A method for processing iron disilicide for manufacture photovoltaic devices. The method includes providing a first sample of iron disilicide comprising at least an alpha phase entity, a beta phase entity, and an epsilon phase entity. The method includes maintaining the first sample of iron disilicide...http://www.google.ca/patents/US20090087370?utm_source=gb-gplus-sharePatent US20090087370 - Method and material for purifying iron disilicide for photovoltaic application

A method for processing iron disilicide for manufacture photovoltaic devices. The method includes providing a first sample of iron disilicide comprising at least an alpha phase entity, a beta phase entity, and an epsilon phase entity. The method includes maintaining the first sample of iron disilicide in an inert environment and subjects the first sample of iron disilicide to a thermal process to form a second sample of iron disilicide. The second sample of iron disilicide comprises substantially beta phase iron disilicide and is characterized by a first particle size. The method includes introducing an organic solvent to the second sample of iron disilicide, forming a first mixture of material comprising the second sample of iron disilicide and the organic solvent. The method processed the first mixture of material including the second sample of iron disilicide using a grinding process. The method converted the second sample of iron disilicide having the first particle size to a third sample of iron disilicide having a second particle size. The organic solvent is removed and output a third sample of iron disilicide characterized by the second particle size and greater than about 90% of the beta phase entity.

Images(4)

Claims(16)

1. A method for processing iron disilicide for manufacture of photovoltaic devices, the method comprising:

providing a first sample of an iron disilicide comprising at least an alpha phase entity ranging from about 5% to about 20% of a total phase entity, a beta phase entity comprising about 30% to about 75% of the phase entity, and an epsilon phase entity comprising about 5% to about 20% of the total phase entity;

maintaining the first sample of iron disilicide in an inert environment;

subjecting the first sample of iron disilicide to a thermal process while maintaining the first sample of iron disilicide in the inert environment to cause formation of a second sample of iron disilicide comprising substantially beta phase iron disilicide, the second iron disilicide being characterized by a first particle size ranging from about 1 micron to about 20 microns;

introducing an organic solvent to the second sample to form a first mixture of material comprising the second sample of iron disilicide and the organic solvent;

processing the first mixture of material including the second sample of iron disilicide using a grinding process to convert the second sample of iron disilicide having the first particle size to a third sample of iron disilicide having a second particle size ranging from about 1 micron to about 2 microns;

removing the organic solvent from the third sample of iron disilicide in the organic solvent; and

outputting the third sample of iron disilicide characterized by the second particle size and greater than about 90% of the beta phase entity.

2. The method of claim 1 wherein the first iron disilicide is from a commercial source.

3. The method of claim 1 wherein the first particle size ranges from about 15 mesh to about 25 mesh.

4. The method of claim 1 wherein the first sample of iron disilicide comprises greater than about 75 percent beta phase iron disilicide.

5. The method of claim 1 wherein the inert environment is provided by nitrogen, argon, helium, and others.

6. The method of claim 1 wherein the thermal process is provided at a temperature ranging from about 800 Degree Celsius to about 850 Degree Celsius for about 16 hours to about 17 hours.

7. The method of claim 1 wherein the thermal process is provided at a temperature ranging from about 700 Degree Celsius to about 800 Degree Celsius for about 16 hours to about 18 hours.

8. The method of claim 1 wherein the organic solvent is selected from:

isopropyl alcohol (IPA), octane, and others.

9. The method of claim 1 wherein the second sample of iron disilicide comprises greater than about 95 percent beta phase iron disilicide.

10. The method of claim 1 wherein the second particle size is about 20 mesh.

11. The method of claim 1 wherein the grinding process is a ball milling process.

STATEMENT AS TO RIGHTS TO INVENTIONS MADE UNDER FEDERALLY SPONSORED RESEARCH AND DEVELOPMENT

[0002]

Not Applicable

REFERENCE TO A “SEQUENCE LISTING,” A TABLE, OR A COMPUTER PROGRAM LISTING APPENDIX SUBMITTED ON A COMPACT DISK

[0003]

Not Applicable

BACKGROUND OF THE INVENTION

[0004]

The present invention relates generally to photovoltaic materials. More particularly, the present invention provides a method and structure for processing semiconductor materials used for the manufacture of photovoltaic devices. Merely by way of example, the present method and structure have been implemented using a commercial source of iron disilicide, but it would be recognized that the invention may have other configurations.

