A61B17/58—Surgical instruments or methods for treatment of bones or joints; Devices specially adapted therefor for osteosynthesis, e.g. bone plates, screws, setting implements or the like

A61B17/68—Internal fixation devices, including fasteners and spinal fixators, even if a part thereof projects from the skin

A61B17/683—Internal fixation devices, including fasteners and spinal fixators, even if a part thereof projects from the skin comprising bone transfixation elements, e.g. bolt with a distal cooperating element such as a nut

Abstract

PROBLEM TO BE SOLVED: To fix an ossicle or an artifact to a bone without losing easiness in curing fracture or osteotomy, by using an oriented bone fixation pin with properties that the cross section area of at least a part in the longitudinal direction is increased by deforming or heating. SOLUTION: A lower hole to be inserted by a bone fixation pin is bored on bone fractures 21, 22 and plastic parts 12 in the tip end side and the base end side are inserted so as to clamp a tip end side fracture 22 and a base end side fracture 21 respectively. After inserting a bone fixture pin 1 is inserted, the cross section area of the tip end side plastic part 11 is increased by external force or heat to form an anchor part 32. After that, drawing the last end of the base end of the bone fixture pin 1, the anchor part 31 is formed and fixed onto the plastic part 11 by external force and heat. Thereby the anchor can be fixed with a bone without a gap. A biodegradable polymer such as polyhydroxy lactic acid, etc., is preferable as the constituting material of the plastic part.

Description

Translated from Japanese

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【０００１】 [0001]

【発明の属する技術分野】本発明は、整形外科や口腔外科において利用される骨固定ピンおよびその製造方法に関する。 The present invention relates to relates to a bone fixation pin and its manufacturing method is utilized in orthopedic and oral surgery.

【０００２】 [0002]

【従来の技術】従来用いられてきた金属で作製されたスクリュー、プレート、ワイヤーや髄内釘などの骨内固定具は、整形外科や口腔外科において骨折治療や変形関節の骨切りの際の骨片固定、さらには人工球蓋や人工関節等の固定をする際に使用されてきた。 Conventionally used is a metal have fabricated screws, plates, bone a fixture such as a wire or intramedullary nail, bone during osteotomy of fracture treatment and deformation joint in orthopedic and oral surgery piece fixed, have further been used to the fixed and artificial ball cover and artificial joints.骨折の治療法にはギプス固定に代表される外固定および骨折部を外科的に開放し骨内固定具を用いて固定する内固定があり、外固定に比べ内固定は術後早期の運動が可能となる。 It has a fixed inner fixing Treatment of bone fractures using surgically opened intra-osseous fixture external fixation and fracture typified cast fixed, in comparison with the external fixation fixation early movement after surgery It can become.内固定に求められる特性は、およそ４週から３カ月かかる骨折癒合期間中接合した骨片同士の位置関係がずれないようにすることにあり、接合面がこの時期にずれると偽関節や遷延治癒といった不具合がおこり、良好に治癒しないことがある。 Characteristics required for the internal fixation is to such positional relationship of the bone pieces bonded to each other in three months according fracture healing period from about 4 weeks is not deviated, bonding surface nonunion or prolonged healing and shifted in this period It occurs problems such as, sometimes that do not heal well.現在使用されているステンレス製内固定具のうち、ピンは先端についた刃によって骨片の位置を合わせながら、２個以上の骨片を串刺しにして固定し、骨から露出した部分はカッター等で容易に切断できるため、骨にネジ山を切る必要のあるネジと比べると簡便に固定ができる。 Of stainless steel in a fixture that is currently in use, pins while aligning the bone pieces by blade tipped, two or more bone fragments and skewered fixed, portions exposed from the bone with a cutter or the like because you can easily cut, it is easily fixed compared to the screws that need to cut the threads to the bone.

【０００３】しかしながら、ステンレスピンの表面が平滑であるためピンの軸方向に骨片がずれやすく、また骨密度の低い骨を接合した場合、ステンレスピンと骨との実質的な接触面積が小さいため、さらに骨片がずれやすく、強固な固定は期待できない。 However, in the axial direction of the pin for the surface of the stainless steel pin is smooth easily shift bone fragments, also when joining low bone bone density, because of their small substantial contact area between the stainless steel pins and bone, even easier to shift the bone fragments, a strong fixation can not be expected.さらに、ステンレスピンと接触している骨がステンレスピンの異物反応によって体内で徐々に吸収されたりした場合、骨とステンレスピンの間に間隙が生じ、ステンレスピンが体内で迷走し、周囲の組織を傷害したりする問題があった。 Further, if the bone in contact with the stainless steel pins is or are slowly absorbed by the body by foreign body reaction of the stainless steel pins, a gap is formed between the bone and stainless steel pins, stainless pin strayed in the body, injury to surrounding tissue there is a problem to be or is.また、 Also,まれに金属アレルギーをおこす患者もあるため、このようなステンレス固定具は、骨折が治癒した後、適当な時期に体外に取り出す２度目の手術（抜釘術）が必要であった。 Because of rare some patients cause metal allergy, such stainless fixture after fracture has healed, the second time surgery retrieve the body at the appropriate time (抜釘 surgery) was required.さらに、近年ＭＲＩにより癒合状態を確認しながら治療することが広く行われるようになったが、ステンレスはＭＲＩ画像を妨害するため、正しい治療判断に苦渋するという不具合もある。 Furthermore, in recent years it has become possible is widely to treat while confirming the fusion state by MRI, stainless steel to prevent the MRI image, there is also a problem that agonizing the correct treatment decision.

【０００４】また最近前記の抜釘術を不要としＭＲＩ画像を妨害せず体内で吸収消失するプラスチック製のピンが市販されてきた。 [0004] Also recently the plastic pin to absorb the loss in the body does not interfere with the MRI image and eliminates the need for 抜釘 surgery have been commercially available.しかしながら、このようなプラスチック製ピンはステンレスと比べて柔らかいためステンレスピンのように先端に刃を付けて孔をあけながら骨内に挿入することは出来ず、プラスチックピンを挿入できる孔をあけた後挿入しなければならない。 However, such plastic pin can not be inserted into the bone while drilling a hole with a cutting edge to the tip as stainless pins softer than the stainless steel, after a hole that can be inserted plastic pins It must be inserted.その結果、作業が煩雑になるだけではなく、孔をプラスチックピンの直径より大きくあけなければ骨とプラスチックピンとの界面での抵抗が高くなりプラスチックピンを挿入する時プラスチックピンが曲がったり壊れたりして挿入し難くなる。 As a result, the work is not only becomes complicated, holes and over or break plastic pins or bent when inserting the high becomes plastic pins resistance at the interface between the bone and the plastic pin should be spaced at greater than the diameter of the plastic pins inserted becomes difficult.一方で、前記孔をプラスチックピンの直径より大きくあければあけるほどプラスチックピンの挿入は容易にできるが、骨とプラスチックピンの界面に隙間ができ骨片ががたつきやすくなるという欠点があった。 On the other hand, although the hole insertion of plastic pins more open I open larger than the diameter of the plastic pins can be easily, it has a drawback that the bone pieces a gap at the interface of bone and the plastic pin is easily rattle.また、このがたつきを軽減するため、テーパー付きのプラスチックピンも考案されている（特開平２-６３４５０）が、 Further, in order to reduce this rattling, even plastic pins tapered have been devised (JP 2-63450),固定した骨片に力が加わったりするとピンの太い方向へずれやすく、緩みやすいことは明らかである。 Easily shifted to a fixed thick direction of the pin when a force is applied or the bone fragment, easy loosening it is clear.

