ABSTRACTPetrify berangkal kapur is an Industrial waste resulting from calcifies production thatsometime deteriorate environment condition. It is possible to exploit it as ossifyingmaterials for road e.g. Rigid pavement, but only a few has been implemented, because of its limitation reason as petrify berangkal kapur. This research was conducted in a way tostudy the properties of petrify berangkal kapur / calcify waste as concretes aggregate aswell as the properties of no fines concrete made of petrify berangkal kapur aggregate. Inthis research, the specimen tested were concrete cylinder of 15 cm diameter and height of 30 cm, the water /cement ratio was 0,40, the variation of aggregate/cement ratio was 6variations, they were 1:5, 1:6, 1:7, 1:8, 1:9, and 1:10, the technical properties of no finesconcrete to be examined were : specific gravity, cavity volume, and strength ness, Testspecimen was conducted at 28 days age of concrete. The experimental result shows, that ingeneral petrify berangkal kapur is favorable to be used for no-fines concrete aggregates.Greater amount of cement has to be used to make no-fines concrete of greater specificgravity, and strength ness. The cavities volumes were tend to minimize. The petrifyberangkal kapur is unfavorable as a light weight aggregates, because of owning to itsspecific gravity that’s nearly 2, 5. The most efficient usage of cement in concrete of petrifies berangkal kapur aggregates were reached aggregate/cement ratio of 1:6, and theresult the strength ness of more than 9 Map. The implementation of developing researchand design of no-fines concrete will be conducted in Skill Training program and planning.