Just got my first sixbanger as well so can add little to GP100man's excellent post. My Lee seemed to take awhile getting up to temp so I'm looking for a hot plate to add to my casting setup. These moulds seem to like to run pretty hot but need cooling down from time to time also, I keep a damp towel around and press the bottom of the mould against it when it gets too hot.

__________________
Life Member NRA, TSRA
Smokeless powder is a passing fad! -Steve Garbe
I hate rude behavior in a man. I won't tolerate it. -Woodrow F. Call Lonesome Dove
My favorite recipes start out with a handful of used wheelweights.

I am using cast iron moulds, I have found that if you heat the mould with a propane torch you will get usable bullets a lot quicker. I use an old 10lb pot and You don't get many over a hundred before the pot gets low and has to be refilled.

Prewarming is key. I use a coleman camp stove during casting and prewarm right in the flame. Run your melt a little on the "cool" side and your mold HOT with plenty of the heat on the sprew plate. Lots of pretty boolits quick that way.

__________________
"Why is is called Common Sense when it seems so few actually possess it?"

Also I recommend just puttin the mold in a boiling pot of water for 10 min. to get all the machining lube from the pores of the aluminum . well most of it anyways .

The above WITH some dawn or other dishwashing soap.

Also, start with the two cavities nearest the hinge bolt for the sprue plate. Cast those a couple of times, then go to 3 a couple more, then to 4-5-6. If your mold is not up to casting temp, pouring all 6 cavities may result in breaking the cam lever of the sprue cutter when trying to shear all 6 at once, ask me how I know!?

Now, It wasn't me, I borrowed the mold to a buddy, he didn't know it would do that. Lee replaced the cam lever, in fact they sent me 2 of them.

Be real careful with using a propane flame on an aluminum mold. You could easily melt the al.

__________________
The more people I meet, the more I love my dog

They're going to get their butts kicked over there this election. How come people can't spell and use words correctly?

Well like the others I have found out there are a few things to getting a 6-banger up and running.

I usually set the mold on top of my pot while it's heating up, then start out by pouring the first three holes, then allowing the boolits to sit in the mold and spread the heat a few seconds after cutting off the sprue. Then as mentioned move a hole at a time until everything is up to a good temp.

Speaking of temps, I purchased a pot thermometer as well as a little digital one that inserts into the end of the mold via a drilled hole. This has helped out dramatically in the consistency of my boolits, in both less numbers of throw backs but also in weight. It took a bit of playing around but I have the temps for my alloy and mold recorded so it only takes a couple of pours and it's a done deal.

The first link is a to a pretty informative thread. It did show me that the temp will effect the weights, and that a constant pressure on the handles will as well. Nothing overly scientific, but it has helped me to narrow down a few things I was not paying attention to.

Yep, broke a handle as well, and it wasn't hard to do, it went with very little effort and I was pretty much like ***. But like mentioned Lee was understanding and shot me two new ones to replace it ASAP. Luckily I had several so I simply pulled off one of the others and went on with my business.

I bought a six cavity bullet mould from lee and cast my first bullets with it, before I got it figured out I was about ready to loose my religion. I finally found that if I ran the alloy a lot hotter than normal it worked well.
They are supposed to be tumble lube but mike at .358-359 and for a 9mm that is a little large, I am looking for .356 so I will order a sizer, I haven't made up my mind which way to go Lee or Lyman, I have an old 450 lubesizer.

I really like the Lee sizer, figure it and the TL boolits are made for each other, bottle of LLA included makes it pretty hard to beat!
I still use my Lyman for BP stuff but really like the TL process for smokeless.

__________________
Life Member NRA, TSRA
Smokeless powder is a passing fad! -Steve Garbe
I hate rude behavior in a man. I won't tolerate it. -Woodrow F. Call Lonesome Dove
My favorite recipes start out with a handful of used wheelweights.

This email link is to reach site administrators for assistance, if you cannot access TFL via other means. If you are a TFL member and can access TFL, please do not use this link; instead, use the forums (like Questions, Suggestions, and Tech Support) or PM an appropriate mod or admin.

If you are experiencing difficulties posting in the Buy/Sell/Trade subforums of TFL, please read the "sticky" announcement threads at the top of the applicable subforum. If you still feel you are qualified to post in those subforums, please contact "Shane Tuttle" (the mod for that portion of TFL) via Private Message for assistance.

This email contact address is not an "Ask the Firearms Expert" service. Such emails will be ignored. If you have a firearm related question, please register and post it on the forums.