In this study, the measurement of FN (ferrite volume fraction) and the solution annealing ratio at a temperature of were determined with 15A elbow fittings of shell cast SSC13, and the corrosion resistance with and without austenitizing solution annealing were investigated in comparison with AISI304. The delta ferrite phase was observed in the material due to the slow cooling effect of the shell mold casting. However, the delta ferrite phase decreased gradually with the solution annealing at a temperature of . The hardness generally decreased with a heat treatment; however, its corrosion resistance was improved with the heat treatment. In addition, when a passivation treatment was applied, its corrosion ratio showed the lowest value. The pattern of general corrosion decreased due to the decrease in the delta ferrite phase with the solution annealing treatment. Consequently, it is suggested that the corrosion resistance of SSC13 elbow fittings can be improved by increasing the ratio of any solution annealing treatment used and by decreasing the ferrite phase. The relationship between the ratio of solution annealing and delta ferrite is expressed as follows: SA (solution annealing ratio,%)

This paper reports the effect of a refractory crucible type on the microstructure of duplex stainless steel (DSS) cast with the addition of gadolinium using air-induction melting. Grade 4A DSSs with 1 wt% of gadolinium (Gd) were fabricated in various crucibles including alumina (), magnesia (MgO), calcia (CaO) coated with yttria () and graphite. The standard free energies of the formation of calcium and yttrium oxide were lower than those of gadolinium oxide and other crucible elements based oxide. The yield of Gd in DSS using , MgO, CaO-coated and graphite was 5, 19, 83 and 96%, respectively. As Gd yield increased, the amount of Gd-based inclusions increased, the size of the inclusions were reduced, and the inclusions became evenly distributed.

The effects of Ti, B and Zr on grain refinement and castability were investigated in Al-4wt%Mg-0.9wt%Si-0.3wt%Mn-0.15wt%Fe alloy. Measurement of cooling curve and micro-structure observation were performed to analyze the effects of the addition of minor elements Ti, B and Zr during solidification. The prominence of effect on grain refinement was in increasing order for Ti, Zr and B element. Fine grain size and an increase of the crystallization temperature for -Al solution were evident as the amount of addition elements increased in this study. Addition of 0.15wt% Ti was most effective for grain refinement, and the resulting grain size of -Al solution for shell mold and steel mold were and , respectively. Fluidity and shrinkage tests were perform to evaluate the castability of the alloy. Maximum fluidity length and minimum ratio of micro shrinkage were recorded for 0.15wt% Ti addition due to the effect of the finest grain size.