A composite material comprises aggregate and an elastomeric composition. The elastomeric composition comprises the reaction product of an isocyanate component and an isocyanate-reactive component. The isocyanate component comprises a polymeric isocyanate, and optionally, an isocyanate-prepolymer. The isocyanate-reactive component comprises a hydrophobic polyol and a chain extender having at least two hydroxyl groups and a molecular weight of from about 62 to about 220. The chain extender is present in the isocyanate-reactive component in an amount of from about 1 to about 20 parts by weight based on 100 parts by weight of the isocyanate-reactive component. The aggregate may be rock, crumb rubber, and/or glass. The composite material has excellent physical properties and may be formed underwater, used in various locations, and used in various applications, such as for pavement, revetments, etc. Methods of forming and using the composite material and systems for forming the elastomeric composition are also disclosed.

Claim:

What is claimed is:

1. A composite material comprising: aggregate; and an elastomeric composition comprising the reaction product of; an isocyanate component comprising a polymericisocyanate, and optionally, an isocyanate-prepolymer, and an isocyanate-reactive component comprising a hydrophobic polyol, and a chain extender having at least two hydroxyl groups and a molecular weight of from about 62 to about 220, wherein said chainextender is present in said isocyanate-reactive component in an amount of from about 1 to about 20 parts by weight based on 100 parts by weight of said isocyanate-reactive component; and wherein said elastomeric composition is present in said compositematerial in an amount of from about 1 to about 10 parts by weight based on 100 parts by weight of said composite material.

2. A composite material as set forth in claim 1 wherein said isocyanate component comprises said polymeric isocyanate and said isocyanate-prepolymer and said isocyanate-prepolymer is present in said isocyanate component in an amount of fromabout 25 to about 75 parts by weight based on 100 parts by weight of said isocyanate component.

3. A composite material as set forth in claim 2 wherein said chain extender is present in said isocyanate-reactive component in an amount of from about 5 to about 10 parts by weight based on 100 parts by weight of said isocyanate-reactivecomponent.

4. A composite material as set forth in claim 1 wherein said aggregate comprises glass.

5. A composite material as set forth in claim 1 wherein said aggregate comprises rock.

6. A composite material as set forth in claim 5 wherein said rock is: i) selected from the group of marble, beach stone, river rock, and combinations thereof; or ii) granite.

7. A composite material as set forth in claim 5 wherein said rock has an average diameter of from about 1/4 inch to about 5 inches.

8. A composite material as set forth in claim 1 wherein said aggregate comprises crumb rubber.

9. A composite material as set forth in claim 1 wherein said hydrophobic polyol comprises a natural oil polyol and wherein said natural oil polyol is castor oil.

10. A composite material as set forth in claim 1 wherein said chain extender comprises an alkylene glycol and wherein said alkylene glycol is dipropylene glycol.

11. A composite material as set forth in claim 1 wherein: i) said isocyanate-prepolymer comprises the reaction product of a diphenylmethane diisocyanate and a polyol, has an NCO content of about 22.9 wt. %, and an average NCO functionality offrom about 2 to about 3; and/or ii) said polymeric isocyanate comprises polymeric diphenylmethane diisocyanate, has an NCO content of about 31.5 wt. %, and an average NCO functionality of from about 2 to about 3.

12. A composite material as set forth in claim 1 wherein said hydrophobic polyol is present in said isocyanate-reactive component in an amount of from about 80 to about 99 parts by weight based on 100 parts by weight of said isocyanate-reactivecomponent.

13. A composite material as set forth in claim 1 wherein said aggregate is selected from the group of glass, rock, rubber crumb, and combinations thereof, said isocyanate component comprises said polymeric isocyanate and saidisocyanate-prepolymer, said isocyanate-prepolymer comprises the reaction product of a diphenylmethane diisocyanate and a polyol, said polymeric isocyanate comprises polymeric diphenylmethane diisocyanate, said hydrophobic polyol comprises a natural oilpolyol, and said chain extender comprises an alkylene glycol.

14. A composite material as set forth in claim 13 wherein said isocyanate-prepolymer is present in said isocyanate component in an amount of from about 25 to about 75 parts by weight based on 100 parts by weight of said isocyanate component,said hydrophobic polyol is present in said isocyanate-reactive component in an amount of from about 80 to about 99 parts by weight, and said chain extender is present in said isocyanate-reactive component in an amount of from about 10 to about 5 parts byweight, each based on 100 parts by weight of said isocyanate-reactive component.

15. A composite material as set forth in claim 14 wherein said natural oil polyol is castor oil, said alkylene glycol is dipropylene glycol, and said elastomeric composition is present in said composite material in an amount of from about 2.5to about 5.0 parts by weight based on 100 parts by weight of said composite material.

16. A revetment or track ballast comprising the composite material as set forth in claim 1.

17. A method of forming a composite material, said method comprising the steps of: providing aggregate; forming an elastomeric composition comprising the reaction product of; an isocyanate component comprising a polymeric isocyanate, andoptionally, an isocyanate-prepolymer, and an isocyanate-reactive component comprising a hydrophobic polyol, and a chain extender having at least two hydroxyl groups and a molecular weight of from about 62 to about 220, wherein the chain extender ispresent in the isocyanate-reactive component in an amount of from about 1 to about 20 parts by weight based on 100 parts by weight of the isocyanate-reactive component; and applying the elastomeric composition to the aggregate to form the compositematerial; wherein the elastomeric composition is present in the composite material in an amount of from about 1 to about 10 parts by weight based on 100 parts by weight of the composite material.

18. A method as set forth in claim 17 wherein: i) the step of applying is further defined as coating the aggregate with the elastomeric composition; and/or ii) the step of applying is further defined as tumble-coating the aggregate with theelastomeric composition in an apparatus; and/or iii) the step of forming and the step of applying are contemporaneous.

19. A method as set forth in claim 17 wherein: i) the isocyanate component comprises the polymeric isocyanate and the isocyanate-prepolymer and the isocyanate-prepolymer is present in the isocyanate component in an amount of from about 25 toabout 75 parts by weight based on 100 parts by weight of the isocyanate component; and/or ii) the chain extender is present in the isocyanate-reactive component in an amount of from about 5 to about 10 parts by weight based on 100 parts by weight of theisocyanate-reactive component.

20. A method as set forth in claim 17 wherein the aggregate comprises glass, rock, crumb rubber, or combinations thereof.

21. A method as set forth in claim 17 wherein the aggregate comprises rock and wherein the rock is: i) selected from the group of marble, beach stone, river rock, and combinations thereof; or ii) granite.

22. A method as set forth in claim 17 wherein: i) the hydrophobic polyol comprises a natural oil polyol and wherein the natural oil polyol is castor oil; and/or ii) the chain extender comprises an alkylene glycol and wherein the alkyleneglycol is dipropylene glycol.

23. A method as set forth in claim 17 wherein: i) the isocyanate-prepolymer comprises the reaction product of a diphenylmethane diisocyanate and a polyol, has an NCO content of about 22.9 wt. %, and an average NCO functionality of from about 2to about 3; and/or ii) the polymeric isocyanate comprises polymeric diphenylmethane diisocyanate, has an NCO content of about 31.5 wt. %, and an average NCO functionality of from about 2 to about 3.

24. A method as set forth in claim 17 wherein the hydrophobic polyol is present in the isocyanate-reactive component in an amount of from about 80 to about 99 parts by weight based on 100 parts by weight of the isocyanate-reactive component.