Abstract

The suitability of low-cost impedance sensors for microbiological purposes and biofilm growth monitoring was evaluated. The sensors with interdigitated electrodes were fabricated in PCB and LTCC technologies. The electrodes were golden (LTCC) or gold-plated (PCB) to provide surface stability. The sensors were used for monitoring growth and degradation of the reference ATCC 15442 Pseudomonas aeruginosa strain biofilm in invitro setting. During the experiment, the impedance spectra of the sensors were measured and analysed using electrical equivalent circuit (EEC) modelling. Additionally, the process of adhesion and growth of bacteria on a sensor’s surface was assessed by means of the optical and SEM microscopy. EEC and SEM microscopic analysis revealed that the gold layer on copper electrodes was not tight, making the PCB sensors susceptible to corrosion while the LTCC sensors had good surface stability. It turned out that the LTCC sensors are suitable for monitoring pseudomonal biofilm and the PCB sensors are good detectors of ongoing stages of biofilm formation.

Abstract

This article presents the results of an examination performed on a set of samples of glass-epoxy core rods used in composite insulators with silicone rubber housings. The goal of the examination was to test the aging resistance of the core material when exposed to Direct Current (DC) high voltage. Long term exposure of a glass-epoxy core rod to DC high voltage may lead to the gradual degradation of its mechanical properties due to the ion migrations. Electrolysis of the core material (glass fiber) may cause electrical breakdown of the insulators and consequently lead to a major failure. After being aged for 6000 hours under DC high voltage, the samples were subjected to microscopic analysis. Their chemical composition was also examined using Raman spectroscopy and their dielectric losses and conductance in the broad range of frequencies were tested using dielectric spectroscopy.

Abstract

The paper presents magnetic fluid as an excellent material platform for producing more complex magnetic drug delivery systems. In addition, the paper discusses the nanoparticle morphological (electron microscopy) and structural (X-ray diffraction) characterizations. M ossbauer spectroscopy and photoacoustic spectroscopy are revisited as key tools in the characterization of the magnetic core and diamagnetic shell of the magnetic nanoparticle, respectively.

Abstract

Hydroxyapatite (HAp) has been attracting widespread interest in medical applications. In a form of coating, it enables to create a durable bond between an implant and surrounding bone tissues. With addition of silver nanoparticles HAp should also provide antibacterial activity. The aim of this research was to evaluate the composition of hydroxyapatite with silver nanoparticles in a non-destructive and non-contact way. For control measurements of HAp molecular composition and solvent evaporation efficiency the Raman spectroscopy has been chosen. In order to evaluate dispersion and concentration of the silver nanoparticles inside the hydroxyapatite matrix, the optical coherence tomography (OCT) has been used. Five samples were developed and examined ‒ a reference sample of pure HAp sol and four samples of HAp colloids with different silver nanoparticle solution volume ratios. The Raman spectra for each solution have been obtained and analyzed. Furthermore, a transverse-sectional visualization of every sample has been created and examined by means of OCT.

Abstract

The technique of electrospinning was employed to fabricate uniform one-dimensional inorganic-organic composite nanofibers at room temperature from a solution containing equal volumes of aluminum 2, 4-pentanedionate in acetone and polyvinylpyrrolidone in ethanol. Upon firing and sintering under carefully pre-selected time-temperature profiles (heating rate, temperature and soak time), high-purity and crystalline alumina nanofibers retaining the original morphological features present in the as-spun composite (cermer) fibers were obtained. Tools such as laser Raman spectroscopy, scanning and transmission electron microscopy together with energy dispersive spectroscopy and selected area electron diffraction were employed to follow the systematic evolution of the ceramic phase and its morphological features in the as-spun and the fired fibers. X-ray diffraction was used to identify the crystalline fate of the final product.

