Halides of a dopant species may be used as a dopant gas source to form shallow doped junctions using a direct gas-phase doping (GPD) process. These halides can also be combined with a carrier gas. Some advantages over conventional gas-phase doping processes include shallower junctions, shorter process...http://www.google.com/patents/US5599735?utm_source=gb-gplus-sharePatent US5599735 - Exposure of semiconductor surface to dopant gas mixture containing a halide of a dopant, and a silicon halide etch suppressant

Exposure of semiconductor surface to dopant gas mixture containing a halide of a dopant, and a silicon halide etch suppressantUS 5599735 A

Abstract

Halides of a dopant species may be used as a dopant gas source to form shallow doped junctions using a direct gas-phase doping (GPD) process. These halides can also be combined with a carrier gas. Some advantages over conventional gas-phase doping processes include shallower junctions, shorter process times, lower processing temperatures, and the elimination of a separate surface cleaning step for native oxide removal.

providing a semiconductor wafer having a surface, said wafer comprising silicon; and

exposing said surface of said wafer to a process medium in order to dope at least a portion of said surface of said wafer, said process medium comprising a dopant gas and an etch suppressing additive, wherein said dopant gas comprises a halide of a dopant species, wherein said etch suppressing additive is a material selected from the group consisting of silicon tetrachloride, silicon tetrafluoride, and dichlorosilane; and

exposing said wafer and said dopant gas to a plasma source, after said step of exposing said surface of said wafer to a process medium.

2. The method of claim 1 wherein said plasma source is hydrogen.

3. The method of claim 1 further comprising, after said step of exposing said wafer and said dopant gas to a plasma source, the step of heating said wafer to provide dopant diffusion into the semiconductor wafer.

4. The method of claim 3 wherein the temperature of said heating step is a higher temperature than the temperature of said exposing step.

Description

FIELD OF THE INVENTION

This invention relates generally to the field of microelectronics and integrated circuits, and more particularly to a direct gas-phase doping (GPD) fabrication process for formation of shallow doped device junctions in semiconductor layers and substrates.

BACKGROUND OF THE INVENTION

Semiconductors are widely used in integrated circuits for electronic applications, including various information systems. Such integrated circuits typically use multiple bipolar junction transistors (BJT) and/or metal-oxide semiconductor field-effect transistors (MOSFET) fabricated in single crystal silicon. Many integrated circuits now require the introduction of dopants to one or more device junction layers for formation of the transistor device structures. Usually when dopants are introduced into a semiconductor wafer surface, they are introduced by a process called ion implantation, wherein the substrate is bombarded by ions of a certain species, thus introducing the dopant.

One problem with the ion implantation process is that the semiconductor crystal structure is damaged and later, a high temperature thermal anneal process must be performed in order to remove the defects. Another problem is that there is a limit on the shallowness of the doped junctions. In order to achieve junctions with depths on the order of 1000 Å or less, alternative device doping methods must be utilized.

Alternative methods of doping include direct gas-phase doping (GPD) such as rapid thermal gas-phase doping (RTGPD) and plasma immersion ion implantation (PIII), which allow the formation of ultra-shallow junctions without the use of conventional ion implantation. Prior art GPD processes usually have employed an ambient consisting of diborane mixed with hydrogen (B2 H6 /H2 ) for p-type doping, to form ultra-shallow boron junctions; or phosphine mixed with hydrogen (PH3 /H2 ) for n-type doping, to form ultra-shallow phosphorus doped junctions. Moreover, both arsine (AsH3) and tertiarybutylarsine (TBA) have been used in GPD processes to form shallow arsenic-doped junctions. The GPD processes rely on the chemisorption of the dopant species followed by thermally activated surface dissociation of the dopant species and solid-state diffusion to form the doped junction. The GPD process usually consists of a native oxide removal process step prior to the formation of an adsorbed dopant layer on the silicon surface and subsequent solid-phase diffusion of dopants from the adsorbed layer into the silicon substrate. Dopants are incorporated into silicon by diffusion in an oxygen-free atmosphere at a relatively low temperature unlike the conventional diffusion process in which dopant diffusion is performed in an oxygen-rich ambient.

The GPD process involves species such as hydrogen, phosphine, diborane, or arsine. The dopant molecules are adsorbed on the semiconductor surface. After surface adsorption, dissociation occurs; the chemical bonds between hydrogen and the dopant atoms break, reducing the adsorbed molecules into arsenic, phosphorous, or boron atoms, which diffuse into the silicon substrate. The byproducts, e.g. hydrogen, then desorb from the surface to make the surface sites available for chemical adsorption of more dopant species.