[0005]

From the beginning of time, mankind has been challenged to find ways of harnessing energy. Energy comes in the forms such as petrochemical, hydroelectric, nuclear, wind, biomass, solar, and more primitive forms such as wood and coal. Over the past century, modern civilization has relied upon petrochemical energy as an important energy source. Petrochemical energy includes gas and oil. Gas includes lighter forms such as butane and propane, commonly used to heat homes and serve as fuel for cooking. Gas also includes gasoline, diesel, and jet fuel, commonly used for transportation purposes. Heavier forms of petrochemicals can also be used to heat homes in some places. Unfortunately, the supply of petrochemical fuel is limited and essentially fixed based upon the amount available on Earth. Additionally, as more people use petrochemicals in growing amounts, it is rapidly becoming a scarce resource, which will eventually be depleted over time.

[0006]

More recently, environmentally clean and renewable sources of energy have been desired. An example of a clean source of energy is hydroelectric power. Hydroelectric power is derived from electric generators driven by the flow of water produced by dams such as the Hoover Dam in Nevada. The electric power generated is used to power a large portion of the city of Los Angeles in California. Clean and renewable sources of energy also include wind, waves, biomass, and the like. That is, windmills convert wind energy into more useful forms of energy such as electricity. Still other types of clean energy include solar energy. Specific details of solar energy can be found throughout the present background and more particularly below.

[0007]

Solar energy technology generally converts electromagnetic radiation from the sun to other useful forms of energy. These other forms of energy include thermal energy and electrical power. For electrical power applications, solar cells are often used. Although solar energy is environmentally clean and has been successful to a point, many limitations remain to be resolved before it becomes widely used throughout the world. As an example, one type of solar cell uses crystalline materials, which are derived from semiconductor material ingots. These crystalline materials can be used to fabricate optoelectronic devices that include photovoltaic and photodiode devices that convert electromagnetic radiation into electrical power. However, crystalline materials are often costly and difficult to make on a large scale. Additionally, devices made from such crystalline materials often have low energy conversion efficiencies. Other types of solar cells use “thin film” technology to form a thin film of photosensitive material to be used to convert electromagnetic radiation into electrical power. Similar limitations exist with the use of thin film technology in making solar cells. That is, efficiencies are often poor. Additionally, film reliability is often poor and cannot be used for extensive periods of time in conventional environmental applications. Often, thin films are difficult to mechanically integrate with each other. These and other limitations of these conventional technologies can be found throughout the present specification and more particularly below.

[0008]

From the above, it is seen that improved techniques for manufacturing photovoltaic materials and resulting devices are desired.

BRIEF SUMMARY OF THE INVENTION

[0009]

According to embodiments of the present invention, a method and a system for forming semiconductor materials for photovoltaic applications is provided. More particularly, the present invention provides a method and structure for processing semiconductor materials used for the manufacture of photovoltaic devices. Merely by way of example, the method has been used to provide beta iron disilicide for photovoltaic application. But it would be recognized that the present invention has a much broader range of applicability.

[0010]

In a specific embodiment, the method includes providing a first sample of iron disilicide. The first sample of iron disilicide comprises at least alpha iron disilicide, beta phase iron disilicide, and epsilon phase iron silicide and characterized by a first particle size. The method includes maintaining the first sample of iron disilicide in an inert environment and subjecting the first sample of iron disilicide to an heating process while maintaining the first sample of iron disilicide in the inert environment to form a second sample of iron disilicide. The second sample of iron disilicide comprises substantially beta phase iron disilicide (greater than about 90 percent). The second iron disilicide is characterized by a second particle size. The method forms a first mixture of material comprising the second sample of iron disilicide and an organic solvent. In a specific embodiment, the first mixture of material including the second sample of iron disilicide is subjected to a grinding process. The method includes removing the organic solvent; and forms a third sample of iron disilicide comprising substantially beta iron disilicide. The third sample of iron disilicide is characterized by a third particle size.

