evaporated deposition processes, and sputtered deposition processes. Additionally, metal can be oxidized to form a high-k dielectric, and the high-k dielectric can be formed as nanolaminates of dielectric material.

Specific chemical formulas are referenced below with respect to various high-k dielectric structures. However, the dielectric structure can include stoichiometric structures, non-stoichiometric structures, and combinations of stoichiometric and non-stoichiometric structures.

AlOX

Various embodiments use an aluminum oxide (AlOX) formed by ALD as a high-k dielectric. For example, a pulse of an oxidant can be provided, followed by a purge or evacuation of the oxidant, followed by a pulse of a precursor containing aluminum, followed by a purge or evacuation of the aluminum-containing precursor. The aluminum precursor can include a variety of precursors, such as trimethylaluminum (TMA), triisobutylaluminum (TIBA), dimethylaluminum hydride (DMAH), AlC3, and other halogenated precursors and organometallic precursors. Oxidants can include a water-argon mixture formed by bubbling an argon carrier through a water reservoir, H2O2, O2, O3, and N2O. The ALD aluminum oxides are not limited to specific aluminum precursors or oxidants. Additional information regarding aluminum oxides formed by ALD can be found in US Patent Application Publication 20030207032A1, entitled “Methods, Systems, and Apparatus for Atomic-Layer Deposition of Aluminum Oxides in Integrated Circuits,” which is herein incorporated by reference.

LaAlO3

Various embodiments use a lanthanum aluminum oxide (LaAlO3) formed by ALD as a high-k dielectric. For example, a LaAlO3 gate dielectric can be formed using atomic layer deposition by employing a lanthanum sequence and an aluminum sequence, where the lanthanum sequence uses La(thd)3 (thd=2,2,6,6-tetramethyl-3,5-heptanedione) and ozone, and the aluminum sequence uses either trimethylaluminum, Al(CH3)3, or DMEAA, an adduct of alane (AlH3) and dimethylethylamine [N(CH3)2(C2H5)], with distilled water vapor.

A dielectric film containing LaAlO3, Al2O3, and La2O3 will have a dielectric constant ranging from the dielectric constant of Al2O3, 9, to the dielectric constant of La2O3, 30. By controlling the number of cycles of the lanthanum sequence and the number of cycles of the aluminum sequence, the amount of lanthanum and aluminum deposited on the surface region of a substrate can be controlled. Thus, a dielectric film formed by ALD using a lanthanum sequence and an aluminum sequence can be formed with a composition containing selected or predetermined percentages of LaAlO3, Al2O3, and La2O3, in which case the effective dielectric constant of the film will be selected or predetermined in the range from 9 to 30. A dielectric film containing almost entirely LaAlO3 will have a dielectric constant in the range of about 21 to about 25. The resulting dielectric containing LaAlO3 should be amorphous if an aluminum sequence is used subsequent to a lanthanum sequence.

In addition to separately controlling the number of cycles of the lanthanum sequence and the aluminum sequence in the ALD process, a dielectric film containing LaAlO3 can be engineered with selected characteristics by also controlling precursor materials for each sequence, processing temperatures and pressures for each sequence, individual precursor pulsing times, and heat treatment at the end of the process, at the end of each cycle, and at the end of each sequence. The heat treatment may include in situ annealing in various atmospheres including argon, nitrogen, and oxygen. A range of equivalent oxide thickness is associated with the capability to provide a composition having a dielectric constant in the range from about 9 to about 30, and the capability to attain physical film thickness in the range from about 0.5 to about 50 nm and above.

Additional information regarding LaAlO3 dielectric films can be found in US Patent Application Publication 20030207540A1, entitled “Atomic Layer-Deposited LaAlO3 Films For Gate Dielectrics,” which is herein incorporated by reference.

HfAlO

Various embodiments use a hafnium aluminum oxide (HfAlO3) formed by ALD as a high-k dielectric. For example, an HfAlO3 gate dielectric can be formed using atomic layer deposition by employing a hafnium sequence and an aluminum sequence, where the hafnium sequence uses HfCl4 and water vapor, and the aluminum sequence uses either trimethylaluminum, Al(CH3)3, or DMEAA, an adduct of alane (AlH3) and dimethylethylamine [N(CH3)2(C2H5)], with distilled water vapor.

A dielectric film containing HfAlO3, Al2O3, and HfO2 has a dielectric constant ranging from the dielectric constant of Al2O3, 9, to the dielectric constant of HfO2, 25. By controlling the number of cycles of the hafnium sequence and the number of cycles of the aluminum sequence, the amount of hafnium and aluminum deposited on the surface region of a substrate can be controlled. Thus, a dielectric film formed by ALD using a hafnium sequence and an aluminum sequence can be formed with a composition containing selected or predetermined percentages of HfAlO3, Al2O3, and HfO2, in which case the effective dielectric constant of the film will be selected or predetermined in the range from 9 to 25. Furthermore, using an aluminum sequence subsequent to a hafnium sequence, the resulting dielectric containing HfAlO3 should be amorphous.

In addition to separately controlling the number of cycles of the hafnium sequence and the aluminum sequence in the ALD process, a dielectric film containing HfAlO3 can be engineered with selected characteristics by also controlling precursor materials for each sequence, processing temperatures and pressures for each sequence, individual precursor pulsing times, and heat treatment at the end of the process, at the end of each cycle, and at the end of each sequence. The heat treatment may include in situ annealing in various atmospheres including argon and nitrogen.

A range of equivalent oxide thickness, teq is associated with the capability to provide a composition having a dielectric constant in the range from about 9 to about 25, and the capability to attain physical film thickness in the range of from about 2 to about 3 nm and above.

Additional information regarding HfAlO3 dielectric films can be found in US Patent Application Publication 20030227033A1, entitled “Atomic Layer-Deposited HfAlO3 Films For Gate Dielectrics,” which is herein incorporated by reference.

Pr2O3-Based La-Oxide

Various embodiments use a Pr2O3-based La-Oxide dielectric as a high-k dielectric. For example, a Pr2O3-based La-Oxide gate dielectric can be formed by electron beam evaporation as a nanolaminate of Pr2O3 and a lanthanide oxide selected from the group consisting of Nd2O3, Sm2O3, Gd2O3, and Dy2O3.

According to one embodiment, an electron gun generates an electron beam that hits a target that contains a ceramic Pr6O11 source, which is evaporated due to the impact of the electron beam. The evaporated material is then distributed throughout a chamber, and a dielectric layer of Pr2O3 is grown, forming a film on the surface of the structure that it contacts. The resultant Pr2O3 layer includes a thin amorphous interfacial layer of about 0.5 nm thickness separating a crystalline layer of Pr2O3 from the substrate on which it is grown. This thin amorphous layer is beneficial in reducing the number of interface charges and eliminating any grain boundary paths for conductance from the substrate. Other source materials can be used for forming the Pr2O3 layer, as are known to those skilled in the art.

Subsequent to the formation of the Pr2O3 layer, another lanthanide oxide is deposited on the film, converting the film from a Pr2O3 layer to a nanolaminate of Pr2O3 and the other lanthanide oxide. In various embodiments, the other lanthanide oxide is selected from the group consisting of Nd2O3, Sm2O3, Gd2O3, and Dy2O3. Depending on the lanthanide oxide selected to form the nanolaminate, a corresponding source material is used in the target for electron beam evaporation. The source material for the particular lanthanide oxide is chosen from commercial materials for forming the lanthanide oxide by electron beam evaporation, as is known by those skilled in the art.

