An adsorbent for oral administration, characterized by comprising a surface-modified spherical activated carbon, having a diameter of 0.01 to 1 mm, a specific surface area determined by Langmuir's adsorption equation of 1000 m.sup.2/g or more, a total amount of acidic groups of 0.40 to 1.00 meq/g, a total amount of basic groups of 0.40 to 1.10 meq/g, and a diffraction intensity ratio, an R value, determined by equation (1) of 1.4 or more. The adsorbents for oral administration exhibit a useful selective adsorbability; that is, a lesser adsorbability of useful substances, and a greater adsorbability of toxic substances, in a body.

Claim:

The invention claimed is:

1. An adsorbent for oral administration, comprising a spherical activated carbon, wherein a diameter is 0.01 to 1 mm, a specific surface area determined by Langmuir'sadsorption equation is 1000 m.sup.2/g or more, and a diffraction intensity ratio, an R value, determined by an equation (1): R=(I.sub.15-I.sub.35)/(I.sub.24-I.sub.35) (1) wherein I.sub.15 is a diffraction intensity when a diffraction angle (2.theta.) ofan X-ray diffractometry is 15.degree., I.sub.35 is a diffraction intensity when a diffraction angle (2.theta.) of an X-ray diffractometry is 35.degree., and I.sub.24 is a diffraction intensity when a diffraction angle (2.theta.) of an X-raydiffractometry is 24.degree., is 1.4 or more.

2. The absorbent for oral administration according to claim 1, wherein a volume of pores having a diameter of 20 to 1000 nm is 0.1 mL/g or less.

3. The absorbent for oral administration according to claim 1, wherein a volume of pores having a diameter of 7.5 to 15000 nm is less than 0.25 mL/g.

4. The absorbent for oral administration according to claim 1, wherein the spherical activated carbon is prepared from the thermosetting resin, as a carbon source.

5. The absorbent for oral administration according to claim 1, wherein the spherical activated carbon is prepared from the thermosetting resin having a carbonization yield of 40% by weight or more by a heat-treatment at 800.degree. C. in anatmosphere of non-oxidative gas, as a carbon source.

6. An adsorbent for oral administration, comprising a surface-modified spherical activated carbon, wherein a diameter is 0.01 to 1 mm, a specific surface area determined by Langmuir's adsorption equation is 1000 m.sup.2/g or more, a totalamount of acidic groups is 0.40 to 1.00 meq/g, a total amount of basic groups is 0.40 to 1.10 meq/g, and a diffraction intensity ratio, an R value, determined by an equation (1): R=(I.sub.15-I.sub.35)/(I.sub.34-I.sub.35) (1) wherein I.sub.15 is adiffraction intensity when a diffraction angle (2.theta.) of an X-ray diffractometry is 15.degree., I.sub.35 is a diffraction intensity when a diffraction angle (2.theta.) of an X-ray diffractometry is 35.degree., and I.sub.24 is a diffraction intensitywhen a diffraction angle (2.theta.) of an X-ray diffractometry is 24.degree., is 1.4 or more.

7. The absorbent for oral administration according to claim 6, wherein a volume of pores having a diameter of 20 to 1000 nm is 0.1 mL/g or less.

8. The absorbent for oral administration according to claim 6, wherein a volume of pores having a diameter of 7.5 to 15000 nm is less than 0.25 mL/g.

9. The absorbent for oral administration according to claim 6, wherein the spherical activated carbon is prepared from a thermosetting resin, as a carbon source.

10. The absorbent for oral administration according to claim 6, wherein the surface-modified spherical activated carbon is prepared from the thermosetting resin having a carbonization yield of 40% by weight or more by a heat-treatment at800.degree. C. in an atmosphere of non-oxidative gas, as a carbon source.

Description:

TECHNICAL FIELD

The present invention relates to an adsorbent for oral administration comprising a spherical activated carbon having a specific pore structure, and an adsorbent for oral administration comprising a surface-modified spherical activated carbonprepared by oxidizing and reducing the spherical activated carbon and having a similar specific pore structure.

The adsorbent for oral administration, according to the present invention, exhibits a selective adsorbability, that is, a high adsorbability of harmful toxins, despite a low adsorbability of useful components such as digestive enzymes in a body. Further, the adsorbent has a specific pore structure, and thus, has a greatly improved selective adsorbability in comparison with that of a conventional adsorbent for oral administration. Therefore, the adsorbent for oral administration, according tothe present invention, is effective for the treatment of a patient suffering from a liver or renal disease.

BACKGROUND ART

In patients suffering with a lack of a renal function or a liver function, harmful toxic substances are accumulated or formed in bodies, such as blood, with a progress of a disorder of the organ functions, and thus an encephalopathia occurs, suchas a disturbance of consciousness or uremia. Yearly, there is a growing number of such patients, and therefore, the development of an organ-substitute apparatus or medicament having a function to remove toxic substances from bodies, in place of suchdefective organs, has become a serious problem. A method for removing toxic substances by hemodialysis as an artificial kidney is prevalent. Nevertheless, the hemodialysis-based artificial kidney requires a special apparatus, and thus, a skilledspecialist is required from a safe operation standpoint. Further, blood must be taken from a patient's body, and thus, there are disadvantages in that patients must bear high physical, mental and economic burdens. Accordingly, hemodialysis is notsatisfactory.

Recently, as a means of remedying the above disadvantages, an oral adsorbent which can be orally administered and cure a disorder of renal and liver functions has received considerable attention. Specifically, an adsorbent disclosed in JapaneseExamined Patent Publication (Kokoku) No. 62-11611 comprises a porous spherical carbonaceous substance having particular functional groups (hereinafter referred to as a surface-modified spherical activated carbon); having a high safety factor and stableto a body; and having a useful selective adsorbability, that is, an excellent adsorbability of harmful substances in the presence of a bile acid in an intestine, and a low adsorbability of useful substances such as digestive enzymes in the intestine. For these reasons, the oral adsorbent is widely and clinically used for a patient suffering from a disorder of a liver or renal function, as an adsorbent having few side effects such as constipation. The above adsorbent disclosed in Japanese ExaminedPatent Publication (Kokoku) No. 62-11611 was prepared by forming a spherical activated carbon from a pitch such as a petroleum pitch as a carbon source, and then carrying out an oxidizing treatment and a reducing treatment.

DISCLOSURE OF THE INVENTION

The inventors of the present invention engaged in intensive research to develop an adsorbent for oral administration exhibiting a greater selective adsorbability than that of the above-mentioned oral adsorbent comprising the conventional porousspherical carbonaceous substance prepared by forming a spherical activated carbon from a pitch and oxidizing and reducing the activated carbon, and surprisingly, found that a spherical activated carbon prepared from a thermosetting resin as a carbonsource, even without the oxidizing and reducing treatments, exhibits an excellent selective adsorbability; that is, on one hand, an excellent adsorbability of .beta.-aminoisobutyric acid which is one of the uremic substances in a body, and on the otherhand, a low adsorbability of useful substances, for example, digestive enzymes, such as .alpha.-amylase, and that a level of the selective adsorbability thereof is superior to that of the adsorbent disclosed in Japanese Examined Patent Publication(Kokoku) No. 62-11611. Because the above-mentioned spherical activated carbon prepared from the thermosetting resin as a carbon source exhibits an excellent adsorbability of .beta.-aminoisobutyric acid, it is presumed that the above-mentioned sphericalactivated carbon has an excellent adsorbability of other toxic substances having a molecular weight similar to that of .beta.-aminoisobutyric acid, for example, octopamine or .alpha.-aminobutyric acid, or dimethylamine, aspartic acid, or arginine whichis a toxic substance or a precursor thereof in a renal disease, or other water-soluble basic or ampholytic substances.

