C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25

C23F3/00—Brightening metals by chemical means

H—ELECTRICITY

H01—BASIC ELECTRIC ELEMENTS

H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR

H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof

H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof

H01L21/04—Manufacture or treatment of semiconductor devices or of parts thereof the devices having at least one potential-jump barrier or surface barrier, e.g. PN junction, depletion layer, carrier concentration layer

H01L21/18—Manufacture or treatment of semiconductor devices or of parts thereof the devices having at least one potential-jump barrier or surface barrier, e.g. PN junction, depletion layer, carrier concentration layer the devices having semiconductor bodies comprising elements of Group IV of the Periodic System or AIIIBV compounds with or without impurities, e.g. doping materials

H01L21/30—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26

H01L21/31—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26 to form insulating layers thereon, e.g. for masking or by using photolithographic techniques; After treatment of these layers

H01L21/3205—Deposition of non-insulating-, e.g. conductive- or resistive-, layers on insulating layers; After-treatment of these layers

H01L21/321—After treatment

H01L21/32115—Planarisation

H01L21/3212—Planarisation by chemical mechanical polishing [CMP]

H—ELECTRICITY

H01—BASIC ELECTRIC ELEMENTS

H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR

H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof

H01L21/70—Manufacture or treatment of devices consisting of a plurality of solid state components formed in or on a common substrate or of parts thereof; Manufacture of integrated circuit devices or of parts thereof

H01L21/71—Manufacture of specific parts of devices defined in group H01L21/70

H01L21/768—Applying interconnections to be used for carrying current between separate components within a device comprising conductors and dielectrics

H01L21/76838—Applying interconnections to be used for carrying current between separate components within a device comprising conductors and dielectrics characterised by the formation and the after-treatment of the conductors