Abstract

In this work studies ofM OVPE growth of InAlGaAs/AlGaAs/GaAs heterostructures are presented. The HRXRD and SIMS measurements indicate the high structural and optical properties as well as high uniformity oft hickness and composition ofI nAlGaAs quantum wells. This work is the .rst step towards elaboration oft he technology oft he strained InAlGaAs/GaAs heterostructures for advanced optoelectronic devices working in the visible part oft he spectrum. The investigations ofSi (n-type), Zn (p-type) .-doped GaAs epilayers and centre Si-.-doped InxGa1-xAs single quantum well (SQW) are presented. The .-doping layer was formed by SiH4 or DEZn introduction during the growth interruption. The electrical and optical properties oft he obtained structures were examined using C-V measurement, EC-V electrochemical pro.ler, Raman spectroscopy (RS), photore.ectance (PR) and photocurrent (PC) spectroscopies. Technology oft hick GaN layers grown on sapphire by HVPE is very promising as a part off reestanding GaN substrates manufacturing. Further works will be focused on the optimisation of growth, separating layers from substrates and surface polishing. The in.uence oft he growth parameters on the properties of( Ga, Al)N/Al2O3 and Mg dopant incorporation was studied.

Abstract

In this paper the overview of the recent study on the rare-earth activated waveguides performed in the Optoelectronic Department of IMiO is presented. We reported on the development of rare earth-doped fluorozirconate (ZBLAN) glass fibers that allow a construction of a new family of visible and ultraviolet fiber lasers pumped by upconversion. Especially the performance of holmium devices is presented. The properties of laser planar waveguides obtained by the LPE process and the growth conditions of rare earths doped YAG layers are presented. In this paper we present also the theoretical study of the nonlinear operation of planar waveguide laser, as an example the microdisk Nd:YAG structure is discussed. We derived an approximate formula which relates the small signal gain in the Nd:YAG active medium and the laser characteristics, obtained for whispering-gallery modes and radial modes, to the output power and real parameters of the laser structure

Abstract

The paper describes an integrated laser absorption system as a potential tool for breath analysis for clinical diagnostics, online therapy monitoring and metabolic disorder control. The sensors operate basing on cavity enhanced spectroscopy and multi-pass spectroscopy supported by wavelength modulation spectroscopy. The aspects concerning selection of operational spectral range and minimization of interference are also discussed. Tests results of the constructed devices collected with reference samples of biomarkers are also presented. The obtained data provide an opportunity to analyse applicability of optoelectronic sensors in medical screening.

Abstract

The photoacoustic cell is the heart of the nondestructive photoacoustic method. This article presents a new simple lumped-components CRLC model of the Helmholtz type photoacoustic cell. This model has been compared with the well known literature models describing the Helmholtz type cells for photoacoustic spectroscopy. Experimental amplitude and phase frequency data obtained for the two photoacoustic cells have been presented and interpreted in a series of models. Results of the fitting of theoretical curves, obtained in these models, to the experimental data have been shown and discussed.

Abstract

This study characterizes the bronze jewellery recovered from the Lusatian culture urn-field in Mała Kępa (Chełmno land, Poland). Among many common ornaments (e.g. necklaces, rings, pins) the ones giving evidence of a steppe-styled inspiration (nail earrings) were also identified. With the dendritic microstructures revealed, the nail earrings prove the implementing of a lost-wax casting method, whereas some of the castings were further subjected to metalworking. The elemental composition indicates the application of two main types of bronze alloys: Cu-Sn and Cu-Sn-Pb. It has been established that the Lusatian metalworkers were familiar with re-melting the scrap bronze and made themselves capable of roasting the sulphide-rich ores. The collection from Mała Kępa has been described in terms of its structure and composition. The investigations were made by means of the energy dispersive X-ray fluorescence spectroscopy (ED-XRF), scanning electron microscopy (SEM) coupled with an energy dispersive X - ray analysis system (EDS) and optical microscopy (OM). In order to fingerprint an alloy profile of the castings with a special emphasis on the nail earrings, the data-set (ED-XRF, EDS) was statistically evaluated using multidimensional analyses (FA, DA).

