Article Synopsis

The status, concepts and challenges toward catalysts free of platinum group metal (pgm) elements for proton-exchange membrane fuel cells (PEMFC) are reviewed. Due to the limited reserves of noble metals in the Earth’s crust, a major challenge for the worldwide development of PEMFC technology is to replace Pt with pgm-free catalysts with sufficient activity and stability. The priority target is the substitution of cathode catalysts (oxygen reduction) that account for more than 80% of pgms in current PEMFCs. Regarding hydrogen oxidation at the anode, ultralow Pt content electrodes have demonstrated good performance, but alternative non-pgm anode catalysts are desirable to increase fuel cell robustness, decrease the H2 purity requirements and ease the transition from H2 derived from natural gas to H2 produced from water and renewable energy sources.

1. Introduction

1.1 Opportunities for PEMFCs

Electrochemical devices, and PEMFCs in particular, are under intense development for a cleaner and more efficient use of energy, including the use of renewable electricity for transportation (1). While rechargeable batteries directly store and discharge electric power, H2/air PEMFCs convert the chemical energy of H2 into electricity and heat. Today, the lion’s share of H2 production comes from natural gas. In the future, H2 could however be produced at competitive price and with lower environmental impact from water and renewable energy. The power-to-gas and gas-to-power consecutive conversions needed to use H2 as an energy carrier might seem a priori less attractive than the reversible storage of electricity in batteries due to its higher complexity and lower roundtrip energy efficiency. However, technical requirements and customer acceptance can favour fuel cells over batteries for certain markets. In the automotive sector for example, lithium-ion battery electric vehicles (BEV) offer shorter driving range than internal combustion engine (ICE) vehicles. In contrast, H2-powered PEMFC vehicles have already demonstrated a driving range of 500 km and refuelling time of less than 4 min (2, 3). Whether battery or fuel cell, the electrification of the automobile could significantly cut carbon dioxide emissions (25% of CO2 emissions originated from the transport sector in 2010 (4)) and reduce our reliance on fossil fuels. Otherwise, CO2 emissions from road transportation will continue increasing over the next decades, due to an increased global fleet of vehicles (Figure 1).

H2 is often perceived as more dangerous than gasoline-fuelled ICE. However the low density of H2 naturally prevents the detonation limit from being reached in an unconfined space. BEVs are distinctly associated with low driving range and the difficulty in knowing the instantaneous state-of-charge of a battery (5). Considering systems able to deliver the same electric power (kW), the weight of a H2-tank/PEMFC stack system becomes systematically lower than that of a rechargeable Li-battery above a certain threshold amount of energy (kWh). While the exact threshold value depends on the technology status and also on the mass of the car, threshold values of 20–30 kWh have been estimated (1, 2). As a comparison, 10 kWh is the electrical energy needed to move a mid-size car over 100 km (1).

While a BEV with longer driving range needs a proportionally higher mass of battery to store more energy, a H2-tank/PEMFC system only needs a larger tank to store more energy, with low associated incremental mass. This simple fact favours H2-PEMFC systems for transport applications requiring long driving range (Figure 2). However, when a short driving range is acceptable, BEVs are more energy efficient than fuel cells (2). Pure BEVs and fuel cell electric vehicles (FCEV) may therefore target different segments of the automotive market (1). Other important applications of PEMFCs are as backup power systems, and for combined heat and power (CHP) (6). For backup power, the chemical energy contained in H2 can be stored for years without ‘discharge’. For CHP, the cell voltage of the PEMFC can be advantageously controlled during operation to tune the electric and thermal power outputs. About 140,000 PEMFC units for CHP have been installed in Japan between 2009 and 2015 and this application is also taking off in South Korea and Europe (6).

Fig. 2.

(a) Calculated energy storage system volume for an electric vehicle (EV) equipped either with a compressed-H2 storage/PEMFC system or with various battery technologies as a function of the vehicle range; (b) same comparison but for the estimated mass of the energy storage and conversion system. The power trains are adjusted to provide a zero to 97 km h–1 acceleration time of 10 s. Reproduced from (2) with permission from Elsevier

The remaining technical challenges for PEMFCs are lowered cost and improved durability, with the electrode catalysts and membrane ionomer materials being at the heart of the vital functions and lifetime of a PEMFC. While at low production volumes, the global demand of Pt for PEMFCs is not high and the share of the Pt cost in the PEMFC stack cost is not excessive, both those scalars would increase dramatically in the case of a massive deployment of PEMFCs. The share of Pt catalyst to fuel cell stack cost would increase due to decreased cost for all other components through economies of scale (Figure 3) (7). Assuming a constant Pt price over time and unchanged Pt mass per rated power of PEMFC (kWelectric), the stack cost would reach a lower-value plateau, nearly incompressible upon further increased production volumes. In parallel, the ratio of Pt-to-stack cost would increase to ca. 50% (Figure 3). It must be noted that this percentage is a conservative estimation, reached assuming a constant Pt price. It is likely, however, that the scarcity of Pt combined with increased demand would lead to increased price. This could possibly lead to an increased stack cost (instead of a levelled-off cost above ca. 100,000 units per year), above a certain threshold of volume production. This may impede reaching (or staying at, in the case of millions of units produced per year) the cost target of US$20 kWelectric–1 for an automotive PEMFC stack (8). Reaching but also staying at this cost is necessary for PEMFCs to be cost competitive with ICE and affordable to the wide public.

Fig. 3.

Predicted automotive PEMFC stack cost as a function of annual volume production. The predicted cost is based on the 2016 automotive technology, including in particular 0.21 gPt kWel (0.116 mgPt cm–2 at cathode, 0.018 mgPt cm–2 at anode). Graph drawn from data in (7), data used with permission from Strategic Analysis Inc, USA

The particular importance of the cathode catalyst (oxygen reduction reaction (ORR) catalysis) is introduced in Section 2, while the anode catalyst (hydrogen oxidation reaction (HOR) catalysis) opportunities are discussed in Section 3. This review gives a focused account of recent achievements and discusses the needs and possibilities toward the rational design of improved non-pgm cathode layers and opportunities in non-pgm anode catalysts. Comprehensive reviews and book chapters on pyrolysed metal-nitrogen-carbon (Me-N-C, where ‘Me’ is a transition metal) cathode catalysts and inorganic non-pgm anode catalysts for PEMFCs can be found elsewhere (9–12).

