Refractor Materials Used in Outdoor Luminaires

There are three materials commonly used in molding refractors for outdoor luminaires. Two are thermoplastic materials, acrylic and polycarbonate, and the third is borosilicate glass.

There is a basic difference between the glass and the plastic materials. Acrylic and polycarbonate are both organic, petroleum based compounds and will eventually break down when exposed to the heat and ultraviolet radiation from a lamp or the outdoor environment. The glass, on the other hand, is an inorganic material that will not deteriorate in normal use.

When evaluating the suitability of a material for this application, there are several characteristics that must be considered. They are as follows:

Impact strength

Light transmittance

Clarity or lack of haze

Surface quality

Surface hardness or resistance to abrasion

Resistance to discoloration

To obtain a true evaluation of these materials, their performance must be evaluated not only when new, but also after a reasonable exposure to their normal operating environment.

While in samples of equal thickness both acrylic and polycarbonate have impact strengths, considerably higher than that of glass, there are two additional factors that must be considered. Typically, a borosilicate glass refractor is molded with a thickness that is much greater than that of the plastic equivalents.

A glass refractor will have a wall thickness of up to 1/2 inch while an acrylic or polycarbonate refractor can have a wall thickness of less than 1/8 inch. This major difference in mass reduces the basic material impact strength advantage of plastic.

Second, the impact strength of both plastic materials will deteriorate to a certain degree with age and exposure to ultraviolet radiation, heat and the normal outdoor environment. This is particularly true of polycarbonate, which can lose all of its basic material impact strength advantage in as little as nine months.

he amount of degradation will, of course, depend on the amount of ultraviolet exposure and the material operating temperature, but even with ultraviolet stabilizing additives, the impact strength of a plastic refractor will drop with time, polycarbonate a great deal, and acrylic somewhat.

The light transmittance of a refractor material directly affects the efficiency of a luminaire. The transmittance of borosilicate glass is 92%, the maximum theoretical value for a non-absorbing optical medium. It does not change with age. Polycarbonate plastic starts out at 85% when new and will drop with exposure to ultraviolet radiation, heat and age. The bluish toners added to polycarbonate to cover its natural amber color will further reduce its initial light transmittance. Acrylic, like glass, has an initial light transmittance of 92% and, while there is some deterioration with normal use, its transmittance remains relatively high when compared with polycarbonate.

When a material loses its clarity, it can no longer function as a refractor. If the optical medium becomes cloudy, the light is scattered and the prisms can no longer function to control the light. Borosilicate glass is crystal clear and remains so indefinitely. Acrylic develops a slight haze with time, while polycarbonate does so to a considerable degree. After three years of outdoor exposure, without additional heat and ultraviolet radiation from a light source, one study showed nearly 20% haze in a polycarbonate sample.

The surface quality of plastic refractors can deteriorate with age and exposure to the outdoor environment. The loss of luster and crazing, or the development of tiny surface cracks, can greatly depreciate the appearance of plastic refractors and adversely affect their ability to control light. The surface of a borosilicate glass refractor will not deteriorate with exposure to a normal outdoor environment and is not affected by lamp heat or ultraviolet radiation from the sun or the lamp.

Borosilicate glass has a much harder surface than either acrylic or polycarbonate plastic and will not abrade in handling or due to any foreseeable environmental condition. An acrylic plastic sample developed 55% haze after 100 cycles of a Taber abrasion test, and a polycarbonate sample developed 75% haze.

Glass will not discolor due to exposure to heat, ultraviolet light or normal environmental conditions. Both acrylic and polycarbonate will discolor when exposed to either heat or ultraviolet. An A.S.T.M. yellowness index of 22 is considered to be "noticeable," and 35 is considered to be "prominent." Polycarbonate refractors have been known to reach the "prominent" stage in as little as nine months' use in an H.I.D. luminaire, although three to five years is more common.

In one test, after 5000 hours of exposure to a white mercury vapor lamp, the yellowness index of an acrylic sample increased by 4.8 and that of a polycarbonate sample by 17.0. It's worth noting that 5000 hours is about 15 months use for a luminaire that is operated from dusk to dawn. In an outdoor exposure test with no light source, an acrylic sample showed a yellowness index increase of 1.0, and a UV-stabilized polycarbonate sample showed a yellowness index increase of 3.5 in only 24 months.

In the final analysis, the inorganic borosilicate will retain its desirable characteristics indefinitely, while plastic will deteriorate in normal use and require replacement... Acrylic after a reasonable length of time, and polycarbonate much sooner in most lighting applications.