Wear nitrile gloves, as oils from your hands can prevent the PDMS from curing and/or bonding properly. Please try to not drip PDMS everywhere. It is extremely hard to clean up. Don't get uncured PDMS onto cured chips, as this will prevent the chips from properly bonding to the glass coverslip. In practive this means you should use one pair of gloves for mixing the PDMS and another, clean pair for cutting out the chips and bonding them to the coverslip.

−

===Mixing the PDMS===

−

Wear nitrile gloves, as oils from your hands can prevent the PDMS from curing and/or bonding properly. Please try to not drip PDMS everywhere. It is extremely hard to clean up.

====Mixing PDMS to fill the mold====

====Mixing PDMS to fill the mold====

Line 45:

Line 43:

====Cutting out the Chip====

====Cutting out the Chip====

# Using a razor blade, carefully cut around the mask components visible through the PDMS. DO NOT CUT YOURSELF. DO NOT under ANY circumstances push down on the underlying silicon wafer. This will crack the wafer rendering it useless for classmates and for future chip making. It is expensive to replace these molds, so BE GENTLE!!! The best way to cut out the PDMS is to gently circle, removing slightly more PDMS each time. When you see an air bubble form under the PDMS you are getting close, but DO NOT rush at this point. Carefully keep circling the groove until the chunk of PDMS pops-out.

# Using a razor blade, carefully cut around the mask components visible through the PDMS. DO NOT CUT YOURSELF. DO NOT under ANY circumstances push down on the underlying silicon wafer. This will crack the wafer rendering it useless for classmates and for future chip making. It is expensive to replace these molds, so BE GENTLE!!! The best way to cut out the PDMS is to gently circle, removing slightly more PDMS each time. When you see an air bubble form under the PDMS you are getting close, but DO NOT rush at this point. Carefully keep circling the groove until the chunk of PDMS pops-out.

−

# Cut the large piece of PDMS into individual chips. You want each chip to fit onto your coverslip. Don't cut your chip too small, as this will give it less surface area with which to bond to the coverslip.

+

# Cut the large piece of PDMS into individual chips. You want each chip to fit onto your coverslip. Don't cut your chip too small, as this will give it less surface area with which to bond to the coverslip. When you have cut out your chip, cover the channel side with scotch tape.

====Punch inlet and outlet ports in your chip====

====Punch inlet and outlet ports in your chip====

=====Blunt Needle Technique=====

=====Blunt Needle Technique=====

−

Place a piece of scrap PDMS flat on your bench and push a blunt needle through the PDMS. Then use a smaller 21 G 1 ½ needle (pointed) to remove the plug of PDMS from the end of the blunt needle before pulling the blunt needle back through the PDMS to leave a port. Ask the course staff if you need a demonstration.

+

Place a piece of scrap PDMS flat on your bench and push a blunt needle through the PDMS. Then use a smaller 21 G 1 ½ needle (pointed) to remove the plug of PDMS from the end of the blunt needle before pulling the blunt needle back through the PDMS to leave a port.

=====Biopsy Punch Technique=====

=====Biopsy Punch Technique=====

−

Put a piece of scrap PDMS flat on your bench and use a biopsy punch to push through the PDMS. Be very careful to punch strain down and please don’t bend the tip of the biopsy punch (this renders them basically useless). Eject the plug of PDMS before pulling the biopsy punch back through the PDMS to leave a hole. Ask the course staff if you need a demonstration.

+

Put a piece of scrap PDMS flat on your bench and use a biopsy punch to push through the PDMS. Be very careful to punch strain down and please don’t bend the tip of the biopsy punch (this renders them basically useless). Eject the plug of PDMS before pulling the biopsy punch back through the PDMS to leave a hole.

−

−

−

+

====Plasma bonding the PDMS chip to the coverslip====

+

# Clean the channel side of the chip using scotch tape. Press and remove scotch tape 3X’s from the channel side of the chip.

+

# Turn on the vacumn pump to the plasma preen (leftmost switch labelled "Vacumn Pump Power"). You will hear the vacumn pump at your feet turn on

+

# Remove the glass chamber. Be careful of the two glass balls on the bottom of the chamber, they tend to catch and the whole chamber can get stuck!

+

# Place your chip (tape free) and a glass coverslip inside. Make sure that the PDMS chip is channel-side up.

Overview

This protocol covers the soft lithography and plasma bonding steps used to make flow cells out of PDMS in our lab. This protocol assumes that you are starting with a silicon wafer mold that already has your desired pattern on it. We make out own SU8 molds in the Princeton Microfluidics Laboratory.

