Copper can be pattern etched in a manner which provides the desired feature dimension and integrity, at acceptable rates, and with selectivity over adjacent materials. To provide for feature integrity, the portion of the copper feature surface which has been etched to the desired dimensions and shape...http://www.google.com/patents/US20020045354?utm_source=gb-gplus-sharePatent US20020045354 - Acid resistance glass; smooth surface

Copper can be pattern etched in a manner which provides the desired feature dimension and integrity, at acceptable rates, and with selectivity over adjacent materials. To provide for feature integrity, the portion of the copper feature surface which has been etched to the desired dimensions and shape must be protected during the etching of adjacent feature surfaces. This is particularly important for feature sizes less than about 0.5 μm, where presence of even a limited amount of a corrosive agent can eat away a large portion of the feature. The copper feature integrity is protected by several different mechanisms: 1) The reactive etchant species are designed to be only moderately aggressive, so that an acceptable etch rate is achieved without loss of control over the feature profile or the etch surface; 2) Hydrogen is applied over the etch surface so that it is absorbed onto the etch surface, where it acts as a boundary which must be crossed by the reactive species and a chemical modulator for the reactive species; and 3) Process variables are adjusted so that byproducts from the etch reaction are rendered more volatile and easily removable from the etch surface. In an inductively coupled plasma etch chamber, we have observed that the preferred chlorine reactive species are generated when the chlorine is dissociated from compounds rather than furnished as Cl2 gas.

Images(9)

Claims(35)

We claim:

1. A method of etching a copper film surface to provide a semiconductor feature, wherein said etching is accomplished using a plasma, said method comprising:

a) supplying a halogen-comprising plasma source gas to a plasma etch chamber, wherein components of said plasma source gas provide sufficient dissociated hydrogen to provide physical and chemical modulation of halogen-comprising etchant species generated from said plasma source gas; and

b) etching said copper film to produce a copper feature having exterior and interior integrity, wherein corrosion of said copper feature is reduced or avoided.

2. The method of claim 1, wherein a halogen-comprising compound is used to generate a majority of etchant species which etch said copper film surface.

3. The method of claim 2, wherein said halogen-comprising compound also generates at least 40% of said dissociated hydrogen.

4. The method of claim 3, wherein at least 80% of said dissociated hydrogen is generated by said halogen-comprising compound.

5. The method of claim 1, or claim 2, or claim 3, or claim 4, wherein the temperature of said copper film is adjusted to facilitate the volatilization of etch products and byproducts, whereby such etch products and byproducts are removed from a surface of said copper film.

6. The method of claim 1 or claim 2, or claim 3, or claim 4, wherein said copper film is etched to form a feature which is 0.5 μm or less in size and having an aspect ratio of 2:1 or greater.

7. The method of claim 2, or claim 3, or claim 4, wherein said halogen-comprising compound is selected from the group consisting of HCl, HBr, and combinations thereof.

8. The method of claim 2, or claim 3, or claim 4, wherein a hydrogen-comprising gas or hydrogen-comprising compound selected from the group consisting of H2, CxHy, CH3F, CHF3, NH3 NH2OH, HI, H3As, H2S, H2Te, H4P2, and H3P, wherein x ranges from 1 to about 4 and y ranges from 2 to about 10, is a component of said halogen-comprising plasma source gas.

9. The method of claim 7, wherein a hydrogen-comprising gas or hydrogen-comprising compound selected from the group consisting of H2, CxHy, CH3F, CHF3, NH3, NH2OH, HI, H3As, H2S, H2Te, H4P2, and H3P, wherein x ranges from 1 to about 4 and y ranges from 2 to about 10, is a component of said halogen-comprising feed gas.

10. The method of claim 1, or claim 2, wherein said halogen-comprising source gas includes nitrogen either as N2 or in the form of a nitrogen-containing compound.

11. The method of claim 9, wherein said halogen-comprising source gas includes nitrogen either as N2 or in the form of a nitrogen-containing compound.

12. The method of claim 1, or claim 2, or claim 3, wherein BCl3 is a component of said halogen-comprising feed gas.

13. The method of claim 7, wherein BCl3 is a component of said halogen-comprising feed gas.

14. The method of claim 12, wherein said halogen-comprising feed gas includes nitrogen either as N2 or in the form of a nitrogen-containing compound.

15. The method of claim 13, wherein said halogen-comprising feed gas includes nitrogen either as N2 or in the form of a nitrogen-containing compound.

16. The method of claim 1, or claim 2, or claim 3, or claim 4, wherein said halogen-comprising source gas includes an additive which functions to improve the etched feature profile, or to improve etch selectivity or to reduce microloading effects during the etch process, and wherein said additive comprises less than about 30% of the plasma-generated reactive species.

17. The method of claim 7, wherein said halogen-comprising source gas includes an additive which functions to improve the etched feature profile, or to improve etch selectivity or to reduce microloading effects during the etch process, and wherein said additive comprises less than about 30% of the plasma-generated reactive species.

18. The method of claim 16, wherein said plasma feed gas includes at least one inert gas which is not reactive with copper.

19. The method of claim 18, wherein said at least one inert gas is selected from the group consisting of argon, helium, and xenon.

20. The method of claim 17, wherein said plasma source gas includes at least one inert gas which is not reactive with copper.

21. The method of claim 20, wherein said inert gas is selected from the group consisting of argon, helium, and xenon.

22. The method of claim 16, wherein said additive is selected from the group consisting of HCl or HBr or HI.

23. A method for etching a copper surface to provide a patterned semiconductor device feature, said method including the steps:

a) supplying to a plasma etch process chamber a plasma source gas which serves as a source for a dissociated halogen species and as a source for dissociated hydrogen, wherein said dissociated hydrogen is sufficient to act as a physical and a chemical modulator for said dissociated halogen species, as said species react with a copper surface to be etched;

b) maintaining said copper surface to be etched at a temperature sufficient to provide for advantageous volatility of halogen-containing etch reaction products and byproducts; and

24. The method of claim 23, wherein gaseous hydrogen is a component of said plasma source gas.

25. The method of claim 23, wherein at least 50 % of said reactive species are supplied by said HCl, HBr, or a combination thereof.

26. A method for etching a copper surface to provide a patterned semiconductor device feature, said method including the steps:

a) supplying to a plasma etch process chamber a plasma source gas which includes a halogen-comprising compound in combination with a hydrogen-generating source, wherein said hydrogen-generating source generates sufficient dissociated hydrogen to act as a physical and a chemical modulator for etchant species generated from said halogen-comprising compound;

b) maintaining said copper surface to be etched at a temperature sufficient to provide for advantageous volatility of halogen-containing etch reaction products and byproducts; and

27. The method of claim 26, wherein said hydrogen-generating source is selected from the group consisting of H2, CxHy, CH3F, CHF3, NH3, NH2OH, HI, H3As, H2S, H2Te, H4P2, and H3P, where x ranges from 1 to about 4 and y ranges from 2 to about 10.

28. The method of claim 26, wherein said halogen-comprising compound is BCl3.

29. The method of claim 27, wherein said halogen-comprising compound is BCl3.

30. The method of claim 28, or claim 29, wherein said plasma feed gas includes a diluent component which does not react with copper or with any etchant species generated by the plasma feed gas mixture.

31. The method of claim 1, or claim 2, or claim 3, or claim 23, or claim 26, wherein said plasma etch chamber is an inductively coupled plasma chamber and said plasma etch pressure ranges from about 20 mT to about 200 mT.

32. The method of claim 1, or claim 2, or claim 3, or claim 23, or claim 26, wherein said plasma etch chamber is a capacitively coupled plasma chamber and said plasma etch pressure ranges from about 100 mT up to about 5 Torr.

33. A method of heating a semiconductor substrate, comprising: using ion bombardment from a plasma upon said substrate surface, wherein the plasma source gas selected to provide the primary source for said ion bombardment does not harm device structures of said substrate and is designed to provide the heating rate and final substrate temperature desired.

34. The substrate heating method of claim 33, wherein said source gas which provides said primary source for ion bombardment is argon.

35. The substrate heating method of claim 33, wherein said ion bombardment of said substrate surface is used in combination with a temperature-controlled substrate support platen.

Description

[0001] This application is a continuation-in-part application of U.S. Ser. No. 08/911,878 of Yan Ye et al., filed Aug. 13, 1997 and titled: “Copper Etch Using HCl and HBr Chemistry”.

BACKGROUND OF THE INVENTION

[0002] 1. Field of the Invention

[0003] The present invention pertains to a particular chemistry which provides advantages in the pattern etching a copper layer on the surface of a semiconductor device substrate. In particular, the etched portion of a feature surface is protected from reactive species during the etching of adjacent feature surfaces.

[0004] 2. Brief Description of the Background Art

[0005] In the multi level metallization architecture used in present day semiconductor devices, aluminum is generally used as the material of construction for interconnect lines and contacts. Although aluminum offers a number of advantages in ease of fabrication, as integrated circuit designers focus on transistor gate velocity and interconnect line transmission time, it becomes apparent that copper is the material of choice for the next generation of interconnect lines and contacts. In particular, when the aluminum wire size becomes smaller than 0.5 μm, the electromigration resistance and the stress migration resistance of aluminum becomes a problem area. In addition, when the feature size of an aluminum-based contact requires an aspect ratio of greater than 1:1, it is difficult to obtain planarization of the substrate during the application of the next insulating layer over the contact area of the substrate. Further, the resistivity of copper is about 1.4 μΩcm, which is only about half of the resistivity of aluminum.

