C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof

C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof

C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof

C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof

C08F220/52—Amides or imides

C08F220/54—Amides

C08F220/60—Amides containing nitrogen in addition to the carbonamido nitrogen

C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE

C09K2208/00—Aspects relating to compositions of drilling or well treatment fluids

C09K2208/12—Swell inhibition, i.e. using additives to drilling or well treatment fluids for inhibiting clay or shale swelling or disintegrating

Abstract

A composition of matter for use in stablizing shale formations in earth boreholes comprising polymeric products, e.g., polymers of a dialkyl aminoalkyl methacrylate, which can optionally be quaternized with an alkyl halide to produce drilling fluid additives which stablize borehole formations containing reactive clays in the presence of an aqueous medium.

Description

BACKGROUND OF THE INVENTION

[0001]

1. Field of the Invention

[0002]

The present invention relates to polymeric compositions that can be used to stabilize reactive clays in subterranean formations and to a method of stabilizing such reactive clays.

[0003]

2. Description of the Prior Art

[0004]

In the drilling of oil and gas wells and other such boreholes, it is generally necessary to use a drilling fluid that performs a variety of functions but is primarily used to lubricate the drill bit and carry the cuttings to the surface. It is not uncommon to encounter formations during the drilling process that are argillaceous. These argillaceous formations contain clay (shale) particles, the proportion of which can vary over a wide range. When these argillaceous formations are encountered, and if a water based drilling fluid is employed, complex chemical reactions take place within the argillaceous formation, including ion exchange, hydration, etc. These reactions result in swelling, crumbling or dispersion of the clay or shale particles in the formation through which the drill bit passes. Indeed, the problems can become so severe that washout and even complete collapse of the borehole can occur.

[0005]

In an attempt to solve these problems, additives are included in the aqueous drilling fluid that are designed to arrest or slow down fluid invasion into the formation by forming an impermeable or semi-impermeable membrane on the surface of the borehole. For example, sodium silicate-based drilling fluids are believed to form such semi-impermeable membranes and are commonly used for maintaining shale stability. Other drilling fluid systems have also been used to deal with the problem of shale stabilization. For example, U.S. Pat. No. 4,299,710 discloses a drilling fluid comprising an aqueous solution of a combination of thickeners such as a copolymer and a polysaccharide. Additionally, U.S. Pat. No. 5,972,848 discloses a method for stabilizing shale formations by employing an aqueous solution containing a polymer with a hydrophilic group and a hydrophobic group.

SUMMARY OF THE INVENTION

[0006]

In one preferred aspect, the present invention provides a composition of matter comprising a polymeric product selected from the group consisting of:

[0007]

(1) polymers of a first monomeric component selected from the group consisting of (a) compounds having the formula:

[0008]

wherein Z is oxygen or NH, R1 is H or CH3, R2 and R3 are independently alkyl groups containing from 1 to 3 carbon atoms, and n is from 1 to 3, (b) quaternized compounds of Formula I obtained by reacting compounds of Formula I with an alkyl halide having the formula:

R4X II

[0009]

wherein R4 is an alkyl group containing from 1 to 22 carbon atoms and X is a halide ion, and (c) mixtures of (a) and (b),

[0010]

(2) polymers of compounds having the Formula I which have been polymersized and then quaternized with compounds having the Formula II,

[0011]

(3) polymeric mixtures of (1) and (2), and

[0012]

(4) polymers of compound (a) or (b) and a second monomeric component selected from the group consisting of (d) vinyl pyrrolidone (e) compounds of the formula:

CH2=C(R1)—CO—Z—R4 III

[0013]

and mixtures of (d) and (e),

[0014]

(5) polymers of compounds (d) and (e) provided that Z is NH,

[0015]

(6) polymeric mixtures of (1) and (4), and

[0016]

(7) polymeric mixtures of (2) and (4).

[0017]

In another preferred aspect of the present invention, there is provided a method of stabilizing borehole formations containing reactive clays in the presence of water comprising contacting the formation with an aqueous medium containing of a polymeric product as described above.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0018]

In a preferred form, the present invention involves hydrophobically modifying water-soluble polymers by adding water-insoluble groupings into the polymer to an extent that does not render the water-soluble polymer insoluble in water; i.e., its water solubility remains.

[0019]

As can be seen from the formulas above, the composition of the present invention can take the form of a number of polymeric products which include:

[0020]

wherein Z is oxygen or NH, R1 is H or CH3, R2 and R3 are independently alkyl groups containing from 1 to 3 carbon atoms, and n is from 1 to 3, (b) quaternized compounds of Formula I obtained by reacting compounds of Formula I with an alkyl halide having the formula:

R4X II

[0021]

wherein R4 is an alkyl group containing from 1 to 22 carbon atoms and X is a halide ion, and (c) mixtures of (a) and (b),

[0022]

(2) polymers of compounds having the Formula I which have been polymersized and then quaternized with compounds having the Formula II,

[0023]

(3) polymeric mixtures of (1) and (2), and

[0024]

(4) polymers of compound (a) or (b) and a second monomeric component selected from the group consisting of (d) vinyl pyrrolidone (e) compounds of the formula:

CH2=C(R1)—CO—Z—R4 III

[0025]

and mixtures of (d) and (e),

[0026]

(5) polymers of compounds (d) and (e) provided that Z is NH,

[0027]

(6) polymeric mixtures of (1) and (4), and

[0028]

(7) polymeric mixtures of (2) and (4).