Materials

Slygard 184 Silicon Elastromer (Ellsworth Adhesives)

4” petri dishes (for storing chips)

Small ~6” pieces of the intramedic tubing (ID 0.86mm OD 1.27mm)

Razor blades

Biopsy Punches (1.2mm, 1.0mm, 0.75mm diameters) (

Nitrile gloves

Stainless steel blunt needle, 16 ½” gauge

Small green needle (21 ½ gauge Becton-Dickinson)

Scotch tape

1ml syringes with Luer-Lok tips

1.5mm Coverslips

Oven set to 65°C

TMCS (chlorotrimethyl silane)

plastic forks for mixing PDMS

plastic beakers for mixing PDMS

Vacumn jar for degassing PDMS

Protocol

Wear nitrile gloves, as oils from your hands can prevent the PDMS from curing and/or bonding properly. Please try to not drip PDMS everywhere. It is extremely hard to clean up. Don't get uncured PDMS onto cured chips, as this will prevent the chips from properly bonding to the glass coverslip. In practive this means you should use one pair of gloves for mixing the PDMS and another, clean pair for cutting out the chips and bonding them to the coverslip.

Mixing PDMS to fill the mold

Mix PDMS in a 1:9 ratio (by weight) curing agent to polymer in a plastic solo cup. The easiest way to do this is by weighing out the polymer first in the plastic solo cup on a balance and then adding the appropriate amount of curing agent

For these molds you will need ~60 g of total solution the first time you fill up the petri dish (assuming a 4" dish).

Mix the PDMS THOROUGHLY using a plastic fork. When you think that you’ve mixed it enough, mix it some more. Uneven mixing will lead to uneven curing of the PDMS.

Degassing the PDMS

Place your PDMS in the vacumn bell jar in the hood and turn on the vacumn. Please wait for your classmates because you will all need to be degassing PDMS at the same time.

Watch the PDMS degassing. If it looks like it is about to bubble over, release the vacumn, let the bubbles collapse, and then restart the vacumn. Keep an eye on it for at least 10 minutes.

Make sure that your PDMS is completely free of bubbles. The total degassing process will probably take 15 minutes. While you are waiting you may move on to testing the chips you made previously.

Pour the PDMS

Pour the PDMS carefully into your mold, trying hard not to introduce bubbles that you have worked so hard to eliminate.

If you do introduce bubbles carefully use a 21G 1 1/2 gauge needle to move them to the side.

Curing the PDMS

Cure the PDMS at 65°C until it is firm and not tacky at all. This will probably take an hour. You can also do this overnight if you are running out of time.

Cutting out the Chip

Using a razor blade, carefully cut around the mask components visible through the PDMS. DO NOT CUT YOURSELF. DO NOT under ANY circumstances push down on the underlying silicon wafer. This will crack the wafer rendering it useless for classmates and for future chip making. It is expensive to replace these molds, so BE GENTLE!!! The best way to cut out the PDMS is to gently circle, removing slightly more PDMS each time. When you see an air bubble form under the PDMS you are getting close, but DO NOT rush at this point. Carefully keep circling the groove until the chunk of PDMS pops-out.

Cut the large piece of PDMS into individual chips. You want each chip to fit onto your coverslip. Don't cut your chip too small, as this will give it less surface area with which to bond to the coverslip. When you have cut out your chip, cover the channel side with scotch tape.

Punch inlet and outlet ports in your chip

Blunt Needle Technique

Place a piece of scrap PDMS flat on your bench and push a blunt needle through the PDMS. Then use a smaller 21 G 1 ½ needle (pointed) to remove the plug of PDMS from the end of the blunt needle before pulling the blunt needle back through the PDMS to leave a port.

Biopsy Punch Technique

Put a piece of scrap PDMS flat on your bench and use a biopsy punch to push through the PDMS. Be very careful to punch strain down and please don’t bend the tip of the biopsy punch (this renders them basically useless). Eject the plug of PDMS before pulling the biopsy punch back through the PDMS to leave a hole.

Plasma bonding the PDMS chip to the coverslip

Clean the channel side of the chip using scotch tape. Press and remove scotch tape 3X’s from the channel side of the chip.

Turn on the vacumn pump to the plasma preen (leftmost switch labelled "Vacumn Pump Power"). You will hear the vacumn pump at your feet turn on

Remove the glass chamber. Be careful of the two glass balls on the bottom of the chamber, they tend to catch and the whole chamber can get stuck!

Place your chip (tape free) and a glass coverslip inside. Make sure that the PDMS chip is channel-side up.