Methods are provided for descaling metallic components devices such as stents. The devices or components are cleaned under ultrasound in a cleaning solution of ammonium hydrogen fluoride at a temperature within a range of about 60° to 80° C., then rinsed at that temperature with an aqueous rinse containing...http://www.google.com.au/patents/US8038803?utm_source=gb-gplus-sharePatent US8038803 - Method of descaling metallic devices

Methods are provided for descaling metallic components devices such as stents. The devices or components are cleaned under ultrasound in a cleaning solution of ammonium hydrogen fluoride at a temperature within a range of about 60° to 80° C., then rinsed at that temperature with an aqueous rinse containing a nonionic surfactant and rinsed again with purified water.

Images(4)

Claims(23)

1. A method of descaling a metallic stent comprising the steps of:

a) placing said stent to be descaled in contact with a solution of ammonium hydrogen fluoride at a temperature in the range of about 60° to 80° C. for a period of time sufficient to descale said stent while applying ultrasonic energy to said solution, wherein the descaling removes substantially all slag material, burrs, and sharp ends from a surface of the stent by dissolving metal atoms of the slag material, burrs, and sharp ends into the ammonium hydrogen fluoride solution;

b) removing said stent from said solution and contacting said stent with a first aqueous rinse containing a nonionic surfactant at a temperature in the range of about 60° to 80° C. while applying ultrasonic energy to said first rinse; and

c) removing said stent from said first rinse and contacting said stent with a second aqueous rinse while applying ultrasonic energy to said second rinse.

2. A method according to claim 1 wherein said solution is at a temperature in the range of about 65° to 75° C.

3. A method according to claim 1 wherein said first aqueous rinse is at a temperature in the range of about 65° to 75° C.

4. A method according to claim 1 wherein said second aqueous rinse is at a temperature in the range of about 65° to 75° C.

5. A method according to claim 1 wherein said solution contains about 3 to 6 percent by volume of ammonium hydrogen fluoride.

6. A method according to claim 1 wherein said first aqueous rinse contains about 0.2 to 1 percent by volume of said nonionic surfactant.

7. A method according to claim 6 wherein said nonionic surfactant comprises polyoxyethylene octyl phenyl ether of a formula C14H220(C2H40)n wherein the average of n per molecule is about 9 or 10.

8. A method according to claim 7 wherein said second aqueous rinse contains about 0.4% by volume of said nonionic surfactant.

10. A method according to claim 9 wherein said second aqueous rinse contains about 1% by volume of said nonionic surfactant.

11. A method according to claim 1 wherein said second aqueous rinse consists of purified water.

12. A method according to claim 1 wherein said period of time sufficient to descale is less than about 12 minutes.

13. A method according to claim 12 wherein said period of time is in the range of about 7 to 10 minutes.

14. A method according to claim 12 wherein said stent is contacted with said first aqueous rinse for a period of about 4 minutes.

15. A method according to claim 12 wherein said stent is contact with said second aqueous rinse for a period of about 4 minutes.

16. A method according to claim 12 wherein said stent comprises a triplex material comprising a layer of radiopaque material between layers of stainless steel.

17. A method according to claim 16 wherein said radiopaque material comprises titanium.

18. A method according to claim 1, further comprising electropolishing the surface of the stent after performing the step of descaling.

19. A method according to claim 1, further comprising removing said stent from said second rinse and immersing said stent in a non-corrosive liquid.

20. A method according to claim 1 wherein the solution of ammonium hydrogen fluoride further comprises nitric acid.

21. A method of descaling a metallic stent, comprising:

placing the stent to be descaled in contact with a solution of ammonium hydrogen fluoride at a temperature in the range of about 60° to 80° C. while applying ultrasonic energy to the solution for a period of time sufficient to descale the stent of substantially all slag material, burrs, and sharp ends by dissolving metal atoms of the slag material, burrs, and sharp ends into the ammonium hydrogen fluoride solution;

removing the stent from the solution and contacting the stent with a first aqueous rinse containing a nonionic surfactant at a temperature in the range of about 60° to 80° C. while applying ultrasonic energy to the first rinse;

removing the stent from the first rinse and contacting the stent with a second aqueous rinse while applying ultrasonic energy to the second rinse; and

electropolishing the stent after contacting the stent with the second aqueous rinse.