[0011]

In a specific embodiment, the method includes providing a first sample of an iron disilicide. The first sample of iron disilicide comprises at least an alpha phase entity ranging from about 5% to about 20% of a total phase entity, a beta phase entity comprising about 30% to about 75% of the phase entity, and an epsilon phase entity comprising about 5% to about 20% of the total phase entity. The method includes maintaining the first sample of iron disilicide in an inert environment, for example, nitrogen, helium, argon, or others. The method subjects the first sample of iron disilicide to a thermal process while maintaining the first sample of iron disilicide in the inert environment to cause formation of a second sample of iron disilicide. The second sample of iron disilicide comprises substantially beta phase iron disilicide and characterized by a first particle size ranging from about 1 to about 20 microns. The method includes introducing an organic solvent to the second sample to form a first mixture of material comprising the second sample of iron disilicide and the organic solvent. In a specific embodiment, the method processes the first mixture of material including the second sample of iron disilicide using a grinding process to convert the second sample of iron disilicide having the first particle size to a third sample of iron disilicide having a second particle size. In a specific embodiment, the second particle size ranges from about 1 micron to about 2 microns. The method then removes the organic solvent from the third sample of iron disilicide and outputting the third sample of iron disilicide characterized by the second particle size and greater than about 90% of the beta phase entity.

[0012]

Many benefits are achieved by ways of present invention. For example, the present invention uses a commercial source of iron disilicide as a starting material to form substantially pure beta phase iron disilicide. The substantially pure beta phase iron disilicide can be further processed to form iron disilicide of desired characteristics, such as particle size, bandgap, resistivity, carrier mobility, carrier density, and others. Additionally, the present method uses environmentally friendly materials that are non-toxic. Depending on the embodiment, one or more of the benefits can be achieved. These and other benefits will be described in more detailed throughout the present specification and particularly below.

BRIEF DESCRIPTION OF THE DRAWINGS

[0013]

FIG. 1 is a simplified flow diagram illustrating a method of forming beta phase iron disilicide according to an embodiment of the present invention.

[0014]

FIG. 2-6 are simplified diagrams illustrating a method of forming beta phase iron disilicide according to an embodiment of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0015]

According to embodiments of the present invention, a method and a system for forming semiconductor materials for photovoltaic applications is provided. More particularly, the present invention provides a method and structure for processing semiconductor materials used for the manufacture of photovoltaic devices. Merely by way of example, the method has been used to provide beta iron disilicide for photovoltaic application. But it would be recognized that the present invention has a much broader range of applicability.

[0016]

FIG. 1 is a simplified flow diagram 100 illustrating a method for forming a sample of beta phase iron disilicide according to an embodiment of the present invention. The method may be summarized as follow:

The above sequence of steps provides a method of forming a sample of iron disilicide comprising substantially beta phase iron disilicide according to an embodiment of the present invention. As shown the method uses a combination of steps, including a thermal process to convert the alpha phase and the epsilon phase iron disilicide into beta phase iron disilicide. Further, the method uses a grinding process to form the sample of iron disilicide comprising substantially beta phase iron disilicide of desired particle size. Merely by way of example, the present method has been used in fabricating photovoltaic devices. But it should be recognized that the present invention has a much broader range of applicability.

[0018]

FIG. 2 is a simplified diagram of a first sample of iron disilicide 202 according to an embodiment of the present invention. The first sample of iron disilicide is commercially available, for example from sources such as Alfa-AESAR of Massachusetts, USA. The first sample of iron disilicide comprises at least alpha phase iron disilicide, beta phase iron disilicide, and epsilon phase iron silicide. The first sample of iron disilicide comprises about 5% to about 20% of the alpha phase entity, about 30% to about 75% of the beta phase entity, and about 5% to about 20% of the epsilon phase entity. Of course there can be other variations, modifications, and alternatives.

