SUPERPOLY 20C is a
specialty high quality polyisoprene natural rubber.
It is produced by blending 20 pbw of vulcanised
and 80 pbw of unvulcanised natural. Blending is
carried out in the latex phase to achieve a homogeneous
intimate mix, so very necessary to achieve uniformity
in product quality. The blend is coagulated under
controlled condition, processed into Crumb Rubber
and pressed into bales. To ensure precision and
product quality uniformity, computer-aided processing
techniques are employed.

Dirt
retained on 44 u aperture

%wt

max

0.02

ISO
249

Nitrogen
Content

%wt

max

0.60

ISO
1656

Volatile
Matter

%wt

max

0.60

ISO
248

Initial
Wallace-Plasticity

Po

min

35.00

RRIM(B.7)

Mooney
Viscosity, ML @(1+4) @ 100℃

ML

min

65.00

ISO/R
289

Acetone
Extract

%
wt

max.

3.80

RRIM(B.7)

Total
Sulphur

%
wt

max.

0.60

TS
1-3

Free
Sulphur

%
wt

max.

0.10

TS
1-3

Extrusion
Die-Swell

%

max.

18.70

RRIM(HDS
1-2)

Toluene
Solubility

Satisfactory

Wooden
Pallet-Crate

(LxWxH)

nominal

1,450 x 1,100 x 1,050

Net
Weight

Per Pallet

800 kgs

No
of Bales

Per Pallet

24

Bale
Wrapper

Per Bale

33.3±0.5 kgs

(LxWxH)

nominal

725 x 368 x 255mm

Type

LDPE Film

Thickness

0.03 - 0.05mm

Density

0.92 g/㎤

Melting
Point

min

109℃(Vicat)

Compatility
with NR

min

@ 110℃

Marking
of Pallets

PROPOLY
57

Production
Lot No

Origin

Malyysia

SUPERPOLY 20S is a specialty high quality polyisoprene natural rubber. It is produced by blending 20 pbw of vulcanised and 80 pbw of unvulcanised natural rubber. Blending is carried out in the latex phase to achieve a homogeneous intimate maix, si very necessary to achieve uniformaity in product quality. To ensure precision and product quality uniformity, computer-aided processing techniques are employed. The polymer is presented in the form of sheets but is baled into blocks for easy handling

Dirt
retained on 44 u aperture

%wt

max

0.02

ISO
249

Nitrogen
Content

%wt

max

0.60

ISO
1656

Volatile
Matter

%wt

max

0.80

ISO
248

Initial
Wallace-Plasticity

Po

min

45.00

RRIM(B.7)

Mooney
Viscosity, ML @(1+4) @ 100℃

ML

min

65.00

ISO/R
289

Acetone
Extract

%
wt

max.

3.80

RRIM(B.7)

Total
Sulphur

%
wt

max.

0.60

TS
1-3

Free
Sulphur

%
wt

max.

0.10

TS
1-3

Extrusion
Die-Swell

%

max.

18.70

RRIM(HDS
1-2)

Toluene
Solubility

Satisfactory

Wooden
Pallet-Crate

(LxWxH)

nominal

1,450 x 1,100 x 1,050

Net
Weight

Per Pallet

1000 kgs

No
of Bales

Per Pallet

30

Bale
Wrapper

Per Bale

33.3±0.5 kgs

(LxWxH)

nominal

660 x 330 x 215mm

Type

LDPE Film

Thickness

0.03 - 0.05mm

Density

0.92 g/㎤

Melting
Point

min

109℃(Vicat)

Compatility
with NR

min

@ 110℃

Marking
of Pallets

SUPERPOLY
20C

Production
Lot No

Origin

Malyysia

SUPERPOLY 40 is a specialty high quality polyisoprene natural rubber. It is produced by blending 40 pbw of vulcanised and 60 pbw of unvulcanised natural rubber. Blending is carried out in the latex phase to achieve a homogeneous intimate mix, so very necessary to achieve uniformity in product quality. To ensure precision and product quality uniformity, computer-aided processing techniques are employed. Both crumbs and sheet forms are available.

Dirt
retained on 44 u aperture

%wt

max

0.02

ISO
24

Ash
Content

%wt

max

0.50

ISO
247

Nitrogen
Content

%wt

max

0.60

ISO
1656

Volatile
Matter

%wt

max

0.80

ISO
248

Initial Wallace-Plasticity

Po

min

40.00*

RRIM(B.7)

Mooney
Viscosity, ML (1+4)
@ 100℃

MS

40±5*

ISO/R
289

Acetone
Extract

%
wt

max

3.80

RRIM(B.7)

Total
Sulphur

%
wt

max

1.15

TS
1-3

Free
Sulphur

%
wt

max

0.35

TS
1-3

Gel
Conent

%
wt

max

50.00

Cage

Extrusion
Die-Swell

%
wt

max

18.70

RRIM(HDS
1-2)

Pressed
Sheet Test
(before mastication)

no
nibs

MRPRA(1997)

Wooden
Pallet-Crate

(LxWxH)

nominal

1,450 x 1,100 x 1,050

Net
Weight

Per Pallet

1000 kgs

No
of Bales

Per Pallet

30

Net
Weight

Per Bale

33.3±0.5 kgs

Bale
Dimensions

(LxWxH)

nominal

660 x 330 x 215mm

Bale
Wrapper

Type

LDPE Film

Thickness

0.03 - 0.05mm

Density

0.92 g/㎤

Melting
Point

min

109℃(Vicat)

Compatility
with NR

min

@ 110℃

Marking
of Pallets

SUPERPOLY
20C

Production
Lot No

Origin

Malyysia

SUPERPOLY 50 is prevulcanised rubber of high quality standard. It is produced by blending 50 pbw of vulcanized and 50 pbw unvulcanized natural. Blending is carried out in the latex phase to achieve a homogeneous intimate mix. The blend is coagulated under controlled conditions, processed in crepe or crumb rubber and pressed into bales. To ensure precision and product quality uniformity, computer-aided processing techniques are employed.