It was thought that the conventional porous spherical carbonaceous substance, that is, the surface-modified spherical activated carbon used for the adsorbent disclosed in Japanese Examined Patent Publication (Kokoku) No. 62-11611, began toexhibit the selective adsorbability as above, after functional groups were introduced by the oxidizing and reducing treatments of the spherical activated carbon prepared from a pitch. Therefore, it is surprising that the spherical activated carbon priorto the oxidizing and reducing treatments exhibit a selective adsorbability, and the adsorbability per se is superior to that of the conventional adsorbent for oral administration.

Further, the present inventors found that the useful selective adsorbability; that is, on one hand, an excellent adsorbability of .beta.-aminoisobutyric acid which is one of the uremic substances in a body, and on the other hand, a lowadsorbability of useful substances, for example, digestive enzymes, such as .alpha.-amylase, is improved in a surface-modified spherical activated carbon prepared by oxidizing and reducing the above spherical activated carbon, in comparison with theadsorbent disclosed in Japanese Examined Patent Publication (Kokoku) No. 62-11611. Therefore, it is presumed that the surface-modified spherical activated carbon has a greater adsorbability of other toxic substances having a molecular weight similar tothat of .beta.-aminoisobutyric acid, for example, octopamine or .alpha.-aminobutyric acid, or dimethylamine, aspartic acid, or arginine which is a toxic substance or a precursor thereof in a renal disease, or other water-soluble basic or ampholyticsubstances.

The present invention is based on the above findings.

Accordingly, the present invention relates to an adsorbent for oral administration, characterized by comprising a spherical activated carbon, wherein a diameter is 0.01 to 1 mm, a specific surface area determined by Langmuir's adsorption equationis 1000 m.sup.2/g or more, and a diffraction intensity ratio, an R value, determined by an equation (1): R=(I.sub.15-I.sub.35)/(I.sub.24-I.sub.35) (1) wherein I.sub.15 is a diffraction intensity when a diffraction angle (2.theta.) of an X-raydiffractometry is 15.degree., I.sub.35 is a diffraction intensity when a diffraction angle (2.theta.) of an X-ray diffractometry is 35.degree., and I.sub.24 is a diffraction intensity when a diffraction angle (2.theta.) of an X-ray diffractometry is24.degree., is 1.4 or more.

The present invention also relates to an adsorbent for oral administration, characterized by comprising a surface-modified spherical activated carbon, wherein a diameter is 0.01 to 1 mm, a specific surface area determined by Langmuir's adsorptionequation is 1000 m.sup.2/g or more, a total amount of acidic groups is 0.40 to 1.00 meq/g, a total amount of basic groups is 0.40 to 1.10 meq/g, and a diffraction intensity ratio, an R value, determined by an equation (1):R=(I.sub.15-I.sub.35)/(I.sub.24-I.sub.35) (1) wherein I.sub.15 is a diffraction intensity when a diffraction angle (2.theta.) of an X-ray diffractometry is 15.degree., I.sub.35 is a diffraction intensity when a diffraction angle (2.theta.) of an X-raydiffractometry is 35.degree., and I.sub.24 is a diffraction intensity when a diffraction angle (2.theta.) of an X-ray diffractometry is 24.degree., is 1.4 or more.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows an X-ray diffraction pattern of a surface-modified spherical activated carbon of the prior art (curve A), an X-ray diffraction pattern of a paste product of a surface-modified spherical activated carbon of the prior art (curve B),and an X-ray diffraction pattern of a surface-modified spherical activated carbon used as the adsorbent for oral administration of the present invention (curve C).

FIG. 2 is a micrograph (magnification: .times.50) illustrating a surface structure of a surface-modified spherical activated carbon of the present invention obtained by a scanning electron microscope.

FIG. 3 is a micrograph (magnification: .times.200) illustrating a cross sectional structure of sectional structure of a surface-modified spherical activated carbon of the present invention obtained by a scanning electron microscope.

FIG. 4 is a micrograph (magnification: .times.50) illustrating a surface structure of a surface-modified spherical activated carbon of the prior art obtained by a scanning electron microscope.

FIG. 5 is a micrograph (magnification: .times.200) illustrating a cross sectional structure of sectional structure of a surface-modified spherical activated carbon of the prior art obtained by a scanning electron microscope.

FIG. 6 is a graph showing the results of the investigation of the effect of the adsorbent for oral administration of the present invention on serum creatinine.

FIG. 7 is a graph showing the results of the investigation of the effect of the adsorbent for oral administration of the present invention on blood urea nitrogen.

FIG. 8 is a graph showing the results of the investigation of the effect of the adsorbent for oral administration of the present invention on creatinine clearance.

FIG. 9 is a graph showing the results of the investigation of the effect of the adsorbent for oral administration of the present invention on an amount of urine protein excreted.

FIG. 10 is a graph showing the results of the investigation of the effect of the adsorbent for oral administration of the present invention on ICG (Indocyanine green).

FIG. 11 is a graph showing the results of the investigation of the effect of the adsorbent for oral administration of the present invention on GOT (glutamic-oxaloacetic transaminase).

FIG. 12 is a graph showing the results of the investigation of the effect of the adsorbent for oral administration of the present invention on GPT (glutamic-pyruvic transaminase).

BEST MODE FOR CARRYING OUT THE INVENTION

The spherical activated carbon or the surface-modified spherical activated carbon used as the adsorbent for oral administration of the present invention has a diffraction intensity ratio (an R value) calculated from an equation (1) of 1.4 ormore, as above-mentioned.

When the surface-modified spherical activated carbon prepared by a conventional method disclosed in Examples 1 to 3 in Japanese Examined Patent Publication (Kokoku) No. 62-11611 is investigated by a powder X-ray diffractometry, an X-raydiffraction pattern having the same tendency as that of the curve A shown in FIG. 1 is obtained. The curve A per se is an X-ray diffraction pattern of the surface-modified spherical activated carbon prepared in Comparative Example 1, as mentioned below. As apparent from the curve A, a diffraction peak corresponding to a 002 plane is observed at the diffraction angle (2.theta.) of around 20.degree. to 30.degree.. The intensity is lowered by a decrease of the diffraction X-ray in the range where thediffraction angle (2.theta.) is higher than 30.degree.. On the other hand, in the range where the diffraction angle (2.theta.) is lower than 20.degree., a strong X-ray is observed even in the range where the diffraction angle (2.theta.) is lower than15.degree., that is, in the range where a diffraction X-ray from 002 plane is rarely observed. Further, when the surface-modified spherical activated carbon prepared by a conventional method disclosed in Examples 1 to 3 in Japanese Examined PatentPublication (Kokoku) No. 62-11611 is investigated by a powder X-ray diffractometry after water is adsorbed, an X-ray diffraction pattern having the same tendency same as that of the curve B shown in FIG. 1 is obtained. The curve B per se is an X-raydiffraction pattern of the surface-modified spherical activated carbon prepared in Comparative Example 1, as mentioned below, after water was adsorbed. As apparent from the curve B, the X-ray intensity of the curve B is considerably lowered in the lowangular range in comparison with the curve A. This phenomenon can be interpreted such that the X-ray intensity in the low angular range is influenced by fine pores, and an X-ray scattering intensity is lowered by an adsorption of water into pores.

As shown in Examples, as mentioned below, on the other hand, in the case of the spherical activated carbon or the surface-modified spherical activated carbon prepared by the method found by the present inventors, an X-ray diffraction patternhaving the same tendency as that of the curve C shown in FIG. 1 is generally obtained, in the condition that water is not adsorbed. The curve C per se is an X-ray diffraction pattern of the surface-modified spherical activated carbon prepared in Example1, as mentioned below. That is, a scattering intensity of the curve C in the low angular range where the diffraction angle (2.theta.) is 15.degree. or less is apparently strong in comparison with that of the curve A. Each of the curves A, B, and C inFIG. 1 is standardized so that the diffraction intensity at the diffraction angle (2.theta.) of 24.degree. becomes 100.