[0006] There are two principal competing technologies under evaluation by material and process developers working to enable the use of copper. The first technology is known as damascene technology. In this technology, a typical process for producing a multilevel structure having feature sizes in the range of 0.5 micron (μm) or less would include: blanket deposition of a dielectric material; patterning of the dielectric material to form openings; deposition of a diffusion barrier layer and, optionally, a wetting layer to line the openings; deposition of a copper layer onto the substrate in sufficient thickness to fill the openings; and removal of excessive conductive material from the substrate surface using chemical-mechanical polishing (CMP) techniques. The damascene process is described in detail by C. Steinbruchel in “Patterning of copper for multilevel metallization: reactive ion etching and chemical-mechanical polishing”, Applied Surface Science 91 (1995) 139-146.

[0007] The competing technology is one which involves the patterned etch of a copper layer. In this technology, a typical process would include deposition of a copper layer on a desired substrate (typically a dielectric material having a barrier layer on its surface); application of a patterned hard mask or photoresist over the copper layer; pattern etching of the copper layer using wet or dry etch techniques; and deposition of a dielectric material over the surface of the patterned copper layer, to provide isolation of conductive lines and contacts which comprise various integrated circuits. An advantage of the patterned etch process is that the copper layer can be applied using sputtering techniques well known in the art. The sputtering of copper provides a much higher deposition rate than the evaporation or CVD processes typically used in the damascene process, and provides a much cleaner, higher quality copper film than CVD. Further, it is easier to etch fine patterns into the copper surface and then deposit an insulating layer over these patterns than it is to get the barrier layer materials and the copper to flow into small feature openings in the top of a patterned insulating film.

[0008] Each of the above-described competing technologies has particular process problems which must be solved to arrive at a commercially feasible process for device fabrication. In the case of the damascene process, due to difficulties in the filling of device feature sizes of 0.25 μm and smaller (and particularly those having an aspect ratio greater than one) on the surface of the dielectric layer, the method of choice for copper deposition is evaporation (which is particularly slow and expensive); or chemical vapor deposition, or CVD (which produces a copper layer containing undesirable contaminants and is also a relatively slow deposition process). Just recently, electroplating has been investigated as a method for copper deposition.

[0009] Regardless of the technique used to deposit copper, the CMP techniques used to remove excess copper from the dielectric surface after deposition create problems. Copper is a soft material which tends to smear across the underlying surface during polishing. “Dishing” of the copper surface may occur during polishing. As a result of dishing, there is variation in the critical dimensions of conductive features. Particles from the slurry used during the chemical mechanical polishing process may become embedded in the surface of the copper and other materials surrounding the location of the copper lines and contacts. The chemicals present in the slurry may corrode the copper, leading to increased resistivity and possibly even corrosion through an entire wire line thickness. Despite the number of problems to be solved in the damascene process, this process is presently viewed in the industry as more likely to succeed than a patterned copper etch process for the following reasons.

[0010] The patterned etch process particularly exposes the copper to corrosion. Although it is possible to provide a protective layer over the etched copper which will protect the copper form oxidation and other forms of corrosion after pattern formation, it is critical to protect the copper during the etch process itself to prevent the accumulation of involatile corrosive compounds on the surface of the etched copper features. These involatile corrosive compounds cause continuing corrosion of the copper even after the application of a protective layer over the etched features.

[0011] Wet etch processes have been attempted; however, there is difficulty in controlling the etch profile of the features; in particular, when the thickness of the film being etched is comparable to the minimum pattern dimension, undercutting due to isotropic etching becomes intolerable. In addition, there is extreme corrosion of the copper during the etch process itself.

[0012] Plasma etch techniques provide an alternative. A useful plasma etch process should have the following characteristics: It should be highly selective against etching the mask layer material; it should be highly selective against etching the material under the film being etched; it should provide the desired feature profile (e.g. the sidewalls of the etched feature should have the desired specific angle); and the etch rate should be rapid, to maximize the throughput rate through the equipment.

[0013] Until very recently etch rates obtained by purely physical bombardment were typically about 300 Å-500 Å per minute or less, as described by Schwartz and Schaible, J. Electrochem. Soc., Vol. 130, No. 8, p. 1777 (1983) and by H. Miyazaki et al., J. Vac. Sci. Technol. B 15(2) p.239 (1997), respectively. Recently, applicants have been able to improve on the etch rates achievable by purely physical bombardment so that etch rates as high as 5,000 Å per minute can be achieved. Further, the selectivity between copper and materials commonly used as barrier layers, insulating layers and patterning masks is more than satisfactory. This technology is disclosed in detail in pending U.S. patent application Ser. No. 08/891,410, filed Jul. 9, 1997. However, etch rate and selectivity must be accompanied by the ability to etch a pattern having the desired cross-sectional profile. To improve etch profile, it is necessary to use a limited amount of chemical reactants during the etch process.

[0014] The chemical reactants must be very carefully selected to react with the copper and create volatile species which can then be removed by application of vacuum to the process chamber. However, when such chemical reactants are used, corrosion is a major problem during the fabrication, as copper does not form any self passivating layer like aluminum does. In particular, oxidation of copper increases resistivity; further, in the case of copper interconnect lines, the whole wire line may corrode all the way through, resulting in device failure. As described in U.S. patent application Ser. No. 08/891,410, referenced above, it is possible to use a limited concentration of particular halogen-based reactants in combination with physical bombardment, when physical bombardment is the controlling etch mechanism and avoid corrosion of the copper by the reactive species used to assist in the etch process.

[0015] There are some etch profiles for which etching in the physical bombardment regime does not provide the best result. In addition, applicants have discovered that it is possible to obtain etch rates which are higher than those obtained to date in the physical bombardment regime and still avoid corrosion of the etched copper. Typically, a chlorine-comprising gas is used in the reactive ion etch processing of the copper. Although the chlorine provides acceptable etch rates, it causes the copper to corrode rapidly. The chlorine reacts very fast, but produces reaction by-products which are not volatile. These byproducts remain on the copper surface, causing corrosion over the entire etched surface. The byproducts can be made volatile subsequent to the etch step by treatment with chemical species which create a volatile reaction product, but by this time the corrosion is already extensive.

[0016] An example of a treatment to remove chlorides and fluorides remaining after the etch of a conductive layer is provided in U.S. Pat. No. 4,668,335 to Mockler et al., issued May 26, 1987. In Mockler et al., the workpiece (wafer) is immersed in a strong acid solution, followed by a weak base solution after the etch of an aluminum-copper alloy, to remove residual chlorides and fluorides remaining on the surface after etching. Another example is provided in U.S. Pat. No. 5,200,031 to Latchford et al., issued Apr. 6, 1993. In Latchford et al, a process is described for removing a photoresist remaining after one or more metal etch steps which also removes or inactivates chlorine-containing residues, to inhibit corrosion of remaining metal for at least 24 hours. Specifically, NH3 gas is flowed through a microwave plasma generator into a stripping chamber containing the workpiece, followed by O2 gas (and optionally NH3 gas), while maintaining a plasma in the plasma generator.

[0017] Attempts have been made to reduce the corrosion by introducing additional gases during the etch process (which can react with the corrosion causing etch byproducts as they are formed). In addition, gaseous compounds which can react to form a protective film over the sidewalls of etched features as they are formed have been added during the etching process and after the etch process. However, residual corrosion continues to be a problem and the protective film, while protecting from future contact with corrosive species, may trap corrosive species already present on the feature surface.

[0018] An example of the formation of a passivating film on pattern sidewalls is presented by J. Torres in “Advanced copper interconnections for silicon CMOS technologies”, Applied Surface Science, 91 (1995) 112-123. Other examples are provided by Igarashi et al. in: “High Reliability Copper Interconnects through Dry Etching Process”, Extended Abstracts of the 1994 International Conference on Solid State Devices and Materials, Yokohama, 1994, pp.943-945; in “Thermal Stability of Interconnect of TiN/Cu/TiN Multilayered Structure”, Jpn. J. Appl. Phys. Vol. 33 (1994) Pt. 1, No. 1B; and, in “Dry Etching Technique for Subquarter-Micron Copper Interconnects”, J. Electrochem. Soc., Vol. 142, No. 3, March 1995. In this 1995 article, Yasushi Igarashi et al. show photomicrographs of cross-sectional views of the subquarter-micron etched features. In reviewing the article, applicants noticed that although the exterior walls of the feature appear to be solid, there appears to be interior hollow areas within the feature where the copper line has been eroded away. Applicants subsequently reproduced this effect, demonstrated by the comparitive example (Example 3) presented subsequently herein. Apparently, reactive chlorine species are trapped interior to the passivating film formed on the wall and these species react with and erode the copper beneath the passivating film.

