Low density polyethylene film is made in monolayer from 100 % virgin grade raw material with MFI of 6 to 8 and through autoclave (low pressure) process without any mix up. It is clear, transparent and treated for perfect lamination.

ToleranceofLDPEFilmthicknessandUnitWeightg/sq.mtr.

LDPEGauge

ThicknessTolerance(mic.)(±10%)

UnitWeightg/sq.mtr.(±10%)

Lower

STD

Upper

Lower

STD

Upper

150

33.8

37.6

41.40

31.17

34.64

38.10

180

40.0

45.10

49.60

37.41

41.57

45.75

CombinedunitWeight(Alufoil+LDPE)andYield(SqmeterperKgoflaminatedfoil)

TypeofLaminates

CombinedUnitWeight(AluFoil+LDPE)Grams/Sqmtroflaminatedfoil

Yield-Standard

Lower

STD

Upper

Sq Mtrs./Kg

0.025mm Foil+ 150 Gauge LDPE Film

93.5

102.39

111.27

9.76

0.03mm Foil + 150 Gauge LDPE Film

105.96

115.94

125.9

8.62

0.04mm Foil + 150 Gauge LDPE Film

130.89

143.04

155.17

6.99

0.025mm Foil+ 180 Gauge LDPE Film

99.74

109.32

118.89

9.14

0.03mm Foil + 180 Gauge LDPE Film

112.2

122.87

133.52

8.13

0.04mm Foil + 180 Gauge LDPE Film

137.13

149.97

162.79

6.67

RecommendedOperatingCondition

Peeling Strength (Bond strength between Foil & LDPE)

250 gms/15 mm (Min.)

Sealing Strength (Bond Strength between LDPE to LDPE)

550 gms/15 mm (Min.)

Sealing Temperature

180° C

Sealing Pressure

3.0 to 6.0 bar

Dwell Time

0.5 Sec

Primer

A thin layer of de-waxed shellac or is applied to de-grease the foil and promote adhesion with printing ink.

Printing

Printing Surface

On Primer side

Design

As per customer’s approved artwork and design.

Colors

Up to 8 Col on Primer side

Length Register

± 0.3 mm

Ink Adhesion and Stability

No peel off or breakage by scotch pull test or under sealing condition.