It is apparent that a porous product with an X-ray diffraction pattern having the same tendency as that of the curve A shown in FIG. 1 has a pore structure different from that of a porous product with an X-ray diffraction pattern having the sametendency as that of the curve C shown in FIG. 1. Further, it is apparent from the comparison of the curve A and the curve B that a scattering intensity observed in a low angular range in the X-ray diffractometry of the surface-modified sphericalactivated carbon is reflected from the pore structure, and the product having a stronger scattering intensity has more pores. In the relationship between the scattering angle and the pore diameter, it is assumed that the higher the scattering angle, thefiner the pore diameter. In order to analyze a pore structure, a method for determining a pore distribution by an adsorption is generally known. In many cases, however, it is difficult to accurately analyze the pore structure in view of differences ina size or shape of the pores, a size of the substances to be adsorbed, adsorbing conditions, and so on. It is an assumption of the present inventors that the scattering intensity around 15.degree. is only slightly influenced by a diffraction X-ray froma 002 plane, influenced by a scattering from the fine pores, and becomes an index indicating the presence of ultra-fine pores which are difficult to find by the adsorption method, and that the presence of such fine pores is advantageous for adsorbing theharmful substance, .beta.-aminoisobutyric acid. That is, the present inventors assume that the higher the scattering intensity at the diffraction angle (2.theta.) around 15.degree., the more effective the adsorption of the harmful substance,.beta.-aminoisobutyric acid, for the spherical activated carbon or the surface-modified spherical activated carbon.

Further, as shown in Examples, as mentioned below, the present inventors experimentally confirmed that the spherical activated carbon or the surface-modified spherical activated carbon having an X-ray diffraction pattern with the same tendency asthat of the curve C shown in FIG. 1 exhibits a greater selective adsorbability in comparison with the conventional spherical activated carbon or the conventional surface-modified spherical activated carbon having an X-ray diffraction pattern with thesame tendency as that of the curve A shown in FIG. 1.

In the present specification, therefore, the spherical activated carbon or the surface-modified spherical activated carbon is defined by the diffraction intensity ratio, the R value, calculated by the equation (1), to clarify the aboverelationship. In the above equation (1), I.sub.15 is the diffraction intensity when a diffraction angle (2.theta.) of an X-ray diffractometry is 15.degree.; that is, in a range where a difference between the diffraction intensity of curve A and that ofcurve C is increased; I.sub.24 is a diffraction intensity when a diffraction angle (2.theta.) of an X-ray diffractometry is 24.degree., that is, in a range where a difference between the diffraction intensity of curve A and that of curve C is decreased;and I.sub.35 is a diffraction intensity when a diffraction angle (2.theta.) of an X-ray diffractometry is 35.degree., and is used to correct a measurement error between the test samples due to background disturbances.

Therefore, a diffraction intensity ratio, an R value, which is calculated by the equation (1) is R=t/u, for the curve A, and R=s/v for the curve C.

The present inventors confirmed that a diffraction intensity ratio, an R value, of each of the conventionally known typical surface-modified spherical activated carbons for oral administration is less than 1.4, and did not find any knownorally-administrating surface-modified spherical activated carbon having a diffraction intensity ratio, an R value, of 1.4 or more, to the knowledge of the present inventors. Further, as shown in Examples, as mentioned below, the surface-modifiedspherical activated carbon having a diffraction intensity ratio, an R value, of 1.4 or more, has an improved adsorbability of .beta.-aminoisobutyric acid in comparison with the surface-modified spherical activated carbon having a diffraction intensityratio, an R value, of less than 1.4, and thus it is apparent that the surface-modified spherical activated carbon having a diffraction intensity ratio, an R value, of 1.4 or more, is useful for the adsorbent for oral administration having an improvedselective adsorbability of toxic substances.

The diffraction intensity ratio, the R value, determined by an equation (1) for the spherical activated carbon or the surface-modified spherical activated carbon used for the adsorbent for oral administration according to the present invention ispreferably 1.4 or more, more preferably 1.5 or more, most preferably 1.6 or more.

The inventors of the present invention found that the spherical activated carbon or the surface-modified spherical activated carbon having a diffraction intensity ratio, an R value, of 1.4 or more can be prepared, using a thermosetting resin as acarbon source, instead of a pitch used as a carbon source for the conventional adsorbent for oral administration. Alternatively, it can be prepared from a pitch as a carbon source as the conventional adsorbent for oral administration, by developing across-linked structure during the treatment imparting infusibility, and disrupting the arrangement of the carbon hexagon network surface.

In the first place, a preparing method using a thermosetting resin as a carbon source will be described.

A spherical material of a thermosetting resin is initially activated at 700 to 1000.degree. C. in reactive gas stream with carbon (for example, steam or carbon dioxide gas) to obtain the spherical activated carbon used as the adsorbent for oraladministration of the present invention. The term spherical "activated carbon" as used herein means a porous product prepared by a heat-treatment of a carbon precursor such as a spherical thermosetting resin, and subsequent activation, and having aspherical shape and a specific surface area of 100 m.sup.2/g or more, preferably 1000 m.sup.2/g or more in the present invention.

If the spherical material of a thermosetting resin is softened by the heat-treatment and changed to an aspheric shape, or fused together by the heat-treatment, the softening can be inhibited by an oxidation at 150.degree. C. to 400.degree. C.in an atmosphere containing oxygen as a treatment imparting infusibility, before the activation as above.

Further, if many pyrolysis gases or the like are generated by the heat-treatment of the spherical thermosetting resin, pyrolysis products may be removed in advance by accordingly carrying out a pre-calcination, prior to the treatment impartinginfusibility.

In order to further improve the selective adsorbability of the spherical activated carbon of the present invention, the resulting spherical activated carbon is subsequently oxidized at 300 to 800.degree. C., preferably 320 to 600.degree. C., inan atmosphere containing 0.1 to 50 vol %, preferably 1 to 30 vol %, particularly preferably 3 to 20 vol % of oxygen, and then reduced by a heat-reaction at 800 to 1200.degree. C., preferably 800 to 1000.degree. C., in an atmosphere of non-oxidativegas, to thereby obtain the surface-modified spherical activated carbon used as the adsorbent for oral administration according to the present invention. The term "surface-modified spherical activated carbon" as used herein means a porous productprepared by the oxidizing and reducing treatments of the spherical activated carbon as above, wherein acidic and basic sites are added in a well-balanced manner on the surface of the spherical activated carbon to thereby improve an adsorbability ofharmful substances in an intestine.

A particle diameter of the spherical product of a thermosetting resin used as a starting material is preferably about 0.02 to 1.5 mm.

It is important for the thermosetting resin used as the starting material that a spherical product can be formed, and it is not fused or softened, or the shape is not changed, by a heat-treatment at a temperature of 500.degree. C. or less. Athermosetting resin which can avoid a fusion oxidation by the treatment imparting infusibility, such as an oxidation treatment, can be used.

A thermosetting resin which can obtain a high carbonization yield by a heat-treatment is preferable as a starting material. If the carbonization yield is low, a strength of the spherical activated carbon becomes low. Further, undesirable poresare formed and a bulk density of the spherical activated carbon is lowered, and thus, a specific surface area per volume is lowered. Therefore, a volume to be orally administered is increased, and thus, a problem arises in that an oral administrationbecomes difficult. Accordingly, a thermosetting resin having a higher carbonization yield is preferable. A yield by a heat-treatment at 800.degree. C. in an atmosphere of non-oxidative gas is preferably 40% by weight or more, more preferably 45% byweight or more.

The thermosetting resin used as a starting material may be, for example, a phenolic resin, such as a novolak phenolic resin, a resol phenolic resin, a novolak alkylphenolic resin, or a resol alkylphenolic resin, or a furan resin, a urea resin, amelamine resin, or an epoxy resin. A copolymer of divinylbenzene and styrene, acrylonitrile, acrylic acid, or methacrylic acid may be used as the thermosetting rein.