In one embodiment, alternating layers of Pr2O3 and another selected lanthanide oxide are formed by controlled electron beam evaporation providing layers of material of predetermined thickness. This control allows the engineering of a dielectric with a predetermined thickness and composition. Through evaluation of different lanthanide oxides at various thicknesses and number of layers, a dielectric layer with a predetermined teq in a narrow range of values can be grown. Alternatively, after forming a Pr2O3 layer and a layer of another lanthanide oxide, additional layers of additional lanthanide oxides can be formed. Each layer of an additional lanthanide oxide selected from a group consisting of Pr2O3, Nd2O3, Sm2O3, Gd2O3, and Dy2O3. Consequently, a dielectric layer can be engineered with electrical characteristics suited for a given application. These electrical characteristics include teq and leakage current. A teq of less than 20 Å can be obtained, typically with sizes of about 14 Å to 8.5 Å.

In an embodiment, nanolaminates of lanthanide oxides are formed by electron beam evaporation. The lanthanide oxides used in these nanolaminates are chosen from the group consisting of Pr2O3, Nd2O3, Sm2O3, Gd2O3, and Dy2O3. The structure of the nanolaminates can be varied with any one of the group used as the initial layer formed on a substrate. Typically, the substrate is silicon based, since these lanthanide oxides are thermodynamically stable with respect to formation on a silicon surface. In an alternate embodiment, lanthanide oxide nanolaminates are formed by atomic layer deposition.

A Pr2O3 film formed on silicon has a dielectric constant of about 31 when formed with little or no interfacial layer between the Pr2O3 film and the substrate. The dielectric constants for the other lanthanide oxides are also in the range of 25-30. As a result, a dielectric layer grown by forming a nanolaminate of lanthanide oxides has a dielectric constant in the range of about 25 to about 31. However, with an interfacial layer formed between the surface of the substrate and the first lanthanide oxide, the teq of the dielectric layer is the teq of the interfacial layer in parallel with the lanthanide oxide nanolaminate. Thus, the dielectric layer formed having an interfacial layer between the substrate on which it is grown and a lanthanide oxide nanolaminate can have an effective dielectric constant considerably less than a dielectric constant associated with a nanolaminate of lanthanide oxides. This is dependent upon the dielectric constant of the interfacial material being considerably less than the dielectric constant of the lanthanide oxides used to form the nanolaminate.

A Pr2O3 layer can be formed on a silicon based substrate having a dielectric constant of about 31 with an interfacial layer of about 0.5 nm (5 Å). In another embodiment, for an interfacial layer of about 10.7 Å, an effective dielectric constant for a thin layer of Pr2O3 on silicon is about 15. Similar effective dielectric constants are associated with thin layers of Nd2O3, Sm2O3, Gd2O3, and Dy2O3 oxides on silicon. For example, a thin layer of Nd2O3 has an effective dielectric constant of about 12.9 with an interfacial layer of about 8.2 Å, a thin layer of Sm2O3 has an effective dielectric constant of about 11.4 with an interfacial layer of about 5.5 Å, a thin layer of Gd2O3 has an effective dielectric constant of about 13.9 with an interfacial layer of about 10 Å, and a thin layer of Dy2O3 has an effective dielectric constant of about 14.3 with an interfacial layer of about 12 Å. Lanthanide oxides grown on silicon with these reduced effective dielectric constants and corresponding interfacial layers can be attained with a teq equal to about 13 Å for Pr2O3, about 12.4 Å for Nd2O3, about 12.2 Å for Sm2O3, about 13 Å for Gd2O3, and about 13.3 Å for Dy2O3. Consequently, nanolaminates of these lanthanide oxides can be formed with an effective dielectric constant in the range of 11 to 15 and a teq in the range of about 12 Å to about 14 Å.

The formation of the interfacial layer is one factor in determining how thin a layer can be grown. An interfacial layer can be SiO2 for many processes forming a non-SiO2 dielectric on a silicon substrate. However, advantageously, in an embodiment forming a lanthanide oxide nanolaminate with an initial layer of Pr2O3, a thin amorphous interfacial layer is formed that is not a SiO2 layer. Typically, this interfacial layer is either an amorphous layer primarily of Pr2O3 formed between the silicon substrate and a crystalline form of Pr2O3, or a layer of Pr—Si—O silicate. The dielectric constant for Pr—Si—O silicate is significantly greater than SiO2, but not as high as Pr2O3.

Another factor setting a lower limit for the scaling of a dielectric layer is the number of monolayers of the dielectric structure necessary to develop a full band gap such that good insulation is maintained between an underlying silicon layer and an overlying conductive layer on the dielectric layer or film. This requirement is necessary to avoid possible short circuit effects between the underlying silicon layer and the overlying conductive layer used. In one embodiment, for a 0.5 nm interfacial layer and several monolayers of lanthanide grown, an expected lower limit for the physical thickness of a dielectric layer grown by forming a lanthanide oxide nanolaminate is anticipated to be in about the 2-4 nm range. Consequently, typical dielectric layers or films can be grown by forming lanthanide oxide nanolaminates having physical thickness in the range of 4 to 10 nm. The number of layers used, the thickness of each layer, and the lanthanide oxide used for each layer can be engineered to provide the desired electrical characteristics. The use of Pr2O3 as the initial layer is expected to provide excellent overall results with respect to reliability, current leakage, and ultra-thin teq.

Some embodiments include forming lanthanide oxide nanolaminates by electron beam evaporation with target material to form Pr2O3, forming lanthanide oxide nanolaminates by atomic layer deposition, and electron beam evaporation forming lanthanide oxide nanolaminates with initial layers of a lanthanide oxide other than Pr2O3. The physical thicknesses can range from about 2 nm to about 10 nm with typical thickness ranging from about 4 nm to about 10 nm. Such layers have an effective dielectric constant ranging from 11 to 31, where a layer with a typical interfacial layer has an effective dielectric constant in the range of 11 to 16, and a layer with a significantly thin interfacial layer can attain an effective dielectric constant in the range of 25 to 31. Consequently, a range for the equivalent oxide thickness of a dielectric layer formed as a lanthanide oxide nanolaminate can be engineered over a significant range. Various embodiments provide a typical teq of about 14 Å. With careful preparation and engineering of the lanthanide oxide nanolaminate limiting the size of interfacial regions, a teq down to 2.5 Å or lower is anticipated.

A lanthanide doped TiOx dielectric layer can be formed by depositing titanium and oxygen onto a substrate surface by atomic layer deposition and depositing a lanthanide dopant by atomic layer deposition onto the substrate surface containing the deposited titanium and oxygen. The dopant can be selected from a group consisting of Nd, Tb, and Dy.

In one embodiment, a method of forming a dielectric film includes depositing titanium and oxygen onto a substrate surface by atomic layer deposition and depositing a lanthanide dopant by atomic layer deposition onto the substrate surface containing the deposited titanium and oxygen. In one embodiment, the titanium sequence and the lanthanide dopant sequence include using precursors that form oxides of the titanium and the lanthanide dopant. For example, precursor TiI4 with H2O2 as its reactant precursor in an ALD process can form TiOx, and precursor La(thd)3 (thd=2,2,6,6-tetramethyl-3,5-heptanedione) with ozone as its reactant precursor in an ALD process can form La2O3.

Depositing the lanthanide dopant includes regulating the deposition of the lanthanide dopant relative to the titanium and oxygen deposited on the substrate surface to form a dielectric layer containing TiOx doped with a predetermined percentage of the lanthanide. In a further embodiment, depositing a lanthanide dopant includes depositing a lanthanide selected from a group consisting of Nd, Tb, and Dy.