Dirt
retained on 44 u aperture

%wt

max

0.03

ISO
249

Ash
Content

%wt

max

0.60

ISO
247

Nitrogen
Content

%wt

max

00.60

ISO
1656

Volatile
Matter

%wt

max

00.80

ISO
248

Mooney
Viscosity, ML (1+4)
@ 100℃

MS

055.00

ISO/R
289

Acetone
Extract

%
wt

max

03.50

RRIM(B.7)

Total
Sulphur

%
wt

max

01.30

TS
1-3

Free
Sulphur

%
wt

max

00.35

TS
1-3

Gel
Conent

%
wt

max

55.00

Cage

Extrusion
Die-Swell

%
wt

max

18.70

RRIM(HDS
1-2)

Pressed
Sheet Test
(before mastication)

no
nibs

MRPRA(1997)

Wooden
Pallet-Crate

(LxWxH)

nominal

1,450 x 1,100 x 1,050

Net
Weight

Per Pallet

1000 kgs

No
of Bales

Per Pallet

30

Net
Weight

Per Bale

33.3±0.5 kgs

Bale
Dimensions

(LxWxH)

nominal

660 x 330 x 215mm

Bale
Wrapper

Type

LDPE Film

Thickness

0.03 - 0.05mm

Density

0.92 g/㎤

Melting
Point

min

109℃(Vicat)

Compatility
with NR

min

@ 110℃

Marking
of Pallets

SUPERPOLY
50C

Production
Lot No

Origin

Malyysia

SUPERPOLY 50B is a specialty high quality polyisoprene natural rubber. It is produced by blending 50 pbw of vulcanised and 50 pbw of unvulcanised natural rubber. Blending is carried out in the latex phase to achieve a homogeneous intimate mix, so very necessary to achieve uniformity in profuct quality. To ensure precision and product quality uniformity, computer-aided processing techniques are employed. The polymer is presented in crepe form but pressed into bales.

Dirt
retained on 44 u aperture

%wt

max

0.02

0.01

ISO
249

Ash
Content

%wt

max

0.50

0.45

ISO
247

Nitrogen
Content

%wt

max

0.60

0.49

ISO
1656

Volatile
Matter

%wt

max

0.55

0.35

ISO
248

Mooney
Viscosity, ML (1+4)
@ 100℃

MS

40-50*

45.00

ISO/R
289

Acetone
Extract

%
wt

max

3.50

3.00

RRIM(B.7)

Total
Sulphur

%
wt

max

0.95-1.25

1.10

TS
1-3

Free
Sulphur

%
wt

max

0.35

0.30

TS
1-3

Gel
Conent

%
wt

max

55.00

53.00

Cage

Extrusion
Die-Swell

%
wt

max

12.5

10.07

RRIM(HDS
1-2)

Pressed
Sheet Test
(before mastication)

no
nibs

MRPRA(1997)

Wooden
Pallet-Crate

(LxWxH)

nominal

1,450 x 1,100 x 1,050

Net
Weight

Per Pallet

1000 kgs

No
of Bales

Per Pallet

30

Net
Weight

Per Bale

33.3±0.5 kgs

Bale
Dimensions

(LxWxH)

nominal

660 x 330 x 215mm

Bale
Wrapper

Type

LDPE Film

Thickness

0.09 - 0.11mm

Density

0.92 g/㎤

Melting
Point

min

109℃(Vicat)

Compatility
with NR

min

@ 110℃

Marking
of Pallets

SUPERPOLY
50B

Production
Lot No

Origin

Malyysia

PROPOLY 57 is prevulcanised rubber of high quality standard. It is produced by blending 80 pbw of vulcanized and 20 pbw unvulcanized natural with 40 pbw of process oil. Blending is carried out in the latex phase to achieve a homogeneous intimate mix. The blend is coagulated under controlled conditions, processed in crumb and pressed into bales. To ensure precision and product quality uniformity, computer-aided processing techniques are employed.

Ash Content

%wt

max

0.80

0.55

ISO247

Nitrogen
Content

%wt

max

0.60

0.50

ISO
1656

Volatile
Matter

%wt

max

0.55

0.40

ISO
248

Mooney
Viscosity, ML (1+4)
@ 100℃

MS

35-45*

42.00

ISO/R
289

Acetone
Extract

%
wt

max

28.5-34.0

32.00

RRIM(B.7)

Total
Sulphur

%
wt

max

1.35

1.20

TS
1-3

Free
Sulphur

%
wt

max

0.30

0.20

TS
1-3

Gel
Conent

%
wt

max

60.00

55.00

Cage

Extrusion
Die-Swell

%
wt

max

18.90

12.00

RRIM(HDS
1-2)

Pressed
Sheet Test
(before mastication)

no
nibs

MRPRA(1997)

Steel
drums internally coated with Atlaskote 302H

895mm high x 596mm diameter

Gross
weight of each drum

222 kgs

Net
weight of each drum

205 kgs

Colour

Red

Marking of Drums

MEGATEX 40

Production Lot No

Origin

Malaysia

PROPOLY 80 is a prevulcanised rubber of high quality standard. It is produced by blending 80 pbw of vulcanized and 20 pbw of unvulcanised natural rubber. Blending is carried out in the latex phase to achieve a homogeneous intimate mix. The blend is coagulated under controlled conditions, processed into crumb rubber and pressed into bales. To ensure precision and product quality uniformity, computer-aided processing techniques are employed.