22. A method according to claim 21 wherein the solution of ammonium hydrogen fluoride further comprises nitric acid.

23. A method of descaling a metallic stent comprising a triplex material comprising a layer of radiopaque material between layers of stainless steel, the method comprising the steps of:

placing said stent to be descaled in contact with a solution of ammonium hydrogen fluoride at a temperature in the range of about 60° to 80° C. for a period of time sufficient to descale said stent while applying ultrasonic energy to said solution, wherein the descaling removes substantially all slag material, burrs, and sharp ends from a surface of the stent by dissolving metal atoms of the slag material, burrs, and sharp ends into the ammonium hydrogen fluoride solution, the ammonium hydrogen fluoride solution dissolving metal of the stainless steel layers at approximately the same rate as metal of the radiopaque material layer so as to result in a substantially even profile across the triplex material after descaling;

removing said stent from said solution and contacting said stent with a first aqueous rinse containing a nonionic surfactant at a temperature in the range of about 60° to 80° C. while applying ultrasonic energy to said first rinse; and

removing said stent from said first rinse and contacting said stent with a second aqueous rinse while applying ultrasonic energy to said second rinse.

Description

RELATED APPLICATION

This application is related to the application entitled “Method and Apparatus for Electropolishing Metallic Stents” by inventors Sanjay Shrivastava, Frank Moloney, Travis Yribbarren, Jeffrey Farina, John Thomas and James Young filed on the same date herewith.

BACKGROUND OF THE INVENTION

The present invention relates generally to methods for descaling devices or components made from metals, and in particular, metallic stents. The methods are particularly directed to the descaling of medical devices made of titanium, stainless steel, tungsten, nickel-titanium, tantalum, cobalt-chromium-tungsten, or cobalt-chromium. While the devices and components to which the present methods are applicable are described mainly as stents, in particular intravascular stents, the invention is not limited to such medical products or stents. For example, the methods may be applied to descale metallic automotive or aerospace structural components.

Stents are generally tube-shaped intravascular devices placed within a blood vessel to maintain the potency of the vessel and, in some cases, to reduce the development of restenosis. The stents may be formed in a variety of configurations which are typically expandable since they are delivered in a compressed form to the desired site. Such a configuration may be a helically wound wire, wire mesh, weaved wire, serpentine stent, or a chain of rings. The walls of stents are typically perforated in a framework design of wire-like connected elements or struts or in a weave design of cross-threaded wire. Some stents are made of more than one material. The stent may be, for example, a sandwich of metals having outer layers of a biocompatible material, such as stainless steel, with an inner layer providing the radioopacity to the stent needed for tracking by imaging devices during placement. A stent made of such material may be, for example, a thin layer of titanium between two layers of stainless steel. In forming such stents from metal, a roughened outer surface of the stent may result from the manufacturing process. It is desirable for the surface of the stent to be smooth so that it can be easily inserted and traversed with low friction through the blood vessels toward the site of implantation. A rough outer surface may not only cause increased frictional obstruction, but may also damage the lining of the vessel wall during insertion. Furthermore, smooth surfaces decrease the probability of thrombogenesis and corrosion.

Since the processing to form metallic stents often results in a product initially having undesirable burrs, sharp ends or debris and slag material from melting the metal during processing, as a first order treatment of the product, descaling of the surface is required in preparation of further surface treatment such as electropolishing.

