PROBLEM TO BE SOLVED: To provide a biodegradable non-woven fabric comprising filament webs each capable of controlling a biodegradation rate and having excellent strength and weave. SOLUTION: This biodegradable non-woven fabric wherein regions comprising mutually fused filaments are disposed at distances is obtained by laminating and thermally fusing one or two filament webs comprising a high mol.wt. polymer prepared by binding the plural molecules of polybutadiene succinate polymer synthesized from 1,4-butanediol and succinic acid to each other through urethane bonds to the surface or both the surfaces of a filament web comprising polylactic acid polymer containing L-lactic acid or D-lactic acid units in an amount of >=80 mol.%. The filament web comprising the polylactic acid polymer containing L-lactic acid or D-lactic acid units in an amount of >=80 mol.% has an average single filament fineness of 1-10 denier and a METSUKE of 5-50 g/m<2> , and the filament webs comprising a high mol.wt. polymer prepared by binding the plural molecules of polybutadiene succinate polymer synthesized from 1,4-butanediol and succinic acid to each other through urethane bonds have an average single filament fineness of 1-10 denier and a METSUKE of 5-50 g/m<2> .

Description

Translated from Japanese

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【０００１】 [0001]

【発明の属する技術分野】本発明は、高強度で良好な地合を有し、且つ堆肥中、湿った土中、あるいは活性汚泥を含む水中、海水中などで微生物により完全に分解可能であり、且つその生分解速度をコントロール可能な、衛生・医療用品の基材、衣料、家庭用、産業用品基材、農業用資材などとして幅広く使用可能な生分解性不織布に関するものである。 BACKGROUND OF THE INVENTION The present invention has good formation in high strength, and in compost, water with moist soil or activated sludge, are completely degradable by microorganisms such as in seawater , and that can control the rate of biodegradation, hygiene and medical supplies of the base material, but clothing, household, industrial supplies the base material, on widely available biodegradable non-woven fabric as such as agricultural materials.

【０００２】 [0002]

【従来の技術】長繊維を構成繊維とするスパンボンド不織布は、短繊維を構成繊維とする短繊維不織布と比較し、高強度で且つ比較的安価であるため、種々の用途に使用されている。 BACKGROUND ART spunbonded nonwoven fabric and the fibers constituting the long fibers, as compared to the short-fiber nonwoven fabric and the fibers constituting the short fiber, because it is and relatively inexpensive high strength, are used in various applications .このスパンボンド不織布を構成する繊維素材としては、ポリエチレン、ポリプロピレン、ポリエステル、ポリアミドなどの重合体が一般的である。 The fiber material constituting the spunbonded nonwoven fabric, polyethylene, polypropylene, polyester, polymers such as polyamides are common.しかし、これらの素材からなるスパンボンド不織布は、微生物などによる生分解性がなく、普通の自然環境下では化学的に非常に安定である。 However, spunbonded nonwoven fabrics made of these materials, not biodegradable due microorganisms under ordinary natural environment is chemically very stable.

【０００３】従って、使い捨て型の長繊維ウェブは、使用後、消却あるいは埋め立てといった方法で処理されているのが現状である。 [0003] Therefore, disposable long fiber web, after use, that has been treated in such a way canceled or reclamation at present.日本では焼却処理が広く行われているが、多大の費用が必要とされるだけでなく、例えばポリアミドであるナイロン系の不織布の場合には、シアンガスのような有毒ガスを発生する恐れもあるため、廃棄プラスチックスによる公害が発生しつつあり、この廃棄プラスチックス処理の問題をどのように解決していくかが自然環境保護や生活環境保護の点で大きな社会問題となっている。 Although incineration in Japan is widely not only great expense is required, for example in the case of a non-woven fabric of nylon polyamides, since there is a risk of generating a toxic gas such as cyan gas , is becoming pollution caused by waste plastics is generated, how do we solve the problem of the waste plastics processing has become a major social problem in terms of the natural environment protection and living environment protection.

【０００４】一方埋め立てに関しては、素材が化学的に安定であるため、土中で長期間にわたって元の状態で残るという問題がある。 On the other hand with respect to landfill, because the material is chemically stable, there is a problem that remains in its original state for long periods in the soil.このような問題を解決する方法として、生分解性を有する素材を使用することで、短期間のうちに自然に分解される新しいスパンボンド不織布が要望されている。 As a method for solving such a problem, the use of materials having biodegradability, new spunbonded nonwoven fabric which is degraded naturally in a short period of time is desired.

【０００５】微生物分解性を有する重合体として、キチンなどの多糖類、カット・グット（腸線）や再生コラーゲンなどのタンパク質やポリペプチド（ポリアミノ酸）、微生物が自然界で作るポリ−３−ヒドロキシブチレートやポリ−３−ヒドロキシバリレートやポリ−３− [0005] As the polymer having biodegradability, polysaccharides, cut the Good (catgut) and such regenerated collagen proteins and polypeptides (polyamino acid), microorganisms made of natural poly-3-hydroxybutyrate, such as chitin and poly-3-hydroxyvalerate and poly-3ヒドロキシカプロレートのような微生物ポリエステル、 Microbial polyesters such as hydroxy mosquitoes professional rate,ポリグリコリドやポリラクチドなどの合成脂肪族ポリエステルなどが知られている。 Such as synthetic aliphatic polyesters such as polyglycolide and polylactide are known.しかし、これらの重合体から繊維を製造する場合は、スパンボンド不織布に不可欠な溶融紡糸性が非常に乏しく、一般に使用されるスパンボンド不織布製造装置では加工できないといった問題がある。 However, when manufacturing fibers from these polymers have very poor critical melt spinnability spunbonded nonwoven fabric, there is a problem can not be processed in the spunbonded nonwoven fabric production apparatus commonly used.

【０００６】また、素材のコストが極めて高いため、使いすておむつや生理用品のカバーストックなどの衛生材料、拭取布、包装材料などの一般使い捨て生活資材としては不向きである。 [0006] In addition, for the cost of the material is extremely high, sanitary materials such as a cover stock of disposable diapers and sanitary napkins, wiping cloth, it is not suitable as a general disposable life materials such as packaging materials.

