Abstract

The rolling fatigue lives (RFL) of five kinds of silicon nitride balls were investigated. Four kinds of Si3N4 balls were fabricated using different raw materials, sintering aids and sintering conditions, Commercially available Si3N4 ball was also studied for comparison. All the balls were finished up to the dimensional accuracy of Grade 10 defined in KS B 2001 (Steel Balls for Ball Bearings) with a size of 9.525mm. RFL tests were then conducted under the initial theoretical maximum contact stress 6.38 GPa and the spindle speed 10,000 rpm. Gear oil was provided by oiled race as lubricant. The results of RFL test indicated the prerequisitic conditions for the long rolling life of Si3N4ball : (1) the high density, (2) mjcrostructures consisted of small uniformly distributed grains, (3) little glassy phase in grainboundary, and (4) little crystalline phase and secondary phase that induces residual thermal stress due to the differences of thermal expansion coefficient with Si3N4Phase.

References

No relevant information is available
If you register references through the customer center, the reference information will be registered as soon as possible.