H01L21/7684—Smoothing; Planarisation

Description

Translated from Japanese

【発明の詳細な説明】 【０００１】 【産業上の利用分野】本発明は研磨剤および研磨方法に関し、特に半導体デバイス製造工程等の微細加工工程等において使用される研磨剤および研磨方法に関する。 It relates DETAILED DESCRIPTION OF THE INVENTION [0001] The present invention relates to a polishing agent and a polishing method, particularly to a polishing agent and a polishing method used in microfabrication process such as a semiconductor device manufacturing process.【０００２】 【従来の技術】近年、ＬＳＩの高集積化、高性能化のため、様々な微細加工技術が研究、開発されている。 [0002] In recent years, high integration of LSI, for high performance, a variety of fine processing technology research, has been developed.化学機械的研磨方法（ケミカルメカニカルポリッシング、以下ＣＭＰと省略する）は、そのような厳しい微細化の要求を満たすために研究されている技術の一つであり、これからの半導体デバイス製造工程、特に、多層配線形成工程における層間絶縁膜の平坦化、金属プラグ形成、埋め込み配線形成において必須の技術である。 Chemical mechanical polishing method (chemical mechanical polishing, hereinafter abbreviated as CMP) is one technique that has been investigated to meet the requirements of such a severe miniaturization, future semiconductor device manufacturing process, in particular, planarization of the interlayer insulating film in a multilayer interconnect forming step, a metal plug formation is an essential technology in the embedded wiring formation.この方法は、例えば、CWKaantaらや、KDBeyer らによって提案されている(VMIC Conference 1991 p.144 CWKaanta This method is described, for example, CWKaanta Raya, proposed by KDBeyer et al (VMIC Conference 1991 p.144 CWKaantaet.al.,USPatentNo.4944836 Beyer et.al.) 。 et.al., USPatentNo.4944836 Beyer et.al.).【０００３】また、ＬＳＩの高速化の観点から、従来より上層配線に使用されているＡｌよりも低い抵抗を有するＣｕが新たな配線材料として検討されている。 [0003] From the viewpoint of speeding up of LSI, Cu having a lower resistivity than Al being conventionally used in the upper layer wiring is considered as a new wiring material.Ｃｕは反応性イオンエッチングによる加工が困難であるので、 Since Cu is difficult to process by reactive ion etching,Ｃｕを配線材料として用いる場合にＣＭＰ技術を利用した埋め込み配線形成方法を採用することが検討されている。 It has been studied to employ a buried wiring forming method utilizing the CMP technique in the case of using Cu as a wiring material.このような埋め込み配線形成方法は、例えば特開平２−２７８８２２号公報等により開示されている。 Such buried wiring forming method is disclosed, for example, by Japanese Patent Laid-Open 2-278822 Patent Publication.この公報においては、研磨粒子、遷移金属のキレート塩、およびこの塩の溶剤からなる研磨スラリーを用いてＣｕを研磨することが開示されている。 In this publication, abrasive particles, a transition metal chelate salts, and to polish the Cu by using a polishing slurry comprising a solvent of the salt are disclosed.【０００４】 【発明が解決しようとする課題】しかしながら、上記の埋め込み配線形成方法によりＣｕに傷を与えることなく高速で研磨しようとする場合には、研磨スラリー中におけるＣｕをエッチングする成分の量を多くしてＣｕのエッチングを強くする必要がある。 [0004] The present Invention is to Solve However, in the case to be polished at high speed without giving damage to Cu by the embedded wiring forming method, the amount of components of etching the Cu in the polishing slurry it is necessary to increase the etching of Cu and more.このようにＣｕをエッチングする成分の量を多くすると、エッチングが等方的に進行して埋め込んだＣｕまで溶解してしまい、配線にディッシングが発生する。 With this increase the amount of components of etching the Cu, will be dissolved to Cu embedded proceeds isotropically etching, dishing occurs in the wiring.このため、信頼性の高いＬＳ For this reason, reliable LSＩ配線を形成するのが困難である。 It is difficult to form the I line.【０００５】また、ＣＭＰ技術を利用したＷ配線形成においても、ディッシングが発生するので、信頼性の高いＬＳＩ配線を形成するのが困難である。 [0005] Also in W wiring formed using the CMP technique, since dishing occurs, it is difficult to form highly reliable LSI wiring.さらに、ＣＭＰ In addition, CMP技術を利用したＷ（タングステン）配線形成においても研磨速度が遅い。 Also slow polishing rate in W (tungsten) wiring formed using techniques.【０００６】本発明はかかる点に鑑みてなされたものであり、ディッシングの発生を抑制し、高い研磨速度で信頼性の高い導体膜を形成することができる研磨剤および研磨方法を提供することを目的とする。 [0006] The present invention has been made in view of the foregoing, that suppresses the occurrence of dishing, to provide a polishing agent and a polishing method capable of forming a high conductive film reliability at a high polishing rate for the purpose.【０００７】 【課題を解決するための手段】一般に、凹凸形状を有する基体に研磨処理を施すことにより、埋め込み金属配線、ビア、あるいはコンタクトを形成する場合、被研磨膜の凸部のみを研磨し、凹部のみに目的とする膜を残存させることが重要である。 [0007] Generally SUMMARY OF THE INVENTION By performing polishing treatment on a substrate having an irregular shape, a case of forming a buried metal wiring, vias or contacts, is polished only convex portions of the film to be polished it is important to leave a film of interest only in the recess.この研磨処理を機械的研磨のみにより行うと、凹部のみに目的とする膜を効率よく残存させることできる、すなわち高い選択比が得られるが、機械的研磨は研磨速度が遅く、半導体デバイス製造工程で必要とされるスループットを確保できない。 Doing only by mechanical polishing with the polishing process, can be made to remain efficiently a desired membrane only in the recess, that is, high selectivity ratio is obtained, the mechanical polishing is slow polishing rate, in the semiconductor device manufacturing process It can not be secured throughput required.一方、この研磨処理を化学的研磨のみにより行うと、研磨速度は速いが、エッチングが等方的に進むために、凹部のみに目的とする膜を残存させることができない。 On the other hand, when the only chemical polishing the polishing process, the polishing speed is high, because the etching proceeds isotropically, it is impossible to leave the film of interest only in the recess.そこで、本発明者らは、機械的研磨と化学的研磨とを組み合わせたＣＭＰを詳細に検討して、研磨剤のうち機械的研磨に寄与する成分と化学的研磨に寄与する成分を明確にした。 Accordingly, the inventors have examined the CMP that combines mechanical polishing and chemical polishing in detail and to clarify the components that contribute the component that contributes to chemical polishing in mechanical polishing of a polishing agent .そして本発明者らは、この考察に基づいて、目的とする膜の材料に特定の化学試薬を含有する研磨剤を用いてＣＭＰを行うことにより、目的とする膜上に保護層を形成して等方的な化学的研磨を抑制し、この保護層を被研磨膜の凸部表面において機械的研磨により容易に除去して、信頼性の高い導体膜を形成することができることを見出だして本発明をするに至った。 The present inventors, based on this consideration, by performing CMP using a polishing agent containing a specific chemical reagent material film of interest, to form a protective layer on the membrane of interest suppress isotropic chemical polishing, the protective layer is readily removed by mechanical polishing in the surface of the protrusion of the film to be polished, and we discovered that it is possible to form a highly conductive film reliability present It has led to the invention.【０００８】すなわち、本発明は、表面に凹部を有する基体上に前記凹部を充填するように金属を主成分とする材料からなる膜を形成する工程と、前記金属を主成分とする材料と反応することにより前記膜表面に保護膜を形成する化学試薬および前記金属を主成分とする材料のエッチング剤を含有する研磨剤を用いた化学機械的研磨方法により、前記膜を研磨して前記凹部内に導体膜を形成する工程とを具備することを特徴とする研磨方法を提供する。 Namely, the present invention includes the steps of forming a film made of a metal material mainly composed so as to fill the recess on a substrate having a concave portion on the surface, a material mainly composed of the metal reaction the film by chemical mechanical polishing method using a polishing agent containing etchant material mainly composed of chemical reagents and the metal forming the protective film on the surface, the recess by polishing the film by to provide a polishing method characterized by comprising the steps of forming a conductive film on.【０００９】ここで、基体としては、シリコン基板、Ｔ [0009] Here, as the substrate, the silicon substrate, TＦＴ−ＬＣＤ用のガラス基板、ＧａＡｓ等の化合物半導体からなる基板等を用いることができる。 Glass substrates for FT-LCD, or the like can be used made of a compound semiconductor such as GaAs.基体表面の凹部は、埋め込み金属配線の配線部、ビア、またはコンタクトホールとして用いられる。 Recess of the substrate surface, the wiring portion of the buried metal wiring is used as a via or contact hole.【００１０】金属を主成分とする材料としては、Ｃｕ、 [0010] as a material consisting mainly of metal, Cu,Ｃｕ合金、Ａｇ、Ａｇ合金、Ａｌ、Ａｌ合金、Ｗ、Ｗ合金、これらの酸化物、これらの金属に少量の不純物や添加元素が含まれているもの等を用いることができる。 Cu alloy, Ag, Ag alloy, Al, Al alloy, W, W alloy, these oxides, can be used like that contain small amounts of impurities and added elements to these metals.また、この材料と反応することにより保護膜を形成する化学試薬としては、ベンゾトリアゾール（以下、ＢＴＡと省略する）、ＢＴＡ誘導体、例えばＢＴＡのベンゼン環の一つの水素原子をメチル基で置換したもの（トリルトリアゾール（ＴＴＡ））等や、これらを含む混合物、チオ尿素、アゾール、中でも特にベンズイミダゾール、トリアゾール、サリチルアルドキシム、クペロン、エチレンジアミン、イオウを含むアミノ酸、特にシスティン、 As the chemical reagents to form a protective film by reacting with the material, benzotriazole (hereinafter abbreviated as BTA), which BTA derivatives, for example, one of the hydrogen atoms of the benzene ring of BTA was substituted with a methyl group (tolyltriazole (TTA)), etc. and mixtures containing these, thioureas, azole, among others benzimidazole, triazole, salicylaldoxime, cupferron, ethylenediamine, amino acids containing sulfur, in particular cysteine,ｐ−アミノベンズアルデヒド、ハロ酢酸、チオール類、 p- aminobenzaldehyde, haloacetic acid, thiols,例えばドデシルメルカプタン、オクタンホスホン酸等のホスホン酸類、グルコースやフルクトース等の単糖類、 For example dodecyl mercaptan, phosphonic acids such as octanoic acid, glucose and monosaccharides fructose,およびこれらの物質の誘導体またはそれらの混合物、Ｎ And derivatives or mixtures thereof of these materials, N−ベンゾイル−Ｎ−フェニルヒドロキシルアミン（以下、ＢＰＡと省略する）、ＢＰＡ誘導体等を用いることができる。 - Benzoyl -N- phenylhydroxylamine (hereinafter abbreviated as BPA), can be used BPA derivatives.また、化学試薬には、疎水部分を有する（疎水性）有機化合物が好ましい。 In addition, the chemical reagent comprises a hydrophobic portion (hydrophobic) organic compounds are preferred.ＢＴＡ、ＢＴＡ誘導体、 BTA, BTA derivatives,例えばＢＰＡのベンゼン環の一つの水素原子をメチル基で置換したもの等や、これらを含む混合物は、金属を主成分とする材料がＣｕまたはＣｕ合金である場合に特に効果を発揮する。 For example BPA, etc. and those of one hydrogen atom of the benzene ring substituted with a methyl group, the mixture containing these are particularly effective when material mainly composed of metal is Cu or Cu alloy.また、ＢＰＡ、ＢＰＡ誘導体、これらの混合物は、金属を主成分とする材料がＷまたはＷ合金である場合に特に効果を発揮する。 Further, BPA, BPA derivatives and mixtures thereof, particularly effective when material mainly composed of metal is W or a W alloy.【００１１】金属を主成分とする材料のエッチング剤は、その材料により適宜選択することができる。 [0011] etchant material mainly containing metal, it can be appropriately selected according to the material.例えば、グリシン等のアミノ酢酸、アミド硫酸、もしくはこれらの混合酸と、過酸化水素（Ｈ 2 Ｏ 2 ）、硝酸、次亜塩素酸、オゾン水等の酸化剤とを含有するエッチング剤を用いる。 For example, amino acid such as glycine, and an amide acid or mixed acid thereof, hydrogen peroxide (H 2 O 2), nitric acid, hypochlorous acid, an etching agent containing an oxidizing agent such as ozone water is used.また、硝酸、アンモニア、アンモニウム塩類、例えば過硫酸アンモニウム、硝酸アンモニウム、塩化アンモニウム等、クロム酸等の水溶液を用いることもできる。 Further, it nitrate, ammonia, ammonium salts such as ammonium persulfate, ammonium nitrate, ammonium chloride, also possible to use an aqueous solution such as chromic acid.これらのエッチング剤は、金属を主成分とする材料がＣｕまたはＣｕ合金である場合に用いることが特に好ましい。 These etchants, it is particularly preferable to use when a material mainly composed of metal is Cu or Cu alloy.【００１２】また、金属を主成分とする材料がＷまたはＷ合金である場合には、エッチング剤としては、過酸化水素水溶液、硝酸鉄水溶液、フェリシアン化カリウムとエチレンジアミンとの混合水溶液、フェリシアン化カリウムとリン酸との混合水溶液等を用いることができる。 Further, when material mainly composed of metal is W or a W alloy, as an etching agent, aqueous hydrogen peroxide, aqueous mixture of potassium ferricyanide and phosphate with aqueous solution of iron nitrate, potassium ferricyanide and ethylenediamine it can be used a mixed aqueous solution or the like with an acid.【００１３】金属を主成分とする材料と化学試薬とが反応して形成される保護膜は、金属のキレート化合物または錯体化合物を包含することが好ましい。 [0013] protective films and materials and chemical reagents mainly composed of metal is formed by the reaction, it is preferable to include a chelating compound or complex compound of a metal.本発明においては、ＣＭＰは上記化学試薬およびエッチング剤を含有する研磨剤を用いて行ってもよいし、また、第１段階として上記エッチング剤を含有し、上記化学試薬を含有しない研磨剤を用いて行い、その後第２段階として上記化学試薬を添加した前記研磨剤を用いて行ってもよい。 In the present invention, CMP is may be performed using a polishing agent containing the chemical reagents and etchants, and as a first stage containing the etching agent, with a polishing agent which does not contain the chemical reagents performed, it may be performed using then the polishing agent added to the chemical reagent in the second stage.