[0019] Passivating films are used to protect the walls of forming features during the etching of aluminum. Such films are generally used to protect the walls of etched features from further etching by incident reactive species during continued vertical etching of the feature through a mask. Typically the protective film comprises an oxide or a nitride or a polymeric material, or a combination thereof. In the case of aluminum, aluminum oxide forms a cohesive, continuous protective film very rapidly. This rapid formation of a continuous protective film protects the interior of the etched feature from exposure to significant amounts of the reactive species which could cause corrosion interior to the etched wall. However, in the case of copper, there is no similar rapidly-formed film which prevents reactive species from reaching the copper surface and being trapped there by a slowly-formed “passivating” film. It appears that the passivating films of the kind described by Igarashi et al. in their March 1995 article trap reactive species inside the feature walls and these reactive species corrode away the copper interior to the feature walls.

[0020] If the patterned etch technique is to be used for fabrication of semiconductor devices having copper interconnects, contacts, and conductive features in general, it is necessary to find an etch method which does not create immediate corrosion or a source of future corrosion.

[0021] In addition to controlling corrosion, it is necessary to control the profile of the etched pattern. An example of a technique used for obtaining a high etch rate and highly directional reactive etching of patterned copper films copper is described by Ohno et al in “Reactive Ion Etching of Copper Films in a SiCl4, N2, Cl2, and NH3 Mixture”, J. Electrochem. Soc., Vol. 143, No. 12, December 1996. In particular, the etching rate of copper is increased by increasing the Cl2 flow rate at temperatures higher than 280° C. However, the addition of Cl2 is said to cause undesirable side etching of the Cu patterns. NH3 is added to the gas mixture to form a protective film that prevents side wall etching. The etch gas mixture which originally contained SiCl4 and N2 was modified to contain SiCl4, N2, Cl4, and NH3.

[0022] Thus, protective films formed during etching are used by some practitioners skilled in the art to reducing corrosion (as described above) and by others for controlling the directional etching of the pattern surface. In either case, although the formation of such a protective film may work well for aluminum etching, it may be harmful in the case of copper etching for the reasons previously described.

[0023] Toshiharu Yanagida, in Japanese Patent Application No. 4-96036, published Oct. 22, 1993, describes a method of dry etching of a copper material in the temperature range at which a polymeric resist mask can be used (below about 200° C.). Etching using a polymeric resist mask is said to be preferable so that the presence of oxygen (present in a silicon oxide hard masking material which can withstand higher temperatures) can be avoided. The oxide causes harmful corrosion of the copper, producing copper oxides which increase the resistivity of etched copper features. In particular, the Yanagida reference describes the use of hydrogen iodide (HI) gas and combinations of HI gas with chloride and/or fluoride compounds to achieve etching at substrate temperatures below about 200° C.

[0024] B. J. Howard and C. Steinbuchel, in their article entitled “Reactive ion etching of copper with BCl3 and SiCl4: Plasma diagnostics and patterning”, J. Vac. Sci. Technol. A 12(4), July/August, 1994, describe the etching of copper film using a plasma source gas mixture of BCl3/N2 or BCl3/Ar. Gas mixtures with N2 are said to provide considerably higher etch rates than mixtures with Ar. This is attributed to nitrogen scavenging the available B to produce BN, which prevents the recombination of Cl with B, thereby increasing the amount of free Cl. However, the authors acknowledged that there are patterning problems when BCl3/N2 is used, despite acceptable etch rates. When we tried to reproduce the results of Howard and Steinbuchel, we discovered that the etched sidewalls of copper lines in a pattern of lines and spaces were deeply pitted, i.e. there were large pockets of void spaces where the etchant had removed pockets of copper.

[0025]FIGS. 5A and 5B illustrate the kind of corrosion which typically is experienced during the reactive ion etching of copper. The pattern etched was one of lines and spaces, wherein the lines and spaces were approximately 0.5 μm in width looking at a cross-sectional profile of the pattern. The details of the preparation of the etched substrates shown in FIGS. 5A and 5B will be discussed in detail subsequently herein, for comparitive purposes. For now, the important features to note are that the copper lines 510 which appear to be solid looking at the exterior walls 516 are actually hollow in the interior, where the copper 520 remaining after etching is surrounded by vacant space 522. The vacant space is created by the harmful copper reactions we are calling “corrosion”. Corrosion is caused when the copper reacts with oxygen or with other reactants present in the process vessel to produce undesirable by-products. Corrosion also includes reaction with halogens which are typically used as etchant reactants, but the reaction occurs at an undesired rate so that the desired etched feature profile cannot be obtained or the surface of the etched feature is badly pitted. FIGS. 5A and 5B are representative of etched copper lines and spaces, where the etched copper lines exhibit interior corrosion and poor exterior profile.

[0026] We have discovered basic chemistries and process parameters which make it possible to etch micron and submicron sized copper features on a semiconductor substrate while maintaining the integrity of the etched copper feature.

SUMMARY OF THE INVENTION

[0027] We have discovered that copper can be pattern etched in a manner which provides the desired feature dimension and integrity, at acceptable rates, and with selectivity over adjacent materials. To provide for feature integrity, the portion of the copper feature surface which has been etched to the desired dimensions and shape must be protected during the etching of adjacent feature surfaces. This is particularly important for feature sizes less than about 0.5 μm, where presence of even a limited amount of a corrosive agent can eat away a large portion of the feature. The copper feature integrity is protected by several different mechanisms: 1) The reactive etchant species are designed to be only moderately aggressive without ion bombardment, so that an acceptable etch rate is achieved without loss of control over the feature profile or the etch surface; 2) Hydrogen is applied over the etch surface so that it is absorbed onto the etch surface, where it acts as a boundary which must be crossed by the reactive species and a chemical modulator for the reactive species; and 3) Process variables are adjusted so that byproducts from the etch reaction are rendered more volatile and easily removable from the etch surface.

[0028] Preferred chlorine-comprising etchant species include HCl, or HCl*, or HCl+, or HCl−, or Cl, or Cl*, or Cl+, or Cl−, or combinations thereof, as opposed to Cl2, or Cl2*, or Cl2+, or Cl2−. In an inductively coupled plasma etch chamber, we have observed that the preferred chlorine reactive species are generated when the chlorine is dissociated from compounds rather than furnished as Cl2 gas.

[0029] The hydrogen which is applied over the etch surface is particularly important, as it is available to react with species which would otherwise penetrate that exterior surface and react with the copper interior to that surface. Sufficient hydrogen must be applied to the exterior surface of the etched portion of the copper feature to prevent incident reactive species present due to etching of adjacent feature surfaces from penetrating the previously etched feature exterior surface.

[0030] Although any plasma feed gas component comprising hydrogen, which is capable of generating sufficient amounts of hydrogen, may be used, the most preferred embodiment of the invention provides for the use of a component which contains both hydrogen and halogen. The etch chemistry for one of the more preferred embodiments utilizes hydrogen chloride (HCl) and/or hydrogen bromide (HBr), as the principal source of the reactive species for etching a copper surface. Dissociation of the HCl and/or HBr provides large amounts of hydrogen for absorption onto the etched copper surfaces, thereby preventing penetration by reactive species into the interior of adjacent the etched surfaces. Further, etch reaction with HCl species is less than with Cl2 species, and the reaction product and by products are more volatile when HCl etch species are used.

[0031] Additional hydrogen gas may be added to the plasma feed gas which comprises the HCl and/or HBr when the reactive species density in the etch process chamber is particularly high. The hydrogen-releasing, halogen-comprising plasma feed gas component may be used as an additive (producing less than 40% of the plasma-generated reactive species) in combination with other plasma etching species.

[0032] When HCl and/or HBr is used as the principal source of reactive species for the copper etching, the HCl or HBr accounts for at least 40%, and more preferably at least 50%, of the reactive species generated by the plasma. Most preferably, HCl or HBr accounts for at least 80% of such reactive species. Other reactive species may be used for purposes of improving the etched feature profile, improving etch selectivity, or reducing microloading effects. The species added for these purposes during etching of the copper feature preferably make up 30% or less, or more preferably make up 10% or less of the plasma-generated reactive species.

[0033] In particular, the preferred method for the etching of a copper surface to provide a patterned semiconductor device feature, includes the following steps:

[0034] a) supplying to a plasma etch process chamber a plasma feed gas which serves as a source for a dissociated halogen species and as a source for hydrogen, wherein the amount of hydrogen generated is sufficient to act as a boundary layer and a chemical modulator for the dissociated halogen species as the species react with a copper surface to be etched;

[0035] b) maintaining the temperature of the copper surface to be etched at a temperature sufficient to provide for advantageous volatility of halogen-containing etch reaction products and byproducts; and

[0037] In one of the more preferred embodiments, the plasma feed gas includes HCl, or HBr, or a combination thereof, in an amount which provides plasma-generated dissociated chlorine or bromine or a combination thereof and dissociated hydrogen in an amount sufficient to act as a boundary layer and chemical modulator for incident halogen-comprising species which strike a portion of a copper feature which has been etched to the desired dimensions. Gaseous hydrogen may be added to the plasma feed gas to adjust the ratio of the amount of hydrogen to the amount of halogen-comprising species, as needed to assist in obtaining the desired etch profile, etch selectivity or to reduce microloading effects.