Abstract

This preliminary study characterizes the bronze metalworking on a defensive settlement of the Lusatian culture in former Kamieniec (Chełmno land, Poland) as it is reflected through casting workshop recovered during recent excavations. Among ready products, the ones giving evidence of local metallurgy (e.g. casting moulds and main runners) were also identified. With the shrinkage cavities and dendritic microstructures revealed, the artifacts prove the implementing a casting method by the Lusatian culture metalworkers. The elemental composition indicates application of two main types of bronzes: Cu-Sn and Cu-Pb. Aside these main alloying additions, some natural impurities such as silver, arsenic, antimony and nickel were found which may be attributed to the origin of the ore and casting technology. The collection from Kamieniec was described in terms of its structure and composition. The investigations were made by means of the energy dispersive X-ray fluorescence spectroscopy (ED-XRF), scanning electron microscopy (SEM) coupled with an energy dispersive Xray analysis system (EDS) and optical microscopy (OM). In order to fingerprint either local or non-local profile of the alloys, the ED-XRF data-set was statistically evaluated using a factor analysis (FA).

Abstract

The spectroscopic FT-IR and FT-Raman methods allowed to identify the cross-linking process of the aqueous composition of poly(acrylic acid)/sodium salt of carboxymethyl starch (PAA/CMS-Na) applied as a binder for moulding sands (as a novel group binders BioCo). The cross-linking was performed by physical agent, applying the UV-radiation. The results of structural studies (IR, Raman) confirm the overlapping of the process of cross-linking polymer composition PAA/CMS-Na in UV radiation. Taking into account the ingredients and structure of the polymeric composition can also refer to a curing process in a binder - mineral matrix mixture. In the system of bindermineral matrix under the influence of ultraviolet radiation is also observed effect of binding. However, the bonding process does not occur in the entire volume of the investigated system, but only on the surface, which gives some possibilities for application in the use of UV curing surface of cores, and also to cure sand moulds in 3D printing technology

Abstract

In this paper, the effect of the resolution of an analogue-to-digital converter (ADC) on the accuracy of timedomain low-frequency electrical impedance spectroscopy is examined. For the first time, we demonstrated that different wideband stimuli signals used for impedance spectroscopy have different sensitivities to the resolution of ADC used in impedance spectroscopy systems. We also proposed Ramp and Half-Gaussian signals as new wideband stimulating signals for EIS. The effect of ADC resolution was studied for Sinc, Gaussian, Half-Gaussian, and Ramp excitation signals using both simulation and experiments. We found that Ramp and Half-Gaussian signals have the best performance, especially at low frequencies. Based on the results, a wideband electrical impedance spectroscopy circuit was implemented with a high accuracy at frequencies bellow 10 Hz.

Abstract

Point of present exploration was to figure out the anticorrosion activity of Acacia Cyanophylla (Saligna leaves) extract on the corrosion of mild steel in dilute sulfuric acid medium, using weight loss measurements and electrochemical impedance spectroscopy. The result of the study revealed that the extract act as a potent inhibitor on mild steel in acid medium. The increase in inhibitor concentration and immersion time showed a positive effect on inhibition efficiency. EIS exhibited one capacitive loop which indicates that the corrosion reaction is controlled by charge transfer process. The increase of phase shift (n) in presence of (ACLE) lower surface roughness. This change reveals the adsorption of the inhibitor compound on the steel surface. According to the results of weight loss measurements, the adsorption of the extract on the steel surface can be described by the Langmuir isotherm. The inhibition mechanism of (ACLE) molecules involves physical interaction between the inhibitor and metal surface. Additionally, Protective film formation against acid attack was confirmed by FT-IR and AFM techniques.

Abstract

Sensing technology has been developed for detection of gases in some environmental, industrial, medical, and scientific applications. The main tasks of these works is to enhance performance of gas sensors taking into account their different applicability and scenarios of operation. This paper presents the descriptions, comparison and recent progress in some existing gas sensing technologies. Detailed introduction to optical sensing methods is presented. In a general way, other kinds of various sensors, such as catalytic, thermal conductivity, electrochemical, semiconductor and surface acoustic wave ones, are also presented. Furthermore, this paper focuses on performance of the optical method in detecting biomarkers in the exhaled air. There are discussed some examination results of the constructed devices. The devices operated on the basis of enhanced cavity and wavelength modulation spectroscopies. The experimental data used for analyzing applicability of these different sensing technologies in medical screening. Several suggestions related to future development are also discussed.

