The thermal decomposition of the paper sludge with poly (acrylonitrile-butadiene-styrene) was using a thermal analysis techniques in the stream of nitrogen gas of 30ml/min at various heating rates from 4 to . The mathmatical, derivative and integral method were used to obtain values of activation energy of decomposition reaction. 1. The values of activation energy evaluated by derivative and Intergral method were consistent with each other very well. 2. The maximum value of heat of decomposition evaluated by DSC method was 10.120cal/g at weight ratio of paper sludge/ABS=20/80. 3. The thermogravimetric trace curve agreed with the theoretical equation.

The physical properties of rubber compounds containing silica and siliane coupling agent in order to replace the carbon black and prepare for environmental regulation showed improved dynamic properties(rebound, heat build-up, ), but the abrasion resistance did not improve compared with the compounds containing carbon black. Also, curing retardation because of coherent structure of silica improved by the addition of DEG, but the mixing step change of activators did not so much improve the static and dynamic properties of the compounds containing high synthetic rubber, the status of mixing and dispersion showed that the compounds containing carbon black was much better than the compounds containing silica by TEM investigation.