The invention is directed to a method of descaling a metallic device or component, such as a stent, comprising:

a) placing the device or component in contact with a solution of ammonium hydrogen fluoride at a temperature in the range of about 60° to 80° C. for a period of time sufficient to descale the device or component while applying ultrasonic energy to the solution;

b) removing the device or component from the solution and contacting it with a first aqueous rinse containing a nonionic surfactant at a temperature in the range of about 60° to 80° C. while applying ultrasonic energy to the first rinse;

c) removing the device or component from the first rinse and contacting it with a second aqueous rinse while applying ultrasonic energy to the second rinse; and

d) optionally, removing the device or component from the second rinse and immersing it in a non-corrosive liquid.

In one embodiment the temperature ranges in steps a) and b) are about 65° to 75° C.

In one embodiment, step c) is conducted within the temperature range of about 60° to 80° C. In another embodiment, step c) is conducted within a temperature range of about 65° to 75° C.

In another embodiment, the concentration of ammonium hydrogen fluoride in the solution is about 3 to 6 percent by volume.

Other features of the invention will become apparent from the following detailed description.

DETAILED DESCRIPTION

The present invention is directed to a method for descaling metallic devices or components, in particular, metallic stents. By descaling it is meant to remove undesirable burrs, nicks, sharp ends or debris and slag material attached to the stent.

The invention is described in connection with an embodiment of descaling a single stent, but it is preferred that the stents be descaled in batches. A typical batch will contain three to seven stents, typically five stents having relatively similar lengths.

Since hazardous materials are used in the method of the invention, it would typically be conducted under a ventilated fume hood with the users using suitable protective clothing.

The primary descaling solution is an ammonium hydrogen fluoride (AHF) solution, NH4F.HF, prepared by mixing ammonium difluoride with about 30% nitric acid. Typically about six ounces of ammonium difluoride is used per gallon of 30% nitric acid. Typically the concentration of ammonium hydrogen fluoride will be in a range of about 4 to 6% by volume in the solution. This solution is typically prepared in advance and warmed to a suitable temperature in the range of about 60° to 80° C. Particularly suitable temperatures are in the range of about 65° to 75° C.

The AHF solution is advantageous because it dissolves metals commonly used in metallic medical devices at approximately the same rate. In the case of multilayered composites of different metals the exposed ends of the composite may comprise several different and distinct metal edges. If these metals are not dissolved at approximately the same rate in the cleaning solution, the slower-dissolving metals will form protrusions as the surrounding faster-dissolving metals dissolve. These protrusions are also defects. To avoid this, the cleaning solution must be sufficient to attack commonly used metals, such as stainless steel, tantalum and titanium, at approximately the same rate.

A first aqueous rinse is prepared containing a nonionic surfactant, such as Triton® X-100. Triton® X-100 comprises a polyoxyethylene octyl phenyl ether of the formula C14H22O(C2H4O)n where the average n per molecule is about 9 or 10. Liquinox® is another suitable nonionic surfactant. It comprises sodium dodecylbenzenesulfonate, typically used at a concentration of about 1% by volume in the first aqueous rinse. The first aqueous rinse will comprise purified water and the nonionic surfactant. Typically a small amount of the surfactant is sufficient, usually in the range of about 0.2 to 1% by volume. A useful concentration is about 0.4% of nonionic surfactant by volume in the purified water.

The method according to the present invention includes the following steps. First, the ammonium hydrogen fluoride (AHF) solution is prepared and brought to the required temperature. A useful working temperature is about 70° C. This is preferably accomplished by partially immersing the vessel containing the solution in a bath. Ultrasonic energy is applied to the bath, preferably during its warm-up period and remains applied during the cleaning stage. Then the stent or batch of stents is immersed into the AHF solution for a period of time sufficient to descale the stent or stents. Depending on the size of the stents and the number of stents in the batch, this period of time may vary from several minutes to 30 minutes or more. In a typical batch of five stents each having a length of about 8 to 15 millimeters, the cleaning time in the AHF solution will be about 7 minutes. If the batch of five contains stents having a length in the range of about 18 to 28 millimeters, the cleaning time will be about 10 minutes. The typical cleaning solution of AHF for metallic stents needs only to be a volume of around 25 to 50 milliliters.