The lanthanide dopant can be included in the TiOx film using different embodiments for atomic layer deposition. In one embodiment, a lanthanide can be doped in the TiOx film by pulsing a lanthanide dopant sequence in place of a titanium sequence. The lanthanide dopant level is then controlled by regulating the number of cycles of the lanthanide dopant sequence with respect to the number of cycles of the titanium sequence. In another embodiment, a lanthanide can be doped in the TiOx film by pulsing a lanthanide dopant precursor substantially simultaneously with a titanium precursor. The titanium/lanthanide dopant sequence includes a precursor for oxidizing the titanium/lanthanide dopant at the substrate surface. The lanthanide dopant level is then controlled by regulating the mixture of the titanium-containing precursor and the lanthanide-containing precursor.

Dielectric films of lanthanide doped TiOx formed by atomic layer deposition can provide not only ultra thin teq films, but also films with relatively low leakage current. In addition to using ALD to provide precisely engineered film thicknesses, attainment of relatively low leakage current is engineered by doping with lanthanides selected from a group consisting of Nd, Tb, and Dy. Though a layer of undoped TiOx can be amorphous, which assists the reduction of leakage current, doping with these lanthanides yields a doped amorphous TiOx with enhanced leakage current characteristics. Leakage currents on the order of 10−7 Å/cm2 or smaller in TiOx layers doped with Nd, Tb, or Dy can be attained, which are orders of magnitude smaller than for undoped TiOx. Further, the breakdown electric fields are several factors larger for layers of TiOx doped with Nd, Tb, or Dy than for layers of undoped TiOx.

The doping of the TiOx layer with a lanthanide occurs as a substitution of a lanthanide atom for a Ti atom. The resultant doped TiOx layer is a layer of amorphous Ti1-yLyOx, where L is a lanthanide. Controlling the ALD cycles of the titanium sequence and the lanthanide dopant sequence allows a Ti1-yLyLyOx, or lanthanide doped TiOx, dielectric layer to be formed where the lanthanide, L, can range from about 5% to about 40% of the dielectric layer formed. Such TiOx layers doped with Nd, Tb, or Dy formed by ALD can provide the reduced leakage current and increased breakdown mentioned above.

A HfSiON dielectric can be formed by atomic layer deposition. A HfSiON layer thickness is controlled by repeating for a number of cycles a sequence including pulsing a hafnium-containing precursor into a reaction chamber, pulsing an oxygen-containing precursor into the reaction chamber, pulsing a silicon-containing precursor into the reaction chamber, and pulsing a nitrogen-containing precursor until a desired thickness is formed.

The hafnium-containing precursor includes a HfCl4 precursor in some embodiments, and a HfI4 precursor in other embodiments. According to some embodiments, the oxygen-containing precursor includes water vapor or a vapor solution of H2O—H2O2 into the reaction chamber. According to some embodiments, the silicon-containing precursor includes a SiCl4 precursor. A nitrogen-containing precursor includes a NH3 precursor in some embodiments. NH3 annealing at about 550° C. can also be performed.

A Zr—Sn—Ti—O dielectric layer can be formed by depositing titanium and oxygen onto a substrate surface by atomic layer deposition, depositing zirconium and oxygen onto a substrate surface by atomic layer deposition, and depositing tin and oxygen onto a substrate surface by atomic layer deposition. Metal chloride precursors can be pulsed for each metal in the Zr—Sn—Ti—O. In some embodiments, the dielectric film is formed by forming TiO2 onto a surface by atomic layer deposition, depositing zirconium and oxygen onto the surface by atomic layer deposition, and depositing tin and oxygen onto the surface by atomic layer deposition. The TiO2 deposition can include pulsing a TiCl4 precursor. The zirconium and oxygen deposition can include pulsing a ZrCl4 precursor. The tin and oxygen deposition can include pulsing a SnCl4 precursor. In various embodiments, the formation of the dielectric film is controlled such that the dielectric film has a composition substantially of ZrySnxTi1-x-yO4 with 0.3<y<0.7 and 0<x<0.2.

In some embodiments, the dielectric film is formed by forming TiO2 onto a surface by atomic layer deposition using a TiI4 precursor; depositing zirconium and oxygen by atomic layer deposition using a zirconium halide precursor following forming TiO2; and depositing tin and oxygen by atomic layer deposition using a tin halide precursor following depositing zirconium and oxygen. The zirconium and oxygen deposition can include pulsing a ZrI4 precursor. The tin and oxygen deposition can include pulsing a SnI4 precursor. In various embodiments, the formation of the dielectric film is controlled such that the dielectric film has a composition substantially of ZrySnxTi1-x-yO4 with 0.3<y<0.7 and 0<x<0.2. In various embodiments, the formation of the dielectric film is controlled such that the dielectric film has a composition substantially of Zr0.2Sn0.2Ti0.6O2.

The high-k dielectric film can be formed as a metal oxynitride, formed by atomic layer deposition of a plurality of reacted monolayers. The monolayers comprise at least one each of a metal, an oxide and a nitride. According to various embodiments, the metal oxynitride layer is formed from zirconium oxynitride, hafnium oxynitride, tantalum oxynitride, or mixtures thereof.

According to various process embodiments, a plurality of gaseous precursors can be separately introduced to a surface of the semiconductor substrate. The gaseous precursors comprise a metal gaseous precursor and at least two nonmetallic gaseous precursors. A first gaseous precursor of the plurality of gaseous precursors is purged or evacuated from the surface of the semiconductor substrate before a second gaseous precursor of the plurality of gaseous precursors is introduced to the surface of the semiconductor substrate. The metal gaseous precursor can include zirconium tetrachloride, zirconium tetraiodide, hafnium tetrachloride, hafnium tetraiodide, or a halogenated tantalum. An oxygen-containing gaseous precursor and a nitrogen-containing gaseous precursor are separately introduced to the surface of the semiconductor substrate. For example, water or hydrogen peroxide can be used as the oxygen-containing gaseous precursor and at least one of ammonia, tert-butylamine, allylamine, and 1,1-dimethylhydrazine can be used as the nitrogen-containing gaseous precursor. Thus, monolayers of metal, oxide, and nitride are formed, and the metal, oxide, and nitride monolayers are reacted to form the metal oxynitride layer.

The high-k dielectric film can be HfO2/Hf, which can be formed by depositing a hafnium metal layer on a substrate surface by atomic layer deposition and depositing a hafnium oxide layer on the hafnium metal layer by atomic layer deposition to form a hafnium oxide dielectric layer substantially free of silicon oxide. In general, a layer of a metal is formed on a substrate by atomic layer deposition, and an oxide of the metal is formed on the metal by atomic layer deposition.

A hafnium nitrate precursor, such as an anhydrous hafnium nitrate precursor, can be used to form the layer of hafnium. A layer of hafnium oxide can be formed using an anhydrous hafnium nitrate precursor and a water vapor precursor. The substrate may be maintained at about 180° C. during the formation of the layer of hafnium and the formation of the layer of hafnium oxide.

Additional information regarding metal oxide/metal dielectric films, such as HfO2/Hf, can be found in US Patent Application Publication 2004/0175882A1, entitled “Atomic Layer Deposited Dielectric Layers,” which is herein incorporated by reference.

ZrAlxOy

The high-k dielectric film can be ZrAlxOy, which can be formed by ALD by pulsing a zirconium-containing precursor onto a substrate, pulsing a first oxygen-containing precursor, pulsing an aluminum-containing precursor, and pulsing a second oxygen-containing precursor to form ZrAlxOy. A precursor can be used that includes both zirconium and oxygen to provide the zirconium and oxygen in one pulsing process, and a precursor can be used that contains both aluminum and oxygen to provide the aluminum and oxygen in one pulse. In various embodiments, the dielectric layer contains Zr4AlO9. An interfacial layer of silicon oxide or silicon between the substrate and the ZrAlxOy dielectric can be less than about 1 nm. The zirconium-containing precursor can be selected from ZrCl4 and ZrI4 precursors. The aluminum-containing precursor can be selected from trimethylaluminum and DMEAA. Oxygen-containing precursors can be selected from H2O, H2O2, and a H2O—H2O2 mixture.