[0029]

Compounds having the Formulas I and III can comprise an acrylic/methacrylic acid deravitive, referred to herein generally as “acrylic acid deravitive”.

[0030]

Generally speaking, when the first and second monomeric components are used to form a copolymer, the molar ratio of the first monomeric component to the second monomeric component will be from about 2:98 to 10:90.

[0031]

The polymers of the present invention can be prepared by several methods. For example, if one desires to use a polymer of compounds having Formula I, a homopolymer can be made. Where first and second monomeric components are employed, one of the first monomeric components can be reacted with one of the second monomeric components to produce a co-polymer of the first and second monomeric components. It will also be apparent that many other variations of preparing the compositions of the present invention can be employed. Thus, a co-polymer can be made from an acrylic acid derivative having the structure of the Formula I and a quaternized version of the acrylic acid derivative having the structure of Formula I.

[0032]

As can also be seen, polymer products obtained by mixing polymers described above can be employed. In yet another method, the acrylic acid derivative that has not been quaternized can be polymerized to form a polymer of the desired molecular weight, following which it can be quaternized to the desired degree by reaction with the alkyl halide.

[0033]

The molecular weight of the polymers of the present invention can vary over wide limits with molecular weights (wt. average) ranging from 50,000 to 500,000 being considered “low” molecular weight polymers, while copolymers having molecular weights ranging from 500,000 to 5,000,000 being considered “high” molecular weight polymers.

[0034]

The modified, i.e., quaternized polymers, of the present invention can be made by two methods:

[0035]

Method 1

[0036]

In this method, the acrylic acid derivative is reacted with the desired alkyl halide, which results in the alkyl halide attaching to the terminal nitrogen and quaternization of the nitrogen. This modified, quaternized monomer is isolated and can then be copolymerized with more of the acrylic acid derivative, (Formula I), vinyl pyrrolidone, a compound of Formula III or a mixture thereof.

[0037]

Method 2

[0038]

In this method, the acrylic acid derivative, as described in Formula I, is homopolymerized, following which this polymer is reacted with a suitable alkyl halide in the presence of a surfactant. The surfactant is necessary because of the fact that the alkyl halide is not water soluble whereas the polymerized acrylic acid derivative is. Accordingly, the surfactant acts to solubilize the alkyl halide such that it can react with the terminal nitrogen of the acrylic acid derivative.

[0039]

The polymers of the present invention have been shown in laboratory testing to vastly reduce shale erosion. A shale erosion test is commonly employed to determine the ability of a drilling fluid and/or the additives therein to prevent a shale from eroding in the presence of an aqueous medium such as an aqueous based drilling fluid. Such erosion, when encountered in actual field conditions in a borehole, and as noted above, can lead to problems ranging from a washout to a complete collapse of the borehole.

[0040]

A typical shale erosion test is conducted by rolling a weighed portion of sized shale particles in an aqueous medium and then screening the particles to determine the amount of shale that eroded to the point of passing through a selected sized screen. In the shale erosion test used with the compositions of the present invention, U.S. Standard Sieve Series No. 6 and No. 14 screens were employed. The shale was crushed and ground into particles that passed through the 6 mesh screen but were retained on the 14 mesh screen; i.e., particles of a size (−6+14) were used for the erosion test. Equal portions (40.00 g) of the shale were put into one laboratory barrel (350 ml) of each of the various test drilling fluids and rolled at 150° F. for 16 hours. The drilling fluids were then screened through the 14 mesh screen and the retained solids were washed, dried, and weighed. The percent of erosion was calculated based on the weight loss, corrected for the moisture content (7.67%) of the original sample.

[0041]

The composition of the present invention can be used in fluid for treating subterranean formations including, but not limited to, drilling fluids, completion fluids, remedial fluids and the like. In the method according to the present invention, a drilling fluid containing one of the compositions described above would be incorporated in a suitable amount, e.g., from 1 to 20 lbs/bbl, in the drilling mud or fluid, which, in the conventional fashion, would be circulated in the borehole during the drilling operation. If, during the drilling operation, a formation were encountered that contained a reactive clay, e.g., a clay that had a tendency to erode in the presence of water, the presence of the polymer compositions of the present invention would stabilize the shale, minimizing or ideally stopping the erosion. It is also to be understood that in addition to incorporating the compositions of the present invention in drilling fluids or muds, it can be also used in other downhole fluids under certain circumstances when it is desired to stabilize shale formations.