【０００５】また、体内での異物反応が少なく、ステンレスよりＭＲＩ画像を妨害しにくく、骨と親和性が良いため骨と密着し易いチタンやサファイヤセラミックスで作製した固定具が市販されている。 Further, less foreign body reaction in the body, the MRI image is hardly disturbing from stainless steel fixtures are commercially available produced in easily titanium and sapphire ceramic close contact with the bone for better affinity to bone.これらの固定具は、 These fasteners,硬い為にしっかり固定できる。 Firm can be fixed to hard.また、体内で異物反応をおこしにくくかつ骨と接着し易い為、骨と固定具の間に隙間ができることで体内を迷走したり金属アレルギーをおこすという不具合が、ステンレス固定具より少ないとされ、体内に残しておいて大きな問題を生ずる危険性は、ステンレス製固定具より少ないとされる。 Further, since easily bonded to the difficult and bone cause foreign body reaction in the body, disadvantageously causing metal allergy or vagus the body by a gap between the bone and the fixture is less than stainless fixture body risk of causing significant problems left in is less than the stainless steel fixture.しかしながら、一方で、チタンやサファイヤ製固定具の近傍での再骨折や、固定不良での遷延治癒、偽関節化、まれに生ずるアレルギー、変形性関節症治療のための骨切り固定手術後長期間たって人工関節を移植する場合などで、固定具を除去する必要が生じても硬い固定具と骨とが強固に接着しているため、容易には除去することが困難であり除去できない場合は、残存する固定具を避けて行う必要があるという不具合があった。 However, on the other hand, and re-fractures in the vicinity of the titanium and sapphire manufactured fixtures, prolonged healing in fixing failure, false articulated, allergy occurring rarely, osteoarthritis treatment for a long time after osteotomy fixation surgery for in a case of Tatte implanted artificial joint, since the bone and hard fixture even when necessary to remove the fasteners are firmly adhered, if not readily are difficult to remove removed, necessary to perform avoiding fasteners remaining there is a problem that is.

【０００６】 [0006]

【発明が解決しようとする課題】本発明は、上述した問題点を鑑み、簡単な固定作業でしっかり固定でき、体内に残存しても安全であり、ＭＲＩ画像を妨害せず、再手術の際邪魔にならない骨固定ピンを提供することにある。 SUMMARY OF THE INVENTION It is an object of the present invention is to provide the above-mentioned problems, firmly be fixed by a simple fixing operation is safe to remain in the body does not interfere with the MRI image, when the re-operation It is to provide a bone fixation pin that does not get in the way.さらに、この骨固定ピンの製造方法である。 Furthermore, a method of manufacturing the bone fixation pin.

【０００７】 [0007]

【課題を解決するための手段】上記課題は以下の本発明により達成される。 The object, according to an aspect of is achieved by the following present invention.（１）長軸方向の少なくとも一部が変形あるいは加熱によって断面積の増大する性質を有する配向されたプラスチックからなる骨固定ピンである。 (1) is a bone fixing pin consisting of oriented plastic having an increasing nature of the cross-sectional area by at least partially deformed or heating of the axial direction.（２）一端がテーパー状に成形され、他端に開口部を有する中空構造体からなる上記（１）に記載の骨固定ピンである。 (2) one end of which is formed into a tapered shape, a bone fixing pin according to (1) consisting of a hollow structure having an opening at the other end.また、その断面が多角形の形状を有することを特徴とする骨固定ピンである。 Also, a bone fixation pin in cross section and having a polygonal shape.

【０００８】（３）前記プラスチックが生体内で分解吸収される材料である上記（１）乃至（２）に記載の骨固定ピンである。 [0008] (3) wherein the plastic is a bone fixing pin according to (1) to (2) is a material that is degraded and absorbed in vivo.（４）前記プラスチックが、ポリヒドロキシ酪酸またはその共重合体からなる上記（１）乃至（３）に記載の骨固定ピンである。 (4) wherein the plastic is a bone fixing pin according to (1) to (3) consisting of polyhydroxy butyric acid or a copolymer thereof.（５）プラスチック材料を金属製管体に挿入し、当該金属製管体と共に延伸を行った後、一定の温度にて処理を行うことを特徴とする骨固定ピンの製造方法である。 (5) the plastic material is inserted into the metal tube, after stretching together with the metal tube, a method for producing a bone fixation pin and performs processing at a constant temperature.

【０００９】本発明の骨固定ピンは、骨或いは移植物に接触するプラスチック部分の実質的な断面積が骨片や移植物に固定具を挿入する前には骨片や移植物にあけられた孔の断面積より小さくしておき、挿入後に変形または加熱によって断面積を増大させることによって骨片あるいは移植物を骨に固定し、さらに骨片あるいは移植物が長軸方向に沿って移動することを効果的に阻止することができる。 [0009] bone fixation pin of the invention, before substantial cross-sectional area of ​​the plastic part in contact with the bone or the implant is inserted a fastener to the bone piece and the implant is drilled in the bone fragment and implant leave smaller than the cross-sectional area of ​​the hole, the bone fragments or implants secured to the bone by increasing the cross-sectional area by deformation or heated after insertion, to move further along the long axis direction bone fragments or implants it can be effectively prevented.本発明の骨固定ピンの変形あるいは加熱によって断面積の増大する部分の位置は骨固定ピン全体でもよく、また固定しようとする骨片や移植物が効果的に固定できる部分のみでも良い。 Position of increasing the portion of the cross-sectional area by deformation or heating of the bone fixing pin of the present invention may even whole bone fixation pins, and bone and implant to be fixed may be only a portion can be effectively secured.例えば、骨固定ピンが２つの骨片を完全に突き通して固定する場合、骨片にあけられた開口部近傍に位置する部分のみとし、この部分のみ屈曲変形あるいは加熱によって断面積を増大させることで骨片が骨固定ピンの長軸方向にそって引き離される作用を阻止できる。 For example, if the bone fixing pin to fix completely pierce the two bone fragments, and only a portion which is located near the opening drilled in the bone, to increase the cross-sectional area by bending deformation or heat only the portion in can block the action of bone pieces are pulled apart along the long axis direction of the bone fixing pin.

【００１０】本発明の骨固定ピンの外観的形状は特に限定されず、棒状体であって少なくとも長軸方向の一部に変形あるいは加熱によって断面積の増大する性質を有する配向したプラスチック部分を有するものであれば良い。 [0010] appearance shape of the bone fixing pin of the present invention is not particularly limited, with the oriented plastic part having increasing nature of the cross-sectional area by deformation or heating at least part of the long axis a rod-shaped body it may be used as long as.また本発明でプラスチック部分の断面積の増大の範囲は特に限定しないが、もとの断面積に対して２００％ The range of increase in the cross-sectional area of ​​the plastic part in the present invention is not particularly limited, but 200% relative to the original cross-sectional area程度までの範囲を示す。 Indicating the scope of the extent.

【００１１】本発明に用いる変形あるいは加熱によって断面積が増大する性質を有するプラスチックの具体的な材料としては、硬質の材料であれば既存の様々な材料が利用可能であり、生体内において分解吸収され、骨固定ピンと骨組織の間にがたつきを生じさせないものであればよく、例えば、ポリ乳酸、ポリジオキサノンやポリヒドロキシ酪酸のような生分解性ポリエステルやキチン、 As a specific material of plastic having a property of the cross-sectional area increased by deformation or heat used in the present invention, various existing materials as long as the material of the hard are available, degraded and absorbed in vivo is, as long as it does not cause rattling between the bone fixation pin and the bone tissue, for example, polylactic acid, polydioxanone and biodegradable polyesters or chitin such as polyhydroxybutyrate,キトサンなどの多糖類、さらにはそれらの材料にヒドロキシアパタイトのような骨置換の可能な燐酸塩類などを含有させたものが利用できる。 Polysaccharides such as chitosan, more available to those obtained by incorporating the like capable phosphates bone replacement, such as hydroxyapatite to those materials.実際にどのような材質を利用するかは、応力を必要とする期間によって選択することができる。 Actually what to use the material, can be selected by the period which requires stress.例えば、ポリ乳酸やポリヒドロキシ酪酸は、移植前の各ポリマーの形状や分子量などにもよるが、体内での応力保持は6カ月から3年の間可能であると予測される。 For example, polylactic acid and polyhydroxybutyric acid, depending on the shape or molecular weight of the polymer before implantation, stress retention in the body is expected to be possible between 3 years 6 months.また、ポリジオキサノンは1から3カ月、吸収性縫合糸に利用されているポリグリコール酸やポリグリコール酸とポリ乳酸との共重合体は2週間前後であると予想される。 Further, polydioxanone is 3 months 1, copolymers of polyglycolic acid and polyglycolic acid and polylactic acid are used in absorbable sutures is expected to be two to three weeks.これらは、骨固定ピンの応力保持の必要な期間から適当に設定可能である。 These are suitably configurable from the required period of stress retention of bone fixation pins.ポリヒドロキシ酪酸は他の生分解性プラスチックに比べ結晶化度が高く延伸により配向しやすいため、変形あるいは加熱によって断面積の増大する性質を生かすプラスチックとしては好適である。 Polyhydroxy butyrate and is easily oriented by crystallization degree is higher stretching compared to other biodegradable plastics, the plastic to take advantage of increasing nature of the cross-sectional area by deformation or heat are preferred.また、他の生分解性プラスチックはその製造法が主に化学合成に頼っているのに対し、ポリヒドロキシ酪酸は微生物の発酵合成で製造しているため、化学合成で使用している合成触媒を含まないことから、分解された後に合成触媒由来の炎症反応などを引き起こす心配がなく好適である。 Also, other biodegradable plastics while its manufacturing method relies mainly on chemical synthesis, since the polyhydroxy acid is produced by fermentation synthesis of a microorganism, a synthetic catalyst that is used in the chemical synthesis since free, it is preferable not worry about causing a synthetic catalyst derived inflammatory response after being decomposed.また、骨片あるいは移植物に接触する以外の部分は別の素材で作製されても良いが、ＭＲＩ造影を妨害しないものや、固定作業直後に切断し体外に除去できるもの等であることが望ましい。 Further, portions other than in contact with the bone fragments or implants may be manufactured in a different material, it is desirable and those that do not interfere with the MRI contrast is like those that can be removed from the body is cut immediately after the fixing work .

【００１２】本発明において、長軸方向に変形あるいは加熱によって断面積が増大する性質を有する配向したプラスチックは、未延伸の上述した材料を金属製の管に挿入し共に延伸した後、一定の温度にて処理することによって得られる。 [0012] In the present invention, oriented plastic having properties the cross-sectional area increased by deformation or heating in a longitudinal direction, after the above-described material of the undrawn and drawn together and inserted into the tube of metal, constant temperature obtained by processing at.本発明の骨固定ピンは、加熱や変形によって分子配向がもとに戻る延伸プラスチックの性質を利用するため、骨固定ピンを利用する温度では配向した分子状態で無負荷で一定の形状を保つ必要があり、従来このような分子状態を目的とする形状で均一に作製することは非常に難しく、かつこのような分子状態を一定形状の延伸配向した同一材料の一部に安定に作製することはさらに困難であったが、本発明の配向させる方法によって克服できる。 Bone fixing pin of the present invention, the molecular orientation by heating and deformation to utilize the properties of stretched plastic back to the original, necessary to maintain a constant shape in an unloaded molecular oriented state at temperatures utilizing bone fixation pin There is, conventionally such a molecular state uniformly it is very difficult to produce a shape for the purpose, and be stably produced on a part of the same materials stretch orientation of such molecules state a certain shape It was the more difficult, can be overcome by a method of orienting the present invention.