後者の場合、ＣＭＰにおいて化学試薬を研磨剤に添加する方法としては、研磨剤供給用のノズルを複数設けておき、第１段階において使用する研磨剤用のノズルと、第２段階において使用する研磨剤用のノズルを区別して用いる方法や、研磨剤用のノズルとは別のノズルあるいは研磨定盤に設けた供給口から化学試薬を含む水溶液を供給して研磨定盤上で研磨剤と混合する方法が挙げられる。 In the latter case, as a method of adding a polishing agent of chemical reagents in CMP, a nozzle for abrasive feed advance plurality, and a nozzle for the abrasive used in the first stage, used in the second stage polishing and methods used to distinguish a nozzle for agent, mixed with the abrasive at the nozzle and the polishing surface plate by supplying an aqueous solution containing a chemical reagent from a supply port formed in a separate nozzle or polishing surface plate of polishing compound the method and the like.【００１４】また、本発明においては、研磨剤のうち化学的研磨に寄与する成分が多いので、研磨剤と被研磨膜とが接触する部分を加熱することにより、さらに高い研磨速度を得ることができる。 [0014] In the present invention, since the component that contributes to the chemical polishing of a polishing agent is more, by heating the portion where the polishing agent and the film to be polished in contact, to obtain a higher removal rate it can.【００１５】また、本発明は、上記研磨方法を達成するために、金属を主成分とする材料と反応することにより、前記材料からなる膜表面に保護膜を形成する化学試薬と、前記材料のエッチング剤とを含有することを特徴とする研磨剤を提供する。 [0015] Further, in order to achieve the above polishing method, by reacting with a material consisting mainly of metal, and chemical reagents to form a protective film on the film surface made of said material, said material to provide a polishing agent characterized by containing an etching agent.ここで、研磨剤としては、アミノ酢酸および／またはアミド硫酸、酸化剤、水およびベンゾトリアゾールあるいはその誘導体を含有する研磨剤が好ましい。 Here, as the polishing agent, amino acid and / or amide acid polishing agent containing an oxidizing agent, water and benzotriazole or a derivative thereof.【００１６】 【作用】本発明は、表面に凹部を有する基体上に前記凹部を充填するように金属を主成分とする材料からなる膜を形成し、前記金属を主成分とする材料と反応することにより前記膜表面に保護膜を形成する化学試薬および前記金属を主成分とする材料のエッチング剤を含有する研磨剤を用いた化学機械的研磨方法により、前記膜を研磨して前記凹部内に導体膜を形成することを特徴としている。 [0016] DETAILED DESCRIPTION OF THE INVENTION The present invention, by forming a film made of a metal material mainly composed so as to fill the recess on a substrate having a concave portion on the surface, reacts with the material mainly containing the metal by chemical mechanical polishing method using a polishing agent containing etchant material mainly composed of chemical reagents and the metal forming the protective layer on the film surface by, in the recess by polishing the film It is characterized by forming a conductor film.【００１７】以下、金属を主成分とする材料がＣｕ系材料であり、化学試薬がＢＴＡである例を用いて本発明の作用を詳細に説明する。 [0017] Hereinafter, materials mainly composed of metal is Cu-based material, chemical reagents the effect of the present invention will be described in detail with reference to examples is BTA.Ｃｕ膜にＢＴＡを接触させた場合、Ｃｕ膜表面のＣｕまたはＣｕ膜上に形成された自然酸化膜のＣｕＯもしくはＣｕ 2 ＯとＢＴＡとが反応してＣｕ（Ｉ）−ＢＴＡあるいはＣｕ（II）−ＢＴＡで表されるＣｕキレート化合物からなる膜がＣｕ膜または自然酸化膜上に強固に形成される。 When contacting the BTA to the Cu film, and the reaction with CuO or Cu 2 O and BTA natural oxide film formed on the Cu or Cu film of the Cu film surface Cu (I)-BTA or Cu (II) film made of Cu chelate compounds represented by -BTA is firmly formed on the Cu film or a natural oxide film.この膜は、Ｃｕを腐食させるような雰囲気中もしくは溶液中、すなわちＣｕを高速でエッチングできる化学腐食域を有するエッチング剤の存在下において酸化または腐食を抑制する保護膜として作用する。 The membrane or in solution in an atmosphere such as corrode the Cu, i.e. acts as a suppressing protective film oxidation or corrosion in the presence of an etching agent having a chemical corrosion area which can etch the Cu at a high speed.また、この保護膜は、ＣＭＰの際に研磨粒子もしくは研磨パッドと物理的・機械的に接触することにより容易にしかも均一に除去される。 Further, the protective film is easily and uniformly removed by polishing to particles or polishing pad physically and mechanical contact during CMP.このような保護膜がＣｕの酸化または腐食を抑制することは従来より知られていたが、ＣＭＰの際に研磨粒子もしくは研磨パッドと物理的・機械的に接触することにより容易にしかも均一に除去されることは本発明者らの研究により初めて明らかになった。 It had been known that such a protective film can be inhibited oxidation or corrosion of Cu, easily and uniformly removed by polishing to particles or polishing pad physically and mechanical contact during CMP as it has been revealed for the first time by the study of the inventors of the present invention that is.【００１８】この保護膜は、図２（Ａ）におけるＣｕ膜２５上全面に形成される。 [0018] The protective film is formed on the Cu film 25 on the entire surface in FIG. 2 (A).凸部に形成された保護膜は研磨粒子もしくは研磨パッドとの接触により容易に除去される。 Protective film formed on the convex portions is easily removed by contact with the abrasive particles or polishing pad.これにより露出したＣｕ膜２５の凸部はエッチング剤により高速にエッチングされる。 This protrusion of the Cu film 25 exposed by is etched faster etching agent.このとき、Ｃｕ膜２５の凹部に充填されているＣｕ膜２５は表面に保護膜が形成されているので、ほとんどエッチングされない。 In this case, the Cu film 25 filled in the recess of the Cu film 25 since the protective film on the surface is formed, it is hardly etched.このようにして基体の凹凸形状に追従していたＣｕ膜２ Cu film 2 was thus not follow the uneven shape of the substrate５の段差が小さくなる。 5 of the step is reduced.その後、Ｃｕ膜２５の凹部上に形成された保護膜は、研磨粒子もしくは研磨パッドと接触することにより除去される。 Thereafter, the protective film formed on recessed portions of the Cu film 25 is removed by contact with abrasive particles or polishing pad.この段階においては、Ｃ In this stage, Cｕ膜２５には段差がほとんどない状態であるので、凹部に充填されているＣｕ膜２５が露出してエッチングが進んでもディッシングは起こらない。 Since the u film 25 is in a state stepped little, it does not occur dishing also progressed etched to expose the Cu film 25 is filled in the recess.その結果、高速でＣ As a result, C at high speedｕを研磨して凹部のみに効率よくＣｕを残存させることができる。 It can be left efficiently Cu only in the recess by polishing the u.【００１９】なお、上記保護膜を除去する方法としては、研磨粒子もしくは研磨パッドと接触させる方法の他に、金属製あるいは樹脂製のブラシを接触させる方法、 [0019] Note that the method as a method of removing the protective film, in addition to the method of contacting the abrasive particles or polishing pad, contacting a metal or resin brush,研磨剤を所定の圧力で吹き付ける方法が挙げられる。 A method of spraying an abrasive at a predetermined pressure, and the like.【００２０】一方、金属を主成分とする材料がＷ系材料であり、化学試薬がＢＰＡである場合にも上記と同様に説明することができる。 Meanwhile, material mainly composed of metal is W-based material, chemical reagents can be described in the same manner as described above even if it is BPA.すなわち、Ｗ膜にＢＰＡを接触させた場合、ＷやＷＯｘとＢＰＡとが反応してＷ−ＢＰ That is, when contacted with BPA to W film, W and WOx and BPA and react with each W-BPＡで表されるＷキレート化合物からなる膜がＷ膜上に強固に形成される。 Film made of W chelate compounds represented by A is firmly formed on the W film.この膜は、Ｗを腐食させるような雰囲気中もしくは溶液中、すなわちＷを高速でエッチングできる化学腐食域を有するエッチング剤の存在下において酸化または腐食を抑制する保護膜として作用する。 The membrane or in solution in an atmosphere such as corrode the W, i.e. W and acts as a suppressing protective film oxidation or corrosion in the presence of an etching agent having a chemical corrosion region can be etched at a high speed.また、この保護膜は、ＣＭＰの際に研磨粒子もしくは研磨パッドと物理的・機械的に接触することにより容易にしかも均一に除去される。 Further, the protective film is easily and uniformly removed by polishing to particles or polishing pad physically and mechanical contact during CMP.【００２１】 【実施例】以下、本発明を図面を参照して具体的に説明する。 [0021] EXAMPLES Hereinafter, the present invention will be specifically described with reference to the drawings.（実施例１）図１は本発明の実施例において使用する研磨装置を示す概略図である。 (Example 1) FIG. 1 is a schematic view showing a polishing apparatus used in the embodiment of the present invention.図中１１は回転可能な真空チャックホルダを示す。 Figure 11 shows a vacuum chuck holder rotatable.真空チャックホルダ１１には、 The vacuum chuck holder 11,被研磨基板１２がその被研磨面を研磨パッド１３と対向するようにして真空チャックされている。 Substrate to be polished 12 is a vacuum chuck with its polished surface to be opposed to the polishing pad 13.研磨パッド１ Polishing pad 1３は、真空チャックホルダ１１の下方に配置された回転可能な研磨定盤１４上に取り付けられている。 3 is mounted on a rotatable polishing platen 14 disposed below the vacuum chuck holder 11.また、図示しない研磨剤タンクに接続された研磨剤供給配管１５ The polishing agent supply pipe 15 connected to the abrasive tank (not shown)の吐出部が研磨パッド１３近傍まで延出されている。 Discharge portion of is extended to the vicinity polishing pad 13.この研磨剤供給配管１５は、研磨剤１６の供給量を制御する手段を備えている。 The slurry supply pipe 15 is provided with means for controlling the supply amount of the polishing agent 16.なお、研磨パッド１３には、樹脂含浸不織布からなるものを用いた。 Note that the polishing pad 13 was used one made of resin-impregnated nonwoven fabric.【００２２】図２（Ａ）は、本実施例で使用する被研磨基板１２を示す断面図である。 FIG. 2 (A) is a sectional view showing a polished substrate 12 used in this embodiment.この被研磨基板１２は次のようにして作製する。 The substrate to be polished 12 is prepared as follows.まず、シリコン基板２１上に厚さ１μｍ程度のシリコン酸化膜２２を形成し、その上に直流マグネトロンスパッタリング法により厚さ約１０ｎ First, a silicon oxide film 22 having a thickness of about 1μm on the silicon substrate 21, a thickness of about 10n by a DC magnetron sputtering on theｍの炭素膜２３を形成する。 Forming a carbon film 23 m.次いで、通常のフォトリソグラフィー工程および反応性イオンエッチング工程により、炭素膜２３およびシリコン酸化膜２２をパターニングして、シリコン酸化膜２２に幅０．４〜１０μｍ、深さ０．４μｍの配線用溝および接続配線用開孔等を形成する。 Then, by a conventional photolithography and reactive ion etching step, by patterning the carbon film 23 and the silicon oxide film 22, the width in the silicon oxide film 22 0.4～10Myuemu, wiring trench depth 0.4μm and forming an aperture such as connection wire.次いで、直流マグネトロンスパッタリング法により厚さ５０ｎｍの窒化チタン膜２４を形成し、引き続き直流マグネトロンスパッタリング法により厚さ約６００ Then, a titanium nitride film 24 having a thickness of 50nm by a DC magnetron sputtering method, about subsequently thickness by DC magnetron sputtering method 600ｎｍのＣｕ膜２５を形成する。 Forming a nm of the Cu film 25.図２（Ａ）に示すように、ＣＭＰ直前のＣｕ膜２５は基体であるシリコン酸化膜２２に設けられた段差に追従しており凹凸形状を有する。 As shown in FIG. 2 (A), CMP just before the Cu film 25 has an uneven shape which follows the step provided on the silicon oxide film 22 is the base.【００２３】このようにして作製した被研磨基板１２を図１に示す研磨装置を用いてＣＭＰを行い、配線用溝および接続配線用開孔以外の余剰なＣｕ膜２５を除去してＣｕの埋め込み配線およびＣｕプラグを形成した。 [0023] The thus polished substrate 12 fabricated by CMP is performed by using the polishing apparatus shown in FIG. 1, the embedding of Cu by removing the wiring grooves and the connection of the other wiring openings excess Cu film 25 to form a wiring and Cu plug.ＣＭ CMＰに使用した研磨剤は、０．１２モル／リットルのグリシン（Ｃ 2 Ｈ 5 Ｏ 2 Ｎ）水溶液と０．４４モル／リットルの過酸化水素水（Ｈ 2 Ｏ 2 ）との混合溶液（Ｃｕのエッチング剤）に、研磨粒子としてシリカ粒子（平均粒径３０ｎｍ）を５．３重量％で分散させ、さらに０．００ Abrasives used for P is 0.12 moles / liter of glycine (C 2 H 5 O 2 N ) aqueous solution and 0.44 mol / l of hydrogen peroxide (H 2 O 2) mixed with a solution (Cu of the etchant), silica particles (average particle diameter 30 nm) 5.3 was dispersed in weight% as the abrasive particles, further 0.00１モル／リットルのベンゾトリアゾール（Ｃ 6 Ｈ 5 Ｎ Benzotriazole 1 mole / liter (C 6 H 5 N3 ）（化学試薬）を添加してなるものである。3) (those obtained by adding a chemical reagent).また、研磨条件は、研磨圧力３００ｇｆ／ｃｍ 2 、研磨定盤１４ The polishing conditions, the polishing pressure 300 gf / cm 2, the polishing platen 14および真空チャックホルダ１１の回転数１００ｒｐｍとし、研磨定盤の温度を室温２５℃で一定になるようにした。 And a rotation speed 100rpm vacuum chuck holder 11, the temperature of the polishing platen was set to a constant at room temperature 25 ° C..【００２４】ＣＭＰの結果、研磨速度は約１２０ｎｍ／ [0024] As a result of the CMP, the polishing rate is about 120nm /分であり、非常に高速であった。 A minute, was very fast.また、Ｃｕ埋め込み配線およびＣｕプラグを形成するために、Ｃｕ膜２５と共にＣｕ膜２５の凸部の上に設けられている窒化チタン膜２４も除去しなければならない。 Further, in order to form a Cu buried wiring and Cu plugs, titanium nitride film 24 is provided on the protruding portions of the Cu film 25 with the Cu film 25 must also be removed.窒化チタン膜２４の研磨速度はＣｕ膜２５の研磨速度より遅く約３０ｎｍ／分であるが、本発明の作用として前述したように、Ｃｕ膜２５の研磨が窒化チタン膜２４の研磨よりも僅かに進んだ時点で窒化チタン膜２４部分と比較してＣｕ膜２５の部分は凹部となるので、Ｃｕ膜２５の表面上に保護膜が形成されてＣｕ膜の研磨がそれ以上進まない。 Although the polishing rate of the titanium nitride film 24 is about 30 nm / min slower than the polishing rate of the Cu film 25, as described above as a function of the present invention, the polishing of the Cu film 25 is slightly above the polishing of the titanium nitride film 24 since the portion recess of the Cu film 25 as compared with the titanium film 24 partially nitrided when advanced, is a protective film is formed on the surface of the Cu film 25 does not proceed polishing of the Cu film is higher.