Further, an ion-exchange resin may be used as the thermosetting resin. Generally, an ion-exchange resin comprises a copolymer of divinylbenzene and styrene, acrylonitrile, acrylic acid, or methacrylic acid, that is, a thermosetting resin, andessentially has a structure wherein ion-exchange groups are bonded to a copolymer matrix having a three-dimensional network skeleton. The ion-exchange resin is generally classified, with respect to the kinds of ion-exchange groups, into a stronglyacidic ion-exchange resin having sulfonic acid groups, a weakly acidic ion-exchange resin having carboxylic or sulfonic acid groups, a strongly basic ion-exchange resin having quaternary ammonium salts, and a weakly basic ion-exchange resin havingprimary or tertiary amines. In addition, so-called hybrid ion-exchange resin having both acidic and basic ion-exchange groups is included as a special ion-exchange resin. In the present invention, all of the above ion-exchange resins may be used as astarting material, but a phenolic resin is preferably used.

Then, a method for preparing the spherical activated carbon or the surface-modified spherical activated carbon used as the adsorbent for oral administration from a pitch as a carbon source, by developing a cross-linked structure during thetreatment imparting infusibility, and disrupting the arrangement of the carbon hexagon network plane will be described.

First, a dicyclic or tricyclic aromatic compound or a mixture thereof having a boiling point of 200.degree. C. or more is added as an additive to a pitch such as a petroleum pitch or a coal pitch. The whole is heated and mixed, and then shapedto obtain a shaped pitch. The spherical activated carbon or the surface-modified spherical activated carbon is for oral administration, and the raw material must have a sufficient purity from a safety standpoint, and have stable properties.

Thereafter, the shaped pitch is dispersed and granulated in hot water, with stirring, to obtain a microspherical shaped pitch. Further, the additive is extracted and removed from the shaped pitch by a solvent having a low solubility to the pitchbut a high solubility to the additive. The resulting porous pitch is oxidized by an oxidizing agent to obtain a porous pitch having an infusibility to a heat. The resulting infusible porous pitch is treated in a gas flow such as steam or carbon dioxidegas reactive with carbon to obtain the spherical activated carbon.

Then, the resulting spherical activated carbon is oxidized by heating in an atmosphere containing oxygen, and thereafter, reduced in an atmosphere of a non-oxidizable gas to obtain the surface-modified spherical activated carbon used as theadsorbent for oral administration according to the present invention.

In the above method for the preparation, the atmosphere containing oxygen in the particular amount may be pure oxygen, or nitrogen oxides or air as the oxygen source. As the atmosphere inert against carbon, for example, nitrogen, argon or heliummay be used alone or in the form of a mixture thereof.

The purposes of the addition of the aromatic compound to the raw pitch are that a flowability of the raw pitch is enhanced, whereby the granulation thereof is made easier, and the porous pitch is produced by extracting and removing the additivefrom the shaped pitch, whereby a structure control and a calcination of the carbonaceous material by oxidization in the subsequent steps is made easier. As the additive, for example, naphthalene, methylnaphthalene, phenyl-naphthalene,benzyl-naphthalene, methylanthracene, phenanthrene, or biphenyl may be used alone or in a mixture thereof. An amount of the additive added to the pitch is preferably 10 to 50 parts by weight of the aromatic compound with respect to 100 parts by weightof the pitch.

It is preferable that the pitch and the additive are mixed under a melted condition with heating, to achieve a homogeneous mixing. Further, it is preferable that the mixture of the pitch and the additive is shaped to form particles having aparticle size of about 0.01 to 1 mm, to control the particle size (diameter) of the resulting spherical activated carbon or the surface-modified spherical activated carbon. The shaping may be conducted during the melted condition, or by grinding themixture after it has cooled.

A preferable solvent used to extract and remove the additive from the mixture of the pitch and the additive may be, for example, an aliphatic hydrocarbon, such as butane, pentane, hexane, or heptane, a mixture comprising an aliphatic hydrocarbonas a main component, such as naphtha or kerosene, or an aliphatic alcohol, such as methanol, ethanol, propanol, or butanol.

The additive may be removed from the shaped mixture by extracting the additive with the solvent from the shaped mixture of the pitch and the additive, while maintaining the shape. It is assumed that, upon the extraction, through-holes of theadditive are formed in the shaped product, and a shaped pitch having a uniform porosity can be obtained.

Then, the resulting porous shaped pitch is subjected to a treatment imparting non-fusibility, that is, the resulting porous shaped pitch is oxidized by an oxidizing agent, preferably at room temperature to 300.degree. C. to obtain the porousinfusible shaped pitch having a non-fusibility to heat. As the oxidizing agent, for example, oxygen gas (O.sub.2), or a gas mixture prepared by diluting oxygen gas (O.sub.2) with air or nitrogen may be used.

The spherical activated carbon or the surface-modified spherical activated carbon used as the adsorbent for oral administration of the present invention is produced by, for example, the above methods using the thermosetting resin or a pitch as astarting material, and has a diameter of 0.01 to 1 mm. If the diameter of the spherical activated carbon or the surface-modified spherical activated carbon is less than 0.01 mm, an exterior surface area of the spherical activated carbon or thesurface-modified spherical activated carbon is increased, and useful substances such as digestive enzymes are easily adsorbed. That is unfavorable. When the diameter is more than 1 mm, a diffusion distance of toxic substances into the inside of thespherical activated carbon or the surface-modified spherical activated carbon is increased, and an adsorption rate is lowered. That, too, is unfavorable. The diameter is preferably 0.02 to 0.8 mm. The expression that "a diameter is Dl to Du" as usedherein means that a screen passing percentage (%) in a range of a screen opening Dl to Du is 90% or more in a particle-sizes accumulating standard curve prepared in accordance with JIS K 1474, as mentioned below in relation with a method for determiningan average particle diameter.

In the spherical activated carbon or the surface-modified spherical activated carbon used as the adsorbent for oral administration of the present invention, a specific surface area (referred to as "SSA" hereinafter) determined by Langmuir'sadsorption equation is 1000 m.sup.2/g or more. When the spherical activated carbon or the surface-modified spherical activated carbon has an SSA of less than 1000 m.sup.2/g, an adsorbability of toxic substances is unfavorably lowered. The SSA ispreferably 1000 m.sup.2/g or more. The upper limit of the SSA is not particularly limited, but the SSA is preferably 3000 m.sup.2/g or less in view of a bulk density and strength.

In the spherical activated carbon or the surface-modified spherical activated carbon used as the adsorbent for oral administration of the present invention, a pore volume within a scope of specific pore diameters is not particularly limited. Forexample, the above-mentioned Japanese Examined Patent Publication (Kokoku) No. 62-11611 discloses an adsorbent comprising a surface-modified spherical activated carbon wherein a volume of voids having a pore radius of 100 to 75000 angstrom, that is, avolume of pores having a diameter of 20 to 15000 nm, is 0.1 to 1 mL/g. However, in the spherical activated carbon or the surface-modified spherical activated carbon used as the adsorbent for oral administration of the present invention, a volume of poreshaving a diameter of 20 to 15000 nm may be 0.1 to 1 mL/g, or 0.1 mL/g or less. When a volume of pores having a diameter of 20 to 1000 nm is more than 1 mL/g, an adsorbed amount of useful substances, such as digestive enzymes, may be increased. Therefore, a volume of pores having a diameter of 20 to 1000 nm is preferably 1 mL/g or less.

In the spherical activated carbon or the surface-modified spherical activated carbon used as the adsorbent for oral administration of the present invention, a volume of pores having a diameter of 7.5 to 15000 nm is preferably less than 0.25 mL/g,more preferably 0.2 mL/g or less, as a more excellent selective adsorbability is thus obtained.

In a constitution of functional groups of the surface-modified spherical activated carbon, that is, the product prepared by oxidizing and reducing the spherical activated carbon, which is used as the adsorbent for oral administration of thepresent invention, a total amount of acidic groups is 0.40 to 1.00 meq/g, and a total amount of basic groups is 0.40 to 1.10 meq/g. When the constitution of functional groups satisfies the condition that a total amount of acidic groups is 0.40 to 1.00meq/g, and a total amount of basic groups is 0.40 to 1.00 meq/g, the selective adsorbability is improved, and particularly, the adsorbability of harmful substances is favorably enhanced. In the constitution of functional groups, a total amount of acidicgroups is preferably 0.40 to 0.90 meq/g, and a total amount of basic groups is preferably 0.40 to 1.00 meq/g.

When the adsorbent of the present invention is used as an agent for treating or preventing a liver or renal disease, a preferable functional-groups constitution is that the total amount of acidic groups is 0.40 to 1.00 meq/g, the total amount ofbasic groups is 0.40 to 1.10 meq/g, a phenolic hydroxyl group is 0.20 to 0.70 meq/g, and a carboxyl group is 0.15 meq/g or less, and a ratio (a/b) of the total amount of acidic groups (a) to the total amount of basic groups (b) is 0.40 to 2.5, and arelation [(b+c)-d] between the total amount of basic groups (b), the phenolic hydroxyl group (c), and the carboxyl group (d) is 0.60 or more.

Properties of the spherical activated carbon or the surface-modified spherical activated carbon used as the adsorbent for oral administration of the present invention, namely, the average particle diameter, the specific surface area, the porevolume, the total amount of acidic groups, and the total amount of basic groups are measured by the following methods.

(1) An Average Particle Diameter

A particle-sizes accumulating standard curve is prepared in accordance with JIS K 1474 for the spherical activated carbon or the surface-modified spherical activated carbon. The average particle diameter is determined from a screen opening (mm)at an intersection point with a line that is horizontal to an abscissa axis and starts from an intersection point in the particle-sizes accumulating standard curve with a perpendicular line from a 50% point of the abscissa axis.

(2) A Specific Surface Area

An amount of gas adsorbed is measured by a specific surface area measuring apparatus (for example, ASAP2010 manufactured by MICROMERITICS) in accordance with a gas adsorbing method for the spherical activated carbon sample or the surface-modifiedspherical activated carbon sample, and a specific surface area can be calculated by Langmuir's adsorption equation. More particularly, the spherical activated carbon or the surface-modified spherical activated carbon is charged as a sample in a sampletube, and dried under reduced pressure at 300.degree. C. Thereafter, a weight of dried sample is measured. Then, the test tube is cooled to -196.degree. C., and nitrogen is introduced into the test tube, whereby nitrogen is adsorbed to the sphericalactivated carbon sample or the surface-modified spherical activated carbon sample. A relation of a nitrogen partial pressure and an adsorbed amount (absorption-isotherm line) is measured.

Langmuir's plotting is carried out, given that a relative pressure of nitrogen is p, and an adsorbed amount at that time is v(cm.sup.3/g STP). That is, the plotting in a range wherein p is 0.05 to 0.3 is carried out, in the field wherein alongitudinal axis is p/v, and an abscissa axis is p. Given that the gradient at that time is b(g/cm.sup.3), a specific surface area S (unit=m.sup.2/g) can be calculated from the equation:

.times..times..times..times. ##EQU00001## wherein MA denotes a cross-sectional area of a nitrogen molecule, and is 0.162 nm.sup.2. (3) A Pore Volume by a Mercury Press-Injection Method

The pore volume can be measured by a mercury porosimeter (for example, AUTOPORE 9200 manufactured by MICROMERITICS). The spherical activated carbon or the surface-modified spherical activated carbon is charged as a sample in a sample vessel, anddegassed under a pressure of 2.67 Pa or less for 30 minutes. Then, mercury is introduced into the sample vessel, a pressure applied is gradually increased (maximum pressure=414 MPa) to force the mercury into the micropores in the spherical activatedcarbon sample or the surface-modified spherical activated carbon sample. A pore volume distribution of the spherical activated carbon sample or the surface-modified spherical activated carbon sample is measured from a relationship between the pressureand an amount of forced mercury, by equations as mentioned below.

Specifically, a volume of mercury inserted into the spherical activated carbon sample or the surface-modified spherical activated carbon sample while a pressure applied is increased from a pressure (0.06 MPa) corresponding to a pore diameter of22 .mu.m to the maximum pressure (414 MPa) corresponding to a pore diameter of 3 nm is measured. A pore diameter can be calculated as follows. When mercury is forced into a cylindrical micropore having a diameter (D) by applying a pressure (P), asurface tension (.gamma.) of mercury is balanced with a pressure acting on a section of the micropore, and thus, the following equation is held: -.pi.D.gamma. cos .theta.=.pi.(D/2).sup.2P wherein .theta. is a contact angle of mercury and a wall of themicropore. Therefore, the following equation: D=(-4.gamma. cos .theta.)/P is held.

In the present specification, the relationship between the pressure (P) and the pore diameter (D) is calculated by the equation: D=1.27/P given that a surface tension of mercury is 484 dyne/cm, a contact angle of mercury and carbon is130.degree., a unit of the pressure P is MPa, and a unit of the pore diameter D is .mu.m. The volume of pores having a pore diameter of 20 to 1000 nm in the present invention corresponds to a volume of mercury inserted by applying a pressure increasingfrom 1.27 MPa to 63.5 MPa. (4) Diffraction Intensity Ratio, R Value

A spherical activated carbon sample or a surface-modified spherical activated carbon sample is dried at 120.degree. C. for 3 hours under reduced pressure, and charged in an aluminum sample plate, that is, a plate (35.times.50 mm.sup.2; t=1.5 mm)having an opening of 20.times.18 mm.sup.2. Then, diffraction intensities I.sub.15, I.sub.24, and I.sub.35 at diffraction angles (2.theta.) of 15.degree., 24.degree., and 35.degree. are measured by a reflection type x-ray diffractometer method, using aCuK.alpha. ray (wave length, .lamda.=0.15418) monochromatized by a graphite monochrometor, as a radiation source. The conditions of an X-ray generating device and a slit are as follows: voltage applied=40 kV, current=100 mA, divergent slit=1/2.degree.,photo-receiver slit=0.15 mm, and scattering slit=1/2.degree.. The diffraction pattern was not corrected with respect to a Lorentz polarization factor, absorption factor, atomic-scattering factor or the like, but the diffraction angle was corrected,using (111) diffraction line of high-purity silicon powder for a standard substance.

(5) Total Amount of Acidic Groups

The total amount of acidic groups is an amount of NaOH consumed, which may be determined by adding 1 g of the spherical activated carbon sample or the surface-modified spherical activated carbon sample, after being crushed to form particleshaving a size of 200 mesh or less, to 50 mL of a 0.05N NaOH solution; shaking the mixture for 48 hours; then filtering out the spherical activated carbon sample or the surface-modified spherical activated carbon sample; and titrating untilneutralization.

(6) Total Amount of Basic Groups

The total amount of basic groups is an amount of HCl consumed, which may be determined by adding 1 g of the spherical activated carbon sample or the surface-modified spherical activated carbon sample after being crushed to form particles having asize 200 mesh or less, to 50 mL of a 0.05N HCl solution; shaking the mixture for 24 hours; then filtering out the spherical activated carbon sample or the surface-modified spherical activated carbon sample; and titrating until neutralization.

As shown in Examples mentioned as below, the spherical activated carbon or the surface-modified spherical activated carbon used as the adsorbent for oral administration of the present invention exhibits an excellent selective adsorbability, thatis, an excellent adsorbability of exacerbation factors of liver diseases or harmful substances of renal diseases, but a lower adsorbability of useful substances such as digestive enzymes, and therefore, may be used as an adsorbent for oral administrationfor treating or preventing a renal disease or a liver disease.

As the liver disease, there may be mentioned, for example, fulminant hepatitis, chronic hepatitis, viral hepatitis, alcoholic hepatitis, hepatic fibrosis, liver cirrhosis, hepatic cancer, autoimmune hepatitis, drug allergic hepatopathy, primarybiliary cirrhosis, tremor, encephalopathia, dysbolism, or dysfunction. Further, the porous spherical carbonaceous substance can be used in a treatment of a disease caused by toxic substances in a body, such as psychosis.

Further, as shown in Examples, the spherical activated carbon or the surface-modified spherical activated carbon used as the adsorbent for oral administration of the present invention has an excellent adsorbability of .beta.-aminoisobutyric acidwhich is one of the uremic substances in a body, and therefore, may be preferably used as an adsorbent for oral administration for treating or preventing a disease bearing a relationship to or deteriorated by uremic substances, such as a chronic renalfailure or a complicated disease thereof. As the complications of the chronic renal failure, there may be mentioned, for example, a disease of a circulatory system, such as cardiac insufficiency, arrhythmia, hypertension, or ischemic heart disease; avascular lesion, such as arterial sclerosis including vascular calcification, or arteriosclerosis obliterans; a cerebrovascular accident; an anemia, such as renal anemia, or erythropoietin-resistant anemia; bone- or calcium-dysbolism or dialysisosteopathy, such as secondary hyperparathyroidism, aplastic bone, anomalous calcification; a dialysis amyloidosis including amyloid spondylosis; a trophic syndrome; a lipid-dysbolism; or an itch.

Therefore, when the adsorbent for oral administration is used as an agent for treating or preventing a renal disease, it contains the spherical activated carbon or the surface-modified spherical activated carbon as an effective component. Whenthe adsorbent for oral administration according to the present invention is used as an agent for a treatment of a liver or renal disease, a dosage thereof depends on the subject (human or other animal), age, individual differences, disease conditions,and so on. Therefore, in some cases, a dosage outside of the following dosage may be appropriate, but in general, the oral dosage in the case of a human is usually 1 to 20 g of the adsorbent per day, wherein the daily dosage may be divided into three tofour portions. The dosage may appropriately vary with the disease conditions. The formulation may be administered in any form, such as powders, granules, tablets, sugar-coated tablets, capsules, suspensions, sticks, divided packages, or emulsions. Inthe case of capsules, the usual gelatin capsules, or if necessary, enteric capsules may be used. In the case of tablets, the formulations must be broken into the original fine particles inside the body. The adsorbent may be used as a mixture with anelectrolyte-controlling agent, such as an aluminum gel or Kayexalate.

EXAMPLES

The present invention now will be further illustrated by, but is by no means limited to, the following Examples.

In the following Examples, an adsorption test of .alpha.-amylase and an adsorption test of DL-.beta.-aminoisobutyric acid were carried out in accordance with the following methods, and the selective adsorption rate was calculated by the followingmethod.

(1) Adsorption Test of .alpha.-Amylase

The spherical activated carbon sample or the surface-modified spherical activated carbon sample was dried, and 0.125 g of the dried sample was accurately weighed and charged into a conical flask equipped with a ground-in stopper. On the otherhand, 0.100 g of .alpha.-amylase (liquefied type) was accurately weighed and dissolved by adding a phosphate buffer (pH 7.4) to prepare a stock solution having an accurate volume of 1000 mL. The stock solution in an accurate amount of 50 mL was chargedto the conical flask equipped with a ground-in stopper. The flask was shaken at 37.+-.1.degree. C. for 3 hours. The product in the flask was filtered with suction through a 0.65 .mu.m membrane filter. A first filtrate (about 20 mL) was discarded, anda subsequent filtrate (about 10 mL) was taken as a sample solution.

Further, the same procedures were repeated except that only a phosphate buffer (pH 7.4) was used, to obtain a filtrate as a correction solution. The sample solution and the correction solution were analyzed by an absorptiometeric analysis, usinga phosphate buffer (pH 7.4) as a control. The absorbance at a wavelength of 282 nm was measured. A difference between the absorbance of the sample solution and the absorbance of the correction solution was taken as a test absorbance.

A standard curve was prepared by adding the .alpha.-amylase stock solution in an accurate amount of 0 mL, 25 mL, 50 mL, 75 mL, or 100 mL to a measuring flask, adding a phosphate buffer (pH 7.4) to 100 mL, and measuring an absorbance at a wavelength of 282 nm. From the test absorbance and the standard curve, an amount (mg/dL) of .alpha.-amylase remaining in the solution was calculated.

To measure a dependence on an amount of the spherical activated carbon sample or the surface-modified spherical activated carbon sample, the same procedures were repeated except that an amount of the spherical activated carbon sample or thesurface-modified spherical activated carbon sample used was 0.500 g, and the test absorbance was measured and the amount of .alpha.-amylase remaining in the solution was calculated as above.

(2) Adsorption Test of Dl-.beta.-Aminoisobutyric Acid

The spherical activated carbon sample or the surface-modified spherical activated carbon sample was dried, and 2.500 g of the dried sample was accurately weighed and charged into a conical flask equipped with a ground-in stopper. On the otherhand, 0.100 g of DL-.beta.-aminoisobutyric acid was accurately weighed and dissolved by adding a phosphate buffer (pH 7.4) to prepare a stock solution having an accurate volume of 1000 mL. The stock solution in an accurate amount of 50 mL was charged tothe conical flask equipped with a ground-in stopper. The flask was shaken at 37.+-.1.degree. C. for 3 hours. The product in the flask was filtered with suction through a 0.65 .mu.m membrane filter. A first filtrate (about 20 mL) was discarded, and asubsequent filtrate (about 10 mL) was taken as a sample solution.

Then, 0.1 mL of the sample solution was accurately weighed and charged in a test tube. A phosphate buffer (pH 8.0) was added in an accurate amount of 5 mL thereto, and the whole was mixed. Thereafter, a solution prepared by dissolving 0.100 gof fluorescamine in 100 mL of acetone (for a non-aqueous titration) was added in an accurate amount of 1 mL, and the whole was mixed and allowed to stand for 15 minutes. The resulting solution was analyzed by fluorometry, and the fluorescence wasmeasured at an exciting wavelength of 390 nm and a fluorescent wavelength of 475 nm.

A standard curve was prepared by producing 100 mL of a mixture of 0 mL, 15 mL, 50 mL, 75 mL, and 100 mL of the DL-.beta.-aminoisobutyric acid stock solution and the balance of a phosphate buffer (pH 7.4), stirring and filtering the mixture,charging the resulting filtrate in an accurate amount of 0.1 mL to a test tube, adding a phosphate buffer (pH 8.0) in an accurate amount of 5 mL, mixing the whole, adding a solution (an accurate amount: 1 mL) prepared by dissolving 0.100 g offluorescamine in 100 mL of acetone (for a non-aqueous titration), mixing the whole, allowing to stand for 15 minutes, analyzing the resulting solution by fluorometry, and measuring the fluorescence at an exciting wavelength of 390 nm and a fluorescentwavelength of 475 nm. Finally, an amount (mg/dL) of DL-.beta.-aminoisobutyric acid remaining in the solution was calculated, using the standard curve.

To measure a dependence on an amount of the spherical activated carbon sample or the surface-modified spherical activated carbon sample, the same procedures were repeated except that an amount of the spherical activated carbon sample or thesurface-modified spherical activated carbon sample used was 0.500 g, and the test fluorescence was measured and the amount of DL-.beta.-aminoisobutyric acid remaining in the solution was calculated as above.

