22,000 PVOH with H3PO4: yellowish color, stiffness increased dramatically. It can be still bended.

100,000 PVOH: less clear film. Very stiff. Harder to bend.

100,000 PVOH with HCl: Dark Black color. still flexible. Stiffness did not change to much.