このため、窒化チタン膜２４も良好に除去することができた。 Therefore, it was possible to titanium nitride film 24 is also excellently removed.また、ＣＭＰ後のＣｕ埋め込み配線およびＣｕプラグの表面を走査型電子顕微鏡で観察したところ、図２（Ｂ） Further, observation of the Cu buried wiring and Cu surface of the plug after CMP with a scanning electron microscope, and FIG. 2 (B)に示すように、ＣＭＰにより発生したと思われる傷等は全く見られなかった。 As shown in, it was not observed at all scratches that may have occurred by CMP.【００２５】なお、ＣＭＰにおいてＣｕ表面は水と接触するので、Ｃｕ膜２５の表面にはＣｕ、ＣｕＯ、Ｃｕ 2 [0025] Since Cu surface is in contact with water in CMP, the surface of the Cu film 25 Cu, CuO, Cu 2Ｏ、Ｃｕ（ＯＨ）ｘ等が混在すると考えられるが、ＢＴ O, it is considered that Cu (OH) x and the like are mixed, BTＡはいずれの物質ともキレート化合物を形成して保護膜を設ける。 A is a protective film to form a chelate compound with any material.【００２６】次に、ＢＴＡを添加した研磨剤を用いて、 [0026] Next, by using a polishing agent was added to the BTA,Ｃｕに対する研磨速度の温度依存性を調べた。 We investigated the temperature dependence of the polishing rate for Cu.このとき、研磨圧力は４００ｇｆ／ｃｍ 2とし、研磨定盤および真空チャックホルダの回転数は共に６０ｒｐｍとした。 At this time, the polishing pressure was 400 gf / cm 2, the rotational speed of the polishing platen and the vacuum chuck holder were both 60 rpm.研磨速度の対数を縦軸、温度の逆数（１／Ｔ）を横軸にしてプロットした結果を図３に示す。 Ordinate the logarithm of the polishing rate, the results of plotting with the horizontal axis the reciprocal of temperature (1 / T) is shown in FIG.図３から明らかなように、温度約０℃から約１００℃までにおいて、 As apparent from FIG. 3, at a temperature of about 0 ℃ to about 100 ° C.,研磨速度の対する温度の逆数（１／Ｔ）とは、ほぼ一直線上にプロットされ、その傾きは負となる。 The inverse of the temperature against the polishing rate (1 / T), is plotted on almost a straight line, the slope is negative.指数に比例している。 It is proportional to the index.したがって、研磨速度は主としてＣＭＰ中に起こる何らかの化学反応によって律速されており、物理的・機械的な要素にはほとんど影響されないと考えられる。 Therefore, the polishing rate is considered primarily are limited by some chemical reactions that occur during CMP, not in physical and mechanical elements are affected most.このことは、Ｃｕ膜２５表面に形成される保護膜が、ＣＭＰにおいて研磨粒子もしくは研磨パッドによる物理的・機械的作用により容易に除去されることを意味する。 This protective film formed on the Cu film 25 surface, meaning that they are easily removed by physical and mechanical action of abrasive particles or polishing pad in CMP.【００２７】また、ＢＴＡの添加量に対する研磨速度およびエッチング速度の変化について調べた。 Further, it was examined for changes in the polishing rate and etching rate of the addition amount of BTA.その結果を図４に示す。 The results are shown in FIG.図４のグラフにおいて横軸はグリシン０． The horizontal axis glycine 0 in the graph of FIG.１２モル／リットルに対するＢＴＡの添加量を表し、縦軸は研磨速度およびエッチング速度を表す。 It represents the amount of BTA for 12 mol / liter, and the ordinate represents the polishing rate and etching rate.図４から明らかなように、ＢＴＡを添加しない場合には、研磨速度は約３５０ｎｍ／分、エッチング速度は約４５ｎｍ／分と高いが、ＢＴＡを添加していくと研磨速度およびエッチング速度は共に指数関数的に減少する。 As apparent from FIG. 4, when not adding the BTA, the polishing rate is about 350 nm / min, the etching rate is high about 45 nm / min, the polishing rate and the etching rate are both index and continue the addition of BTA reduced function manner.ただし、研磨速度はＢＴＡ０．１モル／リットルでほぼ飽和していると考えられる。 However, the polishing rate is considered to be nearly saturated with BTA0.1 mol / liter.また、Ｃｕ膜２５を保護するために必要なＢＴＡの量は、０．００１モル／リットル以下のごくわずかな量でよいことが分かった。 The amount of BTA necessary to protect the Cu film 25 was found to be a very small amount of less 0.001 mole / liter.【００２８】次に、ＢＴＡを０．００１モル／リットル添加した研磨剤を用いて研磨速度の圧力（荷重）依存性について調べた。 Next, we examined the pressure (load) dependence of the polishing rate using the polishing agent added 0.001 mol / l of BTA.このとき、研磨定盤の温度は２５℃で一定になるようにし、研磨定盤および真空チャックホルダの回転数は共に６０ｒｐｍとした。 At this time, the temperature of the polishing surface plate is set to be constant at 25 ° C., the rotational speed of the polishing platen and the vacuum chuck holder were both 60 rpm.その結果を図５に示す。 The results are shown in FIG.図５から明らかなように、研磨速度は研磨圧力に対して比例関係にあり、その直線は図５のグラフの原点を通っていると思われる。 As apparent from FIG. 5, the polishing rate is proportional to the polishing pressure, appear to the straight line is through the origin of the graph in FIG.すなわち、通常のＣＭＰにおいて適用される研磨圧力の範囲では、研磨速度は研磨圧力に律速されている、言い換えるとＣｕ膜２５表面の保護膜が研磨粒子もしくは研磨パッドにより物理的・機械的作用で除去される速度に律速されていると考えられる。 That is, in the range of polishing pressure applied in the ordinary CMP, a removal by physical-mechanical action of the polishing rate is limited by the polishing pressure, the protective film of the other words Cu film 25 surface by polishing particles or polishing pad It believed to be limited by the rate at which.したがって、研磨圧力を高くすることにより、研磨速度を図３に示す各温度での研磨速度の値まで上げることが可能である。 Therefore, by increasing the polishing pressure, it is possible to increase up to the value of the polishing rate at each temperature showing the polishing rate in FIG.【００２９】次に、ディッシング量の配線幅依存性について調べた。 [0029] Next, was examined dishing amount of the wiring width dependence.その結果を図６に示す。 The results are shown in FIG.ここでは、凸部のＣｕ膜２５および窒化チタン膜２４をすべて除去した時を研磨終了時とした。 Here, upon removal of all of the Cu film 25 and the titanium nitride film 24 of the convex portion was at the end of polishing.図６から明らかなように、Ｃｕ埋め込み配線のディッシング値は、配線幅が１０μｍの配線中央部で約１５０ｎｍであり、実用上ほぼ問題のない程度であった。 As apparent from FIG. 6, dishing value of Cu buried wiring, the wiring width of about 150nm wiring central portion of the 10 [mu] m, was much no practical problems in almost.また、研磨時間をさらに延長しても、ディッシング値はほとんど増加しなかったことを考慮すると、Ｃｕ膜２５上に形成された保護膜が効果的に機能していることが分かる。 Further, even if the polishing time further extended, considering that the dishing value was hardly increased, it can be seen that the protective film formed on the Cu film 25 is working effectively.【００３０】本実施例においては、被研磨膜としてＣｕ [0030] In this example, Cu as the film to be polished膜を用いた場合について説明しているが、Ｃｕに少量の不純物や添加元素が含有されている場合や、被研磨膜としてＣｕ以外の金属、例えばＡｇ、Ａｌ、Ｗ等の膜やこれらを主成分とした膜を用いた場合においても同様の効果が得られる。 Have described the case of using the film, and if a small amount of impurities and the additional element is contained in the Cu, the metal other than Cu as a film to be polished, for example Ag, Al, such as W film or these main the same effect can be obtained even in the case of using the film as a component.【００３１】また、本実施例においては、研磨粒子としてシリカ粒子のみを用いた場合について説明しているが、研磨粒子としてシリカ粒子と同等あるいはそれ以上の硬度を有するアルミナ粒子、酸化チタン粒子、酸化ジルコニウム粒子、酸化セリウム粒子、炭化珪素粒子、ダイヤモンド粒子等を用いた場合においても同様の効果が得られる。 Further, in the present embodiment has been described for the case of using only silica particles as abrasive particles, equivalent to the silica particles as abrasive particles or more of the alumina particles having a hardness, titanium oxide particles, oxide zirconium particles, cerium oxide particles, silicon carbide particles, the same effect can be obtained even when using diamond particles.【００３２】また、本実施例においては、エッチング剤としてグリシン水溶液および過酸化水素水の混合溶液を用い、化学試薬としてＢＴＡを用いた場合について説明しているが、エッチング剤としてアミド硫酸もしくはアミノ酢酸とアミド硫酸の混合酸と、過酸化水素（Ｈ 2 Ｏ [0032] In the present embodiment, using a mixed solution of glycine solution and hydrogen peroxide solution as an etchant, it has described the case of using the BTA as a chemical reagent, amido sulfuric acid or amino acid as an etchant amide mixed acid of sulfuric acid and hydrogen peroxide (H 2 O2 ）、硝酸、次亜塩素酸、オゾン水等の酸化剤とからなるもの、硝酸アンモニウム、塩化アンモニウム、クロム酸等を用いた場合においても同様の効果が得られる。2), nitric acid, hypochlorous acid, which consists of an oxidizing agent such as ozone water, ammonium nitrate, ammonium chloride, the same effect can be obtained even in the case of using a chromic acid or the like.また、化学試薬としては、エッチングする膜材料に応じてこの材料とキレート化合物や錯体化合物を形成する試薬、例えばＢＴＡの各種誘導体、これらを含む混合物、 As the chemical reagent, the reagent for forming the material and chelate compound or complex compounds according to the film material to be etched, for example, various derivatives of BTA, the mixture containing them,チオ尿素、チオ尿素誘導体、クペロン、ベンズイミダゾール、トリアゾール、サリチルアルドキシム、エチレンジアミン、システィン、ｐ−アミノベンズアルデヒド、 Thiourea, thiourea derivatives, cupferron, benzimidazole, triazole, salicylaldoxime, ethylenediamine, cysteine, p- aminobenzaldehyde,ハロ酢酸、ドデシルメルカプタン、ホスホン酸類、グルコースやフルクトース等の単糖類等を用いた場合においても同様の効果が得られる。 Haloacetic acid, dodecyl mercaptan, phosphonic acids, the same effect can be obtained in the case of using a monosaccharide such as glucose or fructose.特に、ＢＴＡまたはＢＴＡ In particular, BTA or BTAの各種誘導体は、硫酸水溶液や塩酸水溶液等を用いる場合に有効である。 Various derivatives of is effective when using a sulfuric acid solution or aqueous hydrochloric acid, and the like.【００３３】また、本実施例においては、研磨パッドには樹脂含浸不織布からなる研磨パッドを用いたが、同程度の硬度を有するものであれば良く、例えば、ポリエステル、ポリエーテル等の不織布、発砲ポリウレタンパッド、またはそれら２種類以上の異なるパッドを張り合わせた研磨パッド等を用いてもよい。 Further, in this embodiment, the polishing pad using a polishing pad made of resin-impregnated nonwoven fabric, as long as it has a hardness comparable, for example, polyester, non-woven such as polyether, fire polyurethane pad or with a polishing pad or the like bonding them two or more different pads.なお、上記した各種物質の誘導体としては、水素部分がアルキル基等に置き変わったものが特に好ましい。 As the derivatives of various substances mentioned above, which a hydrogen partial is changed placed in the alkyl group and the like are particularly preferred.（比較例１）研磨剤として、０．１２モル／リットルのグリシン水溶液と０．４４モル／リットルの過酸化水素水との混合溶液（Ｃｕのエッチング剤）に、研磨粒子としてシリカ粒子（平均粒径３０ｎｍ）を５．３重量％で分散させたもの、すなわち実施例で使用した研磨剤においてＢＴＡを添加していないものを用いること以外は実施例と同様にして図２（Ａ）に示す被研磨基板１２にＣ (Comparative Example 1) abrasive, a mixed solution (Cu etching agent) and 0.12 moles / liter of aqueous glycine solution and 0.44 mol / l of hydrogen peroxide, silica particles (average particle as abrasive particles are dispersed in the diameter 30 nm) 5.3 wt%, i.e. the shown but using those without added BTA in the polishing agent used in the same manner as example FIG 2 (a) in example C to the polishing substrate 12ＭＰを行った。 Was MP.【００３４】ＣＭＰの結果、研磨速度は約２５０ｎｍ／ [0034] As a result of the CMP, the polishing rate is about 250nm /分であり高速であるが、ディッシング値が実施例の場合に比べて非常に大きかった。 A minute is fast, dishing value was very large as compared with the case of Example.すなわち、最小線幅の０． In other words, the 0 of the minimum line width.４μｍ配線幅においてはディッシング量が約３００ｎｍ Dishing amount of about 300nm in 4μm wire widthであり、５μｍ以上の配線幅においては配線用溝内のＣ In and, C of the wiring groove in the above line width 5μmｕはほとんど消失していた。 u had almost disappeared.また、研磨時間をさらに延長すると、配線用溝および接続配線用開孔内のすべてのＣｕが消失した。 Moreover, when further extending the polishing time, all of the Cu of the wiring grooves and open hole connection wire is lost.（実施例２）図７（Ａ）は、本実施例で使用する被研磨基板１２を示す断面図である。 (Embodiment 2) FIG. 7 (A) is a sectional view showing a polished substrate 12 used in this embodiment.この被研磨基板１２は次のようにして作製する。 The substrate to be polished 12 is prepared as follows.まず、シリコン基板２１上に厚さ１μｍ程度のシリコン酸化膜２２を形成。 First, a silicon oxide film 22 having a thickness of about 1μm on the silicon substrate 21.次いで、通常のフォトリソグラフィー工程および反応性イオンエッチング工程により、シリコン酸化膜２２をパターニングして、シリコン酸化膜２２に幅０．４〜１０μｍ、深さ０．４μｍの配線用溝および接続配線用開孔等を形成する。 Then, by a conventional photolithography and reactive ion etching step, by patterning the silicon oxide film 22, the width in the silicon oxide film 22 0.4～10Myuemu, open wiring grooves and the connection wiring of depth 0.4μm forming a hole or the like.次いで、その上に、直流マグネトロンスパッタリング法により厚さ約２０ｎｍのチタン膜３１および厚さ約７０ｎｍの窒化チタン膜２４を形成し、引き続き六フッ化タングステン（ＷＦ 6 ）ガスおよび水素ガスの混合ガスを用いた熱ＣＶＤ法により、厚さ約６００ｎｍのブランケットＷ膜３２を形成する。 Then, thereon, a mixed gas of a DC magnetron sputtering method by forming a titanium nitride film 24 of a titanium film 31 and a thickness of about 70nm with a thickness of about 20 nm, subsequently tungsten hexafluoride (WF 6) gas and hydrogen gas by a thermal CVD method using, to form a blanket W film 32 with a thickness of about 600 nm.