Journal ArticlesCastro, C.Sanjines, R.Pulgarin, C.Osorio, P.Giraldo, S. A.Kiwi, J.Structure-reactivity relations for DC-magnetron sputtered Cu-layers during E. coli inactivation in the dark and under lightJournal Of Photochemistry And Photobiology A-Chemistry10.1016/j.jphotochem.2010.06.030216295-302This study addresses unreported features for Cu DC-magnetron sputtering on cotton mediating inactivation of Escherichia coil K12 (from now on E. coil). In-depth profile for the different Cu-species inside the cotton fibers was determined by 5 key Ar+ etching. Sputtering for 40-s deposited 4 x 10(16) atoms Cu/cm(2) (taking similar to 10(15) atoms/cm Cu per atomic layer) and this was the threshold amount of Cu necessary for complete bacterial inactivation. This is equivalent to a Cu-loading of 0.060% w/w or 3 nm/15 atomic layers. The inactivation of E. coli was attained within 30 min under visible light (1.2 mW/cm(2)) and within 120 min in the dark. XPS identified the Cu-species on the cotton as a function of the sputtering time. For a longer sputtering time of 180 s, the Cu-content was 0.294% w/w, but the bacterial inactivation kinetics under light was observed within 30 min, as was the case for the 40s sputtered sample. This suggests that Cu-ionic species play a key role E. coil inactivation. The 40s sputtered samples present the highest amount of Cu-sites held in exposed positions interacting on the cotton surface (or inside the cotton) with E. coil. Confocal microscopy shows the higher rugosity of Cu-cotton fibers compared to bare cotton fibers. The Cu-clusters were observed to be similar to 50 nm after 40s DC-magnetron sputtering and presented a wide size distribution. Cu DC-magnetron sputtering leads to thin metallic semi-transparent grey-brown Cu-coating presenting a moderate hydrophobic behavior as determined by contact angle measurements. (C) 2010 Elsevier B.V. All rights reserved.Sputtering;
Cotton;
E. coli;
Cu-ionic;
Etching;
Xps;
Surface-Area Cuo;
Daylight Irradiation;
Textiles;
Nanoparticles;
Polyester;
Polyamide;
Silver;
2010