The high-k dielectric film can be ZrTiO4, which can be formed by ALD by pulsing a titanium-containing precursor onto a substrate, and pulsing a zirconium-containing precursor to form an oxide containing Zr and Ti. The pulsing of the titanium-containing precursor and the pulsing of the zirconium-containing precursor is controlled to provide a dielectric layer with a predetermined zirconium to titanium ratio. In various embodiments, the ZrTiO4 film is formed with a Zr/Ti ratio of about 0.4/0.6. A zirconium-containing precursor used to form the oxide containing Zr and Ti can include zirconium tertiary-butoxide. The titanium-containing precursor can be selected from TiCl4, TiI4, Ti(OCH(CH3)2)4, and Ti(OC2H5)4. The first pulsing of the titanium-containing precursor can be performed before pulsing the zirconium tertiary-butoxide precursor.

Reactant precursors that can be used after pulsing the titanium-containing precursor and pulsing the zirconium tertiary-butoxide precursor can be selected from H2O, H2O2, ROH, N2O, O3, and O2. The substrate can be kept at a temperature ranging from about 200° C. to about 400° C. A silicon nitride layer can be formed between the substrate and the film containing ZrTiO4. The ALD-formed film can be a nanolaminate of ZrO2 and TiO2.

The high-k dielectric film can be a zirconium-doped tantalum oxide dielectric layer, such as can be formed by depositing tantalum by atomic layer deposition onto a substrate surface and depositing a zirconium dopant by atomic layer deposition onto the substrate surface. The formation of the zirconium-doped tantalum oxide can include pulsing a tantalum-containing precursor to deposit tantalum onto a substrate surface, pulsing an oxygen-containing precursor to deposit oxygen onto the substrate surface, repeating for a number of cycles the pulsing of the tantalum-containing precursor and the pulsing of the oxygen-containing precursor, and substituting a zirconium cycle for one or more cycles of the pulsing of the tantalum-containing precursor. The zirconium cycle includes pulsing a zirconium-containing precursor to deposit zirconium onto the substrate surface. A reactant precursor is selected to produce an oxidizing reaction for the zirconium at the substrate surface. According to various embodiments, a tantalum-containing precursor includes Ta(OC2H5)5, and a zirconium-containing precursor includes ZrI4.

The high-k dielectric layer can be formed by depositing HfO2-Silicon-Nitride by atomic layer deposition. The HfO2-Silicon-Nitirde is formed on SiO2. The silicon nitride can be formed using SiCl4 and NH3 gases, and HfO2 can be formed by ALD using hafnium tetraiodide and oxygen as precursors. Anhydrous Hf(NO3)4 and H2O vapor may also be used.

Ru Gate and La-Oxide

Various embodiments use a lanthanide oxide high-k dielectric with a ruthenium or ruthenium oxide gate. In various embodiments, the lanthanide oxide dielectric layer is formed by depositing lanthanum by atomic layer deposition onto a substrate surface using a trisethylcyclopentadionatolanthanum precursor or a trisdipyvaloylmethanatolanthanum precursor. A ruthenium gate on a lanthanide oxide dielectric layer provides a gate structure that effectively prevents a reaction between the gate and the lanthanide oxide dielectric layer.

Additional information regarding ruthenium on lanthanide oxide can be found in U.S. patent application Ser. No. 10/926,812, filed Aug. 26, 2004, entitled “Ruthenium Gate For a Lanthanide Oxide Dielectric Layer,” which is herein incorporated by reference.

TiAlOX

The high-k dielectric film can be provided by a titanium aluminum oxide film, which can be formed by depositing titanium and/or aluminum by atomic layer deposition onto a substrate surface. The deposited titanium and/or aluminum is annealed using atomic oxygen. After annealing, a layer of titanium aluminum oxide is formed on the annealed layer to form a contiguous layer of titanium aluminum oxide.

Forming the dielectric includes forming an insulating metal oxide, which includes forming a first layer of at least one of a first metal and a second metal by atomic layer deposition, annealing the first layer using oxygen, and forming, after annealing the first layer, a second layer of an insulating metal oxide of the first metal and the second metal onto the first layer by atomic layer deposition to form a contiguous layer. The first layer can include a layer of the first metal and the second metal. The first layer can have a thickness of about one monolayer or at most substantially two monolayers.

According to various embodiments, a first layer of titanium aluminum oxide is formed by atomic layer deposition, and the first layer is annealed using atomic oxygen. A second layer of titanium aluminum oxide is formed onto the first layer by atomic layer deposition, after annealing the first layer, to form a contiguous layer. The first layer of titanium aluminum oxide can be formed using TiI4 or trimethylaluminum as a precursor, and the second layer of titanium aluminum oxide can be formed using TiCl4 as a precursor. The titanium oxide and the titanium aluminum oxide film can be formed as a nanolaminate.

The high-k dielectric film can be provided by a lanthanum aluminum oxide dielectric layer, which can be formed by depositing aluminum and lanthanum by atomic layer deposition onto a substrate surface in which precursors to deposit the lanthanum include a trisethylcyclopentadionatolanthanum precursor and/or a trisdipyvaloylmethanatolanthanum precursor, and a metal (e.g. Al) containing precursor is also used. The lanthanum aluminum oxide can be formed as a compound of lanthanum oxide and aluminum oxide. The dielectric layer can include LaAlO3.

The high-k dielectric can be provided as a lanthanum hafnium oxide layer, which can be formed by depositing hafnium and lanthanum by atomic layer deposition onto a substrate surface. The process includes introducing a lanthanum-containing precursor to a substrate, and introducing a hafnium-containing precursor to the substrate. Embodiments include methods and apparatus in which precursors to deposit the lanthanum include a trisethylcyclopentadionatolanthanum (La(EtCp)3) precursor, a tris(2,2,6,6-tetramethyl-3,5-heptanedionato) lanthanum (III) precursor, a trisdipyvaloylmethanatolanthanum precursor, or a tris(2,2,6,6-tetramethyl-3,5-heptanedionato)lanthanum (III) tetraglyme adduct precursor.

The high-k dielectric can be provided as a hafnium tantalum oxide film, which can be formed by depositing hafnium and tantalum by atomic layer deposition onto a substrate surface. A tantalum-containing precursor can include a tantalum ethoxide precursor, and a hafnium-containing precursor can include a hafnium nitrate precursor.

The high-k dielectric can be provided as hafnium titanium oxide, such as HfTiO4, formed by ALD using precursors substantially free of chlorine and carbon. Precursors capable of being used include a titanium halide precursor such as a titanium iodine precursor, a titanium nitride precursor, a titanium isopropoxide precursor, and a hafnium halide precursor such as a hafnium chloride precursor.