Abstract

Cast axes are one of the most numerous categories of bronze products from earlier phases of the Bronze Age found in Poland. They had multiple applications since they were not only used objects such as tools or weapons but also played the prestigious and cult roles. Investigations of the selected axes from the bronze products treasure of the Bronze Age, found in the territory of Poland, are presented in the hereby paper. The holder of these findings is the State Archaeological Museum in Warsaw. Metallurgical investigations of axes with bushing were performed in respect of the casting technology and quality of obtained castings. Macroscopic observations allowed to document the remains of the gating system and to assess the range and kind of casting defects. Light microscopy revealed the microstructure character of these relicts. The chemical composition was determined by means of the X-ray fluorescence method with energy dispersion (ED-XRF) and by the scanning electron microscopy with X-ray energy dispersion analysis in micro-areas (SEM-EDS). The shape and dimensions of cores, reproducing inner parts of axes were identified on the basis of the X-ray tomography images. Studies reconstructed production technology of the mould with gating system, determined chemical composition of the applied alloys and casting structures as well as revealed the casting defects being the result of construction and usage of moulds and cores.

Abstract

Investment casting technology that utilizes lost-wax casting is one of the most-important achievements of ancient society. In Lower Silesia, Poland (Grzybiany, Legnica county), a 7-6 BC casting workshop was discovered with numerous artifacts, confirming the existence of the manufacturing process of metal ornaments using ceramic molds. The paper presents the research of molds and casts from the Bronze and Early Iron Ages. Microscopic analyses of the casting molds were performed, along with radiographic and chemical composition tests of the artifacts (the latter employing the use of the X-ray fluorescence spectroscopy method). The clustering method was used for alloy classification. The microstructure was analyzed by means of Scanning Electron Microscopy with Energy Dispersive Spectroscopy. Conclusions from the research were utilized in further experiments

Abstract

Studies of electrical properties, including noise properties, of thick-film resistors prepared from various resistive and conductive materials on LTCC substrates have been described. Experiments have been carried out in the temperature range from 300 K up to 650 K using two methods, i.e. measuring (i) spectra of voltage fluctuations observed on the studied samples and (ii) the current noise index by a standard meter, both at constant temperature and during a temperature sweep with a slow rate. The 1/f noise component caused by resistance fluctuations occurred to be dominant in the entire range of temperature. The dependence of the noise intensity on temperature revealed that a temperature change from 300 K to 650 K causes a rise in magnitude of the noise intensity approximately one order of magnitude. Using the experimental data, the parameters describing noise properties of the used materials have been calculated and compared to the properties of other previously studied thick-film materials.

Abstract

This work shows a time-domain method for the discrimination and digitization of parameters of voltage pulses coming from optical detectors, taking into account the presence of electronic noise and afterpulsing. Our scheme is based on an FPGA-based time-to-digital converter as well as an adjustable-threshold comparator complemented with commercial elements. Here, the design, implementation and optimization of a multiphase TDC using delay lines shorter than a single clock period is also described. The performance of this signal processing system is discussed through the results from the statistical code density test, statistical distributions of measurements and information gathered from an optical detector. Unlike dual voltage threshold discriminators or constant-fraction discriminators, the proposed method uses amplitude and time information to define an adjustable discrimination window that enables the acquisition of spectra.

Abstract

The surface properties of particles emitted from six selected coal-fired power and heating plants in Poland have been studied in this work for the first time. Samples were collected beyond the control systems. Surface composition of the size-distributed particles was obtained by photoelectron spectroscopy (XPS). The reflection of the smallest, submicron particles was also measured to calculate their specific/mass absorption. The surface layer of the emitted particles was clearly dominated by oxygen, followed by silicon and carbon. The sum of the relative concentration of these elements was between 85.1% and 91.1% for coarse particles and 71.8–93.4% for fine/submicron particles. Aluminum was typically the fourth or fifth, or at least the sixth most common element. The mass absorption of the submicron particles emitted from the studied plants ranged from 0.02 m2g-1 to 0.03 m2g-1. Only specific absorption obtained for the “Nowy Wirek” heating plant was significantly higher than in other studied plants probably because the obsolete fire grate is used in this heating plant. The obtained results suggest that the power/heating-plant-emitted fine particles contain less carbonaceous material/elemental carbon on their surfaces than those that are typical in urban air.