【００１３】さらに具体的に説明すると、塑性変形し易くかつ初期弾性率が目的のプラスチック延伸物より充分大きい素材、好ましくはアルミ、真鍮、銅のような金属で作製したパイプに、未延伸のプラスチック成形物を挿入し、通常の金属パイプの引き落とし加工と同様に引き落とすことによって、金属パイプと共にプラスチック成形物を引き落とし、プラスチックの分子を配向させる。 [0013] More specifically, plastically deformed easily and initial elastic modulus is sufficiently larger than the plastic orientation of interest materials, preferably aluminum, brass, a pipe manufactured with a metal such as copper, unstretched plastic the molding was inserted, by debiting like the debit processing ordinary metal pipe debiting plastic molding with a metal pipe, to orient the molecules of the plastic.このとき延伸配向した金属パイプの中のプラスチックは、金属パイプとプラスチックとの界面の滑り抵抗と引き落としによって金属パイプの内面方向に生じる圧迫力によって外力を加えずかつ結晶化を進めなくとも分子の配向した状態を広い温度範囲で維持できる。 Plastic in the metal pipe stretched oriented this time, the orientation of the molecule without promoting and crystallized without addition of an external force by pressing force generated in the inner surface direction of the metal pipe by slip resistance and withdrawal of the interface between the metal pipe and plastic the state can be maintained over a wide temperature range.金属パイプ内側に生じる圧迫力は、通常の延伸の際分子間に発生する可能性のある微少なボイドの発生を抑えつつ、均一かつ良好な延伸が可能である。 Compression force generated in the metal pipe inside, while suppressing the generation of fine voids that can occur between molecules during normal stretching, it is possible to uniform and good stretchability.その後、金属パイプと一体の状態で高強度化する必要のある部分のみプラスチックが結晶化する温度に加熱し、もとに戻したい部分はその熱が伝わらないよう冷却したり、あるいは金属パイプをはぎ取っても外径が変化しない適当な熱処理を行うことができる。 Thereafter, the plastic only part that needs to be high strength in the state of metal pipe and integrally heated to a temperature to crystallize, stripped portion to return to the original or cooled so as not transmitted its heat, or metal pipe it is possible to perform appropriate heat treatment the outer diameter is not changed even.

【００１４】すなわち、上述した方法によればプラスチックを配向していながら結晶化が進みにくい状態に特別に外力を加えることなしに維持できるため、例えば熱処理前に金属パイプごと複雑に曲げておいた後に加熱結晶化させて、均一に曲げ癖にのついた延伸物を得ることも可能であり、延伸配向したプラスチック製のバネを造ることも自在にできる。 [0014] That is, since it maintained specially without adding an external force to the hard state crystallization while not oriented plastic proceeds according to the method described above, for example, after which had been intricately bent each metal pipe before the heat treatment by heating crystallization, it is also possible to obtain the attached stretched material to uniformly curl may freely be made of plastic springs stretched orientation.これは、通常のダイス延伸や紡糸に使われる連続延伸、静水圧押し出しによる延伸方法では困難であり、多数の延伸物を均一に作製することはさらに困難である。 This continuous stretching is used for normal die drawing or spinning is difficult in the stretching process according to hydrostatic extrusion, it is more difficult to uniformly produce a large number of stretching thereof.なお、成形と熱処理を終えた金属パイプ被覆プラスチック延伸物を金属パイプから取り出すことは、通常考え得る方法で容易に行える。 Note that to take out the metal pipe coated plastic stretched product having been subjected to molding and heat treatment of a metal pipe, easily in a way that may normally be considered.例えば、複雑な3次元形状にした場合には酸や電気分解で金属を溶かし去ることも可能であり、また金属パイプの軸に平行にスリットを加え引き裂くように金属パイプをはぎ取ることも可能であり、さらにスリットをいれた後３次元形状に成形して酸や電気分解と物理的にはぎ取る方法を混在させることも可能である。 For example, when the complex three-dimensional shape is also possible to leave melted metal with an acid or electrolysis, also it is also possible to strip the metal pipe to tear added a slit parallel to the axis of the metal pipe it is also possible to mix further method stripping the molded to acid or electrolysis and physically three-dimensional shape after put slits.

【００１５】また、上述した方法によると次の３点の利点を有する。 [0015] According to the method described above has the advantage of following three points.結晶化に使う加熱の条件を広く設定できるため、太い成形物でもしっかり温度制御することができ、プラスチック延伸物の内部と外部で熱のかかり具合が違うことによる不均一さが生じにくいという利点もあり、太い延伸高強度プラスチックを作製するためには非常に有効な方法である。 Since it wider heating conditions used for crystallization, can also be tightly temperature-controlled with a thick molded product, an advantage that unevenness hardly occurs due to differ internally and externally takes the heat degree of plastic orientation thereof There is a very effective way to produce a thick stretched high-strength plastic.延伸前のプラスチック成形物は断面が均一な長尺物である必要はなく、テーパー状のものにして出来上がりの延伸成形物をテーパー状の部分延伸ロッドとしたり、2種の異なる材料で作製したプラスチック成形物を使うことで、例えば、パイプのような様々な形の延伸成形物を得ることが可能である。 Plastic moldings before stretching need not be cross section uniform long object, or a tapered portion stretching rod stretched molded product finished by those tapered, produced in two different materials plastic by using a molded product, for example, it is possible to obtain a stretched molded product of various forms, such as a pipe.引き落としダイスを何段階にも変えて、段階で徐々に引き落とすことが可能なため、延伸時に破壊しやすいプラスチックでも延伸しやすいだけでなく、ダイスの孔の形を適当に変えることで、断面が丸以外の、例えば、6角形や星形、楕円など様々な断面形状の延伸プラスチック成形物を得ることができる。 Also changing the debiting die many stages, since it is possible to withdraw gradually stage, not only easily stretched even destroyed easily plastic during stretching, by changing the shape of die holes suitably cross section round other, for example, can be obtained hexagonal or star, stretched plastic molding of various cross-sectional shapes such as elliptical.

【００１６】変形により本発明の骨固定ピンの断面積を増大させる方法としては、骨片、移植物、骨に設けた下孔の開口部付近で屈曲させる等により変形させて増大させる方法がある。 [0016] As a method for increasing the cross-sectional area of ​​the bone fixing pin of the present invention by the deformation, there is a method of increasing by deforming the bone, implants, etc. to bend near the opening of the lower hole provided in the bone .