【０００７】以上の問題を解決するために、特開平４− [0007] In order to solve the above problems, JP-4-５７９５３号公報においては微生物分解性重合物のポリカプロラクトンを３〜３０％含むポリエチレンからなるスパンボンド不織布が提案されている。 Spunbonded nonwoven fabric have been proposed consisting of polyethylene containing 3% to 30% polycaprolactone microbial degradable polymers in 57953 JP.しかし、ポリエチレンは半永久的に分解することがないので、本来の意味での微生物分解性不織布とはいえない。 However, polyethylene because there is no possible to decompose semipermanently, it can not be said that biodegradability nonwoven fabric in its original sense.また、特開平５−２１４６４８号公報には、ポリ−ε−カプロラクトン及び／またはポリ−β−ポロピオラクトンからなるスパンボンド不織布が提案されている。 JP-A-5-214648, spunbonded nonwoven fabric made of poly -ε- caprolactone and / or poly -β- Polo propiolactone has been proposed.この場合、微生物分解性を完全に持たせることができたが、ポリ−ε−カプロラクトンの融点が６０℃前後で、ポリ−β−ポロピオラクトンの融点が１００℃前後であり、熱安定性が不良であるため、実用材料として向かないといった問題がある。 In this case, it was possible to completely free of microbial degradation, before and after the melting point of the poly -ε- caprolactone 60 ° C., the melting point of the poly -β- Polo propiolactone is longitudinal 100 ° C., thermal stability because it is defective, there is a problem not suitable as a practical material.

【０００８】また、特開平７−４８７６８号公報、特開平７−３４３６９号公報において、更に本発明者らが、 Further, JP-A-7-48768 and JP-in Hei 7-34369 discloses further the present inventors,特開平８−６０５１３号公報において、グリコールと脂肪族ジカルボン酸またはその誘導体成分を構成単位として含むことを特徴とする脂肪族ポリエステル樹脂によるスパンボンド不織布を提案した。 In JP-A-8-60513, JP-proposed spunbonded nonwoven according aliphatic polyester resin comprising a glycol and an aliphatic dicarboxylic acid or a derivative component as structural units.この長繊維ウェブは前記問題点をほぼ解決したものの、実用上紡糸性と生分解性を共に満足するものは得られていないのが実状である。 Although the long fiber web was substantially solve the above problems, the has not been obtained which satisfy both the practical spinnability and biodegradability is actual situation.

【０００９】即ち、溶融紡糸に適し、スパンボンド不織布に使用することが可能な上記脂肪族ポリエステルとしては、例えば、１，４−ブタンジオールとコハク酸から合成される脂肪族ポリエステル重合体であるポリブチレンサクシネートのような樹脂の場合は溶融紡糸性が良好で、強度と風合いの優れる生分解性不織布が得られるが、樹脂の融点が１１５℃以下であるため用途によっては、特に産業用資材では耐熱性が不十分であるばかりでなく、生分解速度のコントロールが困難である欠点もある。 [0009] That is, suitable for melt spinning, as the aliphatic polyester which can be used for spunbond nonwoven, for example, an aliphatic polyester polymer synthesized from 1,4-butanediol and succinic acid poly for resins such as polybutylene succinate good melt spinnability, but biodegradable nonwoven fabric excellent in strength and texture is obtained, depending on the application for the melting point of the resin is 115 ° C. or less, in particular in industrial materials not only the heat resistance is insufficient, control of biodegradation rate is also drawback is difficult.

【００１０】更に、Ｌ−乳酸またはＤ−乳酸単位を８０ [0010] In addition, the L- lactic acid or D- lactic acid units 80モル％以上含有するポリ乳酸重合体のような樹脂は、溶融紡糸性が良好で、強度に優れる長繊維ウェブが得られるが、長繊維ウェブが硬いため、使いすておむつや生理用品のカバーストックなどの衛生材料、拭取布、包装材料などには不向きであるばかりでなく、生分解速度のコントロールが困難であるという欠点もある。 The resins such as polylactic acid polymer containing at least mol%, melt spinnability is good, but the long fiber web having excellent strength is obtained, since the long fiber web hard, disposable diapers and sanitary goods coverstock a sanitary materials, such as, wiping cloth, not only is not suitable for such packaging material, the disadvantage of control of biodegradation rate is difficult.生分解性不織布は、目的や用途によって分解速度や寿命の異なるものが必要とされる。 Biodegradable nonwoven fabric is required different decomposition rates and life by the purpose and application.従って生分解速度を広範囲に変えられるような生分解性不織布、つまり広範囲且つ自由に分解性が変えられるようなものが望まれている。 Thus the rate of biodegradation widely varied are such biodegradable nonwoven, i.e. such that extensive and freely degradable is changed is desired.

【００１１】 [0011]

【発明が解決しようとする課題】本発明の目的は、生分解速度をコントロールでき、強度、地合に優れる長繊維ウェブからなる生分解性不織布を提供することにある。 The object of the present invention is to solve the above can control the rate of biodegradation, strength, is to provide a biodegradable nonwoven fabric made of long fiber web having excellent formation.

【００１２】 [0012]

【課題を解決するための手段】本発明者は、かかる現状に鑑み、生分解速度をコントロールでき、且つ強度、地合に優れる長繊維ウェブに関して鋭意研究した結果、特定範囲のＬ−乳酸またはＤ−乳酸単位を８０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブの片面または両面に、特定の１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体樹脂からなる長繊維ウェブを積層することにより、生分解速度をコントロールでき、強度、地合に優れる生分解性不織布を得られることを見い出し、本発明を完成させるに至った。 The present inventors SUMMARY OF THE INVENTION In view of the above circumstances, can control the rate of biodegradation, and strength, extensive research result with respect to the longitudinal fiber web having excellent formation, a specific range L- lactic acid or D - on one side or both sides of the long fiber web composed of polylactic acid polymer containing lactic acid units 80 mol% or more, by urethane bonds the polybutylene succinate polymer synthesized from particular 1,4-butanediol and succinic acid by laminating a long-fiber web made of high molecular weight and polymer resin, can control the rate of biodegradation, strength, found that the resulting biodegradable nonwoven fabric which is excellent in texture, and completed the present invention .