[0038] In addition to the addition of gaseous hydrogen, other species-generating gases may be added for purposes of passivating, various surfaces and reacting with potentially corrosive species on the semiconductor substrate, as well as assisting in profile control, or in etch selectivity or to reduce microloading effects. Other additives may be, for example and not by way of limitation, nitrogen, fluorine-comprising molecules (which are particularly useful in etching barrier layers adjacent the copper layer which is to be patterned), chlorine-comprising molecules which do not contain hydrogen, inorganic hydrogen containing molecules, and hydrocarbon molecules. Specific examples of such molecules include, but are not limited to CxHy, BCl3, SiCl4, CCl4, CH3F, CHF3, N2, NH3, NH2OH, HI, H3As, H2S, H2Te, H4P2, and H3P, wherein x ranges from 1 to about 4 and y ranges from 2 to about 10.

[0039] Plasma feed gases may include additional inert (non-reactive with copper) gases such as argon, helium, or xenon, to enhance the ionization, or dissociation, or to dilute the reactive species. Further, such inert gases may be used as plasma source gases for purposes of heating up a semiconductor substrate during and/or prior to a copper etch.

[0040] In a particularly preferred embodiment of the present invention, copper is patterned on a substrate surface for use in semiconductor fabrication, wherein the method steps comprise:

[0041] a) supplying a plasma feed gas to a plasma etch process chamber, or other controlled environment for the production of a plasma, wherein said feed gas includes HCl, or HBr, or a combination thereof, wherein the amount of HCl or HBr is sufficient that at least 40%, and preferably at least 50%, of the total reactive species present in the plasma are supplied by the HCl or HBr or combination thereof; and

[0042] b) using a plasma created from the plasma feed gas in a manner which provides a reactive species density sufficient to enable a copper etch rate of at least about 2,000 Å per minute.

[0043] Hydrogen gas or a hydrogen-containing compound may be added to the feed gas in an amount which depends on the density of reactive species present at the surface of the copper during etching. Hydrogen gas may be added to the plasma feed gas for only a portion of a copper feature etch time period.

[0044] As previously mentioned, other gases capable of generating reactive species for purposes of surface passivation or as an oxygen “getter”, such as N2 or BCl3, respectively, may be used in the plasma feed gas. In addition, inert gases such as argon may be used.

[0045] The critical feature is the availability of hydrogen at the feature surface during the etching process. The use of HCl or HBr as the primary source of the copper etchant reactive species provides for the availability of dissociated, reactive hydrogen, as the hydrogen is released upon creation of the plasma and is adsorbed on or absorbed near the copper surface during etching, where it buffers the reaction of the chlorine or bromine species with the copper surface which is being etched. This protects the interior of the copper feature from subsequent corrosion while permitting etch rates for adjacent copper surfaces of at least 2,000 Å per minute. To enhance the amount of dissociated hydrogen available, hydrogen may be generated from hydrogen-containing compounds.

[0046] Another important feature of the use of HCl and HBr to generate reactive etchant species is that the species generated are less aggressive than those generated from Cl2, so an acceptable etch rate is achieved and the volatility of the etch products and byproducts is greater, so that the corrosive activity at the copper surface is reduced.

[0047] When the etch process is carried out typically oxygen-comprising species are generated from a silicon oxide hard mask or a photoresist, or from an insulating layer present on the substrate. Under these circumstances, it is advantageous to add boron trichloride (BCl3) or an equivalent oxygen scavenger.

[0048] Another preferred embodiment relates to the use of a plasma source gas including a halogen-comprising primary etchant species (preferably generated from a halogen-comprising compound) in combination with a hydrogen-generating source. Preferably the halogen-comprising primary etchant species is generated from a low molecular weight compound such as, and not by way of limitation, HCl, HBr, BCl3, CHF3, SiCl4, CCl4, and combinations thereof. The most preferred compound for this embodiment is BCl3. The hydrogen-generating source may include hydrogen gas, but always includes at least one hydrogen-generating compound, preferably a low molecular weight hydrocarbon. Examples of the hydrogen-generating compound include, for example, but not by way of limitation, CxHy, CH3F, CHF3, NH3, NH2OH, HI, H3As, H2S, H2Te, H4P2, and H3P, where x ranges from 1 to about 4 and y ranges from 2 to about 10.

[0049] Diluent gases such as argon, helium, krypton, and xenon, and complexing gases such as nitrogen (which promote the presence of reactive halogen species) may be used in combination with the primary etchant source compound and the hydrogen-generating source.

[0050] With regard to all of the embodiments of the invention, whether the primary etchant is HBr, HCl, BCl3, or one of the other named sources for a halogen-comprising species, when other process conditions and materials (such as plasma source power, or substrate bias power, or substrate temperature, or plasma source gas flow rate), which are necessary to provide the desired etch rate or etched pattern profile, cause the surface of the etched profile to exhibit pits or pockets, an increase in the process chamber pressure can be used to reduce the damage to the etched surface. In particular, rather than operating at a process chamber pressure in the range from about 0.1 mT to about 20 mT which is typically used in an inductively coupled plasma chamber, the process chamber pressure is increased to be in the range from about 20 mT up to about 200 mT. In a capacitively coupled plasma chamber the higher pressure regime ranges from about 100 mT up to 5 Torr. As the chamber pressure is increased, copper etch rate is increased and the electron temperature of the etchant species decreases, whereby plasma damage to the device structures (such as transistors) beneath the copper etch surface is reduced.

BRIEF DESCRIPTION OF THE DRAWINGS

[0051]FIG. 1 is a schematic illustrating a decoupled plasma source (DPS) etching chamber of the kind used during the patterned etching of copper as described in the preferred embodiments of the present invention.

[0052]FIG. 2A illustrates the change in copper intensity in the etch plasma during the etching of a pattern of 0.5 μm wide lines and spaces into the surface of a copper film, where the principal source for the copper-etching reactive species is HCl.

[0053]FIG. 2B illustrates the change in copper intensity in the etch plasma during the etching of a pattern of 0.5 μm wide lines and spaces into the surface of a copper film, where the principal source for the copper-etching reactive species is HBr.

[0054]FIG. 3A illustrates the etch rate in μm per minute for a pattern of 0.5 μm wide lines and spaces into the surface of a copper film, as a function of etch chamber pressure. The feed gas to the etch chamber included HCl, N2, and BCl3.

[0055]FIG. 3B illustrates the etch rate for the same patterned copper film as that described with reference to FIG. 3A, but as a function of source power.

[0056]FIG. 3C illustrates the etch rate for the same patterned copper film as that described with reference to FIG. 3A, but as a function of bias power.

[0057]FIG. 4A illustrates the selectivity of copper relative to the patterning mask, shown as the ratio of copper etch rate to silicon oxide etch rate for a standard test pattern of various width lines and spaces, as a function of etch chamber pressure.

[0058]FIG. 4B illustrates the selectivity of copper relative to patterning mask, shown as the ratio of copper etch rate to silicon oxide etch rate for the same test pattern as that described with reference to FIG. 4A, but as a function of source power.

[0059]FIG. 4C illustrates selectivity of copper relative to patterning mask, shown as the ratio of copper etch rate to silicon oxide etch rate for the same test pattern as that described with reference to FIG. 4A, but as a function of bias power.

[0060]FIG. 5A is a three dimensional schematic of a copper film which was reactive ion etched using Cl2, BCl3, N2, and Ar to produce a pattern of 0.5 μm wide lines and spaces. Although the integrity of the etched copper lines appears to be good on the surface, large portions of the interior of the copper lines is vacant space from reacted copper which has exited.

[0061]FIG. 5B is a schematic of the cross-sectional view of the FIG. 5A etched copper pattern, showing additional detail of the structure of the interior of the etched copper line.

[0062]FIG. 6A is a three dimensional schematic of a copper film which was reactive ion etched using a preferred embodiment method of the present invention. The integrity of the interior of the etched copper lines is excellent.

[0063]FIG. 6B is a schematic of the cross-sectional view of FIG. 5A etched copper pattern, showing additional detail of the structure of the interior of the etched copper line.

[0064]FIG. 6C is a schematic of the FIG. 5A etched copper pattern which shows the top surface of the etched lines (as well as the front edge) and the top surface of the etched spaces, to illustrate the absence of any deposits on the exterior of the etched lines and spaces.

[0065]FIG. 7A is a schematic showing a pattern etched copper surface which was etched using BCl3 as the sole reactive etchant species.

[0066]FIG. 7B is a schematic showing a pattern etched copper surface which was etched using BCl3 as the sole reactive etchant species in combination with CH4 as the hydrogen-generating source compound.

[0067]FIG. 8 is a plot of the etchant species Electron Temperature (eV) as a function of the chamber pressure in mT, for an HCl plasma etch in a decoupled plasma source process chamber.

[0068]FIG. 9 is a graph showing substrate (wafer) temperature versus time for heating of a substrate by ion bombardment. One of the plots shown on the graph is for the substrate temperature increase when argon was used as the source gas for the plasma from which ion bombardment was obtained. The other plot is for the substrate temperature increase when nitrogen was used as the source gas.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0069] We have discovered that copper can be pattern etched in a manner which provides the desired feature dimension and integrity, at acceptable rates, and with selectivity over adjacent mask materials. To provide for feature integrity, the portion of the copper feature surface which has been etched to the desired dimensions and shape must be protected during the etching of adjacent feature surfaces. To avoid the trapping of reactive species interior of the etched copper surface, hydrogen is applied to that surface.

