L Li, R Lin, Z Tong and Q Feng

Abstract

Highly dispersive strontium carbonate (SrCO3) nanostructures with uniform dumbbell, ellipsoid, and rod-like morphologies were synthesized in methanol solution without any additives. These SrCO3 were characterized by X-ray diffraction, field emission scanning electron microscopy, and N2 adsorption-desorption. The results showed that the reaction temperature and the methanol/water ratio had important effects on the morphologies of SrCO3 particles. The dumbbell-like SrCO3 exhibited a Broader-Emmett-Teller surface area of 14.9 m2 g-1 and an average pore size of about 32 nm with narrow pore size distribution. The formation mechanism of the SrCO3 crystal was preliminary presented.