2. Non-pgm Cathode Catalysts

2.1 The Need for Non-pgm Cathode Catalysts

Due to the much slower kinetics of the ORR than those of the HOR on Pt surfaces, 80–90% of Pt in H2-fuelled PEMFCs is currently positioned at the cathode (13). In this context, the development of Pt-based catalysts with higher ORR activity normalised per mass Pt is under intense investigation (14–16), with the practical objective of reducing the Pt content in automotive PEMFC stacks down to the current pgm content in catalytic converters of ICE-powered automobiles (1–4 g depending on vehicle size, engine types and local regulations on air quality). The very high ORR activity of some Pt nanostructures (such as Pt nanoframes or jagged nanowires) recently observed in rotating-disk-electrode measurements remain to be transposed to the PEMFC environment, and their long-term durability proven. In addition, a very high turnover frequency for the ORR on a small number of active sites in the cathode, while being a dream for electrocatalysis scientists, may turn out to be an issue for membrane electrode assembly (MEA) developers due to enhanced local O2 diffusion barriers in a PEMFC cathode with low volumetric density of active sites (17, 18). The replacement of Pt-based catalysts with pgm-free cathode catalysts is considered a holy grail. Ideally, highly active and durable pgm-free cathode catalysts could replace Pt-based cathodes in PEMFCs designed for all types of markets. Alternatively, pgm-free cathodes not meeting the stringent durability and power performance targets of the automotive industry may be competitive for other applications (for example, backup power, mobile applications or CHP) (16).

The pgm-free materials that have hitherto displayed the highest ORR activity when tested in aqueous acid medium or in single-cell PEMFC are pyrolysed Me-N-C catalysts, with the metal being iron or cobalt (19, 20). Me-N-C catalysts have been prepared from numerous precursors of metal, nitrogen and carbon via the optimisation of the precursor ratio, metal content and pyrolysis conditions that must be adapted to each system of precursors (10). The nature of the metal-based active sites in such Me-N-C catalysts is fundamentally different from that in Pt-based catalysts (compare Figures 4(b), 4(c) and 4(d) to Figure 4(a)). The most active sites for ORR in pyrolysed Me-N-C catalysts are, from the most recently established knowledge, single metal-ions strongly coordinated with nitrogen ligands (MeNx moieties, x being on average 4), and these MeNx moieties are covalently integrated in graphene, or disordered graphene, sheets (Figure 4) (21, 22, 23–25). The local coordination of such MeNx moieties resembles the metal-ion coordination in phthalocyanine and porphyrin compounds (23), but their covalent integration in the electron-conductive carbon matrix distinguishes them from these well-defined organic compounds, and is critical to reach high current densities in PEMFC.

2.2 Concepts for the Design of Me-N-C Catalysts and Catalyst Layers

Research and development (R&D) efforts and interest in non-pgm catalysts for the ORR in acid medium have never been so intense, as witnessed by a rising number of research groups working on the topic but also an increasing number of R&D funding calls dedicated to this class of catalysts, for example in Europe from the Fuel Cells and Hydrogen 2 Joint Undertaking (FCH 2 JU) (26), and in the USA from the US Department of Energy (DOE) (27). In the USA, R&D efforts in non-pgm catalysts for PEMFC are now organised by the Electrocatalysis Consortium (ElectroCat). A broader incentive to reduce the reliance on Critical Raw Materials and increase their recycling was also initiated by the European Union (EU) for various new energy technologies (28). Two companies are currently engaged in the development of Me-N-C and other non-pgm catalysts for PEMFCs (Pajarito Powder, USA and Nisshinbo Holdings, Japan). In September 2017, Ballard, Canada, and Nisshinbo Holdings announced the first portable PEMFC (30 W) commercialised with a non-pgm cathode catalyst (29). This interest in Me-N-C catalysts and closer shift towards application is the result of important progress in the field since 2009, with breakthroughs achieved in the ORR activity reached at high cell voltage in single-cell PEMFC (30), power density at cell voltage experienced during practical operation (0.5–0.7 V range) (22, 31), and understanding of the nature of the active sites (21, 22, 23, 25) and how they catalyse the ORR at atomistic level (24, 32, 33). Table I gives examples of synthesis strategies and corresponding ORR current density measured in PEMFC at 0.9 V (ORR ‘activity’) for some of the most active Fe-N-C catalysts to date. The cathode catalyst loading used in each work is also indicated in the second column (mgFe-N-C cm–2). Within a certain range (typically 0.5 mgFe-N-C cm–2 to 5 mgFe-N-C cm–2), the current density at 0.9 V increases proportionally with cathode catalyst loading. Based on this, the current density at 0.9 V expected for a loading of 5 mgFe-N-C cm–2 is indicated in the third column in Table I. It must be noted that proportionally increased current density with increased cathode loading is restricted to low current. At high current density (>200 mA cm–2), the cell performance is also impacted by mass- and charge-transport across the cathode active layer (Figure 5). Oxygen transport limitation in a thick cathode is particularly exacerbated when it is fed with air (31, 34), which is the case for almost all PEMFC applications.

While the target in the early stage of non-pgm catalyst development exclusively focused on the activity at high potential (volumetric activity or current density at 0.8 V or 0.9 V), the activity target is now accompanied by a power performance target (PEMFC operating point of typically 0.6–0.7 V) (see Table II). The volumetric-activity concept was specifically defined for non-pgm catalysts by the General Motors Fuel Cell group, USA, in 2003 (40). The volumetric activity is defined as the areal current density of a non-pgm cathode normalised by the cathode thickness (A cm–3, reported at 0.8 V or 0.9 V). As is valid for the Fe-N-C loading effect within certain conditions, the proportionality between current density of the cathode (when it is controlled by electrokinetics) and cathode thickness can be assumed to be valid within a certain range of thickness, Equation (i):

aUS DOE target is equivalent to a Pt-cathode with mass activity of 44 A g–1Pt at 0.9 V and a loading of 0.1 mgPt cm–2

with J the current density (A cm–2), jv the volumetric activity (in A cm–3 at 0.8 V or 0.9 V) and t the cathode thickness (cm). As one can see, a possible approach to increase the current density at high potential may consist of increasing the thickness of the cathode layer (Figures 5(a) and 5(b)). From a cost perspective, this is feasible, but it faces practical limitations due to increasing average path lengths for O2, protons and electrons in order to reach the active sites. The opposite directions of the O2 and protons flow can lead to particularly severe mass-transport limitations if they co-act to form gradients of O2 concentration and electrochemical potential, respectively (schemed as fading arrows in Figure 5). With current MEA technology, 100 μm is considered the upper realistic thickness limit for a Fe-N-C layer. This is already 10 times thicker than usual Pt-based cathode layers (with a 50% Pt/C catalyst and a cathode loading of 0.4 mgPt cm–2, the electrode thickness is ca. 10 μm). The layer thickness for Pt/C and Fe-N-C catalysts alike is governed by the carbon loading, with apparent density of 0.37–0.40 gcarbon from catalyst per cm3 of electrode usually observed (30, 31, 40)). We can extract from this a rule-of-thumb of 25 μm electrode-thickness increment per 1 mg cm–2 of carbon material from the catalyst. Future efforts should thus focus on improving both the volumetric activity of Me-N-C catalysts and the mass-transport properties of Me-N-C layers (Figures 5(c) and 5(d), respectively), to ultimately combine advances in activity and transport properties to compete with Pt-based cathode layers on the whole range of current density (Figure 5(e), curve E).