[0042]

To more fully illustrate the present invention, the following non-limiting examples are presented:

EXAMPLE 1

[0043]

A series of polymers was prepared according to Method 1 described above. To prepare a quaternized monomer of Formula I, to a 100 mL round bottom flask is added 16.7 grams of dimethylaminoethyl methacrylate (DMEMA) and 16.2 grams of hexadecyl bromide. The mixture is heated to 110° F. and stirred for 24 hours. The mixture is then poured into 1 liter of petroleum ether, resulting in precipitation of the quaternized monomer. The monomer is collected on a Buchner funnel, washed with excess petroleum ether, collected, and dried in a vacuum dessicator.

[0044]

To prepare a copolymer, to a 250 ml round bottom flask charge the following: 3.8 grams of DMEMA, 0.7 grams of the quaternized monomer described above, 84.5 grams water, and 1.2 grams concentrated sulfuric acid (to achieve a pH of ˜7.1). This solution is then sparged with nitrogen for 30 minutes, followed by the addition of 0.035 grams 2.2′-azobis (2-amidinopropane) dihydrochloride. The resulting solution is then heated under a nitrogen atmosphere, with stirring, to 110° F. and held for 18 hours to produce a highly viscous polymer solution. In all of the test samples in this example, the acrylic acid derivative employed was DMEMA. The alkyl halide employed was an alkyl bromide, the carbon number appearing in the column labeled “Monomeric Component 1” referring to the chain length of the alkyl group. Except as otherwise indicated, each sample contained 1% by weight of the polymer in deionized water. The results are shown in Table 1 below.

TABLE 1

Monomeric3

Relative

Component 1

Monomeric

Molecular

Sample

(Mole %)

Component 2

Weight

% Erosion

1

—

DMEMA

High

17

21

6% C10

″

″

7

3

″

″

0

4

10% C16

″

″

1

5

15% C16

″

″

−1

6

20% C16

″

″

−1

7

30% C16

″

″

11

82

4% C18

″

″

7

9

—

″

Low

10

10

6% C16

″

″

17

11

15% C16

″

″

18

EXAMPLE 2

[0045]

In this example, the polymers were also prepared according to the procedure of Method 1 as described above with respect to Example 1. In all cases, the acrylic acid derivative employed was DMEMA, and, unless indicated otherwise, each sample contained 1% by weight of the polymer in deionized water. The results are shown in Table 2 below.

TABLE 2

Monomeric2

Relative

Component 1

Monomeric

Molecular

Sample

(Mole %)

Component 2

Weight

% Erosion

1

—

VP

High

33

2

6% C16

″

″

2

3

″

″

Low

44

4

10% C16

″

″

16

5

20% C16

″

″

4.6

EXAMPLE 3

[0046]

In this example, a copolymer was prepared according to Method 2 described above. A homopolymer of DMEMA is prepared as follows. To a 3 L round bottom flask is added 1968.0 grams of water, and this is sparged with nitrogen for 1.5 hours. Next is added 105.0 grams of DMEMA, 25.8 grams concentrated sulfuric acid (to achieve a pH of ˜7.9) and 0.46 grams 2.2′-azobis (2-amidinopropane) dihydrochloride. The mixture is then heated under a nitrogen atomosphere, with stirring, to 110° F. and held for 18 hours to produce a highly viscous polymer solution.

[0047]

The copolymer is produced as follows. To a 250 mL round bottom flask is added 71.0 grams of the DMEMA homopolymer, as described above, followed by 4.0 grams 15% NaOH (to achieve a pH of ˜8.9). Next is added 54.6 grams water, 0.36 grams hexadecyl bromide and 0.39 grams benzylcetyldimethylammonium bromide. This mixture is then heated, with stirring, to 140° F. for 24 hours.

[0048]

The copolymer produced contained 6% (molar) of hexadecyl bromide and was of high molecular weight. A 1% by weight solution of the polymer in deionized water exhibited 0% erosion.

[0049]

As can be seen from Table 1, a homopolymer of DMEMA which has not been quaternized exhibits some degree of erosion control. It has also been found that a homopolymer of DMEMA subsequently quaternized with hexadecyl bromide and of high molecular weight exhibits a −2% erosion. The foregoing description and examples illustrate selected embodiments of the present invention. In light thereof, variations and modifications will be suggested to one skilled in the art, all of which are in the spirit and purview of this invention.

Claims (10)

1. A composition of matter comprising a polymeric product selected from the group consisting of:

wherein Z is oxygen or NH, R1 is H or CH3, R2 and R3 are independently alkyl groups containing from 1 to 3 carbon atoms, and n is from 1 to 3, (b) quaternized compounds of Formula I obtained by reacting compounds of Formula I with an alkyl halide having the formula:

R4X II

wherein R4 is an alkyl group containing from 1 to 22 carbon atoms and X is a halide ion, and (c) mixtures of (a) and (b),

(2) polymers of compounds having the Formula I which have been polymersized and then quaternized with compounds having the Formula II,

(3) polymeric mixtures of (1) and (2), and

(4) polymers of compound (a) or (b) and a second monomeric

component selected from the group consisting of (d) vinyl pyrrolidone (e) compounds of the formula: