The antifouling properties of poly(2-hydroxyethyl methacrylate-co-methyl methacrylate) hydrogels were improved by the surface grafting of a brush of poly(oligoethylene glycol methyl ether acrylate) [poly(OEGA)]. The atom-transfer radical polymerization (ATRP) of OEGA (degree of polymerization = 8) was initiated from the preactivated surface of the hydrogel under mild conditions, thus in water at 25 °C. The catalytic system was optimized on the basis of two ligands [1,1,4,7,10,10-hexamethyl-triethylenetetramine (HMTETA) or tris[2-(dimethylamino)ethyl]amine (Me6TREN)] and two copper salts (CuIBr or CuICl). Faster polymerization was observed for the Me6TREN/CuIBr combination. The chemical composition and morphology of the coated surface were analyzed by X-ray photoelectron spectroscopy, attenuated total reflectance Fourier transform infrared spectroscopy, contact angle measurements by the water droplet and captive bubble methods, scanning electron microscopy, and environmental scanning electron microscopy. The hydrophilicity of the surface increased with the molar mass of the grafted poly(OEGA) chains, and the surface modifications were reported in parallel. The antifouling properties of the coatings were tested by in vitro protein adsorption and cell adhesion tests, with green fluorescent protein, β-lactamase, and lens epithelial cells, as model proteins and model cells, respectively. The grafted poly(OEGA) brush decreased the nonspecific protein adsorption and imparted high cell repellency to the hydrogel surface. [less ▲]

Cataract surgery is a routine ophthalmologic intervention resulting in replacement of the opacified natural lens by a polymeric intraocular lens (IOL). A main postoperative complication, as a result of ... [more ▼]

Cataract surgery is a routine ophthalmologic intervention resulting in replacement of the opacified natural lens by a polymeric intraocular lens (IOL). A main postoperative complication, as a result of protein adsorption and lens epithelial cell (LEC) adhesion, growth, and proliferation, is the secondary cataract, referred to as posterior capsular opacification (PCO). To avoid PCO formation, a poly(ethylene glycol) (PEG) chemical coating was created on the surface of hydrogel IOLs. Attenuated total reflectance Fourier transform infrared spectroscopy, “captive bubble” and “water droplet” contact angle measurements, and atomic force microscopy analyses proved the covalent grafting of the PEG chains on the IOL surface while keeping unchanged the optical properties of the initial material. A strong decrease of protein adsorption and cell adhesion depending on the molar mass of the grafted PEG (1100, 2000, and 5000 g/mol) was observed by performing the relevant in vitro tests with green fluorescent protein and LECs, respectively. Thus, the study provides a facile method for developing materials with nonfouling properties, particularly IOLs. [less ▲]