For Pt-based catalysts in contrast, there is no incentive to increase performance by increasing the Pt loading at the cathode, because Pt is expensive. The trend is opposite, with attempts to reach break-even performance (same current density at a given cell voltage) but with lower Pt loading than today. The key parameter for pgm-based catalysts is the mass activity, iM. Equation (ii):

(ii)

with J the current density (A cm–2), iM the mass activity (in mA mgPt–1 at 0.9 V) and L the Pt loading at the cathode (mgPt cm–2). Reporting the activity of pgm-based catalysts as a mass activity (A gpgm–1) and of non-pgm catalysts as a volumetric activity (A cm–3 cathode) arises therefore from the different nature of the main limitations (cost for pgm-based cathodes and performance for non-pgm cathodes) (16). The targets set for non-pgm catalysts for automotive application in the recent FCH 2 JU call of 2017 (26) and that of the US DOE Office of Energy Efficiency & Renewable Energy (EERE) (27) are reported in Table II. By comparing Table I and Table II, one can see that today’s most active Fe-N-C catalysts could reach, at a cathode loading of 5 mgFe-N-C cm–2, ca. one-third to half of the current density targets at 0.9 V set for the next generation of pgm-free catalysts.

While promising, such cathode layers should also show mass-transport properties appropriate to operation at high current density. Figure 6 shows representative examples of the best power performance single-cell PEMFC obtained with Fe-N-C cathodes and Pt-based anodes, with the cathode fed with fully humidified O2 (Figures 6(a)–6(c)) or fully humidified air (Figure 6(d)). At 0.6 V, the current density reaches 1.0–1.2 A cm–2 in pure O2 and the peak power density is nearly 1 W cm–2 at around 0.4–0.5 V (Figures 5(a), 5(b) and 5(c)) (22, 31, 34). The use of a zinc-based zeolitic imidazolate metal-organic-framework (ZIF-8) as sacrificial precursor of carbon and nitrogen resulted in 2011 in a more open structure and higher accessibility to O2 of the FeNx sites formed during pyrolysis (Figure 5(a)) (31). Since then, ZIF-8 has been extensively studied for the preparation of highly microporous Fe-N-C and also N-C materials (41). Other metal organic frameworks (MOFs) have also been investigated, but Zn-based MOFs are so far the best candidates, and in particular the subcategory of ZIFs (39, 42, 43). The advantage of such ZIFs is the low boiling point of zinc (907°C). During the pyrolysis at T > 950°C, most Zn (undesired in final Fe-N-C catalysts) is evacuated as volatile products while Fe stays. Acid leaching of excess Zn is thus avoidable. While high specific area and high microporous area in particular (pores with width ≤2 nm) are important for reaching high electrocatalytic activity with Fe-N-C catalysts (22, 30, 44), the connection between micropore-hosted FeNx moieties and the macroporous structure of the electrode is an important key for proper accessibility by O2. Mesoporosity can be introduced during the catalyst synthesis preparation (for example, with a silica template approach or pore-forming agents (38, 45, 46)), but macroporosity often depends on the electrode preparation method as a whole, not only on intrinsic catalyst morphology (47). An original approach to combine the microporosity of ZIF-8 derived Fe-N-C catalyst with macroporosity in the electrode resorted to the electrospinning of Fe-doped ZIF-8 with a carrier polymer (34). The carrier polymer forms fibrous structures, imparting inter-fibre macroporosity in the final electrode structure. Another broad approach for the synthesis of highly active Fe-N-C catalysts has involved the use of sacrificial monomers or polymers as C and N sources (48, 49). Figure 5(c) shows the H2/O2 polarisation curve with Fe-N-C cathode prepared from the pyrolysis of an iron salt and two different monomers, aniline and cyanamide. The two different monomers helped in forming a bimodal porosity, with the addition of cyanamide increasing greatly the microporous surface area in the final Fe-N-C catalyst (22).

While the beginning-of-life H2/O2 polarisation curves of single-cell PEMFC comprising Fe-N-C cathodes now approach those of Pt/C cathodes, the performance in H2/air conditions (needed for use in technologically-relevant conditions) is facing severe mass-transport issues. Figures 6(c) and 6(d) show the effect, for a same Fe-N-C cathode, of switching from pure O2 to air. The power density is reduced by a factor >2, and the polarisation curves on air are characterised by a strong bending above ca. 0.4 A cm–2. This bending occurs at lower current densities than when using Pt/C cathodes, likely due to a much greater thickness of Fe-N-C cathodes at a loading of 4 mgFe-N-C cm–2, relative to Pt/C cathodes of typically 0.4 mgPt cm–2 (0.6 gcarbon cm–2, assuming a typical 40% Pt/C catalyst). Such Fe-N-C cathodes are typically about 80–100 μm thick while Pt/C cathode thickness is ≤20 μm.

Another practical advantage of pgm-free Me-N-C cathode catalysts is their strong resistance to poisoning, while Pt-based catalysts suffer from severe poisoning from various species, including some gases that can be present at trace amounts in fossil-derived H2 (Figure 7) (50) but also anions, including chloride anions that are commonly encountered in field applications.

Fig. 7.

(a) H2-O2 polarisation curve for an MEA comprising either a Fe-N-C cathode (4 mg cm–2 loading) or a Pt/C cathode (0.4 mgPt cm–2); cell voltage before and after addition of: (b) 83 ppm H2S; (c) 77 ppm toluene; and (d) 163 ppm benzene in the cathode gas stream. Reproduced with permission from (50). Published by the Royal Society of Chemistry

In summary, further improvement of the power performance of Me-N-C cathode layers in PEMFCs can be reached by either increasing the catalyst activity (the cathode can then be made thinner, while preserving the ‘apparent’ cathode activity) or by increasing the reactant transport properties of the cathode layer, including long-distance transport (through the porous cathode) and short-distance transport (which can be modulated by catalyst morphology or agglomerate size). The major experimental efforts have hitherto focused on increasing the ORR activity of Me-N-C materials. Such efforts are still critical to further increase the activity, selectivity and durability of such catalysts, but work on cathode layer design and catalyst morphology is also critical to improve non-pgm cathode behaviour at high current density when fed with air.

2.3 Deconvoluting Activity of Me-N-C Catalysts into Site Density and Turnover Frequency

If 100–125 μm remains the upper limit of practical Me-N-C layer thickness in the future, then further increasing the current density at 0.9 V will require increasing the volumetric activity. This can mainly be achieved via increasing either the number of active sites per unit volume (site density, SD, i.e. the number of sites that can be electrochemically addressed) or the specific activity for ORR (turnover frequency, TOF) of single sites, Equation (iii):

(iii)

where SD has units of sites cm–3, TOF has units of electrons site–1 s–1 and e is the electric charge of one electron (C electron–1). On one hand, increasing the wt% Pt on a support (typically, carbon powder) nearly proportionally increases the apparent activity of the Pt-supported catalyst. Pt nanoparticles of 2–3 nm size can now be grown on carbon supports up to ca. 50 wt% Pt on carbon (51) before the average Pt particle size significantly increases. This allows high Pt mass and Pt surface area per volume of electrode to be reached. As a consequence, Pt-based cathodes are highly active but at the same time relatively thin (5–15 μm), which secures high accessibility by O2, protons and electrons. For pyrolysed Fe-N-C or Co-N-C catalysts, the situation is different. While the metal atoms are atomically dispersed as Me-Nx moieties at low metal content (up to ca. 3 wt% metal (Fe or Co) on N-C, as is the case for the catalysts of Figure 4), at higher metal contents the metal atoms aggregate during pyrolysis to form reduced metallic particles or metal carbides. Such crystalline structures are often partially or totally surrounded by graphitic shells during pyrolysis, which protects them somewhat from the acidic environment during electrochemistry. While such core-shell Metal@N-C structures may have some ORR activity in acidic medium, many observations show that their intrinsic activity is much less than that of the atomically dispersed Me-Nx moieties (52). As a consequence, Me-N-C catalysts display a much lower weight content (<5 wt%) of active metal relative to Pt/C catalysts (50 wt%). From a given supposed wt% of potentially active metal in Me-N-C material (MeNx moieties in the bulk or on the surface), the atomic mass and the utilisation factor (ratio of electrochemically addressable MeNx moieties to total number of moieties in a given catalyst), it is possible to calculate expected SD values. Table III shows that only a slightly lower SD-value is calculated for Fe-N-C (3 wt% Fe) vs. 50 wt% Pt/C catalyst if one assumes that the site utilisation of Fe-Nx moieties is 100%. Also of practical interest, it in turn implies that the loading of FeNx sites per cm2 of MEA is only four times higher for a 100 μm thick Fe-N-C cathode than for a 10 μm thick Pt/C cathode (Table III). Thus, as a result of combined constraints in cathode layer thickness and in active metal content in pyrolysed Fe-N-C catalysts, these straightforward calculations imply that, in order to reach a same current density at 0.8 V or 0.9 V, such a Fe-N-C cathode must comprise FeNx active sites with a TOF that is in fact very comparable to that of surface-exposed Pt atoms. Table III also reports the numbers calculated assuming that only ¼ of the Fe-Nx moieties are utilised (on the surface). The assumed utilisation factor of 0.25 is in line with very recent quantifications of site utilisation for such materials (see later).

Table III

Examples of Site Density and Site Loading Numbers for Iron-Nitrogen-Carbon and Platinum on Carbon Catalysts for Oxygen Reduction Reaction as well as Ni(P2RN2R′)n+a,b,c

bUltra-low loading of Pt/C for HOR. The value of 0.4 gcarbon per cm3 of electrode volume was assumed for all catalysts. For Fe-N-C, it was assumed that either 100% or 25% of the Fe-Nx moieties are surface-exposed (participate in the ORR), while for Pt/C, it was assumed that ¼ of the Pt atoms are surface exposed (ratio corresponding to Pt particles of ca. 2–3 nm)

cThis Pt site utilisation expresses only the ratio of surface Pt atoms to all Pt atoms. We highlight however that not all Pt surface sites are equivalent in terms of TOF, with terrace sites and concave coordinated Pt sites being more active for ORR (54, 55)

dFor a 100 μm-thick electrode

eFor a 10 μm-thick electrode

fFor a 25 μm-thick electrode

Some possible pathways toward increased activity of Me-N-C catalysts are schemed in Figure 8, reached via increasing either the SD or TOF (Equation (iii)). While increasing the metal content without formation of metallic particles during pyrolysis may remain limited, there might be some gain possible relative to the present status (see Figure 4). Increased density of defects in graphene sheets (in-plane sites) or increased edge length per mass of carbon (edge sites) could allow increase of the density of FeNx active sites (step B in Figure 8). At a fixed bulk metal content, preferential formation of FeNx sites on the surface of the carbon material, rather than statistical distribution on the surface and in the bulk, could increase the utilisation factor of FeNx sites (in electrocatalysis, only the sites at the solid-electrolyte interface are electrochemically active) (step C in Figure 8). The utilisation factor of statistically-dispersed FeNx moieties could also be increased via increased carbon surface area (decreased average number of stacked graphene sheets in the material, step D in Figure 8). The TOF of single metal-atoms in MeNx moieties might also be increased, either through the preferential formation of certain MeNx moieties (for example edge vs. in-plane, if edge defects are more active, or vice versa if in-plane defects are shown to be more active) or the formation of more complex sites. One such possibility is the formation of binuclear Fe2Nx sites, where the Fe–Fe distance is commensurate with the O=O bond distance, allowing the two Fe centres to work faster than two individual FeNx moieties (32). Other additional parameters have been proposed or investigated to tune the TOF, such as bi-metallic catalysts (for example Fe-Mn or Fe-Co) (56, 57), and co-doped carbon by nitrogen and another light element (such as sulfur, phosphorus or boron) (58). The introduction of chemical elements other than Fe(Co), N and C could indeed offer broader perspectives on the electronic properties of the graphene sheets, and thereby of the electron density at the Fe centres (59). The O2 binding energy and therefore the TOF might be increased further with one of those approaches.

Fig. 8.