Reduced junction depths are required in scaled-down semiconductor technologies. For instance, the source/drain junction depth must be reduced with each new IC technology generation. In general, the need for reduced junction depth is driven by the device scale-down and improved device performance. Conventional doping methods have shortcomings: the ion implantation processes and current GPD processes have limitations in terms of minimum junction depth and junction quality.

Ion implantation technology has been widely used in semiconductor device manufacturing because of its superior controllability and relatively high manufacturing throughput, but it is inadequate for junctions shallower than 1000 Å because of ion channeling at low ion energies, end-of-range implant damage, lateral dopant spreading, and poor throughput and process control at low implant energies (e.g. below 10 keV). Another limitation of the implantation-formed junctions is the so-called anomalous transient-enhanced boron diffusion during low-temperature thermal annealing caused by the thermal dissolution of small defect clusters produced by ion implantation. Moreover, ion implantation is not suitable for uniform doping of high-aspect-ratio trenches. Effective removal of the implantation-induced defects in Si requires relatively high thermal annealing temperatures, which further redistribute the dopant.

The GPD processes to date have been exclusively based on the B2 H6 /H2 (for p type), Ph3 /H2 (for n type), and ASH3 /H2 (for n type) chemistries. These processes do not produce any damage in silicon and are the most effective when the semiconductor surface is treated using an in-situ clean to remove any native oxide layer.

SUMMARY OF THE INVENTION

The present invention encompasses using a halide of a dopant species for GPD (gas-phase doping). These halides of a dopant species may also be combined with a carrier gas.

One embodiment is a gas-phase doping method for semiconductor wafers, comprising the steps of exposing the surface of a semiconductor wafer to a process medium in order to dope at least a portion of the surface of the wafer, where the process medium comprising a dopant gas, and the dopant gas comprises a halide of a dopant species.

Another embodiment comprises the steps of exposing the surface of a semiconductor wafer to a dopant gas in order to dope at least a portion of the surface of the wafer, wherein the dopant gas comprises a halide of a dopant species, and exposing the wafer and the dopant gas to a plasma source.

Yet another embodiment comprises the steps of exposing the surface of a semiconductor wafer to a dopant gas in order to dope at least a portion of the surface of the wafer, wherein the dopant gas comprises a halide of a dopant species, exposing the wafer and the dopant gas to a plasma source, and heating the wafer to provide solid-state dopant diffusion.

Some advantages of the invention are the ability to increase the dopant introduction rate into exposed silicon regions, resulting in an increased process throughput rate, and the ability to reduce the temperature of the GPD process and/or make the junction even shallower for a given desired surface concentration. With this invention, the junction depth can be reduced, yet still be heavily doped. Another advantage is increased junction surface dopant concentrations. Yet another advantage is the self-cleaning action of the GPD process ambient due to the presence of halogen atoms which may keep the silicon surface free of native oxide.

BRIEF DESCRIPTION OF THE DRAWINGS

In the drawings, which form an integral part of the specification and are to be read in conjunction therewith, and in which like numerals and symbols are employed to designate similar components in various views unless otherwise indicated:

FIG. 1 is a schematic representation of a typical environment of the preferred embodiment: a single-wafer semiconductor fabrication reactor, such as a rapid thermal processing (RTP) reactor;

FIG. 2 is a timing diagram for a preferred embodiment of the invention, showing a GPD process with the following parameters: temperature, the dopant source flow rate, the hydrogen carrier flow rate, and a remote H2 plasma source;

FIG. 3 is a cross-sectional view of a semiconductor device upon which this process could be used, and;

FIG. 4 is a flow diagram depicting the process steps of the invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The making and use of the presently preferred embodiments are discussed below in detail. However, it should be appreciated that the present invention provides many applicable inventive concepts which can be embodied in a wide variety of specific contexts. The specific embodiments discussed are merely illustrative of specific ways to make and use the invention, and do not delimit the scope of the invention.

The following is a description of several preferred embodiments and alternative embodiments, including schematic representations and manufacturing methods. Corresponding numerals and symbols in the different figures refer to corresponding parts unless otherwise indicated. Table 1 below provides an overview of the elements of the embodiments and the drawings.

Process control computer 104 receives the multi-point temperature sensor signals, checks the status of multi-zone illuminator 84 for diagnosis/prognosis purposes, and provides multiple temperature control signals to multi-zone controller 106 in response to temperature readings of multi-point sensors. The multi-zone controller 106 receives measured multi-point temperature sensor outputs as well as the desired wafer temperature set point (from process control computer 104) and delivers suitable power set points to the multizone illuminator assembly power supply 108. Signal lines 110 between process control computer 104 and multi-zone illuminator assembly 84 include signals from multi-point temperature sensors from real-time semiconductor wafer 38 temperature measurements and lamp power readings.