【００１３】本発明は、Ｌ−乳酸またはＤ−乳酸単位を８０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブの片面または両面に、１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブが積層され、熱融着により繊維同士が融着した区域を間隔を置いて設けてなる生分解性不織布である。 [0013] The present invention is synthesized from L- lactic acid or D- lactic acid unit on one or both sides of the long fiber web composed of polylactic acid polymer containing at least 80 mol%, 1,4-butanediol and succinic acid long fiber web composed of polybutylene succinate polymer from the polymer obtained by molecular weight by urethane bonds are stacked, it is biodegradable nonwoven fabric comprising spaced areas in which fibers are fused by heat fusion .また本発明は、該Ｌ−乳酸またはＤ−乳酸単位を８ The present invention is the L- lactic acid or D- lactic acid units 8０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブの平均繊度が１〜１０デニール、目付が５〜５０ｇ 0 mol% or more of poly lactic acid polymer containing an average fineness 1 to 10 denier long fiber web having a basis weight 5~50g／ｍ 2 、該１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブの平均繊度が１〜１０デニール、目付が５〜５０ｇ／ｍ 2であることを特徴とする生分解性不織布に関するものである。 / M 2, average fineness of 1 to 10 denier polybutylene succinate polymer comprising a polymer weight of the polymer by urethane bond long fiber web to be synthesized from the 1,4-butanediol and succinic acid, the basis weight it relates biodegradable nonwoven fabric, which is a 5 to 50 g / m 2.

【００１４】 [0014]

【発明の実施の形態】本発明に使用可能な脂肪族ポリエステル樹脂としては、１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体に更にイソシアネートを添加し、ポリブチレンサクシネート重合体の間をポリウレタン結合させたもので、数平均分子量が１００００以上で融点が１１０〜１２０℃の範囲にあり、且つＪＩＳ Ｋ ７２１０に記載された方法（１９０℃、２．１６ｋｇ荷重）で測定したメルトフローレートが１０〜７０ｇ／１０分の範囲のものである。 The DETAILED DESCRIPTION OF THE INVENTION Possible aliphatic polyester resin used in the present invention, the addition of 1,4-butanediol and a polybutylene succinate polymer further isocyanate which is synthesized from succinic acid, polybutylene succinate between the polymer which was then polyurethane bond, there melting a number average molecular weight of 10,000 or more is in the range of 110 to 120 ° C., and the method (190 ° C., 2.16 kg load) according to JIS K 7210 measured at melt flow rate is in a range of 10~70g / 10 min.

【００１５】つまり、メルトフローレートが１０ｇ／１ [0015] In other words, the melt flow rate of 10g / 1０分未満のポリブチレンサクシネートをウレタン結合させたものは溶融粘度が高すぎて、溶融温度を高くしなければ高速度での溶融紡糸が容易ではなくなり、高い温度での紡糸は口金面の汚れが発生し易くなり、操業上適さない。 That the polybutylene succinate less than 0 minutes and allowed to urethane bonds is too high melt viscosity, melt spinning at high speed unless a higher melting temperature is not easy, spinning at high temperatures spinneret surface dirt There likely to occur, not suitable on the operation.逆に、メルトフローレートが７０ｇ／１０分を超えると、糸切れが発生し易くなり、得られる生分解性不織布の風合いが悪化するばかりでなく、強度も低下するため適さない。 Conversely, if the melt flow rate exceeds 70 g / 10 min, tends yarn breakage occurs, not only the texture of the biodegradable nonwoven fabric obtained is deteriorated strength unsuitable for lowered.

【００１６】なお、１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体に必要に応じて、 [0016] If necessary polybutylene succinate polymer synthesized from 1,4-butanediol and succinic acid the polymer obtained by high molecular weight by a urethane bond,例えば酸化防止剤、熱安定剤、紫外線吸収剤などの他、 Such as antioxidants, heat stabilizers, other ultraviolet absorber, etc.,滑剤、ワックス剤、着色剤、結晶化促進剤などの各種添加剤を本発明の効果を損なわない範囲内で添加することができる。 Lubricants, waxes, colorants, various additives such as crystallization accelerator can be added within a range that does not impair the effects of the present invention.

【００１７】本発明に使用されるポリ乳酸重合体は、Ｌ The polylactic acid polymer used in the present invention, L−乳酸単位またはＤ−乳酸単位を８０モル％以上含有するポリ乳酸重合体が好適である。 - the polylactic acid polymer containing a lactic acid unit or D- lactic acid units 80 mol% or more are preferred.乳酸モノマーは光学活性の炭素を有しており、そのため、ポリ乳酸には光学異性体であるＤ体とＬ体とがあることが知られているが、 Lactic acid monomer has a carbon of the optically active, therefore, the polylactic acid has been known to have the D-form and L-form is an optical isomer, but両者を共重合すると融点は低下し、光学純度があまり低くなると融点が低すぎて、本発明の目的の１つである良好な紡糸性が得られなくなる。 When copolymerizing both melting point is lowered, and the melting point is too low when the optical purity is too low, good spinnability is one object of the present invention can not be obtained.使用されるポリ乳酸重合体における乳酸単位の光学純度（Ｌ体またはＤ体の比率）は好ましくは８０モル％以上、より好ましくは９５ The optical purity of the lactic acid unit in the polylactic acid polymers used (the ratio of the L-form or D-form) is preferably 80 mol% or more, more preferably 95モル％以上、更に好ましくは９８モル％以上である。 Mol%, more preferably at least 98 mol%.

【００１８】一般には乳酸を発酵法で生産するとＬ体が生産されるので、工業的にはＬ−乳酸の方が大量且つ安価に入手しやすく、本発明によるポリ乳酸重合体は通常Ｌ−乳酸を主体とするものである。 [0018] Since the generally produce by fermentation lactic acid L-form is produced industrially on the easily available large quantities at low cost is more of L- lactic acid, polylactic acid polymers according to the present invention is generally L- lactic acid the one in which a main component.しかしながら、Ｄ− However, D-乳酸を主体とする重合体であってもＬ−乳酸の場合と同様の物性のものを得ることができる。 It can be obtained the same physical properties as the case may be a polymer composed mainly of lactic acid L- lactic acid.

