CPVC J-700

Chlorinated Polyvinyl Chloride CPVC Resin

CPVC resin is a polymer material obtained from chlorination modification with polyvinyl chloride (PVC) resin. CPVC is a white or light yellow, odorless, and nontoxic. CPVC resin can be classified as extrusion grade and injection grade according to the K-value of PVC and chlorine content.

CPVC Resin Product Types

ITEMS

GRADE AND INDEX

Extrusion Grade for Pipes

Injection grade for Fittings

J-700

6067P

B1000

Z-500

5367F/5567F

Chlorine Content

%

67 – 69

67 – 69

67 – 69

66 – 68

66 – 68

30 Mesh Sieving Rate≥

%

99.0

99.0

99.0

99.0

99.0

Volatile Content≤

%

0.35

0.35

0.35

0.35

0.35

Vicat softening Temperature ≥

℃

115

115

115

115

115

Thermal Decomposition Temperature ≥

℃

110

110

110

110

110

Tensile Strength≥

MPa

50

50

50

50

50

Bending strength≥

MPa

90~120

90~120

90~120

90~120

90~120

Density

g/cm3

1.45-1.58

1.45-1.58

1.45-1.58

1.45-1.58

1.45-1.58

K Value

61 <60~63 for Extrusion(RM:K 65)>

55<53~55 for Injection(RM:K 57/60)>

*The above specifications are provided for reference only. Products could be produced per client’s requirements.

CPVC Resin Application

CPVC is highly used to produce pipelines, fittings, and various plastics accessories, it also can be used in the production of anti-corrosion coating and adhesive.

CPVC Resin Packing and specification:

This product adopts polyethylene bags for internal use and polypropylene bags for external use with a net weight of 25 ± 0.2 kg per bag.

CPVC Resin Storage and transportation:

CPVC resin must be stored in a dry and ventilated warehouse with a stack height not exceeding 10 bags. Solarization and damp environments should be avoided and strict precautions should be taken again stress. CPVC is not considered a dangerous cargo.

CPVC resin is a polymer material obtained from chlorination modification with polyvinyl chloride (PVC) resin. VIA Chemical CPVC resin can be classified as extrusion grade and injection grade according to the K-value of PVC and chlorine content.

CPE resin is a polymer material made of high-density polythene resin through chlorination reaction. According to its application, VIA Chemical CPE resin can be classified into CPE for plastic impact modification and CM for rubber.

HCPE is a high-molecular polymer obtained after substantial PE chlorination. VIA Chemical HCPE resin can be made into high viscosity, moderate viscosity and low viscosity HCPE based on PE molecular weight and difference of chlorination processes.