【００１７】加熱により本発明の骨固定ピンの断面積を増大させる方法としては、固定ピンを中空状に成形し、 [0017] As a method for increasing the cross-sectional area of ​​the bone fixing pin of the present invention by heating, molding the fixing pin to the hollow,例えば電気や電磁誘導で発熱するニクロム線やコイル、 For example nichrome wire or a coil which generates heat by electricity or electromagnetic induction,高温に加熱した金属棒などの発熱体、あるいは超音波の発生する棒などを挿入する方法があげられる。 A heating element such as a metal rod which has been heated to a high temperature, or a method of inserting a like rod generated by the ultrasound and the like.この時、 At this time,発熱体は骨固定ピンに挿入前に装着して加熱後骨固定ピンの断面積を増大させた後に骨固定ピンの１端から外部に抜き去っても良いし、骨固定ピンを下孔に挿入後、固定具の一端から挿入して発熱させて骨固定ピンの断面積を増大させた後抜き去っても良い。 Heating element may be retracted away to the outside from one end of the bone fixation pin after increasing the cross-sectional area of ​​the mounting to heating after bone fixation pin prior to insertion into the bone fixing pin, inserting the bone fixing pin into the lower hole after, or by heating inserted from one end of the fixture be retracted away after increasing the cross-sectional area of ​​the bone fixation pin.

【００１８】さらに、棒状体の固定具の少なくとも一端に骨片や移植物に突き通した固定具挿入用の下孔の外径より充分小さい外径で、下孔を容易に通過できる下孔通過用ガイド部分を設けた骨固定ピンにより、このガイド部分から下孔に挿入することにより、屈曲した下孔でも通しやすくできる。 Furthermore, a sufficiently small outer diameter than the outer diameter of the lower hole for at least one end in a fixture insertion that piercing the bone fragments or implant fixture of the rod-shaped body, the lower hole passes readily pass through the lower hole the bone fixation pin having a use guide portion, by inserting the lower hole from the guide portion can easily through even lower hole bent.この時、屈曲した下孔を通過する際、外径が増すため、骨と固定具が密着し易く、よりしっかりとした固定が可能である。 At this time, when passing through the bent lower hole, due to the increased outer diameter, easily contact the bone and the fixture can be more firm fixation.また、前記ガイド部分と固定具部分は、挿入時に実質的に骨に引っかからないようスムースに連結されていることが重要であるが、挿入方向と逆の方向に抜こうとすると骨固定ピンが骨に引っかかるようなカエリがついていても差し支えない。 Further, the guide portion and the fixture portion, it is important that it is connected smoothly to substantially catch on the bone during insertion, the bone fixing pin when you overtake the direction of the insertion direction opposite bone no problem even with a burr that could get caught in.

【００１９】本発明の骨固定ピンは、断面の形状を多角形にしたものであっても良く、固定しようとする骨片同士や骨片と移植物を突き通した下孔を通して挿入する際に効果的である。 The bone fixation pin of the invention, when inserted through the cross-sectional shape may be obtained by a polygonal, lower hole piercing implants and bone to each other and bone fragments to be fixed it is effective.すなわち断面を多角形にすることにより、骨固定ピンと骨あるいは移植物の間の滑り抵抗が低減し、挿入しやすく、かつ、挿入作業時骨固定ピンの角が骨の一部を削ることで、骨固定ピンを軸として骨片や移植物が回転することを防ぐことができ、さらに変形や加熱によって骨固定ピンの太さを増すことで、骨片や移植物が骨固定ピンの軸方向に滑ることも抑えられ、より効果的な固定ができる。 That is, by making the cross-section polygonal, reduces the sliding resistance between the bone fixation pin and a bone or implant inserted easily, and the corner of insertion work time of the bone fixation pins by cutting the part of the bone, it is possible to prevent the bone fragments or implants rotates the bone fixing pin as an axis, by further increasing the thickness of the bone fixing pin by deformation or heating, bone fragments or implants are in the axial direction of the bone fixation pin also suppressed slipping, it can more effectively fixed.また、本発明の骨固定ピンは加熱により断面積を増大させて用いる時に必ずしもヒーターを挿入するために中空構造にする必要はなく、穴をあけながら熱などを加えて断面積を増大させても良い。 Further, the bone fixing pin of the present invention need not necessarily be a hollow structure in order to insert a heater when used to increase the cross-sectional area by heating, even if the heat or the like to increase the cross-sectional area added with a hole good.

【００２０】 [0020]

【発明の実施の形態】図１は本発明の骨固定ピンの第1 DESCRIPTION OF THE PREFERRED EMBODIMENTS Figure 1 is a first bone fixing pin of the present inventionの実施形態を示す上面図及び正面図である。 It is a top view and a front view showing an embodiment.なお、以下、各図中の下側を「先端」、上側を「基端」として説明する。 Hereinafter, explaining the lower side in the figure, "tip", the upper as "proximal".図１に示すように、本発明の骨固定ピン１は、 As shown in FIG. 1, the bone fixing pin 1 of the present invention,主に骨片同士を固定する棒状の部材であって、少なくとも長軸方向の一部に断面積の増大する性質を有する配向した部分を持つプラスチック部分１１とそれ以外の部分１２からなり、先端側のプラスチック部分１１が一方の骨片（先端側骨片２２）の骨界面を挟むように存在する。 Primarily a rod-shaped member for fixing the bone fragments to each other, made from the portion 12 of the other plastic part 11 with oriented portions having increasing nature of the cross-sectional area at least a portion of the long axis direction, the distal end side plastic part 11 is present so as to sandwich the bone interface of one bone fragment (distal end bone fragment 22) of.また、基端側のプラスチック部分１１も基端側骨片２１の骨界面を挟んで存在する。 Further, the plastic portion 11 of the base end side exists across the bone interface of the proximal bone fragment 21.プラスチック部分１１ Plastic part 11の構成材料は、特に限定されないが、例えばポリグリコール酸、ポリ乳酸、ポリジオキサノン、ポリヒドロキシ酪酸、及びそれらの共重合体等の生分解性ポリマーで構成されていることが望ましいが、少なくとも長軸方向の一部に断面積の増大する性質を有する配向した部分を持つプラスチック材料であれば何でもよい。 The materials of construction, but are not limited to, for example, polyglycolic acid, polylactic acid, polydioxanone, polyhydroxybutyric acid, and it is preferably composed of biodegradable polymers such as copolymers thereof, at least the long axis direction It may be any plastic material having an oriented portion having increasing nature of the cross-sectional area in a part of.部分１２は特に限定されずプラスチック部分１１と同じ材料でも良い。 Portion 12 may be the same material as the plastic part 11 is not particularly limited.