【００１９】上述した本発明に使用するポリ乳酸重合体もポリブチレンサクシネートをウレタン結合させたものと同様に、ＪＩＳ Ｋ ７２１０に記載された方法（２ [0019] Similar to that polylactic acid polymer used in the present invention described above also polybutylene succinate was urethane bond, the method described in JIS K 7210 (2００℃、２．１６ｋｇ荷重）で測定したメルトフローレートが１０〜７０ｇ／１０分の範囲のものが適している。 00 ° C., a melt flow rate measured at 2.16kg load) is suitable in the range of 10~70g / 10 min.メルトフローレートが１０ｇ／１０分未満のポリ乳酸は溶融粘度が高すぎて、溶融温度を高くしなければ高速度での溶融紡糸が容易ではなくなり、高い温度での紡糸は口金面の汚れが発生し易くなり、操業上適さない。 Melt flow rate polylactic acid of less than 10 g / 10 minutes is too high melt viscosity, melt spinning at high speed unless a higher melting temperature is not easy, spinning at high temperatures dirt spinneret surface is generated It tends to be, not suitable on the operation to.逆に、メルトフローレートが７０ｇ／１０分を超えると、糸切れが多発し、得られる長繊維ウェブの地合が悪化するばかりでなく、強度も低下するため適さない。 Conversely, if the melt flow rate exceeds 70 g / 10 min, yarn breakage occurred frequently, not only formation of long fibers obtained web is deteriorated strength unsuitable for lowered.

【００２０】また、ポリ乳酸樹脂は、ポリブチレンサクシネートをウレタン結合させたものと同様に、必要に応じて、例えば酸化防止剤、熱安定剤、紫外線吸収剤などの他、滑剤、ワックス剤、着色剤、結晶化促進剤などの各種添加剤を本発明の効果を損なわない範囲内で添加することができる。 Further, polylactic acid resin, similar to that of the polybutylene succinate is a urethane bond, optionally, such as antioxidants, heat stabilizers, other such as ultraviolet absorber, a lubricant, a wax agent, colorants, various additives such as crystallization accelerator can be added within a range that does not impair the effects of the present invention.

【００２１】長繊維ウェブを製造する際に押し出し紡糸機において、１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体、またはＬ−乳酸またはＤ−乳酸単位を８０モル％以上含有するポリ乳酸重合体を加熱溶融し、紡糸する場合の溶融温度は、樹脂の融点より５０〜１３５℃だけ高くする。 [0021] In the spinning extruder in making the long fiber web, 1,4-butane diol and the polymer was high molecular weight by urethane bonds the polybutylene succinate polymer synthesized from succinic acid, or L- lactic acid or D- lactic acid units by heating and melting a polylactic acid polymer containing at least 80 mol%, the melting temperature in the case of spinning, as high as from 50 to 135 ° C. than the melting point of the resin.溶融温度と重合体の融点の差が５０℃未満の場合、溶融した樹脂の粘度が高く、高速度での溶融紡糸が容易ではなくなり、操業上適さない。 If the difference between the melting point of the melting temperature and the polymer is less than 50 ° C., high viscosity of the molten resin, no longer easy to melt spinning at high speed, not suitable on operation.逆に、溶融温度が樹脂の融点より１３５℃を超えて高くなると、樹脂の融点からの温度の隔たりが大きすぎるため、押出し紡糸機の多数の口金から樹脂を紡糸する場合に冷却が難しくなり、繊維同士の融着や糸切れを生じ易くなるばかりでなく、樹脂の安定性が低下し、 Conversely, when the melting temperature is higher than the 135 ° C. than the melting point of the resin, for separation temperature of from the melting point of the resin is too large, the cooling becomes difficult when spinning resin from a number of die extrusion spinning machine, not only tends to occur fusion and yarn breakage between fibers, the stability of the resin is lowered,分解が発生する恐れがある。 There is a possibility that the decomposition occurs.

【００２２】前記１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体は、溶融押出し紡糸機の口金から押し出されて紡糸された後は、エジェクターにより高速エアーで引き取って、延伸され、次いで形成された多数の長繊維フィラメントを衝突板に当てて摩擦帯電させ、電荷による反発力で開繊させる。 [0022] The 1,4-butanediol and polymers and high molecular weight by urethane bonds the polybutylene succinate polymer synthesized from succinic acid, after being spun extruded from the die melt extrusion spinning machine , take back at a high speed air by ejector is drawn, then the number of long fiber filaments formed against a collision plate is triboelectrically charged, it is opened by the repulsive force due to the charge.この場合、帯電方法として、コロナ放電処理を行うことも可能である。 In this case, as a charging method, it is also possible to carry out a corona discharge treatment.

【００２３】本発明の１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブを構成する長繊維の平均繊度は１〜１０デニールの範囲であるのが好ましい。 The average fineness of the long fibers that the polybutylene succinate polymer synthesized from 1,4-butanediol and succinic acid of the present invention constituting the long fiber web composed of high molecular weight and polymer by urethane bond 1 preferably in the range of 10 denier.長繊維の平均繊度が１０デニールを超えて大きくなると、繊維径が太くなりすぎて得られる長繊維ウェブの柔軟性と地合が低下するため適さないことがある。 When the average fineness of the long fibers is larger than 10 deniers, there is the flexibility and texture of the long fiber web fiber diameter can be obtained too thick it is not suitable for reduction.逆に、長繊維の平均繊度が１デニール未満のものは紡糸性が不良になるため適さないことがある。 Conversely, of less than the average fineness of 1 denier long fibers may not be suitable for spinnability is poor.長繊維ウェブを構成する長繊維の断面形状としては、円形断面の他に異形あるいは扁平とすることもできる。 The long fiber cross-sectional shape constituting the long fiber web may be an irregular or flat in addition to the circular cross-section.

【００２４】本発明における１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブの目付は、５〜５０ｇ／ｍ 2の範囲であるのが好ましい。 The basis weight of the long fiber web polybutylene succinate polymer synthesized from 1,4-butanediol and succinic acid in the present invention consists of a high molecular weight and polymer by urethane linkages, 5 to 50 g / m 2 preferably in the range of the is.目付が５０ｇ／ｍ 2を超えると、積層後に得られる長繊維ウェブが硬くなりすぎて、柔軟性が低下し、風合いが悪くなるため適さないことがある。 If the basis weight exceeds 50 g / m 2, too hard long fiber web obtained after lamination, flexibility is lowered, it may not be suitable for the texture is deteriorated.逆に、５ｇ／ｍ 2未満では、長繊維ウェブの強度が低くなるばかりでなく、長繊維ウェブに風合いを付与する効果が低下するため適さないことがある。 Conversely, it is less than 5 g / m 2, not only the strength of the long fiber web is lowered, the effect of imparting texture to the long fiber web may not be suitable to decrease.

