The present research was undertaken to elucidate the mechanism of diffusion and precipitation of helium in metals by nuclear reaction method, nuclear magnetic resonance and transmission electron microscopy.Helium-3 ions were implanted into tantalum foils by the Extrion Implantor. The condition was follows : ion energy 90keV, 5.8x10^<16>He/cm^2, and implantation at room temperature.The results by nuclear reaction method and nuclear magnetic resonance show that both methods are good tools to research the helium behaviour, and implanted helium already diffuses through the sample foil significantly.For the research by TEM, helium was into vanadium alloys implanted by boron-10 method and tritium trick method. Then, the samples were irradiated by JMTR, JOYO and FFTF. After the irradiation the samples were observed by TEM ; irradiated morphology and helium cavity density were measured. These helium behaviour was discussed in terms of the atomic size effect of alloying elements.上述と同一条件でイオン注入したタンタル中のヘリウムをパルス型核磁気共鳴装置を用いて負荷磁場1.34テスラ、周波数43.54MHzの条件下で測定した。ヘリウムー3によると考えられる共鳴エコ-が微弱ながら観測された。イオン注入中にかなりのヘリウムが試料中を拡散し、一部は試料から放出したと考えられる。(3)ボロンー10法およびトリチウムトリック法を用いてヘリウム注入したバナジウム合金の照射組織およびキャビティ分布状態に関する研究バナジウム合金に予め0.1%のボロンを固溶させた試料をJMTRにおいて高温にて中性子照射し核変換によって生成したヘリウムのキャビティの成長過程を電顕観察した。また、トリチウムトリック法を用いてヘリウムを固溶させたバナジウム合金をJMTR,JOYO,FFTFで中性子照射した組織を200kV透過電顕で観察した。(4)核反応模出法によるバナジウムおよびその合金の酸素の拡散の研究ヘリウムと同様にバナジウムの照射特性に重要な影響を及ぼす酸素の拡散の測定を核反応検出法を用いて行なった。特に、合金元素添加の影響について詳細な研究を行なった。