Scheme of possible ways to increase the volumetric activity of Me-N-C catalysts: A typical Fe-N-C catalyst with four stacked graphene sheets including in-plane and edge FeNx sites. Only the FeNx sites on the top and bottom sheets are O2 accessible; B Fe-N-C catalyst with higher Fe content, including O2-accessible and O2 inaccessible sites; C Fe-N-C catalyst with preferential location of FeNx sites on the top and bottom graphene sheets (O2-accessible surfaces); D Fe-N-C catalyst with higher specific surface area (lower number of stacked graphene sheets); E Fe-N-C catalyst featuring binuclear Fe2Nx sites with possible cooperative O=O bond dissociation on the two Fe centres

Whether the MeNx sites are mostly located in-plane or on the edge of graphene or disordered graphene sheets is important (22, 23, 30, 60, 61). Answering that question would indicate whether the in-plane size of graphene sheets must be decreased or the average number of stacked layers decreased. For a set of Fe-N-C catalysts prepared via the silica template method and using nicarbazin and iron nitrate as N, C and Fe precursors, it was shown that decreased stacking led to increased activity, implying that most of the active sites are in-plane moieties for this synthesis (Figure 9) (60). Interestingly, the carbon matrix was highly graphitic for this set of catalysts (60), in contrast with what is usually observed on most Fe-N-C catalysts that are highly ORR-active (31, 62–64). The average number of stacked graphene layers is typically only 4–6, as estimated from Raman spectroscopy, for high-surface-area amorphous carbon structures in Fe-N-C catalysts. Formation of large in-plane voids (several carbon atoms removed, see for example Figure 4(b)) could also allow O2 access to in-plane FeNx moieties that are not situated in the uppermost graphene layer of a graphitic crystallite, thereby breaking the relationship between stacking number and ORR activity. Such a relationship is otherwise expected, with the hypothesis that most FeNx sites are located in-plane.

Fig. 9.

Effect of average number of stacked graphene sheets on ORR activity of pyrolysed Fe-N-C catalyst: (a) Scheme of in-plane and edge FeNx sites and O2 (in)accessibility; (b) PEMFC polarisation curves with H2/O2 or H2/air feed; (c) negative correlation between current density at 0.8 V read on the H2/air polarisation curve and the average number of stacked graphene layers for a set of 12 Fe-N-C catalysts. Test conditions: 80°C, 100% RH, 1.5 bar (H2/O2) and 2.5 bar (H2/air) total gas pressures. Reprinted with permission from (60). Copyright (2017) American Chemical Society

In guiding experimental efforts, disentangling the overall volumetric activity into SD and TOF (Equation (iii)) is not only of scientific importance but also has technological implications on the development of promising catalyst preparation routes and on the design of high-performance non-pgm cathode layers. For example, a low SD-value implies stringent requirements on local mass-transport properties near active sites, for a given current density of the cathode layer. Once methods are developed for quantifying SD in Me-N-C catalysts, TOF values can then be deduced from the combined knowledge of the experimental values of activity and SD. As an example, TOF values much higher than that of surface-located Pt atoms in Pt/C catalysts may lead to additional mass-transport issues at short range (higher local diffusion flux of O2 needed towards individual active sites). In addition, Me-N-C catalysts with high TOF but low SD may not only lead to local O2 starvation when operating at high current density in PEMFC, but may also lead to the build-up of hydrogen peroxide concentration gradients (high concentration locally around active sites), with expected dramatic influence on the long term durability of Me-N-C cathodes (65). For all these reasons, disentangling SD and TOF values from the overall ORR activity will be important for the further development of Me-N-C catalysts.

Whereas established methods exist for Pt-based catalysts (carbon monoxide chemisorption, electrochemical hydrogen sorption) they do not work at room temperature for Me-N-C catalysts. Reliable quantification of the catalytic sites on the surface of pyrolysed Me-N-C catalysts is an ongoing challenge. Attempts have been made in the past to estimate the values of SD and TOF of some Fe-N-C catalysts (66, 67), however those estimations have always included one or more hypotheses such as: (a) full utilisation of all Fe atoms in Fe-N-C (NumberFe cm–3 = SD); or (b) full utilisation of the FeNx moieties (a less crude hypothesis than (a), but still probably far from the real Fe utilisation). 57Fe Mössbauer spectroscopy is powerful in distinguishing FeNx moieties from crystalline Fe structures. Even though clean Fe-N-C catalysts with an 57Fe Mössbauer spectroscopic signature showing only quadrupole doublets (assigned to atomically-dispersed Fe-ions) can now be synthesised, the fact that Mössbauer spectroscopy is a bulk technique implies that it cannot directly distinguish bulk sites from surface sites. The same observation applies to X-ray absorption spectroscopy, the other broadly applied technique to characterise the local environment around Fe and Co centres in pyrolysed Me-N-C catalysts. Recent years have witnessed the development of a few ex situ (gas-solid) and in situ (liquid-solid) sorption techniques to assess the SD of such catalysts. These rely on the strong interaction of a small probe molecule with surface adsorption sites resulting in poisoning of the site.

Early non-pgm catalyst poisoning studies realised that COgas, an intuitive choice of poison for Fe centres, is unable to block Fe-N-C sites quantitatively under ambient temperature and pressure conditions (68, 69). In contrast, the cyanide ion was identified as a suitable in situ poisoning ligand for FeN4 centres (70, 71). Owing to its irreversible adsorption however, CN– adsorption could not be utilised for quantitative SD evaluation. Recently, an ex situ low-temperature (–100°C) CO gas pulse chemisorption-based technique for the quantification of the SD of Fe-Mn-N-C and Mn-N-C catalysts was reported by Strasser’s group (Figures 10(a) and 10(b)). Quantitative values of SD were directly obtained from the total amount of adsorbed CO derived from consecutive CO pulses (72). Subsequent thermal desorption of the adsorbed CO during heating ramps from –100°C to about +400°C provided additional insight on the desorption kinetics and, indirectly, into the relative CO chemisorption energies of different FeNx or dissimilar Me-Nx sites. This SD estimation technique is straightforward, robust and may be applicable to various non-pgm metal centres. Its drawback consists of the fact that it is performed outside the electrolyte, and thus relies on the assumption that all sites probed by gas molecules remain active and accessible in an electrochemical environment. More recently still, an electrochemical in situ technique to probe, evaluate and quantify the SD at the surface of a powder catalyst electrode was reported by Kucernak’s group (73). The authors demonstrated a protocol that allows the quantification of SD in Me-N-C catalysts operating under acidic conditions by means of nitrite adsorption, followed by reductive stripping (Figures 10(c) and 10(d)). The method showed direct correlation to the catalytic activity and was demonstrated for a number of non-pgm catalyst materials. Lastly, a recent study from Los Alamos National Laboratory showed that a specific doublet in the Mössbauer spectrum of an Fe-N-C catalyst was modified in the presence of NO (74). After an electrochemical reduction treatment applied to convert potential FeIIIN4 moieties into FeIIN4 moieties, the introduction of NO-gas strongly modified only one doublet. That doublet accounted for 24% of the relative absorption area while the sum of all doublets (all types of FeNx moieties) accounted for 63% of the absorption area. This defines a utilisation factor of 0.38 for that specific catalyst, in line with the expected utilisation factor if FeNx moieties are statistically dispersed in graphene sheets, and with an average stacking (as determined experimentally) of five graphene sheets.