【００２５】前記Ｌ−乳酸またはＤ−乳酸単位を８０モル％以上含有するポリ乳酸重合体は、溶融押出し紡糸機の口金から押し出されて紡糸された後は、エジェクターにより高速エアーで引き取って、延伸され、次いで形成された多数の長繊維フィラメントを衝突板に当てて摩擦帯電させ、電荷による反発力で開繊させる。 The polylactic acid polymer which contains the L- lactic acid or D- lactic acid units 80 mol% or more is, after being spun extruded from the die melt extrusion spinning machine, take back at a high speed air by ejector, stretching is, then a large number of long fiber filaments formed against a collision plate is triboelectrically charged, it is opened by the repulsive force due to the charge.この場合、 in this case,帯電方法として、コロナ放電処理を行うことも可能である。 As the charging method, it is also possible to carry out a corona discharge treatment.

【００２６】本発明に用いられるＬ−乳酸またはＤ−乳酸単位を８０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブを構成する長繊維の平均繊度は１〜１０ The average fineness of the long fibers constituting the long fiber web composed of polylactic acid polymers of L- lactic acid or D- lactic acid units used in the present invention contains more than 80 mol% is 1 to 10デニールの範囲であるのが好ましい。 Preferably in the range of deniers.長繊維の平均繊度が１０デニールを超えると、繊維径が太くなりすぎて、 When the average fineness of the long fibers is more than 10 deniers, the fiber diameter is too thick,得られる長繊維ウェブの地合と柔軟性が低下し、平均繊度が１デニール未満のものは製造が困難になるため適さないことがある。 Formation and flexibility of the resulting long fiber web is lowered, the average fineness of less than 1 denier may not be suitable for manufacturing it becomes difficult.

【００２７】本発明におけるＬ−乳酸またはＤ−乳酸単位を８０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブの目付は、５〜５０ｇ／ｍ 2の範囲であるのが好ましい。 [0027] The present L- lactic acid or D- lactic acid units in the invention consisting of polylactic acid polymer containing at least 80 mol% of the long fiber web basis weight is preferably in the range of 5 to 50 g / m 2.目付が５０ｇ／ｍ 2を超えると、積層後に得られる長繊維ウェブが硬くなりすぎて、柔軟性が低下するため適さないことがある。 If the basis weight exceeds 50 g / m 2, too hard long fiber web obtained after lamination, it may not be suitable for flexibility is reduced.逆に、５ｇ／ｍ 2未満では、長繊維ウェブの強度が低くなりすぎるため適さないことがある。 Conversely, it is less than 5 g / m 2, may not be suitable for the strength of the long fiber web is too low.

【００２８】本発明でＬ−乳酸またはＤ−乳酸単位を８ [0028] The L- lactic acid or D- lactic acid unit in the present invention 8０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブの両面に１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブを積層すると、該ポリ乳酸重合体からなる長繊維ウェブの片面のみに該ポリブチレンサクシネート重合体をウレタン結合したものを積層する長繊維ウェブと比較して得られる長繊維ウェブの表裏差がなくなり、更に良好な風合いの長繊維ウェブを得ることができるばかりでなく、生分解速度をコントロールする効果を容易にすることもでき、更に好ましい。 0 consists molecular weight of the polymer polybutylene succinate polymer comprising polylactic acid polymer containing mol% or more on both sides of the long fiber web from 1,4-butanediol and succinic acid is synthesized by urethane bond length When laminating the fibrous web, the difference between both sides of the long fiber web obtained in comparison with the long fiber web of laminating that only one surface of the long fiber web made of the polylactic acid polymer the polybutylene succinate polymer and a urethane bond eliminated, further it is possible not only to obtain a good texture of the long fiber web, can also facilitate control effectively the rate of biodegradation, further preferable.

【００２９】本発明でＬ−乳酸またはＤ−乳酸単位を８ [0029] The L- lactic acid or D- lactic acid unit in the present invention 8０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブの両面に１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブを製造する場合、前述したように積層・製造される。 0 consists molecular weight of the polymer polybutylene succinate polymer comprising polylactic acid polymer containing mol% or more on both sides of the long fiber web from 1,4-butanediol and succinic acid is synthesized by urethane bond length when manufacturing a fibrous web, it is laminated and prepared as described above.

【００３０】本発明においては、Ｌ−乳酸またはＤ−乳酸単位を８０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブの片面または両面に１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブを積層した不織ウェブに、シート状の形態保持と強度を付与する目的で、規則的な間隔で繊維同士の自己融着区域を設ける。 [0030] In the present invention, it is synthesized from L- lactic acid or D- lactic acid unit on one or both sides of the long fiber web composed of polylactic acid polymer containing at least 80 mol% 1,4-butanediol and succinic acid the urethane bond polybutylene succinate polymer into a nonwoven web by laminating the long fiber web composed of high molecular weight and polymer, for the purpose of imparting sheet-like form retention and strength, the fibers at regular intervals providing a self-bonding area.この自己融着区域は、 The self-bonding area,ウェブを加熱した凸凹ロールと平滑ロールの間に導入し、加熱と加圧処理を施すことにより、凸凹ロールの凸部に対応した部分が融着することによって形成される。 Introduced between the uneven roll and a smoothing roll heated web, by applying a heat and pressure treatment, a portion corresponding to the convex portion of the concavo-convex rolls are formed by fusion.

【００３１】この場合、ロールの温度は、使用する１， [0031] 1 In this case, the temperature of the roll is to be used,４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体の融点より５〜５０℃低い温度である。 Polybutylene succinate polymer synthesized from 1,4-butanediol and succinic acid by urethane bonds is 5 to 50 ° C. lower than the melting point of the high molecular weight and polymer.ロール温度と樹脂の融点の差が５℃未満では、ロールによる熱圧着処理時に繊維がロールに付着し、製造トラブルの原因となる。 Is less than the difference between the melting point of the roll temperature and the resin is 5 ° C., the fiber adheres to the roll during thermocompression bonding process by rolls, causing production problems.逆に、ロール温度と樹脂の融点の差が５ Conversely, the difference between the melting point of the roll temperature and the resin 5０℃を超えて大きくなると、自己融着部分の形成が不十分となり、長繊維ウェブの強度が著しく低下するので適さない。 Becomes greater beyond the 0 ° C., the formation of self-welding portion becomes insufficient, unsuitable in the strength of the long fiber web is significantly reduced.