(3) The Selective Adsorption Rate

The selective adsorption rate was calculated from an amount of .alpha.-amylase remaining in the solution in the adsorption test of .alpha.-amylase wherein an amount of the spherical activated carbon sample used or the surface-modified sphericalactivated carbon sample used was 0.500 g, and an amount of DL-.beta.-aminoisobutyric acid remaining in the solution in the adsorption test of DL-.beta.-aminoisobutyric acid, wherein an amount of the spherical activated carbon sample used or thesurface-modified spherical activated carbon sample used was 0.500 g, using the equation: A=(10-Tr)/(10-Ur) wherein A denotes the selective adsorption rate, and Tr denotes an amount of DL-.beta.-aminoisobutyric acid remaining in the solution, and Urdenotes an amount of .alpha.-amylase remaining in the solution.

Example 1

Spherical phenolic resin (particle diameter=10 to 700 .mu.m: trade name=High functional true spherical resin "Maririn" HF500 type; Gun Ei Chemical Industry Co., Ltd.) was sieved through a screen having an opening size of 250 .mu.m, to remove finepowders. Then, 150 g of the resulting spherical phenolic resin was charged into a vertical reaction quartz tube having a grating, heated to 350.degree. C. over 1.5 hours under a nitrogen gas stream, and further heated to 900.degree. C. over 6 hours,and maintained at 900.degree. C. for 1 hour to obtain 68.1 g of a spherical carbonaceous material. Thereafter, the product was activated at 900.degree. C. at an atmosphere of a gas mixture of nitrogen gas (3 NL/min) and steam (2.5 NL/min). When apacking density of the spherical activated carbon was lowered to 0.5 mL/g, the activation was ceased to obtain 29.9 g of the spherical activated carbon (yield=19.9% by weight).

Diffraction intensities of the resulting spherical activated carbon were 743 cps at a diffraction angle (2.theta.) of 15.degree., 90 cps at a diffraction angle (2.theta.) of 35.degree., and 473 cps at a diffraction angle (2.theta.) of 24.degree.. Therefore, a diffraction intensity ratio, an R value, was 1.71.

The properties of the resulting spherical activated carbon are listed in Tables 1 and 2.

The curve C in FIG. 1 is a diffraction curve obtained by measuring an intensity of the product prepared by vacuum drying the spherical activated carbon obtained in Example 1 at 120.degree. C. for 2 hours, by the same procedures as thosementioned in the method for measuring a diffraction intensity ratio, an R value.

Diffraction intensities of the resulting spherical activated carbon were 788 cps at a diffraction angle (2.theta.) of 15.degree., 72 cps at a diffraction angle (2.theta.) of 35.degree., and 492 cps at a diffraction angle (2.theta.) of 24.degree.. Therefore, a diffraction intensity ratio, an R value, was 1.71.

The properties of the resulting spherical activated carbon are listed in Tables 1 and 2.

Example 3

The spherical activated carbon obtained in Example 1 was oxidized at 470.degree. C. for 3 hours and 15 minutes on a fluidized bed at an atmosphere of a gas mixture of nitrogen gas and oxygen gas (oxygen concentration=18.5 vol %), and then,reduced at 900.degree. C. for 17 minutes on the fluidized bed at an atmosphere of nitrogen gas to obtain the surface-modified spherical activated carbon.

Diffraction intensities of the resulting surface-modified spherical activated carbon were 627 cps at a diffraction angle (2.theta.) of 15.degree., 66 cps at a diffraction angle (2.theta.) of 35.degree., and 400 cps at a diffraction angle(2.theta.) of 24.degree.. Therefore, a diffraction intensity ratio, an R value, was 1.68.

The properties of the resulting surface-modified spherical activated carbon are listed in Tables 1 and 2.

Example 4

The procedure described in Example 3 was repeated, except that the spherical activated carbon used in Example 2 was used as the starting material, to obtain the surface-modified spherical activated carbon.

Diffraction intensities of the resulting surface-modified spherical activated carbon were 702 cps at a diffraction angle (2.theta.) of 15.degree., 74 cps at a diffraction angle (2.theta.) of 35.degree., and 428 cps at a diffraction angle(2.theta.) of 24.degree.. Therefore, a diffraction intensity ratio, an R value, was 1.77.

The properties of the resulting surface-modified spherical activated carbon are listed in Tables 1 and 2.

Example 5

The procedure described in Example 3 was repeated, except that an ion-exchange resin (styrene based; effective diameter=0.50 to 0.65 mm; trade name=Amberlite 15WET; Organo Corporation) was used instead of the phenolic resin, to obtain thesurface-modified spherical activated carbon.

Diffraction intensities of the resulting surface-modified spherical activated carbon were 765 cps at a diffraction angle (2.theta.) of 15.degree., 82 cps at a diffraction angle (2.theta.) of 35.degree., and 485 cps at a diffraction angle(2.theta.) of 24.degree.. Therefore, a diffraction intensity ratio, an R value, was 1.69.

The properties of the resulting surface-modified spherical activated carbon are listed in Tables 1 and 2.

Further, a micrograph (magnification=.times.50) illustrating a surface structure of the resulting surface-modified spherical activated carbon obtained by a scanning electron microscope is shown in FIG. 2, and a micrograph(magnification=.times.200) illustrating a cross sectional structure of the resulting surface-modified spherical activated carbon obtained by a scanning electron microscope is shown in FIG. 3.

Comparative Example 1

Petroleum pitch (68 kg) (softening point=210.degree. C.; quinoline insoluble contents=not more than 1% by weight; ratio of hydrogen atoms/carbon atoms=0.63) and naphthalene (32 kg) were charged into an autoclave (internal volume=300 L) equippedwith stirring fans, melted at 180.degree. C., and mixed. The mixture was extruded at 80 to 90.degree. C. to form string-like shaped products. Then, the string-like shaped products were broken so that a ratio of a diameter to a length became about 1to 2.

The resulting broken products were added to an aqueous solution prepared by dissolving 0.23% by weight of polyvinyl alcohol (saponification value=88%) and heating to 93.degree. C., and dispersed with stirring to be spheroidized. Then, the wholewas cooled by replacing the polyvinyl alcohol aqueous solution with water, at 20.degree. C. for 3 hours, whereby the pitch was solidified and naphthalene crystals were precipitated, and a slurry of spherical shaped products of pitch was obtained.

After most of the water was removed by filtration, the naphthalene in the pitch was extracted and removed with n-hexane at an amount of about 6 times that of the spherical shaped products of pitch. The resulting porous spherical pitch was heatedto 235.degree. C. by passing a heated air in a fluidized bed, and allowed to stand at 235.degree. C. for 1 hour, to thereby be oxidized, and a porous spherical oxidized pitch was obtained, which is non-fusible to heat. The resulting porous sphericaloxidized pitch had an oxygen content of 14% by weight.

Thereafter, the resulting porous spherical oxidized pitch was activated in a fluidized bed at 900.degree. C. for 170 minutes by a nitrogen gas atmosphere containing 50% by volume of steam to obtain a spherical activated carbon. Further, theresulting spherical activated carbon was oxidized in the fluidized bed at 470.degree. C. for 195 minutes by a nitrogen-oxygen atmosphere containing 18.5% by volume of oxygen, and reduced in the fluidized bed at 900.degree. C. for 17 minutes by anitrogen gas atmosphere, to obtain a surface-modified spherical activated carbon.

Diffraction intensities of the resulting surface-modified spherical activated carbon were 647 cps at a diffraction angle (2.theta.) of 150, 84 cps at a diffraction angle (2.theta.) of 35.degree., and 546 cps at a diffraction angle (2.theta.) of24.degree.. Therefore, a diffraction intensity ratio, an R value, was 1.22.

The properties of the resulting surface-modified spherical activated carbon are listed in Tables 1 and 2.

The curve A in FIG. 1 is a diffraction curve obtained by measuring an intensity of the product prepared by vacuum drying the surface-modified spherical activated carbon obtained in Comparative Example 1 at 120.degree. C. for 2 hours, by the sameprocedures as those mentioned in the method for measuring a diffraction intensity ratio, an R value; and the curve B in FIG. 1 is a diffraction curve obtained by measuring an intensity of the paste product prepared by adding 2 or 3 drops of ion-exchangewater dropwise to 200 mg of the surface-modified spherical activated carbon obtained in Comparative Example 1, by the procedures mentioned as above.

