The Chemical and Physical Properties of Tourmaline

View/Open

Date

Author

Metadata

Abstract

The decomposition temperature of schorl was found to be 880 ± 10°C using X-ray and optical
methods. The main crystalline product in decomposed schorl and dravite was found to be a boron containing
mullrte, the composition of this phase was found to become closer to that of mullite (3Al203.2Si02) as the
decomposition temperature was increased. The size of these possibly slightly.orientated needle shaped microcrystals
was approximately 25 ± 10 u by 3 ± 2 u by 3 ± 2 u. The main decompostion products obtained in reducing
conditions, in addition to the boron containing mudite, were hercynite {FeO-Al203} at low temperatures and
oC— iron at higher temperatures. The decomposition temperature:; of schorl in the presence of activated charcoal
was found to be at least 60^C lower than that for air decomposed schorl. This decrease was thought to be associated
wcth the formation of hercynite by a low temperature reaction between schorl and activated charcoal.
The boric oxide and Iron oxide in air decomposed schorl were both extracted by dilute acid. The
rate of extraction was found to increase as the original schorl decomposition temperature was increased. The
activation energy for the extraction of boric oxide as a function of the schorl decomposition temperature was
found to be equal to 19.2 ± 0.4 kcal/mole. This increase in the rate of extraction of boric oxide was suggested
to be associated with the separation and growth of micro-regions of a boron rich phase within the silica-iron oxide
amorphous matrix. The activation energy for the extraction of boric oxide as a function of the leaching temperature
was found to be equal to 7.99 ± 0.19 kcal/mole, whilst the activation energy for the extraction of iron oxide
from air decomposed schorl was found to be equal to 7.13 ± 1.06 kcal/mole. The similarity between these values
and that of 6.8 kcal/mole for the activation energy oftacTid leaching of phase-separated borosilicate glass (138),
was thought to provide further indirect evidence for the suggestion that the amorphous phase in decomposed
schorl contains phase separated micro-regions. The rate of extraction of both boric oxide and iron from schorl
decomposed in reducing conditions was found to be considerably faster than from air decomposed schorl. This
increased extractability was thought to be connected with the presence of micro-crystals of iron in the decomposed
reduced schorl.
The boric oxide present in both schorl and dravlte was found to be extractable if water vapour was
passed over the decomposed minerals at temperatures above 1000*c. The activation energy for the extraction
of boric oxide by pyrohydrolysis from decomposed schorl was found to be equal to 85 ± 8 kcal/mole, whilst
the activation energy for the extraction of boric oxide by pyrohydrolysis from both decomposed dravite and
"pyrex" glass was found to be equal to 22 ±1 kcal/mole. The higher value was thought to be due to the incorporation
of Fe2+ ions into the amorphous silica lattice in decomposed schorl. This process was suggested to lead to
an increase in the energy barrier towards the diffusion of water vapour through the silica-iron oxide amorphous
matrix to the boron rich reaction surface.

Collections

Publisher

Commissioning body

All items in PEARL are protected by copyright law.
Author manuscripts deposited to comply with open access mandates are made available in accordance with
publisher policies. Please cite only the published version using the details provided on the item record or document.
In the absence of an open licence (e.g. Creative Commons), permissions for further reuse of content should be
sought from the publisher or author.

My Account

Help

Statistics

All items in PEARL are protected by copyright law.
Author manuscripts deposited to comply with open access mandates are made available in accordance with
publisher policies. Please cite only the published version using the details provided on the item record or document.
In the absence of an open licence (e.g. Creative Commons), permissions for further reuse of content should be
sought from the publisher or author.