Fig. 10.

Scheme of methods recently developed to quantify SD in pgm-free cathode catalysts: (a) quantification of moles CO adsorbed on monometallic Fe-N-C and Mn-N-C materials, or bimetallic Fe-Mn-N-C materials (labelled as (Fe,Mn)-N-C, although not necessarily implying binuclear active sites) by pulsed CO chemisorption at low temperature; (b) correlation between CO uptake (mole per mgcatalyst) and ORR activity; (c) scheme showing the poisoning of Fe site by nitrite leading to stable Fe-NO adducts and its removal by reductive stripping, leading to the regeneration of the ORR-active Fe site; (d) the number of Fe sites is determined from the electric charge associated with Fe-NO adducts during electrochemical reduction. Reproduced from (72) and (73)

In the near future, one or several of these methods and possibly new ones will certainly be regularly applied by research groups in the field. This will give more detailed information on both the SD and TOF values in such catalysts and will guide the design of such catalysts and catalyst layers (Figure 11). Such methods that allow deconvolution of SD and TOF values will also inform on how these values change after various electrochemical or chemical aging of the catalysts. This will lead to novel understanding in particular on whether the main instability (decreased ORR activity over time) of pgm-free Me-N-C catalysts in PEMFC mostly originates from a decreasing SD or from a decreasing average TOF over time.

Fig. 11.

Master plot showing the linear relation between site loading (number of active sites per cm2 geometric area of cathode) and site TOF (number of electrons reduced per site and per second, at 0.9 V). The orange line corresponds to an iso-activity curve of 44 mA cm–2 at 0.9 V for the cathode (US DOE target for O2-fed cathode, see Table II), which can be reached with different combinations of SL and TOF values. The SL value is itself a combination of the SD and cathode thickness. The operating point for Pt nanoparticles on carbon is indicated with the orange circle. Two Fe-N-C cathodes with loading of 1 mgFe-N-C cm–2 are represented (open purple circles and filled red circle) as well as three possible paths to reach the cathode activity target, for a fixed cathode thickness

3. Non-pgm Anode Catalysts

3.1 Limitations of Platinum Catalysts

The anode Pt loading in PEMFC is currently around 0.05 mg cm–2 and cannot be further decreased without unacceptably increasing the anode sensitivity to H2-fuel contaminants. Indeed in floating electrode configuration, Pt nanoparticles supported on carbon black (20–50 wt% Pt/C) at ultra-low loadings <5 μgPt cm–2 have shown HOR exchange current density of 100 mA cmPt–2 (80 A mgPt–1 ‘mass-normalised’ exchange current density) at room temperature, with the performance doubling when the temperature is increased to 60°C (75). However, ultra-low loaded Pt catalyst layers (1–5μgPt cm–2) are extremely sensitive to a range of contaminants (CO, hydrogen sulfide) present in the fuel or leached from stack components that reversibly or irreversibly deteriorate their activity. Hence, the design of catalysts with ultra-low Pt content that are more tolerant to contaminants, or of non-Pt HOR catalysts that are immune to contaminants would not only further reduce the total Pt content in PEMFCs but would also facilitate the use of lower cost H2 reformed from natural gas or produced from biomass. This would ease the transition between ‘fossil’ H2 and renewable H2.

3.2 Tungsten and Molybdenum Carbides

Except for pgms, nickel as well as several Ni-alloys can drive HOR catalysis in highly alkaline conditions (76). For a long time, tungsten and molybdenum carbides possibly doped with Co or Ni (WC, M/WC, M = Ni, Co and Co/MoC) were the only pgm-free HOR catalysts that are stable under acidic conditions (77–79). Anodes based on these materials mixed with carbon black have exhibited current densities up to 20–40 mA cm–2 at 0.1 V vs. reversible hydrogen electrode (RHE) (77–79). Such materials have proven quite resistant to CO (80) and have been successfully implemented as MEA anodes together with Pt-based cathodes and displayed a maximum power density of ~20 mW cm–2. The replacement of Pt by such catalysts in single-cell PEMFC has so far resulted in a factor-10 lower power density (Figure 12) (81). However, they suffer from limited activity and also limited stability due to carbide oxidation (and release of CO2) coupled to the formation of the corresponding metal oxides.

Fig. 12.

Fuel cell polarisation curves with a typical Pt/C catalyst at the cathode and, at the anode, Co-Mo carbide or Pt/C. Reproduced from (81) with permission from Elsevier

3.3 Bioinspired Nickel-Diphosphine Catalysts

More recently, a bioinspired approach for pgm-free HOR catalysts was developed. Hydrogenases are enzymes that reversibly catalyse HOR close to the equilibrium potential and with turnover frequencies exceeding 1000 s–1 for both HOR and HER at 0.2 V overpotential (82). Hydrogenases only contain Ni and metal atoms in a sulfur-rich and organometallic environment at their active sites (Figure 13) (83, 84). Inspired by the structure of these active sites, [Ni(P2RN2R′)2]n + catalysts based on a nickel(II) centre coordinated to two diphosphine ligands, and bearing two pendant amine groups in a distorted square-planar geometry were designed by DuBois (Figure 13) (85, 86). Such amine groups mimicking the pendant base found at the [FeFe]-hydrogenase active site act as proton relays in close proximity to the metal-bound hydride to promote H–H bond formation during the hydrogen evolution reaction (HER), and as a polariser of the H–H bond, to promote its cleavage during HOR (87, 88). Bioinspired [Ni(P2RN2R′)2]n + complexes display bidirectional activity in HER and HOR with a few derivatives being reversible HER/HOR catalysts, albeit with a kinetic bias towards one or other direction (89–92). Almost reversible HER/HOR catalysis is observed in fully aqueous electrolyte with [Ni(P2CyN2Arg)2]7+, although at elevated temperatures (91). Maximal HOR TOFs have been reported in the range of 102 s–1 at pH values between 0 and 1, with dramatic decrease as soon as the pH exceeds 2.

Fig. 13.