[0070] One of the more preferred embodiment of the invention provides for the use of hydrogen chloride (HCl) and/or hydrogen bromide (HBr) as the sole-or principal source of the reactive species used in etching copper. Dissociation of the HCl and/or HBr provides the large amounts of hydrogen which acts as both a physical and chemical modulator to protect the etched surfaces of the copper feature from penetration by reactive species adjacent the etched surface. Additional hydrogen gas may be added to the plasma feed gas which comprises the HCl and/or HBr when the reactive species density in the etch process chamber is particularly high.

[0071] In another preferred embodiment of the invention, BCl3 is used as the sole or principal source of reactive species used in etching copper. However, since this etchant source does not produce hydrogen upon dissociation, it is necessary to add a hydrogen-generating source, preferably a hydrogen generating compound which is capable of dissociating under process conditions to produce hydrogen. A particularly preferred hydrogen-generating compound is a hydrocarbon, CxHy where x ranges from 1 to about 4 and y ranges from about 2 to about 10. The hydrocarbon can be in surprisingly small amounts, typically less than 10% by volume of the plasma source gas.

[0072] I. DEFINITIONS

[0073] As a preface to the detailed description, it should be noted that, as used in this specification and the appended claims, the singular forms “a”, “an”, and “the” include plural referents, unless the context clearly dictates otherwise. Thus, for example, the term “a semiconductor” includes a variety of different materials which are known to have the behavioral characteristics of a semiconductor, reference to a “plasma” includes a gas or gas reactants activated by a glow discharge, and a reference to “copper” includes alloys thereof.

[0074] Specific terminology of particular importance to the description of the present invention is defined below.

[0075] The term “anisotropic etching” refers to etching which does not proceed in all directions at the same rate. If etching proceeds exclusively in one direction (e.g. only vertically), the etching process is said to be completely anisotropic.

[0076] The term “aspect ratio” includes but is not limited to the ratio of the height dimension to the width dimension of particular openings into which an electrical contact is to be placed. For example, a via opening which typically extends in a tubular form through multiple layers has a height and a diameter, and the aspect ratio would be the height of the tubular divided by the diameter. The aspect ratio of a trench would be the height of the trench divided by the minimal travel width of the trench at its base.

[0077] The term “bias power” refers to the power used to control ion bombardment energy and the directionality of ions toward a substrate.

[0078] The term “copper” refers to copper and alloys thereof, wherein the copper content of the alloy is at least 80 atomic % copper. The alloy may comprise more than two elemental components.

[0079] The term “decoupled plasma source” refers to a plasma etch apparatus which has separate controls for power input to the plasma source generator and to the substrate bias device. Typically the plasma source controller controls the supply of inductively coupled RF power which determines plasma density (source power) and the bias controller controls the supply of RF power or DC power which is used to generate a DC bias voltage on the semiconductor substrate surface (bias power). The bias voltage affects the ion bombardment energy on the substrate surface. This decoupled plasma source typically incorporates measures to separate (decouple) the influence of the source and bias on one another. The CENTURA® metal etch system available from Applied Materials, Inc. of Santa Clara, Calif. which includes decoupled plasma source power and bias power control is referred to as a “DPS” system. Similar equipment available from other manufactures may be referred to by different nomenclature.

[0080] The term “feature” includes but is not limited to metal lines and openings on a substrate, and other structures which make up the topography of the substrate surface.

[0081] The term “glow discharge sputtering” includes but is not limited to a mechanism in which atoms are dislodged from a surface which is to be sputtered, by collision with high energy particles which are generated by a glow discharge, where the glow discharge is a self-sustaining type of plasma. The high energy particles may be energetic atoms as well as energetic molecules.

[0082] The term “ion bombardment” includes but is not limited to physical bombardment by ions (and other excited species of atoms which are present with the ions) to remove atoms from a surface, where physical momentum transfer is used to achieve the atom removal.

[0083] The term “isotropic etching” refers to an etching process where etching can proceed in all directions at the same rate.

[0084] The term “plasma” includes but is not limited to a partially ionized gas containing an equal number of positive and negative charges, as well as some other number of non-ionized gas particles.

[0085] The term “source power” refers to the power used to generate ions and neutrals whether directly in an etching chamber or remotely as in the case of a microwave plasma generator.

[0086] The term “substrate” includes semiconductor materials, glass, ceramics, polymeric materials, and other materials of use in the semiconductor industry.

[0087] II. AN APPARATUS FOR PRACTICING THE INVENTION

[0088] The etch process was carrier out in a Centura® Integrated Processing System available from Applied Materials, Inc. of Santa Clara, Calif. The system is shown and described in U.S. Pat. No. 5,186,718, the disclosure of which is hereby incorporated by reference. This equipment included a Decoupled Plasma Source (DPS) of the kind described by Yan Ye et al. at the Proceedings of the Eleventh International Symposium of Plasma Processing, May 7, 1996 and as published in the Electrochemical Society Proceedings, Volume 96-12, pp. 222-233 (1996). The plasma processing chamber enables the processing of an 8 inch (200 mm) diameter silicon wafer.

[0089] A schematic of the processing chamber is shown in FIG. 1A which shows an etching process chamber 10, which is constructed to include at least one inductive coil antenna segment 12 positioned exterior to the etch process chamber 10 and connected to a radio frequency (RF) power generator 18. Interior to the process chamber is a substrate 14 support pedestal 16 which is connected to an RF frequency power generator 22 through an impedance matching network 24, and a conductive chamber wall 30 which serves as the electrical ground 34 for the offset bias which accumulates on the substrate 14 as a result of the RF power applied to the substrate support pedestal 16.

[0090] The semiconductor substrate 14 is placed on the support pedestal 16 and gaseous components are fed into the process chamber through entry ports 26. A plasma is ignited in process chamber 10 using techniques well known in the industry. Pressure interior to the etch process chamber 10 is controlled using a vacuum pump (not shown) and a throttle valve 27 connected to a process chamber gas exit line 28. The temperature on the surface of the etch chamber walls is controlled using liquid-containing conduits (not shown) which are located in the walls of the etch chamber 10. The temperature of the semiconductor substrate may be controlled by bombarding the surface of the substrate with an argon plasma to reach initial temperature and subsequently, during the etch process by impact of plasma species on the substrate surface. For example, in the presently described embodiments, it was desired to maintain the substrate temperature above about 150° C. and below about 350° C., which we were able to do relying solely upon surface bombardment of the substrate. However, it would be possible to use a temperature-controlled substrate support pedestal 16, or a combination of substrate surface bombardment and a temperature-controlled support pedestal. The surface of the etching chamber 10 walls was maintained at about 80° C. using the cooling conduits previously described. In the case of a production process, preferably, the substrate support platen provides for backside heating or cooling of the substrate.

[0091] When it is desired to increase the percentage of the etchant species which are ions at the time they strike the substrate surface, the apparatus described above may be modified so that the inductive coil used to generate a plasma is located internal to rather than external to the process chamber. Or, the apparatus may be modified by adding at least one inductive coil which is internal to the process chamber. An etch chamber where the external inductive coil has been replaced by an internal inductive coil is described in detail in U.S. patent application Ser. No. 08/869,798 of Yan Ye et al., filed Jun. 5, 1997, entitled: “RF Plasma Etch Reactor With Internal Inductive Coil Antenna And Electrically Conductive Chamber Walls”, and assigned to the assignee of the present application; this patent application is hereby incorporated herein by reference in its entirety.

[0092] In particular, the apparatus is an RF plasma etch reactor having an etch chamber with electrically conductive walls and a protective layer forming the portion of the walls facing the interior of the chamber. The protective layer prevents sputtering of material from the chamber walls by a plasma formed within the chamber. The etch reactor also has an inductive coil antenna disposed within the etch chamber which is used to generate a plasma by inductive coupling. Like the chamber walls, the inductive coil antenna is conducted to prevent sputtering of the material making up the antenna by the plasma. The coil antenna may have a tubular structure with a hollow interior channel which channel is used to sustain a flow of coolant fluid therethrough, whereby the antenna can be maintained within a prescribed temperature range.

[0093] III. ACHIEVING PATTERNED COPPER ETCH USING THE METHOD OF THE PRESENT INVENTION WHERE AT LEAST THE MAJORITY OF HYDROGEN IS GENERATED BY DISSOCIATION OF THE PRINCIPAL ETCHANT COMPOUND (SUCH AS HCl or HBr)

[0094] The Examples provided below for the etching of patterned copper were practiced in the Centura® Integrated Processing System having an external inductive coil only, of the kind described with reference to FIG. 1.

[0095] The substrate was a silicon wafer overlaid by a silicon oxide dielectric layer. Typically, a 500 Å thick barrier layer of tantalum was applied over the silicon oxide dielectric layer. A 5,000 Å thick layer of copper was sputter deposited over the barrier layer. A 250 Å thick layer of tantalum was applied over the copper layer, and a 5,000 Å thick patterned silicon oxide hard mask was applied over the tantalum layer. When the substrate varied from this general description, the variance is specified in the particular preferred embodiment described.

[0096] A plasma was created in the etch chamber using standard techniques, with the composition of the plasma feed gas being as specified. The power to the external RF coil is specified for each Example, with the frequency being about 2 MHZ in all cases. A substrate offset bias was created by application of RF power at a frequency of about 13.56 MHZ and a wattage above about 50 W (equivalent to a bias voltage of about 20 V). Preferably the power to the support platen ranges from about 400 W to about 800 W.

[0097] The pressure in the etch chamber ranged between about 0.1 mT to 100 mT, and was preferably below about 20 mT. The temperature on the substrate surface ranged from about 130° C. to about 350° C., and controlled by using ion bombardment from a plasma which was generated from a source gas designed to provide the desired temperature, or by heat transfer from an underlying substrate support platen or a combination of both. The wall temperature of the etch chamber was preferably at least 50 degrees lower than the substrate temperature. Typically the etch chamber surface was maintained between about 80° C. and about 150° C., although the precise chamber wall temperature is not critical..

EXAMPLE ONE Etch Rate

[0098]FIG. 2A shows the etch rate curve 210 for the etching of a copper film to form a pattern of 0.35 μm wide lines and spaces using HCl as the principal source of copper etchant reactive species. In particular, the base of the substrate etched was a silicon wafer having a thermal oxide coating on its surface. A 500 Å thick layer of tantalum was applied over the thermal oxide; a 18,000 Å thick layer of copper was applied over the tantalum layer; a 250 Å thick tantalum nitride layer was applied over the copper layer; and, finally, a silicon oxide hard mask 5,000 Å thick was applied over the tantalum nitride layer.

[0099] This stack of materials was etched in the Centura® Integrated Processing System previously described. The plasma feed gas to the process chamber was 100 sccm of HCl, 25 sccm of N2, and 5 sccm BCl3. The substrate temperature during etching was about 200° C., with the process chamber walls at about 80° C. The process chamber pressure during etching was 20 mT. The source power to the plasma inducing coil was about 1,500 W (2 MHZ and the bias power to the substrate support platen was about 500 W @ 13.56 MHZ. A plasma was ignited using techniques standard in the art, and the presence of any copper emissions in the plasma were monitored using an optical sensor measuring at a wavelength of about 3,250 Å. FIG. 2A shows the optical emission intensity 212 for copper appearing in the plasma, as a function of time 214 in seconds. At about 90 seconds, the intensity of the copper in the plasma began dropping, indicating that the copper etching area was depleting. Since etching is slower is some areas than in others, the copper in the plasma gradually decreased, and the curve 210 leveled out at about 120 seconds, indicating that the etch was completed in all areas. Applicants believe the average time for completion of etching to be about 105 seconds. Using 105 seconds as the time for completion of etching, the calculated etch rate is about 10,000 Å per minute or about 1.0 μm per minute.

[0100]FIG. 2B shows the etch rate curve 220 for the etching of a copper film to form a pattern of 0.35 μm wide lines and spaces using HBr as the principal source of copper etchant reactive species . In particular, the base of the substrate etched was a silicon wafer having a thermal oxide coating on its surface. A 500 Å thick layer of tantalum was applied over the thermal oxide; a 5,000 Å thick layer of copper was applied over the tantalum layer; a 250 Å thick tantalum nitride layer was applied over the copper layer; and, finally, a silicon oxide hard mask 5,000 Å thick was applied over the tantalum nitride layer.

[0101] This stack of materials was etched in the Centura® Integrated Processing System previously described. The plasma feed gas to the process chamber was 100 sccm of HBr, 25 sccm of N2, and 5 sccm BCl3. The substrate temperature during etching was about 200° C., with the process chamber walls at about 80° C. The process chamber pressure during etching was 20 mT. The source power to the plasma inducing coil was about 1,500 W and the bias power to the substrate support platen was about 500 W. A plasma was ignited using techniques standard in the art, and copper emissions appearing in the plasma were monitored using an optical sensor measuring at a wavelength of about 3,250 Å. FIG. 2B shows the optical emission intensity reading 222 for the copper appearing in the plasma, as a function of time 224 in seconds. Since a pattern was etched, again, the completion of copper etch was indicated, by a drop in the copper intensity reading over time. At the end of 20 seconds, the amount of copper began to drop, indicating that the majority of the etching was complete, with curve 220 leveling out to show no copper generated at about 30 seconds. Applicants believe the average time for completion of etching to be about 25 seconds. Using 25 seconds as the time for completion of etching, the calculated etch rate is about 12,000 Å per minute or about 1.2 μm per minute.

[0102] As a part of determining the effect of process variables on etch rate, the effect of process chamber pressure, plasma source power, and bias power were investigated. In particular, HCl was the principal source of etchant reactive species; the plasma feed gas was of the composition specified with reference to FIG. 2A above; the substrate stack was the same; the pattern etched was the same; and all process variables were the same with the exception of the variable investigated.

[0103] As a matter of importance, the preferred embodiments described above were carried out at a substrate temperature of about 200° C., and preferably the process is carried out at a temperature of at least about 200° C. as this temperature assists in the volatilization of etch products and byproducts so that these materials are more easily removed from the etched copper surface and from the process chamber. However, the etch process works at temperatures above about 130° C. We have yet to determine the highest recommended temperature; however, one skilled in the art will appreciate that at higher temperatures other materials within the substrate are affected, thermal expansion differences can cause problems, and that there needs to be an optimization of substrate temperature depending on the device and the feature being fabricated. In any case, the substrate temperature should not exceed about 400° C.

[0104] Curve 310 of FIG. 3A shows the etch rate 312 as a function of process chamber pressure 314, with the etch rate increasing with an increase in chamber pressure, at least up to 20 mT.

[0105] Curve 320 of FIG. 3B shows the etch rate 322 as a function of plasma source power 324, with the etch rate increasing with an increase in plasma source power, at least up to 1,600 W.

[0106] Curve 330 of FIG. 3C shows the etch rate 332 as a function of bias power 334, with the etch rate slightly decreasing with an increase in bias power, at least up to 600 W. This is an unexpected result. It may be that the higher bias power is causing the deposition of a species at the surface of the patterned spaces where etching is occurring, and this species is inhibiting the etching of the copper. However, by adjusting other variables such as process chamber pressure and plasma source power, the shape of this curve may be altered.

[0107] We also investigated the variable of feed gas composition, where the sccm of HCl was decreased to 75 or 50 or 25 sccm with other feed gas flow rates held almost constant at the values previously specified for an HCl flow rate of 100 sccm. We discovered that the etch rate was only marginally affected, with a slight increase in etch rate with increasing HCl flow rate. Based on this discovery, we have concluded that, for HCl flow rates above about 25 sccm (and under the process conditions described), it is the surface reaction rate which controls the etch rate, rather than the concentration of reactive species in the plasma or the transfer rate of those species to the surface of the copper.

EXAMPLE TWO Selectivity

[0108] We have determined that, using the substrate and process variables specified with reference to FIG. 2A, the selectivity ratio of copper to silicon oxide hard mask is about 4:1 (i.e., copper etches four times faster than the hard mask).

[0109] Further, the effect of process variables on this selectivity were investigated. In particular, the effect of process chamber pressure, plasma source power, and bias power were investigated. Again, HCl was the principal source of etchant reactive species; the plasma feed gas was of the composition specified with reference to FIG. 3A above; the substrate stack was the same; the pattern etched was the same; and all process variables were the same with the exception of the variable investigated. Curve 410 of FIG. 4A shows the selectivity ratio 412 of copper to silicon oxide hard mask as a function of process chamber pressure 414, with the selectivity ratio increasing with an increase in chamber pressure, at least up to 20 mT.

[0110] Curve 420 of FIG. 4B shows the selectivity ratio 422 as a function of plasma source power 424, with the selectivity ratio increasing with an increase in plasma source power, at least up to 1,600 W.

[0111] Curve 430 of FIG. 4C shows the selectivity ratio 432 as a function of bias power 434, with the selectivity ratio decreasing with an increase in bias power, at least up to 600 W.

[0112] Again, we investigated the effect of varying feed gas composition, where the sccm of HCl was decreased to 75 or 50 or 25 sccm with other feed gas flow rates held essentially constant at the values previously specified for an HCl flow rate of 100 sccm. We discovered that the selectivity ratio for copper to silicon oxide hard mask was relatively unaffected.

EXAMPLE THREE Comparitive Example

[0113] As previously described, we have determined that the etch process typically applied to aluminum does not work well for copper. This is not to say that such a process cannot be made to work if all of the variables are carefully optimized. However, the method of the present invention offers a wider process window.

[0114] In reviewing the March 1995 article “Dry Etching Technique for Subquarter-Micron Copper Interconnects” by Igarashi et al.. where the etch process recommended is a variation of the process used for aluminum, we noticed that the interior of the etched copper features appeared to be hollow at some locations. To determine the cause of this phenomenon, we attempted to reproduce the results of Igarashi et al. This example is provided as a comparitive example, since the process was carried out in the same equipment in which we achieved the elimination of the interior corrosion of the copper features.

[0116] The plasma feed gas comprised 100 sccm Ar, 20 sccm Cl2, 15 sccm N2, and 10 sccm BCl3. A relatively high concentration of N2 and a higher bias power during etching were used to for a thicker passivation layer on the sidewall.

