Advanced Technology 5 Layer

2400/2800/3500mm POF Film Machines

Full Colors Copperplate Printing

Polyolefin Shrink Film Printing Service

HYF003 High Performance Polyolefin Shrink Film

is a perfect shrink film. It can help you solve nearly all shrinking difficulties. HYF003 has excellent low shrink temperature property. Its shrink temperature is nearly same as PVC shrink film's. With quick shrink, good seal strength and over 70% shrinkage, HYF003 can perform perfectly even under the worst shrink conditions. HYF003 also has low shrink force function and good hot slip property.

Features

Exceptional shrinakge under 120℃

Broad shrink temperature range, from 110℃ to 180℃

Quick shrink in 1.5 seconds

Excellent shrinkage

Low sealing temperature

Superior seal strength

Strong tear resistance

Low shrink force property

Outstanding hot slip property after shrinkage

Overlap staic sealing property

compatible for all packaging machinery.

TEST ITEM

UNIT

ASTM TEST

TYPICAL VALUES

THICKNESS

12um

15um

19um

25um

TENSILE

Tensile Strength (MD)

N/mm2

D882

76

71

71

66

Tensile Strength (TD)

66

61

61

61

Elongation (MD)

%

106

106

111

111

Elongation (TD)

86

91

91

96

TEAR

MD

g

D1922

15.6

18.6

32.1

40.1

TD

13.6

16.6

23.6

30.1

SEAL STRENGTH

MD/Hot Wire Seal

N/mm

F88

0.78

0.88

1.05

1.35

TD/Hot Wire Seal

0.72

0.82

1.01

1.27

COF(film to Film)

Dynamic

D1894

0.31

0.28

0.27

0.31

Static

0.32

0.29

0.28

0.32

Static (Hot Slip) @ 60℃

0.39

0.37

0.36

0.35

OPTICS

Haze

D1003

3.2

3.7

4.3

4.6

Clarity

D1746

97.6

98.1

97.1

95.1

Gloss @ 45Deg

D2457

86.6

84.1

82.1

80.6

BARRIER

Oxygen Transmission Rate

cc/m2/day

D3985

12300

11200

9400

6200

Water Vapor Transmission Rate

gm/m2/day

F1249

50

43

36

29

SHRINKAGE PROPERTIES

MD

TD

MD

TD

Free Shrinkage

80℃

%

D2732

24

21

22

18

90℃

30

33

28

27

100℃

51

53

49

48

110℃

60

61

56

57

120℃

66

66

64

66

130℃

71

69

69

68

Shrink Tension

90℃

Mpa

D2838

1.70

1.80

1.80

1.85

100℃

1.90

2.00

2.05

2.15

110℃

2.05

2.10

2.25

2.30

120℃

1.85

1.95

2.00

2.05

Note: This infor mation represents our best judgment on the work done,but the company assumes no liability whatsoever in connection with the use of infomation or findings contained herein.