GPD is the most effective when the silicon surface is initially treated using an in-situ cleaning process to remove any native oxide. It is important to make sure the surface is atomically clean, so that there is no residual native oxide to block the gas-phase doping process. The GPD rate at a given temperature is mostly limited by the processes of surface dissociation and desorption of the hydrogen byproducts from the surface to make more sites available for chemisorption of the dopant species.

The present invention, a method for doped shallow junction formation using direct gas-phase doping, involves halides of various dopant species. Table 2 shows a partial list of several halides of arsenic, phosphorus and boron dopants along with their physical properties. These dopant sources may be combined with a carrier gas, for example, H2. The surface chemisorption, surface dissociation, and solid-state diffusion cycles may be performed in sequential thermal (or thermal and plasma) steps to optimize the overall GPD process. The use of a halide dopant source along with H2 carrier gas (with or without H2 remote plasma exposure cycles used during the surface dissociation cycles) will enhance the surface dissociation rate as well as the byproduct desorption rate (the latter via reaction of atomic hydrogen with the halogen species such as [C1] or [F]), because chlorine, fluorine or bromine atoms react easily with hydrogen atoms, for example, to form HCl, HF, or HBr byproduct species.

The choice of the type of dopant halide source depends on the application and various practical considerations. Only the halides in gas-phase (delivery by mass-flow controllers) and liquid-phase (delivery by liquid-source delivery system) forms are acceptable for use with thermal processing reactors. In particular, halides such as BCl3, AsF5, PF3, PF5, PCl2 F3 are suitable sources since they are in the gas form at room temperature. The liquid-phase halides such as PCl3 are also useful since they can provide sufficient vapor pressure of the halide source when the liquid source is heated. With a halide source used for GPD, one potential problem is the possibility of excessive Si etching during the GPD process. This problem can be avoided by addition of a small amount of SiCl4 (with dopant chlorides), SiF4 (with dopant fluorides) or another Si etch stop gas.

A timing diagram for a preferred embodiment of a GPD process using remote H2 plasma and halide source is shown in FIG. 2. The sequential process shown in FIG.4 is performed after an in-situ clean in order to remove native oxides (although the use of a halide, especially a fluoride, dopant source can eliminate the need for a separate in-situ clean or native oxide removal step). FIG. 2 shows the wafer temperature, the dopant source (such as BCl3) flow rate, hydrogen carrier flow rate, and a remote hydrogen plasma source state (e.g. a source of microwave discharge that injects hydrogen plasma into the chamber). Each doping is a three-step process, with the steps described below:

Step 1) A low-to-medium temperature dopant chemisorption step, where the wafer temperature is at a medium setting, the dopant flow is on, the hydrogen flow is on, but the remote plasma source is off.

Step 2) A low-to-medium temperature surface dissociation and desorption of byproduct step with an option of remote plasma excitation for H2 carrier gas, where the wafer temperature is medium, the dopant flow is on, the hydrogen flow is on, and the remote hydrogen plasma source is on. The reaction results in some chemisorption of dopant species on the available sites on the surface; and

Step 3) A higher temperature solid-state diffusion step to drive the dopant atoms into silicon to form the doped junction.

These 3-step cycles may be repeated as many times as desired, in order to obtain higher doping concentration or deeper junctions.

The novel use of a halide as a dopant species for use with GPD chemistries offers some advantages over the conventional GPD processes based on B2 H6 /H2, PH3 /H2, or AsH3 chemistries. The dopant introduction rate into exposed silicon regions is increased, resulting in an increased throughput rate. The temperature of the process may be reduced, making the junction even shallower for a given surface concentration. Although the junction depth may be reduced, it may still be heavily doped with this invention. In addition, when using the halides, it is possible to eliminate a cleaning step, due to the surface cleaning action of the halogen species.

The above processes can be done with purely thermal doping, or with a combination of thermal and plasma; such as the addition of hydrogen plasma. The sequential multiprocessing GPD process based on the combination of thermal and plasma process energy sources to enhance the chemisorption, surface dissociation, and byproduct desorption processes is also novel and offers potentially significant advantages over the conventional methods of GPD.

FIG. 3 is an example of a structure that benefits from the invention. The substrate 18 is exposed to one of the halide gases in the invention, doping it and forming, for example, the p+ source/drain junction region

While the invention has been described with reference to illustrative embodiments, this description is not intended to be construed in a limiting sense. Various modifications and combinations of the illustrative embodiments, as well as other embodiments of the invention, will be apparent to persons skilled in the art upon reference to the description. It is therefore intended that the appended claims encompass any such modifications or embodiments.