【００３２】凸凹ロールと平滑ロールで熱圧着処理を施す場合の線圧は、１０〜８０ｋｇ／ｃｍである。 The linear pressure in the case where in uneven roll and a smoothing roll subjected to thermal compression bonding process is 10~80kg / cm.線圧が１０ｋｇ／ｃｍ未満では、熱圧着処理による自己融着区域も形成が不十分となり、８０ｋｇ／ｃｍを超えて大きくなると、熱圧着処理時に凸凹ロールの凸部による長繊維の切断が生じてしまい、いずれも長繊維ウェブの強度が低下するので適さない。 The linear pressure is less than 10 kg / cm, a self-bonding zone may form by thermal pressure bonding treatment becomes insufficient, it becomes greater beyond 80 kg / cm, the cutting of the long fibers by the convex portion of the concavo-convex roll during thermocompression bonding process occurs put away, either unsuitable in to decrease the strength of the long fiber web.

【００３３】本発明においては、個々の自己融着区域の面積は、０．０３〜４ｍｍ 2の範囲であることが好ましい。 [0033] In the present invention, the area of each self-bonding zone, is preferably in the range of 0.03~4mm 2.自己融着区域の面積が０．０３ｍｍ 2未満では、得られる長繊維ウェブの強度が不足するため適さない。 In the area of self-bonding area is less than 0.03 mm 2, the strength of the long fiber web obtained is not suitable for the missing.逆に、自己融着区域の面積が４ｍｍ 2を超えると、得られる長繊維ウェブが硬くなりすぎて、柔軟性が低下するため適さない。 Conversely, if the area of self-welding zone exceeds 4 mm 2, too hard long fiber web obtained not suitable for flexibility is reduced.

【００３４】自己融着区域の面積の総和は、生分解性不織布の全表面積の２〜３０％であることが好ましい。 The total area of ​​the self-bonding zone is preferably 2 to 30% of the total surface area of ​​the biodegradable nonwoven fabric.自己融着区域の面積の総和が２％未満では、得られる長繊維ウェブの強度が不足するため適さない。 The sum of the areas of self-welding zone is less than 2%, the strength of the long fiber web obtained is not suitable for the missing.逆に、自己融着面積が３０％を超えると、得られる長繊維ウェブが硬くなりすぎて、柔軟性が低下するため適さない。 Conversely, when the self-welding area is more than 30%, too hard long fiber web obtained not suitable for flexibility is reduced.

【００３５】以上説明したように、１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブ上に、Ｌ−乳酸またはＤ−乳酸単位を８０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブを積層し、両面に積層する場合には、更に前出した１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブを積層させた３層ウェブを熱融着により繊維同士が融着することにより得られる生分解性不織布は、製造に際し、紡糸性と開繊性に優れ、生分解性をコントロール可能であり、且つ高強度でありながら優れた柔軟性と風合いを有するので衛生材料、医療 [0035] As described above, 1,4-butanediol and a polybutylene succinate polymer synthesized from succinic acid by urethane bond to the long fiber web of high molecular weight and polymer, L- lactic acid or the long fiber web of polylactic acid polymer containing D- lactic acid unit at least 80 mol% laminated, when laminated on both sides is synthesized from 1,4-butanediol and succinic acid out further before poly biodegradable nonwoven fabric fibers by heat fusing three layers webs are stacked long-fiber web made of a polybutylene succinate polymer from the polymer obtained by molecular weight by a urethane bond can be obtained by fusing, in the production excellent spinnability and spreadability, a controllable biodegradability, and sanitary materials because they have excellent flexibility and texture, yet high strength, medical基材、衣料用基材、家庭用基材、産業用基材などとして好適に使用することが可能である。 Substrate, clothing substrates, home base, it is possible to suitably used as such industrial base.

【００３６】 [0036]

【実施例】以下に実施例を挙げて本発明をより具体的に説明するが、本発明はもちろんこれらに限定されるものではない。 EXAMPLES The present invention will be described by examples in more detail, but the present invention is not of course limited thereto.尚、実施例及び比較例において、％は特に断りのない限り重量％である。 In Examples and Comparative Examples,% is particularly weight unless otherwise specified.

【００３７】実施例１ メルトフローレートが３１ｇ／１０分、融点が１１８℃ [0037] Example 1 melt flow rate of 31 g / 10 min, a melting point of 118 ° C.の１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体（昭和高分子社製、商品名：ビオノーレ）を準備し、溶融押出機において紡糸用口金を用いて、前記の樹脂を１９０℃に加熱溶融し、多数の微細孔から押出し、紡糸した後、紡出されたフィラメント群をエジェクターにより高速エアーで引き取りながら延伸して開繊し、移動するワイヤー製捕集用支持体上に捕集・ 1,4-butanediol and a polybutylene succinate synthesized from succinic acid succinate polymer polymer has a high molecular weight by a urethane bond (Showa High Polymer Co., Ltd., trade name: BIONOLLE) was prepared, in a melt extruder using spinning die, and heating and melting the resin to 190 ° C., after extrusion, spun from a large number of micropores, by spreading and stretching while drawing by a high speed air by ejector the spun filament group, collected onto a moving wire made for collecting support -堆積させウェブを形成させた。 It is deposited to form a web.得られた長繊維フィラメントの平均繊度は１．３デニール、目付は６ｇ／ｍ 2あった。 The average fineness of the resulting long fiber filaments 1.3 denier and a basis weight was 6 g / m 2.