図７（Ａ）に示すように、ＣＭＰ直前のＷ膜３２は基体であるシリコン酸化膜２２に設けられた段差に追従しており凹凸形状を有する。 As shown in FIG. 7 (A), W film 32 of the CMP just before has a concave-convex shape is to follow the steps provided in the silicon oxide film 22 is the base.【００３５】このようにして作製した被研磨基板１２を図１に示す研磨装置を用いてＣＭＰを行い、配線用溝および接続配線用開孔以外の余剰なＷ膜３２を除去してＷ [0035] Thus the substrate to be polished 12 manufactured by CMP is performed by using the polishing apparatus shown in FIG. 1, the excess W film 32 other than the wiring grooves and the connection wiring opening by removing Wの埋め込み配線およびＷプラグを形成した。 It was the formation of embedded wiring and the W plug.ＣＭＰに使用した研磨剤は、５体積％の過酸化水素水溶液に、研磨粒子としてアルミナ粒子（平均粒径５０ｎｍ）を１．０ Polishing agent used in CMP is a 5 vol% aqueous hydrogen peroxide solution, the alumina particles as abrasive particles (average particle diameter 50 nm) 1.0重量％で分散させ、さらに０．４ｇ／リットルのＮ−ベンゾイル−Ｎ−フェニルヒドロキシルアミン（化学試薬）を添加してなるものである。 Was dispersed in weight%, it is made by adding further 0.4 g / l of N- benzoyl -N- phenylhydroxylamine (chemical reagents).また、研磨条件は、研磨圧力３００ｇｆ／ｃｍ 2 、研磨定盤１４および真空チャックホルダ１１の回転数１００ｒｐｍとし、研磨定盤の温度を室温２５℃で一定になるようにした。 The polishing conditions, the polishing pressure 300 gf / cm 2, and the rotational speed 100rpm of the polishing platen 14 and the vacuum chuck holder 11, the temperature of the polishing platen was set to a constant at room temperature 25 ° C..【００３６】ＣＭＰの結果、研磨速度は約３００ｎｍ／ [0036] As a result of the CMP, the polishing rate is about 300nm /分であり、非常に高速であった。 A minute, was very fast.また、Ｗ埋め込み配線およびＷプラグを形成するために、Ｗ膜３２と共にチタン膜３１および窒化チタン膜２４も除去しなければならない。 Further, in order to form a W buried wiring and W plugs must be removed titanium film 31 and the titanium nitride film 24 with a W film 32.チタン膜３１および窒化チタン膜２４の研磨速度はＷ膜２５とほとんど同じ約３００ｎｍ／分であったため、高速に除去することができた。 Since the polishing rate of a titanium film 31 and the titanium nitride film 24 was almost the same about 300 nm / min and the W film 25 could be removed at a high speed.また、ＣＭＰ後のＷ In addition, W after the CMP埋め込み配線およびＷプラグ、並びに露出したシリコン酸化膜の表面を走査型電子顕微鏡で観察したところ、図３に示すように、ＣＭＰにより発生したと思われる傷等は全く見られなかった。 Observation of the buried wiring and W plugs, as well as the exposed surface of the silicon oxide film with a scanning electron microscope, as shown in FIG. 3, was not observed at all scratches that may have occurred by CMP.【００３７】なお、ＣＭＰにおいてＷ表面には、Ｗ、Ｗ [0037] It is to be noted that the W surface in the CMP, W, WＯｘ等が混在すると考えられるが、ＢＰＡはいずれの物質ともキレート化合物を形成して保護膜を設ける。 Considered Ox like are mixed but, BPA is a protective film to form a chelate compound with any material.次に、ディッシング量の配線幅依存性について調べた。 Next it was examined the dishing amount of the wiring width dependency.その結果を図８に示す。 The results are shown in Figure 8.ここでは、凸部のＷ膜３２、チタン膜３１および窒化チタン膜２４をすべて除去した時を研磨終了時とした。 Here, W film 32 of the convex portion, and the at the end of polishing when removing all the titanium film 31 and the titanium nitride film 24.図８から明らかなように、Ｗ埋め込み配線のディッシング値は、配線幅が１０μｍの配線中央部で約５０ｎｍであり、実用上ほぼ問題のない程度であった。 As apparent from FIG. 8, dishing values ​​of W embedded wiring, the wiring width of about 50nm wiring central portion of the 10 [mu] m, was much no practical problems in almost.また、研磨時間をさらに延長しても、ディッシング値はほとんど増加しなかったことを考慮すると、Ｗ Moreover, even further extending the polishing time, considering that the dishing value was hardly increased, W膜３２上に形成された保護膜が効果的に機能していることが分かる。 It can be seen that the protective film formed on the film 32 is working effectively.【００３８】本実施例においては、被研磨膜としてＷ膜を用いた場合について説明しているが、Ｗに少量の不純物や添加元素が含有されている場合においても同様の効果が得られる。 [0038] In this embodiment, has been described the case of using a W film as a film to be polished, the same effect can be obtained even when a small amount of impurities and the additional element is contained in W.【００３９】さらに、上記実施例では、被研磨体として、Ｗ膜をブランケット状に形成する場合において説明しているが、ＷＦ 6ガスとＳｉＨ 4ガスとの混合ガス、 [0039] Further, in the above embodiment, as material to be polished, has been described in the case of forming a W film is blanket-like, mixed gas of WF 6 gas and SiH 4 gas,もしくはこの混合ガスにＨ 2ガスを添加したガスを用いてＷ膜の選択成長を行う場合に対しても本発明は適用可能である。 Or the present invention is also applicable to the case of performing selective growth of the W film using the added gas and H 2 gas in the mixed gas.すなわち、例えばコンタクトホールやビアホールを有する層間絶縁膜の底に露呈するシリコン層やＴ That is, the silicon layer exposed to the bottom of the interlayer insulating film having, for example, contact holes, via holes and TｉＮ層、ＴｉＳｉ等のシリサイド層等の上に選択的にＷ iN layer, selectively W on top of the silicide layer such as TiSi, etc.膜を成長させる場合において、選択性の崩れにより、絶縁膜表面にＷ粒子が成長することがあるが、上記実施例の研磨方法を用いれば、このＷ粒子を選択的に除去することが可能である。 In the case where the film is grown, the collapse of the selectivity, it is the W particles grow the insulating film surface, by using the polishing method of the above embodiment, can be selectively removed the W particles is there.【００４０】また、本実施例においては、研磨粒子としてアルミナ粒子のみを用いた場合について説明しているが、研磨粒子としてアルミナ粒子と同等あるいはそれ以上の硬度を有するシリカ粒子、酸化チタン粒子、酸化ジルコニウム粒子、酸化セリウム粒子、炭化珪素粒子、ダイヤモンド粒子等を用いた場合においても同様の効果が得られる。 Further, in the present embodiment has been described for the case of using only alumina particles as abrasive particles, silica particles having an alumina particle equal to or higher hardness as abrasive particles, titanium oxide particles, oxide zirconium particles, cerium oxide particles, silicon carbide particles, the same effect can be obtained even when using diamond particles.【００４１】また、本実施例においては、エッチング剤として過酸化水素水溶液を用い、化学試薬としてＢＰＡ Further, in this embodiment, the hydrogen peroxide aqueous solution as an etching agent, BPA as chemical reagentsを用いた場合について説明しているが、エッチング剤として硝酸鉄水溶液、フェリシアン化カリウムとエチレンジアミンとの混合水溶液、フェリシアン化カリウムとリン酸との混合水溶液等を用いた場合においても同様の効果が得られる。 It has described the case of using the iron nitrate aqueous solution, a mixed aqueous solution of potassium ferricyanide and ethylenediamine, the same effect even in the case of using the mixed aqueous solution or the like with potassium ferricyanide and phosphate is obtained as an etching agent.また、化学試薬としては、エッチングする膜材料に応じてこの材料とキレート化合物や錯体化合物を形成する試薬、例えばＢＰＡの各種誘導体等を用いた場合においても同様の効果が得られる。 As the chemical reagent, the reagent according to the film material is etched to form the material and the chelate compound or complex compound, the same effect even when using, for example, various derivatives of BPA etc. obtained.【００４２】また、本実施例においては、研磨パッドには樹脂含浸不織布からなる研磨パッドを用いたが、同程度の硬度を有するものであれば良く、例えば、ポリエステル、ポリエーテル等の不織布、発砲ポリウレタンパッド、またはそれら２種類以上の異なるパッドを張り合わせた研磨パッド等を用いてもよい。 Further, in this embodiment, the polishing pad using a polishing pad made of resin-impregnated nonwoven fabric, as long as it has a hardness comparable, for example, polyester, non-woven such as polyether, fire polyurethane pad or with a polishing pad or the like bonding them two or more different pads.なお、上記した各種物質の誘導体としては、水素部分がアルキル基（メチル基、エチル基等）に置き変わったものが特に好ましい。 As the derivatives of various substances mentioned above, which a hydrogen moiety is placed changes to the alkyl group (methyl group, ethyl group, etc.) are particularly preferred.（比較例２）研磨剤として、５体積％の過酸化水素水溶液に、研磨粒子としてアルミナ粒子（平均粒径５０ｎ (Comparative Example 2) abrasives, the 5 vol% aqueous hydrogen peroxide solution, the alumina particles as abrasive particles (average particle size 50nｍ）を１．０重量％で分散させたもの、すなわち実施例で使用した研磨剤においてＢＰＡを添加していないものを用いること以外は実施例２と同様にして図７（Ａ）に示す被研磨基板１２にＣＭＰを行った。 m) which was dispersed with 1.0 wt%, i.e. the 7 but using those without added BPA in the polishing agent used in Example in the same manner as in Example 2 (A) CMP is performed to polish the substrate 12.【００４３】ＣＭＰの結果、研磨速度は約３５０ｎｍ／ [0043] As a result of the CMP, the polishing rate is about 350nm /分であり高速であるが、ディッシング値が実施例２の場合に比べて非常に大きかった。 A minute is fast, dishing value was very large as compared with the case of Example 2.すなわち、図９に示すように、最小線幅の０．４μｍ配線幅においてはディッシング量が約２００ｎｍであり、さらに、熱ＣＶＤ時に形成される配線中央部のＷ膜の合わせ目に沿ってエッチングが進行し、配線に穴３３が開いた状態になった。 That is, as shown in FIG. 9, in the 0.4μm line width of the minimum line width of about 200nm is dishing amount, further, the etching along the seam of the W film wiring central portion which is formed during the thermal CVD is progress, hole 33 in the wiring is in a state of open.（実施例３）本発明の研磨方法においては、研磨中に金属、例えばＣｕの表面に、化学試薬、例えばＢＴＡと金属との化合物（Ｃｕ−ＢＴＡ）からなる保護膜が形成される。 In the polishing method of (Example 3) The present invention, metal during polishing, for example, on the surface of Cu, chemical reagents, for example, a protective film made of a compound of BTA and metal (Cu-BTA) is formed.この場合、保護膜が機械的に除去された時点で研磨剤中のエッチング成分によりＣｕがエッチングされる。 In this case, the protective film is Cu are etched by the etching component in the polishing agent when it is mechanically removed.この場合、Ｃｕのエッチング速度の活性化エネルギーＥ aeは比較的大きく、Ｃｕの研磨速度の活性エネルギーＥ apは比較的小さい。 In this case, the activation energy E ae etch rate of Cu is relatively large, active energy E ap polishing rate of Cu is relatively small.これは、研磨においては、化学的作用だけでなく機械的作用も含まれるからである。 This is because in the grinding, because also included mechanical action as well as chemical action.したがって、Ｅ ae ＞Ｅ apの関係が成り立つ。 Therefore, it holds the relationship of E ae> E ap.このため、研磨速度／エッチング速度の比の値は低温ほど大きくなるので、ディッシング低減の観点からは低温でＣＭＰを行った方が有利になる。 Therefore, the value of the ratio of the polishing rate / etching rate becomes larger as the low temperature, becomes advantageous to CMP is performed at a low temperature from the viewpoint of dishing reduced.【００４４】そこで、本実施例では、ＣＭＰを低温で行う場合について説明する。 [0044] In the present exemplary embodiment illustrates the case of performing the CMP at low temperatures.ＣＭＰを低温、例えば２０℃ Low temperature CMP, for example, 20 ° C.以下で行う場合には、研磨定盤、研磨パッド、および研磨剤のうち少なくとも一つを冷却してもよく、始めに通常の温度（常温）で第一段階の研磨を行い、続けて低温、例えば２０℃以下で第二段階の研磨を行ってもよい。 When performing in the following, a polishing platen, a polishing pad, and out of the abrasive may be cooled at least one performs the grinding of the first step at normal temperature (room temperature) at the beginning, followed by a low temperature, for example 20 ° C. may be performed to polish the second stage below.【００４５】図２（Ａ）に示す被研磨基板１２を図１に示す研磨装置を用いてＣＭＰを行い、配線用溝および接続配線用開孔以外の余剰なＣｕ膜２５を除去してＣｕの埋め込み配線およびＣｕプラグを形成した。 [0045] The polished substrate 12 shown in FIG. 2 (A) performs the CMP by using the polishing apparatus shown in FIG. 1, the Cu was removed wiring grooves and the connection wiring other than apertures excess Cu film 25 thereby forming a buried wiring and Cu plug.ＣＭＰに使用した研磨剤は、０．１２モル／リットルのグリシン（Ｃ 2 Ｈ 5 Ｏ 2 Ｎ）水溶液と０．４４モル／リットルの過酸化水素水（Ｈ 2 Ｏ 2 ）との混合溶液（Ｃｕのエッチング剤）に、研磨粒子としてシリカ粒子（平均粒径３０ Polishing agent used in CMP is a mixed solution of 0.12 mol / l glycine (C 2 H 5 O 2 N ) aqueous solution and 0.44 mol / l of hydrogen peroxide (H 2 O 2) (Cu of the etchant), silica particles as abrasive particles (average particle size 30ｎｍ）を５．３重量％で分散させ、さらに０．００１モル／リットルのベンゾトリアゾール（Ｃ 6 Ｈ 5 Ｎ 3 ） nm) dispersed with 5.3 wt%, further 0.001 mol / l benzotriazole (C 6 H 5 N 3)（化学試薬）を添加してなるものである。 Those obtained by adding (chemical reagents).また、研磨条件は、研磨圧力４００ｇｆ／ｃｍ 2 、研磨定盤１４および真空チャックホルダ１１の回転数６０ｒｐｍとした。 The polishing conditions, the polishing pressure 400 gf / cm 2, and the rotational speed 60rpm of the polishing platen 14 and the vacuum chuck holder 11.【００４６】このときのＣｕの研磨速度およびエッチング速度の温度依存性を調べた。 [0046] investigated the temperature dependence of the polishing rate and the etching rate of Cu in this case.その結果を図１０に示す。 The results are shown in Figure 10.なお、温度は約−２℃から約１００℃まで変化させた。 The temperature was varied from about -2 ° C. to about 100 ° C..図１０から明らかなように、研磨速度およびエッチング速度は、温度の逆数（１／Ｔ）のexponential(指数) に比例した。 