Search Results

Sort by

A Cummins ISB 5.9 liter medium-duty engine with cooled EGR has been used to study an early extrusion of an advanced ceramic uncatalyzed diesel particulate filter (DPF). Data for the advanced ceramic material (ACM) and an uncatalyzed cordierite filter of similar dimensions are presented. Pressure drop data as a function of mass loadings (0, 4, and 6 grams of particulate matter (PM) per liter of filter volume) for various flow rate/temperature combinations (0.115 - 0.187 kg/sec and 240 - 375 °C) based upon loads of 15, 25, 40 and 60% of full engine load (684 N-m) at 2300 rpm are presented. The data obtained from these experiments were used to calibrate the MTU 1-D 2-Layer computer model developed previously at MTU. Clean wall permeability determined from the model calibration for the ACM was 5.0e-13 m2 as compared to 3.0e-13 m2 for cordierite.

The objective of this research was to study the effect of a catalyzed particulate filter (CPF) with a high loading of catalyst (50 gms/ft3) and ultra low sulfur fuel (ULSF -0.57 ppm of sulfur) on the emissions from a heavy duty diesel engine. The particulate emissions were measured using two different analytical methods, i.e., the gravimetric method and the thermal optical method (TOM). The results from the two different methods of analyses were compared. The experiments were performed at four different operating conditions chosen from the old Environmental Protection Agency (EPA) 13-mode test cycle. A 1995 Cummins M11 heavy-duty engine with manually controlled exhaust gas recirculation (EGR) was used to perform the emission characterization experiments. The emission characterization included total particulate matter (TPM), which is composed of the solids (SOL), soluble organic fractions (SOF) and sulfates (SO4) analyzed using the gravimetric method.

A 1-D 2-layer model developed previously at MTU was used in this research to predict the pressure drop, filtration characteristics and various properties of the particulate filter and the particulate deposit layer. The model was used along with dilute emission data to characterize two catalyzed particulate filters (CPFs) having different catalyst loading and catalyst application processes. The model was calibrated and validated with data obtained from steady state experiments conducted using a 1995 Cummins M11-330E heavy-duty diesel engine with manual EGR with different fuels for the two different CPFs. The two different catalyzed particulate filters were CPF III (5 gms/ft3 Pt) and CPF V (50 gms/ft3 Pt). Both the CPFs had cordierite substrates with CPF III and CPF V had MEX and NEX catalyst type formulation respectively. The CPF III filter was catalyzed using a solution-impregnated process while the CPF V filter was catalyzed using a wash coat process.

A 1-D 2-layer model developed previously at MTU was used in this research to predict the pressure drop, filtration characteristics and various properties of the particulate filter and the particulate deposit layer. The model was calibrated and validated for this CPF with data obtained from steady state experiments conducted using a 1995 Cummins M11-330E heavy-duty diesel engine with manual EGR and using ULSF. The CPF used is a NGK filter having a cordierite substrate with NEX catalyst type formulation (54% porosity, 15.0 μm mean pore diameter and 50 gms/ft3 Pt). The filter was catalyzed using a wash coat process. The model was used to predict the pressure drop, particulate mass retained inside the CPF, particulate mass filtration efficiency and concentration downstream of the CPF with agreement between the experimental and simulated data.