We have developed composition and porosity graded La2−xNiO4+δ (x≥0) cathode interlayers for low-temperature solid oxide fuel cell that exhibit good adhesion with the electrolyte, controlled porosity and grain size and good electrochemical behaviour. La2−xNiO4+δ (x≥0) monolayers are
elaborated from a derived sol–gel method using nitrate salts, acetylacetone and hexamethylenetetramine in acetic acid. As a function of the organic concentration and the molar ratio of lanthanum to nickel, these layers present platelets or spherical shape grains with a size distribution ranging from 50 to 200 nm, as verified by SEM-FEG. On the basis of this processing protocol, we prepared porosity and composition graded lanthanum nickelates interlayers with effective control of the pore distribution, the nanocrystalline phase, the thickness and the subsequent electrochemical properties.

Item Type:

Article

Additional Information:

Thanks to Elsevier editor. The definitive version is available at http://www.sciencedirect.com The original PDF of the article can be found at Journal of Power Sources website : http://www.sciencedirect.com/science/journal/03787753