[0117] The RF plasma source power was approximately 1,500 W. The bias power was approximately 500 W. The pressure in the etch chamber was about 10 mT. The temperature on the substrate surface was about 200° C., while the wall temperature of the etch chamber was about 80° C.

[0118]FIGS. 5A and 5B are schematics of photomicrographs of the etched pattern of 0.5 μm lines 510 and spaces 512 created by the method described above. With reference to FIG. 5A, the silicon oxide hard mask 514 overlies tantalum barrier layer 515. The etched copper lines 510 include the copper 520 remaining after etch, surrounded by vacant space 522 where the copper has reacted with a corrosive agent to produce a volatile species which escaped into the process chamber. The exterior walls 516 of the etched copper have been passivated so that they remain relatively intact despite the corrosion of the interior of the copper line 510. The silicon oxide surface 518 of the etched spaces 512 is relatively free from contaminating deposits.

[0119]FIG. 5B shows the problem of the corrosion of the interior of the etched lines 510 in more detail. Again, the silicon oxide hard mask 114 sets above tantalum barrier layer 515. The copper line exterior walls 516 are apparently continuous and intact. However, interior to the walls 516, the copper 520 has been corroded and the reactive species resulting from the corrosion have escaped leaving open space 522 surrounding the corroded copper 520.

EXAMPLE FOUR A Preferred Embodiment of the Present Invention

[0120] As disclosed in the Summary of the Invention, the preferred embodiment of the invention provides for the use of hydrogen chloride (HCl) and/or hydrogen bromide (HBr) as the sole or principal source of the reactive species used in etching copper. Dissociation of the HCl and/or HBr provides the large amounts of hydrogen necessary to protect the copper feature etched surfaces from penetration by reactive species adjacent the etched surface. Additional hydrogen-comprising gas may be added to the plasma feed gas which comprises the HCl and/or HBr when the reactive species density in the etch process chamber is particularly high.

[0121] In this example, under the conditions specified, it is not necessary to add additional hydrogen-comprising gas to the plasma feed gas. Although this Example is for the use of HCl as the principal source of reactive species, HBr could be substituted in this example with equivalent results.

[0122] In this Example, the plasma feed gas consists of HCl at a flow rate of about 100 sccm, N2 at a flow rate of about 20 sccm and BCl3 at a flow rate of about 5 sccm, where the chemically reactive copper etchant was HCl, the N2 was used to passivate silicon species (and some copper species), and the BCl3 was used to scavenge oxygen generated by etch of the silicon hard mask or the silicon oxide dielectric layer underlying the copper line. In addition, we have evaluated varying ratios of the plasma feed gas components, such as: 50 sccm HCl and 5 sccm N2; 50 sccm HCl, 25 sccm N2, and 5 sccm BCl3; 50 sccm HCl, 5 sccm N2, and 5 sccm CHF3; and, 100 sccm HCl, 5 sccm N2, and 5 sccm BCl3. We also evaluated HCl as the sole plasma feed gas at 50 sccm of HCl. In evaluating all of these plasma feed gases, we learned that we could produce a patterned etch of 0.5 μm wide lines and spaces where etch rate, selectivity, feature dimensions, and feature integrity are all excellent. In fact, the etch results were so similar, that FIGS. 6A, 6B, and 6C which represent this Example are representative of the features obtained for all of the plasma feed gas combinations evaluated, including HCl as the sole feed gas.

[0124] The RF power to the plasma induction coil, the plasma source power, was about 1,500 W @ 2 MHZ, and the RF power to the substrate support platen, the bias power, was about 500 W @ 13.56 MHZ. The pressure in the process chamber was 20 mT. The substrate temperature was about 200° C. and the wall temperature of the process chamber was about 80° C. Etching was carrier out over a time period of about 100 seconds.

[0125]FIGS. 6A and 6B are schematics of photomicrographs of the etched pattern of 0.5 μm lines 610 and spaces 612 created using the method described this Example Four. With reference to FIG. 6A, the silicon oxide hard mask 614 overlies tantalum barrier layer 615. The etched copper lines 610 include the solid interior copper 620 remaining after etch. The exterior walls 616 of the etched copper are deposit free and exhibit the desired profile which is achieved by the anisotropic etch process described above. The silicon oxide surface 618 of the etched spaces 612 also free from contaminating deposits.

[0126]FIG. 6B shows a schematic of the cross-sectional view of the lines and spaces of FIG. 6A. Again, the silicon oxide hard mask 614 sets above tantalum barrier layer 615. The copper line exterior walls 616 are free of deposits from the etch process. In addition, the interior copper 620 solidly fills the exterior walls 616, providing a line 610 structure having integrity.

[0127] By comparison with the line 510 structure from the Comparitive Example Three, the absence of corrosion in the interior copper 620 of the preferred embodiment described in this Example Four is attributed to the generation of a less aggressive chlorine etchant species from the HCl compound and to the generation of a large quantity of dissociated hydrogen upon dissociation of the HCl plasma feed gas. The hydrogen is believed to absorb on the surface of the copper, forming an H-rich layer. This H-rich layer helps moderate the physical and chemical effects of the etchant species and aids in the formation of more volatile byproducts which can be readily removed from the copper surface and from the etch process chamber. Thus, the hydrogen present on the copper surface acts as a buffer which permits etching to occur without leaving behind excess chlorine on the copper surface which causes continuing undesired reaction with the copper after the desired etch is completed. It is this continuing undesired reaction, combined with the formation of copper oxides, which we are calling “corrosion”. It is corrosion which generates vacant spaces (of the kind shown in FIGS. 5A and 5B) inside the walls of the copper lines.

[0128]FIG. 6C shows schematic of a photomicrograph of the FIG. 6A etched copper pattern. The photomicrograph shows the top surface 630 after removal of the silicon oxide hard mask, the walls 616 of the etched lines 610, and the silicon oxide surface 618 of etched spaces 612, to illustrate the absence of any deposits on these surfaces.

[0129] Once the non-corroded etched feature is created, a capping layer can be applied to the copper surface to prevent future corrosion. Preferred capping layers include silicon nitride and silicon oxynitride. These capping layers can be generated by adding nitrogen and/or a nitrogen-containing gaseous compound to an inert carrier gas, forming a plasma, and plasma sputtering against a silicon oxide-containing surface, such as a silicon oxide hard mask.

[0130] Although specific process conditions are described with respect to Example Four above, applicants have learned that the process window is quite broad and that the process variables can be adjusted over a wide range and still provide excellent etched copper features.

[0131] For example, the plasma source power supplied for production of reactive species (ions and neutrals) may vary widely. The minimum power required is the power necessary to break down HCl or HBr into several reactive species, such a H, excited H, H+, Cl, excited Cl, Cl+, excited HCl, HCl, Br, excited Br, and Br+. Often the minimum power required is the power to ignite and sustain the plasma in the process chamber. In a DPS chamber of the kind we used, the minimum inductive RF power required is generally about 200 W @ 2 MHZ. However, the power supplied may range from about 200 W to about 2,500 W, depending on the feature to be etched, the materials involved, and the make up of the plasma feed gas, for example. In addition to dissociation and ionization of the plasma feed gas, the RF power sustaining the plasma is also a source of supplying heat to the wafer surface (the higher the power, the higher the wafer temperature). The RF power also affects the production of UV light and/or IR light which is generated from the plasma. These light sources may impact the reaction taking place on the substrate surface.

[0132] It is important to note that the plasma source power may be supplied from varying types of equipment, including: a parallel plate plasma source; an inductive coil, whether that coil is located externally to the process chamber, internally to the process chamber, or a combination of both; and a microwave plasma source (by way of example and not by way of limitation).

[0133] The bias power used to control ion bombardment on the substrate surface may also be varied over a range depending on the feature to be etched, the materials involved, and desired characteristics of the semiconductor device in general. The minimum bias power required for the HCl and HBr etch chemistry described herein is the power which can provide the desired ion directionality and ion bombardment energy for an anisotropic etch. In a DPS chamber of the kind we used, the minimum RF power required is generally about 50 W @ 13.56 MHZ. However, the RF power supplied may range from about 50 W to about 800 W, depending on the feature to be etched, the materials involved, and the make up of the plasma feed gas, for example. Higher bias power typically increases the etch rate due to the higher ion bombardment energy; however, as shown with regard to Example 1, FIG. 3C, this is not necessarily the case. Higher bias power may result in the generation of additional species which affect etch rate. Bias power also affects the dimensionality, including the etch profile of the feature being etched, and must be adjusted as required to obtain proper feature dimensions. Higher bias power also results in an increase in the temperature of the substrate surface as a result of increased ion bombardment and may require a means for cooling of the substrate during the etch process.

[0134] Process chamber pressure variation, all other variables held constant, may affect the dissociation rate, ionization rate, and recombination rate of various plasma feed gases. It is possible to optimize the reactive species generated and to control the ratios of the etchant species using process chamber pressure. Thus, both passivation and etch rates can be adjusted using process chamber pressure. Pressure may also affect the thickness of the plasma sheath within the reactor and thereby the ion bombardment energy. The optimal process chamber pressure is equipment sensitive. In a DPS chamber of the kind we used, the optimal pressure appears to be about 20 mT. However, we have operated the process chamber at pressures ranging from about 5 mT to about 40 mT and achieved acceptable etch results.