As apparent from FIG. 10, the polishing rate and etching rate was proportional to the exponential (index) of the reciprocal of temperature (1 / T).これらのグラフの傾きから研磨速度の活性化エネルギーＥ apおよびエッチング速度の活性化エネルギーＥ aeをそれぞれ求めると、Ｅ apが約０．７ｅＶ When determining the graphs of inclination from the polishing rate activation energy E ap and the activation energy E ae etch rate, respectively, E ap about 0.7eVであり、Ｅ aeが約０．９ｅＶであった。 In it, E ae was about 0.9eV.それぞれのグラフの傾きは負であり、Ｅ ap ＜Ｅ aeであることから、研磨速度／エッチング速度の比の値は低温ほど大きくなる。 The slope of each graph is negative, since it is E ap <E ae, the value of the ratio of the polishing rate / etching rate increases as the low temperature.したがって、ＣＭＰの温度が低温であるほど、Ｃｕ配線のディッシング量が減少する。 Accordingly, as the temperature of the CMP is at a low temperature, the dishing amount of Cu wirings is reduced.【００４７】次に、研磨温度を室温（２４．０℃）に設定してＣＭＰを行った場合と、研磨温度を１４．０℃に設定してＣＭＰを行った場合のそれぞれのディッシング量の配線幅依存性について調べた。 Next, the case of performing the CMP polishing temperature is set to room temperature (24.0 ° C.), each of dishing amount of wiring in the case of performing CMP by setting the polishing temperature 14.0 ° C. It was studied width dependence.その結果を図１１に示す。 The results are shown in Figure 11.ここでは、凸部上のＣｕ膜２５および窒化チタン膜２４をすべて除去した時を研磨終了時とした。 Here, upon removal of all of the Cu film 25 and the titanium nitride film 24 on the convex portion was at the end of polishing.図１０ Figure 10から明らかなように、Ｃｕ埋め込み配線のディッシング値は、配線幅が１０μｍの配線中央部で約１００ｎｍであり、実用上ほぼ問題のない程度であった。 As apparent from dishing value of Cu buried wiring, the wiring width of about 100nm wiring central portion of the 10 [mu] m, was much no practical problems in almost.【００４８】次に、研磨温度を室温（２４．０℃）に設定してＣＭＰを行った場合と、研磨温度を１４．０℃に設定してＣＭＰを行った場合の配線幅５μｍのディッシング量の研磨時間依存性について調べた。 Next, dishing amount of wiring width 5μm in the case of performing the case of performing the CMP polishing temperature is set to room temperature (24.0 ° C.), the CMP by setting the polishing temperature 14.0 ° C. We were examined for the polishing time-dependent.その結果を図１２に示す。 The results are shown in Figure 12.図１２から明らかなように、低温でＣＭＰ As apparent from FIG. 12, CMP at low temperaturesを行うことにより、オーバーポリッシング時のデッィシング量の増加を抑制することができる。 By performing, it is possible to suppress an increase in De'ishingu amount during overpolishing.【００４９】また、ＣＭＰ後のＣｕ埋め込み配線およびＣｕプラグの表面を走査型電子顕微鏡で観察したところ、図２（Ｂ）に示すように、ＣＭＰにより発生したと思われる傷等は全く見られなかった。 [0049] In addition, observation of the Cu buried wiring and Cu surface of the plug after CMP with a scanning electron microscope, as shown in FIG. 2 (B), not seen at all such as scratches that may have occurred by CMP It was.【００５０】本実施例においては、被研磨膜としてＣｕ [0050] In this example, Cu as the film to be polished膜を用いた場合について説明しているが、Ｃｕに少量の不純物や添加元素が含有されている場合や、被研磨膜としてＣｕ以外の金属、例えばＡｇ、Ａｌ、Ｗ等の膜やこれらを主成分とした膜を用いた場合においても同様の効果が得られる。 Have described the case of using the film, and if a small amount of impurities and the additional element is contained in the Cu, the metal other than Cu as a film to be polished, for example Ag, Al, such as W film or these main the same effect can be obtained even in the case of using the film as a component.【００５１】また、本実施例においては、研磨粒子としてシリカ粒子のみを用いた場合について説明しているが、研磨粒子としてシリカ粒子と同等あるいはそれ以上の硬度を有するアルミナ粒子、酸化チタン粒子、酸化ジルコニウム粒子、酸化セリウム粒子、炭化珪素粒子、ダイヤモンド粒子等を用いた場合においても同様の効果が得られる。 [0051] In the present embodiment has described the case of using only silica particles as abrasive particles, equivalent to the silica particles as abrasive particles or more of the alumina particles having a hardness, titanium oxide particles, oxide zirconium particles, cerium oxide particles, silicon carbide particles, the same effect can be obtained even when using diamond particles.【００５２】また、本実施例においては、エッチング剤としてグリシン水溶液および過酸化水素水の混合溶液を用い、化学試薬としてＢＴＡを用いた場合について説明しているが、エッチング剤としてアミド硫酸もしくはアミノ酢酸とアミド硫酸の混合酸と、過酸化水素（Ｈ 2 Ｏ [0052] In the present embodiment, using a mixed solution of glycine solution and hydrogen peroxide solution as an etchant, it has described the case of using the BTA as a chemical reagent, amido sulfuric acid or amino acid as an etchant amide mixed acid of sulfuric acid and hydrogen peroxide (H 2 O2 ）、硝酸、次亜塩素酸、オゾン水等の酸化剤とからなるもの、アンモニア、硝酸アンモニウム、塩化アンモニウム、クロム酸等を用いた場合においても同様の効果が得られる。2), nitric acid, hypochlorous acid, which consists of an oxidizing agent such as ozone water, ammonia, ammonium nitrate, ammonium chloride, the same effect can be obtained even in the case of using a chromic acid or the like.また、化学試薬としては、エッチングする膜材料に応じてこの材料とキレート化合物や錯体化合物を形成する試薬、例えばＢＴＡの各種誘導体、これらを含む混合物、チオ尿素、チオ尿素誘導体、クペロン、ベンズイミダゾール、トリアゾール、サリチルアルドキシム、エチレンジアミン、システィン、ｐ−アミノベンズアルデヒド、ハロ酢酸、ドデシルメルカプタン、ホスホン酸類、グルコースやフルクトース等の単糖類等を用いた場合においても同様の効果が得られる。 As the chemical reagent, the reagent according to the film material is etched to form the material and chelate compounds and complex compounds, for example, various derivatives of BTA, the mixture containing them, thiourea, thiourea derivatives, cupferron, benzimidazole, triazole, salicylaldoxime, ethylenediamine, cysteine, p- aminobenzaldehyde, haloacetic acid, dodecyl mercaptan, phosphonic acids, the same effect can be obtained in the case of using a monosaccharide such as glucose or fructose.特に、ＢＴＡ In particular, BTAまたはＢＴＡの各種誘導体は、硫酸水溶液や塩酸水溶液等を用いる場合に有効である。 Or various derivatives of BTA is effective when using a sulfuric acid solution or aqueous hydrochloric acid, and the like.【００５３】また、本実施例においては、研磨パッドには樹脂含浸不織布からなる研磨パッドを用いたが、同程度の硬度を有するものであれば良く、例えば、ポリエステル、ポリエーテル等の不織布、発砲ポリウレタンパッド、またはそれら２種類以上の異なるパッドを張り合わせた研磨パッド等を用いてもよい。 [0053] In the present embodiment, the polishing pad using a polishing pad made of resin-impregnated nonwoven fabric, as long as it has a hardness comparable, for example, polyester, non-woven such as polyether, fire polyurethane pad or with a polishing pad or the like bonding them two or more different pads.なお、上記した各種物質の誘導体としては、水素部分がアルキル基等に置き変わったものが特に好ましい。 As the derivatives of various substances mentioned above, which a hydrogen partial is changed placed in the alkyl group and the like are particularly preferred.（実施例４）図１３は本発明の研磨方法に使用する研磨装置の一部を示す概略図である。 (Example 4) FIG. 13 is a schematic view showing a part of a polishing apparatus used in the polishing method of the present invention.この研磨装置においては、研磨定盤１４内に冷媒循環路４１が設けられている。 In this polishing apparatus, a refrigerant circulation path 41 is provided in the polishing table 14.この冷媒循環路４１内に水、エチレングリコール等の冷媒を通流させることにより、研磨定盤１４および研磨パッド１３の温度を調節することができる。 By flow through water, a coolant such as ethylene glycol to the coolant circulation path 41, it is possible to adjust the temperature of the polishing platen 14 and polishing pad 13.研磨定盤の主要部分の材質はグラスファイバーであり、金属材料と比較して熱容量が小さく、熱伝導率が高いので、迅速な温度調節が可能である。 The material of the main part of the polishing platen is glass fiber, smaller heat capacity as compared to metal materials, because of its high thermal conductivity, it is possible to rapid temperature control.冷媒循環路４１は２系統の冷媒冷却装置（冷却器４２，４３）に接続されており、途中の切り替えスイッチ４４で随時、冷媒の循環経路を切り替えることができるようになっている。 Refrigerant circulation channel 41 is connected to the refrigerant cooling device two systems (cooler 43) at any time by switching the switch 44 in the middle, so that it is possible to switch the circulation path of the refrigerant.さらに、冷却器４２および４３には、それぞれ研磨剤供給系統４５および４６がそれぞれ接続されており、供給する研磨剤の温度を調節できるようになっている。 Further, the condenser 42 and 43, respectively abrasive supply system 45 and 46 are connected respectively, are enabled to adjust the temperature of the polishing agent supplied.また、研磨定盤１ In addition, the polishing platen 1４の上方には、冷却された純水を研磨定盤１４上に吹き付けるジェットノズル４７が配置されている。 Above the 4, jet nozzles 47 for spraying pure water that has been cooled on the polishing platen 14 is disposed.【００５４】上記構成を有する研磨装置を用いて、二段階の研磨、すなわち第一の研磨（室温研磨）および第二の研磨（低温研磨）でＣＭＰを行った。 [0054] using a polishing apparatus having the above structure, CMP is performed in two steps polishing, i.e. the first polishing (room temperature grinding) and second polishing (cold grinding).なお、冷却器４ Incidentally, the cooler 4２の設定温度を２４．０℃とし、冷却器４３の設定温度を１４．０℃とすることにより、研磨剤供給系統４５およびその内部の研磨剤の温度を２４．０℃に温度調節し、研磨剤供給系統４６およびその内部の研磨剤の温度を１４．０℃に温度調節した。 The second setting temperature of 24.0 ° C., by the set temperature of the condenser 43 and 14.0 ° C., and temperature control the temperature of the slurry supply line 45 and its internal abrasive 24.0 ° C., the temperature was adjusted to 14.0 ° C. temperature of the polishing agent supply system 46 and its internal abrasive.また、ジェットノズル４ In addition, jet nozzle 4７内部の純水の温度も１４．０℃に温度調節した。 7 internal temperature of the pure water is also thermostated at 14.0 ° C..【００５５】まず、切り替えスイッチ４４により研磨定盤１４の冷媒循環路４１を冷却器４２に接続し、研磨剤供給系統４５を用いて、研磨温度を２４．０℃に設定し、実施例３と同様にしてＣＭＰを行った。 Firstly, the refrigerant circulation channel 41 of the polishing platen 14 is connected to the cooler 42 by changeover switch 44, with the abrasive supply system 45, to set the polishing temperature of 24.0 ° C., as in Example 3 CMP is performed in the same manner.このとき、 At this time,研磨時間は、研磨終了時間の約８０％とした。 Polishing time was about 80% of the polishing end time.その結果、研磨終了時間が２分３７秒であったので、第一の研磨の研磨時間は２分５秒であった。 As a result, the polishing end time was 2 minutes 37 seconds, the first polishing time of the polishing of was 2 minutes 5 seconds.【００５６】第一の研磨の後、研磨剤供給系統４５を停止し、研磨定盤１４の冷媒循環路４１を切り替えスイッチ４４により冷却器４３に接続し、急速に研磨定盤１４ [0056] After the first polishing, an abrasive supply system 45 is stopped, the switch 44 switches the refrigerant circulation channel 41 of the polishing platen 14 is connected to the cooler 43 rapidly polishing platen 14内に１４．０℃の冷却水を循環させると共に、ジェットノズル４７から冷却された純水を噴射することにより、 With circulating 14.0 ° C. cooling water within, by injecting pure water that has been cooled from the jet nozzle 47,研磨定盤１４を冷却した。 The polishing table 14 and cooled.研磨定盤１４上の研磨パッド１３表面の温度が約１４℃になった時点で、研磨剤供給系統４６を用いて、研磨温度を１４．０℃に設定し、実施例３と同様にしてＣＭＰを行った。 When the temperature of the polishing pad 13 surface on the polishing platen 14 was about 14 ° C., using an abrasive supply system 46, to set the polishing temperature of 14.0 ° C., as in Example 3 CMP It was carried out.この第二の研磨により、第一の研磨で残存した部分を全て研磨した。 This second polishing was polished all portions remaining in the first polishing.このとき、第二の研磨の研磨時間は２分２４秒であった。 At this time, the polishing time of the second polishing was 2 minutes 24 seconds.【００５７】次に、研磨されたＣｕ配線におけるディッシング量の配線幅依存性を調べた。 Next, we examined the dishing amount of the wiring width dependency in polished Cu wiring.その結果を図１４に示す。 The results are shown in Figure 14.図１４から明らかなように、室温、低温の二段階のＣＭＰにおいても、低温でのＣＭＰと同程度のディッシング抑制効果が得られる。 As apparent from FIG. 14, at room temperature, in CMP of a low temperature two-stage, dishing inhibitory effect comparable to the CMP at low temperatures is obtained.【００５８】 【発明の効果】以上説明した如く本発明の研磨剤および研磨方法によれば、表面に凹部を有する基体上に前記凹部を充填するように金属を主成分とする材料からなる膜を形成し、前記金属を主成分とする材料と反応することにより前記膜表面に保護膜を形成する化学試薬および前記金属を主成分とする材料のエッチング剤を含有する研磨剤を用いた化学機械的研磨方法により、前記膜を研磨して前記凹部内に導体膜を形成するので、実用上問題のない程度にディッシングや傷の発生を抑制しながら、信頼性の高い導体膜を高速で形成することができる。 [0058] According to abrasives and polishing method or as described the present invention, a film made of a material mainly composed of metal so as to fill the recess on a substrate having a concave portion on the surface formed, a chemical mechanical using an abrasive containing etchant material mainly composed of chemical reagents and the metal forming the protective layer on the membrane surface by reaction with material mainly containing the metal the polishing method, since forming a conductor film in the recess by polishing the film while suppressing the occurrence of dishing or scratches to a degree no practical problem, to form a reliable conductive film at high speed can.

