The surface of Ti-6Al-4V (Ti64) alloy has been modified using beamline implantation of boron. In separate experiments, Ti64 has been implanted with nitrogen using a plasma source ion implantation (PSII) technique utilizing either ammonia (NH{sub 3}), nitrogen (N{sub 2}), or their combinations as the source of nitrogen ions. Beamline experiments have shown the hardness of the N-implanted surface saturates at a dose level of {approximately} 4 {times} 10{sup 17} at/cm{sup 2} at {approximately} 10 GPa. The present work makes comparisons of hardness and tribological tests of (1) B implantation using beamline techniques, and (2) N implanted samples using ammonia and/or ...
continued below

Publishers

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this report.
Follow the links below to find similar items on the Digital Library.

Description

The surface of Ti-6Al-4V (Ti64) alloy has been modified using beamline implantation of boron. In separate experiments, Ti64 has been implanted with nitrogen using a plasma source ion implantation (PSII) technique utilizing either ammonia (NH{sub 3}), nitrogen (N{sub 2}), or their combinations as the source of nitrogen ions. Beamline experiments have shown the hardness of the N-implanted surface saturates at a dose level of {approximately} 4 {times} 10{sup 17} at/cm{sup 2} at {approximately} 10 GPa. The present work makes comparisons of hardness and tribological tests of (1) B implantation using beamline techniques, and (2) N implanted samples using ammonia and/or nitrogen gas in a PSII process. The results show that PSII using N{sub 2} or NH{sub 3} gives similar hardness as N implantation using a beamline process. The presence of H in the Ti alloy surface does not affect the hardness of the implanted surface. Boron implantation increased the surface hardness by as much as 2.5x at the highest dose level. Wear testing by a pin-on-disk method indicated that nitrogen implantation reduced the wear rate by as much as 120x, and boron implantation reduced the wear rate by 6.5x. Increased wear resistance was accompanied by a decreased coefficient of friction.

Collections

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.