Tig welding 5052 Aluminum. which filler ?

guys,
we have a small project at work we will be tig welding which is made from .125" thick sheet metal, the alloy is 5052 aluminum.
i searched the internet and see its safe to use 4043 or 5356 filler, which we already have in the shop.
do you guys agree with this ?
and is there anything special i should look out for when welding this type of aluminum ?
thanks for any input, since i have never welded 5052 before.

Tig welding 5052 Aluminum. which filler ?

Either filler is good unless you are anodising it then go for 5356.
4043 will be more ductile and less likely to crack but on the other hand 5356 is a stronger material but tends to crack if you don't cap the weld properly.

It would help to know what the project is. If it is something that is going to experience high temperatures, 4043 would probably be better. If it is something that needs maximum strength, 5356 would probably be better.

Either filler is good unless you are anodising it then go for 5356.
4043 will be more ductile and less likely to crack but on the other hand 5356 is a stronger material but tends to crack if you don't cap the weld properly.

5356 is actually more ductile, whereas 4043 may be a little softer, but will fatigue much faster than 5356 or 5183. I would never use 4043 on a seam that experiences vibration or variable loads.

If you are welding 5052 sheet into a tank, you are much better of with the stronger filler. Personally I choose 5356 every time unless elevated service temps are experienced.

Lately I have been using Maxal's 4943. Lightning fast for tig work, and bridges the gap in the strength area. Wets like no tomorrow.

Tig welding 5052 Aluminum. which filler ?

So there are some people using 4943. Shovelon have you been using it for just tig or mig also? Also what type of application? I've talked to my lws about bring some in for use on 6061-t4&6 plate for making race snowmobile engine mounts. From what I've talked to maxal it should be the cats a$$ after post weld tempering.

So there are some people using 4943. Shovelon have you been using it for just tig or mig also? Also what type of application? I've talked to my lws about bring some in for use on 6061-t4&6 plate for making race snowmobile engine mounts. From what I've talked to maxal it should be the cats a$$ after post weld tempering.

I have been using it with both mig and tig. I really like the tig rod. It flows like water and is fast. It is very strong too. I am hoping to phase out my 4043 tig rod soon. My LWS said they will stock it too.

As far as mig, it is watery in the flow characteristics, and lays a virtually smut free strong bead. The wire is shockingly brittle but drives nice in the 350p. I won't be switching from 5356 mig wire though as I have that down pat, smut and all.