【００３８】次に、メルトフローレートが２０ｇ／１０ Next, melt flow rate of 20g / 10分、融点が１６３℃のＬ−乳酸またはＤ−乳酸単位を８ Min, a melting point of 163 ° C. L-lactic acid or D- lactic acid units 8０モル％以上含有するポリ乳酸重合体（カネボウ合繊社製、商品名：ラクトロン）を準備し、溶融押出機において紡糸用口金を用いて、前記の樹脂を２２０℃に加熱溶融し、多数の微細孔から押出し、紡糸した後、紡出されたフィラメント群をエジェクターにより高速エアーで引き取りながら延伸して開繊し、１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブを搬送しながら移動するワイヤー製捕集用支持体上に捕集・堆積させウェブを形成させた。 0 polylactic acid polymer containing mol% or more (Kanebo Gosen Co., Ltd., trade name: Rakutoron) was prepared, using a spinning die in a melt extruder, melted by heating the resin to 220 ° C., number of fine after extrusion, spinning through the hole, the spun filaments group by spreading and stretching while drawing by a high speed air by ejector, 1,4-butane diol and urethane polybutylene succinate polymer synthesized from succinic acid bound by to form a web is collected and accumulated in a high molecular weight was made of polymer moves while conveying the long fiber web wire made for collecting support.得られた長繊維フィラメントの平均繊度は１．５デニール、 The average fineness of the resulting long fiber filaments 1.5 denier,目付は７ｇ／ｍ 2あった。 And the basis weight was 7g / m 2.

【００３９】更に、前述した１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブを同じ方法で製造し、積層したウェブの上に捕集・堆積させた。 [0039] Further, to produce a long fiber web composed of a polymer and a high molecular weight by urethane bonds the polybutylene succinate polymer synthesized from 1,4-butanediol and succinic acid as described above in the same manner and laminated It was collecting and deposited on top of the web.

【００４０】次いで、この積層ウェブを１１０℃に加熱した凸凹ロールと平滑ロールの間に導入し、線圧３０ｋ [0040] Then, by introducing the laminate web during the uneven roll and a smoothing roll heated to 110 ° C., a linear pressure 30kｇ／ｃｍで凸凹ロールの凸部に対応する部分を融着することにより、生分解性不織布を得た。 By fusing the portion corresponding to the convex portion of the concavo-convex roll g / cm, to obtain a biodegradable nonwoven fabric.個々の自己融着区域の面積は、０．１２ｍｍ 2であり、自己融着区域の面積の総和は４面積％であった。 Area of each self-bonding zone is 0.12 mm 2, the total sum of the areas of the self-bonding zone was 4 area%.

【００４１】得られた生分解性不織布を下記の試験方法で試験し、その品質を評価した。 The resulting biodegradable nonwoven fabric was tested in the following test method, to evaluate their quality.試験方法 （１）紡糸性 溶融紡糸時の糸切れ数の多少で評価した。 Test method (1) was evaluated in a somewhat yarn breakage number during spinning of melt spinning.評価は以下の５段階で評価した。 The evaluation was evaluated by the following five steps.５点・・・糸切れはなく、紡糸性は極めて良好である。 5 points ... yarn breakage not, spinning property is very good.４点・・・糸切れがほとんどなく、紡糸性は良好である。 4-point ... yarn breakage is almost no spinnability is good.３点・・・糸切れがあるが問題はなく、紡糸性は普通である。 There is a 3-point ... yarn breakage is not a problem, spinning property is common.２点・・・糸切れがかなり多く、紡糸性は悪い。 Quite a few 2-point ... yarn breakage, spinning property is bad.１点・・・糸切れが極めて多く、紡糸性は極めて悪い。 Is very much one point ... yarn breakage, spinning property is very bad.

【００４２】（２）地合（点） 得られた長繊維ウェブの地合を官能で評価した。 [0042] (2) formation (point) of the obtained long fiber web formation was evaluated by functional.評価は以下の５段階で評価した。 The evaluation was evaluated by the following five steps.５点・・・長繊維ウェブの地合が非常に優れている。 Formation of 5-point ... long fiber web is very good.４点・・・長繊維ウェブの地合が優れている。 Formation of four points ... long fiber web is excellent.３点・・・長繊維ウェブの地合が普通である。 Of the 3-point ... long fiber web formation is common.２点・・・長繊維ウェブの地合が劣る。 Of the two points ... long fiber web formation is poor.１点・・・長繊維ウェブの地合が非常に劣る。 Formation of one point ... long fiber web is very poor.

【００４３】（３）生分解性不織布の引張強度（Ｎ／５ [0043] (3) of biodegradable non-woven fabric tensile strength (N / 5０ｍｍ） ＪＩＳ Ｌ １９０６に示された方法で行った。 It was carried out in the manner shown in 0mm) JIS L 1906.（４）柔軟性（点） モニター２０人による官能評価により柔軟性を評価した。 (4) to evaluate the flexibility by a sensory evaluation by 20 people flexibility (point) monitor.モニターは、長繊維ウェブを手で揉み、長繊維ウェブの柔軟性を判定した。 Monitor, kneading by hand a long fiber web, to determine the flexibility of long-fiber web.評価は、以下の基準により１〜 Evaluation 1 according to the following criteria５点で示し、その合計点数（１００点満点）を柔軟性として表し、９０点以上を合格とした。 Indicated by 5-point, represent the total score (100 points) as flexibility, it was passed over 90 points.５点・・・長繊維ウェブの柔軟性が非常に優れている。 The flexibility of the 5-point ... long fiber web is very good.４点・・・長繊維ウェブの柔軟性が優れている。 The flexibility of four points ... long fiber web is excellent.３点・・・長繊維ウェブの柔軟性が普通である。 The flexibility of the 3-point ... long fiber web are common.２点・・・長繊維ウェブの柔軟性が劣る。 The flexibility of the two points ... long fiber web is inferior.１点・・・長繊維ウェブの柔軟性が非常に劣る。 Flexibility of one point ... long fiber web is very poor.

【００４４】（５）生分解速度（月） 大きさ１０cm×２５cmにカットした長繊維ウェブを、牛糞堆肥含有用土（重量構成比率：牛糞堆肥２０％、土７ [0044] (5) the rate of biodegradation (months) size 10 cm × long fiber web was cut into 25 cm, cattle manure containing soil (weight composition ratio: cattle manure 20%, the soil 7６％、ピートモス４％）に、深さ１５cmで各１００枚埋設し、１ヶ月毎に２枚ずつ取り出して重量を測定し、形態がバラバラになり、重量減が５０重量％以上になる期間（月）を測定し、平均値を算出して微生物分解速度とした。 6%, the peat moss 4%), and embedded each 100 sheets at a depth 15cm, 1 month removed by two weighed every, form becomes apart, the period in which weight loss is more than 50 wt% ( month) was measured and the biodegradation rate by calculating the average value.なお、観察は３６ヶ月行った。 In addition, the observation was carried out 36 months.