[0019]

Referring to FIG. 3, a simplified diagram illustrating a method of forming a sample of beta phase iron disilicide is shown. The diagram is merely an example and should not unduly limit the claims herein. One skilled in the art would recognize other variations, modifications, and alternatives. As shown, a first sample of iron disilicide 304 is provided in a chamber 302. In a specific embodiment, the first sample of iron disilicide is maintained in an inert gas environment within the chamber. The inert environment can be provided using, for example, nitrogen, argon, helium, and the like. As shown, the first sample of iron disilicide is subjected to a thermal process 306 while maintaining in the inert environment to form a second sample of iron disilicide. In a specific embodiment, the thermal process is provided at a temperature ranging from about 700 Degree Celsius to about 800 Degree Celsius for a time period of about 16 hours to about 17 hours. In an alternative embodiment, the thermal process can be provided at a temperature ranging from about 800 Degree Celsius to about 850 Degree Celsius for a time period of about 16 hours to about 18 hours. The thermal process converts the alpha phase iron disilicide and the epsilon phase iron silicide to the beta phase entity. The second sample of iron disilicide comprises substantially beta iron disilicide. In a specific embodiment, the second sample of iron disilicide comprises greater than about 90 percent of beta iron disilicide. In a specific embodiment, the second sample of iron disilicide is characterized by a particle size ranging from about 1 micron to about 20 microns. Of course there can be other variations, modifications, and alternatives.

[0020]

The method includes allowing the second sample of iron disilicide to cool to about room temperature. In a specific embodiment, the cooled second sample of iron disilicide is mixed with a suitable organic solvent to form a first mixture of material 402 as shown in FIG. 4. Such organic solvent may include alkanes (such as octane), or alcohols (such as isopropyl alcohol) among others. In a specific embodiment, the first mixture of material including the second sample of iron disilicide, which comprises greater than 90 percent beta phase iron disilicide, is subjected to a grinding process as shown in FIG. 5. The grinding process uses, for example, a ball milling technique in a preferred embodiment. Other grinding processes may also be used. In a specific embodiment, the ball milling technique uses using a plurality of spheres 502. The plurality of spheres may be metal balls or ceramic balls depending on the application. In a specific embodiment, the plurality of spheres are ceramic balls made of zirconium dioxide. Each of the plurality of spheres has a diameter of about 3 mm in a specific embodiment. The first mixture of material, including the second sample of iron disilicide and the plurality of ceramic balls are provided in a suitable vessel. Example of such vessel may include zirconium dioxide coated stainless steel jar from Restsch, Haan, Germany. In a specific embodiment, the vessel containing the first mixture of material and a plurality of zirconium dioxide balls is loaded into a rotating planetary ball mill, provided also by Restsch, Haan, Germany. Depending on the embodiment, milling time ranges from about 15 hours to about 30 hours. Additionally, depending upon the solvent and other conditions, the jar may develop an internal pressure that may be reduced by stopping the ball mill, resting the system for about 1 hour, then continuing the milling process. Of course there can be other modifications, variations, and alternatives. This embodiment uses a stainless steel jar coated with zirconium dioxide (Retsch) as the mixing vessel. The jar is filled with about 50 grams of 3 mm diameter zirconium dioxide balls, 20 grams of the second sample of iron disilicide, and 15 grams of a suitable solvent such as octane. The jar is then loaded into a rotating planetary ball mill (Retsch) and milled for about 15 to 30 hours at a speed of 400 to 600 rpm. Depending upon the solvent and other conditions, the jar may develop an internal pressure that may be reduced by stopping the ball mill, resting the system for about 1 hour, then continuing the milling process.

[0021]

As shown in FIG. 6, the method removes the organic solvent in the first mixture of material using a drying process 602 and forms a third sample of iron disilicide 604. The drying process can include a vacuum process or a heating process, or a combination to evaporate the organic solvent from the first mixture of material. In a specific embodiment, the third sample of iron disilicide comprises at least 95 percent of beta iron phase disilicide. A substantially uniform particle size 606 of about 1 micron to about 2 micron characterizes the third sample of iron disilicide. In a specific embodiment, the third sample of iron disilicide has a desired semiconductor characteristic with a bandgap ranging from 0.8 eV to 0.9 eV. Of course there can be other variations, modifications, and alternatives.

[0022]

It is also understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to persons skilled in the art and are to be included within the spirit and purview of this application and scope of the appended claims.