(a) Three molecular complexes for H2 oxidation and evolution with anchoring groups, inspired from the active sites of [FeFe]-hydrogenases. Here, the active site of C. reinhardtii HydA (B) is represented in its native state and a H2 molecule can coordinate where the red arrow points (83). The NiFe active site of E. coli Hyd1 is represented in a similar fashion (A) (84); (b) three bio-inspired molecularly-engineered nanomaterials for H2 oxidation: MWCNT-COO–/[Ni(P2CyN2Arg)2]7+, MWCNT-NH3+/[Ni(P2CyN2Ester)2]2+ and MWCNT/[Ni(P2CyN2Pyrene)2]2+. Adapted from (96) with permission of the Royal Society of Chemistry

Immobilisation of [Ni(P2RN2R′)2]n+ complexes on carbon nanotubes (CNTs) deposited onto gas diffusion layers (GDL) yields very efficient reversible catalytic materials for HER/HOR (93–95). Three distinct immobilisation modes (covalent, π-stacking and electrostatic) have been developed to attach the bioinspired catalytic site onto such nanostructured electrodes (96). To that aim, various [Ni(P2RN2R′)2]n+ structures incorporating distinct anchoring groups were used. Figure 13 shows the structure of [Ni(P2CyN2Arg)2]7+, [Ni(P2CyN2Ester)2]2+ and [Ni(P2CyN2Py)2]2+ containing arginine, activated ester and pyrene anchoring groups, respectively. With different anchoring groups on the molecular catalyst come different receiving groups on the CNTs (Figure 13(b)). Standard grafting strategies were employed: polycationic/polyanionic electrostatic interaction (95), covalent amide linkage (94) and Π-stacking of a pyrene moiety directly onto CNTs (93). An alternative procedure was developed to construct molecular [Ni(P2RN2R′)]n+ catalytic sites in a stepwise manner on the CNT-based electrode (53), in which the diphosphine ligand was firstly immobilised via amide coupling and the nickel centre was then introduced in a second step in the form of a commercially available nickel salt (97).

Electrochemical characterisation of the final electrodes in acetonitrile allowed quantification of the amount of [Ni(P2RN2R′)2]n+ species that are electrochemically addressable and display a two-electron wave in cyclic voltammetry. In brief, all techniques provide typical site densities (number of sites per geometric area of electrode) of 1–3 × 10–9 mol cm–2 when densely packed CNT electrodes are used. This loading is increased by one order of magnitude when carbon microfibres are used as templates to provide the CNT electrodes with three-dimensional structuring. This value (2 × 10–8 mol cm–2) was used to determine SD and site loading (SL) data in Table III (53).

The electrocatalytic activity of all these materials was first assessed in 0.5 M sulfuric acid aqueous solution in a nitrogen or H2 atmosphere provided from the back of the porous substrate in half-cell configuration (floating electrode technique, Figure 14). In some cases, the [Ni(P2RN2R′)2]n +-coated electrodes were coated with a Nafion membrane to form a stable, pgm-free, air-resistant MEA. Under such conditions, reversible electrocatalytic activity for H+/H2 interconversion was observed (Figure 14) (94). Hydrogen is evolved at potentials just slightly negative compared to the thermodynamic equilibrium (no overpotential required) and anodic current density corresponding to hydrogen oxidation is measured for potentials positive to the thermodynamic equilibrium under H2 supply.

Fig. 14.

Linear sweep voltammograms recorded in 0.5 M H2SO4 for a GDL/MWCNT-[Ni(P2CyN2Ester)] MEA in a hydrogen atmosphere at different temperatures: (a) adapted from (53) with permission of the Royal Society of Chemistry; (b) Tafel plot of the same catalyst (black) compared to a commercial Pt electrode (0.05 mgPt cm–2) (red) at 25°C (dashed trace) and 85°C (solid trace) in 0.5 M H2SO4 (adapted from (53) with permission of the Royal Society of Chemistry); (c) chronoamperometry of Ni(P2CyN2Pyrene)2](BF4)2/MWNT/GDL (red) and a commercial Pt electrode (0.5 mgPt cm–2) (black) in a 50 ppm CO atmosphere (adapted from (93) with permission of Wiley)

Performance was assessed for GDL/MWCNT/[Ni(P2CyN2Ester)]2+ (MWCNT = multi-walled carbon nanotube) in a half-cell floating electrode set-up at ca. 15 mA cm–2 (7.5 A mgNi–1) at room temperature and 0.3 V vs. RHE, and ca. 40 mA cm–2 (>20 A mgNi–1) at 85°C, a technologically relevant operating temperature, and 0.3 V vs. RHE (53). This catalytic performance approaches that of a Pt nanoparticle-based electrode (Tanaka, 0.05 mgPt cm–2) benchmarked under identical conditions. Proton reduction catalysis at room temperature reaches at 100 mV overpotential a current density of 7 mA cm–2 at 25°C, and 38 mA cm–2 at 85°C (Figure 14) (53). Some of these electrode materials furthermore proved quite stable with unchanged catalytic response over 10 hours of continuous operation. The H2 oxidation current measured on GDL/MWCNT/[Ni(P2RN2pyrene)2] electrodes was found stable in the presence of 50 ppm CO, a feature likely shared by covalently immobilised NiPR2 species (93). Resistance to CO poisoning is thus another advantage of this series of catalysts over Pt nanoparticles, the surface of which is irreversibly poisoned within a few minutes under such conditions (Figure 14(c)).

In order to gain structural insights regarding the active species, X-ray absorption spectra (XAS) at the Ni edge on GDL/MWCNT-[Ni(P2RN2pyrene)2] electrodes were measured (93). The XAS of immobilised [Ni(P2RN2pyrene)2]2+ species are quite similar, although not identical, to that of standalone [Ni(P2RN2R′)2]2+ complexes. As-prepared GDL/MWCNT-[Ni(P2RN2pyrene)2] electrodes also contain Ni(II) ions coordinated to light atoms attributed to solvent or water molecules, but these species are washed off during electrochemical equilibration in aqueous electrolytes (93). Of note, the XAS recorded at the Ni edge are found unchanged after 1 h of H2 evolution or H2 oxidation catalysis in aqueous H2SO4 0.5 M solution, attesting for the stability of the grafted species (93).

These materials were implemented and shown to be operational in compact PEMFC prototypes (95, 93). An early fully operational Pt-free PEMFC was developed with MWCNT-[Ni(P2PhN2Pyrene)2]2+ at the anode, and a Co-N-C ORR catalyst (98, 99) at the cathode (93). An output power of 23 μW cm–2 was obtained (Figure 15). More recently, the maximum power of a fuel cell integrating a SWNT-[Ni(P2CyN2Arg)2]7+ (SWNT = single-walled nanotube) anode catalyst was measured just below 2 mW cm2 (95). In that case, the limiting component is however a biocathode based on bilirubin oxidase immobilised on CNTs. Replacing this biocathode by a Pt-based cathode yielded a SWNT-[Ni(P2CyN2Arg)2]7+-Pt/C PEMFC with a power output of 14 mW cm–2 at 0.47 V and 60°C, only seven times lower than a full-Pt PEMFC similarly built and operated under the same conditions (95).