【００４５】実施例２ １，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブの平均繊度を９．３デニール、目付を６ｇ／ｍ 2 、Ｌ−乳酸またはＤ [0045] The average fineness of the long fiber web composed of a polymer and a high molecular weight by urethane bonds the polybutylene succinate polymer synthesized from Example 2 1,4-butanediol and succinic acid 9.3 denier, basis weight the 6g / m 2, L- lactic acid or D−乳酸単位を８０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブの平均繊度を９．７デニール、目付を７ｇ／ｍ 2としたこと以外は実施例１と同様にして生分解性不織布を製造した。 - the polylactic acid average fineness of 9.7 denier polymer consisting body long fiber web, except that a 7 g / m 2 basis weight in the same manner as in Example 1 to biodegradable nonwoven fabric containing lactic acid units 80 mol% or more It was prepared.得られた長繊維ウェブを実施例１と同様の試験法により試験し、その品質を評価した。 The resulting long fiber web were tested by the same test method as in Example 1 to evaluate its quality.

【００４６】実施例３ １，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブの平均繊度を１．２デニール、目付を４５ｇ／ｍ 2 、Ｌ−乳酸またはＤ−乳酸単位を８０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブの平均繊度を１．３デニール、目付を４８ｇ／ｍ 2としたこと以外は実施例１と同様にして生分解性不織布を製造した。 [0046] Example 3 1,4-butanediol and 1.2 denier average fineness of the long fiber web composed of high molecular weight and polymer by urethane bond polybutylene succinate polymer synthesized from succinic acid, basis weight the 45 g / m 2, L-lactic acid or D- lactic acid units composed of polylactic acid polymer containing at least 80 mol% average fineness of 1.3 denier long fiber web, except that the basis weight was 48 g / m 2 in the same manner as in example 1 was produced biodegradable nonwoven fabric.得られた長繊維ウェブを実施例１と同様の試験法により試験し、その品質を評価した。 The resulting long fiber web were tested by the same test method as in Example 1 to evaluate its quality.

【００４７】実施例４ １，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブの平均繊度を９．３デニール、目付を４５ｇ／ｍ 2 、Ｌ−乳酸またはＤ−乳酸単位を８０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブの平均繊度を９．７デニール、目付を４８ｇ／ｍ 2としたこと以外は実施例１と同様にして生分解性不織布を製造した。 [0047] The average fineness of the long fiber web composed of a polymer and a high molecular weight by urethane bonds the polybutylene succinate polymer synthesized from Example 4 1,4-butanediol and succinic acid 9.3 denier, basis weight the 45 g / m 2, L-lactic acid or D- lactic acid units composed of polylactic acid polymer containing at least 80 mol% average fineness of 9.7 denier long fiber web, except that the basis weight was 48 g / m 2 in the same manner as in example 1 was produced biodegradable nonwoven fabric.得られた長繊維ウェブを実施例１と同様の試験法により試験し、その品質を評価した。 The resulting long fiber web were tested by the same test method as in Example 1 to evaluate its quality.得られた結果を表１に示した。 The results obtained are shown in Table 1.

【００４８】 [0048]

【表１】 [Table 1]

【００４９】 [0049]

【発明の効果】表１から明らかなように、本発明の条件に合致する場合には、溶融押出機によって樹脂を溶融紡糸する際に糸切れがなく、得られる生分解性不織布は、 [Effect of the Invention] As apparent from Table 1, if it meets the conditions of the present invention, no yarn breakage during melt spinning the resin by melt-extruder, the resulting biodegradable nonwoven fabric,高強度でありながら柔軟性と地合に優れ、且つ生分解速度をコントロールすることができる。 Excellent flexibility and texture while a high strength, it is possible to and control the rate of biodegradation.本発明は、製造時の紡糸性に優れ、且つ高い強度と良好な地合、柔軟性を有した生分解性不織布を提供するという効果を奏する。 The present invention is excellent in spinnability during production, and high strength and good formation, an effect of providing a biodegradable nonwoven fabric having a flexibility.

Claims (2)

Translated from Japanese

【特許請求の範囲】 [The claims]

【請求項１】Ｌ−乳酸またはＤ−乳酸単位を８０モル％ 1. A the L- lactic acid or D- lactic acid units 80 mol%以上含有するポリ乳酸重合体からなる長繊維ウェブの片面または両面に、１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブを積層し、熱融着により繊維同士が融着した区域を間隔を置いて設けてなることを特徴とする生分解性不織布。 On one or both sides of the long fiber web composed of polylactic acid polymer containing at least a length consisting of high molecular weight and polymer polybutylene succinate polymer synthesized from 1,4-butanediol and succinic acid by urethane bonds the fibrous web is laminated, biodegradable nonwoven fabric fibers by thermal fusion is characterized by comprising spaced areas were fused.

【請求項２】該Ｌ−乳酸またはＤ−乳酸単位を８０モル％以上含有するポリ乳酸重合体からなる長繊維ウェブの平均繊度が１〜１０デニール、目付が５〜５０ｇ／ Wherein said L- lactic acid or long fibers having an average fineness is 1 to 10 denier web of the D- lactic acid unit from polylactic acid polymer containing at least 80 mol%, weight per unit area 5 to 50 g /ｍ 2 、該１，４−ブタンジオールとコハク酸から合成されるポリブチレンサクシネート重合体をウレタン結合により高分子量化した重合体からなる長繊維ウェブの平均繊度が１〜１０デニール、目付が５〜５０ｇ／ｍ 2であることを特徴とする生分解性不織布。 m 2, average fineness of 1 to 10 denier polybutylene succinate polymer comprising a polymer weight of the polymer by urethane bond long fiber web to be synthesized from the 1,4-butanediol and succinic acid, the basis weight is 5 biodegradable nonwoven fabric which is a to 50 g / m 2.