Further, a micrograph (magnification: .times.50) illustrating a surface structure of the resulting surface-modified spherical activated carbon obtained by a scanning electron microscope is shown in FIG. 4, and a micrograph (magnification:.times.200) illustrating a cross sectional structure of the resulting surface-modified spherical activated carbon obtained by a scanning electron microscope is shown in FIG. 5.

Comparative Example 2

The procedure described in Comparative Example 1 was repeated, except that the oxidizing and reducing treatment of the spherical activated carbon were not carried out, to obtain the spherical activated carbon.

Diffraction intensities of the resulting surface-modified spherical activated carbon were 651 cps at a diffraction angle (2.theta.) of 15.degree., 81 cps at a diffraction angle (2.theta.) of 35.degree., and 548 cps at a diffraction angle(2.theta.) of 24.degree.. Therefore, a diffraction intensity ratio, an R value, was 1.22.

The properties of the resulting spherical activated carbon are listed in Tables 1 and 2.

The Hg pore volume in Table 1 was determined by a mercury press-injection method and corresponds to a volume of pores having a diameter of 20 to 1000 nm.

The SSA (BET) in Table 1 is a found value of a specific surface area listed as a reference, and determined by the following method.

As the method for determination of a specific surface area by Langmuir's adsorption equation, nitrogen is adsorbed to the spherical activated carbon sample or the surface-modified spherical activated carbon sample at -196.degree. C., and arelation of a nitrogen partial pressure and an adsorbed amount (absorption isotherm) is measured.

BET plotting is carried out, given that a relative pressure of nitrogen is p, and an adsorbed amount at that time is v (cm.sup.3/g STP). That is, the plotting in a range wherein p is 0.05 to 0.3 is carried out, in the field wherein alongitudinal axis is p/(v(1-p)), and an abscissa axis is p. From the gradient at that time of b (unit=g/cm.sup.3), and an intercept of c (unit=g/cm.sup.3), a specific surface area S (unit=m.sup.2/g) can be calculated from the equation:

.times..times..times..times. ##EQU00002## wherein MA denotes a cross-sectional area of a nitrogen molecule, and was 0.162 nm.sup.2.

Renal failure model rats induced by subtotal nephrectomy of 3/4 kidney were used to carry out a test for confirming pharmacological effects on a renal failure by an administration of the adsorbent for oral administration of the present invention. The adsorbents prepared in Examples 1 and 3 according to the present invention were used as a sample. After six weeks from the induction to produce model rats, the rats were divided into a control group (6 rats; hereinafter referred to as a C1 group), agroup to which the adsorbent prepared in Example 1 was administered (6 rats; hereinafter referred to as a P1 group), and a group to which the adsorbent prepared in Example 3 was administered (6 rats; hereinafter referred to as a P2 group), so that therewas no major imbalance therebetween.

A powdery feed was administered to the rats of the groups. An amount of the feed given to the rats of the groups was determined on the basis of an average amount of feed taken by the rats of the C1 group for 2 or 3 days. A mixed feed containing5% by weight of the adsorbent for oral administration in the same powdery feed as that administered to the C1 group was administered to the rats of the P1 and P2 groups. After 8 weeks from the beginning of the administration of the adsorbents for oraladministration, serum creatinine, urea-nitrogen, urinary creatinine, creatinine clearance, and an amount of protein excreted were measured. Further, a same test was carried out for six normal rats in which subtotal nephrectomy was not conducted (normalgroup).

The results are shown in FIGS. 6 to 9. In the P1 and P2 groups, serum creatinine (FIG. 6) and urea-nitrogen (FIG. 7) were significantly lowered, respectively, in comparison with the C1 group, after 8 weeks from the beginning of theadministration. As to creatinine clearance (FIG. 8), which is an index of a renal function, a reduction was recognized in the C1 group, whereas a significant inhibition of the reduction in the C1 group was observed in the P1 and P2 groups. Further, asto the amount of protein excreted (FIG. 9), an index of a function of a nephric tubules, an increase was recognized in the C1 group, whereas a significant inhibition of the increase in the C1 group was observed in the P1 and P2 groups. In addition,similar results were observed for urinary creatinine.

It is apparent from the above results that the adsorbent for oral administration of the present invention can inhibit a progress of a chronic renal failure, improve a chronic renal failure, prevent a renal hypofunction, or maintain a renalfunction.

Hepatitis model rats induced by carbon tetrachloride were used to carry out a test for confirming pharmacological effects on a liver disease by an administration of the adsorbent for oral administration of the present invention. The adsorbentsprepared in Examples 1 and 3 according to the present invention were used as a sample.

More particularly, carbon tetrachloride was subcutaneously administered at an amount of 12 mg/kg twice a week to Sprague-Dauley rats (produced by Clea Japan, Inc.; male; 7 weeks old), continuously for about 4 months until the end of the test forconfirming pharmacological effects. After two months from the beginning of the administration of carbon tetrachloride, a reduction of liver function was confirmed, and thus, the rats were divided into a control group (6 rats; hereinafter referred to asa C2 group), a group to which the adsorbent prepared in Example 1 was administered (6 rats; hereinafter referred to as a Q1 group), and a group to which the adsorbent prepared in Example 3 was administered (6 rats; hereinafter referred to as a Q2 group),so that there was no major imbalance therebetween with respect to pathosis.

A powdery feed was administered to the rats of the groups. An amount of the feed given to the rats of the groups was determined on the basis of an average amount of feed taken by the rats of the C2 group for 2 or 3 days. A mixed feed containing5% by weight of the adsorbent for oral administration in the same powdery feed as that administered to the C2 group was administered to the rats of the Q1 and Q2 groups for 2 months after the division to the groups. Further, a same test was carried outfor six normal rats to which carbon tetrachloride was not administered (normal group).

For about two months from the beginning of the administration of the adsorbent for oral administration to the end of the administration test, ICG (Indocyanine green), GOT (glutamic-oxaloacetic transaminase), and GPT (glutamic-pyruvictransaminase) were measured. The results obtained after two months from the beginning of the administration of the adsorbent for oral administration are shown in FIG. 10 (ICG), FIG. 11 (GOT), and FIG. 12 (GPT). Comparing the ICG test reflecting hepaticmesenchymal functions, the Q1 and Q2 groups showed significantly lower values than the C2 group. Further, the Q1 and Q2 groups showed significantly lower values than the C2 group, as to GOT and GPT which are leakage of cellular enzymes.

It is apparent from the above results that the adsorbent for oral administration of the present invention can improve a deterioration of liver functions.

INDUSTRIAL APPLICABILITY

The adsorbent for oral administration according to the present invention has a specific pore structure, and thus, has an excellent selective adsorbability, that is, an excellent adsorbability of harmful toxins in an intestine, together with a lowadsorbability of useful substances such as digestive enzymes or the like in a body, when orally administered, and the selective adsorbability is remarkably improved in comparison with that of the conventional adsorbent for oral administration.

The adsorbent for oral administration according to the present invention can be used as an adsorbent for oral administration for treating or preventing a renal disease, or an adsorbent for treating or preventing a liver disease.

As the liver disease, there may be mentioned, for example, fulminant hepatitis, chronic hepatitis, viral hepatitis, alcoholic hepatitis, hepatic fibrosis, liver cirrhosis, hepatic cancer, autoimmune hepatitis, drug allergic hepatopathy, primarybiliary cirrhosis, tremor, encephalopathia, dysbolism, or dysfunction. Further, the porous spherical carbonaceous substance can be used in a treatment of a disease caused by toxic substances in a body, such as psychosis.

Although the present invention has been described with reference to specific embodiments, various changes and modifications obvious to those skilled in the art are possible without departing from the scope of the appended claims.