[0135] The surface temperature of the substrate affects the reaction rates on that surface and the dissociation rate of etch by-products. When copper is etched using HCl or HBr, or a combination thereof as the principal source of the reactive etchant species, desorption of the etch-byproduct appears to be more critical than surface reaction rate, and it appears that a minimum substrate surface temperature of about 150° C. provides the necessary desorption rate.

[0136] Although the preferred embodiments described are with reference to an etching process where the composition of the plasma feed gas was constant throughout, one skilled in the art would appreciate that the feed gas could be varied during an etching process and the method of the present invention could be used for a limited time period during that etching process.

[0137] IV. ACHIEVING PATTERNED COPPER ETCH USING THE METHOD OF THE PRESENT INVENTION WHERE AT LEAST THE MAJORITY OF HYDROGEN IS GENERATED BY DISSOCIATION OF A HYDROGEN-CONTAINING COMPOUND OTHER THAN THE PRINCIPAL ETCHANT SPECIES SOURCE COMPOUND

[0138] The Examples provided below for the etching of patterned copper were practiced in the Centura® Integrated Processing System having an external inductive coil only, of the kind described with reference to FIG. 1.

[0139] The substrate was a silicon wafer overlaid by a silicon oxide dielectric layer. Typically, a 100 Å thick barrier/wetting layer of tantalum was applied over the silicon oxide dielectric layer. A 300 Å thick layer of tantalum nitride was applied over the tantalum barrier/wetting layer. A 100 Å thick barrier/wetting layer of tantalum was applied over the tantalum nitride layer. An 8,000 Å thick layer of copper was sputter deposited over the barrier layer. A 100 Å thick barrier/wetting layer of tantalum was applied over the copper layer, followed by a 300 Å thick layer of tantalum nitride, followed by a 100 Å thick barrier/wetting layer of tantalum. Finally, a 6,000 Å thick silicon oxide hardmask was applied over the top layer of tantalum, for patterning purposes.

[0140] A plasma was created using standard techniques in the inductively coupled plasma etch chamber, with the plasma source power being separately controlled from the substrate bias power, and with the composition of the plasma feed gas being as specified. The plasma source power to the external RF coil is specified for each Example, with the frequency being about 2 MHZ in all cases. Typically the plasma source power ranged from about 1,000 W to about 3,000 W (preferably about 1500 W). A substrate offset bias was created by application of RF power to the substrate support platen at a frequency of about 13.56 MHZ and a wattage ranging from about 300 W to about 1,000 W, and preferably above 500 W. The pressure in the inductively coupled plasma etch chamber ranged between about 0.1 mT to 100 mT, and preferably ranged between about 10 mT and about 50 mT.

[0141] In a capacitive-coupled plasma etch chamber, the plasma source power would typically range from about 500 W to about 2,000 W, and would preferably be about 1000 W. The pressure in the etch chamber would range from about 50 mT to about 5 Torr.

[0142] The temperature on the substrate surface ranged from about 200° C. and about 300° C. (and was preferably about 275° C., while the wall temperature of the etch chamber was preferably at least 50 degrees lower than the substrate temperature. Typically the etch chamber surface was maintained at about 100° C. or less.

EXAMPLE FIVE Etching with BCl3 as the Sole Source of Reactive Etchant Species

[0143] In this Example, the plasma feed gas consists of BCl3 at a flow rate of about 100 sccm, N2 at a flow rate of about 30 sccm and argon at a flow rate of about 50 sccm. The temperature on the substrate surface ranged from about 200° C. and about 300° C., while the wall temperature of the etch chamber was approximately 80° C. The plasma source power was about 1,500 W; and the substrate bias power was about 600 W. The etch chamber pressure was about 25 mT.

[0144]FIG. 7A is a schematic showing a front view of a sidewall surface of a pattern-etched copper line which was one of a series in a pattern of 0.375 μm lines and spaces.

[0145] With reference to FIG. 7A, the line 700 sidewall surface 710 extends above the silicon oxide-covered substrate 712. The silicon oxide hardmask and tantalum/tantalum nitride/tantalum layers which were overlying the upper surface 702 of line 700 during the etching process have been removed. Sidewall surface 710 exhibits severe pitting 714 of the copper. No notching at upper surface 702 (between the overlying layers and the upper surface of the copper) was observed. Based on tunneling electron microscope (TEM) analysis, there was no sidewall passivation layer on the etched copper sidewall 710. Typically TEM analysis of etched copper patterns shows the presence of a silicon oxide passivation film on the copper surface from silicon oxide sputtered from the top hardmask or from the bottom substrate, when the primary etchant is not BCl3. Therefore, it appears that BCl3 reacts with the silicon oxide passivation layer during the etching process.

EXAMPLE SIX Etching with BCl3 as the Sole Source of Reactive Etchant Species, in Combination with a Hydrogen-Generating Source

[0146] In this Example, the plasma feed gas consists of BCl3 at a flow rate of about 100 sccm, N2 at a flow rate of about 30 sccm and CH4 at a flow rate of about 5 sccm. The temperature on the substrate surface ranged from about 250° C. and about 300° C., while the wall temperature of the etch chamber was approximately 80° C. The plasma source power was about 1,500 W; and the substrate bias power was about 600 W. The etch chamber pressure was about 25 mT.

[0147]FIG. 7B is a schematic showing a front view of a sidewall surface of a pattern-etched copper line which was one of a series in a pattern of 0.375 μm lines and spaces.

[0148] With reference to FIG. 7B, the line 730 sidewall surface 730 extends above the silicon oxide-covered substrate 732. The silicon oxide hardmask and tantalum/tantalum nitride/tantalum layers which were overlying the upper surface 722 of line 720 during the etching process have been removed. Sidewall surface 730 exhibits no pitting of the copper. No notching at upper surface 722 (between the overlying layers and the upper surface of the copper) was observed.

[0149] Although the etched sidewall surface 730 was greatly improved by the addition of the CH4 to the etchant source gas mixture, the presence of the CH4 caused the etch rate to slow from approximately 5,000 Å per minute to about 3,000 Å per minute (a still acceptable etch rate).

[0150] Although CH4 was used as the hydrogen-generating hydrocarbon source, other hydrocarbons which dissociate under etch process conditions can be used as well. One skilled in the art can look up the dissociation constants for various hydrocarbons in standard tables and determine which hydrocarbons are expected to perform well under a particular set of process conditions. Preferred hydrocarbons are those which do not contain silicon or oxygen.

[0151]FIG. 8 shows the relationship between the etch chamber pressure in mT and the electron temperature (eV) at the surface on which etching is taking place, for copper etching in the apparatus described above. Curve 800 shows that the electron temperature, shown on scale 802 decreases as the process chamber pressure, shown on scale 804 increases. This is significant, because we have determined that the following advantages are achieved when the electron temperature is lower: 1) the etch selectivity for copper over a silicon hard mask is improved, so that the hard mask is eroded more slowly; 2) the electron shading effect is reduced so that the desired etch profile is achieved, even for high aspect ratio features; and 3) a smoother etched surface, having less pitting and other defects can be obtained at a given etch rate.

EXAMPLE EIGHT Plasma Heating of Substrates

[0152] We discovered, during the development of the preferred embodiments, that it is possible to heat the substrate prior to and during the copper etch using ion bombardment of the substrate surface without harming the device structures on the substrate. We called this plasma heating of the substrate. We also discovered that the amount of substrate heating, all other process variables being relatively constant, depends on the source gas used to create the plasma, since some gases ionize more easily than others and tend to remain in an ionized condition longer. To avoid heat loss to the substrate support platen, the substrate support platen must be thermally isolated from the substrate or the substrate support platen must be a temperature-controlled support platen. Of course the amount of bias power applied to the substrate also has a significant influence on plasma heating.

[0153]FIG. 9 shows a graph 900 with a Temperature scale 910 in ° C. and a time scale 912 in seconds. Curve 914 is representative of the temperature change for a semiconductor wafer substrate due to plasma heating when argon is used as the plasma source gas. Curve 916 is representative of the temperature change for a semiconductor wafer substrate due to plasma heating when nitrogen is used as the plasma source gas. Other process conditions, which were held constant in both cases were a plasma source gas flow rate of 100 sccm, a plasma source power of 1,200 W and a bias source power of 700 W, and a plasma process chamber pressure of about 20 mT. Using the argon plasma source gas, substrate temperatures in excess of 250° C. were obtained in less than 60 seconds via plasma heating. Using the nitrogen plasma source gas, the substrate temperature was less than about 200° C. A helium plasma source gas (not shown) provides substrate plasma heating roughly equivalent to nitrogen. One skilled in the art can evaluate the plasma heating performance of plasma source gases of interest and select the gas which helps achieve a desired heating rate or final substrate temperature. As pressure in the plasma processing chamber is increased, an increase in source power or bias power or a combination thereof is required to reach the desired substrate temperature.

[0154] The above described preferred embodiments are not intended to limit the scope of the present invention, as one skilled in the art can, in view of the present disclosure, expand such embodiments to correspond with the subject matter of the invention claimed below.