【図面の簡単な説明】 【図１】本発明の研磨方法に使用される研磨装置を示す概略説明図。 Schematic diagram illustrating a polishing apparatus used in the polishing method of the BRIEF DESCRIPTION OF THE DRAWINGS [Figure 1] present invention.【図２】（Ａ），（Ｂ）は本発明の研磨方法の一実施例を説明するための断面図。 Figure 2 (A), (B) is a sectional view for explaining an embodiment of a polishing method of the present invention.【図３】本発明の研磨方法における研磨温度と研磨速度との関係を示すグラフ。 Graph showing the relationship between the polishing temperature and the polishing rate in the polishing method of the present invention; FIG.【図４】本発明の研磨方法におけるＢＴＡの添加量に対する研磨速度およびエッチング速度の変化を示すグラフ。 Graph showing the change in the polishing rate and etching rate of the addition amount of BTA in the polishing method of the present invention; FIG.【図５】本発明の研磨方法における研磨圧力と研磨速度との関係を示すグラフ。 Graph showing the relationship between the polishing pressure and the polishing rate in the polishing method of the present invention; FIG.【図６】本発明の研磨方法における配線幅とディッシング量との関係を示すグラフ。 Graph showing the relationship between the line width and the dishing amount in the polishing method of the present invention; FIG.【図７】（Ａ），（Ｂ）は本発明の研磨方法の他の実施例を説明するための断面図。 7 (A), (B) is a sectional view for explaining another embodiment of the polishing method of the present invention.【図８】本発明の研磨方法における配線幅とディッシング量との関係を示すグラフ。 Graph showing the relationship between the line width and the dishing amount in the polishing method of the present invention; FIG.【図９】従来の研磨方法を説明するための断面図。 FIG. 9 is a cross-sectional view for explaining a conventional polishing method.【図１０】本発明の研磨方法における研磨速度およびエッチング速度の温度依存性を示すグラフ。 Figure 10 is a graph showing the temperature dependence of the polishing rate and etching rate in the polishing method of the present invention.【図１１】本発明の研磨方法における配線幅とディッシング量との関係を示すグラフ。 Figure 11 is a graph showing the relationship between the line width and the dishing amount in the polishing method of the present invention.【図１２】本発明の研磨方法におけるディッシング量と研磨時間との関係を示すグラフ。 Graph showing the relationship between the dishing amount and the polishing time in the polishing method of the present invention; FIG.【図１３】本発明の研磨方法に使用される研磨装置の一部を示す概略図。 Figure 13 is a schematic view showing a part of a polishing apparatus used in the polishing method of the present invention.【図１４】本発明の研磨方法における配線幅とディッシング量との関係を示すグラフ。 Figure 14 is a graph showing the relationship between the line width and the dishing amount in the polishing method of the present invention.【符号の説明】 １１…真空チャックホルダ、１２…被研磨基板、１３… [DESCRIPTION OF REFERENCE NUMERALS] 11 ... vacuum chuck holder, 12 ... substrate to be polished, 13 ...研磨パッド、１４…研磨定盤、１５…研磨剤供給配管、 Polishing pad, 14 ... polishing platen, 15 ... polishing agent supply pipe,１６…研磨剤、２１…シリコン基板、２２…シリコン酸化膜、２３…炭素膜、２４…窒化チタン膜、２５…Ｃｕ 16 ... abrasive, 21 ... silicon substrate, 22 ... silicon oxide film, 23 ... carbon film, 24 ... a titanium nitride film, 25 ... Cu膜、３１…チタン膜、３２…Ｗ膜、４１…冷媒循環路、 Film, 31 ... titanium film, 32 ... W film, 41 ... refrigerant circulation path,４２，４３…冷却器、４４…切り替えスイッチ、４５， 42, 43 ... cooler, 44 ... selector switch, 45,４６…研磨剤供給系統、４７…ジェットノズル。 46 ... abrasive supply system, 47 ... jet nozzle.