【００２１】次にこの骨固定ピンの使用方法について、 [0021] Next, how to use this bone fixation pin,図２及び図３に基づき説明する。 It will be described with reference to FIGS.骨片２１、２２に骨固定ピン1が挿入される下孔をあけ、同時に先端側のプラスチック部分１２が一方の骨片（先端側骨片２２）の骨界面を挟むように、さらに基端側のプラスチック部分１ Drilled pilot hole the bone fixing pin 1 to the bone pieces 21 and 22 are inserted, as the tip end side plastic part 12 simultaneously sandwich the bone interface of one bone fragment (distal end bone fragment 22), further proximal side plastic part 1２も基端側骨片２１の骨界面を挟むように挿入する（図２）。 2 also inserted so as to sandwich the bone interface of the proximal bone fragment 21 (Fig. 2).骨固定ピン１を挿入後、先端側のプラスチック部分１２を外力または熱によってその断面積を増大させ、 After inserting a bone fixation pin 1, the plastic part 12 on the tip side increases its cross sectional area by an external force or heat,アンカー部３２を形成させる。 To form the anchor portion 32.続いて骨固定ピン1の基端側最後端を引っ張りながら基端側のプラスチック部分１２に、外力、熱によってアンカー部３１を形成させ固定を行う（図３）。 Then the plastic part 12 of the proximal end edge of the pull while the base end side bone fixing pin 1, the external force, the fixed to form an anchor portion 31 by heat conducted (Fig. 3).なお、プラスチック部分１２にかかる外力とは、曲げによる力、剪断力、捻りによる力、超音波等プラスチック部分１２の断面積を増大させるものであれば限定されない。 Note that the external force applied to the plastic part 12, the force due to bending, shearing forces, forces due to twisting is not limited as long as it increases the cross-sectional area of ​​the ultrasonic wave or the like plastic part 12.また、プラスチック部分１２にかかる熱とは、ヒーターによる加熱、摩擦による熱、超音波による熱、赤外線等、プラスチック部分１２の断面積を増大させるものであれば限定されない。 Further, the heat applied to the plastic part 12, heated by the heater, heat due to friction, heat by ultrasonic, infrared, and the like as long as it increases the cross-sectional area of ​​the plastic part 12.

【００２２】図４は本発明の骨固定ピンの第2の実施形態を示す上面図及び正面図である。 [0022] FIG. 4 is a top view and a front view showing a second embodiment of a bone fixing pin of the present invention.なお、以下、各図中の下側を「先端」、上側を「基端」として説明する。 Hereinafter, explaining the lower side in the figure, "tip", the upper as "proximal".本発明の骨固定ピン４は、少なくとも長軸方向の一部に断面積の増大する性質を有した配向したプラスチック部分４１と、その中心の中空部分４２からなる。 Bone fixing pins 4 of the present invention, the plastic part 41 oriented had the increasing nature of the cross-sectional area at least a portion of the long axis, a hollow portion 42 of the center.プラスチック部分４１の構成材料は、特に限定されないが例えばポリグリコール酸、ポリ乳酸、ポリジオキサノン、ポリヒドロキシ酪酸、及びそれらの共重合体等の生分解性ポリマーで構成されていることが望ましいが、少なくとも一方向において断面積の増大する性質を有した材料であれば限定されない。 The material of the plastic part 41, in particular but not limited to for example polyglycolic acid, polylactic acid, polydioxanone, polyhydroxybutyric acid, and it is preferably composed of biodegradable polymers such as copolymers thereof, at least a not limited as long as the material having a increasing nature of the cross-sectional area in the direction.

【００２３】次にこの骨固定ピンの使用方法について、 [0023] Next, how to use this bone fixation pin,図５及び６に基づき説明する。 It will be described with reference to FIGS. 5 and 6.あらかじめドリルにて骨固定ピンを挿入する孔４５を形成し、プラスチック部分４１の先端側が一方の骨片（先端側骨片４４）の孔４５ Forming a hole 45 for inserting a bone fixation pin in advance drill hole 45 of the tip end side one of the bone pieces of plastic part 41 (distal end bone fragment 44)の先端に届くよう先端部分にヒーターが内蔵されている挿入具５にて挿入する。 Heater insert in insert 5 built in the tip portion so as to be received in the tip.挿入後、挿入具５のヒーターを加熱することによりプラスチック部分４１の断面積を増大させ、骨との隙間のないように固定する。 After insertion, increasing the cross-sectional area of ​​the plastic part 41 by heating the heater of the insert 5 is fixed so as not gap between the bone.また、プラスチック部分４１にかかる熱には、ヒーターによる加熱以外にも、摩擦による熱、超音波、赤外線等があげられ、プラスチック部分４１の断面積を増大させるもので限定されない。 Further, the heat applied to the plastic part 41, in addition to the heating by the heater is also heat due to friction, ultrasonic, infrared, and the like, not limited in that increasing the cross-sectional area of ​​the plastic part 41.

【００２４】図７は本発明の骨固定ピンの第3の実施形態を示す上面図及び正面図である。 FIG. 7 is a top view and a front view showing a third embodiment of a bone fixing pin of the present invention.なお、以下、各図中の下側を「先端」、上側を「基端」として説明する。 Hereinafter, explaining the lower side in the figure, "tip", the upper as "proximal".骨固定ピン６は、少なくとも長軸方向の一部に断面積の増大する性質を有した配向したプラスチック部分６１とそれ以外の部分６２からなりテーパー状に構成されている。 The bone fixation pin 6 is configured becomes tapered from plastic part 61 and the other portion 62 oriented had the increasing nature of the cross-sectional area at least a portion of the long axis direction.プラスチック部分６１の構成材料は、特に限定されないが、例えばポリグリコール酸、ポリ乳酸、ポリジオキサノン、ポリヒドロキシ酪酸、及びそれらの共重合体等の生分解性ポリマーで構成されていることが望ましいが、少なくとも一方向において断面積の増大する性質を有した材料であれば限定されない。 The material of the plastic part 61 is not particularly limited, for example, polyglycolic acid, polylactic acid, polydioxanone, polyhydroxybutyric acid, and it is preferably composed of biodegradable polymers such as copolymers thereof, at least not limited as long as the material having a increasing nature of the cross-sectional area in one direction.