After the desired cleaning period in the cleaning solution has expired, the stents are removed and inserted into the first aqueous rinse containing the nonionic surfactant. This first aqueous rinse should also be at a temperature within a range of about 60° to 80° C., typically about 65° to 75° C. The usual temperature of this rinse will be about 70° C., the same temperature used for the cleaning solution. To rinse a typical batch of about five stents, this first aqueous rinse need only have a volume of about 60 milliliters. Typically the stents will remain in the first aqueous rinse for about 3 to 5 minutes while applying ultrasonic energy to the rinse. For a typical batch of about 5 stents, the stents will remain within the rinse for about 3¾ to 4¼ minutes.

After the first rinse, the stents are then placed into the second aqueous rinse, which is purified water, during which ultrasonic energy is also applied to the rinse. The purified water is also typically between temperatures between about 60° to 80° C., more usually about 65° to 75° C. Preferably the temperature of 70° C. is used, the same temperature used for the first aqueous rinse and the cleaning solution. Typically the stents remain in the second aqueous rinse also for about 3¾ to 4¼ minutes. The volume of the first aqueous rinse for using typical batches of five stents is about 60 mls. The volume of the second aqueous rinse for typical batches of five stents is about 30 mls.

After the second aqueous rinse, the stents are then ready for electro polishing. They may be electropolished immediately or stored for later processing. Typically the stents will be stored in alcohol or other suitable non-corrosive liquid to prevent corrosion.

The following example is provided for purpose of illustration and is not intended to limit the invention in any way.

EXAMPLE

A 4.5 percent by volume solution of ammonium hydrogen fluoride solution (AHF) is prepared by adding 6 oz. of ammonium difluoride to a gallon of 30 percent nitric acid. A 25 ml portion of this solution is placed in a PTFE beaker and placed in an ultrasonic bath. The ultrasound is turned on and set for 20 minutes while the AHF solution is warmed. After approximately 10 minutes, the temperature is checked by a thermocouple probe, and the temperature is checked in approximately one-minute intervals until the solution reaches 70° C. Triplex stents are fabricated having a thin layer of titanium sandwiched between two layers of stainless steel, typically having a total strut thickness of about 0.003 mm. For a batch of five stents (having a length and range of 8 to 15 millimeters) the cleaning time will be about 7 minutes at 70° C. For a batch of five stents having a length in the range of about 18 to 28 millimeters, the cleaning time will be about 10 minutes at 70° C. With about 2 to 3 minutes remaining on the ultrasound timer, a glass beaker containing 60.25 mls of the first aqueous rinse is inserted into the ultrasound bath. This rinse is prepared by dispensing 60 ml of purified water into a glass beaker and adding 5 drops of Triton® X-100 nonionic surfactant (about 0.25 ml). The rinse is allowed to reach 70° C. in the bath. Once the AHF cleaning time has elapsed, the stents are promptly removed from the AHF solution and transferred to the first aqueous rinse where they remain for about 4 minutes. Rinse time is typically about 3¾ to 4¼ minutes, while the first aqueous rinse is in the temperature range of about 65° to 75° C. Once the allotted rinse time has elapsed, the stents are removed immediately and transferred to the second aqueous rinse, which is a beaker containing about 30 mls of purified water. This second aqueous rinse is also in the temperature range of about 60° to 75° C. The rinse time in the second aqueous rinse is again typically about 3¾ to 4¼ minutes. After the second rinse time has elapsed, the stents are removed and placed in vials filled with ethanol. After each run, the AHF solution should be replaced.

The embodiments discussed herein are in no way intended to limit the scope of the invention. Various changes and improvements may also be made to the invention without departing from the scope thereof.