Amorphous Lanthanide Doped TiOX

The high-k dielectric can be provided as an ALD-formed amorphous dielectric layer of titanium oxide (TiOX) doped with lanthanide elements, such as samarium, europium, gadolinium, holmium, erbium and thulium. The dielectric structure is formed by depositing titanium oxide by atomic layer deposition onto a substrate surface using precursor chemicals, followed by depositing a layer of a lanthanide dopant, and repeating to form a sequentially deposited interleaved structure. The leakage current of the dielectric layer is reduced when the percentage of the lanthanide element doping is optimized. The amorphous dielectric layer is formed on a substrate by atomic layer deposition at a predetermined temperature, such as within a range of approximately 100° C. to 250° C. The amorphous dielectric layer can be comprised of a plurality of individual titanium oxide layers, with at least one lanthanide layer interleaved between each individual one of the titanium oxide layers. The dielectric layer can have a titanium to lanthanide ratio selected to obtain a dielectric constant value of from 50 to 100, and can be selected with a titanium to lanthanide ratio selected to obtain a leakage current of less than 10−8 A/cm2 and a breakdown voltage of greater than 2.0 MV/cm.

The high-k dielectric can be provided as a Ti gate dielectric, which may be formed by providing a substrate assembly in a vacuum chamber, and forming a gate dielectric on the surface, including forming a metal oxide on at least a portion of the surface of the substrate assembly by electron beam evaporation, and generating an ion beam using an inert gas to provide inert gas ions for contacting the metal oxide during formation thereof. An environment including oxygen (e.g. ozone) can be provided in the vacuum chamber to form the metal oxide in the oxygen environment. The metal oxide can be selected from the group consisting of TiO2, Y2O3, Al2O3, ZrO2, HfO2, Y2O3—ZrO2, ZrSiO4, LaAlO3, and MgAl2O4.

Additional information regarding titanium aluminum oxide films can be found in U.S. Pat. No. 6,495,436, entitled “Formation Of Metal Oxide Gate Dielectric,” which is herein incorporated by reference.

TiO2

The high-k dielectric can be provided as a TiO2 dielectric, which can be physically vapor formed as a high purity metal layer over the semiconductor substrate. After forming such a layer, the high purity metal layer can be oxidized employing atomic oxygen generated in a high density plasma environment to form the dielectric material. The physically vapor formed high purity metal layer can have at least about 99.9% purity over the semiconductor substrate. The physical vapor formation can include electron beam evaporation. Prior to the electron beam evaporation, the vacuum chamber can be evacuated to a base pressure of about 1×10−7 Torr or lower, and a low-energy ion-bombardment source is directed towards the semiconductor substrate during the electron beam evaporation. A low-energy argon ion-bombardment can be directed towards the semiconductor substrate during the electron beam evaporation. The high purity metal layer can include two or more high purity metals, such as a metal-silicon alloy. The high purity metal can be selected from titanium, yttrium, zirconium, hafnium and various mixtures thereof.

Additional information regarding TiO2 films can be found in U.S. Pat. No. 6,534,420, entitled “Methods For Forming Dielectric Materials and Methods for Forming Semiconductor Devices,” which is herein incorporated by reference.

Amorphous HfO2

The high-k dielectric can include hafnium oxide, which can be formed by forming a thin hafnium (Hf) film by thermal evaporation at a low substrate temperature, and radically oxidizing the thin hafnium film using a krypton/oxygen (Kr/O2) high-density plasma to form the gate dielectric layer of hafnium oxide (HfO2). The resulting gate dielectric layer is thermally stable in contact with silicon and is resistive to impurity diffusion at the HfO2/silicon interface. The formation of the HfO2 eliminates the need for a diffusion barrier layer, allows thickness uniformity of the field oxide on the isolation regions, and preserves the atomically smooth surface of the silicon substrate. The hafnium layer can be formed by electron beam evaporation.

Additional information regarding HfO2 and other amorphous high-k gate oxide films can be found in U.S. Pat. No. 6,514,828, entitled “Method of Fabricating a Highly Reliable Gate Oxide,” which is herein incorporated by reference.

CoTiO3

The high-k dielectric can be provided by CoTiO3, which can be formed from alloys such as cobalt-titanium. These alloys are thermodynamically stable such that the gate dielectrics formed will have minimal reactions with a silicon substrate or other structures during any later high temperature processing stages. The underlying substrate surface smoothness is preserved by using a thermal evaporation technique to deposit the layer to be oxidized. A metal alloy layer is evaporation deposited on the body region, and the metal alloy layer is oxidized to form a metal oxide layer on the body region. Cobalt and titanium can be evaporation deposited, such as by electron beam evaporation. The evaporation deposition of the metal alloy layer can be performed at a substrate temperature range of 100-150° C., and the oxidation of the metal alloy layer can be performed at a temperature of approximately 400° C. A krypton (Kr)/oxygen (O2) mixed plasma can be used in the oxidization process.

The high-k gate dielectric can be formed from elements like zirconium, such as ZrO2, which are thermodynamically stable such that the gate dielectric will have little reaction with a silicon substrate or other structures during any later high temperature processing stages. The gate dielectric can be formed by evaporation depositing a metal layer on the body region, the metal being chosen from the group IVB elements of the periodic table, and oxidizing the metal layer to form a metal oxide layer on the body region. The metal layer can include a zirconium layer, which can be deposited by electron beam evaporation. The substrate temperature range for the deposition can be within a range of 150-400° C. The oxidation can be performed using atomic oxygen or with a krypton (Kr)/oxygen (O2) mixed plasma, for example.

Group IIIB/Rare Earth Series (Crystalline or Amorphous Y2O3 and Gd2O3)

The high-k dielectric can be provided using elements such as yttrium and gadolinium, which are thermodynamically stable such that the resulting gate dielectrics have minimal reaction with a silicon substrate or other structures during any later high temperature processing stages. The underlying substrate surface smoothness is preserved using a thermal evaporation technique to deposit the layer to be oxidized. The gate dielectric can be formed by evaporation depositing a metal layer on the body region, where the metal is chosen from a group consisting of the group IIIB elements and the rare earth series of the periodic table, and by oxidizing the metal layer to form a metal oxide layer on the body region. The metal layer can be yttrium and can be gadolinium. Electron beam evaporation can be used. The substrate temperature for the deposition can be approximately 150-400° C. Atomic oxygen and a krypton (Kr)/oxygen (O2) mixed plasma can be used to oxidize the metal layer, for example.

Additional information regarding gate oxides formed from elements such as yttrium and gadolinium can be found in U.S. Pat. No. 6,844,203 entitled “Gate Oxides, and Methods of Forming,” which is herein incorporated by reference.

Praseodymium Oxide

The gate dielectric can be provided by a praseodymium oxide. The Pr gate oxide is thermodynamically stable so that the oxide reacts minimally with a silicon substrate or other structures during any later high temperature processing stages. The underlying substrate surface smoothness is preserved using a thermal evaporation technique to deposit a Pr layer to be oxidized. The gate dielectric can be formed by evaporation depositing a praseodymium (Pr) layer on the body region, and oxidizing the Pr layer to form a Pr2O3 layer on the body region. Electron beam evaporation can be used. The substrate temperature for the deposition can be in an approximate range of 150-400° C. Atomic oxygen and a krypton (Kr)/oxygen (O2) mixed plasma can be used to oxidize the Pr layer, for example. The Pr2O3 layer can be formed to have an equivalent oxide thickness of less than 2 nm.

The high-k dielectric can be provided by a metal oxynitride such as ZrOXNY. The addition of nitrogen to the microstructure of the gate dielectric promotes an amorphous phase that provides the gate dielectric with improved electrical properties. The underlying substrate surface smoothness is preserved by using a thermal evaporation technique to first deposit a metal layer. The gate dielectric can be formed by evaporation depositing a metal layer such as a zirconium layer on the body region, oxidizing the metal layer, and nitriding the metal layer. Electron beam evaporation can be used. The substrate temperature for the deposition can be in an approximate temperature range of 150-400° C. Atomic oxygen and a krypton (Kr)/oxygen (O2) mixed plasma, for example, can be used to oxidize the metal layer. The metal layer can be annealed in NH3 at a temperature of approximately 700° C.

The high-k dielectric can be provided by LaAlO3. A LaAlO3 gate dielectric can be formed by evaporating Al2O3 at a given rate, evaporating La2O3 at another rate, and controlling the two rates to provide an amorphous film containing LaAlO3 on a transistor body region. The evaporation deposition of the LaAlO3 film is performed using two electron guns to evaporate dry pellets of Al2O3 and La2O3. The two rates for evaporating the materials are selectively chosen to provide a dielectric film composition having a predetermined dielectric constant ranging from the dielectric constant of an Al2O3 film to the dielectric constant of a La2O3 film. Electron beam evaporation can be used. A predetermined dielectric constant can be achieved by controlling the evaporation rates.

Additional information regarding evaporated LaAlO3 gate dielectrics can be found in U.S. Pat. No. 6,893,984, entitled “Evaporated LaAlO3 Films for Gate Dielectrics,” which is herein incorporated by reference.

TiOX

The high-k dielectric can be provided by TiOX. The dielectric film can be formed by ion assisted electron beam evaporation of TiO2 and electron beam evaporation of a lanthanide selected from a group consisting of Nd, Tb, and Dy. The growth rate is controlled to provide a dielectric film having a lanthanide content ranging from about ten to about thirty percent of the dielectric film. These dielectric films containing lanthanide doped TiOx are amorphous and thermodynamically stable such that the lanthanide doped TiOx will have minimal reaction with a silicon substrate or other structures during processing.

The film can be formed by evaporating TiO2 at a first rate, evaporating a lanthanide at a second rate, and controlling the first rate and the second rate to grow a dielectric film on a substrate, the dielectric film containing TiOx doped with the lanthanide. The lanthanide can be selected from a group consisting of Nd, Tb, Dy. Electron beam evaporation can be used. The rates can be controlled to selectively grow the dielectric film doped in the range from about 10% to about 30% lanthanide. The rates can be controlled so that the dielectric film has a dielectric constant ranging from about 50 to about 110.

The high-k dielectric can be provided by TiOX, which can be formed by ion assisted electron beam evaporation of Ti, electron beam evaporation of a lanthanide selected from a group consisting of Nd, Tb, and Dy, and oxidation of the evaporated Ti/lanthanide film in a Kr/oxygen plasma. The growth rate is controlled to provide a dielectric film having a lanthanide content ranging from about five to about forty percent of the dielectric film. These dielectric films containing lanthanide doped TiOx are amorphous and thermodynamically stable such that the lanthanide doped TiOx will have minimal reaction with a silicon substrate or other structures during processing. Electron beam evaporation can be used. The rates can be controlled to provide a lanthanide doped Ti film on the substrate for growing a dielectric film doped in the range from about 5% to about 40% lanthanide. The rates can be controlled to provide the film with a dielectric constant ranging from about 50 to about 110.

The dielectric can be provided by Y—Si—O dielectrics formed by evaporation deposition techniques.

Oxidation of Metals

The high-k dielectric can be provided by oxidizing metal. Examples of metal oxides include PbO, Al2O3, Ta2O5, TiO2, ZrO2, and Nb2O5.

Additional information regarding oxidation of metals for high-k dielectrics can be found in US Patent Application Publication 2003/0043637 entitled “Flash Memory With Low Tunnel Barrier Interpoly Insulators,” which is herein incorporated by reference.

HfO2/La2O3

The high-k dielectric can be provided by an HfO2/La2O3 nanolaminate structure. The dielectric can be formed by forming a first metal-containing dielectric layer over the surface of the substrate, the metal comprising an element selected from Group IVB of the periodic table, and forming a second metal-containing dielectric layer over the first metal-containing dielectric layer. For example, the first metal-containing dielectric layer can include hafnium, and the second metal-containing dielectric layer comprises lanthanum.

A layer of silicon dioxide can be formed to overlie at least one portion of the surface; and the first metal-containing dielectric layer can be formed by forming a metal layer over the layer of silicon dioxide, and combining metal of the metal layer with oxygen of the silicon dioxide layer to form a metal oxide dielectric material. The second metal-containing dielectric layer can be an element selected from Group IIIB of the periodic table.

According to various embodiments, the dielectric is formed by forming a hafnium-containing layer, forming a lanthanum-containing layer over the hafnium-containing layer, and exposing the hafnium-containing layer and the lanthanum-containing layer to an oxygen-comprising atmosphere and heating the hafnium-containing layer and the lanthanum-containing layer to a temperature effective to form a hafnium-containing dielectric layer and a lanthanum-containing dielectric layer. Physical vapor deposition can be used. The thickness of each of the hafnium-containing dielectric layer and the lanthanum-containing dielectric layer can be less than about 5 nm. The ratio of the hafnium thickness to the lanthanum thickness can be from about 1 to 3 to about 1 to 4.

Additional information regarding nanolaminates such as HfO2/La2O3 as high-k dielectrics can be found in US Patent Application Publication 2002/0192974 entitled “Dielectric Layer Forming Method and Devices Formed Therewith,” which is herein incorporated by reference.

La2O3/Hf2O3

The high-k dielectric can be provided by an La2O3/Hf2O3 nanolaminate. Alternate layers of hafnium oxide and lanthanum oxide over a substrate can be deposited to form a composite. The dielectric can be provided by forming one hafnium oxide monolayer, forming one lanthanum oxide monolayer, and repeating to form a plurality of single hafnium oxide monolayers interspersed among a plurality of single lanthanum oxide monolayers. Multiple hafnium oxide monolayers can be formed to create a hafnium oxide multilayer, and multiple lanthanum oxide monolayers can be formed to create a lanthanum oxide multilayer. A plurality of hafnium oxide multilayers can be interspersed among a plurality of lanthanum oxide multilayers. The hafnium oxide can comprise thermally stable, crystalline hafnium oxide, and the lanthanum oxide can comprise thermally stable, crystalline lanthanum oxide.

According to various methods, at least one monolayer of a first material is chemisorbed over a substrate, where the first material comprises a first metal. At least some of the chemisorbed first material is treated and an oxide of the first metal is formed. At least one monolayer of a second material (second metal) is chemisorbed on the first metal oxide. An oxide of the second metal is formed. One of the first and second metals comprises hafnium and the other comprises lanthanum. The first material can comprise HfCl4, and the chemisorbed first material can be treated by exposure to H2O to form HfO2. The first material can comprise La(thd)3, and the chemisorbed first material can be treated by exposure to H2O to form La2O3.

Additional information regarding nanolaminates such a La2O3/Hf2O3 as high-k dielectrics can be found in US Patent Application Publication 2004/0038554 entitled “Composite Dielectric Forming Methods and Composite Dielectrics,” which is herein incorporated by reference.

HfO2/ZrO2

The high-k dielectric can be provided by a HfO2/ZrO2 nanolaminate, which can be formed by atomic layer deposition of HfO2 using a HfI4 precursor followed by the formation of ZrO2 on the HfO2 layer. The HfO2 layer thickness is controlled by repeating for a number of cycles a sequence including pulsing the HfI4 precursor into a reaction chamber, pulsing a purging gas into the reaction chamber, pulsing a first oxygen-containing precursor into the reaction chamber, and pulsing the purging gas until the desired thickness is formed. These gate dielectrics containing HfO2/ZrO2 nanolaminates are thermodynamically stable such that the HfO2/ZrO2 nanolaminates will have minimal reaction with a silicon substrate or other structures during processing.

The layer of zirconium oxide can be formed by rapid thermal CVD at about 500° C. A nitrogen anneal between about 700° C. and about 900° C. can be performed after the layer of zirconium oxide is formed. The layer of hafnium oxide can be formed by pulsing a first oxygen-containing precursor, such as water vapor, into the reaction chamber after pulsing the HfI4 precursor into the reaction chamber.

Additional information regarding nanolaminates such a HfO2/ZrO2 as high-k dielectrics can be found in US Patent Application Publication 2004/0023461 entitled “Atomic Layer Deposited Nanolaminates of HfO2/ZrO2 films as Gate Dielectrics,” which is herein incorporated by reference.

Lanthanide Oxide/Zirconium Oxide

The high-k dielectric can be provided by a lanthanide oxide/zirconium oxide nanolaminate. According to various embodiments, the ZrO2 is deposited by multiple cycles of reaction sequence atomic layer deposition (RS-ALD) that includes depositing a ZrI4 precursor onto the surface of the substrate in a first pulse followed by exposure to H2O/H2O2 in a second pulse, thereby forming a thin ZrO2 layer on the surface. After depositing the ZrO2 layer, the lanthanide oxide layer is deposited by electron beam evaporation. The composite laminate zirconium oxide/lanthanide oxide dielectric layer has a relatively high dielectric constant and can be formed in layers of nanometer dimensions.

Various embodiments provide a layer of ZrO2, and a layer of a lanthanide oxide having a thickness of about 2-12 nm on the ZrO2 layer. The ZrO2 layer has a thickness of about 1-6 nm, and the composite laminate dielectric layer has a thickness of about 3-18 nm. The lanthanide oxide can include Pr2O3, Nd2O3, Sm2O3, Gd2O3, Dy2O3 and PrTiXOY. According to various embodiments, the composite laminate dielectric layer has a dielectric constant between about 12 and about 23. The ZrO2 layer can be formed by atomic layer deposition from a ZrI4 precursor followed by oxidation with H2O/H2O2, and the lanthanide oxide layer can be formed by electron beam evaporation of a lanthanide oxide.

The high-k dielectric can be provided by a lanthanide oxide/hafnium oxide nanolaminate, such as can be formed by forming a layer of hafnium oxide by atomic layer deposition and forming a layer of a lanthanide oxide by electron beam evaporation. According to various embodiments, the combined thickness of lanthanide oxide layers is limited to between about 2 nm and about 10 nm. Multi-layers of hafnium oxide can be formed, where each layer of lanthanide oxide is limited to a thickness between about 2 nm and 10 nm. Some embodiments limit the combined thickness of hafnium oxide layers to a thickness between about 2 nm and about 10 nm. The lanthanide oxide can include Pr2O3, Nd2O3, Sm2O3, Gd2O3, and Dy2O3. The substrate temperature for the deposition can range between about 100° C. to about 150° C. The hafnium oxide can be formed using a HfI4 precursor, and the lanthanide oxide can be formed on the layer of hafnium oxide by electron beam evaporation.

Additional information regarding nanolaminates such a lanthanide oxide/hafnium oxide as high-k dielectrics can be found in US Patent Application Publication 2005/0020017 entitled “Lanthanide Oxide/Hafnium Oxide Dielectric Layers,” which is herein incorporated by reference.

Lanthanide Oxide/Hafnium Oxide

The high-k dielectric can be provided by a lanthanide oxide/hafnium oxide nanolaminate. The hafnium oxide can be formed by chemical vapor deposition and the lanthanide oxide can be formed by electron beam evaporation. Forming the layer of hafnium oxide by chemical vapor deposition using precursors that do not contain carbon permits the formation of the dielectric layer without carbon contamination. Various embodiments limit a combined thickness of lanthanide oxide layers to a thickness ranging from about 2 nm to about 10 nm. Various embodiments provide a multilayer of lanthanide oxide, with each layer of lanthanide oxide having a thickness ranging from about 2 nm to about 10 nm. Various embodiments limit a combined thickness of hafnium oxide layers to a thickness ranging from about 2 nanometers to about 10 nanometers. The lanthanide oxide can be selected from Pr2O3, Nd2O3, Sm2O3, Gd2O3, and Dy2O3. The substrate can be maintained at a temperature ranging from about 100° C. to about 150° C. during electron beam deposition and the substrate can be maintained at a temperature ranging from about 200° C. to about 400° C. during chemical vapor deposition. The dielectric layer can be formed by forming a layer of hafnium oxide on a substrate by chemical vapor deposition using a Hf(NO3)4 precursor, and forming a layer of a lanthanide oxide on the layer of hafnium oxide by electron beam evaporation.

Additional information regarding nanolaminates such a lanthanide oxide/hafnium oxide as high-k dielectrics can be found in US Patent Application Publication 2004/0262700 entitled “Lanthanide Oxide/Hafnium Oxide Dielectric Layers,” which is herein incorporated by reference.

PrOx/ZrO2

The high-k dielectric can be provided by a PrOX/ZrO2 nanolaminate. The nanolaminate layered dielectric structure is formed by depositing praseodymium by atomic layer deposition onto a substrate surface using precursor chemicals, followed by depositing zirconium onto the substrate using precursor chemicals, and repeating to form the thin laminate structure. The dielectric layer can be formed using either a reaction sequence atomic layer deposition, a metallo-organic chemical vapor deposition, or a combination thereof. The praseodymium oxide layer includes forming an amorphous oxide including Pr6O1, Pr2O3, PrO3, and PrO2, and combinations thereof. The zirconium oxide layer can include an amorphous oxide including ZrO, ZrO2, and combinations thereof.

Each individual one of the praseodymium oxide layers can be less than or equal to two monolayers in thickness, or can be a continuous monolayer. The resulting monolayer has a root mean square surface roughness that is less than one tenth of the layer thickness. The thickness of the praseodymium oxide layer and the zirconium oxide layer can be selected to provide the dielectric structure with a dielectric constant greater than 30. The dielectric film can be formed at a temperature of less than 350° C. The dielectric film can be formed using a precursor material comprising a formula Pr(OCMe2CH2Me)3.

Additional information regarding nanolaminates such a lanthanide oxide/hafnium oxide as high-k dielectrics can be found in U.S. patent application Ser. No. 11/010,766, filed Dec. 13, 2004 entitled “Hybrid ALD-CVD of PrXOY/ZrO2 Films as Gate Dielectrics,” which is herein incorporated by reference.

Hf3N4/HfO2

The high-k dielectric can be provided by a hafnium nitride (Hf3N4)/hafnium oxide (HfO2) nanolaminate. At least one hafnium oxide layer and at least one hafnium nitride layer form the nanolaminate. Both the hafnium oxide and the hafnium nitride can be formed using atomic layer deposition. The dielectric layer can include an amorphous dielectric that includes HfO2, Hf3N4, and combinations thereof.

The hafnium oxide layer can be comprised of a plurality of individually deposited hafnium oxide layers, where each individual one of the hafnium oxide layers is less than or equal to two monolayers in thickness. Each individual one of the hafnium oxide layers can be a continuous monolayer. Each individual one of the hafnium oxide layers can have a thickness within a range from 1.3 to 1.5 Å. The resulting dielectric layer can have a root mean square surface roughness that is less than one tenth of the layer thickness. A ratio of a thickness of hafnium oxide to a thickness of hafnium nitride can be selected to result in a dielectric constant of the dielectric film of greater than 20. Some embodiments separate the dielectric film from the substrate by a diffusion barrier. The dielectric film can be formed at a temperature less than 300° C.

Hf[(CH3)2]4 can be used as a precursor and water vapor can be used as a reactant to form the hafnium oxide in a deposition process with a temperature between 250° C. to 300° C. HfCl4 can be used as a precursor and water vapor can be used as a reactant to form the hafnium oxide in a deposition process with a temperature of approximately 300° C. Hf[(CH3)2]4 can be used as a precursor and ammonia (NH3) can be used as a reactant to form the hafnium oxide in a deposition process with a temperature of approximately 250° C. Various embodiments provide the hafnium nitride and hafnium oxide film as a continuous layer with a root mean square surface roughness of less than 10 Å and a current leakage rate of less than 5×10−7 amps per cm2 at an electric field strength of 1 megavolt per cm.

Additional information regarding nanolaminates such a lanthanide oxide/hafnium oxide as high-k dielectrics can be found in U.S. patent application Ser. No. 11/063,717 filed Feb. 23, 2005 entitled “Atomic Layer Deposition of Hf3N4/HfO2 Films as Gate Dielectrics,” which is herein incorporated by reference.

Zr3N4/ZrO2

The high-k dielectric can be provided by a Zr3N4/ZrO2 nanolaminate. Atomic layer deposition can be used to form at least one zirconium oxide layer and at least one zirconium nitride layer. The dielectric layer can include an amorphous dielectric that includes ZrO2, Zr3N4, and combinations thereof. The zirconium oxide layer can be comprised of a plurality of individually deposited zirconium oxide layers, where each individual one of the zirconium oxide layers is less than or equal to two monolayers in thickness. Each individual one of the zirconium oxide layers can be a continuous monolayer with a step coverage of greater than 90% over 90 degree angle steps. In various embodiments, each individual one of the zirconium oxide layers has a thickness within a range from 1.3 to 1.5 Å. Some embodiments provide the dielectric layer with a root mean square surface roughness that is less than one tenth of the layer thickness. A ratio of a thickness of zirconium oxide to a thickness of zirconium nitride can be selected to result in a dielectric constant of the dielectric film of greater than 20. A diffusion barrier can separate the dielectric film from the substrate. The dielectric film can be formed at a temperature of between 275° C. to 325° C. ZrI4 can be used as a precursor, and water vapor and hydrogen peroxide can be used as reactants to form zirconium oxide in a deposition process where the temperature is between 325° C. to 500° C. ZrCl4 can be used as a precursor, and water vapor can be used as a reactant to form zirconium oxide in a deposition process where the temperature is approximately 300° C. Zr[(CH3)2]4, can be used as a precursor and ammonia (NH3) can be used as a reactant to form zirconium oxide in a deposition process where the temperature is approximately 250° C. The zirconium nitride and zirconium oxide film can each be a continuous layer having a root mean square surface roughness of less than 5 Å and a current leakage rate of less than 1.1×10−7 amps per cm2 at an electric field strength of 1 megavolt per cm.

Additional information regarding nanolaminates such a Zr3N4/ZrO2 oxide as high-k dielectrics can be found in U.S. patent application Ser. No. 11/058,563, filed Feb. 15, 2005 entitled “Atomic Layer Deposition of Zr3N4/ZrO2 Films as Gate Dielectrics,” which is herein incorporated by reference.

TiO2/CeO2

The high-k dielectric can be provided by a TiO2/CeO2 nanolaminate using ALD processes.

Wafer Level

FIG. 3 illustrates a wafer 340, upon which the transistors with metal substituted gates can be fabricated according to embodiments of the present subject matter. A common wafer size is 8 inches in diameter. However, wafers are capable of being fabricated in other sizes, and the present subject matter is not limited to wafers of a particular size. A number of dies can be formed on a wafer. A die 341 is an individual pattern, typically rectangular, on a substrate that contains circuitry to perform a specific function. A semiconductor wafer typically contains a repeated pattern of such dies containing the same functionality. A die is typically packaged in a protective casing (not shown) with leads extending therefrom (not shown) providing access to the circuitry of the die for communication and control.

System Level

FIG. 4 illustrates a simplified block diagram of a high-level organization of an electronic system that includes the transistor with the metal-substituted gate, according to various embodiments. In various embodiments, the system 450 is a computer system, a process control system or other system that employs a processor and associated memory. The electronic system 450 has functional elements, including a processor or arithmetic/logic unit (ALU) 451, a control unit 452, a memory device unit 453 and an input/output (I/O) device 454. Generally such an electronic system 450 will have a native set of instructions that specify operations to be performed on data by the processor 451 and other interactions between the processor 451, the memory device unit 453 and the I/O devices 454. The control unit 452 coordinates all operations of the processor 451, the memory device 453 and the I/O devices 454 by continuously cycling through a set of operations that cause instructions to be fetched from the memory device 453 and executed. According to various embodiments, the memory device 453 includes, but is not limited to, random access memory (RAM) devices, read-only memory (ROM) devices, and peripheral devices such as a floppy disk drive and a compact disk CD-ROM drive. As one of ordinary skill in the art will understand upon reading and comprehending this disclosure, any of the illustrated electrical components are capable of being fabricated to include a transistor with a substituted gate in accordance with the present subject matter.

FIG. 5 illustrates a simplified block diagram of a high-level organization of an electronic system that includes transistors with metal substituted gates, according to various embodiments. The system 560 includes a memory device 561 which has an array of memory cells 562, address decoder 563, row access circuitry 564, column access circuitry 565, read/write control circuitry 566 for controlling operations, and input/output circuitry 567. The memory device 561 further includes power circuitry 568, and sensors 569 for determining the state of the memory cells. The illustrated power circuitry 568 includes power supply circuitry, circuitry for providing a reference voltage, circuitry for providing the word line with pulses, and circuitry for providing the bit line with pulses. Also, as shown in FIG. 5, the system 560 includes a processor 570, or memory controller for memory accessing. The memory device receives control signals from the processor over wiring or metallization lines. The memory device is used to store data which is accessed via I/O lines. It will be appreciated by those skilled in the art that additional circuitry and control signals can be provided, and that the memory device has been simplified. At least one of the processor or memory device includes the transistor with the metal substituted gate according to the present subject matter.

The illustration of system 560, as shown in FIG. 5, is intended to provide a general understanding of one application for the structure and circuitry of the present subject matter, and is not intended to serve as a complete description of all the elements and features of an electronic system. As one of ordinary skill in the art will understand, such an electronic system can be fabricated in single-package processing units, or even on a single semiconductor chip, in order to reduce the communication time between the processor and the memory device.

Applications containing transistors with metal gates on high-k dielectrics, as described in this disclosure, include electronic systems for use in memory modules, device drivers, power modules, communication modems, processor modules, and application-specific modules, and may include multilayer, multichip modules. Such circuitry can further be a subcomponent of a variety of electronic systems, such as a clock, a television, a cell phone, a personal computer, an automobile, an industrial control system, an aircraft, and others.

This disclosure includes several processes; circuit diagrams, and structures. The present invention is not limited to a particular process order or logical arrangement. Although specific embodiments have been illustrated and described herein, it will be appreciated by those of ordinary skill in the art that any arrangement which is calculated to achieve the same purpose may be substituted for the specific embodiments shown. This application is intended to cover adaptations or variations. It is to be understood that the above description is intended to be illustrative, and not restrictive. Combinations of the above embodiments, and other embodiments, will be apparent to those of skill in the art upon reviewing the above description. The scope of the present invention should be determined with reference to the appended claims, along with the full scope of equivalents to which such claims are entitled.

A diamond-like-carbon layer is used as masking structure to protect gate dielectric layer from contamination during high temperature annealing, removal by plasma etching, forming metal gate electrode in space vacated by masking layer

Electronic and computer products, are generally built layer by layer on a silicon substrate. One common layer-formation technique, known as chemical-vapor deposition (CVD), produces uneven layers and covers vertical surfaces poorly. An emergent