Claims (1)

Translated from Japanese

(57)【特許請求の範囲】 【請求項１】 表面に凹部を有する基体上に、前記凹部を充填するように金属を主成分とする材料からなる膜を形成する工程と、 前記金属を主成分とする材料と反応することにより前記膜表面に保護膜を形成する化学試薬と、前記金属を主成分とする材料のエッチング剤とを含有する研磨剤を用いた化学機械的研磨方法により、前記膜を研磨して前記凹部内に導体膜を形成する工程と、 を具備し、前記エッチング剤がアミノ酢酸および／またはアミド硫酸、酸化剤、および水を含有したことを特徴とする研磨方法。 (57) on a substrate having a recess to the Claims 1 surface, forming a film made of a material mainly composed of metal so as to fill the recess, mainly the metal a chemical reagent to form a protective layer on the membrane surface by reaction with the material to the component, by chemical mechanical polishing method using a polishing agent containing an etchant material mainly containing the metal, the by polishing the film comprises a step of forming a conductive film in the recess, wherein the etching agent is an amino acid and / or amide acid polishing method characterized by containing an oxidizing agent, and water.【請求項２】 前記金属がＣｕまたはＣｕ合金である請求項１記載の研磨方法。 2. A polishing method according to claim 1, wherein said metal is Cu or Cu alloy.【請求項３】 前記化学試薬が少なくともベンゾトリアゾールまたはその誘導体を包含する請求項２記載の研磨方法。 Wherein the chemical reagent polishing method according to claim 2, wherein comprises at least benzotriazole or a derivative thereof.【請求項４】 前記エッチング剤として、Ｃｕを主成分とする材料に対するエッチング速度が１０ｎｍ／分以上となるように、アミノ酢酸および／またはアミド硫酸と酸化剤との混合比率を調整してなるエッチング剤を用いる請求項２記載の研磨方法。 As claimed in claim 4, wherein the etching agent, made by adjusting the mixing ratio of such that the etch rate for the material mainly composed of Cu is 10 nm / min or more, and an oxidant amino acid and / or amide acid etching the polishing method according to claim 2, wherein the use of agents.【請求項５】 前記エッチング剤中のアミノ酢酸および／またはアミド硫酸の濃度に対する前記化学試薬の濃度がモル比で１／１０００〜３／１００の範囲である請求項２または３記載の研磨方法。 5. The polishing method of claim 2 or 3 wherein the concentration of the chemical reagent to the concentration of the amino acid and / or amide sulfuric acid in the etchant is in the range of 1 / 1000-3 / 100 molar ratio.【請求項６】 表面に凹部を有する基体上に、前記凹部を充填するように金属を主成分とする材料からなる膜を形成する工程と、 前記金属を主成分とする材料と反応することにより前記膜表面に保護膜を形成する化学試薬と、前記金属を主成分とする材料のエッチング剤とを含有する研磨剤を用いた化学機械的研磨方法により、前記膜を研磨して前記凹部内に導体膜を形成する工程と、 を具備し、前記金属がＷまたはＷ合金であり、前記化学試薬が少なくともＮ−ベンゾイル−Ｎ−フェニルヒドロ On a substrate having a recess 6. A surface, forming a film made of a material mainly composed of metal so as to fill the recess, by reacting with a material mainly composed of the metal a chemical reagent to form a protective layer on the membrane surface, by chemical mechanical polishing method using a polishing agent containing an etchant material mainly containing the metal, in the recess by polishing the film comprising a step of forming a conductive film, wherein the metal is W or a W alloy, the chemical reagent is at least N- benzoyl -N- phenyl-hydroキシルアミンまたはその誘導体を包含したことを特徴とする研磨方法。Hexylamine or polishing method is characterized in that encompass derivatives thereof.【請求項７】 表面に凹部を有する基体上に、前記凹部を充填するように金属を主成分とする材料からなる膜を形成する工程と、 前記金属を主成分とする材料のエッチング剤を含有する研磨剤を用いた化学機械的研磨方法により前記膜を研磨する工程と、 前記金属を主成分とする材料と反応することにより前記膜表面に保護膜を形成する化学試薬を加えた前記研磨剤を用いた化学機械的研磨方法により前記膜を研磨して前記凹部内に導体膜を形成する工程と、 を具備し、前記エッチング剤がアミノ酢酸および／またはアミド硫酸、酸化剤、および水を含有したことを特徴とする研磨方法。 On a substrate having a recess 7. A surface, containing the steps of forming a film made of a material mainly composed of metal so as to fill the recess, the etchant material mainly containing the metal the abrasive plus a chemical reagent to form a protective layer on the film surface by a chemical mechanical polishing method using an abrasive polishing the film, by reacting with a material mainly composed of the metal to be anda step of forming a conductive film in the recess by polishing the film by a chemical mechanical polishing method using the etchant amino acid and / or an amide acid, containing an oxidizing agent, and water polishing method characterized by the.【請求項８】 前記金属がＣｕまたはＣｕ合金である請求項７記載の研磨方法。 8. The polishing method according to claim 7, wherein said metal is Cu or Cu alloy.【請求項９】 前記化学試薬が少なくともベンゾトリアゾールまたはその誘導体を包含する請求項８記載の研磨方法。 Wherein said chemical reagent polishing method according to claim 8, wherein comprises at least benzotriazole or a derivative thereof.【請求項１０】 金属を主成分とする材料と反応することにより、前記材料からなる膜表面に保護膜を形成する化学試薬と、前記材料のエッチング剤とを含有し、前記エッチング剤がアミノ酢酸および／またはアミド硫酸、 By 10. react with material mainly composed of metal, and chemical reagents to form a protective film on the film surface made of said material, containing an etching agent of the material and the etchant amino acid and / or amide acid,酸化剤、および水を含有したことを特徴とする研磨剤。 Polishing agent characterized by containing an oxidizing agent, and water.【請求項１１】 アミノ酢酸および／またはアミド硫酸、酸化剤、水およびベンゾトリアゾールあるいはその誘導体を含有することを特徴とする研磨剤。 11. Amino acid and / or amide acid, oxidizing agent, polishing agent characterized by containing water and benzotriazole or its derivative.【請求項１２】 表面に凹部を有する基体上に、前記凹部を充填するように金属を主成分とする材料からなる導電性膜を形成する工程と、 前記金属を主成分とする材料と反応することにより前記導電性膜の表面に保護膜を形成する化学試薬と、前記金属を主成分とする材料のエッチング剤とを含有する研磨剤を施しつつ、研磨定盤に取り付けられた研磨パッドを用いて、前記導電性膜を化学機械的研磨方法により研磨する工程とを具備し、前記研磨を、前記研磨パッド、前記研磨定盤、および前記研磨剤からなる群から選ばれた少なくとも１つを冷却しつつ行い、前記エッチング剤が On a substrate having a recess 12. A surface, forming a conductive film made of a material mainly composed of metal so as to fill the recess, to react with material mainly containing the metal wherein the chemical reagent to form a protective film on the surface of the conductive film, while applying an abrasive containing a etchant material mainly containing the metal, with a polishing pad attached to the polishing table by Te, comprising a step of polishing the conductive film by chemical mechanical polishing method, the polishing, the polishing pad, the polishing platen, and at least one said member selected from the group consisting of abrasive cooling There line while the etchantアミノ酢酸および／またはアミド硫酸、酸化剤、およびAmino acid and / or amide acid, oxidizing agent, and水を含有したことを特徴とする研磨方法。 Polishing method characterized by containing water.