Electrical Insulation Mat having very high voltage insulation resistance (upto 33KV). Volt-Safe is lifesaving, protecting people working around high voltage panels or AC & DC Electrical installations, from electrical shocks

Dimension(L*W*H)

Standard

Weight

60 Kilograms (kg)

Color

Blue, Black

Product Description

SHEET PVC INSULATION MATT

SPECIFICATION: IS 15652 :2006 THICKNESS: 2.00MM , 3.00MM

Shape 6.1

2 mm: Should be specific shape or Roll

3mm: Should be specific shape or Roll

Leakage Current 8.2.2 (ÃÂa)

2 mm: 10 mA Max

3mm: 10 mA Max.

Dimensions 6.2 (Mm)Length

2 mm: Should be 1000 mm + 20 mm Should be 1000 mm + 20 0r in other width agreement with purchaser

3mm: Should be 1000 mm + 20 mm Should be 1000 mm + 20 0r in other width agreement with purchaser

Aging Properties (70+10c) For 168 H Tensile strength

2 mm: 75 % OF corresponding value of same lot sample without conditioning

3mm: 75 % OF corresponding value of same lot sample without conditioning

Elongation

2 mm: 75 % OF corresponding value of same lot sample without conditioning

3mm: 75 % OF corresponding value of same lot sample without conditioning

Thickness 6.3(mm)

2 mm: 2.00 mm + 10 %

3mm: 3.00 mm + 10 %

AC Proof Voltage 8.2.4 (kv)

2 mm: 10 Kv

3mm: 36 Kv

Tensile Strength 8.1 (n/mmÃÂ²)

2 mm: 15 (-10 to 15 0C ) 12 (-40 to 27 0C )

3mm: 15 (-10 to 15 0C ) 12 (-40 to 27 0C )

Thermal Flame Retardence 8.2.1(Second)

2 mm: 5 s after removal of blue flame

3mm: 5 s after removal of blue flame

Elongation 8.1 (%)

2 mm: 15 (-10 to 15 0C ) 12 (-40 to 27 0C )

3mm: 15 (-10 to 15 0C ) 12 (-40 to 27 0C )

Acid /Alkalis And Oil Resistance 8.5 (n/mmÃÂ²)

(Acid Resistance) Tensile strength Elongation

3mm: 80 % OF corresponding value of same lot sample without conditioning

(Alkalis Resistance) Tensile strength Elongation

2mm: 80 % OF corresponding value of same lot sample without conditioning

3mm: 80 % OF corresponding value of same lot sample without conditioning

(Oil Resistance) Tensile strength Elongation

2mm: 80 % OF corresponding value of same lot sample without conditioning