The aim of this work is examination of the above mentioned compounds with variety physical methods. The samples were obtained by the induction melt in polycrystalline form. The sample with gadolinium crystallized in hexagonal Th7Fe3 – type of crystal structure.

The electrical resistivity measurements and ac magnetic susceptibility show a complex magnetic behaviour of these compounds. Several transitions are observed besides of the main peak in ac measurements. Moreover, an anomaly at about 270 K was observed for all compounds in ac and electrical resistivity temperature dependences.