【００２５】次にこの骨固定ピンの使用方法について、 [0025] Next, how to use this bone fixation pin,図８及び９に基づき説明する。 It will be described with reference to FIGS. 8 and 9.あらかじめドリルにて骨固定ピンを挿入するテーパー状の孔を形成し、プラスチック部分６１が一方の骨片（基端側骨片６３）の骨界面を挟んで存在するように挿入する。 Forming a tapered hole for inserting a bone fixation pin in advance a drill, inserted as the plastic part 61 is present across the bone interface of one bone fragment (base end side bone fragment 63).挿入後、基端部分を引っ張り上げ、外力、熱によってプラスチック部分６１ After insertion, pulling up the proximal portion, the plastic portion 61 external forces, by heatの断面積を増大させ、アンカー部７を形成させ骨との隙間のないように固定する。 Sectional area of ​​the increase, to secure as no gaps between the bone to form an anchor portion 7.なお、プラスチック部分６１ It should be noted that the plastic part 61にかかる外力とは、曲げによる力、剪断力、捻りによる力、超音波等プラスチック部分６１の断面積を増大させるものであれば限定されない。 In a such an external force, the force due to bending, shearing forces, forces due to twisting is not limited as long as it increases the cross-sectional area of ​​the ultrasonic wave or the like plastic part 61.また、プラスチック部分６１にかかる熱とは、ヒーターによる加熱、摩擦による熱、超音波、赤外線等、プラスチック部分１２の断面積を増大させるものであれば限定されない。 Further, the heat applied to the plastic part 61, heated by the heater, heat due to friction, ultrasonic, infrared, and the like as long as it increases the cross-sectional area of ​​the plastic part 12.プラスチック部分４１にかかる熱とは、ヒーターによる加熱、摩擦による熱、超音波、赤外線等、プラスチック部分４１の断面積を増大させるものであれば限定されない。 The heat applied to the plastic part 41, heated by the heater, heat due to friction, ultrasonic, infrared, and the like as long as it increases the cross-sectional area of ​​the plastic part 41.

【００２６】 [0026]

【実施例】以下、実施例を本発明を更に詳細に説明する。 EXAMPLES The following further illustrate the present invention Example.（実施例１）直径３ｍｍのポリ乳酸からなる棒体を銅管と共に延伸した後、そのまま２０〜１６０℃の温度で４ (Example 1) 4 bar body made of polylactic acid 3mm diameter after stretched with copper pipe, as it is at a temperature of 20 to 160 ° C.時間熱処理し、配向した直径２.０ｍｍのポリ乳酸の棒体を得た。 And time heat treatment to obtain a rod of polylactic acid oriented diameter 2.0 mm.次に、この棒体をプラスチック部分１１とする図１に示す形状の骨固定ピン１を作成した。 Then, created a bone fixation pin 1 of the shape shown the rod in FIG. 1, the plastic part 11.

【００２７】羊前腕骨肘頭に骨切りを施した後、電動ドリルにて２.１ｍｍの下穴を開けた。 [0027] After having been subjected to osteotomy in sheep forearm bone elbow head, opened the bottom hole of 2.1mm in an electric drill.そして図２に示すように骨固定ピン１を骨切り線に対して垂直に挿入した。 The bone fixation pin 1 as shown in FIG. 2 was inserted perpendicular to the osteotomy line.先端側のプラスチック部分１１を左右に９０度屈曲させたところ、骨固定ピン１の断面積より４０％断面積が増大し、アンカー部３２（図３に記載）が形成された。 When a plastic part 11 on the distal end side were left to bend 90 degrees, increased 40% cross-sectional area than the cross-sectional area of ​​the bone fixation pin 1, the anchor portion 32 (described in FIG. 3) is formed.図3に示すように先端側プラスチック部分１１を骨界面になるべく近いところで切断し、骨固定ピンの基端側を引っ張り上げた後、基端側プラスチック部材１１を左右に９０度屈曲させ、骨固定ピンの断面積より４０％ The distal end side plastic part 11 as shown in FIG. 3 was cut at as close as possible to the bone interface, after raised to pull the base end side of the bone fixing pin, is bent 90 degrees proximal side plastic member 11 to the left and right, the bone fixation than the cross-sectional area of ​​the pins 40%断面積を増大させ、固定を行った。 The cross-sectional area is increased, was fixed.また同様な方法で、 For the same way,それぞれの骨片のドリル穴が屈曲してつながっている穴を開け（穴と穴の角度が９０度）固定を行ったところ、 When the drill holes of the respective bone fragments bore the drilled that is connected to the bending (angle of the hole and the hole is 90 degrees) were fixed,ドリル穴が９０度で屈曲しているところでプラスチック部分１１の断面積が増大し、より固定力が保持できる固定を行うことができた。 Sectional area of ​​the plastic part 11 is increased where the drill holes are bent at 90 degrees, and more fixing force is able to perform fixing to hold.この際、プラスチック部分１１ In this case, the plastic part 11の先端部分はガイド部分として直径１.５ｍｍに切削して用いた。 The tip portion of used by cutting into 1.5mm diameter as a guide portion.

【００２８】（実施例２）実施例１と同様の方法により配向した直径３.５ｍｍのポリヒドロキシ酪酸の棒体を得た。 [0028] was obtained (Example 2) rods of polyhydroxybutyrate diameter 3.5mm oriented in the same manner as in Example 1.この棒体の一端から中空状に直径２ｍｍの穴を開け、この穴を中空部分４２とする図４にその形状を示す骨固定ピン４を作製した。 Hollow in a hole with a diameter of 2mm from one end of the rod, to prepare a bone fixation pin 4 showing the shape in FIG. 4 that the hole and the hollow portion 42.羊上腕骨骨頭に骨切りを施した後、電動ドリルにて３.６ｍｍの下穴を開けた。 After having been subjected to osteotomy in sheep humeral head, opened the bottom hole of 3.6mm in an electric drill.骨固定ピンを、骨切り線に対して垂直にヒーターを内蔵した挿入具5を用いて挿入した。 The bone fixation pin was inserted using the insertion tool 5 with a built-in heater perpendicular to the osteotomy line.その後挿入具５に内蔵したヒーターによりプラスチック部分４１の断面積を増大させ、骨との隙間のないように固定を行うことができた。 Then increase the cross-sectional area of ​​the plastic part 41 with a heater incorporated in the inserter 5, it was possible to perform the fixing to no gaps between the bone.また、配向した直径３.９２ｍｍのポリヒドロキシ酪酸からなる骨固定ピン４と同形状の骨固定ピンを使用して、ヒーターを内蔵した挿入具5の代わりに同形状で先端から超音波（４０.０ｋＨｚ）が発生する装置を用いて骨固定ピンの断面積の増大を求めたところ、最大で１ Further, by using the bone fixing pin of the same shape as the bone fixing pin 4 consisting of polyhydroxy butyric acid oriented diameter 3.92Mm, ultrasonic waves from the tip in the same shape instead of the insert 5 with a built-in heater (40. was determined an increase in the cross-sectional area of ​​the bone fixation pin with a device 0 kHz) is generated, at most 1２２％の断面積の増大が見られた。 22% increase in cross sectional area was observed.実際に牛中手骨を用いて、2つの骨片に４.０ｍｍ径のドリルで下穴を開け、 Actually using bovine metacarpals, drilled pilot hole drill of 4.0mm diameter two bone fragments,配向した直径３.９２ｍｍの骨固定ピンを挿入し、超音波にて骨固定ピンの断面積を増大させ固定を行ったところ良好な固定が得られた。 Insert the bone fixation pin oriented diameter 3.92Mm, it was subjected to stationary increase the cross-sectional area of ​​the bone fixation pin by an ultrasonic good fixation is obtained.

