The aim of this paper was to address the effects of multiple laser shock processing (LSP) impacts with different pulse energy on mechanical properties and wear behaviors of AISI 8620 steel. Wear analyses were conducted by means of calculation of volume loss and scanning electron microscope (SEM) of the wear surface. Surface profiles, roughness and micro-hardness were measured. The micro-structures in the surface layer of the untreated and LSPed samples (treated by multiple LSP impacts) were investigated by using transmission electron microscopy (TEM) observations. Experimental results and analyses indicated that multiple LSP impacts can remarkably improve the wear resistance of AISI 8620 steel, and the wear mechanism of multiple LSP impacts on AISI 8620 steel was also entirely revealed. The wear process of the unpolished sample subjected to multiple LSP impacts can be described as follows: the wear rate was big at the beginning of sliding dry wear, but then decreased after the micro-indention in the sample surface was polished to the disappear. This phenomenon can be attributed to the fact that multiple LSP impacts generate many micro-indents in the sample surface.

Every reasonable effort has been made to ensure that permission has been obtained for items included in DRO. If you believe that your rights have been infringed by this repository, please contact drosupport@deakin.edu.au.