Fig. 15.

Schematic representation of the PEMFC assembly from (93); the inset shows polarisation and power density curves recorded at 60°C with supply of partially humidified H2 (20 ml min–1) at the anode and passive air convection at the cathode. Adapted from (93) with permission of Wiley

4. Conclusions

Major breakthroughs have been achieved over the last decade in the design of catalysts based on Earth-abundant metals for catalysing the ORR or HOR, that are compatible with PEMFC technology and operate with overpotential requirements similar to those of conventional Pt catalysts. These catalysts are also more selective and therefore less sensitive to poisoning, a major asset for worldwide introduction of PEMFC technology if such innovative catalysts can be implemented in full devices while retaining other key specifications, i.e. power performance and durability. Still, progress has to be made in two directions. First, the electrochemical activities of such catalysts are still lower than those of optimised Pt-based catalysts. Closing the gap can be pursued by increasing the site density or the turnover frequency of the active sites, both for ORR and HOR noble metal-free catalysts. Additionally, specific optimisation of the catalyst layer structures for such catalysts could help promoting the power density reached for pgm-free H2/air PEMFCs through a better control of protons and substrate/product diffusion together with avoidance of flooding. The other direction, in which it is urgent to invest, is the stability of the catalyst materials during representative drive cycles.

‘Communication from the Commission to the European Parliament, the Council, the European Economic and Social Committee and the Committee of the Regions on the Review of the List of Critical Raw Materials for the EU and the Implementation of the Raw Materials Initiative’, COM/2014/0297 final, 26th May, 2014 LINK http://eur-lex.europa.eu/legal-content/EN/TXT/?uri=CELEX:52014DC0297

Acknowledgements

This work was supported by the FCH Joint Undertaking (CRESCENDO Project, Grant Agreement n°779366) and the French National Research Agency (Labex programme, ARCANE, ANR-11-LABX-0003-01). Goran Drazic from the National Institute of Chemistry, Ljubljana, Slovenia, is acknowledged for his work on the HR-STEM microscopy on the Fe-N-C catalyst from Centre National de la Recherche Scientifique (CNRS).

The Authors

Frédéric Jaouen obtained his PhD at the Royal Institute of Technology (KTH), Stockholm, Sweden, in 2003 under the supervision of Professor Göran Lindbergh. From 2004 to 2011, he was a research associate in Professor Jean-Pol Dodelet’s group at Institute National de la Recherche Scientifique (INRS), Canada, where he focused on non-precious metal catalysts for oxygen electro-reduction. In 2011, Frédéric Jaouen was awarded an excellence chair from the ANR and moved to Université de Montpellier, France, to pursue his research on novel pgm-free catalysts for electrochemical energy conversion devices as a CNRS research fellow. He currently coordinates the H2020 project CREATE on anion-exchange membrane fuel cells and electrolysers and is strongly involved in several other European and national projects focusing on catalysts free of critical raw materials for O2 and CO2 reduction. He was awarded the academic research prize from the Energy division of the French Chemical Society in 2017.

Deborah J. Jones received her PhD in 1982 from the University of London, King’s College, UK, under the supervision of John Emsley. After a period at Southampton University, UK, she moved to France first with a Royal Society Fellowship and then a European Commission Sectoral Grant in Non-Nuclear Energy at the University of Montpellier, France. She is currently Director of Research at CNRS, Associate Director of the Institute Charles Gerhardt for Molecular Chemistry and Materials in Montpellier and serves as vice-president of the International Society of Electrochemistry. Her interests encompass the development of membrane, catalyst and electrode materials for proton exchange membrane fuel cells and electrolysers. She is a Fellow of the Electrochemical Society (2015) and recipient (2016) of the Sir William Grove award of the International Association for Hydrogen Energy.

Nathan Coutard graduated in 2015 from Université Pierre et Marie Curie in Paris, France. His master’s internship in Professor Kylie Vincent’s lab at University of Oxford, UK, aimed to study the regulatory hydrogenase from Ralstonia eutropha using in operando spectro-electrochemistry. His PhD project in Dr Vincent Artero’s group aims to optimise and integrate bio-inspired catalysts in a functional proton-exchange membrane fuel cell. His work includes electrode nanostructuration, electrochemistry, catalyst design, synthesis and tinkering.

Vincent Artero studied at the Ecole Normale Supérieure, Ulm, Germany, and graduated with his PhD in Inorganic Chemistry at the Université Pierre et Marie Curie in Paris in 2000. After a post-doctoral stay in RWTH Aachen, Germany, in the group of Professor Ulrich Kölle, he moved to the CEA centre in Grenoble (Fundamental Research Division) in 2001 to develop bioinspired chemistry related to hydrogen production and artificial photosynthesis. He received the ‘Grand Prix Mergier-Bourdeix de l’Académie des Sciences’ (2011) and was granted a Starting Grant from the European Research Council (ERC 2012–17). He currently acts as Chair of the Scientific Advisory Board of the ARCANE Excellence Laboratory Network (LABEX) for bio-driven chemistry in Grenoble and as co-chair of the French Research Network (GDR) on solar fuels.

Peter Strasser is the chaired professor of Electrochemistry and Electrocatalysis in the Chemical Engineering Division of the Department of Chemistry at the Technical University Berlin, Germany. Prior to his appointment, he was Assistant Professor at the Department of Chemical and Biomolecular Engineering at the University of Houston, USA. Before moving to Houston, Professor Strasser served as Senior Member of staff at Symyx Technologies, Inc, USA. In 1999, he received his doctoral degree in Physical Chemistry and Electrochemistry from the Fritz-Haber-Institute of the Max-Planck-Society, Berlin, Germany, under the direction of Gerhard Ertl. Peter Strasser was awarded the Otto-Hahn Research Medal by the Max-Planck Society, the Otto Roelen medal for catalysis awarded by the German Catalysis Society and the Ertl Prize awarded by the Ertl Center for Catalysis.

Anthony Kucernak received his PhD from Southampton University, UK, in 1991 and carried out postdoctoral research at Cambridge University, UK. He subsequently moved to Imperial College London, UK, where he has held the post of Professor of Physical Chemistry since 2009. He has published more than seventy papers on novel methods for screening catalysts under realistic operating conditions; the study of individual catalyst particles and the modification of surface composition to probe the fundamentals of electrocatalysis. He has been an invited plenary speaker at the 2005 International Fuel Cell Workshop, Japan, and co-chaired the Gordon Conference on fuel cells in 2004. In 2006 he was awarded the Helmut Fisher medal for his work on fuel cell electrode structure and fundamental results in electrocatalysis.