【００２９】本発明の骨固定ピンは棒状であれば、その断面が円形とは限らず多角形でもよく、六角形にポリヒドロキシ酪酸の延伸を行い、その六角形の一辺が２ｍｍ [0029] If the bone fixing pin of the rod-like of the present invention may be in cross-section a polygonal shape not necessarily circular, performs drawing of polyhydroxybutyrate hexagonal, 2 mm is one side of the hexagonの骨固定ピンに１ｍｍの穴をあけ中空構造としたものを用いて、先端から超音波（４（４０.０ｋＨｚ）が発生する装置を用いて断面積を増大させて羊肘頭の骨折を固定したところ、良好な固定結果が得られた。 Using those hollow structure a hole of 1mm in the bone fixing pin of the fixing fractures Hitsujihijiatama by increasing the cross-sectional area by using the apparatus ultrasound (4 (40.0kHz) is generated from the tip where was, good fixation results were obtained.

【００３０】（実施例３）実施例１と同様の方法により、配向した直径３.５ｍｍのポリヒドロキシ酪酸の棒体を得た。 [0030] the same manner as Example 3 Example 1 to obtain a rod of polyhydroxybutyrate -oriented diameter 3.5 mm.この棒体を先端５ｍｍ、基端２ｍｍとなるようなテーパー形状に成形し骨固定ピンを得た。 Tip the rod 5 mm, formed into a tapered shape such that proximal 2mm to give a bone fixation pin.羊中手骨にに電動ドリルにて３ｍｍから５ｍｍの下穴を開けた後、骨固定ピンを挿入した。 After opening the pilot hole of 5mm from 3mm at an electric drill to the sheep metacarpal bone, the insertion of the bone fixation pin.その後基端部分を引っ張り上げ、左右に９０度屈曲させて断面積を増大させ固定を行ったところ、良好な固定が得られた。 Then pulled up the proximal portion was subjected to a fixed increase the cross-sectional area depends on being bent 90 degrees, good fixation is obtained.

【００３１】 [0031]

【発明の効果】上述したとおり、本発明により長軸方向の少なくとも一部に断面積の増大する性質を有する配向したプラスチック部分からなる骨固定ピンを提供することができる。 [Effect of the Invention] As described above, it is possible to provide a bone fixing pin consisting of oriented plastic part having increasing nature of the cross-sectional area at least a portion of the longitudinal direction by the present invention.本発明の骨固定ピンは、骨折や骨切り術での骨片や人工物の骨への固定の際に、屈曲等による変形や、ヒーターによる加熱、摩擦による加熱、超音波及び赤外線の照射等の操作により、簡便性を失うことなく強固にそれらを固定することができる。 Bone fixing pin of the present invention, at the time of fixation to the bone of the bone pieces and artifacts in the fracture or osteotomy, or deformation due to bending or the like, heating by a heater, heating by friction, ultrasound and infrared irradiation or the like the operation can firmly fix them without losing convenience.また、分解吸収性の材料で作製することより、抜釘が不要になり患者に対する負担を軽減させることもできる。 Further, from the be made of resorbable materials may be 抜釘 is to reduce the burden on patients becomes unnecessary.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図１】本発明の骨固定ピンの第１の実施形態の上面図及び正面図である。 1 is a top view and a front view of a first embodiment of a bone fixing pin of the present invention.

【図２】図１に示す骨固定ピンを骨片に挿入した状態を示す模式（断面）図である。 The bone fixation pin shown in FIG. 1. FIG is a schematic (cross-sectional) view showing a state in which inserted into the bone fragments.

【図３】図１に示す骨固定ピンの一部分の断面積を増大させた状態を示す模式（断面）図である。 3 is a schematic (cross-sectional) view showing a state in which increased the cross-sectional area of ​​a portion of the bone fixation pin shown in Figure 1.

【図４】本発明の骨固定ピンの第２の実施形態の上面図及び正面図である。 4 is a top view and a front view of a second embodiment of a bone fixing pin of the present invention.

【図５】図４に示す骨固定ピンを骨片に挿入した状態を示す模式（断面）図である。 [5] The bone fixation pin shown in FIG. 4 is a schematic (cross-sectional) view showing a state in which inserted into the bone fragments.

【図６】図４に示す骨固定ピンの一部分の断面積を増大させた状態を示す模式（断面）図である。 6 is a schematic (cross-sectional) view showing a state in which increased the cross-sectional area of ​​a portion of the bone fixing pin illustrated in FIG.

【図７】本発明の骨固定ピンの第３の実施形態の上面図及び正面図である。 7 is a top view and a front view of a third embodiment of a bone fixing pin of the present invention.

【図８】図７に示す骨固定ピンを骨片に挿入した状態を示す模式（断面）図である。 The bone fixation pin shown in FIG. 8 7 is a schematic (cross-sectional) view showing a state in which inserted into the bone fragments.

【図９】図７に示す骨固定ピンの一部分の断面積を増大させた状態を示す模式（断面）図である。 9 is a schematic (cross-sectional) view showing a state in which increased the cross-sectional area of ​​a portion of the bone fixing pin illustrated in FIG.

Claims (4)

Translated from Japanese

【特許請求の範囲】 [The claims]

【請求項１】長軸方向の少なくとも一部が変形あるいは加熱によって断面積の増大する性質を有する配向されたプラスチックからなる骨固定ピン。 Bone fixing pin consisting of oriented plastic claim 1 wherein at least a portion of the axial direction has increased to the nature of the cross-sectional area by deformation or heat.

【請求項２】前記プラスチックが生体内で分解吸収される材料である請求項1に記載の骨固定ピン。 The bone fixation pin according to claim 1 wherein a material in which the plastic is degraded and absorbed in vivo.

【請求項３】前記プラスチックが、ポリヒドロキシ酪酸またはその共重合体からなる請求項１乃至請求項２に記載の骨固定ピン。 Wherein the plastic is a bone fixing pin according to claim 1 or claim 2 consisting of polyhydroxybutyric acid or a copolymer thereof.

【請求項４】プラスチック材料を金属製管体に挿入し、 The 4. A plastic material is inserted into the metal tube,当該金属製管体と共に延伸を行った後、一定の温度にて処理を行うことを特徴とする骨固定ピンの製造方法。 After stretching together with the metallic tube body, a manufacturing method of bone fixation pins, which comprises carrying out the process at a constant temperature.